Refine
Year of publication
Document Type
- Article (67)
- Postprint (8)
- Review (3)
- Conference Proceeding (1)
- Habilitation Thesis (1)
- Other (1)
- Preprint (1)
Language
- English (82)
Is part of the Bibliography
- yes (82)
Keywords
- ring-opening polymerization (6)
- biomaterials (5)
- biodegradable polymers (4)
- self-assembly (4)
- XPS (3)
- crystallization (3)
- metathesis (3)
- nanoparticles (3)
- photochemistry (3)
- spider silk (3)
Institute
This opinion article describes recent approaches to use the "biorefinery" concept to lower the carbon footprint of typical mass polymers, by replacing parts of the fossil monomers with similar or even the same monomer made from regrowing dendritic biomass. Herein, the new and green catalytic synthetic routes are for lactic acid (LA), isosorbide (IS), 2,5-furandicarboxylic acid (FDCA), and p-xylene (pXL). Furthermore, the synthesis of two unconventional lignocellulosic biomass derivable monomers, i.e., alpha-methylene-gamma-valerolactone (MeGVL) and levoglucosenol (LG), are presented. All those have the potential to enter in a cost-effective way, also the mass market and thereby recover lost areas for polymer materials. The differences of catalytic unit operations of the biorefinery are also discussed and the challenges that must be addressed along the synthesis path of each monomers.
This study aims to explore the photoinitiated cationic ring-opening polymerization of levoglucosenyl methyl ether (LGME), a chemical obtained from the most abundant biomass - cellulose. Direct and sensitized photopolymerizations of LGME using photoinitiators acting at the near UV or visible range in conjunction with diphenyliodonium hexafluoroantimonate (DPI) yielded unsaturated polyacetals with varying molar masses and distributions.
A series of biomass-derived levoglucosenyl alkyl ethers (alkyl = methyl, ethyl, n-propyl, isopropyl, and n-butyl) were synthesized and polymerized by ring-opening olefin metathesis polymerization using the Grubbs catalyst C793 at room temperature. Polymerizations were successfully performed in conventional solvents such as 1,4-dioxane and dichloromethane as well as in polar aprotic "green" solvents such as 2-methyltetrahydrofuran, dihydrolevoglucosenone (Cyrene), and ethyl acetate. The prepared polyacetals with degrees of polymerization of similar to 100 exhibit Schulz-Flory-type molar mass distributions and are thermoplastic materials with rather low glass transition temperatures in the range of 43-0 degrees C depending on the length of the alkyl substituent. Kinetic studies revealed that the polymerization proceeded rapidly to a steady state with a certain minimum monomer concentration threshold. When the steady state was reached, just about half of the [Ru] catalyst had been effective to initiate the polymerization, indicating that the initiation step was a slow process. The remaining catalyst was still active and did no longer react with monomers but with in-chain double bonds, cutting the formed polymer chains into shorter fragments. In the long term, all catalyst was consumed and propagating [Ru] chain ends were deactivated by the elimination of [Ru] from the chain ends to form inactive chains with terminal aldehyde groups.
Modular toolkit of multifunctional block copoly(2-oxazoline)s for the synthesis of nanoparticles
(2021)
Post-polymerization modification provides an elegant way to introduce chemical functionalities onto macromolecules to produce tailor-made materials with superior properties. This concept was adapted to well-defined block copolymers of the poly(2-oxazoline) family and demonstrated the large potential of these macromolecules as universal toolkit for numerous applications. Triblock copolymers with separated water-soluble, alkyne- and alkene-containing segments were synthesized and orthogonally modified with various low-molecular weight functional molecules by copper(I)-catalyzed azide-alkyne cycloaddition (CuAAC) and thiol-ene (TE) click reactions, respectively. Representative toolkit polymers were used for the synthesis of gold, iron oxide and silica nanoparticles.
Focusing on the phase-coexistence region in Langmuir films of poly(L-lactide), we investigated changes in nonequilibrated morphologies and the corresponding features of the isotherms induced by different experimental pathways of lateral compression and expansion. In this coexistence region, the surface pressure II was larger than the expected equilibrium value and was found to increase upon compression, i.e., exhibited a nonhorizontal plateau. As shown earlier by using microscopic techniques [Langmuir 2019, 35, 6129-6136], in this plateau region, well-ordered mesoscopic clusters coexisted with a surrounding matrix phase. We succeeded in reducing Pi either by slowing down the rate of compression or through increasing the waiting time after stopping the movement of the barriers, which allowed for relaxations in the coexistence region. Intriguingly, the most significant pressure reduction was observed when recompressing a film that had already been compressed and expanded, if the recompression was started from an area value smaller than the one anticipated for the onset of the coexistence region. This observation suggests a "self-seeding" behavior, i.e., pre-existing nuclei allowed to circumvent the nucleation step. The decrease in Pi was accompanied by a transformation of the initially formed metastable mesoscopic clusters into a thermodynamically favored filamentary morphology. Our results demonstrate that it is practically impossible to obtain fully equilibrated coexisting phases in a Langmuir polymer film, neither under conditions of extremely slow continuous compression nor for long waiting times at a constant area in the coexistence region which allow for reorganization.
