TY - JOUR A1 - Koc, Julian A1 - Simovich, Tomer A1 - Schönemann, Eric A1 - Chilkoti, Ashutosh A1 - Gardner, Harrison A1 - Swain, Geoffrey W. A1 - Hunsucker, Kelli A1 - Laschewsky, André A1 - Rosenhahn, Axel T1 - Sediment challenge to promising ultra-low fouling hydrophilic surfaces in the marine environment JF - Biofouling : the journal of bioadhesion and biofilm research N2 - Hydrophilic coatings exhibit ultra-low fouling properties in numerous laboratory experiments. In stark contrast, the antifouling effect of such coatings in vitro failed when performing field tests in the marine environment. The fouling release performance of nonionic and zwitterionic hydrophilic polymers was substantially reduced compared to the controlled laboratory environment. Microscopy and spectroscopy revealed that a large proportion of the accumulated material in field tests contains inorganic compounds and diatomaceous soil. Diatoms adhered to the accumulated material on the coating, but not to the pristine polymer. Simulating field tests in the laboratory using sediment samples collected from the test sites showed that incorporated sand and diatomaceous earth impairs the fouling release characteristics of the coatings. When exposed to marine sediment from multiple locations, particulate matter accumulated on these coatings and served as attachment points for diatom adhesion and enhanced fouling. Future developments of hydrophilic coatings should consider accumulated sediment and its potential impact on the antifouling performance. KW - hydrogel KW - field test KW - fouling release KW - marine biofouling KW - sediment Y1 - 2019 U6 - https://doi.org/10.1080/08927014.2019.1611790 SN - 0892-7014 SN - 1029-2454 VL - 35 IS - 4 SP - 454 EP - 462 PB - Taylor & Francis CY - London ER - TY - GEN A1 - Schönemann, Eric A1 - Koc, Julian A1 - Aldred, Nick A1 - Clare, Anthony S. A1 - Laschewsky, André A1 - Rosenhahn, Axel A1 - Wischerhoff, Erik T1 - Synthesis of novel sulfobetaine polymers with differing dipole orientations in their side chains, and their effects on the antifouling properties T2 - Postprints der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe N2 - The impact of the orientation of zwitterionic groups, with respect to the polymer backbone, on the antifouling performance of thin hydrogel films made of polyzwitterions is explored. In an extension of the recent discussion about differences in the behavior of polymeric phosphatidylcholines and choline phosphates, a quasi-isomeric set of three poly(sulfobetaine methacrylate)s is designed for this purpose. The design is based on the established monomer 3-[N-2-(methacryloyloxy)ethyl-N,N-dimethyl]ammonio-propane-1-sulfonate and two novel sulfobetaine methacrylates, in which the positions of the cationic and the ionic groups relative to the polymerizable group, and thus also to the polymer backbone, are altered. The effect of the varied segmental dipole orientation on their water solubility, wetting behavior by water, and fouling resistance is compared. As model systems, the adsorption of the model proteins bovine serum albumin (BSA), fibrinogen, and lysozyme onto films of the various polyzwitterion surfaces is studied, as well as the settlement of a diatom (Navicula perminuta) and barnacle cyprids (Balanus improvisus) as representatives of typical marine fouling communities. The results demonstrate the important role of the zwitterionic group's orientation on the polymer behavior and fouling resistance T3 - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe - 1184 KW - antifouling KW - coatings KW - crosslinking KW - hydrophilic polymers KW - polyzwitterions Y1 - 2019 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-524820 SN - 1866-8372 IS - 1 ER - TY - JOUR A1 - Koc, Julian A1 - Schönemann, Eric A1 - Arnuthalingam, Ajitha A1 - Clarke, Jessica L. A1 - Finlay, John A. A1 - Clare, Anthony S. A1 - Laschewsky, Andre A1 - Rosenhahn, Axel T1 - Low-fouling thin hydrogel coatings made of photo-cross-linked polyzwitterions JF - Langmuir N2 - Although zwitterionic chemistries are among the most promising materials for producing nonfouling surfaces, their