TY - JOUR A1 - Zu, Fengshuo A1 - Schultz, Thorsten A1 - Wolff, Christian Michael A1 - Shin, Dongguen A1 - Frohloff, Lennart A1 - Neher, Dieter A1 - Amsalem, Patrick A1 - Koch, Norbert T1 - Position-locking of volatile reaction products by atmosphere and capping layers slows down photodecomposition of methylammonium lead triiodide perovskite JF - RSC Advances N2 - The remarkable progress of metal halide perovskites in photovoltaics has led to the power conversion efficiency approaching 26%. However, practical applications of perovskite-based solar cells are challenged by the stability issues, of which the most critical one is photo-induced degradation. Bare CH3NH3PbI3 perovskite films are known to decompose rapidly, with methylammonium and iodine as volatile species and residual solid PbI2 and metallic Pb, under vacuum under white light illumination, on the timescale of minutes. We find, in agreement with previous work, that the degradation is non-uniform and proceeds predominantly from the surface, and that illumination under N-2 and ambient air (relative humidity 20%) does not induce substantial degradation even after several hours. Yet, in all cases the release of iodine from the perovskite surface is directly identified by X-ray photoelectron spectroscopy. This goes in hand with a loss of organic cations and the formation of metallic Pb. When CH3NH3PbI3 films are covered with a few nm thick organic capping layer, either charge selective or non-selective, the rapid photodecomposition process under ultrahigh vacuum is reduced by more than one order of magnitude, and becomes similar in timescale to that under N-2 or air. We conclude that the light-induced decomposition reaction of CH3NH3PbI3, leading to volatile methylammonium and iodine, is largely reversible as long as these products are restrained from leaving the surface. This is readily achieved by ambient atmospheric pressure, as well as a thin organic capping layer even under ultrahigh vacuum. In addition to explaining the impact of gas pressure on the stability of this perovskite, our results indicate that covalently "locking" the position of perovskite components at the surface or an interface should enhance the overall photostability. Y1 - 2020 U6 - https://doi.org/10.1039/d0ra03572f SN - 2046-2069 VL - 10 IS - 30 SP - 17534 EP - 17542 PB - Royal Society of Chemistry CY - Cambridge ER - TY - JOUR A1 - Perdigon-Toro, Lorena A1 - Zhang, Huotian A1 - Markina, Anastaa si A1 - Yuan, Jun A1 - Hosseini, Seyed Mehrdad A1 - Wolff, Christian Michael A1 - Zuo, Guangzheng A1 - Stolterfoht, Martin A1 - Zou, Yingping A1 - Gao, Feng A1 - Andrienko, Denis A1 - Shoaee, Safa A1 - Neher, Dieter T1 - Barrierless free charge generation in the high-performance PM6:Y6 bulk heterojunction non-fullerene solar cell JF - Advanced materials N2 - Organic solar cells are currently experiencing a second golden age thanks to the development of novel non-fullerene acceptors (NFAs). Surprisingly, some of these blends exhibit high efficiencies despite a low energy offset at the heterojunction. Herein, free charge generation in the high-performance blend of the donor polymer PM6 with the NFA Y6 is thoroughly investigated as a function of internal field, temperature and excitation energy. Results show that photocurrent generation is essentially barrierless with near-unity efficiency, regardless of excitation energy. Efficient charge separation is maintained over a wide temperature range, down to 100 K, despite the small driving force for charge generation. Studies on a blend with a low concentration of the NFA, measurements of the energetic disorder, and theoretical modeling suggest that CT state dissociation is assisted by the electrostatic interfacial field which for Y6 is large enough to compensate the Coulomb dissociation barrier. KW - driving force KW - non-fullerene acceptors KW - organic solar cells KW - photocurrent generation Y1 - 2020 U6 - https://doi.org/10.1002/adma.201906763 SN - 0935-9648 SN - 1521-4095 VL - 32 IS - 9 PB - Wiley-VCH CY - Weinheim ER - TY - GEN A1 - Stolterfoht, Martin A1 - Grischek, Max A1 - Caprioglio, Pietro A1 - Wolff, Christian Michael A1 - Gutierrez-Partida, Emilio A1 - Peña-Camargo, Francisco A1 - Rothhardt, Daniel A1 - Zhang, Shanshan A1 - Raoufi, Meysam A1 - Wolansky, Jakob A1 - Abdi-Jalebi, Mojtaba A1 - Stranks, Samuel D. A1 - Albrecht, Steve A1 - Kirchartz, Thomas A1 - Neher, Dieter T1 - How to quantify the efficiency potential of neat perovskite films BT - Perovskite semiconductors with an implied efficiency exceeding 28% T2 - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe N2 - Perovskite photovoltaic (PV) cells have demonstrated power conversion efficiencies (PCE) that are close to those