Aminolysis induced functionalization of (RAFT) polymer-dithioester with thiols and disulfides
(2020)
A series of polystyrene- and poly(methyl methacrylate)-dithioesters was subjected to aminolysis under ambient atmospheric conditions, i.e., in the presence of oxygen. Polymer disulfide coupling by oxidation occurred within tens of minutes and the yield of disulfide-coupled polymer increased with decreasing polymer molar mass. Oxidation of thiolates is usually an unwanted side reaction, here it is employed to obtain exclusively polymeric mixed disulfides through in situ aminolysis/functionalization in the presence of a thiol. The in situ aminolysis/functionalization in the presence of a disulfide, Ellman's reagent or polymer disulfide, resulted in the exclusive formation of polymer-dithionitrobenzoic acid, which can be further reacted with a thiol to exchange the terminal functionality, or block copolymer with dynamic disulfide linker, respectively.
Epoxidized 1,4-polymyrcene
(2020)
1,4-Polymyrcene was synthesized by anionic polymerization and epoxidized using meta-chloroperbenzoic acid. Samples with different degrees of epoxidation (25%, 49%, 74%, and 98%) were prepared and examined according to their chemical and thermal properties. Epoxidation was found to increase the glass transition temperature (T-g = 14 degrees C for the 98% epoxidized 1,4-polymyrcene) as well as the shelf live (>10 months). The trisubstituted epoxide groups were remarkably stable against nucleophiles under basic conditions but cross-linked or hydrolyzed in the presence of an acid. Also, highly epoxidized 1,4-polymyrcene readily cross-linked upon annealing at 260 degrees C to produce an epoxy resin.
This opinion article describes recent approaches to use the "biorefinery" concept to lower the carbon footprint of typical mass polymers, by replacing parts of the fossil monomers with similar or even the same monomer made from regrowing dendritic biomass. Herein, the new and green catalytic synthetic routes are for lactic acid (LA), isosorbide (IS), 2,5-furandicarboxylic acid (FDCA), and p-xylene (pXL). Furthermore, the synthesis of two unconventional lignocellulosic biomass derivable monomers, i.e., alpha-methylene-gamma-valerolactone (MeGVL) and levoglucosenol (LG), are presented. All those have the potential to enter in a cost-effective way, also the mass market and thereby recover lost areas for polymer materials. The differences of catalytic unit operations of the biorefinery are also discussed and the challenges that must be addressed along the synthesis path of each monomers.
A set of new functionalized poly(2-oxazoline) homopolymers and copolymers carrying protected catecholic side chains were prepared by microwave-assisted cationic ring-opening (co)polymerization. The copolymerizations of 2-ethyl-2-oxazoline with either 2-(3,4-dimethoxyphenyl)-, 2-(3,4-dimethoxybenzyl)-, or 2-(3,4-dimethoxycinnamyl)-2-oxazoline (comonomer ratio 90 : 10) produced gradient or random copolymers with narrow molar mass distributions. During the copolymerization with the 2-(3,4-dimethoxycinnamyl)-2-oxazoline, however, chain coupling reactions occurred at monomer conversions of >50%, supposedly via Michael-type addition of intermediately formed ketene N,O-acetal end groups to 3,4-dimethoxycinnamyl amide side chains. A poly[(2-ethyl-2-oxazoline)-grad-(2-(3,4-dimethoxyphenyl)-2-oxazoline)] was examplarily subjected to partial demethylation and acidic hydrolysis to give a hydrophilic copolymer carrying both catecholic and cationic units, which is designed as a bioinspired adhesive copolymer mimicking mussel adhesive protein.
Isoprene and beta-myrcene were polymerized by anionic polymerization in bulk and in the 'green' ether solvents cyclopentyl methyl ether and 2-methyltetrahydrofuran and, for comparison, in cyclohexane and tetrahydrofuran. The polydienes produced in bulk and in cyclohexane contained high amounts of 1,4 units (>90%) whereas those produced in ether solvents were rich in 1,2 and 3,4 units (36%-86%). Comparison of the microstructures and glass transition temperatures of the polydienes obtained in the various solvents suggests that conventionally used solvents can be substituted by environmentally more friendly alternatives.
The acyclic monoterpene beta-myrcene is polymerized by anionic polymerization at room temperature using sec-butyllithium as the initiator and the cyclic monoterpene DL-limonene as an unsaturated hydrocarbon solvent. The polymerization is a living process and allows production of polymyrcenes with narrow molar mass distribution ((sic) similar to 1.06) and high content of 1,4 units (similar to 90%) as well as block copolymers.
