TY - JOUR A1 - Qiu, Xunlin A1 - Mellinger, Axel A1 - Wirges, Werner A1 - Gerhard, Reimund T1 - Spectroscopic study of dielectric barrier discharges in cellular polypropylene ferroelectrets N2 - The transient light emission from the dielectric barrier discharges (DBDs) in cellular polypropylene ferroelectrets subjected to high electric poling fields was spectroscopically measured. The spectrum shows strong emission from the second positive system of molecular nitrogen, N-2(C (3)Pi(u))-> N-2(B (3)Pi(g)), and the first negative system of N-2(+), N-2(+)(B (2)Sigma(+)(u))-> N-2(+)(X (2)Sigma(+)(g)), consistent with a DBD in air. When a dc voltage is applied stepwise to the ferroelectret film, light emission starts above a threshold, coinciding with the threshold voltage in obtaining piezoelectricity. From selected vibronic band strength ratios, the electric field in the discharge was determined and found to agree with Townsend breakdown. Y1 - 2007 UR - http://apl.aip.org/ U6 - https://doi.org/10.1063/1.2786597 ER - TY - JOUR A1 - Qiu, Xunlin A1 - Mellinger, Axel A1 - Wirges, Werner A1 - Gerhard, Reimund T1 - Dielectric barrier discharges during the generation of ferroelectrets : optical spectroscopy for process monitoring Y1 - 2007 SN - 978-1-4244-1482-6 ER - TY - JOUR A1 - Qiu, Xunlin A1 - Mellinger, Axel A1 - Wegener, Michael A1 - Wirges, Werner A1 - Gerhard, Reimund T1 - Barrier discharges in cellular polypropylene ferroelectrets : how do they influence the electromechanical properties? Y1 - 2007 ER - TY - JOUR A1 - Altafim, Ruy Alberto Pisani A1 - Qiu, Xunlin A1 - Wirges, Werner A1 - Gerhard, Reimund A1 - Altafim, Ruy Alberto Pisani A1 - Basso, Heitor Cury A1 - Jenninger, Werner A1 - Wagner, Joachim T1 - Template-based fluoroethylenepropylene piezoelectrets with tubular channels for transducer applications N2 - We describe the concept, the fabrication, and the most relevant properties of a piezoelectric-polymer system: Two fluoroethylenepropylene (FEP) films with good electret properties are laminated around a specifically designed and prepared polytetrafluoroethylene (PTFE) template at 300 degrees C. After removing the PTFE template, a two-layer FEP film with open tubular channels is obtained. For electric charging, the two-layer FEP system is subjected to a high electric field. The resulting dielectric barrier discharges inside the tubular channels yield a ferroelectret with high piezoelectricity. d(33) coefficients of up to 160 pC/N have already been achieved on the ferroelectret films. After charging at suitable elevated temperatures, the piezoelectricity is stable at temperatures of at least 130 degrees C. Advantages of the transducer films include ease of fabrication at laboratory or industrial scales, a wide range of possible geometrical and processing parameters, straightforward control of the uniformity of the polymer system, flexibility, and versatility of the soft ferroelectrets, and a large potential for device applications e.g., in the areas of biomedicine, communications, production engineering, sensor systems, environmental monitoring, etc. Y1 - 2009 UR - http://jap.aip.org/ U6 - https://doi.org/10.1063/1.3159039 SN - 0021-8979 ER - TY - JOUR A1 - Fang, Peng A1 - Qiu, Xunlin A1 - Wirges, Werner A1 - Gerhard, Reimund A1 - Zirkel, Larissa T1 - Polyethylene-naphthalate (PEN) ferroelectrets : cellular structure, piezoelectricity and thermal stability N2 - Cellular polyethylene-naphthalate (PEN) ferroelectrets are useful as soft and flexible electromechanical transducer materials. Improved cellular PEN foams are prepared by means of a "voiding + inflation + stretching" process and investigated with respect to their structure and their applications-relevant properties. It is found that most of the cellular voids have heights below 8 mu m. The polymer walls do not allow sufficient gas exchange between the voids and the ambient atmosphere, when the cellular films are exposed to atmospheric pressures between a millibar and a few bars. As expected for ferroelectrets, a threshold voltage for charging is observed: A reasonable piezoelectric coefficient d(33) is only found when the charging voltage is higher than 4 kV. Furthermore, d(33) increases with charging voltage and reaches saturation at approximately 8 kV. Annealing after charging or charging at elevated temperatures may enhance the thermal stability of the PEN ferroelectrets. The d(33) of properly annealed samples is stable up to the respective annealing temperatures, but the annealing process reduces the piezoelectric activity of charged ferroelectret films to some extent. Samples charged at suitable elevated temperatures show much