TY - JOUR A1 - Goebel, Ronald A1 - Xie, Zai-Lai A1 - Neumann, Mike A1 - Günter, Christina A1 - Loebbicke, Ruben A1 - Kubo, Shiori A1 - Titirici, Maria-Magdalena A1 - Giordano, Cristina A1 - Taubert, Andreas T1 - Synthesis of mesoporous carbon/iron carbide hybrids with unusually high surface areas from the ionic liquid precursor [Bmim][FeCl4] JF - CrystEngComm N2 - Mesoporous carbon/iron carbide hybrid materials with surface areas reaching 800 m(2) g(-1) were synthesized via an exotemplating route using monolithic mesoporous silica as template and the ionic liquid 1-butyl-3-methylimidazolium tetrachloridoferrate(III) [Bmim][FeCl4] as carbon and iron source. After heat treatment (750 degrees C under argon) of the [Bmim][FeCl4] precursor confined within the silica matrix, the silica exotemplate was removed with HF leaving the mesoporous C/Fe3C hybrid behind. The surface areas and the pore sizes depend on the exotemplate and the surface areas a significantly larger than any other surface area reported for C/Fe3C hybrid materials so far. The approach is thus a prototype for the synthesis of high-surface area iron carbide-based hybrid materials with potential application in catalysis. Y1 - 2012 U6 - https://doi.org/10.1039/c2ce25064k SN - 1466-8033 VL - 14 IS - 15 SP - 4946 EP - 4951 PB - Royal Society of Chemistry CY - Cambridge ER - TY - GEN A1 - Bhattacharyya, Biswajit A1 - Balischewski, Christian A1 - Sperlich, Eric A1 - Günter, Christina A1 - Mies, Stefan A1 - Kelling, Alexandra A1 - Taubert, Andreas T1 - N-Butyl Pyridinium Diiodido Argentate(I) BT - A One-Dimensional Ag-I Network with Superior Solid-State Ionic Conductivity at Room Temperature T2 - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe N2 - A new solid-state material, N-butyl pyridinium diiodido argentate(I), is synthesized using a simple and effective one-pot approach. In the solid state, the compound exhibits 1D ([AgI2](-))(n) chains that are stabilized by the N-butyl pyridinium cation. The 1D structure is further manifested by the formation of long, needle-like crystals, as revealed from electron microscopy. As the general composition is derived from metal halide-based ionic liquids, the compound has a low melting point of 100-101 degrees C, as confirmed by differential scanning calorimetry. Most importantly, the compound has a conductivity of 10(-6) S cm(-1) at room temperature. At higher temperatures the conductivity increases and reaches to 10(-4 )S cm(-1) at 70 degrees C. In contrast to AgI, however, the current material has a highly anisotropic 1D arrangement of the ionic domains. This provides direct and tuneable access to fast and anisotropic ionic conduction. The material is thus a significant step forward beyond current ion conductors and a highly promising prototype for the rational design of highly conductive ionic solid-state conductors for battery or solar cell applications. T3 - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe - 1341 KW - AgI KW - ionic conductivity KW - Ionic liquids KW - thermal properties Y1 - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-604874 SN - 1866-8372 IS - 1341 ER - TY - JOUR A1 - Bhattacharyya, Biswajit A1 - Balischewski, Christian A1 - Sperlich, Eric A1 - Günter, Christina A1 - Mies, Stefan A1 - Kelling, Alexandra A1 - Taubert, Andreas T1 - N-Butyl Pyridinium Diiodido Argentate(I) BT - A One-Dimensional Ag-I Network with Superior Solid-State Ionic Conductivity at Room Temperature JF - Advanced materials interfaces N2 - A new solid-state material, N-butyl pyridinium diiodido argentate(I), is synthesized using a simple and effective one-pot approach. In the solid state, the compound exhibits 1D ([AgI2](-))(n) chains that are stabilized by the N-butyl pyridinium cation. The 1D structure is further manifested by the formation of long, needle-like crystals, as revealed from electron microscopy. As the general composition is derived from metal halide-based ionic liquids, the compound has a low melting point of 100-101 degrees C, as confirmed by differential scanning calorimetry. Most importantly, the compound has a conductivity of 10(-6) S cm(-1) at room temperature. At higher temperatures the conductivity increases and reaches to 10(-4 )S cm(-1) at 70 degrees C. In contrast to AgI, however, the current material has a highly anisotropic 1D arrangement of the ionic domains. This provides direct and tuneable access to fast and anisotropic ionic conduction. The material is thus a significant step forward beyond current ion conductors and a highly promising prototype for the rational design of highly conductive ionic solid-state conductors for battery or solar cell applications. KW - AgI KW - ionic conductivity KW - Ionic liquids KW - thermal properties Y1 - 2023 U6 - https://doi.org/10.1002/admi.202202363 SN - 2196-7350 VL - 10 IS - 12 PB - Wiley CY - Hoboken ER - TY - JOUR A1 - Block, Inga A1 - Günter, Christina A1 - Duarte Rodrigues, Alysson A1 - Paasch, Silvia A1 - Hesemann, Peter A1 - Taubert, Andreas T1 - Carbon adsorbents from spent coffee for removal of methylene blue and methyl orange from water JF - Materials / Molecular Diversity Preservation International N2 - Activated carbons (ACs) were prepared from dried spent coffee (SCD), a biological waste product, to produce adsorbents for methylene blue (MB) and methyl orange (MO) from aqueous solution. Pre-pyrolysis activation of SCD was achieved via treatment of the SCD with aqueous sodium hydroxide solutions at 90 °C. Pyrolysis of the pretreated SCD at 500 °C for 1 h produced powders with typical characteristics of AC suitable and effective for dye adsorption. As an alternative to the rather harsh base treatment, calcium carbonate powder, a very common and abundant resource, was also studied as an activator. Mixtures of SCD and CaCO3 (1:1 w/w) yielded effective ACs for MO and MB removal upon pyrolysis needing only small amounts of AC to clear the solutions. A selectivity of the adsorption process toward anionic (MO) or cationic (MB) dyes was not observed. KW - water KW - spent coffee KW - dye adsorption KW - methylene blue KW - methyl orange KW - calcium carbonate KW - activated carbon KW - water treatment KW - dye removal Y1 - 2021 U6 - https://doi.org/10.3390/ma14143996 SN - 1996-1944 VL - 14 IS - 14 PB - Molecular Diversity Preservation International CY - Basel ER -