TY - THES A1 - Fischer, Anna T1 - "Reactive hard templating" : from carbon nitrides to metal nitrides T1 - Synthese von Metallnitrid Nanostrukturen durch "Reaktives Hardtemplating" N2 - Nanostructured inorganic materials are routinely synthesized by the use of templates. Depending on the synthesis conditions of the product material, either “soft” or “hard” templates can be applied. For sol-gel processes, usually “soft” templating techniques are employed, while “hard” templates are used for high temperature synthesis pathways. In classical templating approaches, the template has the unique role of structure directing agent, in the sense that it is not participating to the chemical formation of the resulting material. This work investigates a new templating pathway to nanostructured materials, where the template is also a reagent in the formation of the final material. This concept is described as “reactive templating” and opens a synthetic path toward materials which cannot be synthesised on a nanometre scale by classical templating approaches. Metal nitrides are such kind of materials. They are usually produced by the conversion of metals or metal oxides in ammonia flow at high temperature (T > 1000°C), which make the application of classical templating techniques difficult. Graphitic carbon nitride, g-C3N4, despite its fundamental and theoretical importance, is probably one of the most promising materials to complement carbon in material science and many efforts are put in the synthesis of this material. A simple polyaddition/elimination reaction path at high temperature (T = 550°C) allows the polymerisation of cyanamide toward graphitic carbon nitride solids. By hard templating, using nanostructured silica or aluminium oxide as nanotemplates, a variety of nanostructured graphitic carbon nitrides such as nanorods, nanotubes, meso- and macroporous powders could be obtained by nanocasting or nanocoating. Due to the special semi-conducting properties of the graphitic carbon nitride matrix, the nanostructured graphitic carbon nitrides show unexpected catalytic activity for the activation of benzene in Friedel-Crafts type reactions, making this material an interesting metal free catalyst. Furthermore, due to the chemical composition of g-C3N4 and the fact that it is totally decomposed at temperatures between 600°C and 800°C even under inert atmosphere, g-C3N4 was shown to be a good nitrogen donor for the synthesis of early transition metal nitrides at high temperatures. Thus using the nanostructured carbon nitrides as “reactive templates” or “nanoreactors”, various metal nitride nanostructures, such as nanoparticles and porous frameworks could be obtained at high temperature. In this approach the carbon nitride nanostructure played both the role of the nitrogen source and of the exotemplate, imprinting its size and shape to the resulting metal nitride nanostructure. N2 - Die Nanostrukturierung anorganischer Materialien, d.h. die Kontrolle ihrer Form und Größe auf der Nanometerebene durch unterschiedliche Herstellungsverfahren, ist ein sich immer noch erweiterndes Forschungsgebiet. Eine solche Nanostrukturierung wird oft über sogenannte Templatierungsverfahren erreicht: Hier werden Formgeber (Template) mit definierter Morphologie und Größe verwendet und deren Struktur in ein neues Material abgebildet. Templatierungsverfahren können, je nach der Beschaffenheit des Templats, zwischen „weich“ und „hart“ unterschieden werden. Die Begriffe beziehen sich dabei vor allem auf die mechanische und thermische Stabilität der Template, d.h. weiche Template sind vornehmlich organischer, harte Template anorganischer Natur. Wo weiche Template in milden chemischen Verfahren eingesetzt werden, werden harte Template zur Herstellung von Materialien bei Hochtemperaturverfahren verwendet (z. B. poröse Kohlenstoffe). Allgemein dienen Template ausschließlich als Strukturgeber und gehen in keiner Weise in Form einer chemischen Reaktion in die Synthese des gewünschten Materials mit ein. Gegenstand dieser Arbeit ist ein neues Templatierungsverfahren: Die „reaktive Templatierung“. Hierbei wird das Templat - neben seiner Funktion als Strukturgeber – auch als Reagenz für die Synthese des Produktes verwendet. Dieser Synthese-Ansatz öffnet damit neue Wege für die Synthese von nanostrukturierten Materialien, die durch klassische Templatierungsansätze schwer zugänglich sind. Hierzu zählen zum Beispiel die Metallnitride. Üblicherweise werden Metallnitride über die Umsetzung von Metallen oder Metalloxiden in einem Ammoniakstrom bei Mindesttemperaturen von 1000°C gewonnen, was die Anwendung klassischer Templatierungsverfahren beinahe unmöglich macht. Darüber hinaus sind konzentrierte Lauge oder Flusssäure, welche zur Entfernung klassischer harter Template benötigt werden auch Aufschlussmittel für Metallnitride. Graphitisches Kohlenstoffnitrid, g-C3N4, ist wohl eines der meistversprechendsten Materialien um Kohlenstoff in der Materialwissenschaft zu ergänzen. Es wurden bereits viele potentielle Syntheseansätze beschrieben. Eine durch Groenewolt M. erstellte Route ist die thermisch induzierte Polykondensation von Cyanamid (NCNH2) bei 550°C. Da g-C3N4 sich zwischen 600°C und 800°C vollständig in NH3 und CxNyH-Gase zersetzt, ist es eine geeignete Festkörper-Stickstoffquelle für die Herstellung von Metalnitriden. Daher boten sich nanostrukturierte graphitische Kohlenstoffnitride als geeignete reaktive Template oder Nanoreaktoren zur Herstellung von nano-strukturierten Metalnitriden an. Die Templatierung der g-C3N4-Matrix wurde über klassische Harttemplatierungsverfahren erreicht. So konnte eine Vielzahl nano-strukturierter g-C3N4 Materialien synthetisiert werden wie zum Beispiel Nanostäbchen, Nanoröhren, mesoporöse oder makroporöse graphitische Kohlenstoffnitride. Diese haben sich interessanterweise, als metalfreie Katalysatoren für die Aktivierung von Benzol in Friedel-Crafts-Acylierung und -Alkylierung erwiesen. Durch die Infiltrierung der nano-strukturierten g-C3N4-Materialien mit diversen Metal-Präkursoren und nachfolgendem Tempern bei 800°C unter Schutzgas, konnten entsprechende nano-strukturierte Metalnitride, als Nanoabdrücke der vorgegebenen Kohlenstoffnitrid Nanostrukturen hergestellt werden. So konnten TiN, VN, GaN, AlGaN und TiVN Nanopartikel synthetisiert werden, macroporöse TiN/Kohlenstoff Komposite sowie TiN Hohlkugeln. Die so hergestellten Materialien erwiesen sich als effektive basische Katalysatoren für Aldol-Kondensations Reaktionen. KW - Kohlenstoffnitride KW - Metallnitride KW - nano KW - Templatierung KW - Carbonitrides KW - metal nitrides KW - reactive templating KW - confinement KW - nano Y1 - 2008 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-19777 ER - TY - THES A1 - Vranic, Marija T1 - 3D Structure of the biomarker hepcidin-25 in its native state T1 - 3D-Struktur des Biomarkers Hepcidin-25 im eigenen nativen Zustand N2 - Hepcidin-25 (Hep-25) plays a crucial role in the control of iron homeostasis. Since the dysfunction of the hepcidin pathway leads to multiple diseases as a result of iron imbalance, hepcidin represents a potential target for the diagnosis and treatment of disorders of iron metabolism. Despite intense research in the last decade targeted at developing a selective immunoassay for iron disorder diagnosis and treatment and better understanding the ferroportin-hepcidin interaction, questions remain. The key to resolving these underlying questions is acquiring exact knowledge of the 3D structure