of monocrystalline silicon cells; however, in contrast to silicon PV, perovskites are not limited by Auger recombination under 1-sun illumination. Nevertheless, compared to GaAs and monocrystalline silicon PV, perovskite cells have significantly lower fill factors due to a combination of resistive and non-radiative recombination losses. This necessitates a deeper understanding of the underlying loss mechanisms and in particular the ideality factor of the cell. By measuring the intensity dependence of the external open-circuit voltage and the internal quasi-Fermi level splitting (QFLS), the transport resistance-free efficiency of the complete cell as well as the efficiency potential of any neat perovskite film with or without attached transport layers are quantified. Moreover, intensity-dependent QFLS measurements on different perovskite compositions allows for disentangling of the impact of the interfaces and the perovskite surface on the non-radiative fill factor and open-circuit voltage loss. It is found that potassium-passivated triple cation perovskite films stand out by their exceptionally high implied PCEs > 28%, which could be achieved with ideal transport layers. Finally, strategies are presented to reduce both the ideality factor and transport losses to push the efficiency to the thermodynamic limit. T3 - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe - 1434 KW - non-radiative interface recombination KW - perovskite solar cells KW - photoluminescence Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-516622 SN - 1866-8372 IS - 17 ER - TY - GEN A1 - Wang, Qiong A1 - Smith, Joel A. A1 - Skroblin, Dieter A1 - Steele, Julian A. A1 - Wolff, Christian Michael A1 - Caprioglio, Pietro A1 - Stolterfoht, Martin A1 - Köbler, Hans A1 - Turren-Cruz, Silver-Hamill A1 - Li, Meng A1 - Gollwitzer, Christian A1 - Neher, Dieter A1 - Abate, Antonio T1 - Managing phase purities and crystal orientation for high-performance and photostable cesium lead halide perovskite solar cells T2 - Postprints der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe N2 - Inorganic perovskites with cesium (Cs+) as the cation have great potential as photovoltaic materials if their phase purity and stability can be addressed. Herein, a series of inorganic perovskites is studied, and it is found that the power conversion efficiency of solar cells with compositions CsPbI1.8Br1.2, CsPbI2.0Br1.0, and CsPbI2.2Br0.8 exhibits a high dependence on the initial annealing step that is found to significantly affect the crystallization and texture behavior of the final perovskite film. At its optimized annealing temperature, CsPbI1.8Br1.2 exhibits a pure orthorhombic phase and only one crystal orientation of the (110) plane. Consequently, this allows for the best efficiency of up to 14.6% and the longest operational lifetime, T-S80, of approximate to 300 h, averaged of over six solar cells, during the maximum power point tracking measurement under continuous light illumination and nitrogen atmosphere. This work provides essential progress on the enhancement of photovoltaic performance and stability of CsPbI3 - xBrx perovskite solar cells. T3 - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe - 1210 KW - cesium lead halides KW - crystal orientation KW - inorganic perovskites KW - ISOS-L-1I protocol KW - phase purity KW - photostability Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-525374 SN - 1866-8372 IS - 9 ER - TY - GEN A1 - Wolff, Christian Michael A1 - Canil, Laura A1 - Rehermann, Carolin A1 - Nguyen, Ngoc Linh A1 - Zu, Fengshuo A1 - Ralaiarisoa, Maryline A1 - Caprioglio, Pietro A1 - Fiedler, Lukas A1 - Stolterfoht, Martin A1 - Kogikoski, Junior, Sergio A1 - Bald, Ilko A1 - Koch, Norbert A1 - Unger, Eva L. A1 - Dittrich, Thomas A1 - Abate, Antonio A1 - Neher, Dieter T1 - Correction to 'Perfluorinated self-assembled monolayers enhance the stability and efficiency of inverted perovskite solar cells' (2020, 14 (2), 1445−1456) T2 - ACS nano Y1 - 2020 U6 - https://doi.org/10.1021/acsnano.0c08081 SN - 1936-0851 SN - 1936-086X VL - 14 IS - 11 SP - 16156 EP - 16156 PB - American Chemical Society CY - Washington, DC ER - TY - JOUR A1 - Wang, Qiong A1 - Smith, Joel A. A1 - Skroblin, Dieter A1 - Steele, Julian A. A1 - Wolff, Christian Michael A1 - Caprioglio, Pietro A1 - Stolterfoht, Martin A1 - Köbler, Hans A1 - Turren-Cruz, Silver-Hamill A1 - Li, Meng A1 - Gollwitzer, Christian A1 - Neher, Dieter A1 - Abate, Antonio T1 - Managing phase purities and crystal orientation for high-performance and photostable cesium lead halide perovskite solar cells JF - Solar RRL N2 - Inorganic perovskites with cesium (Cs+) as the cation have great potential as photovoltaic materials if their phase purity and