structural diversity has been low until now. Here, we compare the in vitro fouling behavior of a set of four systematically varied sulfa-/sulfobetaine-containing zwitterionic hydrogel coatings against a series of proteins and nonmotile as well as motile marine organisms as model foulers. The coatings are prepared by simultaneous photoinduced cross-linking and surface anchoring to elucidate the effect of the molecular structure of the zwitterionic moieties on their antifouling activity. Analogously prepared coatings of poly(butyl methacrylate) and poly(oligoethylene glycol methacrylate) serve as references. Photoreactive polymers are synthesized by the statistical copolymerization of sulfobetaine or sulfabetaine methacrylates and methacrylamides with a benzophenone derivative of 2-hydroxyethyl methacrylate and are applied as a thin film coating. While keeping the density of the zwitterionic and cross-linker groups constant, the molecular structure of the zwitterionic side chains is varied systematically, as is the arrangement of the ion pairs in the side chain by changing the classical linear geometry to a novel Y-shaped geometry. All of the polyzwitterions strongly reduce fouling compared to poly(butyl methacrylate). Overall, the sulfabetaine polyzwitterion coatings studied matches the high antifouling effectiveness of oligo(ethylene glycol)-based ones used as a control. Nevertheless, performances varied individually for a given pair of polymer and fouler. The case of the polysulfobetaines exemplifies that minor chemical changes in the polymer structure affect the antifouling performance markedly. Accordingly, the antifouling performance of such polymers cannot be correlated simply to the type of zwitterion used (which could be generally ranked as better performing or poorer performing) but is a result of the polymer’s precise chemical structure. Our findings underline the need to enlarge the existing structural diversity of polyzwitterions for antifouling purposes to optimize the potential of their chemical structure. Y1 - 2019 U6 - https://doi.org/10.1021/acs.langmuir.8b02799 SN - 0743-7463 VL - 35 IS - 5 SP - 1552 EP - 1562 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Schönemann, Eric A1 - Koc, Julian A1 - Aldred, Nick A1 - Clare, Anthony S. A1 - Laschewsky, André A1 - Rosenhahn, Axel A1 - Wischerhoff, Erik T1 - Synthesis of Novel Sulfobetaine Polymers with Differing Dipole Orientations in Their Side Chains, and Their Effects on the Antifouling Properties JF - Macromolecular rapid communications N2 - The impact of the orientation of zwitterionic groups, with respect to the polymer backbone, on the antifouling performance of thin hydrogel films made of polyzwitterions is explored. In an extension of the recent discussion about differences in the behavior of polymeric phosphatidylcholines and choline phosphates, a quasi-isomeric set of three poly(sulfobetaine methacrylate)s is designed for this purpose. The design is based on the established monomer 3-[N-2-(methacryloyloxy)ethyl-N,N-dimethyl]ammonio-propane-1-sulfonate and two novel sulfobetaine methacrylates, in which the positions of the cationic and the ionic groups relative to the polymerizable group, and thus also to the polymer backbone, are altered. The effect of the varied segmental dipole orientation on their water solubility, wetting behavior by water, and fouling resistance is compared. As model systems, the adsorption of the model proteins bovine serum albumin (BSA), fibrinogen, and lysozyme onto films of the various polyzwitterion surfaces is studied, as well as the settlement of a diatom (Navicula perminuta) and barnacle cyprids (Balanus improvisus) as representatives of typical marine fouling communities. The results demonstrate the important role of the zwitterionic group's orientation on the polymer behavior and fouling resistance. KW - antifouling KW - coatings KW - crosslinking KW - hydrophilic polymers KW - polyzwitterions Y1 - 2019 U6 - https://doi.org/10.1002/marc.201900447 SN - 1022-1336 SN - 1521-3927 VL - 41 IS - 1 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Koc, Julian A1 - Schardt, Lisa