of native Hep-25. Since it was determined that the N-terminus, which is responsible for the bioactivity of Hep-25, contains a small Cu(II)-binding site known as the ATCUN motif, it was assumed that the Hep-25-Cu(II) complex is the native, bioactive form of the hepcidin. This structure has thus far not been elucidated in detail. Owing to the lack of structural information on metal-bound Hep-25, little is known about its possible biological role in iron metabolism. Therefore, this work is focused on structurally characterizing the metal-bound Hep-25 by NMR spectroscopy and molecular dynamics simulations. For the present work, a protocol was developed to prepare and purify properly folded Hep-25 in high quantities. In order to overcome the low solubility of Hep-25 at neutral pH, we introduced the C-terminal DEDEDE solubility tag. The metal binding was investigated through a series of NMR spectroscopic experiments to identify the most affected amino acids that mediate metal coordination. Based on the obtained NMR data, a structural calculation was performed in order to generate a model structure of the Hep-25-Ni(II) complex. The DEDEDE tag was excluded from the structural calculation due to a lack of NMR restraints. The dynamic nature and fast exchange of some of the amide protons with solvent reduced the overall number of NMR restraints needed for a high-quality structure. The NMR data revealed that the 20 Cterminal Hep-25 amino acids experienced no significant conformational changes, compared to published results, as a result of a pH change from pH 3 to pH 7 and metal binding. A 3D model of the Hep-25-Ni(II) complex was constructed from NMR data recorded for the hexapeptideNi(II) complex and Hep-25-DEDEDE-Ni(II) complex in combination with the fixed conformation of 19 C-terminal amino acids. The NMR data of the Hep-25-DEDEDE-Ni(II) complex indicates that the ATCUN motif moves independently from the rest of the structure. The 3D model structure of the metal-bound Hep-25 allows for future works to elucidate hepcidin’s interaction with its receptor ferroportin and should serve as a starting point for the development of antibodies with improved selectivity. N2 - Hepcidin-25 (Hep-25) spielt eine entscheidende Rolle bei der Kontrolle der Eisenhomöostase. Da die Dysfunktion des Hepcidin-Signalweges aufgrund des Eisenungleichgewichts zu mehreren Krankheiten führt, stellt Hepcidin ein potenzielles Ziel für die Diagnose und Behandlung von Störungen des Eisenstoffwechsels dar. Trotz intensiver Forschung in den letzten zehn Jahren, die darauf abzielte, einen selektiven Immunoassay für die Diagnose und Behandlung von Eisenerkrankungen zu entwickeln und die Ferroportin-Hepcidin-Interaktion besser zu verstehen, bleiben Fragen offen. Der Schlüssel zur Lösung dieser grundlegenden Fragen liegt darin, genaue Kenntnisse über die 3D-Struktur des nativen Hep-25 zu erlangen. Da festgestellt wurde, dass der N-Terminus, der für die Bioaktivität von Hep-25 verantwortlich ist, eine kleine Cu(II)-Bindungsstelle enthält, die als ATCUN-Motiv bekannt ist, wurde angenommen, dass der Hep-25- Cu(II)-Komplex die native, bioaktive Form des Hepcidins ist. Diese Struktur ist bisher noch nicht im Detail untersucht worden. Aufgrund fehlender Strukturinformationen über metallgebundenes Hep-25 ist wenig über seine mögliche biologische Rolle im Eisenstoffwechsel bekannt. Daher konzentriert sich diese Arbeit auf die strukturelle Charakterisierung des metallgebundenen Hep-25 mittels NMR-Spektroskopie und Molekulardynamik Simulationen. In der vorliegenden Arbeit wurde ein Protokoll zur Präparation und Reinigung von korrekt gefaltetem Hep-25 in hohen Mengen entwickelt. Um das Problem der geringen Löslichkeit von Hep-25 bei neutralem pH-Wert zu überwinden, haben wir einen C-terminalen DEDEDEDE Löslichkeits-Tag eingeführt. Die Metallbindung wurde durch eine Reihe von NMRspektroskopischen Experimenten untersucht, um die Aminosäuren zu identifizieren, welche an der Metallkoordination beteiligt sind. Basierend auf den erhaltenen NMR-Daten wurde eine Strukturberechnung durchgeführt, um eine Modellstruktur des Hep-25-Ni(II)-Komplexes zu erzeugen. Der DEDEDE-Tag wurde aufgrund fehlender NMR- restraints von der Strukturberechnung ausgeschlossen. Die dynamische Natur und der schnelle Austausch eines Teils der Amid-Protonen mit dem Lösungsmittel reduzierten die Gesamtzahl der NMR- restraints, die für eine hochwertige Struktur erforderlich waren. Die NMR-Daten zeigten, dass die 20 C-terminalen Hep-25-Aminosäuren keine signifikanten Konformationsänderungen als Folge eines pH-Wechsels von pH 3 auf pH 7 und einer Metallbindung erfuhren. Ein 3D-Modell des Hep-25-Ni(II)-Komplexes wurde aus den NMR-Daten des Hexapeptid-Ni(II)-Komplexes und des Hep-25-DEDEDE-Ni(II)-Komplexes in Kombination mit der bekannten Konformation der 19 C-terminalen Aminosäuren erstellt. Die NMR-Daten des Hep-25-DEDEDE-Ni(II)Komplexes zeigen, dass sich das Ni-ATCUN-Motiv unabhängig vom C-Terminus bewegt. Die 3D-Modellstruktur des metallgebundenen Hep-25 ermöglicht es, in Zukunft die Interaktion von Hepcidin mit seinem Rezeptor Ferroportin zu untersuchen und soll als Ausgangspunkt für die Entwicklung von Antikörpern mit verbesserter Selektivität dienen. KW - iron KW - hepcidin KW - peptide KW - metal KW - binding KW - NMR KW - Eisen KW - Hepcidin KW - Peptid KW - Metall KW - Bindung KW - NMR Y1 - 2019 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-459295 ER - TY - THES A1 - Villatoro Leal, José Andrés T1 - A combined approach for the analysis of biomolecules using IR-MALDI ion mobility spectrometry and molecular dynamics simulations of peptide ions in the gas phase T1 - Kombinierter Einsatz von IR-MALDI Ionenmobilitätsspektrometrie und Simulationen der Molekulardynamik von Peptidionen in der Gasphase zur Analyse von Biomolekülen N2 - The aim of this doctoral thesis was to establish a technique for the analysis of biomolecules with infrared matrix-assisted laser dispersion (IR-MALDI) ion mobility (IM) spectrometry. The main components of the work were the characterization of the IR-MALDI process, the development and characterization of different ion mobility spectrometers, the use of IR-MALDI-IM spectrometry as a robust, standalone spectrometer and the development of a collision cross-section estimation approach for peptides based on molecular dynamics and thermodynamic reweighting. First, the IR-MALDI source was studied with atmospheric pressure ion mobility spectrometry and shadowgraphy. It consisted of a metal capillary, at the tip of which a self-renewing droplet of analyte solution was met by an IR laser beam. A relationship between peak shape, ion desolvation, diffusion and extraction pulse delay time (pulse delay) was established. First order desolvation kinetics were observed and related to peak broadening by diffusion, both influenced by the pulse delay. The transport mechanisms in IR-MALDI were then studied by relating different laser impact positions on the droplet surface to the corresponding ion mobility spectra. Two different transport mechanisms were determined: phase explosion due to the laser pulse and electrical transport due to delayed ion extraction. The velocity of the ions stemming from the phase explosion was then measured by ion mobility and shadowgraphy at different time scales and distances from the source capillary, showing an initially very high but rapidly decaying velocity. Finally, the anatomy of the dispersion plume was observed in detail with shadowgraphy