Quyet Doan Nguyen, Jingwen Wang, Dmitry Rychkov, Reimund Gerhard

• In the present study, the charge distribution and the charge transport across the thickness of 2- and 3-dimensional polymer nanodielectrics was investigated. Chemically surface-treated polypropylene (PP) films and low-density polyethylene nanocomposite films with 3 wt % of magnesium oxide (LDPE/MgO) served as examples of 2-D and 3-D nanodielectrics, respectively. Surface charges were deposited onto the non-metallized surfaces of the one-side metallized polymer films and found to broaden and to thus enter the bulk of the films upon thermal stimulation at suitable elevated temperatures. The resulting space-charge profiles in the thickness direction were probed by means of Piezoelectrically-generated Pressure Steps (PPSs). It was observed that the chemical surface treatment of PP which led to the formation of nano-structures or the use of bulk nanoparticles from LDPE/MgO nanocomposites enhance charge trapping on or in the respective polymer films and also reduce charge transport inside the respective samples.