Synthesis, assembly and thermo-responsivity of polymer-functionalized magnetic cobalt nanoparticles

Synthese, Assemblierung und Temperatur-Responsivität von Polymer-funktionalisierten magnetischen Cobalt Nanopartikeln

  • This thesis mainly covers the synthesis, surface modification, magnetic-field-induced assembly and thermo-responsive functionalization of superparamagnetic Co NPs initially stabilized by hydrophobic small molecules oleic acid (OA) and trioctylphosphine oxide (TOPO), as well as the synthesis of both superparamagnetic and ferromagnetic Co NPs by using end-functionalized-polystyrene as stabilizer. Co NPs, due to their excellent magnetic and catalytic properties, have great potential application in various fields, such as ferrofluids, catalysis, and magnetic resonance imaging (MRI). Superparamagnetic Co NPs are especially interesting, since they exhibit zero coercivity. They get magnetized in an external magnetic field and reach their saturation magnetization rapidly, but no magnetic moment remains after removal of the applied magnetic field. Therefore, they do not agglomerate in the body when they are used in biomedical applications. Normally, decomposition of metallic precursors at high temperature is one of the most important methodsThis thesis mainly covers the synthesis, surface modification, magnetic-field-induced assembly and thermo-responsive functionalization of superparamagnetic Co NPs initially stabilized by hydrophobic small molecules oleic acid (OA) and trioctylphosphine oxide (TOPO), as well as the synthesis of both superparamagnetic and ferromagnetic Co NPs by using end-functionalized-polystyrene as stabilizer. Co NPs, due to their excellent magnetic and catalytic properties, have great potential application in various fields, such as ferrofluids, catalysis, and magnetic resonance imaging (MRI). Superparamagnetic Co NPs are especially interesting, since they exhibit zero coercivity. They get magnetized in an external magnetic field and reach their saturation magnetization rapidly, but no magnetic moment remains after removal of the applied magnetic field. Therefore, they do not agglomerate in the body when they are used in biomedical applications. Normally, decomposition of metallic precursors at high temperature is one of the most important methods in preparation of monodisperse magnetic NPs, providing tunability in size and shape. Hydrophobic ligands like OA, TOPO and oleylamine are often used to both control the growth of NPs and protect them from agglomeration. The as-prepared magnetic NPs can be used in biological applications as long as they are transferred into water. Moreover, their supercrystal assemblies have the potential for high density data storage and electronic devices. In addition to small molecules, polymers can also be used as surfactants for the synthesis of ferromagnetic and superparamagnetic NPs by changing the reaction conditions. Therefore, chapter 2 gives an overview on the basic concept of synthesis, surface modification and self-assembly of magnetic nanoparticles. Various examples were used to illustrate the recent work. The hydrophobic Co NPs synthesized with small molecules as surfactants limit their biological applications, which require a hydrophilic or aqueous environment. Surface modification (e.g., ligand exchange) is a general idea for either phase transition or surface-functionalization. Therefore, in chapter 3, a ligand exchange process was conducted to functionalize the surface of Co NPs. PNIPAM is one of the most popular smart polymers and its lower critical solution temperature (LCST) is around 32 °C, with a reversible change in the conformation structure between hydrophobic and hydrophilic. The novel nanocomposites of superparamagnetic Co NPs and thermo-responsive PNIPAM are of great interest. Thus, well-defined superparamagnetic Co NPs were firstly synthesized through the thermolysis of cobalt carbonyl by using OA and TOPO as surfactants. A functional ATRP initiator, containing an amine (as anchoring group) and a 2-bromopropionate group (SI-ATRP initiator), was used to replace the original ligands. This process is rapid and facial for efficient surface functionalization and afterwards the Co NPs can be dispersed into polar solvent