Macrocycles based on L-cystine were synthesized by ring-closing metathesis (RCM) and subsequently polymerized by entropy-driven ring-opening metathesis polymerization (ED-ROMP). Monomer conversion reached similar to 80% in equilibrium and the produced poly (ester-amine-disulfide-alkene)s exhibited apparent molar masses (M-w(app)) of up to 80 kDa and dispersities (D) of similar to 2. The polymers can be further functionalized with acid anhydrides and degraded by reductive cleavage of the main-chain disulfide.
Multiblock-like amphiphilic polyurethanes constituted by poly(ethylene oxide) and biosourced betulin are designed for antifouling and synthesized by a convenient organocatalytic route comprising tandem chain-growth and step-growth polymerizations. The doping density of betulin (D-B) in the polymer chain structure is readily varied by a mixed-initiator strategy. The spin-coated polymer films exhibit unique nanophase separation and protein resistance behaviors. Higher D-B leads to enhanced surface hydrophobicity and, unexpectedly, improved protein resistance. It is found that the surface holds molecular-level heterogeneity when D-B is substantially high due to restricted phase separation; therefore, broad-spectrum protein resistance is achieved despite considerable surface hydrophobicity. As D-B decreases, the distance between adjacent betulin units increases so that hydrophobic nanodomains are formed, which provide enough landing areas for relatively small-sized proteins to adsorb on the surface.
Metal-free entropy-driven disulfide metathesis polymerization of unsaturated L-cystine based macrocycles produces high-molar-mass heterofunctional poly(disulfide)s, i.e., poly(ester-disulfide-alkene) and poly(amide-disulfide-alkene); M-w(app) = 44-60 kDa, (sic) > 1.7. The polymerization is fast and reaches equilibrium within 1-5 minutes (monomer conversion 70-90%) in polar aprotic solvents such as N,N-dimethylacetamide, dimethylsulfoxide, or y-valerolactone. Thiol-terminated polymers are stable in bulk or when dissolved in weakly polar solvents, but rapidly depolymerize in dilute polar solution.
1,4-Polymyrcene was synthesized by anionic polymerization of -myrcene and was subjected to photochemical functionalization with various thiols (i.e. methyl thioglycolate, methyl 3-mercaptopropionate, butyl 3-mercaptopropionate, ethyl 2-mercaptopropionate and 2-methyl-2-propanethiol) using benzophenone/UV light as the radical source. The yield of thiol addition to the trisubstituted double bonds of 1,4-polymyrcene decreased in the order 1 degrees thiol (ca 95%) > 2 degrees thiol (ca 80%) > 3 degrees thiol (<5%), due to the reversibility of the thiol-ene reaction. Remarkably, thiol addition to the side-chain double bonds was 8 - 10 times (1 degrees thiol) or 24 times (2 degrees thiol) faster than to the main-chain double bonds, which can be explained by the different accessibility of the double bonds and steric hindrance. Despite the use of a 10-fold excess of thiol with respect to myrcene units, the thiol-ene addition was accompanied by chain coupling reactions, which in the extreme case of 3 degrees thiol (or in the absence of thiol) resulted in the formation of insoluble crosslinked material. As an example, a methyl-thioglycolate-functionalized 1,4-polymyrcene was saponified/crosslinked to give submicron polyelectrolyte particles in dilute alkaline solution. (c) 2018 Society of Chemical Industry
Stable covalently photo-cross-linked porous poly(ionic liquid) membrane with gradient pore size
(2018)
Porous polyelectrolyte membranes stable in a highly ionic environment are obtained by covalent crosslinking of an imidazolium-based poly(ionic liquid). The crosslinking reaction involves the UV light-induced thiol-ene (click) chemistry, and the phase separation, occurring during the crosslinking step, generates a fully interconnected porous structure in the membrane. The porosity is on the order of the micrometer scale and the membrane shows a gradient of pore size across the membrane cross-section. The membrane can separate polystyrene latex particles of different size and undergoes actuation in contact with acetone due to the asymmetric porous structure.
Helical structures are ubiquitous in biological materials and often serve a structural purpose. Bioinspired helical materials can be challenging to synthesize and rarely reach the degree of hierarchy of their natural counterparts. Here we report the first example of particles synthesized by direct emulsification of polypeptides found to display spiral morphologies in the dry state. The polypeptides were alpha-helical homo- and copolypeptides of gamma-benzyl glutamate and allylglycine. The chirality of the spirals was controlled by the chirality of the alpha-helices. Notably, right-handed alpha-helical polypeptides (rich in 1, residues) produced clockwise spirals, whereas left-handed alpha-helical polypeptides (rich in D residues) produced the enantiomorphs, i.e., counterclockwise spirals. The disruption of the alpha-helical conformation by the introduction of chiral defects led to less regular spirals and in some cases their suppression. A hypothesis for the transmission of helicity and chirality from a molecular to a higher hierarchical level, involving fibril bundling of coiled alpha-helices, is proposed.