and general conclusions over the process were drawn. Understanding the IR-MALDI process enabled the optimization of the different IM spectrometers at atmospheric and reduced pressure (AP and RP, respectively). At reduced pressure, both an AP and an RP IR-MALDI source were used. The influence of the pulsed ion extraction parameters (pulse delay, width and amplitude) on peak shape, resolution and area was systematically studied in both AP and RP IM spectrometers and discussed in the context of the IR-MALDI process. Under RP conditions, the influence of the closing field and of the pressure was also examined for both AP and RP sources. For the AP ionization RP IM spectrometer, the influence of the inlet field (IF) in the source region was also examined. All of these studies led to the determination of the optimal analytical parameters as well as to a better understanding of the initial ion cloud anatomy. The analytical performance of the spectrometer was then studied. Limits of detection (LOD) and linear ranges were determined under static and pulsed ion injection conditions and interpreted in the context of the IR-MALDI mechanism. Applications in the separation of simple mixtures were also illustrated, demonstrating good isomer separation capabilities and the advantages of singly charged peaks. The possibility to couple high performance liquid chromatography (HPLC) to IR-MALDI-IM spectrometry was also demonstrated. Finally, the reduced pressure spectrometer was used to study the effect of high reduced field strength on the mobility of polyatomic ions in polyatomic gases. The last focus point was on the study of peptide ions. A dataset obtained with electrospray IM spectrometry was characterized and used for the calibration of a collision cross-section (CCS) determination method based on molecular dynamics (MD) simulations at high temperature. Instead of producing candidate structures which are evaluated one by one, this semi-automated method uses the simulation as a whole to determine a single average collision cross-section value by reweighting the CCS of a few representative structures. The method was compared to the intrinsic size parameter (ISP) method and to experimental results. Additional MD data obtained from the simulations was also used to further analyze the peptides and understand the experimental results, an advantage with regard to the ISP method. Finally, the CCS of peptide ions analyzed by IR-MALDI were also evaluated with both ISP and MD methods and the results compared to experiment, resulting in a first validation of the MD method. Thus, this thesis brings together the soft ionization technique that is IR-MALDI, which produces mostly singly charged peaks, with ion mobility spectrometry, which can distinguish between isomers, and a collision cross-section determination method which also provides structural information on the analyte at hand. N2 - Das Ziel dieser Arbeit war die Zusammenführung der schonende Ionisationsquelle Infrared Matrix-Assisted Laser Dispersion Ionization (IR-MALDI), der Isomer-diskriminierende Ionenmobilitätsspektrometrie und einer neuartigen, auf Molecular Dynamics (MD) Simulationen basierte Berechnungsmethode für Stoßquerschnitte. Der erste Schritt war die Charakterisierung des Flüssigkeitsdispersionsphänomens in IR-MALDI: Zwei verschiedenen Ionentransportmechanismen wurden nachgewiesen und weiter studiert. Die Beziehung zwischen Peakform, Diffusion, Desolvatation und Ionen Extraktionspuls wurde beschrieben. Die Geschwindigkeit der Ionen, die aus dem Dispersionsphänomen stammen, wurde durch Ionenmobilitätsspektrometrie und Shadowgraphie untersucht. Shadowgraphie hat ebenfalls das Verhalten des Dispersionsphänomens erläutert. Eine hohe, schnell abklingende initielle Geschwindigkeit wurde beobachtet. Das Verständnis des IR-MALDI Verfahrens ermöglichte die Optimierung der verschiedenen Ionenmobilität (IM) Spektrometer zum analytischen Zweck. Eine Atmosphärendruck- und zwei Niederdruckvariante von IM Spektrometern wurden mit gepulster Ionenextraktion genutzt. Die Pulsparameter (Pulsverzögerung, ‑breite, -höhe) und verschiedene elektrische Felder an unterschiedlichen Stellen der Spektrometer wurden systematisch variiert. Deren Einfluss auf die Peakauflösung und -fläche wurde untersucht und im Rahmen des IR-MALDI Verfahrens erklärt. Das Verständnis der Anatomie der Anfangsionenwolke wurde ebenfalls durch diese Experimente vertieft. Die analytische Leistungsfähigkeit eines IM-Spektrometers wurde dann untersucht. Nachweisgrenzen und lineare Bereiche wurden bestimmt und in Zusammenhang mit dem IR-MALDI Verfahren interpretiert. Anhand der Trennung von Isomeren und einfachen Mischungen wurde die Anwendung dieser Technik demonstriert und ihre Vorteile, die Detektion einfachgeladener Ionen und die Möglichkeit der HPLC-Kopplung (High Performance Liquid Chromatography), aufgezeigt. Mit dem Niederdruckspektrometer wurde der Einfluss hoher reduzierter Feldstärken auf die Ionenmobilität von polyatomische Ionen in polyatomische Gasen untersucht. Der letzte Schwerpunkt war die Charakterisierung von Peptidionen. Die Peptiden wurden mit Elektrospray (ESI) IM-Spektrometrie vermessen. Der hieraus erhaltene Datensatz diente zur Etablierung einer Stoßquerschnitt Berechnungsmethode mittels MD. Anstatt verschiedener Kandidat-Strukturen und deren Stoßquerschnitte, ergibt diese neuartige semi-automatisierte Methode einen einzigen, gemittelten Stoßquerschnitt. Die MD Methode wurde dann mit einer anderen, einfacheren Methode und mit den experimentellen Ergebnissen von ESI und IR-MALDI-IM Spektrometrie verglichen. Zudem wurde der Zusammenhang zwischen Ladungszustands- und Stoßquerschnittsdifferenzen zwischen den Peptiden untersucht. Weitere Strukturelle Informationen konnten aus den Simulationen extrahiert, und zur Charakterisierung der Peptiden verwendet werden. KW - Ion mobility spectrometry KW - Molecular dynamics KW - IR-MALDI KW - Peptides KW - Shadowgraphy KW - Liquid dispersion KW - Ionenmobilitätsspektrometrie KW - Molekulardynamik KW - Collision cross-section KW - IR-MALDI KW - Peptiden KW - Shadowgraphie KW - Stoßquerschnitt KW - Flüssigkeitszerstäubung Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-419723 ER - TY - THES A1 - Gebauer, Denis T1 - A novel view on the early stage of crystallization T1 - Ein Neuartiges Bild der frühen Kristallisationsphase N2 - This thesis provides a novel view on the early stage of crystallization utilizing calcium carbonate as a model system. Calcium carbonate is of great economical, scientific and ecological importance, because it is a major part of water hardness, the most abundant Biomineral and forms huge amounts of geological sediments thus binding large amounts of carbon dioxide. The primary experiments base on the evolution of supersaturation via slow addition of dilute calcium chloride solution into dilute carbonate buffer. The time-dependent measurement of the Ca2+ potential and concurrent pH = constant titration facilitate the calculation of the amount of calcium and carbonate ions bound in pre-nucleation stage clusters, which have never been detected experimentally so far, and in the new phase after nucleation, respectively. Analytical Ultracentrifugation independently proves the existence of pre-nucleation stage clusters, and shows that the clusters forming at pH = 9.00 have a proximately time-averaged size of altogether 70 calcium and carbonate ions. Both experiments show that pre-nucleation stage cluster formation can be