A1 - Nolte, Kim A1 - Beyer, Cindy A1 - Eckhard, Till A1 - Schwiderowski, Philipp A1 - Clarke, Jessica L. A1 - Finlay, John A. A1 - Clare, Anthony S. A1 - Muhler, Martin A1 - Laschewsky, André A1 - Rosenhahn, Axel T1 - Effect of dipole orientation in mixed, charge-equilibrated self-assembled monolayers on protein adsorption and marine biofouling JF - ACS applied materials & interfaces N2 - While zwitterionic interfaces are known for their excellent low-fouling properties, the underlying molecular principles are still under debate. In particular, the role of the zwitterion orientation at the interface has been discussed recently. For elucidation of the effect of this parameter, self-assembled monolayers (SAMs) on gold were prepared from stoichiometric mixtures of oppositely charged alkyl thiols bearing either a quaternary ammonium or a carboxylate moiety. The alkyl chain length of the cationic component (11-mercaptoundecyl)-N,N,N-trimethylammonium, which controls the distance of the positively charged end group from the substrate's surface, was kept constant. In contrast, the anionic component and, correspondingly, the distance of the negatively charged carboxylate groups from the surface was varied by changing the alkyl chain length in the thiol molecules from 7 (8-mercaptooctanoic acid) to 11 (12-mercaptododecanoic acid) to 15 (16-mercaptohexadecanoic acid). In this way, the charge neutrality of the coating was maintained, but the charged groups exposed at the interface to water were varied, and thus, the orientation of the dipoles in the SAMs was altered. In model biofouling studies, protein adsorption, diatom accumulation, and the settlement of zoospores were all affected by the altered charge distribution. This demonstrates the importance of the dipole orientation in mixed-charged SAMs for their inertness to nonspecific protein adsorption and the accumulation of marine organisms. Overall, biofouling was lowest when both the anionic and the cationic groups were placed at the same distance from the substrate's surface. KW - SAM KW - antifouling coatings KW - zwitterionic KW - XPS KW - Navicula perminuta KW - Ulva linza KW - SPR Y1 - 2020 U6 - https://doi.org/10.1021/acsami.0c11580 SN - 1944-8244 SN - 1944-8252 VL - 12 IS - 45 SP - 50953 EP - 50961 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Schönemann, Eric A1 - Koc, Julian A1 - Karthäuser, Jana A1 - Özcan, Onur A1 - Schanzenbach, Dirk A1 - Schardt, Lisa A1 - Rosenhahn, Axel A1 - Laschewsky, André T1 - Sulfobetaine methacrylate polymers of unconventional polyzwitterion architecture and their antifouling properties JF - Biomacromolecules : an interdisciplinary journal focused at the interface of polymer science and the biological sciences N2 - Combining high hydrophilicity with charge neutrality, polyzwitterions are intensely explored for their high biocompatibility and low-fouling properties. Recent reports indicated that in addition to charge neutrality, the zwitterion's segmental dipole orientation is an important factor for interacting with the environment. Accordingly, a series of polysulfobetaines with a novel architecture was designed, in which the cationic and anionic groups of the zwitterionic moiety are placed at equal distances from the backbone. They were investigated by in vitro biofouling assays, covering proteins of different charges and model marine organisms. All polyzwitterion coatings reduced the fouling effectively compared to model polymer surfaces of poly(butyl methacrylate), with a nearly equally good performance as the reference polybetaine poly(3-(N-(2-(methacryloyloxy)ethyl)-N,N-dimethylammonio)propanesulfonate). The specific fouling resistance depended on the detailed chemical structure of the polyzwitterions. Still, while clearly affecting the performance, the precise dipole orientation of the sulfobetaine group in the polyzwitterions seems overall to be only of secondary importance for their antifouling behavior. Y1 - 2021 U6 - https://doi.org/10.1021/acs.biomac.0c01705 SN - 1525-7797 SN - 1526-4602 VL - 22 IS - 4 SP - 1494 EP - 1508 PB - American Chemical Society CY - Washington ER -