TY  - GEN
A1  - Bhattacharyya, Biswajit
A1  - Balischewski, Christian
A1  - Sperlich, Eric
A1  - Günter, Christina
A1  - Mies, Stefan
A1  - Kelling, Alexandra
A1  - Taubert, Andreas
T1  - N-Butyl Pyridinium Diiodido Argentate(I)
BT  - A One-Dimensional Ag-I Network with Superior Solid-State Ionic Conductivity at Room Temperature
T2  - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe
N2  - A new solid-state material, N-butyl pyridinium diiodido argentate(I), is synthesized using a simple and effective one-pot approach. In the solid state, the compound exhibits 1D ([AgI2](-))(n) chains that are stabilized by the N-butyl pyridinium cation. The 1D structure is further manifested by the formation of long, needle-like crystals, as revealed from electron microscopy. As the general composition is derived from metal halide-based ionic liquids, the compound has a low melting point of 100-101 degrees C, as confirmed by differential scanning calorimetry. Most importantly, the compound has a conductivity of 10(-6) S cm(-1) at room temperature. At higher temperatures the conductivity increases and reaches to 10(-4 )S cm(-1) at 70 degrees C. In contrast to AgI, however, the current material has a highly anisotropic 1D arrangement of the ionic domains. This provides direct and tuneable access to fast and anisotropic ionic conduction. The material is thus a significant step forward beyond current ion conductors and a highly promising prototype for the rational design of highly conductive ionic solid-state conductors for battery or solar cell applications.
T3  - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe - 1341 
KW  - AgI
KW  - ionic conductivity
KW  - Ionic liquids
KW  - thermal properties
Y1  - 2023
U6  - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-604874
SN  - 1866-8372
IS  - 1341
ER  - 
TY  - GEN
A1  - Schneider, Matthias
A1  - Günter, Christina
A1  - Taubert, Andreas
T1  - Co-deposition of a hydrogel/calcium phosphate hybrid layer on 3D printed poly(lactic acid) scaffolds via dip coating
BT  - Towards automated biomaterials fabrication
T2  - Postprints der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe
N2  - The article describes the surface modification of 3D printed poly(lactic acid) (PLA) scaffolds with calcium phosphate (CP)/gelatin and CP/chitosan hybrid coating layers. The presence of gelatin or chitosan significantly enhances CP co-deposition and adhesion of the mineral layer on the PLA scaffolds. The hydrogel/CP coating layers are fairly thick and the mineral is a mixture of brushite, octacalcium phosphate, and hydroxyapatite. Mineral formation is uniform throughout the printed architectures and all steps (printing, hydrogel deposition, and mineralization) are in principle amenable to automatization. Overall, the process reported here therefore has a high application potential for the controlled synthesis of biomimetic coatings on polymeric biomaterials.
T3  - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe - 1057 
KW  - 3D printing
KW  - dip-coating
KW  - poly(lactic acid)
KW  - PLA
KW  - calcium phosphate
KW  - gelatin
KW  - chitosan
KW  - hydrogel
KW  - calcium phosphate hybrid material
KW  - biomaterials
Y1  - 2020
U6  - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-474427
SN  - 1866-8372
IS  - 1057
ER  -