TY - JOUR A1 - Tiseanu, Carmen A1 - Parvulescu, Vasile Ion A1 - Cojocaru, Bogdan A1 - Lorenz-Fonfria, Victor A. A1 - Kumke, Michael Uwe A1 - Gessner, Andre A1 - Enculescu, Ion T1 - Polymer-microporous host interactions probed by photoluminescence spectroscopy N2 - Zeolites NaY and ZSM-5 were used as hosts for styrene polymerization after ion-exchange with europium ions. The parent and hybrid, polystyrene coated Eu-NaY (Eu-NaY/PS) and Eu-ZSM-5 (Eu-ZSM-5/PS) zeolites were investigated by using thermal analysis, SEM, PXRD, FT-IR, DR-UV/Vis, steady state and time-resolved photoluminescence spectroscopy. FT-IR spectra evidenced for the interaction between the zeolitic hosts and polystyrene while the PXRD spectra supported for the presence of the polymer inside the channels/pores of Eu-NaY/PS and Eu-ZSM-5/PS materials. The optical properties of Eu-NaY/PS and Eu-ZSM-5/PS were significantly changed relative to those of the parent zeolites, giving further evidence for the presence of polymer inside zeolites. An interesting case is presented by NaY zeolite: following styrene polymerization, the polymer interacted selectively with one of the two main species co-existing inside zeolite while for ZSM-5 a similar effect was not observed. Y1 - 2010 UR - http://www.rsc.org/Publishing/Journals/CP/index.asp U6 - https://doi.org/10.1039/B922591a SN - 1463-9076 ER - TY - JOUR A1 - Tiseanu, Carmen A1 - Geßner, Andre A1 - Kumke, Michael Uwe A1 - Gagea, Bogdan A1 - Parvulescu, Vasile Ion A1 - Martens, Johan T1 - Photoluminescence spectra and dynamics of lanthanide-doped microporous materials N2 - A series of terbium- and europium-exchanged microporous-mesoporous zeolite Socony Mobil Five (MFI)-type materials such as Zeotile-1 and Zeogrid with varying Si/Al ratios was investigated using FTIR, PXRD, adsorption- desorption isotherms of N-2 at 77 K and time-resolved luminescence spectroscopy. Silylation of the lanthanides-exchanged Zeotile-1 and Zeogrid with hexadecyl trimethoxysilanes via post-synthesis grafting was also studied. The results showed that the lanthanide's photoluminescence spectra and decays were modified due to silylation. The different silylation effects in Zeotile-1 and Zeogrid were correlated with the textural properties of the investigated materials. (C) 2007 Elsevier B.V. All rights reserved. Y1 - 2008 UR - http://www.sciencedirect.com/science/article/pii/S0022231307003262 U6 - https://doi.org/10.1016/j.jlumin.2007.10.018 ER - TY - JOUR A1 - Tiseanu, Carmen A1 - Kumke, Michael Uwe A1 - Pârvulescu, Vasile Ion A1 - Martens, Johan T1 - Species-related luminescence-structure relationships in europium-exchanged mesoporous material N2 - Europium exchanged into a mesoporous material (Zeotile-1) was extensively characterized with respect to the Si/ Al ratio and surface silylation by using time-resolved emission spectroscopy. Qualitative as well as quantitative details of the europium species-related luminescence-structure relationships were obtained and discussed such as the decay associated spectra, local distortion and structure of the bonding environment, crystal-field strength, radiative relaxation rates, and the quantum efficiency. Thus, two europium species were found in the parent as well as in the silylated materials: one species located on the internal surface and the second inside the 2-2.5 nm pores. The species located on the internal surface is characterized by photoluminescence decay times of 105 mu s