TY - JOUR A1 - Krüger-Genge, Anne A1 - Dietze, Stefanie A1 - Yan, Wan A1 - Liu, Yue A1 - Fang, Liang A1 - Kratz, Karl A1 - Lendlein, Andreas A1 - Jung, Friedrich T1 - Endothelial cell migration, adhesion and proliferation on different polymeric substrates JF - Clinical hemorheology and microcirculation : blood flow and vessels N2 - BACKGROUND: The formation of a functionally-confluent endothelial cell (EC) monolayer affords proliferation of EC, which only happens in case of appropriate migratory activity. AIM OF THE STUDY: The migratory pathway of human umbilical endothelial cells (HUVEC) was investigated on different polymeric substrates. MATERIAL AND METHODS: Surface characterization of the polymers was performed by contact angle measurements and atomic force microscopy under wet conditions. 30,000 HUVEC per well were seeded on polytetrafluoroethylene (PTFE) (theta(adv) = 119 degrees +/- 2 degrees), on low-attachment plate LAP (theta(adv) = 28 degrees +/- 2 degrees) and on polystyrene based tissue culture plates (TCP, theta(adv) = 22 degrees +/- 1 degrees). HUVEC tracks (trajectories) were recorded by time lapse microscopy and the euclidean distance (straight line between starting and end point), the total distance and the velocities of HUVEC not leaving the vision field were determined. RESULTS: On PTFE, 42 HUVEC were in the vision field directly after seeding. The mean length of single migration steps (SML) was 6.1 +/- 5.2 mu m, the mean velocity (MV) 0.40 +/- 0.3 mu m.min(-1) and the complete length of the trajectory (LT) was 710 +/- 440 mu m. On TCP 82 HUVEC were in the vision field subsequent to seeding. The LT was 840 +/- 550 mu m, the SML 6.1 +/- 5.2 mu m and the MV 0.44 +/- 0.3 mu m.min(-1). The trajectories on LAP differed significantly in respect to SML (2.4 +/- 3.9 mu m, p <0.05), the MV (0.16 +/- 0.3 mu m.min(-1), p <0.05) and the LT (410 +/- 300 mu m, p <0.05), compared to PTFE and TCP. Solely on TCP a nearly confluent EC monolayer developed after three days. While on TCP diffuse signals of vinculin were found over the whole basal cell surface organizing the binding of the cells by focal adhesions, on PTFE vinculin was merely arranged at the cell rims, and on the hydrophilic material (LAP) no focal adhesions were found. CONCLUSION: The study revealed that the wettability of polymers affected not only the initial adherence but also the migration of EC, which is of importance for the proliferation and ultimately the endothelialization of polymer-based biomaterials. KW - Endothelial cells KW - migration KW - polymer-based biomaterials KW - cytokine release Y1 - 2019 U6 - https://doi.org/10.3233/CH-189317 SN - 1386-0291 SN - 1875-8622 VL - 70 IS - 4 SP - 511 EP - 529 PB - IOS Press CY - Amsterdam ER - TY - JOUR A1 - Liu, Yue A1 - Razzaq, Muhammad Yasar A1 - Rudolph, Tobias A1 - Fang, Liang A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Two-Level Shape Changes of Polymeric Microcuboids Prepared from Crystallizable Copolymer Networks JF - Macromolecules : a publication of the American Chemical Society N2 - Polymeric microdevices bearing features like nonspherical shapes or spatially segregated surface properties are of increasing importance in biological and medical analysis, drug delivery, and bioimaging or microfluidic systems as well as in micromechanics, sensors, information storage, or data carrier devices. Here, a method to fabricate programmable microcuboids with shape-memory capability and the quantification of their recovery at different levels is reported. The method uses the soft lithographic technique to create microcuboids with well-defined sizes and surface properties. Microcuboids having an edge length of 25 mu m and a height of 10 mu m were prepared from cross-linked poly[ethylene-co-(vinyl acetate)] (cPEVA) with different vinyl acetate contents and were programmed by compression with various deformation degrees at elevated temperatures. The microlevel shape-recovery of the cuboidal geometry during heating was monitored by optical microscopy (OM) and atomic force microscopy (AFM) studying the related changes in the projected area (PA) or height, while the nanolevel changes of the nanosurface roughness were investigated by in situ AFM. The shape-memory effect at the microlevel was quantified by the recovery ratio of cuboids (R-r,R-micro), while at the. nanolevel, the recovery ratio of the nanoroughness (R-r,R-nano) was measured. The values of R-r,R-micro,,micro could be tailored in a range from 42 +/- 1% to 102 +/- 1% and Rr,nano from 89 +/- 6% to 136 +/- 21% depending on the applied compression ratio and the amount of vinyl acetate content in the cPEVA microcuboids. Y1 - 2017 U6 - https://doi.org/10.1021/acs.macromol.6b02237 SN - 0024-9297 SN - 1520-5835 VL - 50 SP - 2518 EP - 2527 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Liu, Yue A1 - Gould, Oliver E. C. A1 - Rudolph, Tobias A1 - Fang, Liang A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Polymeric microcuboids programmable for temperature-memory JF - Macromolecular materials and engineering N2 - Microobjects with programmable mechanical functionality are highly desirable for the creation of flexible electronics, sensors, and microfluidic systems, where fabrication/programming and quantification methods are required to fully control and implement dynamic physical behavior. Here, programmable microcuboids with defined geometries are prepared by a template-based method from crosslinked poly[ethylene-co-(vinyl acetate)] elastomers. These microobjects could be programmed to exhibit a temperature-memory effect or a shape-memory polymer actuation capability. Switching temperaturesT(sw)during shape recovery of 55 +/- 2, 68 +/- 2, 80 +/- 2, and 86 +/- 2 degrees C are achieved by tuning programming temperatures to 55, 70, 85, and 100 degrees C, respectively. Actuation is achieved with a reversible strain of 2.9 +/- 0.2% to 6.7 +/- 0.1%, whereby greater compression ratios and higher separation temperatures induce a more pronounced actuation. Micro-geometry change is quantified using optical microscopy and atomic force microscopy. The realization and quantification of microparticles, capable of a tunable temperature responsive shape-change or reversible actuation, represent a key development in the creation of soft microscale devices for drug delivery or microrobotics. KW - actuation KW - atomic force microscopy KW - biomaterials KW - microparticles KW - shape-memory polymers Y1 - 2020 U6 - https://doi.org/10.1002/mame.202000333 SN - 1438-7492 SN - 1439-2054 VL - 305 IS - 10 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Izraylit, Victor A1 - Liu, Yue A1 - Tarazona, Natalia A. A1 - Machatschek, Rainhard Gabriel A1 - Lendlein, Andreas T1 - Crystallization and degradation behaviour of multiblock copolyester blends in Langmuir monolayers JF - MRS communications / a publication of the Materials Research Society N2 - Supporting the wound healing of soft tissues requires fixation devices becoming more elastic while degrading. To address this unmet need, we designed a blend of degradable multiblock copolymers, which is cross-linked by PLA stereocomplexation combining two soft segments differing substantially in their hydrolytic degradation rate. The degradation path and concomitant structural changes are predicted by Langmuir monolayer technique. The fast hydrolysis of one soft segment leads to a decrease of the total polymer mass at constant physical cross-linking density. The corresponding increase of the average spacing between the network nodes suggests the targeted increase of the blend's flexibility. KW - Degradable KW - In situ KW - Microstructure KW - Thin film Y1 - 2021 U6 - https://doi.org/10.1557/s43579-021-00107-y SN - 2159-6859 SN - 2159-6867 VL - 11 IS - 6 SP - 850 EP - 855 PB - Springer CY - Berlin ER - TY - CHAP A1 - Sauter, Tilman A1 - Lützow, Karola A1 - Schossig, Michael A1 - Kosmella, Hans A1 - Weigel, Thomas A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Pore morphology as structural parameter to tailor the shape-memory effect of polyuetherurethane foams T2 - Abstracts of papers : joint conference / The Chemical Institute of Cananda, CIC, American Chemical Society, ACS Y1 - 2013 SN - 0065-7727 VL - 245 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Tarazona, Natalia A. A1 - Machatschek, Rainhard Gabriel A1 - Schulz, Burkhard A1 - Auxiliadora Prieto Jiménez, M. A1 - Lendlein, Andreas T1 - Molecular Insights into the Physical Adsorption of Amphiphilic Protein PhaF onto Copolyester Surfaces JF - Biomacromolecules : an interdisciplinary journal focused at the interface of polymer science and the biological sciences N2 - Phasins are amphiphilic proteins located at the polymer-cytoplasm interface of bacterial polyhydroxyalkanoates (PHA). The immobilization of phasins on biomaterial surfaces is a promising way to enhance the hydrophilicity and supply cell- directing elements in bioinstructing processes. Optimizing the physical adsorption of phasins requires deep insights into molecular processes during polymer-protein interactions to preserve their structural conformation while optimizing surface coverage. Here, the assembly, organization, and stability of phasin PhaF from Pseudomonas putida at interfaces is disclosed. The Langmuir technique, combined with in situ microscopy and spectroscopic methods, revealed that PhaF forms stable and robust monolayers at different temperatures, with an almost flat orientation of its alpha-helix at the air-water interface. PhaF adsorption onto preformed monolayers of poly[(3-R-hydroxyoctanoate)-co-(3-R-hydroxyhexanoate)] (PHOHHx), yields stable mixed layers below pi = similar to 15.7 mN/m. Further insertion induces a molecular reorganization. PHOHHx with strong surface hydrophobicity is a more adequate substrate for PhaF adsorption than the less hydrophobic poly[(rac-lactide)-co-glycolide] (PLGA). The observed orientation of the main axis of the protein in relation to copolyester interfaces ensures the best exposure of the hydrophobic residues, providing a suitable coating strategy for polymer functionalization. Y1 - 2019 U6 - https://doi.org/10.1021/acs.biomac.9b00069 SN - 1525-7797 SN - 1526-4602 VL - 20 IS - 9 SP - 3242 EP - 3252 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Hoffmann, Falk A1 - Machatschek, Rainhard Gabriel A1 - Lendlein, Andreas T1 - Understanding the impact of crystal lamellae organization on small molecule diffusion using a Monte Carlo approach JF - MRS advances : a journal of the Materials Research Society (MRS) N2 - Many physicochemical processes depend on the diffusion of small molecules through solid materials. While crystallinity in polymers is advantageous with respect to structure performance, diffusion in such materials is difficult to predict. Here, we investigate the impact of crystal morphology and organization on the diffusion of small molecules using a lattice Monte Carlo approach. Interestingly, diffusion determined with this model does not depend on the internal morphology of the semi-crystalline regions. The obtained insight is highly valuable for developing predictive models for all processes in semi-crystalline polymers involving mass transport, like polymer degradation or drug release, and provide design criteria for the time-dependent functional behavior of multifunctional polymer systems. Y1 - 2020 U6 - https://doi.org/10.1557/adv.2020.386 SN - 2059-8521 VL - 5 IS - 52-53 SP - 2737 EP - 2749 PB - Cambridge University Press CY - Cambridge ER - TY - JOUR A1 - Heilmann, Katja A1 - Groth, Thomas A1 - Schossig, Michael A1 - Lendlein, Andreas A1 - Micheel, Burkhard T1 - Modulation of hybridoma cell growth and antibody production by coating cell culture material with extracellular matrix proteins N2 - The influence of coating polystyrene tissue culture plates with different proteins on murine hybridoma cell growth and antibody production was investigated. Fibronectin, collagen I, bovine serum albumin and laminin were used to coat NUNC and COSTAR cell culture plates. Cell number and antibody concentration in culture fluids were quantified as indicators for cell viability, proliferation and productivity. Adhesive behaviour, morphology, expression of surface receptors of hybridoma cells and the presence of tyrosine-phosphorylated proteins in cell lysates were characterized by cell adhesion experiments, microscopy, flow cytometry and Western Blot analysis. It was shown that coatings with fibronectin (0.2 ;g/ml) lead to a substantial improvement of cell growth by 50-70% and an increase of monoclonal antibody production by 100-120%. Collagen I coatings showed an improvement in cell growth by 30-70% and by 60% for the production of monoclonal antibodies. Coatings with BSA and laminin had minor effects on these parameters. It was found that the hybridoma cell lines used in this study did not express the ;2-chain of the ;2;1-integrin, which is responsible for binding to collagen and laminin. However, the presence of ;1- integrin on the cell surface was shown, which should enable hybridoma cells to bind fibronectin. We propose, therefore, that fibronectin adsorption to cell culture materials may be a promising approach to enhance the production of monoclonal antibodies by cultivated hybridoma cells. Y1 - 2007 UR - http://www.sciencedirect.com/science/journal/1369703X U6 - https://doi.org/10.1016/j.bej.2007.01.035 SN - 1369-703X ER - TY - JOUR A1 - Braune, Steffen A1 - Walter, M. A1 - Schulze, F. A1 - Lendlein, Andreas A1 - Jung, Friedrich T1 - Changes in platelet morphology and function during 24 hours of storage JF - Clinical hemorheology and microcirculation : blood flow and vessels N2 - For in vitro studies assessing the interaction of platelets with implant materials, common and standardized protocols for the preparation of platelet rich plasma (PRP) are lacking, which may lead to non-matching results due to the diversity of applied protocols. Particularly, the aging of platelets during prolonged preparation and storage times is discussed to lead to an underestimation of the material thrombogenicity. Here, we study the influence of whole blood-and PRP-storage times on changes in platelet morphology and function. Whole blood PFA100 closure times increased after stimulation with collagen/ADP and collagen/epinephrine. Twenty four hours after blood collection, both parameters were prolonged pathologically above the upper limit of the reference range. Numbers of circulating platelets, measured in PRP, decreased after four hours, but no longer after twenty four hours. Mean platelet volumes (MPV) and platelet large cell ratios (P-LCR, 12 fL - 40 fL) decreased over time. Immediately after blood collection, no debris or platelet aggregates could be visualized microscopically. After four hours, first debris and very small aggregates occurred. After 24 hours, platelet aggregates and also debris progressively increased. In accordance to this, the CASY system revealed an increase of platelet aggregates (up to 90 mu m diameter)with increasing storage time. The percentage of CD62P positive platelets and PF4 increased significantly with storage time in resting PRP. When soluble ADP was added to stored PRP samples, the number of activatable platelets decreased significantly over storage time. The present study reveals the importance of a consequent standardization in the preparation of WB and PRP. Platelet morphology and function, particularly platelet reactivity to adherent or soluble agonists in their surrounding milieu, changed rapidly outside the vascular system. This knowledge is of crucial interest, particularly in the field of biomaterial development for cardiovascular applications, and may help to define common standards in the in vitro hemocompatibility testing of biomaterials. KW - Platelet KW - platelet function KW - platelet rich plasma KW - whole blood KW - platelet aging KW - platelet storage KW - hemocompatibility KW - biomaterials Y1 - 2014 U6 - https://doi.org/10.3233/CH-141876 SN - 1386-0291 SN - 1875-8622 VL - 58 IS - 1 SP - 159 EP - 170 PB - IOS Press CY - Amsterdam ER - TY - JOUR A1 - Yan, Wan A1 - Fang, Liang A1 - Nöchel, Ulrich A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Influence of deformation temperature on structural variation and shape-memory effect of a thermoplastic semi-crystalline multiblock copolymer JF - eXPRESS polymer letters N2 - A multiblock copolymer termed as PCL-PIBMD, consisting of crystallizable poly(epsilon-caprolactone) (PCL) segments and crystallizable poly(3S-isobutyl-morpholine-2,5-dione) (PIBMD) segments, has been reported as a material showing a thermally-induced shape-memory effect. While PIBMD crystalline domains act as netpoints to determine the permanent shape, both PCL crystalline domains and PIBMD amorphous domains, which have similar transition temperatures (T-trans) can act as switching domains. In this work, the influence of the deformation temperature (T-deform = 50 or 20 degrees C), which was above or below T-trans, on the structural changes of PCL-PIBMD during uniaxial deformation and the shapememory properties were investigated. Furthermore, the relative contribution of crystalline PCL and PIBMD amorphous phases to the fixation of the temporary shape were distinguished by a toluene vapor treatment approach. The results indicated that at 50 degrees C, both PCL and PIBMD amorphous phases can be orientated during deformation, resulting in thermally-induced crystals of PCL domains and joint contribution to the switching domains. In contrast at 20 degrees C, the temporary shape was mainly fixed by PCL crystals generated via strain-induced crystallization. KW - biodegradable polymers KW - shape-memory polymer KW - multiblock copolymer KW - polydepsipeptide Y1 - 2015 U6 - https://doi.org/10.3144/expresspolymlett.2015.58 SN - 1788-618X VL - 9 IS - 7 SP - 624 EP - 635 PB - Budapest University of Technology and Economics, Department of Polymer Engineering CY - Budapest ER - TY - JOUR A1 - Schöne, Anne-Christin A1 - Schulz, Burkhard A1 - Richau, Klaus A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Characterization of Langmuir films prepared from copolyesterurethanes based on oligo(omega-pentadecalactone) and oligo(epsilon-caprolactone)segments JF - Macromolecular chemistry and physics N2 - A series of multiblock copolymers (PDLCL) synthesized from oligo(omega-pentadecalactone) diol (OPDL) and oligo(epsilon-caprolactone) diol (OCL), which are linked by 2,2(4), 4-trimethyl-hexamethylene diisocyanate (TMDI), is investigated by the Langmuir monolayer technique at the air-water interface. Brewster angle microscopy (BAM) and spectroscopic ellipsometry are employed to characterize the polymer film morphologies in situ. PDLCL containing >= 40 wt% OCL segments form homogeneous Langmuir monofilms after spreading. The film elasticity modulus decreases with increasing amounts of OPDL segments in the copolymer. In contrast, the OCL-free polyesterurethane OPDL-TMDI cannot be spread to monomolecular films on the water surface properly, and movable slabs are observed by BAM even at low surface pressures. The results of the in situ morphological characterization clearly show that essential information concerning the reliability of Langmuir monolayer degradation (LMD) experiments cannot be obtained from the evaluation of the pi-A isotherms only. Consequently, in situ morphological characterization turns out to be indispensable for characterization of Langmuir layers before LMD experiments. KW - brewster angle microscopy KW - ellipsometry KW - Langmuir layers KW - morphology KW - polyesterurethanes Y1 - 2014 U6 - https://doi.org/10.1002/macp.201400377 SN - 1022-1352 SN - 1521-3935 VL - 215 IS - 24 SP - 2437 EP - 2445 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Reiche, Jürgen A1 - Kratz, Karl A1 - Hofmann, Dieter A1 - Lendlein, Andreas T1 - Current status of Langmuir monolayer degradation of polymeric biomaterials JF - The international journal of artificial organs N2 - Langmuir monolayer degradation (LMD) experiments with polymers possessing outstanding biomedical application potential yield information regarding the kinetics of their hydrolytic or enzymatic chain scission under well-defined and adjustable degradation conditions. A brief review is given of LMD investigations, including the author's own work on 2-dimensional (2D) polymer systems, providing chain scission data, which are not disturbed by simultaneously occurring transport phenomena, such as water penetration into the sample or transport of scission fragments out of the sample. A knowledge-based approach for the description and simulation of polymer hydrolytic and enzymatic degradation based on a combination of fast LMD experiments and computer simulation of the water penetration is briefly introduced. Finally, the advantages and disadvantages of this approach are discussed. KW - Monolayer KW - Hydrolytic degradation KW - Enzymatic degradation KW - Biomaterial KW - Degradable polymer Y1 - 2011 U6 - https://doi.org/10.5301/IJAO.2011.6401 SN - 0391-3988 VL - 34 IS - 2 SP - 123 EP - 128 PB - Wichtig CY - Milano ER - TY - JOUR A1 - Tartivel, Lucile A1 - Behl, Marc A1 - Schröter, Michael A1 - Lendlein, Andreas T1 - Hydrogel networks based on ABA triblock copolymers JF - Journal of applied biomaterials & functional materials N2 - Background: Triblock copolymers from hydrophilic oligo(ethylene glycol) segment A and oligo(propylene glycol) segment B, providing an ABA structure (OEG-OPG-OEG triblock), are known to be biocompatible and are used as self-solidifying gels in drug depots. A complete removal of these depots would be helpful in cases of undesired side effects of a drug, but this remains a challenge as they liquefy below their transition temperature. Therefore we describe the synthesis of covalently cross-linked hydrogel networks. Method: Triblock copolymer-based hydrogels were created by irradiating aqueous solutions of the corresponding macro-dimethacrylates with UV light. The degree of swelling, swelling kinetics, mechanical properties and morphology of the networks were investigated. Results: Depending on