described by means of equilibrium thermodynamics. Effectively, the cluster formation equilibrium is physico-chemically characterized by means of a multiple-binding equilibrium of calcium ions to a ‘lattice’ of carbonate ions. The evaluation gives GIBBS standard energy for the formation of calcium/carbonate ion pairs in clusters, which exhibits a maximal value of approximately 17.2 kJ mol^-1 at pH = 9.75 and relates to a minimal binding strength in clusters at this pH-value. Nucleated calcium carbonate particles are amorphous at first and subsequently become crystalline. At high binding strength in clusters, only calcite (the thermodynamically stable polymorph) is finally obtained, while with decreasing binding strength in clusters, vaterite (the thermodynamically least stable polymorph) and presumably aragonite (the thermodynamically intermediate stable polymorph) are obtained additionally. Concurrently, two different solubility products of nucleated amorphous calcium carbonate (ACC) are detected at low binding strength and high binding strength in clusters (ACC I 3.1EE-8 M^2, ACC II 3.8EE-8 M^2), respectively, indicating the precipitation of at least two different ACC species, while the clusters provide the precursor species of ACC. It is proximate that ACC I may relate to calcitic ACC –i.e. ACC exhibiting short range order similar to the long range order of calcite and that ACC II may relate to vateritic ACC, which will subsequently transform into the particular crystalline polymorph as discussed in the literature, respectively. Detailed analysis of nucleated particles forming at minimal binding strength in clusters (pH = 9.75) by means of SEM, TEM, WAXS and light microscopy shows that predominantly vaterite with traces of calcite forms. The crystalline particles of early stages are composed of nano-crystallites of approximately 5 to 10 nm size, respectively, which are aligned in high mutual order as in mesocrystals. The analyses of precipitation at pH = 9.75 in presence of additives –polyacrylic acid (pAA) as a model compound for scale inhibitors and peptides exhibiting calcium carbonate binding affinity as model compounds for crystal modifiers- shows that ACC I and ACC II are precipitated in parallel: pAA stabilizes ACC II particles against crystallization leading to their dissolution for the benefit of crystals that form from ACC I and exclusively calcite is finally obtained. Concurrently, the peptide additives analogously inhibit the formation of calcite and exclusively vaterite is finally obtained in case of one of the peptide additives. These findings show that classical nucleation theory is hardly applicable for the nucleation of calcium carbonate. The metastable system is stabilized remarkably due to cluster formation, while clusters forming by means of equilibrium thermodynamics are the nucleation relevant species and not ions. Most likely, the concept of cluster formation is a common phenomenon occurring during the precipitation of hardly soluble compounds as qualitatively shown for calcium oxalate and calcium phosphate. This finding is important for the fundamental understanding of crystallization and nucleation-inhibition and modification by additives with impact on materials of huge scientific and industrial importance as well as for better understanding of the mass transport in crystallization. It can provide a novel basis for simulation and modelling approaches. New mechanisms of scale formation in Bio- and Geomineralization and also in scale inhibition on the basis of the newly reported reaction channel need to be considered. N2 - Die vorliegende Arbeit zeichnet ein neuartiges Bild der frühen Kristallisationsphase von Calciumcarbonat. Calciumcarbonat hat als Hauptbestandteil der Wasserhärte und als weit verbreitetes Biomineral und Geomineral, das als Sediment in den Ozeanen große Mengen Kohlendioxid bindet, große Bedeutung. Die grundlegenden Experimente basieren auf der sehr langsamen Einstellung von Übersättigung, die durch langsame Zugabe verdünnter Calciumlösung in verdünnten Carbonatpuffer erreicht wird. Zeitabhängige Messung des Ca2+ Potentials bei gleichzeitiger pH = konstant Titration zeigt, dass zeitgemittelt vor der Nukleation gleiche Stoffmengen von Calcium- und Carbonat Ionen in Clustern gebunden sind, die bis jetzt noch nicht experimentell nachgewiesen werden konnten. Analytische Ultrazentrifugation belegt unabhängig die Existenz der Cluster, und es zeigt sich, dass sich die bei pH = 9,00 bildenden Cluster zeitgemittelt aus insgesamt etwa 70 Calcium und Carbonat Ionen bestehen. Die Experimente weisen darauf hin, dass sich die Clusterbildung auf der Grundlage von Gleichgewichtsthermodynamik beschreiben lässt. Ein multiples Bindungsgleichgewichtsmodell ermöglicht die Bestimmung der freien Standard Reaktionsenthalpie für die Bildung von Calcium/Carbonat Ionenpaaren in den Clustern, die ein Maß für die Bindungsstärke in Clustern darstellt. Die Bindungsstärke weist ein Minimum bei pH = 9,75 auf, und es zeigt sich, dass außerhalb dieses Minimums amorphes Calciumcarbonat ausfällt, das sich letztendlich in Calcit (das thermodynamisch stabile Calciumcarbonat Polymorph) umwandelt, während im Minimum und in der Nähe des Minimums amorphes Calciumcarbonat ausfällt, das sich letztendlich hauptsächlich in Vaterit (das thermodynamisch am wenigsten stabile Polymorph), Calcit und möglicherweise Spuren von Aragonit (das Polymorph mittlerer Stabilität) umwandelt. Gleichzeitig treten zwei unterschiedliche Löslichkeitsprodukte für das bei hoher und niedriger Bindungsstärke in Clustern ausgefällte, amorphe Calciumcarbonat auf (ACC I 3,1EE-8 M^2, ACC II 3,8EE-8 M^2). Das zeigt, dass die sich vor der Nukleation bildenden Cluster Vorläuferspezies (Precursor) des ausgefällten, amorphen Calciumcarbonats darstellen, wobei ACC I in der Literatur diskutiertem, calcitischem ACC entsprechen und ACC II vateritischem Calcit entsprechen kann. Eine detaillierte SEM, TEM, WAXS und Lichtmikroskopie Untersuchung der bei minimaler Bindungsstärke in Clustern (pH = 9,75) ausgefällten Partikel zeigt, dass sich hauptsächlich Vaterit mit Spuren von Calcit und möglicherweise Aragonit bildet. Die sich früh bildenden, kristallinen Partikel sind jeweils aus nano-Kristalliten von etwa 5 bis 10 nm Größe aufgebaut, die wie in Mesokristallen eine hohe wechselseitige Ordnung aufweisen. Die Untersuchung der frühen Kristallisation in Gegenwart von Additiven wurde ebenfalls bei minimaler Bindungsstärke in Clustern durchgeführt. Als Additive wurden Polyacrylsäure (PAA) als Beispiel für einen Hemmstoff gegen die Bildung von Verkalkungen und drei Peptide, die Bindungsaffinität zu Calciumcarbonat zeigen, als Beispiel für Kristallisations-Modifikatoren untersucht. Die Analyse zeigt, dass ACC I und ACC II parallel ausfallen; pAA stabilisiert ACC II gegenüber Kristallisation und führt dazu, dass es sich zugunsten von Kristallen, die sich aus ACC I bilden, auflöst, wobei letztendlich reines Calcit erhalten wird. Die Peptide hingegen hemmen die Bildung von Calcit in analoger Weise, wobei in einem Fall letztendlich reines Vaterit entsteht. Die Ergebnisse zeigen, dass die klassische Nukleationstheorie auf die Nukleation von Calciumcarbonat kaum anwendbar ist. Das metastabile System wird durch die Clusterbildung deutlich stabilisiert, und nicht Ionen, sondern Cluster sind die relevanten Spezies in der Nukleation. Wahrscheinlich ist das gefundene Konzept der Clusterbildung ein allgemeines Phänomen, das während der Kristallisation