better thermal stability than those charged at room temperature, but the charging temperature should be limited to values below the material's glass-transition temperature T-g. Furthermore, the relevant elastic modulus c(33) of PEN ferroelectrets may decrease upon thermal treatment. Y1 - 2010 UR - http://ieeexplore.ieee.org/servlet/opac?punumber=94 U6 - https://doi.org/10.1109/TDEI.2010.5539678 SN - 1070-9878 ER - TY - GEN A1 - Qiu, Xunlin T1 - Patterned piezo-, pyro-, and ferroelectricity of poled polymer electrets T2 - Journal of applied physics Y1 - 2011 U6 - https://doi.org/10.1063/1.3638069 SN - 0021-8979 VL - 110 IS - 5 PB - American Institute of Physics CY - Melville ER - TY - JOUR A1 - Sun, Zhuanlan A1 - Zhang, Xiaoqing A1 - Xia, Zhongfu A1 - Qiu, Xunlin A1 - Wirges, Werner A1 - Gerhard, Reimund A1 - Zeng, Changchun A1 - Zhang, Chuck A1 - Wang, Ben T1 - Polarization and piezoelectricity in polymer films with artificial void structure JF - Applied physics : A, Materials science & processing N2 - Laminated polymer-film systems with well-defined void structures were prepared from fluoroethylenepropylene (FEP) and polytetrafluoroethylene (PTFE) layers. First the PTFE films were patterned and then fusion-bonded with the FEP films. The laminates were subjected to either corona or contact charging in order to obtain the desired piezoelectricity. The build-up of the "macro-dipoles" in the laminated films was studied by recording the electric hysteresis loops. The resulting electro-mechanical properties were investigated by means of dielectric resonance spectroscopy (DRS) and direct measurements of the stress-strain relationship. Moreover, the thermal stability of the piezoelectric d (33) coefficient was investigated at elevated temperatures and via thermally stimulated discharge (TSD) current measurements in short circuit. For 150 mu m thick laminated films, consisting of one 25 mu m thick PTFE layer, two 12.5 mu m thick FEP layers, and a void of 100 mu m height, the critical voltage necessary for the build-up of the "macro-dipoles" in the inner voids was approximately 1400 V, which agrees with the value calculated from the Paschen Law. A quasi-static piezoelectric d (33) coefficient up to 300 pC/N was observed after corona charging. The mechanical properties of the film systems are highly anisotropic. At room temperature, the Young's moduli of the laminated film system are around 0.37 MPa in the thickness direction and 274 MPa in the lateral direction, respectively. Using these values, the theoretical shape anisotropy ratio of the void was calculated, which agrees well with experimental observation. Compared with films that do not exhibit structural regularity, the laminates showed improved thermal stability of the d (33) coefficients. The thermal stability of d (33) can be further improved by pre-aging. E.g., the reduction of the d (33) value in the sample pre-aged at 150A degrees C for 5 h was less than 5% after annealing for 30 h at a temperature of 90A degrees C. Y1 - 2011 U6 - https://doi.org/10.1007/s00339-011-6481-2 SN - 0947-8396 VL - 105 IS - 1 SP - 197 EP - 205 PB - Springer CY - New York ER - TY - JOUR A1 - Qiu, Xunlin A1 - Wirges, Werner A1 - Gerhard, Reimund T1 - Beneficial and detrimental fatigue effects of dielectric barrier discharges on the piezoelectricity of polypropylene ferroelectrets JF - Journal of applied physics N2 - Cellular polypropylene (PP) ferroelectrets combine a large piezoelectricity with mechanical flexibility and elastic compliance. Their charging process represents a series of dielectric barrier discharges (DBDs) that generate a cold plasma with numerous active species and thus modify the inner polymer surfaces of the foam cells. Both the threshold for the onset of DBDs and the piezoelectricity of ferroelectrets are sensitive to repeated DBDs in the voids. It is found that the threshold voltage is approximately halved and the charging efficiency is clearly improved after only 10(3) DBD cycles. However, plasma modification of the inner surfaces from repeated DBDs deteriorates the chargeability of the voids, leading to a significant reduction of the piezoelectricity in ferroelectrets. After a significant waiting period, the chargeability of previously fatigued voids shows a partial recovery. The plasma modification is, however, detrimental to the stability of the deposited charges and thus also of the macroscopic dipoles and of the piezoelectricity. Fatigue from only 10(3) DBD cycles already results in significantly less stable piezoelectricity in cellular PP ferroelectrets. The fatigue rate as a function of the number of voltage cycles follows a stretched