TY - JOUR A1 - Wang, Weijia A1 - Kaune, Gunar A1 - Perlich, Jan A1 - Paradakis, Christine M. A1 - Bivigou Koumba, Achille Mayelle A1 - Laschewsky, André A1 - Schlage, K. A1 - Röhlsberger, Ralf A1 - Roth, Stephan V. A1 - Cubitt, Robert A1 - Müller-Buschbaum, Peter T1 - Swelling and switching kinetics of gold coated end-capped poly(N-isopropylacrylamide) thin films N2 - Thin thermoresponsive hydrogel films of poly(N-isopropylacrylamide) end-capped with n-butyltrithiocarbonate(nbc- PNIPAM) oil si I icon supports with a gold layer on top, causing an asymmetric confinement, are investigated. For two different gold layer thicknesses (nominally 0.4 and 5 rim), the swelling and switching kinetics are probed with in situ neutron reflectivity. With a temperature jump from 23 to 40 degrees C the film is switched from a swollen into a collapsed state. For the thin gold layer this switching is faster as compared to the thick gold layer. The switching is a two-step process of water release and a subsequent structural relaxation. fit swelling and deswelling cycles, aging of the films is probed. After five cycles, the film exhibits enhanced water storage capacity. Grazing-incidence small-angle X-ray scattering (GISAXS) shows that these gold coated nbc-PNIPAM films do not age with respect to the inner structure but slightly roughen at the gold surface. As revealed by atomic force microscopy, the morphology of the gold layer is changed by the water uptake and release. Y1 - 2010 UR - http://pubs.acs.org/journal/mamobx U6 - https://doi.org/10.1021/Ma902637a SN - 0024-9297 ER - TY - JOUR A1 - Zhong, Qi A1 - Wang, Weinan A1 - Adelsberger, Joseph A1 - Golosova, Anastasia A1 - Koumba, Achille M. Bivigou A1 - Laschewsky, André A1 - Funari, Sergio S. A1 - Perlich, Jan A1 - Roth, Stephan V. A1 - Papadakis, Christine M. A1 - Müller-Buschbaum, Peter T1 - Collapse transition in thin films of poly(methoxydiethylenglycol acrylate) JF - Colloid and polymer science : official journal of the Kolloid-Gesellschaft N2 - The thermal behavior of poly(methoxydiethylenglycol acrylate) (PMDEGA) is studied in thin hydrogel films on solid supports and is compared with the behavior in aqueous solution. The PMDEGA hydrogel film thickness is varied from 2 to 422 nm. Initially, these films are homogenous, as measured with optical microscopy, atomic force microscopy, X-ray reflectivity, and grazing-incidence small-angle X-ray scattering (GISAXS). However, they tend to de-wet when stored under ambient conditions. Along the surface normal, no long-ranged correlations between substrate and film surface are detected with GISAXS, due to the high mobility of the polymer at room temperature. The swelling of the hydrogel films as a function of the water vapor pressure and the temperature are probed for saturated water vapor pressures between 2,380 and 3,170 Pa. While the swelling capability is found to increase with water vapor pressure, swelling in dependence on the temperature revealed a collapse phase transition of a lower critical solution temperature type. The transition temperature decreases from 40.6 A degrees C to 36.6 A degrees C with increasing film thickness, but is independent of the thickness for very thin films below a thickness of 40 nm. The observed transition temperature range compares well with the cloud points observed in dilute (0.1 wt.%) and semi-dilute (5 wt.%) solution which decrease from 45 A degrees C to 39 A degrees C with increasing concentration. KW - Hydrogel KW - Thin film KW - Thermoresponsive KW - LCST behavior KW - GISAXS KW - AFM Y1 - 2011 U6 - https://doi.org/10.1007/s00396-011-2384-1 SN - 0303-402X VL - 289 IS - 5-6 SP - 569 EP - 581 PB - Springer CY - New York ER - TY - JOUR A1 - Zhong, Qi A1 - Mi, Lei A1 - Metwalli, Ezzeldin A1 - Biessmann, Lorenz A1 - Philipp, Martine A1 - Miasnikova, Anna A1 - Laschewsky, Andre A1 - Papadakis, Christine M. A1 - Cubitt, Robert A1 - Schwartzkopf, Matthias A1 - Roth, Stephan V. A1 - Wang, Jiping A1 - Müller-Buschbaum, Peter T1 - Effect of chain architecture on the swelling and thermal response of star-shaped thermo-responsive (poly(methoxy diethylene glycol acrylate)-block-polystyrene)(3) block copolymer films JF - Soft matter N2 - The effect of chain architecture on the swelling and thermal response of thin films obtained from an amphiphilic three-arm star-shaped thermo-responsive block copolymer poly(methoxy diethylene glycol acrylate)-block-polystyrene ((PMDEGA-b-PS)(3)) is investigated by in situ neutron reflectivity (NR) measurements. The PMDEGA and PS blocks are micro-phase separated with randomly distributed PS nanodomains. The (PMDEGA-b-PS)(3) films show a transition temperature (TT) at 33 degrees C in white light interferometry. The swelling capability of the (PMDEGA-b-PS)(3) films in a D2O vapor atmosphere is better than that of films from linear PS-b-PMDEGA-b-PS triblock copolymers, which can be attributed to the hydrophilic end groups and limited size of the PS blocks in (PMDEGA-b-PS)(3). However, the swelling kinetics of the as-prepared (PMDEGA-b-PS)(3) films and the response of the swollen film to a temperature change above the TT are significantly slower than that in the PS-b-PMDEGA-b-PS films, which may be related to the conformation restriction by the star-shape. Unlike in the PS-b-PMDEGA-b-PS films, the amount of residual D2O in the collapsed (PMDEGA-b-PS)(3) films depends on the final temperature. It decreases from (9.7 +/- 0.3)% to (7.0 +/- 0.3)% or (6.0 +/- 0.3)% when the final temperatures are set to 35 degrees C, 45 degrees C and 50 degrees C, respectively. This temperature-dependent reduction of embedded D2O originates from the hindrance of chain conformation from the star-shaped chain architecture. Y1 - 2018 U6 - https://doi.org/10.1039/c8sm00965a SN - 1744-683X SN - 1744-6848 VL - 14 IS - 31 SP - 6582 EP - 6594 PB - Royal Society of Chemistry CY - Cambridge ER -