aller schwer löslichen Substanzen auftritt, da es auch für Calciumoxalat und Calciumphosphat qualitativ gezeigt werden konnte. Das Ergebnis ist wichtig für das fundamentale Verständnis der Nukleation, von Nukleationshemmung und der Modifikation von Kristallen mit Auswirkungen auf Materialen von großer industrieller und auch wissenschaftlicher Bedeutung. Ferner gibt es einen Hinweis, wie Masse während der Kristallisation –auch in Lebewesen transportiert werden kann und es kann einen neuen Ansatz für Kristallisationssimulationen liefern. Auf der Basis dieses neuartigen Reaktionskanals müssen neue Kristallisations-Mechanismen in Bio- und Geomineralization in Betracht gezogen werden. KW - Calciumcarbonat KW - Kristallisation KW - Nukleation KW - Cluster KW - Additive KW - calcium carbonate KW - crystallization KW - nucleation KW - clusters KW - additives Y1 - 2008 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-19818 ER - TY - THES A1 - Jehannin, Marie T1 - About the role of physico-chemical properties and hydrodynamics on the progress of a precipitation reaction T1 - Über die Rolle physikalisch-chemischer Eigenschaften und Hydrodynamiken auf den Fortschritt einer Fällungsreaktion BT - the case of cerium oxalate particles produced during coalescence of drops BT - Ceroxalat-Partikel, entstanden während der Koaleszenz von Tropfen N2 - The size and morphology control of precipitated solid particles is a major economic issue for numerous industries. For instance, it is interesting for the nuclear industry, concerning the recovery of radioactive species from used nuclear fuel. The precipitates features, which are a key parameter from the post-precipitate processing, depend on the process local mixing conditions. So far, the relationship between precipitation features and hydrodynamic conditions have not been investigated. In this study, a new experimental configuration consisting of coalescing drops is set to investigate the link between reactive crystallization and hydrodynamics. Two configurations of aqueous drops are examined. The first one corresponds to high contact angle drops (>90°) in oil, as a model system for flowing drops, the second one correspond to sessile drops in air with low contact angle (<25°). In both cases, one reactive is dissolved in each drop, namely oxalic acid and cerium nitrate. When both drops get into contact, they may coalesce; the dissolved species mix and react to produce insoluble cerium oxalate. The precipitates features and effect on hydrodynamics are investigated depending on the solvent. In the case of sessile drops in air, the surface tension difference between the drops generates a gradient which induces a Marangoni flow from the low surface tension drop over the high surface tension drop. By setting the surface tension difference between the two drops and thus the Marangoni flow, the hydrodynamics conditions during the drop coalescence could be modified. Diols/water mixtures are used as solvent, in order to fix the surface tension difference between the liquids of both drops regardless from the reactant concentration. More precisely, the used diols, 1,2-propanediol and 1,3-propanediol, are isomer with identical density and close viscosity. By keeping the water volume fraction constant and playing with the 1,2-propanediol and 1,3-propanediol volume fractions of the solvents, the mixtures surface tensions differ up to 10 mN/m for identical/constant reactant concentration, density and viscosity. 3 precipitation behaviors were identified for the coalescence of water/diols/recatants drops depending on the oxalic excess. The corresponding precipitates patterns are visualized by optical microscopy and the precipitates are characterized by confocal microscopy SEM, XRD and SAXS measurements. In the intermediate oxalic excess regime, formation of periodic patterns can be observed. These patterns consist in alternating cerium oxalate precipitates with distinct morphologies, namely needles and “microflowers”. Such periodic fringes can be explained by a feedback mechanism between convection, reaction and the diffusion. N2 - Die Kontrolle der Morphologie und Größe fester durch Fällung erzeugter Partikel ist eine wichtige Herausforderung in Industrie und Forschung. Insbesondere gilt dies für die Wiederaufbereitung verbrauchter Brennstäber in der Atomindustrie. Die Eigenschaften der Ausfällungen hängen von den Mischbedingungen der Flüssigkeiten in den Prozessen ab. Dennoch sind die Beziehungen zwischen den physischen Charakteristiken der erzeugten Partikeln und den hydrodynamischen Bedingungen ungewiss. In dieser Arbeit werden Zwei-Tropfen-Koalezenz-Experiment genutzt, um die Verbindungen zwischen Hydrodynamik und Fällungsreaktion besser zu verstehen. Zwei Konfigurationen von ruhenden wässrigen Tropfen wurden untersucht: Zum einen Tropfen mit hohem Kontaktwinkel (> 90°) in Öl und zum anderen Tropfen mit kleinem Kontaktwinkel (< 25°) in Luft. In beiden Fällen wurde Oxalsäure und Ceriumnitrat jeweils in einem Tropfen gelöst. Wenn beide Tropfen einander in Kontakt treten, können sie sich vereinigen. Dabei mischen sich die Reagenzien und erzeugen Ceriumoxalat. In Abhängigkeit von Lösungsmitteln werden die Eigenschaften der Fällung sowie ihr Einfluss auf die Hydrodynamik untersucht. In Experimenten Tropfen in Luft ist es außerdem möglich, mittels Wasser/Diol-Mischungen den Oberflächenspannungsgradienten zwischen beiden Tropfenflüssigkeiten zu ändern. Damit ist es möglich den resultierenden Marangoni-Fluss zu kontrollieren. So werden die hydrodynamischen Bedingungen unabhängig von dem Oxalsäureüberschuss verwirklicht. In diesem Fall werden drei Fällungsverhalten abhängig er Oxalsäure-Konzentration beobachtet. Das Zwischenverhalten zeigt überraschende periodische Strukturen, welche verschiedenen Morphologien bilden, nämlich Nägeln und „Microflower“. Die Strukturen wurden über Optische Mikroskopie Identifiziert und charakterisiert mit Hilfe von Konfokaler Mikroskopie, SEM, XRD und SAXS. Die Entstehung solcher Strukturen könnte durch eine Konvektion- Diffusion- Reaktion-Rückkopplung erklärt werden. N2 - Réussir à contrôler la morphologie et la taille de particules solides obtenues par précipitation est un enjeu industriel majeur. C’est notamment le cas dans l’industrie nucléaire pour le recyclage du combustible usé. Les caractéristiques des précipités sont liées aux conditions de mélange des phases liquides dans les procédés. Les corrélations entre les paramètres physiques des particules obtenues et les conditions hydrodynamiques n’ont pas été examinées jusqu’à présent. Dans cette étude, des systèmes expérimentaux originaux, basés sur la coalescence de deux gouttes, sont utilisés afin de mieux comprendre les liens entre hydrodynamique et réaction de précipitation. Deux configurations de gouttes aqueuses ont été investiguées, la première consiste en deux goutes posées à fort angle de contact (>90°) dans l’huile, il s’agit d’un système modèle pour les gouttes en émulsion, la second configuration correspond à deux gouttes posées à faible angle de contact (>25°) dans l’air. Dans chaque cas, une espèce réactive est dissoute dans chaque goutte, à savoir de l’acide oxalique ou du nitrate de cérium dans la seconde. Lorsque les deux gouttes se touchent, elles peuvent éventuellement coalescer, alors les espèces chimiques se mélangent et réagissent pour produire un précipité d’oxalate de cérium. Les caractéristiques de ce précipité et ses effets sur l’hydrodynamique sont examinés en fonction du