@phdthesis{Tronci2010,
  author    = {Tronci, Giuseppe},
  title     = {Synthesis, characterization, and biological evaluation of gelatin-based scaffolds},
  url       = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus-49727},
  school      = {Universit{\"a}t Potsdam},
  year      = {2010},
  abstract  = {This work presents the development of entropy-elastic gelatin based networks in the form of films or scaffolds. The materials have good prospects for biomedical applications, especially in the context of bone regeneration. Entropy-elastic gelatin based hydrogel films with varying crosslinking densities were prepared with tailored mechanical properties. Gelatin was covalently crosslinked above its sol gel transition, which suppressed the gelatin chain helicity. Hexamethylene diisocyanate (HDI) or ethyl ester lysine diisocyanate (LDI) were applied as chemical crosslinkers, and the reaction was conducted either in dimethyl sulfoxide (DMSO) or water. Amorphous films were prepared as measured by Wide Angle X-ray Scattering (WAXS), with tailorable degrees of swelling (Q: 300-800 vol. \%) and wet state Young's modulus (E: 70 740 kPa). Model reactions showed that the crosslinking reaction resulted in a combination of direct crosslinks (3-13 mol.-\%), grafting (5-40 mol.-\%), and blending of oligoureas (16-67 mol.-\%). The knowledge gained with this bulk material was transferred to the integrated process of foaming and crosslinking to obtain porous 3-D gelatin-based scaffolds. For this purpose, a gelatin solution was foamed in the presence of a surfactant, Saponin, and the resulting foam was fixed by chemical crosslinking with a diisocyanate. The amorphous crosslinked scaffolds were synthesized with varied gelatin and HDI concentrations, and analyzed in the dry state by micro computed tomography (µCT, porosity: 65±11-73±14 vol.-\%), and scanning electron microscopy (SEM, pore size: 117±28-166±32 µm). Subsequently, the work focused on the characterization of the gelatin scaffolds in conditions relevant to biomedical applications. Scaffolds showed high water uptake (H: 630-1680 wt.-\%) with minimal changes in outer dimension. Since a decreased scaffold pore size (115±47-130±49 µm) was revealed using confocal laser scanning microscopy (CLSM) upon wetting, the form stability could be explained. Shape recoverability was observed after removal of stress when compressing wet scaffolds, while dry scaffolds maintained the compressed shape. This was explained by a reduction of the glass transition temperature upon equilibration with water (dynamic mechanical analysis at varied temperature (DMTA)). The composition dependent compression moduli (Ec: 10 50 kPa) were comparable to the bulk micromechanical Young's moduli, which were measured by atomic force microscopy (AFM). The hydrolytic degradation profile could be adjusted, and a controlled decrease of mechanical properties was observed. Partially-degraded scaffolds displayed an increase of pore size. This was likely due to the pore wall disintegration during degradation, which caused the pores to merge. The scaffold cytotoxicity and immunologic responses were analyzed. The porous scaffolds enabled proliferation of human dermal fibroblasts within the implants (up to 90 µm depth). Furthermore, indirect eluate tests were carried out with L929 cells to quantify the material cytotoxic response. Here, the effect of the sterilization method (Ethylene oxide sterilization), crosslinker, and surfactant were analyzed. Fully cytocompatible scaffolds were obtained by using LDI as crosslinker and PEO40 PPO20-PEO40 as surfactant. These investigations were accompanied by a study of the endotoxin material contamination. The formation of medical-grade materials was successfully obtained (<0.5 EU/mL) by using low-endotoxin gelatin and performing all synthetic steps in a laminar flow hood.},
  language  = {en}
}
@phdthesis{Leiendecker2016,
  author    = {Leiendecker, Mai-Thi},
  title     = {Physikalische Hydrogele auf Polyurethan-Basis},
  url       = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-103917},
  school      = {Universit{\"a}t Potsdam},
  pages     = {109},
  year      = {2016},
  abstract  = {Physical hydrogels have gained recent attention as cell substrates, since viscoelasticity or stress relaxation is a powerful parameter in mechanotransduction, which has long been neglected. We designed multi-functional polyurethanes to form physical hydrogels via a unique tunable gelation mechanism. The anionic polyurethanes spontaneously form aggregates in water that are kept in a soluble state through electrostatic repulsion. Fast subsequent gelation can be triggered by charge shielding which allows the aggregation and network building to proceed. This can be induced by adding either acids or salts, resulting in acidic (pH 4-5) or pH-neutral hydrogels, respectively. Whereas conventional polyurethane-based hydrogels are commonly prepared from toxic isocyanate precursors, the physical hydrogelation mechanism described here does not involve chemically reactive species which is ideal for in situ applications in sensitive environments. Both stiffness and stress relaxation can be tuned independently over a broad range and the gels exhibit excellent stress recovery behavior.},