In this study, we present a novel and facile method for the synthesis of multiresponsive plasmonic nanoparticles with an interesting interfacial behavior. We used thiol-initiated photopolymerization technique to graft poly(N-isopropylacrylamide) onto the surface of protein-coated gold nanoparticles. The combination of the protein bovine serum albumin with the thermoresponsive polymer leads to smart hybrid nanoparticles, which show a stimuli-responsive behavior of their aggregation and a precisely controllable phase transfer behavior. Three interconnected stimuli, namely, temperature, ionic strength, and pH, were identified as property tuning switches. The aggregation was completely reversible and was quantified by determining Smoluchowski’s instability ratios with time-resolved dynamic light scattering. The tunable hydrophobicity via the three stimuli was used to study interfacial activity and phase transfer behavior of the nanoparticles at an octanol/water interface. Depending on the type of coating (i.e., protein or protein/polymer) as well as the three external stimuli, the nanoparticles either remained in the aqueous phase (aggregated or nonaggregated), accumulated at the oil/water interface, wet the glass wall between the glass vial and the octanol phase, or even crossed the oil/water interface. Such smart and interfacially active nanoparticles with external triggers that are capable of crossing oil/water interfaces under physiological conditions open up new avenues for a variety of applications ranging from the development of drug-delivery nanosystems across biological barriers to the preparation of new catalytic materials.
Silk protein-based materials show promise for application as biomaterials for tissue engineering. The simple and rapid photochemical modification of silk protein-based materials composed of either Bombyx mori silkworm silk or engineered spider silk proteins (eADF4(C16)) is reported. Radicals formed on the silk-based materials initiate the polymerization of monomers (acrylic acid, methacrylic acid, or allylamine) which functionalize the surface of the silk materials with poly(acrylic acid) (PAA), poly(methacrylic acid) (PMAA), or poly(allylamine) (PAAm). To demonstrate potential applications of this type of modification, the polymer-modified silks are mineralized. The PAA- and PMAA-functionalized silks are mineralized with calcium carbonate, whereas the PAAm-functionalized silks are mineralized with silica, both of which provide a coating on the materials that may be useful for bone tissue engineering, which will be the subject of future investigations.
Polypeptoids are noticeable biological materials due to their versatile properties and various applications in drug delivery, surface modification, self-assembly, etc. N-Substituted glycine N-thiocarboxyanhydrides (NNTAs) are more stable monomers than the corresponding N-carboxyanhydrides (NNCAs) and enable one to prepare polypeptoids via ring-opening polymerization even in the presence of water. However, larger amounts of water (>10,000 ppm) cause inhibition of the polymerization. Herein, we discover that during polymerization hydrogen sulfide evolves from the hydrolysis of carbonyl sulfide, which is the byproduct of ring-opening reaction, and reacts with NNTA to produce cyclic oligopeptoids. The capture of N-ethylethanethioic acid as an intermediate product confirms the reaction mechanism together with density functional theory quantum computational results. By bubbling the polymerization solution with argon, the side reaction can be suppressed to allow the synthesis of polysarcosine with high molar mass (M-n = 11,200 g/mol, D = 1.25) even in the presence of similar to 10,000 ppm of water.
A series of phenolic-acid-based 2-oxazoline monomers with methoxy-substituted phenyl and cinnamyl side chains is synthesized and polymerized in a microwave reactor at 140 °C using methyl tosylate as the initiator. The obtained poly(2-oxazoline)s are characterized by NMR spectroscopy, MALDI-TOF mass spectrometry, and size-exclusion chromatography (SEC). Kinetic studies reveal that the microwave-assisted polymerization is fast and completed within less than ≈10 min for low monomer-to-initiator ratios of ≤25. Polymers with number-average molar masses of up to 6500 g mol−1 and low dispersity (1.2–1.3) are produced. The aryl methyl ethers are successfully cleaved with aluminum triiodide/N,N′-diisopropylcarbodiimide to give a poly(2-oxazoline) with pendent catechol groups.
The aqueous self-assembly behavior of a series of poly(ethylene glycol)-poly(l-/d-lactide) block copolymers and corresponding stereocomplexes is examined by differential scanning calorimetry, dynamic light scattering, and transmission electron microscopy. Block copolymers assemble into spherical micelles and worm-like aggregates at room temperature, whereby the fraction of the latter seemingly increases with decreasing lactide weight fraction or hydrophobicity. The formation of the worm-like aggregates arises from the crystallization of the polylactide by which the spherical micelles become colloidally unstable and fuse epitaxically with other micelles. The self-assembly behavior of the stereocomplex aggregates is found to be different from that of the block copolymers, resulting in rather irregular-shaped clusters of spherical micelles and pearl-necklace-like structures.