solvant utilisé. De plus, dans le cas des gouttes posées sur une surface de silice dans l’air, une différence de tension de surface entre deux gouttes crée un gradient qui génère un flux de Marangoni dirigé de la goutte de faible tension de surface au-dessus de la goutte de forte tension de surface. En jouant sur la différence de tension de surface entre les deux gouttes, et ainsi sur le flux de Marangoni, il est possible de modifier les conditions hydrodynamiques lors de la coalescence des gouttes. Des mélanges eau/diols ont été utilisés comme solvant afin de pouvoir modifier la différence de tension de surface entre les liquides des deux gouttes indépendamment de leur concentration en réactif. Les diols utilisés, le 1,2-propanediol et le 1,3-propanediol sont des isomères, ils sont la même densité, des viscosités semblables mais des tensions de surface différentes. En fixant la fraction volumique d’eau dans le solvant, et en jouant sur les fractions volumiques de chaque diols, il est possible de contrôler la tension de surface des mélanges sur une gamme de 10 mN/m pour une concentration en réactifs donnée, et en conservant la densité et viscosité des solvants. Trois régimes de précipitation ont été identifiés dans le cas de la coalescence de gouttes d’eau/diols/réactifs en fonction de l’excès oxalique. Les motifs de précipitation en découlant ont été imagés par microscopie optique et les différents précipités ont été caractérisés à l’aide de microscopie confocale, MEB, DRX et SAXS. Le régime intermédiaire présente des motifs périodiques surprenants. Ces motifs correspondent à des domaines nettement délimités d’oxalate de cérium de différentes morphologies, à savoir des aiguilles et des « microflowers ». L’obtention de tels motifs peut s’expliquer par un mécanisme de rétroaction entre convection, réaction et diffusion. KW - Marangoni flow KW - coalescence KW - periodic pattern KW - oxalic precipitation KW - drop KW - Marangoni-Fluss KW - Koaleszenz KW - Tropfen KW - Fällungsreaktion KW - periodisches Muster KW - Oxalat-Fällung KW - flux de Marangoni KW - coalescence KW - gouttes KW - précipitation KW - motif périodique KW - précipitation oxalique Y1 - 2015 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-88364 ER - TY - THES A1 - Lemke, Karina T1 - Abtrennung und Charakterisierung von Polyelektrolyt-modifizierten Nanopartikeln T1 - Separation and characterization of polyelectrolyte-modified nanoparticles N2 - Gegenstand der Dissertation ist die größen- und eigenschaftsoptimierte Synthese und Charakterisierung von anorganischen Nanopartikeln in einer geeigneten Polyelektrolytmodifizierten Mikroemulsion. Das Hauptziel bildet dabei die Auswahl einer geeigneten Mikroemulsion, zur Synthese von kleinen, stabilen, reproduzierbaren Nanopartikeln mit besonderen Eigenschaften. Die vorliegende Arbeit wurde in zwei Haupteile gegliedert. Der erste Teil befasst sich mit der Einmischung von unterschiedlichen Polykationen (lineares Poly (diallyldimethylammoniumchlorid) (PDADMAC) und verzweigtes Poly (ethylenimin) (PEI)) in verschiedene, auf unterschiedlichen Tensiden (CTAB - kationisch, SDS - anionisch, SB - zwitterionisch) basierenden, Mikroemulsionssysteme. Dabei zeigt sich, dass das Einmischen der Polykationen in die Wassertröpfchen der Wasser-in-Öl (W/O) Mikroemulsion prinzipiell möglich ist. Der Einfluss der verschiedenen Polykationen auf das Phasenverhalten der W/O Mikroemulsion ist jedoch sehr unterschiedlich. In Gegenwart des kationischen Tensids führen die repulsiven Wechselwirkungen mit den Polykationen zu einer Destabilisierung des Systems, während die ausgeprägten Wechselwirkungen mit dem anionischen Tensid in einer deutlichen Stabilisierung des Systems resultieren. Für das zwitterionische Tensid führen die moderaten Wechselwirkungen mit den Polykationen zu einer partiellen Stabilisierung. Der zweite Teil der Arbeit beschäftigt sich mit dem Einsatz der unterschiedlichen, Polyelektrolyt- modifizierten Mikroemulsionen als Templatphase für die Herstellung verschiedener, anorganischer Nanopartikel. Die CTAB-basierte Mikroemulsion erweist sich dabei als ungeeignet für die Herstellung von CdS Nanopartikeln, da zum einen nur eine geringe Toleranz gegenüber den Reaktanden vorhanden ist (Destabilisierungseffekt) und zum anderen das Partikelwachstum durch den Polyelektrolyt-Tensid-Film nicht ausreichend begrenzt wird. Zudem zeigt sich, dass eine Abtrennung der Partikel aus der Mikroemulsion nicht möglich ist. Die SDS-basierten Mikroemulsionen, erweisen sich als geeignete Templatphase zur Synthese kleiner anorganischer Nanopartikel (3 – 20 nm). Sowohl CdS Quantum Dots, als auch Gold Nanopartikel konnten erfolgreich in der Mikroemulsion synthetisiert werden, wobei das verzweigte PEI einen interessanten Templat-Effekt in der Mikroemulsion hervorruft. Als deutlicher Nachteil der SDS-basierten Mikroemulsionen offenbaren sich die starken Wechselwirkungen zwischen dem Tensid und den Polyelektrolyten während der Aufarbeitung der Nanopartikel aus der Mikroemulsion. Dabei erweist sich die Polyelektrolyt-Tensid-Komplexbildung als hinderlich für die Redispergierung der CdS Quantum Dots in Wasser, so dass Partikelaggregation einsetzt. Die SB-basierten Mikroemulsionen erweisen sich als günstige Templatphase für die Bildung von größen- und eigenschaftenoptimierten Nanopartikeln (< 4 nm), wobei insbesondere eine Modifizierung mit PEI als ideal betrachtet werden kann. In Gegenwart des verzweigten PEI gelang es erstmals ultrakleine, fluoreszierende Gold Cluster (< 2 nm) in einer SB-basierten Mikroemulsion als Templatphase herzustellen. Als besonderer Vorteil der SB-basierten Mikroemulsion zeigen sich die moderaten Wechselwirkungen zwischen dem zwitterionischen Tensid und den Polyelektrolyten, welche eine anschließende Abtrennung der Partikel aus der Mikroemulsion unter Erhalt der Größe und ihrer optischen Eigenschaften ermöglichen. In der redispergierten wässrigen Lösung gelang somit eine Auftrennung der PEI-modifizierten Partikel mit Hilfe der asymmetrischer Fluss Feldflussfraktionierung (aF FFF). Die gebildeten Nanopartikel zeigen interessante optische Eigenschaften und können zum Beispiel erfolgreich zur Modifizierung von Biosensoren eingesetzt werden. N2 - This work is focused on the formation, recovery and characterisation of inorganic nanoparticles in a tailor-made polycation-modified reverse microemulsion. The main aim is the choice of an adequate microemulsion for the synthesis of small, uniform, reproducible nanoparticles with specialn characteristics. The first part is focused on the incorporation of two different polycations, low molecular weight linear poly(diallyldimethylammonium chloride) (PDADMAC) and low molecular weight branched poly(ethyleneimine) (PEI) in different surfactant-based (CTAB – cationic, SDS – anionic, SB - zwitterionic) w/o microemulsions. In principle the incorporation of the polycations in the small water droplets is possible, but the influence of the polycations on the phase behaviour is different. Repulsive interactions induce a destabilisation of the w/o microemulsion for cationic surfactant CTAB, while the distinctive interactions between the anionic surfactant SDS and the polycations induce an extension of the phase range and a considerable stabilisation. In case of zwitterionic surfactant SB a partial destabilisation can be observed, according to the lower interactions with the polycations. The second part is focused on the formation of different, inorganic nanoparticles in these