precursor concentration, equilibrium degree of swelling of the films ranged between 500% and 880% and was reached in 1 hour. In addition, values for storage and loss moduli of the hydrogel networks were in the 100 Pa to 10 kPa range. Conclusion: Although OEG-OPG-OEG triblocks are known for their micellization, which could hamper polymer network formation, reactive OEG-OPG-OEG triblock oligomers could be successfully polymerized into hydrogel networks. The degree of swelling of these hydrogels depends on their molecular weight and on the oligomer concentration used for hydrogel preparation. In combination with the temperature sensitivity of the ABA triblock copolymers, it is assumed that such hydrogels might be beneficial for future medical applications -e.g., removable drug release systems. KW - Hydrogel KW - Rheological characterization KW - Oligo(ethylene glycol) derivatization KW - OEG-OPG-OEG triblock copolymer KW - UV crosslinking Y1 - 2012 U6 - https://doi.org/10.5301/JABFM.2012.10295 SN - 2280-8000 VL - 10 IS - 3 SP - 243 EP - 248 PB - Wichtig CY - Milano ER - TY - JOUR A1 - Schöne, Anne-Christin A1 - Richau, Klaus A1 - Kratz, Karl A1 - Schulz, Burkhard A1 - Lendlein, Andreas T1 - Influence of Diurethane Linkers on the Langmuir Layer Behavior of Oligo[(rac-lactide)-co-glycolide]-based Polyesterurethanes JF - Macromolecular rapid communications N2 - Three oligo[(rac-lactide)-co-glycolide] based polyesterurethanes (OLGA-PUs) containing different diurethane linkers are investigated by the Langmuir monolayer technique and compared to poly[(rac-lactide)-co-glycolide] (PLGA) to elucidate the influence of the diurethane junction units on hydrophilicity and packing motifs of these polymers at the air-water interface. The presence of diurethane linkers does not manifest itself in the Langmuir layer behavior both in compression and expansion experiments when monomolecular films of OLGA-PUs are spread on the water surface. However, the linker retard the evolution of morphological structures at intermediate compression level under isobaric conditions (with a surface pressure greater than 11 mN m(-1)) compared to the PLGA, independent on the chemical structure of the diurethane moiety. The layer thicknesses of both OLGA-PU and PLGA films decrease in the high compression state with decreasing surface pressure, as deduced from ellipsometric data. All films must be described with the effective medium approximation as water swollen layers. KW - Brewster angle microscopy KW - Langmuir monolayer KW - poly[(rac-lactide)-co-glycolide] KW - polyesterurethanes KW - spectroscopic ellipsometry Y1 - 2015 U6 - https://doi.org/10.1002/marc.201500316 SN - 1022-1336 SN - 1521-3927 VL - 36 IS - 21 SP - 1910 EP - 1915 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Wang, Li A1 - Baudis, Stefan A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Characterization of bi-layered magnetic nanoparticles synthesized via two-step surface-initiated ring-opening polymerization JF - Pure and applied chemistry : official journal of the International Union of Pure and Applied Chemistry N2 - A versatile strategy to integrate multiple functions in a polymer based material is the formation of polymer networks with defined nanostructures. Here, we present synthesis and comprehensive characterization of covalently surface functionalized magnetic nanoparticles (MNPs) comprising a bi-layer oligomeric shell, using Sn(Oct)(2) as catalyst for a two-step functionalization. These hydroxy-terminated precursors for degradable magneto-and thermo-sensitive polymer networks were prepared via two subsequent surfaceinitiated ring-opening polymerizations (ROPs) with omega-pentadecalactone and e-caprolactone. A two-step mass loss obtained in thermogravimetric analysis and two distinct melting transitions around 50 and 85 degrees C observed in differential scanning calorimetry experiments, which are attributed to the melting of OPDL and OCL crystallites, confirmed a successful preparation of the modified MNPs. The oligomeric coating of the nanoparticles could be visualized by transmission electron microscopy. The investigation of degrafted oligomeric coatings by gel permeation chromatography and H-1-NMR spectroscopy showed an increase in number average molecular weight as well as the presence of signals related to both of oligo(omega-pentadecalactone) (OPDL) and oligo(e-caprolactone) (OCL) after the second ROP. A more detailed analysis of the NMR results revealed that only a few.-pentadecalactone repeating units are present in the degrafted oligomeric bi-layers, whereby a considerable degree of transesterification could be observed when OPDL was polymerized in the 2nd ROP step. These findings are supported by a low degree of crystallinity for OPDL in the degrafted oligomeric bi-layers obtained in wide angle X-ray scattering experiments. Based on these findings it can be concluded that Sn(Oct)(2) was suitable as catalyst for the preparation of nanosized bi-layered coated MNP precursors by a two-step ROP. KW - degradable polyester KW - magnetic nanoparticles KW - nanoparticle characterization KW - NICE-2014 KW - ring opening polymerization KW - surface functionalization Y1 - 2015 U6 - https://doi.org/10.1515/pac-2015-0607 SN - 0033-4545 SN - 1365-3075 VL - 87 IS - 11-12 SP - 1085 EP - 1097 PB - De Gruyter CY - Berlin ER - TY - GEN A1 - Jiang, Yi A1 - Mansfeld, Ulrich A1 - Fang, Liang A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Temperature-induced evolution of microstructures on poly[ethylene-co-(vinyl acetate)] substrates switches their underwater wettability T2 - Postprints der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe N2 - Material surfaces with tailored aerophobicity are crucial for applications where gas bubble wettability has to be controlled, e.g., gas storage and transport, electrodes, bioreactors or medical devices. Here, we present switchable underwater aerophobicity of hydrophobic polymeric substrates, which respond to heat with multilevel micro- and nanotopographical changes. The cross-linked poly[ethylene-co-(vinyl acetate)] substrates possess arrays of microcylinders with a nanorough top surface. It is hypothesized that the specific micro-/nanotopography of the surface allows trapping of a water film at the micro interspace and in this way generates the aerophobic behavior. The structured substrates were programmed to a temporarily stable, nanoscale flat substrate showing aerophilic behavior. Upon heating, the topographical changes caused a switch in contact angle from aerophilic to aerophobic for approaching air bubbles. In this way, the initial adhesion of air bubbles to the programmed flat substrate could be turned into repellence for the recovered substrate surface. The temperature at which the repellence of air bubbles starts can be adjusted from 58 ± 3 °C to 73 ± 3 °C by varying the deformation temperature applied during the temperature-memory programming procedure. The presented actively switching polymeric substrates are attractive candidates for applications, where an on-demand gas bubble repellence is advantageous. T3 - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe - 639 KW - aerophobicity KW - temperature-memory effect KW - switchable wettability KW - air bubble repellence KW - thermo-responsive polymer Y1 - 2019 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-424601 SN - 1866-8372 IS - 639 ER - TY - JOUR A1 - Tetali, Sarada D. A1 - Jankowski, Vera A1 - Luetzow, Karola A1 - Kratz, Karl A1 - Lendlein, Andreas A1 - Jankowski, Joachim T1 - Adsorption capacity of poly(ether imide) microparticles to uremic toxins JF - Clinical hemorheology and microcirculation : blood flow and vessels N2 - Uremia is a phenomenon caused by retention of uremic toxins in the plasma due to functional impairment of kidneys in the elimination of urinary waste products. Uremia is presently treated by dialysis techniques like hemofiltration, dialysis or hemodiafiltration. However, these techniques in use are more favorable towards removing hydrophilic than hydrophobic uremic toxins. Hydrophobic uremic toxins, such as hydroxy hipuric acid (OH-HPA), phenylacetic acid (PAA), indoxyl sulfate (IDS) and p-cresylsulfate (pCRS), contribute substantially to the progression of chronic kidney disease (CKD) and cardiovascular disease. Therefore, objective of the present study is to test adsorption capacity of highly porous microparticles prepared from poly(ether imide) (PEI) as an alternative technique for the removal of uremic toxins. Two types of nanoporous, spherically shaped microparticles were prepared from PEI by a spraying/coagulation process. PEI particles were packed into a preparative HPLC column to which a mixture of the four types of uremic toxins was injected and eluted with ethanol. Eluted toxins were quantified by analytical HPLC. PEI particles were able to adsorb all four toxins, with the highest affinity for PAA and pCR. IDS and OH-HPA showed a partially non-reversible binding. In summary, PEI particles are interesting candidates to be explored for future application in CKD. KW - Adsorption of uremic toxins KW - chronic kidney disease (CKD) KW - hydrophobic uremic toxins KW - poly(ether imide) KW - microparticles KW - uremia Y1 - 2016 U6 - https://doi.org/10.3233/CH-152026 SN - 1386-0291 SN - 1875-8622 VL - 61 SP - 657 EP - 665 PB - IOS Press CY - Amsterdam ER - TY - JOUR A1 - Kumar, Reddi K. A1 - Basu, Sayantani A1 - Lemke, Horst-Dieter A1 - Jankowski, Joachim A1 - Kratz, Karl A1 - Lendlein, Andreas A1 - Tetali, Sarada D. T1 - Effect of extracts of poly(ether imide) microparticles on cytotoxicity, ROS generation and proinflammatory effects on human monocytic (THP-1) cells JF - Clinical hemorheology and microcirculation : blood flow and vessels N2 - A high cell viability of around 99 +/- 18% and 99 +/- 5% was observed when THP-1 cells were cultured in the presence of aqueous extracts of the PEI microparticles in medium A and medium B respectively. The obtained microscopic data suggested that PEI particle extracts have no significant effect on cell death, oxidative stress or differentiation to macrophages. It was further found that the investigated proinflammatory markers in THP-1 cells were not up-regulated. These results are promising with regard to the biocompatibility of PEI microparticles and in a next step the hemocompatibility of the microparticles will be examined. KW - Chronic kidney disease (CKD) KW - cytotoxicity KW - human monocytic (THP-1) cells KW - poly(ether imide) microparticles KW - reactive oxygen species (ROS) Y1 - 2016 U6 - https://doi.org/10.3233/CH-152027 SN - 1386-0291 SN - 1875-8622 VL - 61 SP - 667 EP - 680 PB - IOS Press CY - Amsterdam ER - TY - JOUR A1 - Schöne, Anne-Christin A1 - Schulz, Burkhard A1 - Lendlein, Andreas T1 - Stimuli Responsive and Multifunctional Polymers: Progress in Materials and Applications JF - Macromolecular rapid communications Y1 - 2016 U6 - https://doi.org/10.1002/marc.201600650 SN - 1022-1336 SN - 1521-3927 VL - 37 SP - 1856 EP - 1859 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Fang, Liang A1 - Yan, Wan A1 - Nöchel, Ulrich A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Programming structural functions in phase-segregated polymers by implementing a defined thermomechanical history JF - Polymer : the international journal for the science and technology of polymers N2 - Unwanted shrinkage behaviors or failure in structural functions such as mechanical strength or deformability of polymeric products related to their thermomechanical history are a major challenge in production of plastics. Here, we address the question whether we can turn this challenge into an opportunity by creating defined thermomechanical histories in polymers, represented by a specific morphology and nanostructure, to equip polymeric shaped bodies with desired functions, e.g. a temperature-memory, by hot, warm or cold deformation into multiblock copolymers having two partially overlapping melting transitions. A copolyesterurethane named PDLCL, consisting of poly(epsilon-caprolactone) (PCL) and poly(omega-pentadecalactone) (PPDL) crystalline domains, exhibiting a pronounced phase-segregated morphology and partially overlapping melting transitions was selected for this study. Different types of PCL and PPDL crystals as well as distinct degrees of orientation in both amorphous and crystalline domains were obtained after deformation at 20 or 40 degrees C and to a lower extent at 60 degrees C. The generated non-isotropic structures were stable at ambient temperature and represent the different stresses stored. Stress-free heating experiments showed that the relaxation in both amorphous and crystalline phases occurred predominantly with melting of PCL crystals. When the switching temperature, which was similar to the applied deformation temperature (temperature-memory), was exceeded in stress-free heating experiments, the implemented thermomechanical history could be reversed. In contrast, during constant-strain heating to 60 degrees C the generated structural features remained almost unchanged. These findings provide insights about the structure function relation in multiblock copolymers with two crystalline phases exhibiting a temperature-memory effect by implementation of specific thermomechanical histories, which might be a general principle for tailoring other functions like mechanical strength or deformability in polymers. (C) 2016 Elsevier Ltd. All rights reserved. KW - Temperature-memory effect KW - Phase morphology KW - Thermomechanical history Y1 - 2016 U6 - https://doi.org/10.1016/j.polymer.2016.08.105 SN - 0032-3861 SN - 1873-2291 VL - 102 SP - 54 EP - 62 PB - Elsevier CY - Oxford ER - TY - JOUR A1 - Schöne, Anne-Christin A1 - Kratz, Karl A1 - Schulz, Burkhard A1 - Lendlein, Andreas T1 - The relevance of hydrophobic segments in multiblock copolyesterurethanes for their enzymatic degradation at the air-water interface JF - Polymer : the international journal for the science and technology of polymers N2 - The interplay of an enzyme with a multiblock copolymer PDLCL containing two segments of different hydrophilicity and degradability is explored in thin films at the air-water interface. The enzymatic degradation was studied in homogenous Langmuir monolayers, which are formed when containing more than 40 wt% oligo(epsilon-caprolactone) (OCL). Enzymatic degradation rates were significantly reduced with increasing content of hydrophobic oligo(omega-pentadecalactone) (OPDL). The apparent deceleration of the enzymatic process is caused by smaller portion of water-soluble degradation fragments formed from degradable OCL fragments. Beside the film degradation, a second competing process occurs after adding lipase from Pseudomonas cepacia into the subphase, namely the enrichment of the lipase molecules in the polymeric monolayer. The incorporation of the lipase into the Langmuir film is experimentally revealed by concurrent surface area enlargement and by Brewster angle microscopy (BAM). Aside from the ability to provide information about the degradation behavior of polymers, the Langmuir monolayer degradation (LMD) approach enables to investigate polymer-enzyme interactions for non-degradable polymers. (C) 2016 Elsevier Ltd. All rights reserved. KW - Multiblock copolymer KW - Enzymatic polymer degradation KW - Oligo(omega-pentadecalactone) KW - Oligo(epsilon-caprolactone) KW - Langmuir monolayer degradation technique Y1 - 2016 U6 - https://doi.org/10.1016/j.polymer.2016.09.001 SN - 0032-3861 SN - 1873-2291 VL - 102 SP - 92 EP - 98 PB - Elsevier CY - Oxford ER - TY - JOUR A1 - Schöne, Anne-Christin A1 - Kratz, Karl A1 - Schulz, Burkhard A1 - Lendlein, Andreas T1 - Polymer architecture versus chemical structure as adjusting tools for the enzymatic degradation of oligo(epsilon-caprolactone) based films at the air-water interface JF - Polymer Degradation and Stability N2 - The enzymatic degradation of oligo(epsilon-caprolactone) (OCL) based films at the air-water interface is investigated by Langmuir monolayer degradation (LMD) experiments to elucidate the influence of the molecular architecture and of the chemical structure on the chain scission process. For that purpose, the interactions of 2D monolayers of two star-shaped poly(epsilon-caprolactone)s (PCLs) and three linear OCL based copolyesterurethanes (P(OCL-U)) with the lipase from Pseudomonas cepacia are evaluated in comparison to linear OCL. While the architecture of star-shaped PCL Langmuir layers slightly influences their degradability compared to OCL films, significantly retarded degradations are observed for P(OCL-U) films containing urethane junction units derived from 2, 2 (4), 4-trimethyl hexamethylene diisocyanate (TMDI), hexamethylene diisocyanate (HDI) or lysine ethyl ester diisocyanate (LDI). The enzymatic degradation of the OCL based 2D structures is related to the presence of hydrophilic groups within the macromolecules rather than to the packing density of the film or to the molecular weight. The results reveal that the LMD technique allows the parallel analysis of both the film/enzyme interactions and the degradation process on the molecular level. (C) 2016 Elsevier Ltd. All rights reserved. KW - Langmuir technique KW - Oligo(epsilon-caprolactone) KW - Enzymatic degradation KW - Polymer architecture Y1 - 2016 U6 - https://doi.org/10.1016/j.polymdegradstab.2016.07.010 SN - 0141-3910 SN - 1873-2321 VL - 131 SP - 114 EP - 121 PB - Elsevier CY - Oxford ER - TY - JOUR A1 - Yan, Wan A1 - Fang, Liang A1 - Nöchel, Ulrich A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Influence of programming strain rates on the shape-memory performance of semicrystalline multiblock copolymers JF - Journal of polymer science : B, Polymer physics N2 - Multiblock copolymers named PCL-PIBMD consisting of crystallizable poly(epsilon-caprolactone) segments and crystallizable poly[oligo(3S-iso-butylmorpholine-2,5-dione)] segments coupled by trimethyl hexamethylene diisocyanate provide a versatile molecular architecture for achieving shape-memory effects (SMEs) in polymers. The mechanical properties as well as the SME performance of PCL-PIBMD can be tailored by the variation of physical parameters during programming such as deformation strain or applied temperature protocols. In this study, we explored the influence of applying different strain rates during programming on the resulting nanostructure of PCL-PIBMD. Programming was conducted at 50 degrees C by elongation to epsilon(m)=50% with strain rates of 1 or 10 or 50 mmmin(-1). The nanostructural changes were visualized by atomic force microscopy (AFM) measurements and investigated by in situ wide and small angle X-ray scattering experiments. With increasing the strain rate, a higher degree of orientation was observed in the amorphous domains. Simultaneously the strain-induced formation of new PIBMD crystals as well as the fragmentation of existing large PIBMD crystals occurred. The observed differences in shape fixity ratio and recovery stress of samples deformed with various strain rates can be attributed to their different nanostructures. The achieved findings can be relevant parameters for programming the shape-memory polymers with designed recovery forces. (c) 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2016, 54, 1935-1943 KW - atomic force microscopy (AFM) KW - crystal structures KW - crystallization KW - multiblock copolymer KW - stimuli-sensitive polymers KW - SAXS KW - shape-memory effect KW - WAXS KW - X-ray scattering Y1 - 2016 U6 - https://doi.org/10.1002/polb.24097 SN - 0887-6266 SN - 1099-0488 VL - 54 SP - 1935 EP - 1943 PB - Wiley-Blackwell CY - Hoboken ER - TY - JOUR A1 - Braune, Steffen A1 - Gross, M. A1 - Walter, M. A1 - Zhou, Shengqiang A1 - Dietze, Siegfried A1 - Rutschow, S. A1 - Lendlein, Andreas A1 - Tschoepe, C. A1 - Jung, Friedrich T1 - Adhesion and activation of platelets from subjects with coronary artery disease and apparently healthy individuals on biomaterials JF - Journal of biomedical materials research : an official journal of the Society for Biomaterials, the Japanese Society for Biomaterials; the Australian Society for Biomaterials N2 - On the basis of the clinical studies in patients with coronary artery disease (CAD) presenting an increased percentage of activated platelets, we hypothesized that hemocompatibility testing utilizing platelets from healthy individuals may result in an underestimation of the materials' thrombogenicity. Therefore, we investigated the interaction of polymer-based biomaterials with platelets from CAD patients in comparison to platelets from apparently healthy individuals. In vitro static thrombogenicity tests revealed that adherent platelet densities and total platelet covered areas were significantly increased for the low (polydimethylsiloxane, PDMS) and medium (Collagen) thrombogenic surfaces in the CAD group compared to the healthy subjects group. The area per single platelet—indicating the spreading and activation of the platelets—was markedly increased on PDMS treated with PRP from CAD subjects. This could not be observed for collagen or polytetrafluoroethylene (PTFE). For the latter material, platelet adhesion and surface coverage did not differ between the two groups. Irrespective of the substrate, the variability of these parameters was increased for CAD patients compared to healthy subjects. This indicates a higher reactivity of platelets from CAD patients compared to the healthy individuals. Our results revealed, for the first time, that utilizing platelets from apparently healthy donors bears the risk of underestimating the thrombogenicity of polymer-based biomaterials. KW - platelets KW - biomaterials KW - hemocompatibility KW - cardiovascular disease KW - cardiovascular implant Y1 - 2016 U6 - https://doi.org/10.1002/jbm.b.33366 SN - 1552-4973 SN - 1552-4981 VL - 104 SP - 210 EP - 217 PB - Wiley-Blackwell CY - Hoboken ER - TY - JOUR A1 - Braune, Steffen A1 - Froehlich, G. M. A1 - Lendlein, Andreas A1 - Jung, Friedrich T1 - Effect of temperature on platelet adherence JF - Clinical hemorheology and microcirculation : blood flow and vessels N2 - BACKGROUND: Thrombogenicity is one of the main parameters tested in vitro to evaluate the hemocompatibility of artificial surfaces. While the influence of the temperature on platelet aggregation has been addressed by several studies, the temperature influence on the adherence of platelets to body foreign surfaces as an important aspect of biomedical device handling has not yet been explored. Therefore, we analyzed the influence of two typically applied incubation-temperatures (22 degrees C and 37 degrees C) on the adhesion of platelets to biomaterials. MATERIAL AND METHODS: Thrombogenicity of three different polymers - medical grade poly(dimethyl siloxane) (PDMS), polytetrafluoroethylene (PTFE) and polyethylene terephthalate (PET) - were studied in an in vitro static test. Platelet adhesion was studied with stringently characterized blood from apparently healthy subjects. Collection of whole blood and preparation of platelet rich plasma (PRP) was carried out at room temperature (22 degrees C). PRP was incubated with the polymers either at 22 degrees C or 37 degrees C. Surface adherent platelets were fixed, fluorescently labelled and assessed by an image-based approach. RESULTS AND DISCUSSION: Differences in the density of adherent platelets after incubation at 22 degrees C and 37 degrees C occurred on PDMS and PET. Similar levels of adherent platelets were observed on the very thrombogenic PTFE. The covered surface areas per single platelet were analyzed to measure the state of platelet activation and revealed no differences between the two incubation temperatures for any of the analyzed polymers. Irrespective of the observed differences between the low and medium thrombogenic PDMS and PET and the higher variability at 22 degrees C, the thrombogenicity of the three investigated polymers was evaluated being comparable at both incubation temperatures. KW - Biomaterial KW - thrombogenicity KW - platelet adhesion KW - platelet activation KW - temperature Y1 - 2016 U6 - https://doi.org/10.3233/CH-152028 SN - 1386-0291 SN - 1875-8622 VL - 61 SP - 681 EP - 688 PB - IOS Press CY - Amsterdam ER - TY - JOUR A1 - Bhaskar, Thanga Bhuvanesh Vijaya A1 - Ma, Nan A1 - Lendlein, Andreas A1 - Roch, Toralf T1 - The interaction of human macrophage subsets with silicone as a biomaterial JF - Clinical hemorheology and microcirculation : blood flow and vessels N2 - Silicones are widely used as biomaterials for medical devices such as extracorporeal equipments. However, there is often conflicting evidence about their supposed cell-and histocompatibility. Macrophages could mediate silicone-induced adverse responses such as foreign body reaction and fibrous encapsulation. The polarization behaviour of macrophages could determine the clinical outcome after implantation of biomaterials. Induction of classically activated macrophages (CAM) may induce and support uncontrolled inflammatory responses and undesired material degradation. In contrast, polarization into alternatively activated macrophages (AAM) is assumed to support healing processes and implant integration. This study compared the interaction of non-polarized macrophages (M0), CAM, and AAM with commercially available tissue culture polystyrene (TCP) and a medical grade silicone-based biomaterial, regarding the secretion of inflammatory mediators such as cytokines and chemokines. Firstly, by using the Limulus amoebocyte lysate (LAL) test the silicone films were shown to be free of soluble endotoxins, which is the prerequisite to investigate their interaction with primary immune cells. Primary human monocyte-derived macrophages (M0) were polarized into CAM and AAM by addition of suitable differentiation factors. These macrophage subsets were incubated on the materials for 24 hours and their viability and cytokine secretion was assessed. In comparison to TCP, cell adhesion was lower on silicone after 24 hours for all three macrophage subsets. However, compared to TCP, silicone induced higher levels of certain inflammatory and chemotactic cytokines in M0, CAM, and AAM macrophage subsets. Conclusively, it was shown that silicone has the ability to induce a pro-inflammatory state to different magnitudes dependent on the macrophage subsets. This priming of the macrophage phenotype by silicone could explain the incidence of severe foreign body complications observed in vivo. KW - Biomaterials KW - silicone KW - macrophage subsets KW - cytokines/chemokines Y1 - 2015 U6 - https://doi.org/10.3233/CH-151991 SN - 1386-0291 SN - 1875-8622 VL - 61 IS - 2 SP - 119 EP - 133 PB - IOS Press CY - Amsterdam ER - TY - JOUR A1 - Roch, Toralf A1 - Kratz, Karl A1 - Ma, Nan A1 - Lendlein, Andreas T1 - Polymeric inserts differing in their chemical composition as substrates for dendritic cell cultivation JF - Clinical hemorheology and microcirculation : blood flow and vessels N2 - Dendritic cells (DC) contribute to immunity by presenting antigens to T cells and shape the immune response by the secretion of cytokines. Due to their immune stimulatory potential DC-based therapies are promising approaches to overcome tolerance e.g. against tumors. In order to enforce the immunogenicity of DCs, they have to be matured and activated in vitro, which requires an appropriate cell culture substrate, supporting their survival expansion and activation. Since most cell culture devices are not optimized for DC growth, it is hypothesized that polymers with certain physicochemical properties can positively influence the DC cultures. With the aim to evaluate the effects that polymers with different chemical compositions have on the survival, the activation status, and the cytokine/chemokine secretion profile of DC, their interaction with polystyrene (PS), polycarbonate (PC), poly(ether imide) (PEI), and poly(styrene-co-acrylonitrile) (PSAN)-based cell culture inserts was investigated. By using this insert system, which fits exactly into 24 well cell culture plates, effects induced from the culture dish material can be excluded. The viability of untreated DC after incubation with the different inserts was not influenced by the different inserts, whereas LPS-activatedDCshowed an increased survival after cultivation on PC, PS, and PSAN compared to tissue culture polystyrene (TCP). The activation status of DC estimated by the expression of CD40, CD80, CD83, CD86 and HLA-DR expression was not altered by the different inserts in untreated DC but slightly reduced when LPS-activated DC were cultivated on PC, PS, PSAN, and PEI compared to TCP. For each polymeric cell culture insert a distinct cytokine profile could be observed. Since inserts with different chemical compositions of the inserts did not substantially alter the behavior of DC all insert systems could be considered as alternative substrate. The observed increased survival on some polymers, which showed in contrast to TCP a hydrophobic surface, could be beneficial for certain applications such as T cell expansion and activation. KW - Biomaterials KW - dendritic cells KW - cell culture device KW - amorphous polymers Y1 - 2015 U6 - https://doi.org/10.3233/CH-152004 SN - 1386-0291 SN - 1875-8622 VL - 61 IS - 2 SP - 347 EP - 357 PB - IOS Press CY - Amsterdam ER - TY - JOUR A1 - Schöne, Anne-Christin A1 - Roch, Toralf A1 - Schulz, Burkhard A1 - Lendlein, Andreas T1 - Evaluating polymeric biomaterial-environment interfaces by Langmuir monolayer techniques JF - Interface : journal of the Royal Society N2 - Polymeric biomaterials are of specific relevance in medical and pharmaceutical applications due to their wide range of tailorable properties and functionalities. The knowledge about interactions of biomaterials with their biological environment is of crucial importance for developing highly sophisticated medical devices. To achieve optimal in vivo performance, a description at the molecular level is required to gain better understanding about the surface of synthetic materials for tailoring their properties. This is still challenging and requires the comprehensive characterization of morphological structures, polymer chain arrangements and degradation behaviour. The review discusses selected aspects for evaluating polymeric biomaterial-environment interfaces by Langmuir monolayer methods as powerful techniques for studying interfacial properties, such as morphological and degradation processes. The combination of spectroscopic, microscopic and scattering methods with the Langmuir techniques adapted to polymers can substantially improve the understanding of their in vivo behaviour. KW - Langmuir monolayer KW - biodegradable polymers KW - air - water interface KW - protein Langmuir layers Y1 - 2017 U6 - https://doi.org/10.1098/rsif.2016.1028 SN - 1742-5689 SN - 1742-5662 VL - 14 PB - Royal Society CY - London ER - TY - JOUR A1 - Balk, Maria A1 - Behl, Marc A1 - Nöchel, Ulrich A1 - Lendlein, Andreas T1 - Enzymatically triggered Jack-in-the-box-like hydrogels JF - ACS applied materials & interfaces / American Chemical Society N2 - Enzymes can support the synthesis or degradation of biomacromolecules in natural processes. Here, we demonstrate that enzymes can induce a macroscopic-directed movement of microstructured hydrogels following a mechanism that we call a "Jack-in-the-box" effect. The material's design is based on the formation of internal stresses induced by a deformation load on an architectured microscale, which are kinetically frozen by the generation of polyester locking domains, similar to a Jack-in-thebox toy (i.e., a compressed spring stabilized by a closed box lid). To induce the controlled macroscopic movement, the locking domains are equipped with enzyme-specific cleavable bonds (i.e., a box with a lock and key system). As a result of enzymatic reaction, a transformed shape is achieved by the release of internal stresses. There is an increase in entropy in combination with a swelling-supported stretching of polymer chains within the microarchitectured hydrogel (i.e., the encased clown pops-up with a pre-stressed movement when the box is unlocked). This utilization of an enzyme as a physiological stimulus may offer new approaches to create interactive and enzyme-specific materials for different applications such as an optical indicator of the enzyme's presence or actuators and sensors in biotechnology and in fermentation processes. KW - enzyme KW - hydrogels KW - stimuli-sensitive materials KW - shape change KW - poly(e-caprolactone) KW - switch KW - microporous Y1 - 2021 U6 - https://doi.org/10.1021/acsami.1c00466 SN - 1944-8244 SN - 1944-8252 VL - 13 IS - 7 SP - 8095 EP - 8101 PB - American Chemical Society CY - Washington, DC ER - TY - JOUR A1 - Frieß, Fabian A1 - Lendlein, Andreas A1 - Wischke, Christian T1 - Switching microobjects from low to high aspect ratios using a shape-memory effect JF - Soft matter N2 - Spherical particles from shape-memory polymers (SMP) can be stretched to ellipsoids with high aspect ratio (AR) and temporarily stabilized. They can switch back to low AR upon thermal stimulation. Here, the creation of an alternative shape-switching capability of particles from low to high AR is introduced, where a SMP matrix from polyvinyl alcohol (PVA) is used to create crosslinked high AR particles and to program the embedded micrometer-sized particles from a second SMP (oligo(epsilon-caprolactone) micronetworks, MN) with a low switching temperature T-sw. This programming proceeds through shape-recovery of the PVA matrix, from which the MN are harvested by PVA matrix dissolution. The use of a dissolvable SMP matrix may be a general strategy to efficiently create systems with complex moving capabilities. Y1 - 2021 U6 - https://doi.org/10.1039/d1sm00947h SN - 1744-6848 VL - 17 IS - 41 SP - 9326 EP - 9331 PB - Royal Society of Chemistry CY - London ER - TY - INPR A1 - Julich-Gruner, Konstanze K. A1 - Pandit, Abhay A1 - Lendlein, Andreas T1 - Advanced Functional Polymers Addressing the Needs of Modern Medicine T2 - Macromolecular rapid communications Y1 - 2015 U6 - https://doi.org/10.1002/marc.201500575 SN - 1022-1336 SN - 1521-3927 VL - 36 IS - 21 SP - 1859 EP - 1861 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Lau, Skadi A1 - Gossen, Manfred A1 - Lendlein, Andreas T1 - Designing cardiovascular implants taking in view the endothelial basement membrane JF - International journal of molecular sciences N2 - Insufficient endothelialization of cardiovascular grafts is a major hurdle in vascular surgery and regenerative medicine, bearing a risk for early graft thrombosis. Neither of the numerous strategies pursued to solve these problems were conclusive. Endothelialization is regulated by the endothelial basement membrane (EBM), a highly specialized part of the vascular extracellular matrix. Thus, a detailed understanding of the structure-function interrelations of the EBM components is fundamental for designing biomimetic materials aiming to mimic EBM functions. In this review, a detailed description of the structure and functions of the EBM are provided, including the luminal and abluminal interactions with adjacent cell types, such as vascular smooth muscle cells. Moreover, in vivo as well as in vitro strategies to build or renew EBM are summarized and critically discussed. The spectrum of methods includes vessel decellularization and implant biofunctionalization strategies as well as tissue engineering-based approaches and bioprinting. Finally, the limitations of these methods are highlighted, and future directions are suggested to help improve future design strategies for EBM-inspired materials in the cardiovascular field. KW - endothelial cells KW - bioinstructive implants KW - vascular grafts KW - tissue KW - engineering KW - bioprinting KW - bioinspired materials KW - biological membrane KW - endothelial basement membrane KW - biomaterial Y1 - 2021 U6 - https://doi.org/10.3390/ijms222313120 SN - 1422-0067 VL - 22 IS - 23 PB - MDPI CY - Basel ER - TY - JOUR A1 - Machatschek, Rainhard Gabriel A1 - Heuchel, Matthias A1 - Lendlein, Andreas T1 - Thin-layer studies on surface functionalization of polyetherimide BT - hydrolysis versus amidation JF - Journal of materials research : JMR / Materials Research Society N2 - Among the high-performance and engineering polymers, polyimides and the closely related polyetherimide (PEI) stand out by their capability to react with nucleophiles under relatively mild conditions. By targeting the phthalimide groups in the chain backbone, post-functionalization offers a pathway to adjust surface properties such as hydrophilicity, solvent resistance, and porosity. Here, we use ultrathin PEI films on a Langmuir trough as a model system to investigate the surface functionalization with ethylene diamine and tetrakis(4-aminophenyl)porphyrin as multivalent nucleophiles. By means of AFM, Raman spectroscopy, and interfacial rheology, we show that hydrolysis enhances the chemical and mechanical stability of ultrathin films and allows for the formation of EDC/NHS-activated esters. Direct amidation of PEI was achieved in the presence of a Lewis acid catalyst, resulting in free amine groups rather than cross-linking. When comparing amidation with hydrolysis, we find a greater influence of the latter on material properties. KW - Membrane KW - Nanostructure KW - Polymer KW - Raman spectroscopy KW - Scanning probe microscopy (SPM) KW - Surface reaction KW - Thin film Y1 - 2021 U6 - https://doi.org/10.1557/s43578-021-00339-7 SN - 0884-2914 SN - 2044-5326 VL - 37 IS - 1 SP - 67 EP - 76 PB - Springer CY - Berlin ER - TY - JOUR A1 - Machatschek, Rainhard Gabriel A1 - Lendlein, Andreas T1 - Fundamental insights in PLGA degradation from thin film studies JF - Journal of controlled release : official journal of the Controlled Release Society and of the Japanese Society of Drug Delivery Systems N2 - Poly(lactide-co-glycolide)s are commercially available degradable implant materials, which are typically selected based on specifications given by the manufacturer, one of which is their molecular weight. Here, we address the question whether variations in the chain length and their distribution affect the degradation behavior of Poly[(rac-lactide)-co-glycolide]s (PDLLGA). The hydrolysis was studied in ultrathin films at the air-water interface in order to rule out any morphological effects. We found that both for purely hydrolytic degradation as well as under enzymatic catalysis, the molecular weight has very little effect on the overall degradation kinetics of PDLLGAs. The quantitative analysis suggested a random scission mechanism. The monolayer experiments showed that an acidic micro-pH does not accelerate the degradation of PDLLGAs, in contrast to alkaline conditions. The degradation experiments were combined with interfacial rheology measurements, which showed a drastic decrease of the viscosity at little mass loss. The extrapolated molecular weight behaved similar to the viscosity, dropping to a value near to the solubility limit of PDLLGA oligomers before mass loss set in. This observation suggests a solubility controlled degradation of PDLLGA. Conclusively, the molecular weight affects the degradation of PDLLGA devices mostly in indirect ways, e.g. by determining their morphology and porosity during fabrication. Our study demonstrates the relevance of the presented Langmuir degradation method for the design of controlled release systems. KW - PDLLGA KW - Degradation KW - Langmuir monolayer Y1 - 2019 U6 - https://doi.org/10.1016/j.jconrel.2019.12.044 SN - 0168-3659 SN - 1873-4995 VL - 319 SP - 276 EP - 284 PB - Elsevier CY - New York ER - TY - JOUR A1 - Wang, Weiwei A1 - Naolou, Toufik A1 - Ma, Nan A1 - Deng, Zijun A1 - Xu, Xun A1 - Mansfeld, Ulrich A1 - Wischke, Christian A1 - Gossen, Manfred A1 - Neffe, Axel T. A1 - Lendlein, Andreas T1 - Polydepsipeptide Block-Stabilized Polyplexes for Efficient Transfection of Primary Human Cells JF - Biomacromolecules : an interdisciplinary journal focused at the interface of polymer science and the biological sciences N2 - The rational design of a polyplex gene carrier aims to balance maximal effectiveness of nucleic acid transfection into cells with minimal adverse effects. Depsipeptide blocks with an M (n) similar to 5 kDa exhibiting strong physical interactions were conjugated with PEI moieties (2.5 or 10 kDa) to di- and triblock copolymers. Upon nanoparticle formation and complexation with DNA, the resulting polyplexes (sizes typically 60-150 nm) showed remarkable stability compared to PEI-only or lipoplex and facilitated efficient gene delivery. Intracellular trafficking was visualized by observing fluorescence-labeled pDNA and highlighted the effective cytoplasmic uptake of polyplexes and release of DNA to the perinuclear space. Specifically, a triblock copolymer with a middle depsipeptide block and two 10 kDa PEI swallowtail structures mediated the highest levels of transgenic VEGF secretion in mesenchymal stem cells with low cytotoxicity. These nanocarriers form the basis for a delivery platform technology, especially for gene transfer to primary human cells. Y1 - 2017 U6 - https://doi.org/10.1021/acs.biomac.7b01034 SN - 1525-7797 SN - 1526-4602 VL - 18 SP - 3819 EP - 3833 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Hommes-Schattmann, Paul J. A1 - Neffe, Axel T. A1 - Ahmad, Bilal A1 - Williams, Gareth R. A1 - Vanneaux, Valerie A1 - Menasche, Philippe A1 - Kalfa, David A1 - Lendlein, Andreas T1 - RGD constructs with physical anchor groups as polymer co-electrospinnable cell adhesives JF - Polymers for advanced technologies N2 - The tissue integration of synthetic polymers can be promoted by displaying RGD peptides at the biointerface with the objective of enhancing colonization of the material by endogenous cells. A firm but flexible attachment of the peptide to the polymer matrix, still allowing interaction with receptors, is therefore of interest. Here, the covalent coupling of flexible physical anchor groups, allowing for temporary immobilization on polymeric surfaces via hydrophobic or dipole-dipole interactions, to a RGD peptide was investigated. For this purpose, a stearate or an oligo(ethylene glycol) (OEG) was attached to GRGDS in 51-69% yield. The obtained RGD linker constructs were characterized by NMR, IR and MALDI-ToF mass spectrometry, revealing that the commercially available OEG and stearate linkers are in fact mixtures of similar compounds. The RGD linker constructs were co-electrospun with poly(p-dioxanone) (PPDO). After electrospinning, nitrogen could be detected on the surface of the PPDO fibers by X-ray photoelectron spectroscopy. The nitrogen content exceeded the calculated value for the homogeneous material mixture suggesting a pronounced presentation of the peptide on the fiber surface. Increasing amounts of RGD linker constructs in the electrospinning solution did not lead to a detection of an increased amount of peptide on the scaffold surface, suggesting inhomogeneous distribution of the peptide on the PPDO fiber surface. Human adipose-derived stem cells cultured on the patches showed similar viability as when cultured on PPDO containing pristine RGD. The fully characterized RGD linker constructs could serve as valuable tools for the further development of tissue-integrating polymeric scaffolds. Copyright (c) 2016 John Wiley & Sons, Ltd. KW - electrospinning KW - RGD peptides KW - cell adhesion KW - biofunctionalization Y1 - 2017 U6 - https://doi.org/10.1002/pat.3963 SN - 1042-7147 SN - 1099-1581 VL - 28 SP - 1312 EP - 1317 PB - Wiley CY - Hoboken ER - TY - JOUR A1 - Naolou, Toufik A1 - Lendlein, Andreas A1 - Neffe, Axel T. T1 - Amides as non-polymerizable catalytic adjuncts enable the ring-opening polymerization of lactide with ferrous acetate under mild conditions JF - Frontiers in Chemistry N2 - Sn-based catalysts are effective in the ring-opening polymerization (ROP) but are toxic. Fe(OAc)(2) used as an alternative catalyst is suitable for the ROP of lactide only at higher temperatures (>170 degrees C), associated with racemization. In the ROP of ester and amide group containing morpholinediones with Fe(OAc)(2) to