stability can be addressed. Herein, a series of inorganic perovskites is studied, and it is found that the power conversion efficiency of solar cells with compositions CsPbI1.8Br1.2, CsPbI2.0Br1.0, and CsPbI2.2Br0.8 exhibits a high dependence on the initial annealing step that is found to significantly affect the crystallization and texture behavior of the final perovskite film. At its optimized annealing temperature, CsPbI1.8Br1.2 exhibits a pure orthorhombic phase and only one crystal orientation of the (110) plane. Consequently, this allows for the best efficiency of up to 14.6% and the longest operational lifetime, T-S80, of approximate to 300 h, averaged of over six solar cells, during the maximum power point tracking measurement under continuous light illumination and nitrogen atmosphere. This work provides essential progress on the enhancement of photovoltaic performance and stability of CsPbI3 - xBrx perovskite solar cells. KW - cesium lead halides KW - crystal orientation KW - inorganic perovskites KW - ISOS-L-1I protocol KW - phase purity KW - photostability Y1 - 2020 VL - 4 IS - 9 PB - WILEY-VCH CY - Weinheim ER - TY - JOUR A1 - Stolterfoht, Martin A1 - Grischek, Max A1 - Caprioglio, Pietro A1 - Wolff, Christian Michael A1 - Gutierrez-Partida, Emilio A1 - Peña-Camargo, Francisco A1 - Rothhardt, Daniel A1 - Zhang, Shanshan A1 - Raoufi, Meysam A1 - Wolansky, Jakob A1 - Abdi-Jalebi, Mojtaba A1 - Stranks, Samuel D. A1 - Albrecht, Steve A1 - Kirchartz, Thomas A1 - Neher, Dieter T1 - How to quantify the efficiency potential of neat perovskite films BT - Perovskite semiconductors with an implied efficiency exceeding 28% JF - Advanced Materials N2 - Perovskite photovoltaic (PV) cells have demonstrated power conversion efficiencies (PCE) that are close to those of monocrystalline silicon cells; however, in contrast to silicon PV, perovskites are not limited by Auger recombination under 1-sun illumination. Nevertheless, compared to GaAs and monocrystalline silicon PV, perovskite cells have significantly lower fill factors due to a combination of resistive and non-radiative recombination losses. This necessitates a deeper understanding of the underlying loss mechanisms and in particular the ideality factor of the cell. By measuring the intensity dependence of the external open-circuit voltage and the internal quasi-Fermi level splitting (QFLS), the transport resistance-free efficiency of the complete cell as well as the efficiency potential of any neat perovskite film with or without attached transport layers are quantified. Moreover, intensity-dependent QFLS measurements on different perovskite compositions allows for disentangling of the impact of the interfaces and the perovskite surface on the non-radiative fill factor and open-circuit voltage loss. It is found that potassium-passivated triple cation perovskite films stand out by their exceptionally high implied PCEs > 28%, which could be achieved with ideal transport layers. Finally, strategies are presented to reduce both the ideality factor and transport losses to push the efficiency to the thermodynamic limit. KW - non-radiative interface recombination KW - perovskite solar cells KW - photoluminescence Y1 - 2020 U6 - https://doi.org/10.1002/adma.202000080 SN - 0935-9648 SN - 1521-4095 VL - 32 IS - 17 SP - 1 EP - 10 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Wang, Qiong A1 - Mosconi, Edoardo A1 - Wolff, Christian Michael A1 - Li, Junming A1 - Neher, Dieter A1 - De Angelis, Filippo A1 - Suranna, Gian Paolo A1 - Grisorio, Roberto A1 - Abate, Antonio T1 - Rationalizing the molecular design of hole-selective contacts to improve charge extraction in Perovskite solar cells JF - dvanced energy materials N2 - Two new hole selective materials (HSMs) based on dangling methylsulfanyl groups connected to the C-9 position of the fluorene core are synthesized and applied in perovskite solar cells. Being structurally similar to a half of Spiro-OMeTAD molecule, these HSMs (referred as FS and DFS) share similar redox potentials but are endowed with slightly higher hole mobility, due to the planarity and large extension of their structure. Competitive power conversion efficiency (up to 18.6%) is achieved by using the new HSMs in suitable perovskite solar cells. Time-resolved photoluminescence decay measurements and electrochemical impedance spectroscopy show more efficient charge extraction at the HSM/perovskite interface with respect to Spiro-OMeTAD, which is reflected in higher photocurrents exhibited by DFS/FS-integrated perovskite solar cells. Density functional theory simulations reveal that the interactions of methylammonium with methylsulfanyl groups in DFS/FS strengthen their electrostatic attraction with