polyelectrolyte-modified reverse microemulsions as a template phase. The CTAB-based microemulsion is not adequate for the formation of CdS nanoparticles, according to the low tolerance towards the reactants (destabilisation effect). Furthermore the particle growth cannot be limited by the surfactant-polycation-film and a recovery of the nanoparticles from the microemulsion is not possible. The results show that the SDS-based quaternary template phase consisting of water, toluene-pentanol (1:1), and the anionic surfactant SDS in presence of PEI or PDADMAC can be successfully used for the synthesis of polymer capped inorganic nanoparticles (3 – 20 nm). CdS quantum dots, as well as gold nanoparticles are successfully synthesised in the microemulsion droplets. Especially PEI acts as a reducing and stabilizing agent and shows an additional, interesting template effect in the microemulsion. Unfortunately a recovery of the nanoparticles without a particle aggregation is not possible due to the strong surfactant polycation interactions, which lead to polycation-surfactant complexes. The SB-based microemulsion can be successfully used as a tailor-made polycation-modifiedreverse microemulsion for the formation of small, uniform nanoparticles (< 4 nm) with special characteristics. Especially a modification with PEI is optimal and for the first time small, fluorescent gold cluster (< 2 nm) can be synthesised in a SB-based microemulsion as template phase. The results show that the electrostatic interactions between the polycation and the surfactant are of high relevance especially in the solvent evaporation and redispersion process. That means only in the case of moderate polycation-surfactant interactions a redispersion of the polymer capped particles without problems of aggregation is possible and the size and characteristics are unchanged in the redispersed solution. By means of asymmetric flow field flow fractionation (af-fff) it becomes possible to separate the two cluster fractions from each other as well as from the nanoparticle fraction with diameter > 5 nm. This opens a way to use the nanoparticles with their interesting, optical characteristics in different new fields of application for example for modification of biosensors. KW - Mikroemulsion KW - Gold Cluster KW - Quantum Dots KW - Feldflussfraktionierung KW - Nanopartikel KW - Microemulsion KW - Gold Cluster KW - Quantum Dots KW - Field Flow Fractionation KW - Nanoparticles Y1 - 2013 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-68133 ER - TY - THES A1 - Steeples, Elliot T1 - Amino acid-derived imidazolium salts: platform molecules for N-Heterocyclic carbene metal complexes and organosilica materials T1 - Imidazolium-Salze aus Aminosäure: Bausteine für N-Heterozyklische-Carben Metallkomplexe und Organosilicamaterialien N2 - In the interest of producing functional catalysts from sustainable building-blocks, 1, 3-dicarboxylate imidazolium salts derived from amino acids were successfully modified to be suitable as N-Heterocyclic carbene (NHC) ligands within metal complexes. Complexes of Ag(I), Pd(II), and Ir(I) were successfully produced using known procedures using ligands derived from glycine, alanine, β-alanine and phenylalanine. The complexes were characterized in solid state using X-Ray crystallography, which allowed for the steric and electronic comparison of these ligands to well-known NHC ligands within analogous metal complexes. The palladium complexes were tested as catalysts for aqueous-phase Suzuki-Miyaura cross-coupling. Water-solubility could be induced via ester hydrolysis of the N-bound groups in the presence of base. The mono-NHC–Pd complexes were seen to be highly active in the coupling of aryl bromides with phenylboronic acid; the active catalyst of which was determined to be mostly Pd(0) nanoparticles. Kinetic studies determined that reaction proceeds quickly in the coupling of bromoacetophenone, for both pre-hydrolyzed and in-situ hydrolysis catalyst dissolution. The catalyst could also be recycled for an extra run by simply re-using the aqueous layer. The imidazolium salts were also used to produce organosilica hybrid materials. This was attempted via two methods: by post-grafting onto a commercial organosilica, and co-condensation of the corresponding organosilane. The co-condensation technique harbours potential for the production of solid-support catalysts. N2 - Um Katalysatoren aus nachhaltigen Chemikalien herzustellen, wurden 1,3-Dicarbonsäure-Imidazolium-Salze, welche aus Aminosäuren synthetisiert wurden als N-heterozyklische-Carben-Liganden (NHC) in Metallkomplexen modifiziert. Liganden aus Glycin, Alanin, β-Alanin und Phenylalanin wurden wiederum genutzt, um Metallkomplexe aus Silber(I), Palladium(II) und Iridium(I) darzustellen. Alle Komplexverbindungen wurden mit Röntgenkristallographie charakterisiert. Die Palladiumkomplexe wurden als Katalysatoren in der Suzuki-Miyaura Reaktion eingesetzt. Durch zusätzliche Hydrolyse der Ester-Gruppen konnte eine gute Wasserlöslichkeit erreicht werden. Die hohe Aktivität der Mono-NHC–Palladium-Komplexe konnte bei der Kupplung von Arylbromiden mit Phenylboronsäuren aufgezeigt werden. Die aktive Spezies wurde hauptsächlich Pd(0) Nanopartikeln zugeschrieben. Nach erfolgreichem Recycling konnte der Katalysator noch einmal wiederverwendet werden. Die Imidazolium-Salze wurden ebenfalls herangezogen, um Organosilicamaterialien zu synthetisieren. Die Herstellung wurde durch zwei Methoden erreicht. Zum einen durch nachträgliches Aufbringen auf kommerzielle Siliziummaterialien, sowie durch Co-Kondensation auf das entsprechende Organosilan. Diese Co-Kondensation birgt Potential zur Herstellung von festen Trägerkatalysatoren. KW - synthesis KW - Synthese KW - sustainable chemistry KW - nachhaltige Chemie KW - organometallics KW - Metallorganischen KW - water KW - Wasser Y1 - 2016 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-101861 ER - TY - THES A1 - Kristen, Juliane Ute T1 - Amphiphilic BAB-triblock copolymers bearing fluorocarbon groups : synthesis and self-organization in aqueous media T1 - Amphiphile BAB-Triblockcopolymere mit Fluorcarbon-Gruppen : Synthese und Selbstorganisation in wässrigen Medien N2 - In this work new fluorinated and non-fluorinated mono- and bifunctional trithiocarbonates of the structure Z-C(=S)-S-R and Z-C(=S)-S-R-S-C(=S)-Z were synthesized for the use as chain transfer agents (CTAs) in the RAFT-process. All newly synthesized CTAs were tested for their efficiency to moderate the free radical polymerization process by polymerizing styrene (M3). Besides characterization of the homopolymers by GPC measurements, end- group analysis of the synthesized block copolymers via 1H-, 19F-NMR, and in some cases also UV-vis spectroscopy, were performed attaching suitable fluorinated moieties to the Z- and/or R-groups of the CTAs. Symmetric triblock copolymers of type BAB and non-symmetric fluorine end- capped polymers were accessible using the RAFT process in just two or one polymerization step. In particular, the RAFT-process enabled the controlled polymerization of hydrophilic monomers such as N-isopropylacrylamide (NIPAM) (M1) as well as N-acryloylpyrrolidine (NAP) (M2) for the A-blocks and of the hydrophobic monomers styrene (M3), 2-fluorostyrene (M4), 3-fluorostyrene (M5), 4-fluorostyrene (M6) and 2,3,4,5,6-pentafluorostyrene (M7) for the B-blocks. The properties of the BAB-triblock copolymers were investigated in dilute, concentrated and highly concentrated