Cystine was used as a platform chemical to prepare cyclic and acyclic monomers for entropy-driven ringopening polymerization (ED-ROMP) via olefin or disulfide metathesis and for step-growth polymerization. The olefin ED-ROMP of an olefin/disulfide containing 16-atom macrocycle using the 3rd generation Grubbs catalyst was examined in greater detail. Kinetic studies revealed that the catalyst turned inactive during the polymerization, which limited the achievable (apparent) polymer molar mass to similar to 70 kg mol(-1). Such limitation could be overcome with the disulfide ED-ROMP of the same macrocycle to yield polymers with molar masses of up to 180 kg mol(-1). The step-growth polymerizations of acyclic diene and dithiol monomers via olefin metathesis or oxidation were far less effective and yielded just low molar mass polymers or oligomers; photopolymerization of a thiol-ene monomer produced a polyester with a molar mass of 35 kg mol(-1).
We studied morphological changes in a quasi-two-dimensional Langmuir film of low molar mass poly(L-lactide) upon increasing the surface density, starting from randomly distributed molecules to a homogeneous monolayer of closely packed molecules, followed by nucleation and growth of mesoscopic, three-dimensional clusters from an overcompressed monolayer. The corresponding nucleation density of mesoscopic clusters within the monolayer can be tailored through variation of the rate of compression. For a given surface density and temperature, the nucleation probability was found to increase linearly with the rate of compression, allowing to adjust the density of mesoscopic clusters over nearly 2 orders magnitude.
In virtue of the rising demand for metal-free polymeric materials, organocatalytic polymerization has emerged and blossomed unprecedentedly in the past 15 years into an appealing research area and a powerful arsenal for polymer synthesis. In addition to the inherent merits as being metal-free, small molecule organocatalysts have also provided opportunities to develop alternative and, in many cases, more expedient synthetic approaches toward macromolecular architectures, that play a crucial role in shaping the properties of the obtained polymers. A majority of preliminary studies exploring for new catalysts, catalytic mechanisms and optimized polymerization conditions are extended to application of the catalytic systems on rational design and controlled synthesis of various macromolecular architectures. Such endeavors are described in this review, categorized by the architectural elements including chain structure (types, sequence and composition of monomeric units constituting the polymer chains), topological structure (the fashion different polymer chains are covalently attached to each other within the macromolecule) and functionality (position and amount of functional groups that endow the entire macromolecule with specific chemical, physico-chemical or biological properties). (C) 2017 Published by Elsevier B.V.
The readily available cellulose-derived bicyclic compound levoglucosenol was polymerized through ring-opening metathesis polymerization (ROMP) to yield polylevoglucosenol as a novel type of biomass-derived thermoplastic polyacetal, which, unlike polysaccharides, contains cyclic as well as linear segments in its main chain. High-molar-mass polyacetals with apparent weight-average molar masses of up to 100kgmol(-1) and dispersities of approximately 2 were produced despite the non-living/controlled character of the polymerization due to irreversible deactivation or termination of the catalyst/active chain ends. The resulting highly functionalized polyacetals are glassy in bulk with a glass transition temperature of around 100 degrees C. In analogy to polysaccharides, polylevoglucosenol degrades slowly in an acidic environment.
Near ambient pressure - x-ray photoelectron spectroscopy (NAP-XPS) is a less traditional form of XPS that allows samples to be analyzed at relatively high pressures, i.e., at 2500Pa or higher. With NAP-XPS, one can analyze moderately volatile liquids, biological samples, porous materials, and/or polymeric materials that outgas significantly. In this submission we show C 1s, O 1s, and survey NAP-XPS spectra from poly(L-lactic acid). The C 1s and O 1s envelopes were fit with three and two Gaussian-Lorentzian sum functions, respectively. Water vapor (800Pa) was used as the residual gas for charge compensation, which was confirmed by the sharp peak at 535.0 eV in the O 1s narrow scan. The uniqueness plot corresponding to the C 1s fit shows that the fit parameters had statistical significance. C 1s and O 1s spectra of PLLA damaged by exposure to x-rays for ca. 1 hour are also included. Published by the AVS.
Near-ambient pressure x-ray photoelectron spectroscopy (NAP-XPS) is a less traditional form of XPS that allows samples to be analyzed at relatively high pressures, i. e., at greater than 2500 Pa. In this study, poly(.- benzyl L- glutamate) (PBLG) with a molar mass of 11.3 kg/mol was analyzed by NAP-XPS; here, we show the survey, C 1s, N 1s, and O 1s narrow scans of PBLG. The C 1s peak envelope was fitted in three different ways, to five, six, or seven synthetic peaks. In each fit, there was also a shake-up signal. The O 1s narrow scan was well fit with three peaks: CZO and CvO in a 1:2 ratio from the polymer, and a higher energy signal from water vapor. Hartree-Fock orbital energies of a model monomer served as a guide to an additional fit of the C 1s envelope.
