TY - JOUR A1 - Teixeira, C. V. A1 - Blanzat, Muriel A1 - Koetz, Joachim A1 - Rico-Lattes, I. A1 - Brezesinski, Gerald T1 - In-plane miscibility and mixed bilayer microstructure in mixtures of catanionic glycolipids and zwitterionic phospholipids JF - Biochimica et biophysica acta : Biomembranes N2 - SAXS/WAXS studies were performed in combination with freeze fracture electron microscopy using mixtures of a new Gemini catanionic surfactant (Gem 16-12, formed by two sugar groups bound by a hydrocarbon spacer with 12 carbons and two 16-carbon chains) and the zwitterionic phospholipid 1,2-dipalmitoyl-sn-glycero-3-phosphocholine(DPPC) to establish the phase diagram. Gem 16-12 in water forms bilayers with the same amount of hydration water as DPPC. A frozen interdigitated phase with a low hydration number is observed below room temperature. The kinetics of the formation of this crystalline phase is very slow. Above the chain melting temperature, multilayered vesicles are formed. Mixing with DPPC produces mixed bilayers above the corresponding chain melting temperature. At room temperature, partially lamellar aggregates with local nematic order are observed. Splitting of infinite lamellae into discs is linked to immiscibility in frozen state. The ordering process is always accompanied by dehydration of the system. As a consequence, an unusual order-disorder phase transition upon cooling is observed. KW - SAXS KW - bilayer KW - gemini surfactant KW - ordering process KW - Anti-HIV KW - miscibility Y1 - 2006 U6 - https://doi.org/10.1016/j.bbamem.2006.05.025 SN - 0005-2736 VL - 1758 SP - 1797 EP - 1808 PB - Elsevier CY - Amsterdam ER - TY - JOUR A1 - Yan, Wan A1 - Fang, Liang A1 - Nöchel, Ulrich A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Influence of programming strain rates on the shape-memory performance of semicrystalline multiblock copolymers JF - Journal of polymer science : B, Polymer physics N2 - Multiblock copolymers named PCL-PIBMD consisting of crystallizable poly(epsilon-caprolactone) segments and crystallizable poly[oligo(3S-iso-butylmorpholine-2,5-dione)] segments coupled by trimethyl hexamethylene diisocyanate provide a versatile molecular architecture for achieving shape-memory effects (SMEs) in polymers. The mechanical properties as well as the SME performance of PCL-PIBMD can be tailored by the variation of physical parameters during programming such as deformation strain or applied temperature protocols. In this study, we explored the influence of applying different strain rates during programming on the resulting nanostructure of PCL-PIBMD. Programming was conducted at 50 degrees C by elongation to epsilon(m)=50% with strain rates of 1 or 10 or 50 mmmin(-1). The nanostructural changes were visualized by atomic force microscopy (AFM) measurements and investigated by in situ wide and small angle X-ray scattering experiments. With increasing the strain rate, a higher degree of orientation was observed in the amorphous domains. Simultaneously the strain-induced formation of new PIBMD crystals as well as the fragmentation of existing large PIBMD crystals occurred. The observed differences in shape fixity ratio and recovery stress of samples deformed with various strain rates can be attributed to their different nanostructures. The achieved findings can be relevant parameters for programming the shape-memory polymers with designed recovery forces. (c) 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2016, 54, 1935-1943 KW - atomic force microscopy (AFM) KW - crystal structures KW - crystallization KW - multiblock copolymer KW - stimuli-sensitive polymers KW - SAXS KW - shape-memory effect KW - WAXS KW - X-ray scattering Y1 - 2016 U6 - https://doi.org/10.1002/polb.24097 SN - 0887-6266 SN - 1099-0488 VL - 54 SP - 1935 EP - 1943 PB - Wiley-Blackwell CY - Hoboken ER - TY - JOUR A1 - Wessig, Pablo A1 - Budach, Dennis B. A1 - Thünemann, Andreas F. T1 - Dendrimers with Oligospiroketal (OSK) Building Blocks: Synthesis and Properties JF - Chemistry - a European journal N2 - The development of novel dendrimers containing oligospiroketal (OSK) rods as building blocks is described. The linkage between the core unit (CU), branching units (BU), and OSK rods relies on the CuAAC reaction between terminal alkynes and azides. Two different strategies of dendrimer synthesis were investigated and it was found that the convergent approach is clearly superior to the divergent one. SAXS measurements and MD simulations indicate that the obtained dendrimer features a globular structure with very low density. Obviously, the OSK rods stabilize a rather loose mass-fractal structure. KW - click chemistry KW - dendrimers KW - molecular rods KW - oxygen heterocycles KW - SAXS Y1 - 2015 U6 - https://doi.org/10.1002/chem.201501386 SN - 0947-6539 SN - 1521-3765 VL - 21 IS - 29 SP - 10466 EP - 10471 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Zhong, Qi A1 - Adelsberger, Joseph A1 - Niedermeier, M. A. A1 - Golosova, Anastasi A1 - Bivigou Koumba, Achille Mayelle A1 - Laschewsky, André A1 - Funari, S. S. A1 - Papadakis, Christine M. A1 - Müller-Buschbaum, Peter T1 - The influence of selective solvents on the transition behavior of poly(styrene-b-monomethoxydiethylenglycol-acrylate-b-styrene) thick films JF - Colloid and polymer science : official journal of the Kolloid-Gesellschaft N2 - Thick poly(styrene-b-monomethoxydiethylenglycol-acrylate-b-styrene) [P(S-b-MDEGA-b-S)] films (thickness 5 mu m) are prepared from different solvents on flexible substrates by solution casting and investigated with small-angle X-ray scattering. As the solvents are either PS- or PMDEGA-selective, micelles with different core-shell micellar structures are formed. In PMDEGA-selective solvents, the PS block is the core and PMDEGA is the shell, whereas in PS-selective solvents, the order is reversed. After exposing the films to liquid D2O, the micellar structure inside the films prepared from PMDEGA-selective solvents remains unchanged and only the PMDEGA (shell part) swells. On the contrary, in the films prepared from PS-selective solvents, the micelles revert the core and the shell. This reversal causes more entanglements of the PMDEGA chains between the micelles. Moreover, the thermal collapse transition of the PMDEGA block in liquid D2O is significantly broadened. Irrespective of the solvent used for film preparation, the swollen PMDEGA shell does not show a prominent shrinkage when passing the phase transition, and the transition process occurs via compaction. The collapsed micelles have a tendency to densely pack above the transition temperature. KW - Hydrogel KW - Thin film KW - Thermo-responsive KW - LCST behavior KW - SAXS Y1 - 2013 U6 - https://doi.org/10.1007/s00396-012-2879-4 SN - 0303-402X VL - 291 IS - 6 SP - 1439 EP - 1451 PB - Springer CY - New York ER -