TY - THES A1 - Chaleawlert-Umpon, Saowaluk T1 - Sustainable electrode materials based on lignin T1 - Ligninbasierte nachhaltige Elektrodenmaterialien N2 - The utilization of lignin as renewable electrode material for electrochemical energy storage is a sustainable approach for future batteries and supercapacitors. The composite electrode was fabricated from Kraft lignin and conductive carbon and the charge storage contribution was determined in terms of electrical double layer (EDL) and redox reactions. The important factors at play for achieving high faradaic charge storage capacity contribute to high surface area, accessibility of redox sites in lignin and their interaction with conductive additives. A thinner layer of lignin covering the high surface area of carbon facilitates the electron transfer process with a shorter pathway from the active sites of nonconductive lignin to the current collector leading to the improvement of faradaic charge storage capacity. Composite electrodes from lignin and carbon would be even more sustainable if the fluorinated binder can be omitted. A new route to fabricate a binder-free composite electrode from Kraft lignin and high surface area carbon has been proposed by crosslinking lignin with glyoxal. A high molecular weight of lignin is obtained to enhance both electroactivity and binder capability in composite electrodes. The order of the processing step of crosslinking lignin on the composite electrode plays a crucial role in achieving a stable electrode and high charge storage capacity. The crosslinked lignin based electrodes are promising since they allow for more stable, sustainable, halogen-free and environmentally benign devices for energy storage applications. Furthermore, improvement of the amount of redox active groups (quinone groups) in lignin is useful to enhance the capacity in lithium battery applications. Direct oxidative demethylation by cerium ammonium nitrate has been carried out under mild conditions. This proves that an increase of quinone groups is able to enhance the performance of lithium battery. Thus, lignin is a promising material and could be a good candidate for application in sustainable energy storage devices. N2 - Die Verwendung von Lignin als erneuerbares Ausgangsmaterial für Elektroden ist ein nachhaltiger Ansatz für die Herstellung der nächsten Generation von Batterien und Superkondensatoren. In dieser Arbeit werden Verbundelektroden auf der Basis von Kraft-Lignin und leitfähigem Kohlenstoff hergestellt und getestet. Die Beiträge des Aufbaus einer elektrischen Doppelschicht (EDL) und der Redoxreaktionen zur Kapazität der Elektrode werden diskutiert. Die wichtigsten Faktoren um eine hohe faradaysche Kapazität der aktiven Gruppen in Lignin zu erreichen sind eine große Oberfläche, die Zugänglichkeit der redoxaktiven Gruppen, sowie die Wechselwirkung mit leitfähigen Additiven. Dabei verringert eine dünnere Ligninschicht auf der Oberfläche des leitfähigen Kohlenstoffs den Elektronentransportweg zwischen den redoxaktiven Gruppen und dem Stromabnehmer und wirkt sich somit positiv auf die faradaysche Kapazität aus. Traditionelle Verbundelektroden enthalten in der Regel fluorierte Bindemittel, was deren Nachhaltigkeit in Frage stellt. Die Verwendung von Glyoxal als Quervernetzer für Lignin stellt eine Alternative zur Herstellung von bindemittelfreien ligninbasierten Verbundelektroden dar. Durch die Quervernetzung wird Lignin mit hohem Molekulargewicht erhalten, was sich insbesondere vorteilhaft auf die Stabilität der Elektroden auswirkt. Für das Erreichen einer hohen Kapazität spielt allerdings die Reihenfolge der Produktionsschritte eine entscheidende Rolle, was hier auch diskutiert wird. Eine Erhöhung der Anzahl an redoxativen Gruppen, insbesondere Chinon-Funktionalitäten, im Lignin führt darüber hinaus zur Erhöhung der Kapazität in primären Lithiumbatterien. Die direkte oxidative Demethylierung von Phenylethern mit Hilfe von Cerammoniumnitrat wurde in dieser Arbeit unter milden Reaktionsbedingungen durchgeführt und die