Molecular dynamics simulations in conjunction with the Martini coarse-grained model have been used to investigate the (nonequilibrium) behavior of helical 22-residue poly(gamma-benzyl-L-glutamate) (PBLG) peptides at the water/vapor interface. Preformed PBLG mono- or bilayers homogeneously covering the water surface laterally collapse in tens of nanoseconds, exposing significant proportions of empty water surface. This behavior was also observed in recent AFM experiments at similar areas per monomer, where a complete coverage had been assumed in earlier work. In the simulations, depending on the area per monomer, either elongated clusters or fibrils form, whose heights (together with the portion of empty water surface) increase over time. Peptides tend to align with respect to the fiber axis or with the major principal axis of the cluster, respectively. The aspect ratio of the cluster observed is 1.7 and, hence, comparable to though somewhat smaller than the aspect ratio of the peptides in alpha-helical conformation, which is 2.2. The heights of the fibrils is 3 nm after 20 ns and increases to 4.5 nm if the relaxation time is increased by 2 orders of magnitude, in agreement with the experiment. Aggregates with heights of about 3 or 4.5 nm are found to correspond to local bi- or trilayer structures, respectively.
The aqueous solution behavior of thermoresponsive-hydrophilic block copolypeptoids, i.e., poly(N-(n-propyl)glycine) (x) -block-poly(N-methylglycine) (y) (x = 70; y = 23, 42, 76), in the temperature range of 20-45 A degrees C is studied. Turbidimetric analyses of the 0.1 wt% aqueous solutions reveal two cloud points at T (cp)similar to 30 and 45 A degrees C and a clearing point in between at T (cl)similar to 42 A degrees C. Temperature-dependent dynamic light scattering (DLS) suggest that right above the first collapse temperature, single polymer molecules assemble into large structures which upon further heating, i.e., at the clearing point temperature, disassemble into micelle-like structures. Upon further heating, the aggregates start to grow again in size, as recognized by the second cloud point, through a crystallization process.
Porous polyelectrolyte membranes stable in a highly ionic environment are obtained by covalent crosslinking of an imidazolium-based poly(ionic liquid). The crosslinking reaction involves the UV light-induced thiol-ene (click) chemistry, and the phase separation, occurring during the crosslinking step, generates a fully interconnected porous structure in the membrane. The porosity is on the order of the micrometer scale and the membrane shows a gradient of pore size across the membrane cross-section. The membrane can separate polystyrene latex particles of different size and undergoes actuation in contact with acetone due to the asymmetric porous structure.
The mechanism of the primary ammonium/tertiary amine-mediated ring-opening polymerization of gamma-benzyl-L-glutamate N-carboxyanhydride (BLG-NCA) was investigated. Kinetic analyses revealed that the normal amine mechanism (NAM) together with a dormant-active chain end equilibrium were responsible for the controlled nature of this polymerization pathway, but that the polymerization also proceeded via the activated monomer mechanism (AMM). Mixtures of primary amines (1 equiv) and tertiary amines (0-1.5 equiv) were therefore tested to confirm the co-existence of the NAM and AMM and determine the limits for a controlled polymerization. For tertiary amine molar fractions smaller than 0.8 equiv, the reaction times were greatly reduced (compared to primary amine-initiated polymerization) without compromising the control of the reaction. Hence, the polymerization of NCA can proceed in a controlled manner even when the AMM contributes to the overall chain growth mechanism. (C) 2017 Elsevier Ltd. All rights reserved.
The nucleophilic thiol-ene (thia-Michael) reaction between molecular rods bearing terminal thiols and bis-maleimides was investigated. The molecular rods have oligospiroketal (OSK) and oligospirothioketal (OSTK) backbones. Contrary to the expectations, cyclic oligomers were always obtained instead of linear rigid-rod polymers. Replacing the OS(T)K rods with a flexible chain yielded polymeric products, suggesting that the OS(T) K structure is responsible for the formation of cyclic products. The reason for the preferred formation of cyclic products is due to the presence of folded conformations, which have already been described for articulated rods.
A unique fabrication process of low molar mass, crystalline polypeptoid fibers is described. Thermoresponsive fiber mats are prepared by electrospinning a homogeneous blend of semicrystalline poly(N-(n-propyl) glycine) (PPGly; 4.1 kDa) with high molar mass poly(ethylene oxide) (PEO). Annealing of these fibers at approximate to 100 degrees C selectively removes the PEO and produces stable crystalline fiber mats of pure PPGly, which are insoluble in aqueous solution but can be redissolved in methanol or ethanol. The formation of water-stable polypeptoid fiber mats is an important step toward their utilization in biomedical applications such as tissue engineering or wound dressing.