DMF without aggregation. FT-IR spectroscopy showed that the TOPO was completely replaced, but a small amount of OA remained on the surface. A TGA measurement allowed the calculation of the grafting density of the initiator as around 3.2 initiator/nm2. Then, the surface-initiated ATRP was conducted for the polymerization of NIPAM on the surface of Co NPs and rendered the nanocomposites water-dispersible. A temperature-dependent dynamic light scattering study showed the aggregation behavior of PNIPAM-coated Co NPs upon heating and this process was proven to be reversible. The combination of superparamagnetic and thermo-responsive properties in these hybrid nanoparticles is promising for future applications e.g. in biomedicine. In chapter 4, the magnetic-field-induced assembly of superparamagnetic cobalt nanoparticles both on solid substrates and at liquid-air interface was investigated. OA- and TOPO-coated Co NPs were synthesized via the thermolysis of cobalt carbonyl and dispersed into either hexane or toluene. The Co NP dispersion was dropped onto substrates (e.g., TEM grid, silicon wafer) and at liquid-air (water-air or ethylene glycol-air) interface. Due to the attractive dipolar interaction, 1-D chains formed in the presence of an external magnetic field. It is known that the concentration and the strength of the magnetic field can affect the assembly behavior of superparamagnetic Co NPs. Therefore, the influence of these two parameters on the morphology of the assemblies was studied. The formed 1-D chains were shorter and flexible at either lower concentration of the Co NP dispersion or lower strength of the external magnetic field due to thermal fluctuation. However, by increasing either the concentration of the NP dispersion or the strength of the applied magnetic field, these chains became longer, thicker and straighter. The reason could be that a high concentration led to a high fraction of short dipolar chains, and their interaction resulted in longer and thicker chains under applied magnetic field. On the other hand, when the magnetic field increased, the induced moments of the magnetic nanoparticles became larger, which dominated over the thermal fluctuation. Thus, the formed short chains connected to each other and grew in length. Thicker chains were also observed through chain-chain interaction. Furthermore, the induced moments of the NPs tended to direct into one direction with increased magnetic field, thus the chains were straighter. In comparison between the assembly on substrates, at water-air interface and at ethylene glycol-air interface, the assembly of Co NPs in hexane dispersion at ethylene glycol-air interface showed the most regular and homogeneous chain structures due to the better spreading of the dispersion on ethylene glycol subphase than on water subphase and substrates. The magnetic-field-induced assembly of superparamagnetic nanoparticles could provide a powerful approach for applications in data storage and electronic devices. Chapter 5 presented the synthesis of superparamagnetic and ferromagnetic cobalt nanoparticles through a dual-stage thermolysis of cobalt carbonyl (Co2(CO)8) by using polystyrene as surfactant. The amine end-functionalized polystyrene surfactants with different molecular weight were prepared via atom transfer radical polymerization technique. The molecular weight determination of polystyrene was conducted by gel permeation chromatography (GPC) and matrix-assisted laser desorption/ionization time-of-flight (MALDI-ToF) mass spectrometry techniques. The results showed that, when the molecular weight distribution is low (Mw/Mn < 1.2), the measurement by GPC and MALDI-ToF MS provided nearly similar results. For example, the molecular weight of 10600 Da was obtained by MALDI-ToF MS, while GPC gave 10500 g/mol (Mw/Mn = 1.17). However, if the polymer is poly distributed, MALDI-ToF MS cannot provide an accurate value. This was exemplified for a polymer with a molecular weight of 3130 Da measured by MALDI-TOF MS, while GPC showed 2300 g/mol (Mw/Mn = 1.38). The size, size distribution and magnetic properties of the hybrid particles were different by changing either the molecular weight or concentration of the polymer surfactants. The analysis from TEM