TY - JOUR A1 - Tiseanu, Carmen A1 - Parvulescu, Vasile A1 - Parvulescu, Victoria A1 - Cotoi, Elena A1 - Gessner, Andre A1 - Kumke, Michael Uwe A1 - Simon, Simion A1 - Vasiliu, Florin T1 - Structural and photoluminescence characterization of mesoporous silicon-phosphates N2 - Two different types of mesoporous silicon-phosphate supports using different surfactants (a mixture of (CH3)(3)C13H27NBr with an organophosphorus coupling molecule (HO-PO(i-C3H7)(2)) and with a co-surfactant ((C2H5)(3)(C6H5)PCl), respectively) were synthesized. Trivalent europium (Eu) ions were immobilized via ion-exchange on these supports. The resulting materials were characterized using nitrogen adsorption isotherms at -196 degrees C, thermogravimetric analysis, SEM, TEM, FT-IR, PXRD, CP/MAS. (HSi)-H-1-Si-29 and P-31 NMR, DR-UV-vis as well as steady- state and time-resolved photoluminescence spectroscopy. The results evidenced that the co-polymerization of silicon and phosphorous yielded a unique morphology in these materials. Following calcination at 450 and 900 degrees C europium- exchanged silicon-phosphates with great surface area (BET=600-705 m(2) g(-1)) and 3.4 nm sized mesopores were obtained. The differences among the optical properties of the non-calcined europium materials such as the emission lifetimes, local environment at the europium sites or the relative contribution of the upper excited levels to the total photoluminescence were assigned to the surfactants used in the synthesis. Calcination of the silicon-phosphates at higher temperatures than 450 degrees C did not induce major changes in the structural properties: in contrast, photoluminescence properties of europium were markedly improved in terms of intensity and average lifetime. Y1 - 2010 UR - http://www.sciencedirect.com/science/journal/10106030 U6 - https://doi.org/10.1016/j.jphotochem.2010.07.015 SN - 1010-6030 ER - TY - JOUR A1 - Tiseanu, Carmen A1 - Geßner, Andre A1 - Kumke, Michael Uwe A1 - Gagea, Bogdan A1 - Parvulescu, Vasile Ion A1 - Martens, Johan T1 - Photoluminescence spectra and dynamics of lanthanide-doped microporous materials N2 - A series of terbium- and europium-exchanged microporous-mesoporous zeolite Socony Mobil Five (MFI)-type materials such as Zeotile-1 and Zeogrid with varying Si/Al ratios was investigated using FTIR, PXRD, adsorption- desorption isotherms of N-2 at 77 K and time-resolved luminescence spectroscopy. Silylation of the lanthanides-exchanged Zeotile-1 and Zeogrid with hexadecyl trimethoxysilanes via post-synthesis grafting was also studied. The results showed that the lanthanide's photoluminescence spectra and decays were modified due to silylation. The different silylation effects in Zeotile-1 and Zeogrid were correlated with the textural properties of the investigated materials. (C) 2007 Elsevier B.V. All rights reserved. Y1 - 2008 UR - http://www.sciencedirect.com/science/article/pii/S0022231307003262 U6 - https://doi.org/10.1016/j.jlumin.2007.10.018 ER - TY - JOUR A1 - Tiseanu, Carmen A1 - Parvulescu, Vasile Ion A1 - Cojocaru, Bogdan A1 - Lorenz-Fonfria, Victor A. A1 - Kumke, Michael Uwe A1 - Gessner, Andre A1 - Enculescu, Ion T1 - Polymer-microporous host interactions probed by photoluminescence spectroscopy N2 - Zeolites NaY and ZSM-5 were used as hosts for styrene polymerization after ion-exchange with europium ions. The parent and hybrid, polystyrene coated Eu-NaY (Eu-NaY/PS) and Eu-ZSM-5 (Eu-ZSM-5/PS) zeolites were investigated by using thermal analysis, SEM, PXRD, FT-IR, DR-UV/Vis, steady state and time-resolved photoluminescence spectroscopy. FT-IR spectra evidenced for the interaction between the zeolitic hosts and polystyrene while the PXRD spectra supported for the presence of the polymer inside the channels/pores of Eu-NaY/PS and Eu-ZSM-5/PS materials. The optical properties of Eu-NaY/PS and Eu-ZSM-5/PS were significantly changed relative to those of the parent zeolites, giving further evidence for the presence of polymer inside zeolites. An interesting case is presented by NaY zeolite: following styrene polymerization, the polymer interacted selectively with one of the two main species co-existing inside zeolite while for ZSM-5 a similar effect was not observed. Y1 - 2010 UR - http://www.rsc.org/Publishing/Journals/CP/index.asp U6 - https://doi.org/10.1039/B922591a SN - 1463-9076 ER - TY - JOUR A1 - Tiseanu, Carmen A1 - Kumke, Michael Uwe A1 - Pârvulescu, Vasile Ion A1 - Martens, Johan T1 - Species-related luminescence-structure relationships in europium-exchanged mesoporous material N2 - Europium exchanged into a mesoporous material (Zeotile-1) was extensively characterized with respect to the Si/ Al ratio and surface silylation by using time-resolved emission spectroscopy. Qualitative as well as quantitative details of the europium species-related luminescence-structure relationships were obtained and discussed such as the decay associated spectra, local distortion and structure of the bonding environment, crystal-field strength, radiative relaxation rates, and the quantum efficiency. Thus, two europium species were found in the parent as well as in the silylated materials: one species located on the internal surface and the second inside the 2-2.5 nm pores. The species located on the internal surface is characterized by photoluminescence decay times of 105 mu s