TY  - JOUR
A1  - Zhong, Qi
A1  - Adelsberger, Joseph
A1  - Niedermeier, M. A.
A1  - Golosova, Anastasi
A1  - Bivigou Koumba, Achille Mayelle
A1  - Laschewsky, André
A1  - Funari, S. S.
A1  - Papadakis, Christine M.
A1  - Müller-Buschbaum, Peter
T1  - The influence of selective solvents on the transition behavior of poly(styrene-b-monomethoxydiethylenglycol-acrylate-b-styrene) thick films
JF  - Colloid and polymer science : official journal of the Kolloid-Gesellschaft
N2  - Thick poly(styrene-b-monomethoxydiethylenglycol-acrylate-b-styrene) [P(S-b-MDEGA-b-S)] films (thickness 5 mu m) are prepared from different solvents on flexible substrates by solution casting and investigated with small-angle X-ray scattering. As the solvents are either PS- or PMDEGA-selective, micelles with different core-shell micellar structures are formed. In PMDEGA-selective solvents, the PS block is the core and PMDEGA is the shell, whereas in PS-selective solvents, the order is reversed. After exposing the films to liquid D2O, the micellar structure inside the films prepared from PMDEGA-selective solvents remains unchanged and only the PMDEGA (shell part) swells. On the contrary, in the films prepared from PS-selective solvents, the micelles revert the core and the shell. This reversal causes more entanglements of the PMDEGA chains between the micelles. Moreover, the thermal collapse transition of the PMDEGA block in liquid D2O is significantly broadened. Irrespective of the solvent used for film preparation, the swollen PMDEGA shell does not show a prominent shrinkage when passing the phase transition, and the transition process occurs via compaction. The collapsed micelles have a tendency to densely pack above the transition temperature.
KW  - Hydrogel
KW  - Thin film
KW  - Thermo-responsive
KW  - LCST behavior
KW  - SAXS
Y1  - 2013
U6  - https://doi.org/10.1007/s00396-012-2879-4
SN  - 0303-402X
VL  - 291
IS  - 6
SP  - 1439
EP  - 1451
PB  - Springer
CY  - New York
ER  -