characterization showed that the size of cobalt nanoparticles stabilized with polystyrene of lower molecular weight (Mn = 2300 g/mol) varied from 12–22 nm, while the size with middle (Mn = 4500 g/mol) and higher molecular weight (Mn = 10500 g/mol) of polystyrene-coated cobalt nanoparticles showed little change. Magnetic measurements exhibited that the small cobalt particles (12 nm) were superparamagnetic, while larger particles (21 nm) were ferromagnetic and assembled into 1-D chains. The grafting density calculated from thermogravimetric analysis showed that a higher grafting density of polystyrene was obtained with lower molecular weight (Mn = 2300 g/mol) than those with higher molecular weight (Mn = 10500 g/mol). Due to the larger steric hindrance, polystyrene with higher molecular weight cannot form a dense shell on the surface of the nanoparticles, which resulted in a lower grafting density. Wide angle X-ray scattering measurements revealed the epsilon cobalt crystalline phases of both superparamagnetic Co NPs coated with polystyrene (Mn = 2300 g/mol) and ferromagnetic Co NPs coated with polystyrene (Mn = 10500 g/mol). Furthermore, a stability study showed that PS-Co NPs prepared with higher polymer concentration and polymer molecular weight exhibited a better stability.show moreshow less
  • Im Rahmen dieser Arbeit wurden superparamagnetische Cobalt Nanopartikel (NP) synthetisiert, die Selbstassemblierung im Magnetfeld untersucht und die ursprünglichen Liganden Ölsäure (Englisch oleic acid, OA) und Trioctylphosphanoxid (TOPO) ersetzt, um eine Funktionalisierung der Nanopartikel mit einem Temperatur-responsiven Polymer zu erreichen. Außerdem wurden superparamagnetische und ferromagnetische Co NP mit Polystyrol als Stabilisator synthetisiert. Co NP haben aufgrund ihrer herausragenden magnetischen und katalytischen Eigenschaften viele potentielle Anwendungen beispielsweise als Ferrofluide, in der Katalyse und der Magnetresonanztomografie (Englisch magnetic resonance imaging, MRI). Besonders interessant sind dabei superparamagnetische Co NP, die in einem äußeren Magnetfeld magnetisiert werden, aber nach Entfernen des angelegten Magnetfelds keine Magnetisierung mehr aufweisen. Bei biomedizinischen Anwendungen aggregieren sie daher nicht im Körper. Hydrophobe Co NP, die von kleinen Molekülen stabilisiert werden, eignen sichIm Rahmen dieser Arbeit wurden superparamagnetische Cobalt Nanopartikel (NP) synthetisiert, die Selbstassemblierung im Magnetfeld untersucht und die ursprünglichen Liganden Ölsäure (Englisch oleic acid, OA) und Trioctylphosphanoxid (TOPO) ersetzt, um eine Funktionalisierung der Nanopartikel mit einem Temperatur-responsiven Polymer zu erreichen. Außerdem wurden superparamagnetische und ferromagnetische Co NP mit Polystyrol als Stabilisator synthetisiert. Co NP haben aufgrund ihrer herausragenden magnetischen und katalytischen Eigenschaften viele potentielle Anwendungen beispielsweise als Ferrofluide, in der Katalyse und der Magnetresonanztomografie (Englisch magnetic resonance imaging, MRI). Besonders interessant sind dabei superparamagnetische Co NP, die in einem äußeren Magnetfeld magnetisiert werden, aber nach Entfernen des angelegten Magnetfelds keine Magnetisierung mehr aufweisen. Bei biomedizinischen Anwendungen aggregieren sie daher nicht im Körper. Hydrophobe Co NP, die von kleinen Molekülen stabilisiert werden, eignen sich nicht für biologische Anwendungen, für die ein hydrophiles oder wässriges Medium vonnöten ist. Kapitel 3 beschreibt einen Ligandenaustausch zur Funktionalisierung von Co Nanopartikeln und das Herstellen neuer Nanokomposite aus superparamagnetischen Co NP und Temperatur-responsivem PNIPAM. Zunächst wurden wohldefinierte superparamagnetische Co NP mit OA und TOPO als Stabilisatoren durch die Thermolyse von Cobalt Carbonyl synthetisiert. Die ursprünglichen Liganden wurden dann durch einen funktionalen Liganden mit einer Amingruppe (zum Binden an die Oberfläche) und einer 2 Brompropionat-Gruppe (Polymerisationsinitiator) ersetzt. Nach diesem schnellen und einfachen Prozess der Oberflächenfunktionalisierung können die Nanopartikel ohne Aggregation in dem polaren Lösungsmittel DMF dispergiert werden. Nach thermogravimetrischen Messungen konnte die Dichte der