Polysarcosine (M-n = 3650-20 000 g mol(-1), D similar to 1.1) was synthesized from the air and moisture stable N-phenoxycarbonyl-N-methylglycine. Polymerization was achieved by in situ transformation of the urethane precursor into the corresponding N-methylglycine-N-carboxyanhydride, when in the presence of a non-nucleophilic tertiary amine base and a primary amine initiator.
Block copolypeptoids comprising a thermosensitive, crystallizable poly(N-(n-propyl)glycine) block and a watersoluble poly(N-methylglycine) block, P70My (y = 23, 42, 76, 153, and 290), were synthesized bY ring-opening polymerization of the corresponding N-alkylglycine N-carboxyanhydrides (NCAs) and examined according to their thermo-induced aggregation and crystallization in water by turbidimetty, micro-differential scanning calorimetry (micro-DSC); cryogenic scanning electron microscopy (cryo-SEM), analytical ultracentrifugation (AUC), and static light scattering (SLS). At a temperature above the cloud point temperature, the initially formed micellar aggregates started to crystallize and grow into larger complex assemblies of about 100-500 nm, exhibiting flower-like (P70M23), ellipsoidal (P70M42 and P70M72) or irregular shapes (P70M153 and.P70M290).
Poly(2-alkyl-2-oxazoline)s (PAOx) exhibit different crystallization behavior depending on the length of the alkyl side chain. PAOx having methyl, ethyl, or propyl side chains do not show any bulk crystallization. Crystallization in the heating cycle, that is, cold crystallization, is observed for PAOx with butyl and pentyl side chains. For PAOx with longer alkyl side chains crystallization occurs in the cooling cycle. The different crystallization behavior is attributed to the different polymer chain mobility in line with the glass transition temperature (T-g) dependency on alkyl side chain length. The decrease in chain mobility with decreasing alkyl side chain length hinders the relaxation of the polymer backbone to the thermodynamic equilibrium crystalline structure. Double melting behavior is observed for PButOx and PiPropOx which is explained by the melt-recrystallization mechanism. Isothermal crystallization experiments of PButOx between 60 and 90 degrees C and PiPropOx between 90 and 150 degrees C show that PAOx can crystallize in bulk when enough time is given. The decrease of Tg and the corresponding increase in chain mobility at T > T-g with increasing alkyl side chain length can be attributed to an increasing distance between the polymer backbones and thus decreasing average strength of amide dipole interactions. (C) 2015 Wiley Periodicals, Inc.
Bio-inspired Laponite (clay)-liquid crystal (LC) polymer composite materials with high clay fractions (>80%) and a high level of orientation of the clay platelets, i.e. with structural features similar to the ones found in natural nacre, have been shown to exhibit a promising behavior in the context of reduced oxygen transmission. Key characteristics of these bio-inspired composite materials are their high inorganic content, high level of exfoliation and orientation of the clay platelets, and the use of a LC polymer forming the organic matrix in between the Laponite particles. Each single feature may be beneficial to increase the materials gas barrier property rendering this composite a promising system with advantageous barrier capacities. In this detailed study, Laponite/LC polymer composite coatings with different clay loadings were investigated regarding their oxygen transmission rate. The obtained gas barrier performance was linked to the quality, respective Laponite content and the underlying composite micro-and nanostructure of the coatings. Most efficient oxygen barrier properties were observed for composite coatings with 83% Laponite loading that exhibit a structure similar to sheet-like nacre. Further on, advantageous mechanical properties of these Laponite/LC polymer composites reported previously give rise to a multifunctional composite system.
Owing to its rod-like alpha-helical secondary structure, the synthetic polypeptide poly(gamma-benzyl-L-glutamate) (PBLG) can form physical and thermoreversible gels in helicogenic solvents such as toluene. The versatility of PBLG can be increased by introducing functionalizable comonomers, such as allylglycine (AG). In this work we examined the secondary structure of PBLG and a series of statistical poly(gamma-benzyl-L-glutamate-co-allylglycine) copolypeptides, varying in composition and chain length, by circular dichroism (CD), Fourier-transform infrared (FTIR) and Raman spectroscopy, and wide-angle X-ray scattering (WAXS). The secondary structure of PBLG and the copolypeptides presented dissimilarities that increased with increasing AG molar fraction, especially when racemic AG units were incorporated. The physical gelation behavior of these copolypeptides was analyzed by temperature-sweep H-1 NMR and rheological measurements. The study revealed that both copolypeptide composition and chain length affected secondary structure, gelation temperature, and gel stiffness.