polydepsipeptides at 135 degrees C, ester bonds were selectively opened. Here, it was hypothesized that ROP of lactones is possible with Fe(OAc)(2) when amides are present in the reactions mixture as Fe-ligands could increase the solubility and activity of the metal catalytic center. The ROP of lactide in the melt with Fe(OAc)(2) is possible at temperatures as low as 105 degrees C, in the presence of N-ethylacetamide or N-rnethylbenzamide as non-polymerizable catalytic adjuncts (NPCA), with high conversion (up to 99 mol%) and yield (up to 88 mol%). Polydispersities of polylactide decreased with decreasing reaction temperature to <= 1.1. NMR as well as polarimetric studies showed that no racemization occurred at reaction temperatures <= 145 degrees C. A kinetic study demonstrated a living chain-growth mechanism. MALDI analysis revealed that no side reactions (e.g., cyclization) occurred, though transesterification took place. KW - ring-opening polymerization KW - polyester KW - catalyst KW - iron KW - amide ligand Y1 - 2019 U6 - https://doi.org/10.3389/fchem.2019.00346 SN - 2296-2646 VL - 7 PB - Frontiers Research Foundation CY - Lausanne ER - TY - JOUR A1 - Piluso, Susanna A1 - Lendlein, Andreas A1 - Neffe, Axel T. T1 - Enzymatic action as switch of bulk to surface degradation of clicked gelatin-based networks JF - Polymers for advanced technologies N2 - Polymer degradation occurs under physiological conditions in vitro and in vivo, especially when bonds susceptible to hydrolysis are present in the polymer. Understanding of the degradation mechanism, changes of material properties over time, and overall rate of degradation is a necessary prerequisite for the knowledge-based design of polymers with applications in biomedicine. Here, hydrolytic degradation studies of gelatin-based networks synthesized by copper-catalyzed azide-alkyne cycloaddition reaction are reported, which were performed with or without addition of an enzyme. In all cases, networks with a stilbene as crosslinker proofed to be more resistant to degradation than when an octyl diazide was used. Without addition of an enzyme, the rate of degradation was ruled by the crosslinking density of the network and proceeded via a bulk degradation mechanism. Addition of Clostridium histolyticum collagenase resulted in a much enhanced rate of degradation, which furthermore occurred via surface erosion. The mesh size of the hydrogels (>7nm) was in all cases larger than the hydrodynamic radius of the enzyme (4.5nm) so that even in very hydrophilic networks with large mesh size enzymes may be used to induce a fast surface degradation mechanism. This observation is of general interest when designing hydrogels to be applied in the presence of enzymes, as the degradation mechanism and material performance are closely interlinked. Copyright (c) 2016 John Wiley & Sons, Ltd. KW - Hydrogel KW - Biopolymer KW - Degradation Y1 - 2017 U6 - https://doi.org/10.1002/pat.3962 SN - 1042-7147 SN - 1099-1581 VL - 28 SP - 1318 EP - 1324 PB - Wiley CY - Hoboken ER - TY - JOUR A1 - Zaupa, Alessandro A1 - Neffe, Axel T. A1 - Pierce, Benjamin F. A1 - Nöchel, Ulrich A1 - Lendlein, Andreas T1 - Influence of tyrosine-derived moieties and drying conditions on the formation of helices in gelatin JF - Biomacromolecules : an interdisciplinary journal focused at the interface of polymer science and the biological sciences N2 - The single and triple helical organization of protein chains strongly influences the mechanical properties of gelatin-based materials. A chemical method for obtaining different degrees of helical organization in gelatin is covalent functionalization, while a physical method for achieving the same goal is the variation of the drying conditions of gelatin solutions. Here we explored how the introduction of desaminotyrosine (DAT) and desaminotyrosyl tyrosine (DATT) linked to lysine residues of gelatin influenced the kinetics and thermodynamic equilibrium of the helicalization process of single and triple helices following different drying conditions. Drying at a temperature above. the helix-to-coil transition temperature of gelatin (T > T-c, called nu(short)) generally resulted in gelatins with relatively lower triple helical content (X-c,X-t = 1-2%) than lower temperature drying (T < T-c, called nu(long)) (X-c,X-t = 8-10%), where the DAT(T) functional groups generally disrupted helix formation. While different helical contents affected the thermal transition temperatures only slightly, the mechanical properties were strongly affected for swollen hydrogels (E = 4-13 kPa for samples treated by nu(long) and E = 120-700 kPa for samples treated by nu(short)). This study shows that side group functionalization and different drying conditions are viable options to control the helicalization and macroscopic properties of gelatin-based materials. Y1 - 2011 U6 - https://doi.org/10.1021/bm101029k SN - 1525-7797 VL - 12 IS - 1 SP - 75 EP - 81 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Vukicevic, Radovan A1 - Neffe, Axel T. A1 - Luetzow, Karola A1 - Pierce, Benjamin F. A1 - Lendlein, Andreas T1 - Conditional Ultrasound Sensitivity of Poly[(N-isopropylacrylamide)-co-(vinyl imidazole)] Microgels for Controlled Lipase Release JF - Macromolecular rapid communications N2 - Triggering the release of cargo from a polymer network by ultrasonication as an external, non-invasive stimulus can be an interesting concept for on-demand release. Here, it is shown that, in pH-and thermosensitive microgels, the ultrasound sensitivity of the polymer network depends on the external conditions. Crosslinked poly[(N-isopropylacrylamide)-co-(vinyl imidazole)] microgels showed a volume phase transition temperature (VPTT) of 25-50 degrees C, which increases with decreasing pH. Above the VPTT the polymer chains are collapsed, while below VPTT they are extended. Only in the case of maximum observed swelling, where the polymer chains are expanded, the microgels are mechanically fragmented through ultrasonication. In contrast, when the polymer chains are partially collapsed it is not possible to manipulate the microgels by ultrasound. Additionally, the ultrasound-induced on-demand release of wheat germ lipase from the microgels could be demonstrated successfully. The principle of conditional ultrasound sensitivity is likely to be general and can be used for selection of matrix-cargo combinations. KW - ultrasound KW - polymers KW - microgels KW - lipase release KW - controlled release KW - thermoresponsive polymers KW - biomaterials Y1 - 2015 U6 - https://doi.org/10.1002/marc.201500311 SN - 1022-1336 SN - 1521-3927 VL - 36 IS - 21 SP - 1891 EP - 1896 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Piluso, Susanna A1 - Hiebl, Bernhard A1 - Gorb, Stanislav N. A1 - Kovalev, Alexander A1 - Lendlein, Andreas A1 - Neffe, Axel T. T1 - Hyaluronic acid-based hydrogels crosslinked by copper-catalyzed azide-alkyne cycloaddition with tailorable mechanical properties JF - The international journal of artificial organs N2 - Biopolymers of the extracellular matrix are attractive starting materials for providing degradable and biocompatible biomaterials. In this study, hyaluronic acid-based hydrogels with tunable mechanical properties were prepared by the use of copper-catalyzed azide-alkyne cycloaddition (known as "click chemistry"). Alkyne-functionalized hyaluronic acid was crosslinked with linkers having two terminal azide functionalities, varying crosslinker density as well as the lengths and rigidity of the linker molecules. By variation of the crosslinker density and crosslinker type, hydrogels with elastic moduli in the range of 0.5-4 kPa were prepared. The washed materials contained a maximum of 6.8 mg copper per kg dry weight and the eluate of the gel crosslinked with diazidostilbene did not show toxic effects on L929 cells. The hyaluronic acid-based hydrogels have potential as biomaterials for cell culture or soft tissue regeneration applications. KW - Biomaterial KW - Hydrogel KW - Hyaluronic acid KW - Microindentation KW - Rheology Y1 - 2011 U6 - https://doi.org/10.5301/IJAO.2011.6394 SN - 0391-3988 VL - 34 IS - 2 SP - 192 EP - 197 PB - Wichtig CY - Milano ER - TY - JOUR A1 - Neffe, Axel T. A1 - Loebus, Axel A1 - Zaupa, Alessandro A1 - Stötzel, Christian A1 - Müller, Frank A. A1 - Lendlein, Andreas T1 - Gelatin functionalization with tyrosine derived moieties to increase the interaction with hydroxyapatite fillers JF - Acta biomaterialia N2 - Combining gelatins functionalized with the tyrosine-derived groups desaminotyrosine or desaminotyrosyl tyrosine with hydroxyapatite (HAp) led to the formation of composite materials with much lower swelling ratios than those of the pure matrices. Shifts of the infra-red (IR) bands related to the free carboxyl groups could be observed in the presence of HAp, which suggested a direct interaction of matrix and filler that formed additional physical cross-links in the material. In tensile tests and rheological measurements the composites equilibrated in water had increased Young's moduli (from 200 kPa up to 2 MPa) and tensile strengths (from 57 kPa up to 1.1 MPa) compared with the matrix polymers without affecting the elongation at break. Furthermore, an increased thermal stability of the networks from 40 to 85 degrees C could be demonstrated. The differences in the behaviour of the functionalized gelatins compared with pure gelatin as a matrix suggested an additional stabilizing bond between the incorporated aromatic groups and the HAp as supported by the IR results. The composites can potentially be applied as bone fillers. KW - Gelatin KW - Hydroxyapatite KW - Composite KW - Hydrogel KW - Biomaterial Y1 - 2011 U6 - https://doi.org/10.1016/j.actbio.2010.11.025 SN - 1742-7061 VL - 7 IS - 4 SP - 1693 EP - 1701 PB - Elsevier CY - Oxford ER - TY - JOUR A1 - Lange, Maik A1 - Braune, Steffen A1 - Luetzow, Karola A1 - Richau, Klaus A1 - Scharnagl, Nico A1 - Weinhart, Marie A1 - Neffe, Axel T. A1 - Jung, Friedrich A1 - Haag, Rainer A1 - Lendlein, Andreas T1 - Surface functionalization of poly(ether imide) membranes with linear, methylated oligoglycerols for reducing thrombogenicity JF - Macromolecular rapid communications N2 - Materials for biomedical applications are often chosen for their bulk properties. Other requirements such as a hemocompatible surface shall be fulfilled by suitable chemical functionalization. Here we show, that linear, side-chain methylated oligoglycerols (OGMe) are more stable to oxidation than oligo(ethylene glycol) (OEG). Poly(ether imide) (PEI) membranes functionalized with OGMes perform at least as good as, and partially better than, OEG functionalized PEI membranes in view of protein resistance as well as thrombocyte adhesion and activation. Therefore, OGMes are highly potent surface functionalizing molecules for improving the hemocompatibility of polymers. KW - hemocompatibility KW - poly(ethylene glycol) KW - polyglycerol KW - polyimides KW - surface chemistry Y1 - 2012 U6 - https://doi.org/10.1002/marc.201200426 SN - 1022-1336 VL - 33 IS - 17 SP - 1487 EP - 1492 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Neffe, Axel T. A1 - von Rüsten-Lange, Maik A1 - Braune, Steffen A1 - Lützow, Karola A1 - Roch, Toralf A1 - Richau, Klaus A1 - Jung, Friedrich A1 - Lendlein, Andreas T1 - Poly(ethylene glycol) grafting to Poly(ether imide) membranes - influence on protein adsorption and Thrombocyte adhesion JF - Macromolecular bioscience N2 - The chain length and end groups of linear PEG grafted on smooth surfaces is known to influence protein adsorption and thrombocyte adhesion. Here, it is explored whether established structure function relationships can be transferred to application relevant, rough surfaces. Functionalization of poly(ether imide) (PEI) membranes by grafting with monoamino PEG of different chain lengths (M-n=1kDa or 10kDa) and end groups (methoxy or hydroxyl) is proven by spectroscopy, changes of surface hydrophilicity, and surface shielding effects. The surface functionalization does lead to reduction of adsorption of BSA, but not of fibrinogen. The thrombocyte adhesion is increased compared to untreated PEI surfaces. Conclusively, rough instead of smooth polymer or gold surfaces should be investigated as relevant models. KW - biomaterials KW - poly(ethylene glycol) KW - protein adsorption KW - surface functionalization KW - thrombocyte adhesion Y1 - 2013 U6 - https://doi.org/10.1002/mabi.201300309 SN - 1616-5187 SN - 1616-5195 VL - 13 IS - 12 SP - 1720 EP - 1729 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Federico, Stefania A1 - Pierce, Benjamin F. A1 - Piluso, Susanna A1 - Wischke, Christian A1 - Lendlein, Andreas A1 - Neffe, Axel T. T1 - Design of Decorin-Based Peptides That Bind to CollagenI and their Potential as Adhesion Moieties in Biomaterials JF - Angewandte Chemie : a journal of the Gesellschaft Deutscher Chemiker ; International edition N2 - Mimicking the binding epitopes of protein-protein interactions by using small peptides is important for generating modular biomimetic systems. A strategy is described for the design of such bioactive peptides without accessible structural data for the targeted interaction, and the effect of incorporating such adhesion peptides in complex biomaterial systems is demonstrated. The highly repetitive structure of decorin was analyzed to identify peptides that are representative of the inner and outer surface, and it was shown that only peptides based on the inner surface of decorin bind to collagen. The peptide with the highest binding affinity for collagenI, LHERHLNNN, served to slow down the diffusion of a conjugated dye in a collagen gel, while its dimer could physically crosslink collagen, thereby enhancing the elastic modulus of the gel by one order of magnitude. These results show the potential of the identified peptides for the design of biomaterials for applications in regenerative medicine. KW - biomaterials KW - collagen KW - gels KW - peptides KW - protein-protein interactions Y1 - 2015 U6 - https://doi.org/10.1002/anie.201505227 SN - 1433-7851 SN - 1521-3773 VL - 54 IS - 37 SP - 10980 EP - 10984 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Naolou, Toufik A1 - Lendlein, Andreas A1 - Neffe, Axel T. T1 - Influence of metal softness on the metal-organic catalyzed polymerization of inorpholin-2,5-diones to oligodepsipeptides JF - European polymer journal Y1 - 2016 U6 - https://doi.org/10.1016/j.eurpolymj.2016.10.011 SN - 0014-3057 SN - 1873-1945 VL - 85 SP - 139 EP - 149 PB - Elsevier CY - Oxford ER - TY - JOUR A1 - Neffe, Axel T. A1 - Lendlein, Andreas T1 - Going Beyond Compromises in Multifunctionality of Biomaterials JF - Advanced healthcare materials Y1 - 2015 U6 - https://doi.org/10.1002/adhm.201400724 SN - 2192-2640 SN - 2192-2659 VL - 4 IS - 5 SP - 642 EP - 645 PB - Wiley-Blackwell CY - Hoboken ER - TY - INPR A1 - Lendlein, Andreas A1 - Neffe, Axel T. A1 - Jerome, Christine T1 - Advanced functional polymers for medicine T2 - Advanced healthcare materials Y1 - 2014 U6 - https://doi.org/10.1002/adhm.201400718 SN - 2192-2640 SN - 2192-2659 VL - 3 IS - 12 SP - 1939 EP - 1940 PB - Wiley-Blackwell CY - Hoboken ER - TY - CHAP A1 - Neffe, Axel T. A1 - Zaupa, Alessandro A1 - Lendlein, Andreas T1 - Physical crosslinking of gelatin a supramolecular approach tobiomaterial T2 - The international journal of artificial organs Y1 - 2011 SN - 0391-3988 VL - 34 IS - 8 SP - 656 EP - 656 PB - Wichtig CY - Milano ER - TY - JOUR A1 - Sarem, Melika A1 - Arya, Neha A1 - Heizmann, Miriam A1 - Neffe, Axel T. A1 - Barbero, Andrea A1 - Gebauer, Tim P. A1 - Martin, Ivan A1 - Lendlein, Andreas A1 - Shastri, V. Prasad T1 - Interplay between stiffness and degradation of architectured gelatin hydrogels leads to differential modulation of chondrogenesis in vitro and in vivo JF - Acta biomaterialia N2 - The limited capacity of cartilage to heal large lesions through endogenous mechanisms has led to extensive effort to develop materials to facilitate chondrogenesis. Although physical-chemical properties of biomaterials have been shown to impact in vitro chondrogenesis, whether these findings are translatable in vivo is subject of debate. Herein, architectured 3D hydrogel scaffolds (ArcGel) (produced by crosslinking gelatin with ethyl lysine diisocyanate (LDI)) were used as a model system to investigate the interplay between scaffold mechanical properties and degradation on matrix deposition by human articular chondrocytes (HAC) from healthy donors in vitro and in vivo. Using ArcGel scaffolds of different tensile and shear modulus, and degradation behavior; in this study, we compared the fate of ex vivo engineeredArcGels-chondrocytes constructs, i.e. the traditional tissue engineering approach, with the de novo formation of cartilaginous tissue in HAC laden ArcGels in an ectopic nude mouse model. While the softer and fast degrading ArcGel (LNCO3) was more efficient at promoting chondrogenic differentiation in vitro, upon ectopic implantation, the stiffer and slow degrading ArcGel (LNCO8) was superior in maintaining chondrogenic phenotype in HAC and retention of cartilaginous matrix. Furthermore, surprisingly the de novo formation of cartilage tissue was promoted only in LNCO8. Since HAC cultured for only three days in the LNCO8 environment showed upregulation of hypoxia-associated genes, this suggests a potential role for hypoxia in the observed in vivo outcomes. In summary, this study sheds light on how immediate environment (in vivo versus in vitro) can significantly impact the outcomes of cell-laden biomaterials. Statement of Significance In this study, 3D architectured hydrogels (ArcGels) with different mechanical and biodegradation properties were investigated for their potential to promote formation of cartilaginous matrix by human articular chondrocytes in vitro and in vivo. Two paradigms were explored (i) ex vivo engineering followed by in vivo implantation in ectopic site of nude mice and (ii) short in vitro culture (3 days) followed by implantation to induce de novo cartilage formation. Softer and fast degrading ArcGel were better at promoting chondrogenesis in vitro, while stiffer and slow degrading ArcGel were strikingly superior in both maintaining chondrogenesis in vivo and inducing de novo formation of cartilage. Our findings highlight the importance of the interplay between scaffold mechanics and degradation in chondrogenesis. KW - Cartilage repair KW - Scaffold stiffness KW - Scaffold contraction KW - Scaffold degradation KW - Matrix metalloproteinase KW - Hypoxia Y1 - 2018 U6 - https://doi.org/10.1016/j.actbio.2018.01.025 SN - 1742-7061 SN - 1878-7568 VL - 69 SP - 83 EP - 94 PB - Elsevier CY - Oxford ER - TY - JOUR A1 - Brunacci, Nadia A1 - Neffe, Axel T. A1 - Wischke, Christian A1 - Naolou, Toufik A1 - Nöchel, Ulrich A1 - Lendlein, Andreas T1 - Oligodepsipeptide (nano)carriers BT - computational design and analysis of enhanced drug loading JF - Journal of controlled release N2 - High drug loads of nanoparticles are essential to efficiently provide a desired dosage in the required timeframe, however, these conditions may not be reached with so far established degradable matrices. Our conceptual approach for increasing the drug load is based on strengthening the affinity between drug and matrix in combination with stabilizing drug-matrix-hybrids through strong intermolecular matrix interactions. Here, a method for designing such complex drug-matrix hybrids is introduced employing computational methods (molecular dynamics and docking) as well as experimental studies (affinity, drug loading and distribution, drug release from films and nanoparticles). As model system, dexamethasone (DXM), relevant for the treatment of inflammatory diseases, in combination with poly[(rac-lactide)-co-glycolide] (PLGA) as standard degradable matrix or oligo[(3-(S)-sec-butyl) morpholine-2,5-dione] diol (OBMD) as matrix with hypothesized stronger interaction with DXM were investigated. Docking studies predicted higher affinity of DXM to OBMD than PLGA and displayed amide bond participation in hydrogen bonding with OBMD. Experimental investigations on films and nanoparticles, i.e. matrices of different shapes and sizes, confirmed this phenomenon as shown e.g. by a similar to 10 times higher solid state solubility of DXM in OBMD than in PLGA. DXM-loaded particles of similar to 150 nm prepared by nanoprecipitation in aqueous environment had a drug loading (DL) up to 16 times higher when employing OBMD as matrix compared to PLGA carriers due to enhanced drug retention in the OBMD phase. Importantly, drug relase periods were not altered as the release from films and particles was mainly ruled by the diffusion length as well as matrix degradation rather than the matrix type, which can be assigned to water diffusing into the matrix and breaking up of drug-matrix hydrogen bonds. Overall, the presented design and fabrication scheme showed predictive power and might universally enable the screening of drug/matrix interactions particularly to expand the oligodepsipeptide platform technology, e.g. by varying the depsipeptide side chains, for drug carrier and release systems. KW - Oligodepsipeptide KW - Drug loading KW - Nanoparticles KW - Docking study KW - Molecular interaction design Y1 - 2019 U6 - https://doi.org/10.1016/j.jconrel.2019.03.004 SN - 0168-3659 SN - 1873-4995 VL - 301 SP - 146 EP - 156 PB - Elsevier CY - Amsterdam ER - TY - JOUR A1 - Hauser, Sandra A1 - Wodtke, Robert A1 - Tondera, Christoph A1 - Wodtke, Johanna A1 - Neffe, Axel T. A1 - Hampe, Jochen A1 - Lendlein, Andreas A1 - Löser, Reik A1 - Pietzsch, Jens T1 - Characterization of Tissue Transglutaminase as a Potential Biomarker for Tissue Response toward Biomaterials JF - ACS biomaterials science & engineering N2 - Tissue transglutaminase (TGase 2) is proposed to be important for biomaterial-tissue interactions due to its presence and versatile functions in the extracellular environment. TGase 2 catalyzes the cross-linking of proteins through its Ca2+-dependent acyltransferase activity. Moreover, it enhances the interactions between