  language  = {de}
}
@phdthesis{Folikumah2022,
  author    = {Folikumah, Makafui Yao},
  title     = {Stimuli-promoted in situ formation of hydrogels with thiol/thioester containing peptide precursors},
  doi       = {10.25932/publishup-56971},
  url       = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-569713},
  school      = {Universit{\"a}t Potsdam},
  pages     = {159},
  year      = {2022},
  abstract  = {Hydrogels are potential synthetic ECM-like substitutes since they provide functional and structural similarities compared to soft tissues. They can be prepared by crosslinking of macromolecules or by polymerizing suitable precursors. The crosslinks are not necessarily covalent bonds, but could also be formed by physical interactions such as π-π interactions, hydrophobic interactions, or H-bonding. On demand in situ forming hydrogels have garnered increased interest especially for biomedical applications over preformed gels due to the relative ease of in vivo delivery and filling of cavities. The thiol-Michael addition reaction provides a straightforward and robust strategy for in situ gel formation with its fast reaction kinetics and ability to proceed under physiological conditions. The incorporation of a trigger function into a crosslinking system becomes even more interesting since gelling can be controlled with stimulus of choice. The use of small molar mass crosslinker precursors with active groups orthogonal to thiol-Michael reaction type electrophile provides the opportunity to implement an on-demand in situ crosslinking without compromising the fast reaction kinetics. It was postulated that short peptide sequences due to the broad range structural-function relations available with the different constituent amino acids, can be exploited for the realisation of stimuli-promoted in situ covalent crosslinking and gelation applications. The advantages of this system over conventional polymer-polymer hydrogel systems are the ability tune and predict material property at the molecular level. The main aim of this work was to develop a simplified and biologically-friendly stimuli-promoted in situ crosslinking and hydrogelation system using peptide mimetics as latent crosslinkers. The approach aims at using a single thiodepsipeptide sequence to achieve separate pH- and enzyme-promoted gelation systems with little modification to the thiodepsipeptide sequence. The realization of this aim required the completion of three milestones. In the first place, after deciding on the thiol-Michael reaction as an effective in situ crosslinking strategy, a thiodepsipeptide, Ac-Pro-Leu-Gly-SLeu-Leu-Gly-NEtSH (TDP) with expected propensity towards pH-dependent thiol-thioester exchange (TTE) activation, was proposed as a suitable crosslinker precursor for pH-promoted gelation system. Prior to the synthesis of the proposed peptide-mimetic, knowledge of the thiol-Michael reactivity of the would-be activated thiol moiety SH-Leu, which is internally embedded in the thiodepsipeptide was required. In line with pKa requirements for a successful TTE, the reactivity of a more acidic thiol, SH-Phe was also investigated to aid the selection of the best thiol to be incorporated in the thioester bearing peptide based crosslinker precursor. Using 'pseudo' 2D-NMR investigations, it was found that only reactions involving SH-Leu yielded the expected thiol-Michael product, an observation that was attributed to the steric hindrance of the bulkier nature of SH-Phe. The fast reaction rates and complete acrylate/maleimide conversion obtained with SH-Leu at pH 7.2 and higher aided the direct elimination of SH-Phe as a potential thiol for the synthesis of the peptide mimetic. Based on the initial studies, for the pH-promoted gelation system, the proposed Ac-Pro-Leu-Gly-SLeu-Leu-Gly-NEtSH was kept unmodified. The subtle difference in pKa values between SH-Leu (thioester thiol) and the terminal cysteamine thiol from theoretical conditions should be enough to effect a 'pseudo' intramolecular TTE. In polar protic solvents and under basic aqueous conditions, TDP successfully undergoes a 'pseudo' intramolecular TTE reaction to yield an α,ω-dithiol tripeptide, HSLeu-Leu-Gly-NEtSH. The pH dependence of thiolate ion