verbesserte Kapazität in Lithiumbatterien aufgrund der erhöhten Anzahl an redoxaktiven Gruppen aufgezeigt. Abschließend kann Lignin, quervernetzt oder oxidiert, als vielversprechender Wegbereiter für nachhaltige Materialen in der Energiespeicherung angesehen werden. KW - lignin KW - energy storage KW - sustainable energy storage materials KW - Lignin KW - Energiespeicher KW - nachhaltige Energiespeichermaterialien Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-411793 ER - TY - THES A1 - Schutjajew, Konstantin T1 - Electrochemical sodium storage in non-graphitizing carbons - insights into mechanisms and synthetic approaches towards high-energy density materials T1 - Elektrochemische Natriumspeicherung in nicht-graphitisierbaren Kohlenstoffen - Untersuchungen zu Mechanismen und synthetische Ansätze für die Darstellung von Materialien mit hohen Energiedichten N2 - To achieve a sustainable energy economy, it is necessary to turn back on the combustion of fossil fuels as a means of energy production and switch to renewable sources. However, their temporal availability does not match societal consumption needs, meaning that renewably generated energy must be stored in its main generation times and allocated during peak consumption periods. Electrochemical energy storage (EES) in general is well suited due to its infrastructural independence and scalability. The lithium ion battery (LIB) takes a special place, among EES systems due to its energy density and efficiency, but the scarcity and uneven geological occurrence of minerals and ores vital for many cell components, and hence the high and fluctuating costs will decelerate its further distribution. The sodium ion battery (SIB) is a promising successor to LIB technology, as the fundamental setup and cell chemistry is similar in the two systems. Yet, the most widespread negative electrode material in LIBs, graphite, cannot be used in SIBs, as it cannot store sufficient amounts of sodium at reasonable potentials. Hence, another carbon allotrope, non-graphitizing or hard carbon (HC) is used in SIBs. This material consists of turbostratically disordered, curved graphene layers, forming regions of graphitic stacking and zones of deviating layers, so-called internal or closed pores. The structural features of HC have a substantial impact of the charge-potential curve exhibited by the carbon when it is used as the negative electrode in an SIB. At defects and edges an adsorption-like mechanism of sodium storage is prevalent, causing a sloping voltage curve, ill-suited for the practical application in SIBs, whereas a constant voltage plateau of relatively high capacities is found immediately after the sloping region, which recent research attributed to the deposition of quasimetallic sodium into the closed pores of HC. Literature on the general mechanism of sodium storage in HCs and especially the role of the closed pore is abundant, but the influence of the pore geometry and chemical nature of the HC on the low-potential sodium deposition is yet in an early stage. Therefore, the scope of this thesis is to investigate these relationships using suitable synthetic and characterization methods. Materials of precisely known morphology, porosity, and chemical structure are prepared in clear distinction to commonly obtained ones and their impact on the sodium storage characteristics is observed. Electrochemical impedance spectroscopy in combination with distribution of relaxation times analysis is further established as a technique to study the sodium storage process, in addition to classical direct current techniques, and an equivalent circuit model is proposed to qualitatively describe the HC sodiation mechanism, based on the recorded data. The obtained knowledge is used to develop a method for the preparation of closed porous and non-porous materials from open porous ones, proving not only the necessity of closed pores for efficient sodium storage, but also providing a method for effective pore closure and hence the increase of the sodium storage