exponential. Fatigue from repeated DBDs can be avoided if most of the gas molecules inside the voids are removed via a suitable evacuation process. Y1 - 2011 U6 - https://doi.org/10.1063/1.3610507 SN - 0021-8979 SN - 1089-7550 VL - 110 IS - 2 PB - American Institute of Physics CY - Melville ER - TY - JOUR A1 - Qiu, Xunlin A1 - Gerhard, Reimund A1 - Mellinger, Axel T1 - Turning polymer foams or polymer-film systems into ferroelectrets dielectric barrier discharges in voids JF - IEEE transactions on dielectrics and electrical insulation N2 - Polymer foams and void-containing polymer-film systems with internally charged voids combine large piezoelectricity with mechanical flexibility and elastic compliance. This new class of soft materials (often called ferro-or piezoelectrets) has attracted considerable attention from science and industry. It has been found that the voids can be internally charged by means of dielectric barrier discharges (DBDs) under high electric fields. The charged voids can be considered as man-made macroscopic dipoles. Depending on the ferroelectret structure and the pressure of the internal gas, the voids may be highly compressible. Consequently, very large dipole-moment changes can be induced by mechanical or electrical stresses, leading to large piezoelectricity. DBD charging of the voids is a critical process for rendering polymer foams piezoelectric. Thus a comprehensive exploration of DBD charging is essential for the understanding and the optimization of piezoelectricity in ferroelectrets. Recent studies show that DBDs in the voids are triggered when the internal electric field reaches a threshold value according to Townsend's model of Paschen breakdown. During the DBDs, charges of opposite polarity are generated and trapped at the top and bottom internal surfaces of the gas-filled voids, respectively. The deposited charges induce an electric field opposite to the externally applied one and thus extinguish the DBDs. Back discharges may eventually be triggered when the external voltage is reduced or turned off. In order to optimize the efficiency of DBD charging, the geometry (in particular the height) of the voids, the type of gas and its pressure inside the voids are essential factors to be considered and to be optimized. In addition, the influence of the plasma treatment on the internal void surfaces during the DBDs should be taken into consideration. KW - Ferroelectret KW - piezoelectret KW - dielectric barrier discharge (DBD) KW - effective polarization KW - man-made dipole Y1 - 2011 U6 - https://doi.org/10.1109/TDEI.2011.5704490 SN - 1070-9878 VL - 18 IS - 1 SP - 34 EP - 42 PB - Inst. of Electr. and Electronics Engineers CY - Piscataway ER - TY - JOUR A1 - Wirges, Werner A1 - Raabe, Sebastian A1 - Qiu, Xunlin T1 - Dielectric elastomer and ferroelectret films combined in a single device how do they reinforce each other? JF - Applied physics : A, Materials science & processing N2 - Dielectric elastomers (DE) are soft polymer materials exhibiting large deformations under electrostatic stress. When a prestretched elastomer is stuck to a flat plastic frame, a complex structure that can be used as an actuator (DEA) is formed due to self-organization and energy minimization. Here, such a DEA was equipped with a ferroelectret film. Ferroelectrets are internally charged polymer foams or void-containing polymer-film systems combining large piezoelectricity with mechanical flexibility and elastic compliance. In their dielectric spectra, ferroelectrets show piezoelectric resonances that can be used to analyze their electromechanical properties. The antiresonance frequencies ( ) of ferroelectret films not only are directly related to their geometric parameters, but also are sensitive to the boundary conditions during measurement. In this paper, a fluoroethylenepropylene (FEP) ferroelectret film with tubular void channels was glued to a plastic frame prior to the formation of self-organized minimum-energy DEA structure. The dielectric resonance spectrum (DRS) of the ferroelectret film was measured in-situ during the actuation of the DEA under applied voltage. It is found that the antiresonance frequency is a monotropic function of the bending angle of the actuator. Therefore, the actuation of DEAs can be used to modulate the of ferroelectrets, while the can also be taken for in-situ diagnosis and for precise control of the actuation of the DEA. Combination of DEAs and ferroelectrets brings a number of possibilities for application. Y1 - 2012 U6 - https://doi.org/10.1007/s00339-012-6833-6 SN - 0947-8396 SN - 1432-0630 VL - 107 IS - 3 SP - 583 EP - 588 PB - Springer CY - New York ER -