fibronectin and integrins, which in turn mediates the adhesion, migration, and motility of the cells. TGase 2 is also a key player in the pathogenesis of fibrosis. In this study, we investigated whether TGase 2 is present at the biomaterial tissue interface and might serve as an informative biomarker for the visualization of tissue response toward gelatin-based biomaterials. Two differently cross-linked hydrogels were used, which were obtained by the reaction of gelatin with lysine diisocyanate ethyl ester. The overall expression of TGase 2 by endothelial cells, macrophages, and granulocytes was partly influenced by contact to the hydrogels or their degradation products, although no clear correlation was evidenced. In contrast, the secretion of TGase 2 differed remarkably between the different cells, indicating that it might be involved in the cellular reaction toward gelatin-based hydrogels. The hydrogels were implanted subcutaneously in immunocompetent, hairless SKH1-Elite mice. Ex vivo immunohistochemical analysis of tissue sections over 112 days revealed enhanced expression of TGase 2 around the hydrogels, in particular at days 14 and 21 post-implantation. The incorporation of fluorescently labeled cadaverine derivatives for the detection of active TGase 2 was in accordance with the results of the expression analysis. The presence of an irreversible inhibitor of TGase 2 led to attenuated incorporation of the cadaverines, which verified the catalytic action of TGase 2. Our in vitro and ex vivo results verified TGase 2 as a potential biomarker for tissue response toward gelatin-based hydrogels. In vivo, no TGase 2 activity was detectable, which is mainly attributed to the unfavorable physicochemical properties of the cadaverine probe used. KW - extracellular matrix modifying enzymes KW - gelatin-based hydrogels KW - biomaterial-tissue interface KW - polyamines KW - optical imaging Y1 - 2019 U6 - https://doi.org/10.1021/acsbiomaterials.9b01299 SN - 2373-9878 VL - 5 IS - 11 SP - 5979 EP - 5989 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Zhang, Nan A1 - Said, Andre A1 - Wischke, Christian A1 - Kral, Vivian A1 - Brodwolf, Robert A1 - Volz, Pierre A1 - Boreham, Alexander A1 - Gerecke, Christian A1 - Li, Wenzhong A1 - Neffe, Axel T. A1 - Kleuser, Burkhard A1 - Alexiev, Ulrike A1 - Lendlein, Andreas A1 - Schäfer-Korting, Monika T1 - Poly[acrylonitrile-co-(N-vinyl pyrrolidone)] nanoparticles - Composition-dependent skin penetration enhancement of a dye probe and biocompatibility JF - European Journal of Pharmaceutics and Biopharmaceutics N2 - Nanoparticles can improve topical drug delivery: size, surface properties and flexibility of polymer nanoparticles are defining its interaction with the skin. Only few studies have explored skin penetration for one series of structurally related polymer particles with systematic alteration of material composition. Here, a series of rigid poly[acrylonitrile-co-(N-vinyl pyrrolidone)] model nanoparticles stably loaded with Nile Red or Rhodamin B, respectively, was comprehensively studied for biocompatibility and functionality. Surface properties were altered by varying the molar content of hydrophilic NVP from 0 to 24.1% and particle size ranged from 35 to 244 nm. Whereas irritancy and genotoxicity were not revealed, lipophilic and hydrophilic nanoparticles taken up by keratinocytes affected cell viability. Skin absorption of the particles into viable skin ex vivo was studied using Nile Red as fluorescent probe. Whilst an intact stratum corneum efficiently prevented penetration, almost complete removal of the horny layer allowed nanoparticles of smaller size and hydrophilic particles to penetrate into viable epidermis and dermis. Hence, systematic variations of nanoparticle properties allows gaining insights into critical criteria for biocompatibility and functionality of novel nanocarriers for topical drug delivery and risks associated with environmental exposure. KW - Biocompatibility testing KW - Drug delivery systems KW - Nanoparticle KW - Poly[acrylonitrile-co-(N-vinyl pyrrolidone)] KW - Polymers KW - Skin absorption Y1 - 2017 U6 - https://doi.org/10.1016/j.ejpb.2016.10.019 SN - 0939-6411 SN - 1873-3441 VL - 116 SP - 66 EP - 75 PB - Elsevier CY - Amsterdam ER - TY - JOUR A1 - Brunacci, Nadia A1 - Wischke, Christian A1 - Naolou, Toufik A1 - Neffe, Axel T. A1 - Lendlein, Andreas T1 - Influence of surfactants on depsipeptide submicron particle formation JF - European Journal of Pharmaceutics and Biopharmaceutics N2 - Surfactants are required for the formation and stabilization of hydrophobic polymeric particles in aqueous environment. In order to form submicron particles of varying sizes from oligo[3-(S)-sec-butylmorpholine-2,5-dione]diols ((OBMD)-diol), different surfactants were investigated. As new surfactants, four-armed star-shaped oligo(ethylene glycol)s of molecular weights of 5-20 kDa functionalized with desamino-tyrosine (sOEG-DAT) resulted in smaller particles with lower PDI than with desaminotyrosyl tyrosine (sOEG-DATT) in an emulsion/solvent evaporation method. In a second set of experiments, sOEG-DAT of M-n= 10 kDa was compared with the commonly employed emulsifiers polyvinylalcohol (PVA), polyoxyethylene (20) sorbitan monolaurate (Tween 20), and D-alpha-tocopherol polyethylene glycol succinate (VIT E-TPGS) for OBMD particle preparation. sOEG-DAT allowed to systematically change sizes in a range of 300 up to 900 nm with narrow polydispersity, while in the other cases, a lower size range (250-400 nm, PVA; 300 nm, Tween 20) or no effective particle formation was observed. The ability of tailoring particle size in a broad range makes sOEG-DAT of particular interest for the formation of oligodepsipeptide particles, which can further be investigated as drug carriers for controlled delivery. (C) 2016 Elsevier B.V. All rights reserved. KW - Depsipeptide KW - Particle size KW - Surfactants KW - Submicron particles Y1 - 2017 U6 - https://doi.org/10.1016/j.ejpb.2016.11.011 SN - 0939-6411 SN - 1873-3441 VL - 116 SP - 61 EP - 65 PB - Elsevier CY - Amsterdam ER - TY - JOUR A1 - Folikumah, Makafui Yao A1 - Neffe, Axel T. A1 - Behl, Marc A1 - Lendlein, Andreas T1 - Thiol Michael-Type reactions of optically active mercapto-acids in aqueous medium JF - MRS advances : a journal of the Materials Research Society N2 - Defined chemical reactions in a physiological environment are a prerequisite for the in situ synthesis of implant materials potentially serving as matrix for drug delivery systems, tissue fillers or surgical glues. ‘Click’ reactions like thiol Michael-type reactions have been successfully employed as bioorthogonal reaction. However, due to the individual stereo-electronic and physical properties of specific substrates, an exact understanding their chemical reactivity is required if they are to be used for in-situ biomaterial synthesis. The chiral (S)-2-mercapto-carboxylic acid analogues of L-phenylalanine (SH-Phe) and L-leucine (SH-Leu) which are subunits of certain collagenase sensitive synthetic peptides, were explored for their potential for in-situ biomaterial formation via the thiol Michael-type reaction. In model reactions were investigated the kinetics, the specificity and influence of stereochemistry of this reaction. We could show that only reactions involving SH-Leu yielded the expected thiol-Michael product. The inability of SH-Phe to react was attributed to the steric hindrance of the bulky phenyl group. In aqueous media, successful reaction using SH-Leu is thought to proceed via the sodium salt formed in-situ by the addition of NaOH solution, which was intented to aid the solubility of the mercapto-acid in water. Fast reaction rates and complete acrylate/maleimide conversion were only realized at pH 7.2 or higher suggesting the possible use of SH-Leu under physiological conditions for thiol Michael-type reactions. This method of in-situ formed alkali salts could be used as a fast approach to screen mercapto-acids for thio Michael-type reactions without the synthesis of their corresponding esters. KW - biomaterial KW - biomedical KW - biomimetic (chemical reaction) KW - chemical synthesis Y1 - 2019 U6 - https://doi.org/10.1557/adv.2019.308 SN - 2059-8521 VL - 4 IS - 46-47 SP - 2515 EP - 2525 PB - Springer Nature Switzerland AG CY - Cham ER - TY - JOUR A1 - Zhang, Shanshan A1 - Liu, Yue A1 - Machatschek, Rainhard Gabriel A1 - Lendlein, Andreas T1 - Ultrathin collagen type I films formed at the air-water interface JF - MRS advances : a journal of the Materials Research Society (MRS) N2 - Collagen-based biomaterials with oriented fibrils have shown great application potential in medicine. However, it is still challenging to control the type I collagen fibrillogenesis in ultrathin films. Here, we report an approach to produce cohesive and well-organized type I collagen ultrathin films of about 10 nm thickness using the Langmuir-Blodgett technique. Ellipsometry, rheology, and Brewster angle microscopy are applied to investigate in situ how the molecules behave at the air-water interface, both at room temperature and 37 degrees C. The interfacial storage modulus observed at room temperature vanishes upon heating, indicating the existence and disappearance of the network structure in the protein nanosheet. The films were spanning over holes as large as 1 mm diameter when transferred at room temperature, proving the strong cohesive interactions. A highly aligned and fibrillar structure was observed by atomic force microscopy (AFM) and optical microscopy. Y1 - 2022 U6 - https://doi.org/10.1557/s43580-021-00160-8 SN - 2059-8521 VL - 7 IS - 4 SP - 56 EP - 62 PB - Springer Nature Switzerland AG CY - Cham ER - TY - JOUR A1 - Tarazona, Natalia A. A1 - Machatschek, Rainhard Gabriel A1 - Lendlein, Andreas T1 - Unraveling the interplay between abiotic hydrolytic degradation and crystallization of bacterial polyesters comprising short and medium side-chain-length Polyhydroxyalkanoates JF - Biomacromolecules : an interdisciplinary journal focused at the interface of polymer science and the biological sciences N2 - Polyhydroxyalkanoates (PHAs) have attracted attention as degradable (co)polyesters which can be produced by microorganisms with variations in the side chain. This structural variation influences not only the thermomechanical properties of the material but also its degradation behavior. Here, we used Langmuir monolayers at the air-water (A-W) interface as suitable models for evaluating the abiotic degradation of two PHAs with different side-chain lengths and crystallinity. By controlling the polymer state (semi crystalline, amorphous), the packing density, the pH, and the degradation mechanism, we could draw several significant conclusions. (i) The maximum degree of crystallinity for a PHA film to be efficiently degraded up to pH = 12.3 is 40%. (ii) PHA made of repeating units with shorter side-chain length are more easily hydrolyzed under alkaline conditions. The efficiency of alkaline hydrolysis decreased by about 65% when the polymer was 40% crystalline. (iii) In PHA films with a relatively high initial crystallinity, abiotic degradation initiated a chemicrystallization phenomenon, detected as an increase in the storage modulus (E'). This could translate into an increase in brittleness and reduction in the material degradability. Finally, we demonstrate the stability of the measurement system for long-term experiments, which allows degradation conditions for polymers that could closely simulate real-time degradation. Y1 - 2019 U6 - https://doi.org/10.1021/acs.biomac.9b01458 SN - 1525-7797 SN - 1526-4602 VL - 21 IS - 2 SP - 761 EP - 771 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Zhang, Pengfei A1 - Behl, Marc A1 - Balk, Maria A1 - Peng, Xingzhou A1 - Lendlein, Andreas T1 - Shape-programmable architectured hydrogels sensitive to ultrasound JF - Macromolecular rapid communications N2 - On-demand motion of highly swollen polymer systems can be triggered by changes in pH, ion concentrations, or by heat. Here, shape-programmable, architectured hydrogels are introduced, which respond to ultrasonic-cavitation-based mechanical forces (CMF) by directed macroscopic movements. The concept is the implementation and sequential coupling of multiple functions (swellability in water, sensitivity to ultrasound, shape programmability, and shape-memory) in a semi-interpenetrating polymer network (s-IPN). The semi-IPN-based hydrogels are designed to function through rhodium coordination (Rh-s-IPNH). These coordination bonds act as temporary crosslinks. The porous hydrogels with coordination bonds (degree of swelling from 300 +/- 10 to 680 +/- 60) exhibit tensile strength sigma(max) up to 250 +/- 60 kPa. Shape fixity ratios up to 90% and shape recovery ratios up to 94% are reached. Potential applications are switches or mechanosensors. KW - cavitation-based mechanical force KW - rhodium-phosphine coordination bonds KW - semi-IPN hydrogels KW - shape-memory effect Y1 - 2020 U6 - https://doi.org/10.1002/marc.201900658 SN - 1022-1336 SN - 1521-3927 VL - 41 IS - 7 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Behl, Marc A1 - Balk, Maria A1 - Lützow, Karola A1 - Lendlein, Andreas T1 - Impact of block sequence on the phase morphology of multiblock copolymers obtained by high-throughput robotic synthesis JF - European polymer journal : EPJ N2 - The chemical nature, the number length of integrated building blocks, as well as their sequence structure impact the phase morphology of multiblock copolymers (MBC) consisting of two non-miscible block types. We hypothesized that a strictly alternating sequence should favour phase segregation and in this way the elastic properties. A library of well-defined MBCs composed of two different hydrophobic, semi-crystalline blocks providing domains with well-separated melting temperatures (T(m)s) were synthesized from the same type of precursor building blocks as strictly alternating (MBCsalt) or random (MBCsran) MBCs and compared. Three different series of MBCsalt or MBCsran were synthesized by high-throughput synthesis by coupling oligo(e-caprolactone) (OCL) of different molecular weights (2, 4, and 8 kDa) with oligotetrahydrofuran (OTHF, 2.9 kDa) via Steglich esterification in which the molar ratio of the reaction partners was slightly adjusted. Maximum of weight average molecular weight (M-w) were 65,000 g center dot mol(-1), 165,000 g center dot mol(-1), and 168,000 g center dot mol(-1) for MBCsalt and 80,500 g center dot mol(-1), 100,000 g center dot mol(-1), and 147,600 g center dot mol(-1) for MBCsran. When Mw increased, a decrease of both Tms associated to the melting of the OCL and OTHF domains was observed for all MBCs. T-m (OTHF) of MBCsran was always higher than Tm (OTHF) of MBCsalt, which was attributed to a better phase segregation. In addition, the elongation at break of MBCsalt was almost half as high when compared to MBCsran. In this way this study elucidates role of the block length and sequence structure in MBCs and enables a quantitative discussion of the structure-function relationship when two semi-crystalline block segments are utilized for the design of block copolymers. KW - Multiblock copolymers KW - Sequence structure KW - Phase morphology KW - Polymer KW - library KW - Robotic synthesis KW - High-throughput Y1 - 2021 U6 - https://doi.org/10.1016/j.eurpolymj.2020.110207 SN - 0014-3057 SN - 1873-1945 VL - 143 PB - Elsevier CY - Oxford ER - TY - JOUR A1 - Hoffmann, Falk A1 - Machatschek, Rainhard Gabriel A1 - Lendlein, Andreas T1 - Analytical model and Monte Carlo simulations of polymer degradation with improved chain cut statistics JF - Journal of materials research : JMR N2 - The degradation of polymers is described by mathematical models based on bond cleavage statistics including the decreasing probability of chain cuts with decreasing average chain length. We derive equations for the degradation of chains under a random chain cut and a chain end cut mechanism, which are compared to existing models. The results are used to predict the influence of internal molecular parameters. It is shown that both chain cut mechanisms lead to a similar shape of the mass or molecular mass loss curve. A characteristic time is derived, which can be used to extract the maximum length of soluble fragments l of the polymer. We show that the complete description is needed to extract the degradation rate constant k from the molecular mass loss curve and that l can be used to design polymers that lose less mechanical stability before entering the mass loss phase. KW - Modeling KW - Degradable KW - Polymer KW - Molecular weight KW - Simulation Y1 - 2022 U6 - https://doi.org/10.1557/s43578-022-00495-4 SN - 0884-2914 SN - 2044-5326 VL - 37 IS - 5 SP - 1093 EP - 1101 PB - Springer CY - Heidelberg ER - TY - JOUR A1 - Machatschek, Rainhard Gabriel A1 - Schöne, Anne-Christin A1 - Raschdorf, Elisa A1 - Ihlenburg, Ramona A1 - Schulz, Burkhard A1 - Lendlein, Andreas T1 - Interfacial properties of morpholine-2,5-dione-based oligodepsipeptides and multiblock copolymers JF - MRS Communications N2 - Oligodepsipeptides (ODPs) with alternating amide and ester bonds prepared by ring-opening polymerization of morpholine-2,5-dione derivatives are promising matrices for drug delivery systems and building blocks for multifunctional biomaterials. Here, we elucidate the behavior of three telechelic ODPs and one multiblock copolymer containing ODP blocks at the air-water interface. Surprisingly, whereas the oligomers and multiblock copolymers crystallize in bulk, no crystallization is observed at the air-water interface. Furthermore, polarization modulation infrared reflection absorption spectroscopy is used to elucidate hydrogen bonding and secondary structures in ODP monolayers. The results will direct the development of the next ODP-based biomaterial generation with tailored properties for highly sophisticated applications. Y1 - 2019 U6 - https://doi.org/10.1557/mrc.2019.21 SN - 2159-6859 SN - 2159-6867 VL - 9 IS - 1 SP - 170 EP - 180 PB - Cambridge Univ. Press CY - New York ER - TY - GEN A1 - Machatschek, Rainhard Gabriel A1 - Schöne, Anne-Christin A1 - Raschdorf, Elisa A1 - Ihlenburg, Ramona A1 - Schulz, Burkhard A1 - Lendlein, Andreas T1 - Interfacial properties of morpholine-2,5-dione-based oligodepsipeptides and multiblock copolymers T2 - Postprints der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe N2 - Oligodepsipeptides (ODPs) with alternating amide and ester bonds prepared by ring-opening polymerization of morpholine-2,5-dione derivatives are promising matrices for drug delivery systems and building blocks for multifunctional biomaterials. Here, we elucidate the behavior of three telechelic ODPs and one multiblock copolymer containing ODP blocks at the air-water interface. Surprisingly, whereas the oligomers and multiblock copolymers crystallize in bulk, no crystallization is observed at the air-water interface. Furthermore, polarization modulation infrared reflection absorption spectroscopy is used to elucidate hydrogen bonding and secondary structures in ODP monolayers. The results will direct the development of the next ODP-based biomaterial generation with tailored properties for highly sophisticated applications. T3 - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe - 1106 KW - block-copolymer KW - enzymatic degradation KW - poly(ester amide)s KW - controlled-release KW - films KW - nanocarriers Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-469755 SN - 1866-8372 IS - 1106 SP - 170 EP - 180 ER - TY - JOUR A1 - Piluso, Susanna A1 - Vukicevie, Radovan A1 - Nöchel, Ulrich A1 - Braune, Steffen A1 - Lendlein, Andreas A1 - Neffe, Axel T. T1 - Sequential alkyne-azide cycloadditions for functionalized gelatin hydrogel formation JF - European polymer journal N2 - While click chemistry reactions for biopolymer network formation are attractive as the defined reactions may allow good control of the network formation and enable subsequent functionalization, tailoring of gelatin network properties over a wide range of mechanical properties has yet to be shown. Here, it is demonstrated that copper-catalyzed alkyne-azide cycloaddition of alkyne functionalized gelatin with diazides gave hydrogel networks with properties tailorable by the ratio of diazide to gelatin and diazide rigidity. 4,4′-diazido-2,2′-stilbenedisulfonic acid, which has been used as rigid crosslinker, yielded hydrogels with Young’s moduli E of 50–390 kPa and swelling degrees Q of 150–250 vol.%, while the more flexible 1,8-diazidooctane resulted in hydrogels with E = 125–280 kPa and Q = 225–470 vol.