capacity and efficiency of carbon materials. The insights obtained and methods developed within this work hence not only contribute to the better understanding of the sodium storage mechanism in carbon materials of SIBs, but can also serve as guidance for the design of efficient electrode materials. N2 - Eine nachhaltige Energiewirtschaft kann nur durch die Abkehr von fossilen Brennstoffen als Energiequellen und den ausschließlichen Einsatz erneuerbarer Quellen für die Energieerzeugung erreicht werden. Da diese jedoch naturgemäß nur diskontinuierlich zur Verfügung stehen und sich die tageszeitliche Verfügbarkeit kaum mit dem Bedarf deckt, muss erneuerbar gewonnene Energie zwischengespeichert werden. Dies kann mittels elektrochemischer Energiespeicher geschehen, wobei sich die Lithium-Ionen-Batterie (LIB) aufgrund ihrer hohen Energiedichte und Effizienz besonders dafür eignet. Da jedoch Ressourcen, welche für entscheidende Zellkomponenten der LIB benötigt werden, knapper werden und oft in geopolitisch komplizierten Regionen vorkommen, muss auch dafür eine Alternative gefunden werden. Die Natrium-Ionen-Batterie (NIB) bietet sich als Nachfolger für LIBs an, da sich die Zellchemie der beiden Systeme ähnelt und somit Kenntnisse direkt aus der LIB-Forschung übernommen werden können. Es erweist sich allerdings als problematisch, dass das kommerziell wichtigste negative Elektrodenmaterial in LIBs, Graphit, nicht für die Anwendung in NIBs eignet und daher eine andere Kohlenstoffmodifikation, sogenannter nicht-graphitisierbarer Kohlenstoff, oder aus dem Englischen hard carbon (HC), verwendet werden muss. HC ist durch eine besondere Art der Fehlordnung geprägt und besteht im Wesentlichen aus Regionen, in denen die Kohlenstoffschichten parallel zueinander verlaufen und aus Regionen, in denen die Schichten innere Hohlräume, sogenannte geschlossene Poren bilden. Die Lade-Entladekurve von HCs ist geprägt von diesen Strukturmerkmalen, sodass sie in einen linear-abflachenden, aus dem Englischen sloping Bereich, und einen Plateaubereich unterteilt werden kann. Die Speicherung im für Energieanwendungen relevanteren Plateaubereich erfolgt durch Abscheidung quasimetallischer Natriumstrukturen in eingangs erwähnten geschlossenen Poren, bei geringen, konstanten Spannungen, wie zahlreiche Forschungsarbeiten unter Berufung auf verschiedene Strukturcharakterisierungsmethoden � uberzeugend nahelegen. Jedoch ist über den Einfluss der Größe und Form der geschlossenen Poren sowie derer chemischer Eigenschaften auf die Natriumspeicherung nur wenig bekannt. Eben diese Fragestellung soll in der vorliegenden Arbeit behandelt werden. Durch die Herstellung von Materialien mit genau definierter und bekannter Morphologie, Porenstruktur sowie chemischer Beschaffenheit wird die Bedeutung dieser Merkmale für die Natriumabscheidung bei geringen Potentialen beleuchtet. Mittels elektrochemischer Impedanzspektroskopie wird desweiteren der Natriumspeichermechanismus detailliert untersucht und die Kinetik der reversiblen Natriumspeicherung mit der der irreversiblen Metallabscheidung verglichen, wobei eine bemerkenswerte Ähnlichkeit der beiden Prozesse zu beobachten ist. Abschließend ist die gezielte Herstellung geschlossenporiger Materialien aus offenporigen Vorläufermaterialien gelungen, welche es nicht nur ermöglicht, geschlossen- und offenporige Materialien ansonsten gleicher Porenstruktur zu vergleichen und die Notwendigkeit geschlossener Poren nachzuweisen, sondern auch die Speicherkapazität und Effizienz der Elektrodenmaterialien zu erhöhen. Insgesamt tragen die im Rahmen der vorliegenden Dissertation gewonnenen Erkenntisse nicht nur zum tiefergehenden Verständnis des Natriumspeichermechanismus in HCs bei, sondern es werden auch synthetische und analytische Methoden vorgestellt, die der weiteren Forschung auf diesem Gebiet dienen werden. KW - sodium-ion batteries KW - energy storage KW - carbon KW - Natrium-Ionen-Akkumulator KW - Energiespeicher KW - Kohlenstoff Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-541894 ER -