generation by the cysteamine thiol aided the incorporation of the needed stimulus (pH) for the overall success of TTE (activation step) - thiol-Michael addition (crosslinking) strategy. Secondly, with potential biomedical applications in focus, the susceptibility of TDP, like other thioesters, to intermolecular TTE reaction was probed with a group of thiols of varying thiol pKa values, since biological milieu characteristically contain peptide/protein thiols. L-cysteine, which is a biologically relevant thiol, and a small molecular weight thiol, methylthioglycolate both with relatively similar thiol pKa, values, led to an increase concentration of the dithiol crosslinker when reacted with TDP. In the presence of acidic thiols (p-NTP and 4MBA), a decrease in the dithiol concentration was observed, an observation that can be attributed to the inability of the TTE tetrahedral intermediate to dissociate into exchange products and is in line with pKa requirements for successful TTE reaction. These results additionally makes TDP more attractive and the potentially the first crosslinker precursor for applications in biologically relevant media. Finally, the ability of TDP to promote pH-sensitive in situ gel formation was probed with maleimide functionalized 4-arm polyethylene glycol polymers in tris-buffered media of varying pHs. When a 1:1 thiol: maleimide molar ratio was used, TDP-PEG4MAL hydrogels formed within 3, 12 and 24 hours at pH values of 8.5, 8.0 and 7.5 respectively. However, gelation times of 3, 5 and 30 mins were observed for the same pH trend when the thiol: maleimide molar was increased to 2:1. A direct correlation of thiol content with G' of the gels at each pH could also be drawn by comparing gels with thiol: maleimide ratios of 1:1 to those with 2:1 thiol: maleimide mole ratios. This is supported by the fact that the storage modulus (G') is linearly dependent on the crosslinking density of the polymer. The values of initial G′ for all gels ranged between (200 - 5000 Pa), which falls in the range of elasticities of certain tissue microenvironments for example brain tissue 200 - 1000 Pa and adipose tissue (2500 - 3500 Pa). Knowledge so far gained from the study on the ability to design and tune the exchange reaction of thioester containing peptide mimetic will give those working in the field further insight into the development of new sequences tailored towards specific applications. TTE substrate design using peptide mimetic as presented in this work has revealed interesting new insights considering the state-of-the-art. Using the results obtained as reference, the strategy provides a possibility to extend the concept to the controlled delivery of active molecules needed for other robust and high yielding crosslinking reactions for biomedical applications. Application for this sequentially coupled functional system could be seen e.g. in the treatment of inflamed tissues associated with urinary tract like bladder infections for which pH levels above 7 were reported. By the inclusion of cell adhesion peptide motifs, the hydrogel network formed at this pH could act as a new support layer for the healing of damage epithelium as shown in interfacial gel formation experiments using TDP and PEG4MAL droplets. The versatility of the thiodepsipeptide sequence, Ac-Pro-Leu-Gly-SLeu-Leu-Gly-(TDPo) was extended for the design and synthesis of a MMP-sensitive 4-arm PEG-TDPo conjugate. The purported cleavage of TDPo at the Gly-SLeu bond yields active thiol units for subsequent reaction of orthogonal Michael acceptor moieties. One of the advantages of stimuli-promoted in situ crosslinking systems using short peptides should be the ease of design of required peptide molecules due to the predictability of peptide functions their sequence structure. Consequently the functionalisation of a 4-arm PEG core with the collagenase active TDPo sequence yielded an MMP-sensitive 4-arm thiodepsipeptide-PEG conjugate (PEG4TDPo) substrate. Cleavage studies using thiol flourometric assay in the presence of MMPs -2 and -9 confirmed the susceptibility of PEG4TDPo towards these enzymes. The resulting time-dependent increase in fluorescence intensity in the presence of thiol assay signifies the successful cleavage of TDPo at the Gly-SLeu bond as expected. It was observed that the cleavage studies with thiol flourometric assay introduces a sigmoid non-Michaelis-Menten type kinetic profile, hence making it difficult to accurately determine the enzyme cycling parameters, kcat and KM . Gelation studies with PEG4MAL at 10 \% wt. concentrations revealed faster gelation with MMP-2 than MMP-9 with 28 and 40 min gelation times respectively. Possible contributions by hydrolytic cleavage of PEG4TDPo has resulted in the gelation