the perovskite surface, providing an additional path for hole extraction compared to the sole presence of methoxy groups in Spiro-OMeTAD. Importantly, the low-cost synthesis of FS makes it significantly attractive for the future commercialization of perovskite solar cells. KW - hole extraction KW - hole selective materials KW - perovskite solar cells KW - sulfur KW - triple-cation perovskite Y1 - 2019 U6 - https://doi.org/10.1002/aenm.201900990 SN - 1614-6832 SN - 1614-6840 VL - 9 IS - 28 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Zu, Fengshuo A1 - Wolff, Christian Michael A1 - Ralaiarisoa, Maryline A1 - Amsalem, Patrick A1 - Neher, Dieter A1 - Koch, Norbert T1 - Unraveling the Electronic Properties of Lead Halide Perovskites with Surface Photovoltage in Photoemission Studies JF - ACS applied materials & interfaces N2 - The tremendous success of metal-halide perovskites, especially in the field of photovoltaics, has triggered a substantial number of studies in understanding their optoelectronic properties. However, consensus regarding the electronic properties of these perovskites is lacking due to a huge scatter in the reported key parameters, such as work function (Φ) and valence band maximum (VBM) values. Here, we demonstrate that the surface photovoltage (SPV) is a key phenomenon occurring at the perovskite surfaces that feature a non-negligible density of surface states, which is more the rule than an exception for most materials under study. With ultraviolet photoelectron spectroscopy (UPS) and Kelvin probe, we evidence that even minute UV photon fluxes (500 times lower than that used in typical UPS experiments) are sufficient to induce SPV and shift the perovskite Φ and VBM by several 100 meV compared to dark. By combining UV and visible light, we establish flat band conditions (i.e., compensate the surface-state-induced surface band bending) at the surface of four important perovskites, and find that all are p-type in the bulk, despite a pronounced n-type surface character in the dark. The present findings highlight that SPV effects must be considered in all surface studies to fully understand perovskites’ photophysical properties. KW - lead halide perovskite films KW - ultraviolet photoelectron spectroscopy KW - Kelvin probe KW - surface band bending KW - surface photovoltage KW - surface states Y1 - 2019 U6 - https://doi.org/10.1021/acsami.9b05293 SN - 1944-8244 SN - 1944-8252 VL - 11 IS - 24 SP - 21578 EP - 21583 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Kegelmann, Lukas A1 - Tockhorn, Philipp A1 - Wolff, Christian Michael A1 - Márquez, José A. A1 - Caicedo Dávila, Sebastián A1 - Korte, Lars A1 - Unold, Thomas A1 - Loevenich, Wilfried A1 - Neher, Dieter A1 - Rech, Bernd A1 - Albrecht, Steve T1 - Mixtures of Dopant-Free Spiro-OMeTAD and Water-Free PEDOT as a Passivating Hole Contact in Perovskite Solar Cells JF - ACS applied materials & interfaces N2 - Doped spiro-OMeTAD at present is the most commonly used hole transport material (HTM) in n-i-p-type perovskite solar cells, enabling high efficiencies around 22%. However, the required dopants were shown to induce nonradiative recombination of charge carriers and foster degradation of the solar cell. Here, in a novel approach, highly conductive and inexpensive water-free poly(3,4-ethylenedioxythiophene) (PEDOT) is used to replace these dopants. The resulting spiro-OMeTAD/PEDOT (SpiDOT) mixed films achieve higher lateral conductivities than layers of doped spiro-OMeTAD. Furthermore, combined transient and steady-state photoluminescence studies reveal a passivating effect of PEDOT, suppressing nonradiative recombination losses at the perovskite/HTM interface. This enables excellent quasi-Fermi level splitting values of up to 1.24 eV in perovskite/SpiDOT layer stacks and high open-circuit voltages (V-OC) up to 1.19 V in complete solar cells. Increasing the amount of dopant-free spiro-OMeTAD in SpiDOT layers is shown to enhance hole extraction and thereby improves the fill factor in solar cells. As a consequence, stabilized efficiencies up to 18.7% are realized, exceeding cells with doped spiro-OMeTAD as a HTM in this study. Moreover, to the best of our knowledge, these results mark the lowest nonradiative recombination loss in the V-OC (140 mV with respect to the Shockley-Queisser limit) and highest efficiency reported so far for perovskite solar cells using PEDOT as a HTM. KW - perovskite solar cell KW - selective contact KW - spiro-OMeTAD KW - PEDOT KW - recombination KW - passivation KW - quasi-Fermi level splitting Y1 - 2019 U6 - https://doi.org/10.1021/acsami.9b01332 SN - 1944-8244 SN - 1944-8252 VL - 11 IS - 9 SP - 9172 EP - 9181 PB - American Chemical Society CY - Washington ER -