%. Storage moduli could be varied by two orders of magnitude (G′ = 100–20,000 Pa). An indirect cytotoxicity test did not show cytotoxic properties. Even when employing 1:1 ratios of alkyne and azide moieties, the hydrogels were shown to contain both, unreacted alkyne groups on the gelatin backbone as well as dangling chains carrying azide groups as shown by reaction with functionalized fluorescein. The free groups, which can be tailored by the employed ratio of the reactants, are accessible for covalent attachment of drugs, as was demonstrated by functionalization with dexamethasone. The sequential network formation and functionalization with click chemistry allows access to multifunctional materials relevant for medical applications. KW - Click chemistry KW - Hydrogel KW - Polymer functionalization KW - Biopolymer KW - Rheology KW - Multifunctionality Y1 - 2018 U6 - https://doi.org/10.1016/j.eurpolymj.2018.01.017 SN - 0014-3057 SN - 1873-1945 VL - 100 SP - 77 EP - 85 PB - Elsevier CY - Oxford ER - TY - JOUR A1 - Lützow, Karola A1 - Hommes-Schattmann, Paul J. A1 - Neffe, Axel T. A1 - Ahmad, Bilal A1 - Williams, Gareth R. A1 - Lendlein, Andreas T1 - Perfluorophenyl azide functionalization of electrospun poly(para-dioxanone) JF - Polymers for advanced technologies N2 - Strategies to surface-functionalize scaffolds by covalent binding of biologically active compounds are of fundamental interest to control the interactions between scaffolds and biomolecules or cells. Poly(para-dioxanone) (PPDO) is a clinically established polymer that has shown potential as temporary implant, eg, for the reconstruction of the inferior vena cava, as a nonwoven fiber mesh. However, PPDO lacks suitable chemical groups for covalent functionalization. Furthermore, PPDO is highly sensitive to hydrolysis, reflected by short in vivo half-life times and degradation during storage. Establishing a method for covalent functionalization without degradation of this hydrolyzable polymer is therefore important to enable the surface tailoring for tissue engineering applications. It was hypothesized that treatment of PPDO with an N-hydroxysuccinimide ester group bearing perfluorophenyl azide (PFPA) under UV irradiation would allow efficient surface functionalization of the scaffold. X-ray photoelectron spectroscopy and attenuated total reflectance Fourier-transformed infrared spectroscopy investigation revealed the successful binding, while a gel permeation chromatography study showed that degradation did not occur under these conditions. Coupling of a rhodamine dye to the N-hydroxysuccinimide esters on the surface of a PFPA-functionalized scaffold via its amine linker showed a homogenous staining of the PPDO in laser confocal microscopy. The PFPA method is therefore applicable even to the surface functionalization of hydrolytically labile polymers, and it was demonstrated that PFPA chemistry may serve as a versatile tool for the (bio-)functionalization of PPDO scaffolds. KW - biological applications of polymers KW - fibers KW - functionalization of polymers KW - microstructure Y1 - 2018 U6 - https://doi.org/10.1002/pat.4331 SN - 1042-7147 SN - 1099-1581 VL - 30 IS - 5 SP - 1165 EP - 1172 PB - Wiley CY - Hoboken ER - TY - JOUR A1 - Tronci, Giuseppe A1 - Neffe, Axel T. A1 - Pierce, Benjamin Franklin A1 - Lendlein, Andreas T1 - An entropy-elastic gelatin-based hydrogel system N2 - Gelatin is a non-immunogenic and degradable biopolymer, which is widely applied in the biomedical field e. g. for drug capsules or as absorbable hemostats. However, gelatin materials present limited and hardly reproducible mechanical properties especially in aqueous systems, particularly caused by the uncontrollable partial renaturation of collagen-like triple helices. Therefore, mechanically demanding applications for gelatin-based materials, such as vascular patches, i.e. hydrogel films that seal large incisions in vessel walls, and for induced autoregeneration, are basically excluded if this challenge is not addressed. Through the synthesis of a defined chemical network of gelatin with hexamethylene diisocyanate (HDI) in DMSO, the self-organization of gelatin chains could be hindered and amorphous gelatin films were successfully prepared having Young's moduli of 60-530 kPa. Transferring the crosslinking reaction with HDI and, alternatively, ethyl lysine diisocyanate (LDI), to water as reaction medium allowed the tailoring of swelling behaviour and mechanical properties by variation of crosslinker content while suppressing the formation of helices. The hydrogels had Young's moduli of 70-740 kPa, compressive moduli of 16-48 kPa, and degrees of swelling of 300-800 vol%. Test reactions investigated by ESI mass spectrometry allowed the identification and quantification of reaction products of the crosslinking reaction. The HDI crosslinked networks were stabilized by direct covalent crosslinks (ca. 10 mol%), supported by grafting (50 mol%) and blending of hydrophobic oligomeric chains. For the LDI- based networks, less crosslinked (3 mol%) and grafted species (5 mol%) and much higher amounts of oligomers were observed. The adjustable hydrogel system enables the application of gelatin-based materials in physiological environments. Y1 - 2010 UR - http://www.rsc.org/Publishing/Journals/jm/index.asp U6 - https://doi.org/10.1039/C0jm00883d SN - 0959-9428 ER - TY - JOUR A1 - von Rüsten-Lange, Maik A1 - Luetzow, Karola A1 - Neffe, Axel T. A1 - Lendlein, Andreas T1 - Characterization of oligo(ethylene glycol) and oligoglycerol functionalized poly(ether imide) by angle-dependent X-ray photoelectron spectroscopy JF - Journal of applied biomaterials & functional materials N2 - Purpose: Previous investigations have shown that poly(ether imide) (PEI) membranes can be functionalized with aminated macromolecules. In this study we explored whether the characterization of PEI functionalized with oligo(ethylene glycol) (OEG) or linear, side chain methylated oligoglycerols (OGMe), by angle-dependent X-ray induced photoelectron spectroscopy (XPS) can be used to prove the functionalization, give insight into the reaction mechanism and reveal the spatial distribution of the grafts. Methods: PEI membranes were functionalized under alkaline conditions using an aqueous solution with 2 wt% of alpha-amino-methoxy oligo(ethylene glycol) (M-n = 1,320 g.mol(-1)) or linear, side chain methylated monoamine oligoglycerols (M-n = 1,120, 1,800 or 2,270 g.mol(-1)), respectively. The functionalized membranes were investigated using XPS measurements at different detector angles to enable comparison between the signals related to the bulk and surface volume and were compared with untreated and alkaline-treated PEI membranes. Results: While at a perpendicular detector angle the bulk signals of the PEI were prominent, at larger surface volume-related detector angles, the signals for OGMe and OEG were determinable. Conclusion: The surface functionalization of PEI with OEG and OGMe could be verified by the angle-dependent XPS. The observations proved the functionalization at the PEI surface, as the polyethers were detected at angles providing signals of the surface volume. Furthermore, the chemical functions determined verified a covalent binding via the nucleophilic addition of the amine functionalized OGMe and OEG to the PEI imide function. KW - Poly(ether imide) KW - Oligo(ethylene glycol) KW - Oligoglycerols KW - Angle-dependent X-ray induced photoelectron spectroscopy KW - Surface functionalization Y1 - 2012 U6 - https://doi.org/10.5301/JABFM.2012.10345 SN - 2280-8000 VL - 10 IS - 3 SP - 215 EP - 222 PB - Wichtig CY - Milano ER - TY - JOUR A1 - Zaupa, Alessandro A1 - Neffe, Axel T. A1 - Pierce, Benjamin F. A1 - Lendlein, Andreas A1 - Hofmann, Dieter T1 - A molecular dynamic analysis of gelatin as an amorphous material Prediction of mechanical properties of gelatin systems JF - The international journal of artificial organs N2 - Biomaterials are used in regenerative medicine for induced autoregeneration and tissue engineering. This is often challenging, however, due to difficulties in tailoring and controlling the respective material properties. Since functionalization is expected to offer better control, in this study gelatin chains were modified with physically interacting groups based on tyrosine with the aim of causing the formation of physical crosslinks. This method permits application-specific properties like swelling and better tailoring of mechanical properties. The design of the crosslink strategy was supported by molecular dynamic (MD) simulations of amorphous bulk models for gelatin and functionalized gelatins at different water contents (0.8 and 25 wt.-%). The results permitted predictions to be formulated about the expected crosslink density and its influence on equilibrium swelling behavior and on elastic material properties. The models of pure gelatin were used to validate the strategy by comparison between simulated and experimental data such as density, backbone conformation angle distribution, and X-ray scattering spectra. A key result of the simulations was the prediction that increasing the number of aromatic functions attached to the gelatin chain leads to an increase in the number of physical netpoints observed in the simulated bulk packing models. By comparison with the Flory-Rehner model, this suggested reduced equilibrium swelling of the functionalized materials in water, a prediction that was subsequently confirmed by our experimental work. The reduction and control of the equilibrium degree of swelling in water is a key criterion for the applicability of functionalized gelatins when used, for example, as matrices for induced autoregeneration of tissues. KW - Physical Network KW - Biopolymer material KW - Molecular modeling KW - Gelatin Y1 - 2011 U6 - https://doi.org/10.5301/IJAO.2010.6083 SN - 0391-3988 VL - 34 IS - 2 SP - 139 EP - 151 PB - Wichtig CY - Milano ER - TY - JOUR A1 - Zhang, Pengfei A1 - Rešetič, Andraž A1 - Behl, Marc A1 - Lendlein, Andreas T1 - Multifunctionality in polymer networks by dynamic of coordination bonds JF - Macromolecular chemistry and physics N2 - The need for multifunctional materials is driven by emerging technologies and innovations, such as in the field of soft robotics and tactile or haptic systems, where minimizing the number of operational components is not only desirable, but can also be essential for realizing such devices. This study report on designing a multifunctional soft polymer material that can address a number of operating requirements such as solvent resistance, reshaping ability, self-healing capability, fluorescence stimuli-responsivity, and anisotropic structural functions. The numerous functional abilities are associated to rhodium(I)-phosphine coordination bonds, which in a polymer network act with their dynamic and non-covalently bonded nature as multifunctional crosslinks. Reversible aggregation of coordination bonds leads to changes in fluorescence emission intensity that responds to chemical or mechanical stimuli. The fast dynamics and diffusion of rhodium-phosphine ions across and through contacting areas of the material provide for reshaping and self-healing abilities that can be further exploited for assembly of multiple pieces into complex forms, all without any loss to material-sensing capabilities. KW - assembly capabilities KW - fluorescence stimuli‐ responsivity KW - multiple functions KW - reshaping abilities KW - rhodium(I)– phosphine KW - coordination bonds KW - solvent resistance Y1 - 2021 U6 - https://doi.org/10.1002/macp.202000394 SN - 1521-3935 VL - 222 IS - 3 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Sauter, Tilman A1 - Kratz, Karl A1 - Farhan, Muhammad A1 - Heuchel, Matthias A1 - Lendlein, Andreas T1 - Design and fabrication of fiber mesh actuators JF - Applied materials today N2 - Soft actuator performance can be tuned by chemistry or mechanical manipulation, but this adjustability is limited especially in view of their growing technological relevance. Inspired from textile engineering, we designed and fabricated fiber mesh actuators and introduced new features like anisotropic behavior and soft-tissue like elastic deformability. Design criteria for the meshes are the formation of fiber bundles, the angle between fiber bundles in different stacked layers and covalent crosslinks forming within and between fibers at their interfacial contact areas. Through crosslinking the interfiber bond strength increased from a bond transmitting neither axial nor rotational loads (pin joint) to a bond strength capable of both (welded joint). For non-linear elastic stiffening, stacked fiber bundles with four embracing fibers were created forming microstructural rhombus shapes. Loading the rhombus diagonally allowed generation of “soft tissue”-like mechanics. By adjustment of stacking angles, the point of strong increase in stress is tuned. While the highest stresses are observed in aligned and crosslinked fiber mats along the direction of the fiber, the strongest shape-memory actuation behavior is found in randomly oriented fiber mats. Fiber mesh actuators controlled by temperature are of high significance as soft robot skins and as for active patches supporting tissue regeneration. Y1 - 2022 U6 - https://doi.org/10.1016/j.apmt.2022.101562 SN - 2352-9407 VL - 29 PB - Elsevier CY - Amsterdam ER - TY - JOUR A1 - Tartivel, Lucile A1 - Blocki, Anna M. A1 - Braune, Steffen A1 - Jung, Friedrich A1 - Behl, Marc A1 - Lendlein, Andreas T1 - An Inverse shape-memory hydrogel scaffold switching upon cooling in a tissue-tolerated temperature range JF - Advanced materials interfaces N2 - Tissue reconstruction has an unmet need for soft active scaffolds that enable gentle loading with regeneration-directing bioactive components by soaking up but also provide macroscopic dimensional stability. Here microporous hydrogels capable of an inverse shape-memory effect (iSME) are described, which in contrast to classical shape-memory polymers (SMPs) recover their permanent shape upon cooling. These hydrogels are designed as covalently photo cross-linked polymer networks with oligo(ethylene glycol)-oligo(propylene glycol)-oligo(ethylene glycol) (OEG-OPG-OEG) segments. When heated after deformation, the OEG-OPG-OEG segments form micelles fixing the temporary shape. Upon cooling, the micelles dissociate again, the deformation is reversed and the permanent shape is obtained. Applicability of this iSME is demonstrated by the gentle loading of platelet-rich plasma (PRP) without causing any platelet activation during this process. PRP is highly bioactive and is widely acknowledged for its regenerative effects. Hence, the microporous inverse shape-memory hydrogel (iSMH) with a cooling induced pore-size effect represents a promising candidate scaffold for tissue regeneration for potential usage in minimally invasive surgery applications. KW - active scaffold KW - critical micellation temperature KW - hydrogel KW - inverse KW - shape-memory effect KW - platelet-rich plasma Y1 - 2022 U6 - https://doi.org/10.1002/admi.202101588 SN - 2196-7350 VL - 9 IS - 6 PB - Wiley CY - Hoboken ER - TY - JOUR A1 - Machatschek, Rainhard Gabriel A1 - Heuchel, Matthias A1 - Lendlein, Andreas T1 - Hydrolytic stability of polyetherimide investigated in ultrathin films JF - Journal of materials research : JMR / Materials Research Society N2 - Increasing the surface hydrophilicity of polyetherimide (PEI) through partial hydrolysis of the imide groups while maintaining the length of the main-chain was explored for adjusting its function in biomedical and membrane applications. The outcome of the polymer analogous reaction, i.e., the degree of ring opening and chain cleavage, is difficult to address in bulk and microstructured systems, as these changes only occur at the interface. Here, the reaction was studied at the air-water interface using the Langmuir technique, assisted by atomic force microscopy and vibrational spectroscopy. Slow PEI hydrolysis sets in at pH > 12. At pH = 14, the ring opening is nearly instantaneous. Reduction of the layer viscosity with time at pH = 14 suggested moderate chain cleavage. No hydrolysis was observed at pH = 1. Hydrolyzed PEI films had a much more cohesive structure, suggesting that the nanoporous morphology of PEI can be tuned via hydrolysis. KW - 2D materials KW - Membrane KW - Polymer KW - Water KW - Nanostructure Y1 - 2021 U6 - https://doi.org/10.1557/s43578-021-00267-6 SN - 0884-2914 SN - 2044-5326 VL - 36 IS - 14 SP - 2987 EP - 2994 PB - Springer CY - Berlin ER - TY - JOUR A1 - Bochove, Bas van A1 - Grijpma, Dirk W. A1 - Lendlein, Andreas A1 - Seppälä, Jukka T1 - Designing advanced functional polymers for medicine JF - European polymer journal : EPJ Y1 - 2021 U6 - https://doi.org/10.1016/j.eurpolymj.2021.110573 SN - 0014-3057 VL - 155 PB - Elsevier CY - Oxford ER - TY - JOUR A1 - Folikumah, Makafui Yao A1 - Behl, Marc A1 - Lendlein, Andreas T1 - Thiol-Thioester exchange reactions in precursors enable pH-triggered hydrogel formation JF - Biomacromolecules : an interdisciplinary journal focused at the interface of polymer science and the biological sciences N2 - Bio-interactive hydrogel formation in situ requires sensory capabilities toward physiologically relevant stimuli. Here, we report on pH-controlled in situ hydrogel formation relying on latent cross-linkers, which transform from pH sensors to reactive molecules. In particular, thiopeptolide/thio-depsipeptides were capable of pH-sensitive thiol-thioester exchange reactions to yield a,co-dithiols, which react with maleimide-functionalized multi-arm polyethylene glycol to polymer networks. Their water solubility and diffusibility qualify thiol/thioester-containing peptide mimetics as sensory precursors to drive in situ localized hydrogel formation with potential applications in tissue regeneration such as treatment of inflamed tissues of the urinary tract. Y1 - 2021 U6 - https://doi.org/10.1021/acs.biomac.0c01690 SN - 1525-7797 SN - 1526-4602 VL - 22 IS - 5 SP - 1875 EP - 1884 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Neffe, Axel T. A1 - Löwenberg, Candy A1 - Julich-Gruner, Konstanze K. A1 - Behl, Marc A1 - Lendlein, Andreas T1 - Thermally-induced shape-memory behavior of degradable gelatin-based networks JF - International journal of molecular sciences N2 - Shape-memory hydrogels (SMH) are multifunctional, actively-moving polymers of interest in biomedicine. In loosely crosslinked polymer networks, gelatin chains may form triple helices, which can act as temporary net points in SMH, depending on the presence of salts. Here, we show programming and initiation of the shape-memory effect of such networks based on a thermomechanical process compatible with the physiological environment. The SMH were synthesized by reaction of glycidylmethacrylated gelatin with oligo(ethylene glycol) (OEG) alpha,omega-dithiols of varying crosslinker length and amount. Triple helicalization of gelatin chains is shown directly by wide-angle X-ray scattering and indirectly via the mechanical behavior at different temperatures. The ability to form triple helices increased with the molar mass of the crosslinker. Hydrogels had storage moduli of 0.27-23 kPa and Young's moduli of 215-360 kPa at 4 degrees C. The hydrogels were hydrolytically degradable, with full degradation to water-soluble products within one week at 37 degrees C and pH = 7.4. A thermally-induced shape-memory effect is demonstrated in bending as well as in compression tests, in which shape recovery with excellent shape-recovery rates R-r close to 100% were observed. In the future, the material presented here could be applied, e.g., as self-anchoring devices mechanically resembling the extracellular matrix. KW - shape-memory hydrogel KW - active polymer KW - biopolymer KW - mechanical KW - properties KW - degradation Y1 - 2021 U6 - https://doi.org/10.3390/ijms22115892 SN - 1422-0067 SN - 1661-6596 VL - 22 IS - 11 PB - Molecular Diversity Preservation International CY - Basel ER - TY - JOUR A1 - Julich-Gruner, Konstanze K. A1 - Löwenberg, Candy A1 - Neffe, Axel T. A1 - Behl, Marc A1 - Lendlein, Andreas T1 - Recent trends in the chemistry of shape-memory polymers JF - Macromolecular chemistry and physics N2 - Shape-memory polymers (SMPs) are stimuli-sensitive materials capable of performing complex movements on demand, which makes them interesting candidates for various applications, for example, in biomedicine or aerospace. This trend article highlights current approaches in the chemistry of SMPs, such as tailored segment chemistry to integrate additional functions and novel synthetic routes toward permanent and temporary netpoints. Multiphase polymer networks and multimaterial systems illustrate that SMPs can be constructed as a modular system of different building blocks and netpoints. Future developments are aiming at multifunctional and multistimuli-sensitive SMPs. KW - multifunctional polymers KW - networks KW - shape-memory polymers KW - stimuli-sensitive polymers KW - triple-shape effect Y1 - 2013 U6 - https://doi.org/10.1002/macp.201200607 SN - 1022-1352 VL - 214 IS - 5 SP - 527 EP - 536 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Federico, Stefania A1 - Nöchel, Ulrich A1 - Löwenberg, Candy A1 - Lendlein, Andreas A1 - Neffe, Axel T. T1 - Supramolecular hydrogel networks formed by molecular recognition of collagen and a peptide grafted to hyaluronic acid JF - Acta biomaterialia N2 - The extracellular matrix (ECM) is a nano-structured, highly complex hydrogel, in which the macromolecules are organized primarily by non-covalent interactions. Here, in a biomimetic approach, the decorin-derived collagen-binding peptide LSELRLHNN was grafted to hyaluronic acid (HA) in order to enable the formation of a supramolecular hydrogel network together with collagen. The storage modulus of a mixture of collagen and HA was increased by more than one order of magnitude (G′ = 157 Pa) in the presence of the HA-grafted peptide compared to a mixture of collagen and HA (G′ = 6 Pa). The collagen fibril diameter was decreased, as quantified using electron microscopy, in the presence of the HA-grafted peptide. Here, the peptide mimicked the function of decorin by spatially organizing collagen. The advantage of this approach is that the non-covalent crosslinks between collagen molecules and the HA chains created by the peptide form a reversible and dynamic hydrogel, which could be employed for a diverse range of applications in regenerative medicine. Statement of Significance Biopolymers of the extracellular matrix (ECM) like collagen or hyaluronan are attractive starting materials for biomaterials. While in biomaterial science covalent crosslinking is often employed, in the native ECM, stabilization and macromolecular organization is primarily based on non-covalent interactions, which allows dynamic changes of the materials. Here, we show that collagen-binding peptides, derived from the small proteoglycan decorin, grafted to hyaluronic acid enable supramolecular stabilization of collagen hydrogels. These hydrogels have storage moduli more than one order of magnitude higher than mixtures of collagen and hyaluronic acid. Furthermore, the peptide supported the structural organization of collagen. Such hydrogels could be employed for a diverse range of applications in regenerative medicine. Furthermore, the rational design helps in the understanding ECM structuring. KW - Biopolymers KW - Collagen-binding peptide KW - Hyaluronic acid KW - Hydrogels KW - Mechanical properties Y1 - 2016 U6 - https://doi.org/10.1016/j.actbio.2016.04.018 SN - 1742-7061 SN - 1878-7568 VL - 38 SP - 1 EP - 10 PB - Elsevier CY - Oxford ER - TY - JOUR A1 - Blocki, Anna A1 - Löwenberg, Candy A1 - Jiang, Yi A1 - Kratz, Karl A1 - Neffe, Axel T. A1 - Jung, Friedrich A1 - Lendlein, Andreas T1 - Response of encapsulated cells to a gelatin matrix with varied bulk and microenvironmental elastic properties JF - Polymers for advanced technologies N2 - Gelatin-based hydrogels offer various biochemical cues that support encapsulated cells and are therefore suitable as cell delivery vehicles in regenerative medicine. However, besides the biochemical signals, biomechanical cues are crucial to ensure an optimal support of encapsulated cells. Hence, we aimed to correlate the cellular response of encapsulated cells to macroscopic and microscopic elastic properties of glycidylmethacrylate (GMA)-functionalized gelatin-based hydrogels. To ensure that different observations in cellular behavior could be attributed to differences in elastic properties, an identical concentration as well as degree of functionalization of biopolymers was utilized to form covalently crosslinked hydrogels. Elastic properties were merely altered by varying the average gelatin-chain length. Hydrogels exhibited an increased degree of swelling and a decreased bulk elastic modulus G with prolonged autoclaving of the starting solution. This was accompanied by an increase of hydrogel mesh size and thus by a reduction of crosslinking density. Tougher hydrogels retained the largest amount of cells; however, they also interfered with cell viability. Softer gels contained a lower cell density, but supported cell elongation and viability. Observed differences could be partially attributed to differences in bulk properties, as high crosslinking densities interfere with diffusion and cell spreading and thus can impede cell viability. Interestingly, a microscopic elastic modulus in the range of native soft tissue supported cell viability and elongation best while ensuring a good cell entrapment. In conclusion, gelatin-based hydrogels providing a soft tissue-like microenvironment represent adequate cell delivery vehicles for tissue engineering approaches. Copyright (c) 2016 John Wiley & Sons, Ltd. KW - mechanotransduction KW - hydrogel KW - gelatin KW - cell encapsulation KW - matrix elasticity Y1 - 2017 U6 - https://doi.org/10.1002/pat.3947 SN - 1042-7147 SN - 1099-1581 VL - 28 SP - 1245 EP - 1251 PB - Wiley CY - Hoboken ER - TY - JOUR A1 - You, Zewang A1 - Behl, Marc A1 - Löwenberg, Candy A1 - Lendlein, Andreas T1 - pH-sensitivity and conformation change of the n-terminal methacrylated peptide VK20 JF - MRS advances : a journal of the Materials Research Society (MRS) N2 - N-terminal methacrylation of peptide MAXI, which is capable of conformational changes variation of the pH, results in a peptide, named VK20. Increasing the reactivity of this terminal group enables further coupling reactions or chemical modifications of the peptidc. However, this end group functionalization may influence the ability of confonnational changes of VK20; as well as its properties. In this paper; the influence of pH on the transition between random coil and beta-sheet conformation of VK20; including the transition kinetics, were investigated. At pH values of 9 and higher, the kinetics beta-sheet formation increased tor VK(2 0, compared to MAXI. The self-assembly into beta-sheets recognized by the formation of a physically crosslinked gel was furthermore indicated by a significant increase of G. An increase in pH (from 9 to 9.5) led to a faster gelation of the peptide VK20. Simultaneously, G was increased from 460 +/- 70 Pa (at pH 9) to 1520 +/- 180 Pa (at pH 9.5). At the nanoscale, the gel showed a highly interconnected fibrillar/network structure with uniform fibril widths of approximately 3.4 +/- 0.5 nm (N=30). The recovery of the peptide conformation back to random coil resulted in the dissolution of the gel; whereby the kinetics of the recovery depended on the pH. Conclusively, the ability of MAXI to undergo confommtional changes was not affected by N-terminal methacrylation whereas the kinetics of pH-sensitive beta-sheet formations has been increased. Y1 - 2017 U6 - https://doi.org/10.1557/adv.2017.491 SN - 2059-8521 VL - 2 SP - 2571 EP - 2579 PB - Cambridge University Press CY - Cambridge ER - TY - JOUR A1 - Löwenberg, Candy A1 - Tripodo, Giuseppe A1 - Julich-Gruner, Konstanze K. A1 - Neffe, Axel T. A1 - Lendlein, Andreas T1 - Supramolecular gelatin networks based on inclusion complexes JF - Macromolecular bioscience N2 - Hydrogel forming physical networks based on gelatin are an attractive approach toward multifunctional biomaterials with the option of reshaping, self-healing, and stimuli-sensitivity. However, it is challenging to design such gelatin-based hydrogels to be stable at body temperature. Here, gelatin functionalized with desaminotyrosine (DAT) or desaminotyrosyl tyrosine (DATT) side chains is crosslinked with cyclodextrin (CD) dimers under formation of inclusions complexes. The supramolecular networks displayed at room temperature decreased water uptake (200-600 wt% for DAT-based systems, 200 wt% for DATT based systems), and increased storage moduli up to 25.6 kPa determined by rheology compared to DAT(T) gelatin. The gel-sol transition temperature increased from 33 up to 42 degrees C. The presented system that is completely based on natural building blocks may form the basis for materials that may potentially respond by dissolution or changes of properties to changes in environmental conditions or to the presence of CD guest molecules. KW - cyclodextrin KW - gelatin KW - inclusion complex KW - supramolecular polymer network Y1 - 2020 U6 - https://doi.org/10.1002/mabi.202000221 SN - 1616-5187 SN - 1616-5195 VL - 20 IS - 10 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Neffe, Axel T. A1 - Löwenberg, Candy A1 - Lendlein, Andreas T1 - Hydrogel networks by aliphatic dithiol Michael addition to glycidylmethacrylated gelatin JF - MRS advances : a journal of the Materials Research Society (MRS) N2 - Functionalization of gelatin with glycidylmethacrylate (GMA-gelatin) enables network formation employing the double bond, so that the reaction is orthogonal to the inherent functional groups in the biomacromolecule. Here, network formation by crosslinking of GMA-gelatin with hexane 1,6-dithiol or nonane 1,9-dithiol to tailor properties and enable a shape-memory effect is shown by H-1 NMR and FT-IR spectroscopy. Hydrogel swelling (460-1900 vol%) and mechanical properties (Young's modulus E = 59-512 kPa, elongation at break epsilon(b) = 44-127%) depended on the molecular composition of the networks and temperature. Increased crosslinker length, thiol:methacrylate molar ratio, and precursor concentrations led to denser networks. Change of properties with temperature suggested adoption of triple helices by gelatin chains, forming physical netpoints at lower temperatures (< 20 degrees C). However, the limited freedom of the gelatin chains to move allowed only a minimal extent of triple helices formation, as it became apparent from the related signal in wide-angle X-ray scattering and the thermal transition associated to triple helices in some networks by DSC. The presented strategy is likely transferable to other biomacromolecules, and the results suggest that too short crosslinkers may result in a significant amount of grafting rather than network formation. Y1 - 2021 U6 - https://doi.org/10.1557/s43580-021-00136-8 SN - 2059-8521 VL - 6 IS - 33 SP - 796 EP - 800 PB - Springer Nature Switzerland AG CY - Cham ER - TY - JOUR A1 - Machatschek, Rainhard Gabriel A1 - Saretia, Shivam A1 - Lendlein, Andreas T1 - Assessing the influence of temperature-memory creation on the degradation of copolyesterurethanes in ultrathin films JF - Advanced materials interfaces N2 - Copolyesterurethanes (PDLCLs) based on oligo(epsilon-caprolactone) (OCL) and oligo(omega-pentadecalactone) (OPDL) segments are biodegradable thermoplastic temperature-memory polymers. The temperature-memory capability in these polymers with crystallizable control units is implemented by a thermomechanical programming process causing alterations in the crystallite arrangement and chain organization. These morphological changes can potentially affect degradation. Initial observations on the macroscopic level inspire the hypothesis that switching of the controlling units causes an accelerated degradation of the material, resulting in programmable degradation by sequential coupling of functions. Hence, detailed degradation studies on Langmuir films of a PDLCL with 40 wt% OPDL content are carried out under enzymatic catalysis. The temperature-memory creation procedure is mimicked by compression at different temperatures. The evolution of the chain organization and mechanical properties during the degradation process is investigated by means of polarization-modulated infrared reflection absorption spectroscopy, interfacial rheology and to some extend by X-ray reflectivity. The experiments on PDLCL Langmuir films imply that degradability is not enhanced by thermal switching, as the former depends on the temperature during cold programming. Nevertheless, the thin film experiments show that the leaching of OCL segments does not induce further crystallization of the OPDL segments, which is beneficial for a controlled and predictable degradation. KW - block copolymers KW - degradation KW - Langmuir monolayers KW - rheology KW - temperature-memory polymers Y1 - 2021 U6 - https://doi.org/10.1002/admi.202001926 SN - 2196-7350 VL - 8 IS - 6 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Deng, Zijun A1 - Wang, Weiwei A1 - Xu, Xun A1 - Ma, Nan A1 - Lendlein, Andreas T1 - Polydopamine-based biofunctional substrate coating promotes mesenchymal stem cell migration JF - MRS advances : a journal of the Materials Research Society (MRS) N2 - Rapid migration of mesenchymal stem cells (MSCs) on device surfaces could support in vivo tissue integration and might facilitate in vitro organoid formation. Here, polydopamine (PDA) is explored as a biofunctional coating to effectively promote MSC motility. It is hypothesized that PDA stimulates fibronectin deposition and in this way enhances integrin-mediated migration capability. The random and directional cell migration was investigated by time-lapse microscopy and gap closure assay respectively, and analysed with softwares as computational tools. A higher amount of deposited fibronectin was observed on PDA substrate, compared to the non-coated substrate. The integrin beta 1 activation and focal adhesion kinase (FAK) phosphorylation at Y397 were enhanced on PDA substrate, but the F-actin cytoskeleton was not altered, suggesting MSC migration on PDA was regulated by integrin initiated FAK signalling. This study strengthens the biofunctionality of PDA coating for regulating stem cells and offering a way of facilitating tissue integration of devices. Y1 - 2021 U6 - https://doi.org/10.1557/s43580-021-00091-4 SN - 2059-8521 VL - 6 IS - 31 SP - 739 EP - 744 PB - Springer Nature Switzerland AG CY - Cham ER - TY - JOUR A1 - Farhan, Muhammad A1 - Rudolph, Tobias A1 - Nöchel, Ulrich A1 - Yan, Wan A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Noncontinuously Responding Polymeric Actuators JF - ACS applied materials & interfaces N2 - Reversible movements of current polymeric actuators stem from the continuous response to signals from a controlling unit, and subsequently cannot be interrupted without stopping or eliminating the input trigger. Here, we present actuators based on cross-linked blends of two crystallizable polymers capable of pausing their movements in a defined manner upon continuous cyclic heating and cooling. This noncontinuous actuation can be adjusted by varying the applied heating and cooling rates. The feasibility of these devices for technological applications was shown in a 140 cycle experiment of free-standing noncontinuous shape shifts, as well as by various demonstrators. KW - soft robotics KW - polymer actuators KW - thermo-sensitivity KW - shape shifting materials KW - crystallization behavior Y1 - 2017 U6 - https://doi.org/10.1021/acsami.7b11316 SN - 1944-8244 VL - 9 SP - 33559 EP - 33564 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Farhan, Muhammad A1 - Rudolph, Tobias A1 - Nöchel, Ulrich A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Extractable Free Polymer Chains Enhance Actuation Performance of Crystallizable Poly(epsilon-caprolactone) Networks and Enable Self-Healing JF - Polymers N2 - Crosslinking of thermoplastics is a versatile method to create crystallizable polymer networks, which are of high interest for shape-memory actuators. Here, crosslinked poly(epsilon-caprolactone) thermosets (cPCLs) were prepared from linear starting material, whereby the amount of extractable polymer was varied. Fractions of 5-60 wt % of non-crosslinked polymer chains, which freely interpenetrate the crosslinked network, were achieved leading to differences in the resulting phase of the bulk material. This can be described as "sponge-like" with open or closed compartments depending on the amount of interpenetrating polymer. The crosslinking density and the average network chain length remained in a similar range for all network structures, while the theoretical accessible volume for reptation of the free polymer content is affected. This feature could influence or introduce new functions into the material created by thermomechanical treatment. The effect of interpenetrating PCL in cPCLs on the reversible actuation was analyzed by cyclic, uniaxial tensile tests. Here, high reversible strains of up to Delta epsilon = 24% showed the enhanced actuation performance of networks with a non-crosslinked PCL content of 30 wt % resulting from the crystal formation in the phase of the non-crosslinked PCL and co-crystallization with network structures. Additional functionalities are reprogrammability and self-healing capabilities for networks with high contents of extractable polymer enabling reusability and providing durable actuator materials. KW - shape-memory polymer actuators KW - soft actuators KW - self-healing KW - poly(epsilon-caprolactone) KW - thermoplastics Y1 - 2018 U6 - https://doi.org/10.3390/polym10030255 SN - 2073-4360 VL - 10 IS - 3 PB - MDPI CY - Basel ER - TY - JOUR A1 - Farhan, Muhammad A1 - Rudolph, Tobias A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Torsional Fiber Actuators from Shape-memory Polymer JF - MRS Advances N2 - Humanoid robots, prosthetic limbs and exoskeletons require soft actuators to perform their primary function, which is controlled movement. In this wont we explored whether crosslinked poly[ethylene-co-(vinyl acetate)] (cPEVA) fibers, with different vinyl acetate (VA) content can serve as torsional fiber actuators. exhibiting temperature controlled reversible rotational changes. Broad melting transitions ranging from 50 to 90 degrees C for cPEVA18-165 or from 40 to 80 degrees C for cPEVA28-165 fibers in combination with complete crystallization at temperatures around 10 degrees C make them suitable actuating materials with adjustable actuation temperature ranges between 10 and 70 degrees C during repetitive cooling and heating. The obtained fibers exhibited a circular cross section with diameters around 0.4 +/- 0.1 mm, while a length of 4 cm was employed for the investigation of reversible rotational actuation after programming by twist insertion using 30 complete rotations at a temperature above melting transition. Repetitive heating and cooling between 10 to 60 degrees C or 70 degrees C of one-end-tethered programmed fibers revealed reversible rotations and torsional force. During cooling 3 +/- 1 complete rotations (Delta theta(r) = + 1080 +/- 360 degrees) in twisting direction were observed, while 4 +/- 1 turns in the opposite direction (Delta theta(r) = - 1440 +/- 1360 degrees) were found during heating. Such torsional fiber actuators, which are capable of approximately one rotation per cm fiber length, can serve as miniaturized rotary motors to provide rotational actuation in futuristic humanoid robots. Y1 - 2018 U6 - https://doi.org/10.1557/adv.2018.621 SN - 2059-8521 VL - 3 IS - 63 SP - 3861 EP - 3868 PB - Cambridge Univ. Press CY - New York ER - TY - GEN A1 - Moradian, Hanieh A1 - Roch, Toralf A1 - Lendlein, Andreas A1 - Gossen, Manfred T1 - mRNA transfection-induced activation of primary human monocytes and macrophages BT - Dependence on carrier system and nucleotide modifcation T2 - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe N2 - Monocytes and macrophages are key players in maintaining immune homeostasis. Identifying strategies to manipulate their functions via gene delivery is thus of great interest for immunological research and biomedical applications. We set out to establish conditions for mRNA transfection in hard-to-transfect primary human monocytes and monocyte-derived macrophages due to the great potential of gene expression from in vitro transcribed mRNA for modulating cell phenotypes. mRNA doses, nucleotide modifications, and different carriers were systematically explored in order to optimize high mRNA transfer rates while minimizing cell stress and immune activation. We selected three commercially available mRNA transfection reagents including liposome and polymer-based formulations, covering different application spectra. Our results demonstrate that liposomal reagents can particularly combine high gene transfer rates with only moderate immune cell activation. For the latter, use of specific nucleotide modifications proved essential. In addition to improving efficacy of gene transfer, our findings address discrete aspects of innate immune activation using cytokine and surface marker expression, as well as cell viability as key readouts to judge overall transfection efficiency. The impact of this study goes beyond optimizing transfection conditions for immune cells, by providing a framework for assessing new gene carrier systems for monocyte and macrophage, tailored to specific applications. T3 - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe - 1403 KW - sirna transfection KW - mediated delivery KW - gene delivery KW - efficient KW - immunogenicity KW - lipoplexes KW - cells KW - therapeutics KW - polarization KW - pathways Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-515694 SN - 1866-8372 IS - 1 ER - TY - GEN A1 - Farhan, Muhammad A1 - Chaudhary, Deeptangshu A1 - Nöchel, Ulrich A1 - Behl, Marc A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Electrical actuation of coated and composite fibers based on poly[ethylene-co-(vinyl acetate)] T2 - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe N2 - Robots are typically controlled by electrical signals. Resistive heating is an option to electrically trigger actuation in thermosensitive polymer systems. In this study electrically triggerable poly[ethylene-co-(vinyl acetate)] (PEVA)-based fiber actuators are realized as composite fibers as well as polymer fibers with conductive coatings. In the coated fibers, the core consists of crosslinked PEVA (cPEVA), while the conductive coating shell is achieved via a dip coating procedure with a coating thickness between 10 and 140 mu m. The conductivity of coated fibers sigma = 300-550 S m(-1) is much higher than that of the composite fibers sigma = 5.5 S m(-1). A voltage (U) of 110 V is required to heat 30 cm of coated fiber to a targeted temperature of approximate to 65 degrees C for switching in less than a minute. Cyclic electrical actuation investigations reveal epsilon '(rev) = 5 +/- 1% reversible change in length for coated fibers. The fabrication of such electro-conductive polymeric actuators is suitable for upscaling so that their application potential as artificial muscles can be explored in future studies. T3 - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe - 1375 KW - artificial muscles KW - fiber actuators KW - resistive heating KW - shape‐memory polymer actuators KW - soft robotics Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-571679 SN - 1866-8372 IS - 2 ER - TY - JOUR A1 - Moradian, Hanieh A1 - Roch, Toralf A1 - Lendlein, Andreas A1 - Gossen, Manfred T1 - mRNA transfection-induced activation of primary human monocytes and macrophages BT - Dependence on carrier system and nucleotide modifcation JF - Scientific reports N2 - Monocytes and macrophages are key players in maintaining immune homeostasis. Identifying strategies to manipulate their functions via gene delivery is thus of great interest for immunological research and biomedical applications. We set out to establish conditions for mRNA transfection in hard-to-transfect primary human monocytes and monocyte-derived macrophages due to the great potential of gene expression from in vitro transcribed mRNA for modulating cell phenotypes. mRNA doses, nucleotide modifications, and different carriers were systematically explored in order to optimize high mRNA transfer rates while minimizing cell stress and immune activation. We selected three commercially available mRNA transfection reagents including liposome and polymer-based formulations, covering different application spectra. Our results demonstrate that liposomal reagents can particularly combine high gene transfer rates with only moderate immune cell activation. For the latter, use of specific nucleotide modifications proved essential. In addition to improving efficacy of gene transfer, our findings address discrete aspects of innate immune activation using cytokine and surface marker expression, as well as cell viability as key readouts to judge overall transfection efficiency. The impact of this study goes beyond optimizing transfection conditions for immune cells, by providing a framework for assessing new gene carrier systems for monocyte and macrophage, tailored to specific applications. KW - sirna transfection KW - mediated delivery KW - gene delivery KW - efficient KW - immunogenicity KW - lipoplexes KW - cells KW - therapeutics KW - polarization KW - pathways Y1 - 2020 U6 - https://doi.org/10.1038/s41598-020-60506-4 SN - 2045-2322 VL - 10 IS - 1 SP - 1 EP - 15 PB - Springer Nature CY - London ER - TY - GEN A1 - Jiang, Yi A1 - Mansfeld, Ulrich A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Programmable microscale stiffness pattern of flat polymeric substrates by temperature-memory technology T2 - Postprints der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe N2 - Temperature-memory technology was utilized to generate flat substrates with a programmable stiffness pattern from cross-linked poly(ethylene-co-vinyl acetate) substrates with cylindrical microstructures. Programmed substrates were obtained by vertical compression at temperatures in the range from 60 to 100 degrees C and subsequent cooling, whereby a flat substrate was achieved by compression at 72 degrees C, as documented by scanning electron microscopy and atomic force microscopy (AFM). AFM nanoindentation experiments revealed that all programmed substrates exhibited the targeted stiffness pattern. The presented technology for generating polymeric substrates with programmable stiffness pattern should be attractive for applications such as touchpads. optical storage, or cell instructive substrates. T3 - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe - 1102 KW - shape KW - surfaces KW - modulus Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-469745 SN - 1866-8372 VL - 9 IS - 1 SP - 181 EP - 188 ER - TY - JOUR A1 - Lau, Skadi A1 - Gossen, Manfred A1 - Lendlein, Andreas A1 - Jung, Friedrich T1 - Differential sensitivity of assays for determining vein endothelial cell senescence JF - Clinical hemorheology and microcirculation : blood flow and vessels N2 - In vivo endothelialization of polymer-based cardiovascular implant materials is a promising strategy to reduce the risk of platelet adherence and the subsequent thrombus formation and implant failure. However, endothelial cells from elderly patients are likely to exhibit a senescent phenotype that may counteract endothelialization. The senescence status of cells should therefore be investigated prior to implantation of devices designed to be integrated in the blood vessel wall. Here, human umbilical vein endothelial cells (HUVEC) were cultivated up to passage (P) 4, 10 and 26/27 to determine the population doubling time and the senescence status by four different methods. Determination of the senescence-associated beta-galactosidase activity (SA-beta-Gal) was carried out by colorimetric staining and microscopy (i), as well as by photometric quantification (ii), and the expression of senescence-associated nuclear proteins p16 and p21 as well as the proliferation marker Ki67 was assessed by immunostaining (iii), and by flow cytometry (iv). The population doubling time of P27-cells was remarkably greater (103 +/- 65 h) compared to P4-cells (24 +/- 3 h) and P10-cell (37 +/- 15 h). Among the four different methods tested, the photometric SA-beta-Gal activity assay and the flow cytometric determination of p16 and Ki67 were most effective in discriminating P27-cells from P4- and P10-cells. These methods combined with functional endothelial cell analyses might aid predictions on the performance of implant endothelialization in vivo. KW - Ageing KW - population doubling time KW - senescence-associated KW - beta-galactosidase KW - cell cycle inhibitors KW - p16 KW - p21 KW - Ki67 Y1 - 2022 U6 - https://doi.org/10.3233/CH-211294 SN - 1386-0291 SN - 1875-8622 VL - 81 IS - 3 SP - 191 EP - 203 PB - IOS Press CY - Amsterdam ER - TY - JOUR A1 - Lau, Skadi A1 - Maier, Anna A1 - Braune, Steffen A1 - Gossen, Manfred A1 - Lendlein, Andreas T1 - Effect of endothelial culture medium composition on platelet responses to polymeric biomaterials JF - International journal of molecular sciences N2 - Near-physiological in vitro thrombogenicity test systems for the evaluation of blood-contacting endothelialized biomaterials requires co-cultivation with platelets (PLT). However, the addition of PLT has led to unphysiological endothelial cell (EC) detachment in such in vitro systems. A possible cause for this phenomenon may be PLT activation triggered by the applied endothelial cell medium, which typically consists of basal medium (BM) and nine different supplements. To verify this hypothesis, the influence of BM and its supplements was systematically analyzed regarding PLT responses. For this, human platelet rich plasma (PRP) was mixed with BM, BM containing one of nine supplements, or with BM containing all supplements together. PLT adherence analysis was carried out in six-channel slides with plasma-treated cyclic olefin copolymer (COC) and poly(tetrafluoro ethylene) (PTFE, as a positive control) substrates as part of the six-channel slides in the absence of EC and under static conditions. PLT activation and aggregation were analyzed using light transmission aggregometry and flow cytometry (CD62P). Medium supplements had no effect on PLT activation and aggregation. In contrast, supplements differentially affected PLT adherence, however, in a polymer- and donor-dependent manner. Thus, the use of standard endothelial growth medium (BM + all supplements) maintains functionality of PLT under EC compatible conditions without masking the differences of PLT adherence on different polymeric substrates. These findings are important prerequisites for the establishment of a near-physiological in vitro thrombogenicity test system assessing polymer-based cardiovascular implant materials in contact with EC and PLT. KW - cyclic olefin copolymer KW - poly(tetrafluoroethylene) KW - endothelial cells KW - platelets KW - in vitro thrombogenicity testing Y1 - 2021 U6 - https://doi.org/10.3390/ijms22137006 SN - 1422-0067 SN - 1661-6596 VL - 22 IS - 13 PB - Molecular Diversity Preservation International CY - Basel ER - TY - JOUR A1 - Folikumah, Makafui Y. A1 - Behl, Marc A1 - Lendlein, Andreas T1 - Reaction behaviour of peptide-based single thiol-thioesters exchange reaction substrate in the presence of externally added thiols JF - MRS communications / a publication of the Materials Research Society N2 - Identification of patterns in chemical reaction pathways aids in the effective design of molecules for specific applications. Here, we report on model reactions with a water-soluble single thiol-thioester exchange (TTE) reaction substrate, which was designed taking in view biological and medical applications. This substrate consists of the thio-depsipeptide, Ac-Pro-Leu-Gly-SLeu-Leu-Gly-NEtSH (TDP) and does not yield foul-smelling thiol exchange products when compared with aromatic thiol containing single TTE substrates. TDP generates an alpha,omega-dithiol crosslinker in situ in a 'pseudo intramolecular' TTE. Competitive intermolecular TTE of TDP with externally added "basic" thiols increased the crosslinker concentration whilst "acidic" thiols decreased its concentration. TDP could potentially enable in situ bioconjugation and crosslinking applications. KW - Biomaterials KW - Biomimetic KW - Mass spectrometry KW - Nuclear magnetic resonance KW - (NMR) Y1 - 2021 U6 - https://doi.org/10.1557/s43579-021-00041-z SN - 2159-6859 SN - 2159-6867 VL - 11 IS - 4 SP - 402 EP - 410 PB - Springer CY - Berlin ER - TY - GEN A1 - Deng, Zijun A1 - Wang, Weiwei A1 - Xua, Xun A1 - Gould, Oliver E. C. A1 - Kratz, Karl A1 - Ma, Nan A1 - Lendlein, Andreas T1 - Polymeric sheet actuators with programmable bioinstructivity T2 - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe N2 - Stem cells are capable of sensing and processing environmental inputs, converting this information to output a specific cell lineage through signaling cascades. Despite the combinatorial nature of mechanical, thermal, and biochemical signals, these stimuli have typically been decoupled and applied independently, requiring continuous regulation by controlling units. We employ a programmable polymer actuator sheet to autonomously synchronize thermal and mechanical signals applied to mesenchymal stem cells (MSC5). Using a grid on its underside, the shape change of polymer sheet, as well as cell morphology, calcium (Ca2+) influx, and focal adhesion assembly, could be visualized and quantified. This paper gives compelling evidence that the temperature sensing and mechanosensing of MSC5 are interconnected via intracellular Ca2+. Up-regulated Ca2+ levels lead to a remarkable alteration of histone H3K9 acetylation and activation of osteogenic related genes. The interplay of physical, thermal, and biochemical signaling was utilized to accelerate the cell differentiation toward osteogenic lineage. The approach of programmable bioinstructivity provides a fundamental principle for functional biomaterials exhibiting multifaceted stimuli on differentiation programs. Technological impact is expected in the tissue engineering of periosteum for treating bone defects. T3 - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe - 1441 KW - reversible shape-memory actuator KW - mesenchymal stem cells KW - calcium influx KW - HDAC1 KW - RUNX2 Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-515490 SN - 1866-8372 IS - 4 ER - TY - JOUR A1 - Saretia, Shivam A1 - Machatschek, Rainhard Gabriel A1 - Lendlein, Andreas T1 - Degradation kinetics of oligo(ε-caprolactone) ultrathin films BT - Influence of crystallinity JF - MRS advances : a journal of the Materials Research Society (MRS) N2 - The potential of using crystallinity as morphological parameter to control polyester degradation in acidic environments is explored in ultrathin films by Langmuir technique. Films of hydroxy or methacrylate end-capped oligo(epsilon-caprolactone) (OCL) are prepared at the air-water interface as a function of mean molecular area (MMA). The obtained amorphous, partially crystalline or highly crystalline ultrathin films of OCL are hydrolytically degraded at pH similar to 1.2 on water surface or on silicon surface as-transferred films. A high crystallinity reduces the hydrolytic degradation rate of the films on both water and solid surfaces. Different acceleration rates of hydrolytic degradation of semi-crystalline films are achieved either by crystals complete melting, partially melting, or by heating them below their melting temperatures. Semi-crystalline OCL films transferred via water onto a solid surface retain their crystalline morphology, degrade in a controlled manner, and are of interest as thermoswitchable coatings for cell substrates and medical devices. Y1 - 2021 U6 - https://doi.org/10.1557/s43580-021-00067-4 SN - 2059-8521 VL - 6 IS - 33 SP - 790 EP - 795 PB - Springer Nature Switzerland AG CY - Cham ER - TY - JOUR A1 - Tarazona Lizcano, Natalia Andrea A1 - Machatschek, Rainhard Gabriel A1 - Balcucho, Jennifer A1 - Castro-Mayorga, Jinneth Lorena A1 - Saldarriaga, Juan Francisco A1 - Lendlein, Andreas T1 - Opportunities and challenges for integrating the development of sustainable polymer materials within an international circular (bio)economy concept JF - MRS energy & sustainability : science & technology & socio-economics & policy N2 - The production and consumption of commodity polymers have been an indispensable part of the development of our modern society. Owing to their adjustable properties and variety of functions, polymer-based materials will continue playing important roles in achieving the Sustainable Development Goals (SDG)s, defined by the United Nations, in key areas such as healthcare, transport, food preservation, construction, electronics, and water management. Considering the serious environmental crisis, generated by increasing consumption of plastics, leading-edge polymers need to incorporate two types of functions: Those that directly arise from the demands of the application (e.g. selective gas and liquid permeation, actuation or charge transport) and those that enable minimization of environmental harm, e.g., through prolongation of the functional lifetime, minimization of material usage, or through predictable disintegration into non-toxic fragments. Here, we give examples of how the incorporation of a thoughtful combination of properties/functions can enhance the sustainability of plastics ranging from material design to waste management. We focus on tools to measure and reduce the negative impacts of plastics on the environment throughout their life cycle, the use of renewable sources for their synthesis, the design of biodegradable and/or recyclable materials, and the use of biotechnological strategies for enzymatic recycling of plastics that fits into a circular bioeconomy. Finally, we discuss future applications for sustainable plastics with the aim to achieve the SDGs through international cooperation.
Leading-edge polymer-based materials for consumer and advanced applications are necessary to achieve sustainable development at a global scale. It is essential to understand how sustainability can be incorporated in these materials via green chemistry, the integration of bio-based building blocks from biorefineries, circular bioeconomy strategies, and combined smart and functional capabilities. KW - biomaterial KW - degradable KW - functional KW - life cycle assessment KW - renewable KW - sustainability Y1 - 2022 U6 - https://doi.org/10.1557/s43581-021-00015-7 SN - 2329-2229 SN - 2329-2237 VL - 9 IS - 1 SP - 28 EP - 34 PB - Springer Nature CY - London ER - TY - JOUR A1 - Tung, Wing Tai A1 - Sun, Xianlei A1 - Wang, Weiwei A1 - Xu, Xun A1 - Ma, Nan A1 - Lendlein, Andreas T1 - Structure, mechanical properties and degradation behavior of electrospun PEEU fiber meshes and films JF - MRS advances : a journal of the Materials Research Society (MRS) N2 - The capability of a degradable implant to provide mechanical support depends on its degradation behavior. Hydrolytic degradation was studied for a polyesteretherurethane (PEEU70), which consists of poly(p-dioxanone) (PPDO) and poly(epsilon-caprolactone) (PCL) segments with a weight ratio of 70:30 linked by diurethane junction units. PEEU70 samples prepared in the form of meshes with average fiber diameters of 1.5 mu m (mesh1.5) and 1.2 mu m (mesh1.2), and films were sterilized and incubated in PBS at 37 degrees C with 5 vol% CO2 supply for 1 to 6 weeks. Degradation features, such as cracks or wrinkles, became apparent from week 4 for all samples. Mass loss was found to be 11 wt%, 6 wt%, and 4 wt% for mesh1.2, mesh1.5, and films at week 6. The elongation at break decreased to under 20% in two weeks for mesh1.2. In case of the other two samples, this level of degradation was achieved after 4 weeks. The weight average molecular weight of both PEEU70 mesh and film samples decreased to below 30 kg/mol when elongation at break dropped below 20%. The time period of sustained mechanical stability of PEEU70-based meshes depends on the fiber diameter and molecular weight. Y1 - 2021 U6 - https://doi.org/10.1557/s43580-020-00001-0 SN - 2059-8521 VL - 6 IS - 10 SP - 276 EP - 282 PB - Springer Nature Switzerland AG CY - Cham ER - TY - JOUR A1 - Xu, Xun A1 - Nie, Yan A1 - Wang, Weiwei A1 - Ullah, Imran A1 - Tung, Wing Tai A1 - Ma, Nan A1 - Lendlein, Andreas T1 - Generation of 2.5D lung bud organoids from human induced pluripotent stem cells JF - Clinical hemorheology and microcirculation : blood flow and vessels N2 - Human induced pluripotent stem cells (hiPSCs) are a promising cell source to generate the patient-specific lung organoid given their superior differentiation potential. However, the current 3D cell culture approach is tedious and time-consuming with a low success rate and high batch-to-batch variability. Here, we explored the establishment of lung bud organoids by systematically adjusting the initial confluence levels and homogeneity of cell distribution. The efficiency of single cell seeding and clump seeding was compared. Instead of the traditional 3D culture, we established a 2.5D organoid culture to enable the direct monitoring of the internal structure via microscopy. It was found that the cell confluence and distribution prior to induction were two key parameters, which strongly affected hiPSC differentiation trajectories. Lung bud organoids with positive expression of NKX 2.1, in a single-cell seeding group with homogeneously distributed hiPSCs at 70% confluence (SC 70% hom) or a clump seeding group with heterogeneously distributed cells at 90% confluence (CL 90% het), can be observed as early as 9 days post induction. These results suggest that a successful lung bud organoid formation with single-cell seeding of hiPSCs requires a moderate confluence and homogeneous distribution of cells, while high confluence would be a prominent factor to promote the lung organoid formation when seeding hiPSCs as clumps. 2.5D organoids generated with defined culture conditions could become a simple, efficient, and valuable tool facilitating drug screening, disease modeling and personalized medicine. KW - lung organoid KW - human induced pluripotent stem cell KW - cell culture Y1 - 2021 U6 - https://doi.org/10.3233/CH-219111 SN - 1386-0291 SN - 1875-8622 VL - 79 IS - 1 SP - 217 EP - 230 PB - IOS Press CY - Amsterdam ER - TY - JOUR A1 - Zhou, Shuo A1 - Xu, Xun A1 - Ma, Nan A1 - Jung, Friedrich A1 - Lendlein, Andreas T1 - Influence of sterilization conditions on sulfate-functionalized polyGGE JF - Clinical hemorheology and microcirculation : blood flow and vessels N2 - Sulfated biomolecules are known to influence numerous biological processes in all living organisms. Particularly, they contribute to prevent and inhibit the hypercoagulation condition. The failure of polymeric implants and blood contacting devices is often related to hypercoagulation and microbial contamination. Here, bioactive sulfated biomacromolecules are mimicked by sulfation of poly(glycerol glycidyl ether) (polyGGE) films. Autoclaving, gamma-ray irradiation and ethylene oxide (EtO) gas sterilization techniques were applied to functionalized materials. The sulfate group density and hydrophilicity of sulfated polymers were decreased while chain mobility and thermal degradation were enhanced post autoclaving when compared to those after EtO sterilization. These results suggest that a quality control after sterilization is mandatory to ensure the amount and functionality of functionalized groups are retained. KW - Sulfated polymer KW - sulfation KW - sterilization KW - ethylene oxide Y1 - 2021 U6 - https://doi.org/10.3233/CH-211241 SN - 1386-0291 SN - 1875-8622 VL - 79 IS - 4 SP - 597 EP - 608 PB - IOS Press CY - Amsterdam ER - TY - JOUR A1 - Nie, Yan A1 - Wang, Weiwei A1 - Xu, Xun A1 - Ma, Nan A1 - Lendlein, Andreas T1 - The response of human induced pluripotent stem cells to cyclic temperature changes explored by BIO-AFM JF - MRS advances : a journal of the Materials Research Society (MRS) N2 - Human induced pluripotent stem cells (hiPSCs) are highly sensitive to extrinsic physical and biochemical signals from their extracellular microenvironments. In this study, we analyzed the effect of cyclic temperature changes on hiPSCs behaviors, especially by means of scanning force microscopy (BIO-AFM). The alternation in cellular mechanics, as well as the secretion and pattern of deposition of extracellular matrix (ECM) protein in hiPSCs were evaluated. The arrangement of the actin cytoskeleton changed with the variation of the temperature. The rearranged cytoskeleton architecture led to the subsequent changes in cell mechanics (Young's modulus of hiPSCs). With the exposure to the cyclic cold stimuli, an increase in the average surface roughness (Ra) and roughness mean square (RMS) was detected. This observation might be at least in part due to the upregulated secretion of Laminin alpha 5 during repeated temporary cooling. The expression of pluripotent markers, NANOG and SOX2, was not impaired in hiPSCs, when exposed to the cyclic cold stimuli for 24 h. Our findings provide an insight into the effect of temperature on the hiPSC behaviors, which may contribute to a better understanding of the application of locally controlled therapeutic hypothermia. Y1 - 2021 U6 - https://doi.org/10.1557/s43580-021-00110-4 SN - 2059-8521 VL - 6 IS - 31 SP - 745 EP - 749 PB - Springer CY - Cham ER - TY - JOUR A1 - Moradian, Hanieh A1 - Roch, Toralf A1 - Anthofer, Larissa A1 - Lendlein, Andreas A1 - Gossen, Manfred T1 - Chemical modification of uridine modulates mRNA-mediated proinflammatory and antiviral response in primary human macrophages JF - Molecular therapy N2 - In vitro transcribed (IVT)-mRNA has been accepted as a promising therapeutic modality. Advances in facile and rapid production technologies make IVT-mRNA an appealing alternative to protein- or virus-based medicines. Robust expression levels, lack of genotoxicity, and their manageable immunogenicity benefit its clinical applicability. We postulated that innate immune responses of therapeutically relevant human cells can be tailored or abrogated by combinations of 5'-end and internal IVT-mRNA modifications. Using primary human macrophages as targets, our data show the particular importance of uridine modifications for IVT-mRNA performance. Among five nucleotide modification schemes tested, 5-methoxy-uridine outperformed other modifications up to 4-fold increased transgene expression, triggering moderate proinflammatory and non-detectable antiviral responses. Macrophage responses against IVT-mRNAs exhibiting high immunogenicity (e.g., pseudouridine) could be minimized upon HPLC purification. Conversely, 5'-end modifications had only modest effects on mRNA expression and immune responses. Our results revealed how the uptake of chemically modified IVT-mRNA impacts human macrophages, responding with distinct patterns of innate immune responses concomitant with increased transient transgene expression. We anticipate our findings are instrumental to predictively address specific cell responses required for a wide range of therapeutic applications from eliciting controlled immunogenicity in mRNA vaccines to, e.g., completely abrogating cell activation in protein replacement therapies. Y1 - 2022 U6 - https://doi.org/10.1016/j.omtn.2022.01.004 SN - 2162-2531 VL - 27 SP - 854 EP - 869 PB - Cell Press CY - Cambridge ER -