Materials based on biodegradable polyesters, such as poly(butylene terephthalate) (PBT) or poly(butylene terephthalate-co-poly(alkylene glycol) terephthalate) (PBTAT), have potential application as pro-regenerative scaffolds for bone tissue engineering. Herein, the preparation of films composed of PBT or PBTAT and an engineered spider silk protein, (eADF4(C16)), that displays multiple carboxylic acid moieties capable of binding calcium ions and facilitating their biomineralization with calcium carbonate or calcium phosphate is reported. Human mesenchymal stem cells cultured on films mineralized with calcium phosphate show enhanced levels of alkaline phosphatase activity suggesting that such composites have potential use for bone tissue engineering.
This report describes the aggregation behavior of an ABC-type ampholytic block copolypeptide, poly(ethylene oxide)-block-poly(L-lysine)-block-poly(L-glutamate), in aqueous media in dependence of pH. Polypeptide secondary structures and self-assemblies are investigated by circular dichroism (CD), Fourier transform infrared (FT-IR) and NMR spectroscopy, zeta potential measurements, analytical ultracentrifugation (AUC), dynamic/static light scattering (DLS/SLS), and cryogenic transmission electron microscopy (cryoTEM). The polymer chains tend to form vesicles when the hydrophobic polypeptide helix is located at the chain end (acidic pH) and are existing as single chains when it is located in the center and flanked by the two hydrophilic segments (basic pH). Precipitation occurs in the intermediate pH range due to polyion complexation of the charged polypeptide segments.
Due to the adsorption of biomolecules, the control of the biodistribution of nanoparticles is still one of the major challenges of nanomedicine. Poly(2-ethyl-2-oxazoline) (PEtOx) for surface modification of nanoparticles is applied and both protein adsorption and cellular uptake of PEtOxylated nanoparticles versus nanoparticles coated with poly(ethylene glycol) (PEG) and non-coated positively and negatively charged nanoparticles are compared. Therefore, fluorescent poly(organosiloxane) nanoparticles of 15 nm radius are synthesized, which are used as a scaffold for surface modification in a grafting onto approach. With multi-angle dynamic light scattering, asymmetrical flow field-flow fractionation, gel electrophoresis, and liquid chromatography-mass spectrometry, it is demonstrated that protein adsorption on PEtOxylated nanoparticles is extremely low, similar as on PEGylated nanoparticles. Moreover, quantitative microscopy reveals that PEtOxylation significantly reduces the non-specific cellular uptake, particularly by macrophage-like cells. Collectively, studies demonstrate that PEtOx is a very effective alternative to PEG for stealth modification of the surface of nanoparticles.
Yolk@Shell Nanoarchitectures with Bimetallic Nanocores - Synthesis and Electrocatalytic Applications
(2016)
A one-step moderate energy vibrational emulsification method was successfully employed to produce thermo-responsive olive/silicone-based Janus emulsions stabilized by poly(N,N-diethylacrylamide) carrying 0.7 mol% oleoyl side chains. Completely engulfed emulsion droplets remained stable at room temperature and could be destabilized on demand upon heating to the transition temperature of the polymeric stabilizer. Time-dependent light micrographs demonstrate the temperature-induced breakdown of the Janus droplets, which opens new aspects of application, for instance in biocatalysis.
A one-step moderate energy vibrational emulsification method was successfully employed to produce thermo-responsive olive/silicone-based Janus emulsions stabilized by poly(N,N-diethylacrylamide) carrying 0.7 mol% oleoyl side chains. Completely engulfed emulsion droplets remained stable at room temperature and could be destabilized on demand upon heating to the transition temperature of the polymeric stabilizer. Time-dependent light micrographs demonstrate the temperature-induced breakdown of the Janus droplets, which opens new aspects of application, for instance in biocatalysis.
Materials based on biodegradable polyesters, such as poly(butylene terephthalate) (PBT) or poly(butylene terephthalate-co-poly(alkylene glycol) terephthalate) (PBTAT), have potential application as pro-regenerative scaffolds for bone tissue engineering. Herein, the preparation of films composed of PBT or PBTAT and an engineered spider silk protein, (eADF4(C16)), that displays multiple carboxylic acid moieties capable of binding calcium ions and facilitating their biomineralization with calcium carbonate or calcium phosphate is reported. Human mesenchymal stem cells cultured on films mineralized with calcium phosphate show enhanced levels of alkaline phosphatase activity suggesting that such composites have potential use for bone tissue engineering.
Macrocycles based on L-cystine were synthesized by ring-closing metathesis (RCM) and subsequently polymerized by entropy-driven ring-opening metathesis polymerization (ED-ROMP). Monomer conversion reached ∼80% in equilibrium and the produced poly(ester-amine-disulfide-alkene)s exhibited apparent molar masses (Mappw) of up to 80 kDa and dispersities (Đ) of ∼2. The polymers can be further functionalized with acid anhydrides and degraded by reductive cleavage of the main-chain disulfide.