TY - JOUR A1 - Behl, Marc A1 - Balk, Maria A1 - Lützow, Karola A1 - Lendlein, Andreas T1 - Impact of block sequence on the phase morphology of multiblock copolymers obtained by high-throughput robotic synthesis JF - European polymer journal : EPJ N2 - The chemical nature, the number length of integrated building blocks, as well as their sequence structure impact the phase morphology of multiblock copolymers (MBC) consisting of two non-miscible block types. We hypothesized that a strictly alternating sequence should favour phase segregation and in this way the elastic properties. A library of well-defined MBCs composed of two different hydrophobic, semi-crystalline blocks providing domains with well-separated melting temperatures (T(m)s) were synthesized from the same type of precursor building blocks as strictly alternating (MBCsalt) or random (MBCsran) MBCs and compared. Three different series of MBCsalt or MBCsran were synthesized by high-throughput synthesis by coupling oligo(e-caprolactone) (OCL) of different molecular weights (2, 4, and 8 kDa) with oligotetrahydrofuran (OTHF, 2.9 kDa) via Steglich esterification in which the molar ratio of the reaction partners was slightly adjusted. Maximum of weight average molecular weight (M-w) were 65,000 g center dot mol(-1), 165,000 g center dot mol(-1), and 168,000 g center dot mol(-1) for MBCsalt and 80,500 g center dot mol(-1), 100,000 g center dot mol(-1), and 147,600 g center dot mol(-1) for MBCsran. When Mw increased, a decrease of both Tms associated to the melting of the OCL and OTHF domains was observed for all MBCs. T-m (OTHF) of MBCsran was always higher than Tm (OTHF) of MBCsalt, which was attributed to a better phase segregation. In addition, the elongation at break of MBCsalt was almost half as high when compared to MBCsran. In this way this study elucidates role of the block length and sequence structure in MBCs and enables a quantitative discussion of the structure-function relationship when two semi-crystalline block segments are utilized for the design of block copolymers. KW - Multiblock copolymers KW - Sequence structure KW - Phase morphology KW - Polymer KW - library KW - Robotic synthesis KW - High-throughput Y1 - 2021 U6 - https://doi.org/10.1016/j.eurpolymj.2020.110207 SN - 0014-3057 SN - 1873-1945 VL - 143 PB - Elsevier CY - Oxford ER - TY - JOUR A1 - Fang, Liang A1 - Yan, Wan A1 - Nöchel, Ulrich A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Programming structural functions in phase-segregated polymers by implementing a defined thermomechanical history JF - Polymer : the international journal for the science and technology of polymers N2 - Unwanted shrinkage behaviors or failure in structural functions such as mechanical strength or deformability of polymeric products related to their thermomechanical history are a major challenge in production of plastics. Here, we address the question whether we can turn this challenge into an opportunity by creating defined thermomechanical histories in polymers, represented by a specific morphology and nanostructure, to equip polymeric shaped bodies with desired functions, e.g. a temperature-memory, by hot, warm or cold deformation into multiblock copolymers having two partially overlapping melting transitions. A copolyesterurethane named PDLCL, consisting of poly(epsilon-caprolactone) (PCL) and poly(omega-pentadecalactone) (PPDL) crystalline domains, exhibiting a pronounced phase-segregated morphology and partially overlapping melting transitions was selected for this study. Different types of PCL and PPDL crystals as well as distinct degrees of orientation in both amorphous and crystalline domains were obtained after deformation at 20 or 40 degrees C and to a lower extent at 60 degrees C. The generated non-isotropic structures were stable at ambient temperature and represent the different stresses stored. Stress-free heating experiments showed that the relaxation in both amorphous and crystalline phases occurred predominantly with melting of PCL crystals. When the switching temperature, which was similar to the applied deformation temperature (temperature-memory), was exceeded in stress-free heating experiments, the implemented thermomechanical history could be reversed. In contrast, during constant-strain heating to 60 degrees C the generated structural features remained almost unchanged. These findings provide insights about the structure function relation in multiblock copolymers with two crystalline phases exhibiting a temperature-memory effect by implementation of specific thermomechanical histories, which might be a general principle for tailoring other functions like mechanical strength or deformability in polymers. (C) 2016 Elsevier Ltd. All rights reserved. KW - Temperature-memory effect KW - Phase morphology KW - Thermomechanical history Y1 - 2016 U6 - https://doi.org/10.1016/j.polymer.2016.08.105 SN - 0032-3861 SN - 1873-2291 VL - 102 SP - 54 EP - 62 PB - Elsevier CY - Oxford ER -