TY  - JOUR
A1  - Tiseanu, Carmen
A1  - Lorenz-Fonfria, Victor A.
A1  - Geßner, André
A1  - Kumke, Michael Uwe
A1  - Gagea, Bogdan
T1  - Comparative luminescence study of terbium-exchanged zeolites silylated with alkoxysilanes
N2  - Terbium-exchanged ZSM-5, MOR and (H)BEA zeolites were silylated with phenyl-, vinyl- and hexadecyl trimethoxysilanes via a post-synthesis grafting. All samples were investigated by means of PXRD, FT-IR, TGA, physical adsorption, DR-UV-Vis and time-resolved photoluminescence spectroscopy. From the comparison of the photoluminescence decays of terbium-exchanged in parent (non-silylated) and silylated zeolites, it resulted that the silylation efficiency of the various alkoxysilanes is determined by the type of zeolite and follows the sequences: phenyl > vinyl > hexadecyl > parent for ZSM-5, hexadecyl a parts per thousand phenyl a parts per thousand vinyl > parent for MOR and hexadecyl > phenyl a parts per thousand vinyl > a parts per thousand parent for BEA zeolites, respectively.
Y1  - 2009
UR  - http://www.springerlink.com/content/100190
U6  - https://doi.org/10.1007/s10854-008-9597-1
SN  - 0957-4522
ER  - 
TY  - JOUR
A1  - Tiseanu, Carmen
A1  - Lorenz-Fonfria, Victor A.
A1  - Parvulescu, Vasile Ion
A1  - Geßner, Andre
A1  - Kumke, Michael Uwe
T1  - Photoluminescence study of terbium-exchanged ultrastable Y zeolites: Number of species, photoluminescence decays and decay-associated spectra
Y1  - 2008
UR  - http://scitation.aip.org/getpdf/servlet/ GetPDFServlet?filetype=pdf&id=JAPIAU000104000003033530000001&idtype=cvips&doi=10.1063/1.2966304&prog=normal
U6  - https://doi.org/10.1063/1.2966304
ER  - 
TY  - JOUR
A1  - Tiseanu, Carmen
A1  - Parvulescu, Vasile Ion
A1  - Cojocaru, Bogdan
A1  - Lorenz-Fonfria, Victor A.
A1  - Kumke, Michael Uwe
A1  - Gessner, Andre
A1  - Enculescu, Ion
T1  - Polymer-microporous host interactions probed by photoluminescence spectroscopy
N2  - Zeolites NaY and ZSM-5 were used as hosts for styrene polymerization after ion-exchange with europium ions. The parent and hybrid, polystyrene coated Eu-NaY (Eu-NaY/PS) and Eu-ZSM-5 (Eu-ZSM-5/PS) zeolites were investigated by using thermal analysis, SEM, PXRD, FT-IR, DR-UV/Vis, steady state and time-resolved photoluminescence spectroscopy. FT-IR spectra evidenced for the interaction between the zeolitic hosts and polystyrene while the PXRD spectra supported for the presence of the polymer inside the channels/pores of Eu-NaY/PS and Eu-ZSM-5/PS materials. The optical properties of Eu-NaY/PS and Eu-ZSM-5/PS were significantly changed relative to those of the parent zeolites, giving further evidence for the presence of polymer inside zeolites. An interesting case is presented by NaY zeolite: following styrene polymerization, the polymer interacted selectively with one of the two main species co-existing inside zeolite while for ZSM-5 a similar effect was not observed.
Y1  - 2010
UR  - http://www.rsc.org/Publishing/Journals/CP/index.asp
U6  - https://doi.org/10.1039/B922591a
SN  - 1463-9076
ER  -