TY - JOUR A1 - Jiang, Wei A1 - Tao, Chen A1 - Stolterfoht, Martin A1 - Jin, Hui A1 - Stephen, Meera A1 - Lin, Qianqian A1 - Nagiri, Ravi C. R. A1 - Burn, Paul L. A1 - Gentle, Ian R. T1 - Hole-transporting materials for low donor content organic solar cells BT - charge transport and device performance JF - Organic electronics : physics, materials and applications N2 - Low donor content solar cells are an intriguing class of photovoltaic device about which there is still considerable discussion with respect to their mode of operation. We have synthesized a series of triphenylamine-based materials for use in low donor content devices with the electron accepting [6,6]-phenyl-C71-butyric acid methyl ester (PC(7)0BM). The triphenylamine-based materials absorb light in the near UV enabling the PC(7)0BM to be be the main light absorbing organic semiconducting material in the solar cell. It was found that the devices did not operate as classical Schottky junctions but rather photocurrent was generated by hole transfer from the photo-excited PC(7)0BM to the triphenylamine-based donors. We found that replacing the methoxy surface groups with methyl groups on the donor material led to a decrease in hole mobility for the neat films, which was due to the methyl substituted materials having the propensity to aggregate. The thermodynamic drive to aggregate was advantageous for the performance of the low donor content (6 wt%) films. It was found that the 6 wt% donor devices generally gave higher performance than devices containing 50 wt% of the donor. KW - photoexcited hole transfer KW - photocurrent generation KW - synthesis KW - hole KW - mobility KW - low donor content KW - Schottky junction Y1 - 2020 U6 - https://doi.org/10.1016/j.orgel.2019.105480 SN - 1566-1199 SN - 1878-5530 VL - 76 PB - Elsevier CY - Amsterdam ER - TY - JOUR A1 - Turner, Sarah T. A1 - Pingel, Patrick A1 - Steyrleuthner, Robert A1 - Crossland, Edward J. W. A1 - Ludwigs, Sabine A1 - Neher, Dieter T1 - Quantitative analysis of bulk heterojunction films using linear absorption spectroscopy and solar cell performance JF - Advanced functional materials N2 - A fundamental understanding of the relationship between the bulk morphology and device performance is required for the further development of bulk heterojunction organic solar cells. Here, non-optimized (chloroform cast) and nearly optimized (solvent-annealed o-dichlorobenzene cast) P3HT:PCBM blend films treated over a range of annealing temperatures are studied via optical and photovoltaic device measurements. Parameters related to the P3HT aggregate morphology in the blend are obtained through a recently established analytical model developed by F. C. Spano for the absorption of weakly interacting H-aggregates. Thermally induced changes are related to the glass transition range of the blend. In the chloroform prepared devices, the improvement in device efficiency upon annealing within the glass transition range can be attributed to the growth of P3HT aggregates, an overall increase in the percentage of chain crystallinity, and a concurrent increase in the hole mobilities. Films treated above the glass transition range show an increase in efficiency and fill factor not only associated with the change in chain crystallinity, but also with a decrease in the energetic disorder. On the other hand, the properties of the P3HT phase in the solvent-annealed o-dichlorobenzene cast blends are almost indistinguishable from those of the corresponding pristine P3HT layer and are only weakly affected by thermal annealing. Apparently, slow drying of the blend allows the P3HT chains to crystallize into large domains with low degrees of intra- and interchain disorder. This morphology appears to be most favorable for the efficient generation and extraction of charges. KW - Organic electronics KW - morphology KW - solar cells KW - mobility KW - absorption spectroscopy Y1 - 2011 U6 - https://doi.org/10.1002/adfm.201101583 SN - 1616-301X VL - 21 IS - 24 SP - 4640 EP - 4652 PB - Wiley-VCH CY - Weinheim ER -