@phdthesis{Cheng2018,
  author    = {Cheng, Xiao},
  title     = {Controlled solvent vapor annealing of block copolymer films},
  doi       = {10.25932/publishup-42417},
  url       = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-424179},
  school      = {Universit{\"a}t Potsdam},
  pages     = {X, 166},
  year      = {2018},
  abstract  = {This project was focused on exploring the phase behavior of poly(styrene)187000-block-poly(2-vinylpyridine)203000 (SV390) with high molecular weight (390 kg/mol) in thin films, in which the self-assembly of block copolymers (BCPs) was realized via thermo-solvent annealing. The advanced processing technique of solvent vapor treatment provides controlled and stable conditions. In Chapter 3, the factors to influence the annealing process and the swelling behavior of homopolymers are presented and discussed. The swelling behavior of BCP in films is controlled by the temperature of the vapor and of the substrate, on one hand, and variation of the saturation of the solvent vapor atmosphere (different solvents), on the other hand. Additional factors like the geometry and material of the chamber, the type of flow inside the chamber etc. also influence the reproducibility and stability of the processing. The slightly selective solvent vapor of chloroform gives 10\% more swelling of P2VP than PS in films with thickness of ~40 nm. The tunable morphology in ultrathin films of high molecular weight BCP (SV390) was investigated in Chapter 4. First, the swelling behavior can be precisely tuned by temperature and/or vapor flow separately, which provided information for exploring the multiple-parameter-influenced segmental chain mobility of polymer films. The equilibrium state of SV390 in thin films influenced by temperature was realized at various temperatures with the same degree of swelling. Various methods including characterization with SFM, metallization and RIE were used to identify the morphology of films as porous half-layer with PS dots and P2VP matrix. The kinetic investigations demonstrate that on substrates with either weak or strong interaction the original morphology of the BCP with high molecular weight is changed very fast within 5 min, and the further annealing serves for annihilation of defects. The morphological development of symmetric BCP in films with thickness increasing from half-layer to one-layer influenced by confinement factors of gradient film thicknesses and various surface properties of substrates was studied in Chapter 5. SV390 and SV99 films show bulk lamella-forming morphology after slightly selective solvent vapor (chloroform) treatment. SV99 films show cylinder-forming morphology under strongly selective solvent vapor (toluene) treatment since the asymmetric structure (caused by toluene uptake in PS blocks only) of SV99 block copolymer during annealing. Both kinds of morphology (lamella and cylinder) are influenced by the film thickness. The annealed morphology of SV390 and SV99 influenced by the combination of confined film and substrate property is similar to the morphology on flat silicon wafers. In this chapter the gradients in the film thickness and surface properties of the substrates with regard to their influence on the morphological development in thin BCP films are presented. Directed self-assembly (graphoepitaxy) of this SV390 was also investigated to compare with systematically reported SV99. In Chapter 6 an approach to induced oriented microphase separation in thick block copolymer films via treatment with the oriented vapor flow using mini-extruder is envisaged to be an alternative to existing methodologies, e.g. via non-solvent-induced phase separation. The preliminary tests performed in this study confirm potential perspective of this method, which alters the structure through the bulk of the film (as revealed by SAXS measurements), but more detailed studies have to be conducted in order to optimize the preparation.},
  language  = {en}
}
@phdthesis{Nizardo2018,
  author    = {Nizardo, Noverra Mardhatillah},
  title     = {Thermoresponsive block copolymers with UCST-behavior aimed at biomedical environments},
  url       = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-412217},
  school      = {Universit{\"a}t Potsdam},
  pages     = {xiii, 134},
  year      = {2018},
  abstract  = {Thermoresponsive block copolymers of presumably highly biocompatible character exhibiting upper critical solution temperature (UCST) type phase behavior were developed. In particular, these polymers were designed to exhibit UCST-type cloud points (Tcp) in physiological saline solution (9 g/L) within the physiologically interesting window of 30-50°C. Further, their use as carrier for controlled release purposes was explored. Polyzwitterion-based block copolymers were synthesized by atom transfer radical polymerization (ATRP) via a macroinitiator approach with varied molar masses and co-monomer contents. These block copolymers can self-assemble in the amphiphilic state to form micelles, when the thermoresponsive block experiences a coil-to-globule transition upon cooling. Poly(ethylene glycol) methyl ether (mPEG) was used as the permanently hydrophilic block to stabilize the colloids formed, and polyzwitterions as the thermoresponsive block to promote the temperature-triggered assembly-disassembly of the micellear aggregates at low temperature. Three zwitterionic monomers were used for this studies, namely 3-((2-(methacryloyloxy)ethyl)dimethylammonio)propane-1-sulfonate (SPE), 4-((2-(methacryloyl- oxy)ethyl)dimethylammonio)butane-1-sulfonate (SBE), and 3-((2-(methacryloyloxy)ethyl)- dimethylammonio)propane-1-sulfate) (ZPE). Their (co)polymers were characterized with respect to their molecular structure by proton nuclear magnetic resonance (1H-NMR) and gel permeation chromatography (GPC). Their phase behaviors in pure water as well as in physiological saline were studied by turbidimetry and dynamic light scattering (DLS). These (co)polymers are thermoresponsive with UCST-type phase behavior in aqueous solution. Their phase transition temperatures depend strongly on the molar masses and the incorporation of co-monomers: phase transition temperatures increased with increasing molar masses and content of poorly water-soluble co-monomer. In addition, the presence of salt influenced the phase transition dramatically. The phase transition temperature decreased with increasing salt content in the solution. While the PSPE homopolymers show a phase transition only in pure water, the PZPE homopolymers are able to exhibit a phase transition only in high salinity, as in physiological saline. Although both polyzwitterions have similar chemical structures that differ only in the anionic group (sulfonate group in SPE and sulfate group in ZPE), the water solubility is very different. Therefore, the phase transition temperatures of targeted block copolymers were modulated by using statistical copolymer of SPE and ZPE as thermoresponsive block, and varying the ratio of SPE to ZPE. Indeed, the statistical copolymers of P(SPE-co-ZPE) show phase transitions both in pure water as well as in physiological saline. Surprisingly, it was found that mPEG-b-PSBE block copolymer can display "schizophrenic" behavior in pure water, with the UCST-type cloud point occurring at lower temperature than the LCST-type one. The block copolymer, which satisfied best the boundary conditions, is block copolymer mPEG114-b-P(SPE43-co-ZPE39) with a cloud point of 45°C in physiological saline. Therefore, it was chosen for solubilization studies of several solvatochromic dyes as models of active agents, using the thermoresponsive block copolymer as "smart" carrier. The uptake and release of the dyes were explored by UV-Vis and fluorescence spectroscopy, following the shift of the wavelength of the absorbance or emission maxima at low and high temperature. These are representative for the loaded and released state, respectively. However, no UCST-transition triggered uptake and release of these dyes could be observed. Possibly, the poor affinity of the polybetaines to the dyes in aqueous environtments may be related to the widely reported antifouling properties of zwitterionic polymers.},
  language  = {en}
}