Initiatoren mit ungefähr 3,2 Initiatoren / nm2 berechnet werden. Anschließend wurde Oberflächen-initiierte ATRP zur Polymerisation von NIPAM durchgeführt. Temperatur-abhängige Messungen der dynamischen Lichtstreuung der nun in Wasser dispergierbaren Nanokomposite zeigte das reversible Aggregationsverhalten nach Erhitzen über 32 °C. Kapitel 4 behandelt die Untersuchung der Assemblierung von superparamagnetischen OA- und TOPO-stabilisierten Co NP im äußeren Magnetfeld sowohl auf festen Oberflächen als auch der Flüssigkeit-Luft Grenzfläche. Durch die anziehende dipolare Wechselwirkung bildeten sich im äußeren Magnetfeld 1-D Ketten. Der Einfluss der Konzentration der Dispersion und der Stärke des Magnetfelds auf die Morphologie der assemblierten Strukturen wurde untersucht. Bei niedrigerer Konzentration der Dispersion und geringerer Magnetfeldstärke bildeten sich kurze und flexible Ketten. Bei höherer Konzentration oder höherer Magnetfeldstärke wurden die Ketten länger, breiter und gerader. Andererseits sind die induzierten magnetischen Momente bei erhöhter Magnetfeldstärke größer und dominieren über die thermische Fluktuation. Daher verbinden sich die kurzen Ketten zu längeren, und dickere Ketten entstehen durch Interaktion benachbarter Ketten. Außerdem zeigen die induzierten Momente der NP verstärkt in die gleiche Richtung je größer das äußere Magnetfeld ist, weshalb die Ketten gerader werden. Im Vergleich der Assemblierung auf Substraten (TEM-Grids, Siliciumwafer), an der Wasser-Luft und Ethylenglycol-Luft Grenzfläche, zeigte die Assemblierung von Co NP aus Hexan-Dispersion an der Ethylenglycol-Luft Grenzfläche die geordnetsten und homogensten Strukturen. Kapitel 5 präsentierte die Synthese von superparamagnetischen und ferromagnetischen Cobalt Nanopartikeln durch die zwei-stufige Thermolyse von Cobalt Carbonyl (Co2(CO)8) mit Polystyrol als Stabilisator. Polystyrol Polymere mit Amin-Endgruppen wurden durch ATRP-Technik mit unterschiedlichen Molekulargewichten hergestellt. Die Größe, Größenverteilung und magnetischen Eigenschaften der hybriden Partikel haben sich mit dem Molekulargewicht und der Konzentration der Polymer-Stabilisatoren unterschieden. Eine Analyse mit Transmissionselektronenmikroskopie zeigte, dass die Größe der Co NP zwischen 12–22 nm variierte, wenn sie durch Polystyrol geringen Molekulargewichts (Mn = 2300 g/mol) stabilisiert wurden, während sich die Größe der Partikel mit Polystyrol mittleren (Mn = 4500 g/mol) und höheren (Mn = 10500 g/mol) Molekulargewichts kaum unterschied. Messungen der magnetischen Eigenschaften zeigten, dass die kleinen Cobalt Partikel (12 nm) superparamagnetisch waren, während größere Partikel (21 nm) ferromagnetisch waren und zu 1-D Ketten assemblierten. Die Dichte der Polymere auf der Oberfläche wurde nach einer thermogravimetrischen Analyse berechnet. Mit kleinem Molekulargewicht (Mn = 2300 g/mol) wurde eine höhere Dichte erreicht als mit hohem Molekulargewicht (Mn = 10500 g/mol). Durch eine stärker ausgeprägte sterische Hinderung kann ein Polymer hohen Molekulargewichts keine dichte Hülle um die Nanopartikel bilden. Das Vorliegen einer epsilon kristallinen Phase wurde durch Weitwinkel-Röntgenstreuung sowohl für superparamagnetische Co NP (mit PS Mn = 2300 g/mol) als auch ferromagnetische Co NP (mit PS Mn = 10500 g/mol) bestimmt.show moreshow less

Download full text files

  • tan_diss.pdfeng
    (11699KB)

    SHA-1:2d1decd67595ee3f4a07ad06b99ac10003857489

Export metadata

Metadaten
Author:Li TanORCiD
URN:urn:nbn:de:kobv:517-opus4-418153
Advisor:Alexander Böker, Ulrich Glebe
Document Type:Doctoral Thesis
Language:English
Year of Completion:2018
Publishing Institution:Universität Potsdam
Granting Institution:Universität Potsdam
Date of final exam:2018/10/02
Release Date:2018/10/22
Tag:Assemblierung; Cobalt Nanopartikeln; Polymer; magnetische Nanopartikel
assembly; cobalt nanoparticles; magnetic nanoparticles; polymer
Pagenumber:X, 111
RVK - Regensburg Classification:VE 9857
Organizational units:Mathematisch-Naturwissenschaftliche Fakultät / Institut für Chemie
Dewey Decimal Classification:5 Naturwissenschaften und Mathematik / 54 Chemie / 540 Chemie und zugeordnete Wissenschaften
Licence (German):License LogoCreative Commons - Namensnennung, 4.0 International