of PEG4MAL blank samples but only after 60 minutes of reaction. From theoretical considerations, the simultaneous gelation reaction would be expected to more negatively impact the enzymatic than hydrolytic cleavage. The exact contributions from hydrolytic cleavage of PEG4TDPo would however require additional studies. In summary this new and simplified in situ crosslinking system using peptide-based crosslinker precursors with tuneable properties exhibited in situ crosslinking gelation kinetics on similar levels with already active dithiols reported. The advantageous on-demand functionality associated with its pH-sensitivity and physiological compatibility makes it a strong candidate worth further research as biomedical applications in general and on-demand material synthesis is concerned. Results from MMP-promoted gelation system unveils a simple but unexplored approach for in situ synthesis of covalently crosslinked soft materials, that could lead to the development of an alternative pathway in addressing cancer metastasis by making use of MMP overexpression as a trigger. This goal has so far not being reach with MMP inhibitors despite the extensive work this regard.},
  language  = {en}
}
@phdthesis{MartinezGuajardo2024,
  author    = {Mart{\´i}nez Guajardo, Alejandro},
  title     = {New zwitterionic polymers for antifouling applications},
  doi       = {10.25932/publishup-62682},
  url       = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-626820},
  school      = {Universit{\"a}t Potsdam},
  pages     = {XIX, 145},
  year      = {2024},
  abstract  = {The remarkable antifouling properties of zwitterionic polymers in controlled environments are often counteracted by their delicate mechanical stability. In order to improve the mechanical stabilities of zwitterionic hydrogels, the effect of increased crosslinker densities was thus explored. In a first approach, terpolymers of zwitterionic monomer 3-[N -2(methacryloyloxy)ethyl-N,N-dimethyl]ammonio propane-1-sulfonate (SPE), hydrophobic monomer butyl methacrylate (BMA), and photo-crosslinker 2-(4-benzoylphenoxy)ethyl methacrylate (BPEMA) were synthesized. Thin hydrogel coatings of the copolymers were then produced and photo-crosslinked. Studies of the swollen hydrogel films showed that not only the mechanical stability but also, unexpectedly, the antifouling properties were improved by the presence of hydrophobic BMA units in the terpolymers. Based on the positive results shown by the amphiphilic terpolymers and in order to further test the impact that hydrophobicity has on both the antifouling properties of zwitterionic hydrogels and on their mechanical stability, a new amphiphilic zwitterionic methacrylic monomer, 3-((2-(methacryloyloxy)hexyl)dimethylammonio)propane-1-sulfonate (M1), was synthesized in good yields in a multistep synthesis. Homopolymers of M1 were obtained by free-radical polymerization. Similarly, terpolymers of M1, zwitterionic monomer SPE, and photo-crosslinker BPEMA were synthesized by free-radical copolymerization and thoroughly characterized, including its solubilities in selected solvents. Also, a new family of vinyl amide zwitterionic monomomers, namely 3-(dimethyl(2-(N -vinylacetamido)ethyl)ammonio)propane-1-sulfonate (M2), 4-(dimethyl(2-(N-vinylacetamido)ethyl)ammonio)butane-1-sulfonate (M3), and 3-(dimethyl(2-(N-vinylacetamido)ethyl)ammonio)propyl sulfate (M4), together with the new photo-crosslinker 4-benzoyl-N-vinylbenzamide (M5) that is well-suited for copolymerization with vinylamides, are introduced within the scope of the present work. The monomers are synthesized with good yields developing a multistep synthesis. Homopolymers of the new vinyl amide zwitterionic monomers are obtained by free-radical polymerization and thoroughly characterized. From the solubility tests, it is remarkable that the homopolymers produced are fully soluble in water, evidence of their high hydrophilicity. Copolymerization of the vinyl amide zwitterionic monomers, M2, M3, and M4 with the vinyl amide photo-crosslinker M5 proved to require very specific polymerization conditions. Nevertheless, copolymers were successfully obtained by free-radical copolymerization under appropriate conditions. Moreover, in an attempt to mitigate the intrinsic hydrophobicity introduced in the copolymers by the photo-crosslinkers, and based on the proven affinity of quaternized diallylamines to copolymerize with vinyl amides, a new quaternized diallylamine sulfobetaine photo-crosslinker 3-(diallyl(2-(4-benzoylphenoxy)ethyl)ammonio)propane-1-sulfonate (M6) is synthesized. However, despite a priori promising copolymerization suitability, copolymerization with the vinyl amide zwitterionic monomers could not be achieved.},
  language  = {en}
}