aqueous solutions using DLS, turbidimetry, 1H- and 19F-NMR, rheology, determination of the CMC, foam height- and surface tension measurements and microscopy. Furthermore, their ability to stabilize emulsions and microemulsions and the wetting behaviour of their aqueous solutions on different substrates was investigated. The behaviour of the fluorine end-functionalized polymers to form micelles was studied applying DLS measurements in diluted organic solution. All investigated BAB-triblock copolymers were able to form micelles and show surface activity at room temperature in dilute aqueous solution. The aqueous solutions displayed moderate foam formation. With different types and concentrations of oils, the formation of emulsions could be detected using a light microscope. A boosting effect in microemulsions could not be found adding BAB-triblock copolymers. At elevated polymer concentrations, the formation of hydrogels was proved applying rheology measurements. N2 - Im Rahmen dieser Arbeit wurden neue fluorierte und unfluorierte mono- und bifunktionelle Trithiocarbonate der Typen Z-C(=S)-S-R und Z-C(=S)-S-R-S-C(=S)-Z zur Anwendung als CTAs (chain- transfer agents) im RAFT-Polymerisationsverfahren hergestellt. Alle CTAs wurden erfolgreich auf ihre Effizienz zur Steuerung des radikalischen Polymerisationsverfahrens hin durch Polymerisation von Styrol (M3) getestet. Neben GPC-Messungen wurden Endgruppenanalysen der synthetisierten Blockcopolymere mittels 1H-, 19F-NMR und in manchen Fällen auch UV-Vis Spektroskopie durchgeführt. Dazu wurden die Z- und/oder R-Gruppen der CTAs mit geeigneten fluorierten Gruppen versehen. Durch Anwendung des RAFT Verfahrens konnten symmetrische Triblockcopolymere vom Typ BAB bzw. mit einer Fluoralkylgruppe endgecappte unsymmetrische Polymere in nur zwei bzw. einem Polymerisationsschritt hergestellt werden. Das RAFT- Polymerisationsverfahren ermöglicht sowohl die Polymerisation hydrophiler Monomere wie N-Isopropylacrylamid (NIPAM) (M1) oder N-Acryloylpyrrolidin (NAP) (M2) für die A-Blöcke als auch der hydropoben Monomere Styrol (M3), 2-Fluorostyrol (M4), 3-Fluorostyrol (M5), 4- Fluorostyrol (M6) und 2,3,4,5,6- Pentafluorostyrol (M7) für die B-Blöcke. Die Eigenschaften der Blockcopolymere in verdünnten, konzentrierten und hochkonzentrierten wässrigen Lösungen wurden mittels DLS, Trübungsphotometrie, 1H- und 19F-NMR, Rheologie, CMC- sowie Schaumhöhen- und Oberflächenspannungsmessungen und Lichtmikroskopie untersucht. Weiterhin wurden ihre Eigenschaften als Emulgatoren und in Mikroemulsion untersucht. Das Micellbildungsverhalten der hydrophob endfunktionalisierten Polymere wurde mittels DLS Messungen in verdünnter organischer Lösung untersucht. Alle untersuchten BAB-Triblöcke bildeten Micellen und zeigten Oberflächenaktivität bei Raumtemperatur in verdünnter, wässriger Lösung. Weiterhin zeigen die wässrigen Lösungen der Polymere mäßige Schaumbildung. Mit verschiedenen Öltypen und Ölkonzentrationen wurden Emulsionen bzw. Mikroemulsionen gebildet. In Mikroemulsion wurde durch Zugabe von BAB-Triblockopolymeren kein Boosting-Effekt erzielt werden. Bei Untersuchung höherer Polymerkonzentrationen wurde die Bildung von Hydrogelen mittels rheologischer Messungen nachgewiesen. Verschiedene Substrate konnten benetzt werden. Die hydrophob endgecappten Polymere bilden in verdünnter organischer Lösung Micellen, die mittels DLS untersucht wurden, und zeigen somit Tensidverhalten in nichtwässriger Lösung. KW - Fluorierte Blockcopolymere KW - RAFT KW - Rheologie KW - Tenside KW - Gele KW - wässrige Systeme KW - thermisch schaltbare Polymere KW - fluorinated Blockcopolymers KW - RAFT-Polymerisation KW - rheology KW - surfactants KW - gels KW - aqueous systems KW - thermosensitive polymers Y1 - 2011 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-61782 ER - TY - THES A1 - Lüdecke, Nils T1 - Bio-sourced adsorbing poly(2-oxazoline)s mimicking mussel glue proteins for antifouling applications T1 - Biobasierende, adsorbeirende, Muschelklebeproteine nachahmende Poly(2-oxazoline) für Antifouling-Anwendungen N2 - Nature developed countless systems for many applications. In maritime environments, several organisms established extra-ordinary mechanisms to attach to surfaces. Over the past years, the scientific interest to employ those mechanisms for coatings and long-lasting adhering materials gained significant attention. This work describes the synthesis of bio-inspired adsorbing copoly(2-oxazoline)s for surface coatings with protein repelling effects, mimicking mussel glue proteins. From a set of methoxy substituted phenyl, benzyl, and cinnamyl acids, 2-oxazoline monomers were synthesized. All synthesized 2-oxazolines were analyzed by FT-IR spectroscopy, NMR spectroscopy, and EI mass spectrometry. With those newly synthesized 2-oxazoline monomers and 2-ethyl-2-oxazoline, kinetic studies concerning homo- and copolymerization in a microwave reactor were conducted. The success of the polymerization reactions was demonstrated by FT-IR spectroscopy, NMR spectroscopy, MALDI-TOF mass spectrometry, and size exclusion chromatography (SEC). The copolymerization of 2-ethyl-2-oxazoline with a selection of methoxy-substituted 2-oxazolines resulted in water-soluble copolymers. To release the adsorbing catechol and cationic units, the copoly(2-oxazoline)s were modified. The catechol units were (partially) released by a methyl aryl ether cleavage reaction. A subsequent partial acidic hydrolysis of the ethyl unit resulted in mussel glue protein-inspired catechol and cation-containing copolymers. The modified copolymers were analyzed by NMR spectroscopy, UV-VIS spectroscopy, and SEC. The catechol- and cation-containing copolymers and their precursors were examined by a Quartz Crystal Microbalance with Dissipation (QCM-D), so study the adsorption performance on gold, borosilicate, iron, and polystyrene surfaces. An exemplary study revealed that a catechol and cation-containing copoly(2-oxazoline)-coated gold surface exhibits strong protein repelling properties. N2 - In der Natur entwickelten sich unzählige Anpassungen für ebenso viele Lebensbereiche. In maritimen Umgebungen haben sich beispiels-weise bei verschiedenen Organis-men außergewöhnliche Strategien entwickelt, um sich an Oberflächen an-zuheften. In den letzten Jahren hat das wissenschaftliche Interesse an der Nutzung dieser Mechanismen für an Oberflächen haftende Materialien stark zugenommen. Diese Arbeit beschreibt die Synthese von Muschelklebeprotein nachahmenden, bioinspirierten Copoly(2-oxazolinen) für Oberflächen-beschichtungen mit protein-abweisender Wirkung. Aus einer Gruppe von methoxysubstituierten Phenyl-, Benzyl , und Zimtsäuren wurden 2-Oxazolin-Monomere synthetisiert. Alle synthetisierten 2-Oxazoline wurden mittels FT-IR-Spektroskopie, NMR Spektroskopie und EI-Massenspektrometrie analysiert. Mit diesen neu synthetisierten 2-Oxazolin-Monomeren und 2-Ethyl-2-oxazolin (wasserlösliche Komponente) wurden kinetische Studien zur Homo- und Copolymerisation in einem Mikrowellenreaktor durchgeführt. Der Nachweis der Polymerisationsreaktionen erfolgte durch FT-IR Spektroskopie, NMR Spektroskopie, MALDI-TOF Massenspektrometrie und Gel-Permeations-Chromatographie (GPC). Die Copolymerisation von 2-Ethyl-2-Oxazolin mit Methoxyaryl-substituierten 2-Oxazolinen führte zu wasserlöslichen Copolymeren. Um die adsorbierenden Catechol- und kationischen-Einheiten freizusetzen, wurden die Copolymere modifiziert. Die Catechol-Einheiten wurden durch eine (partielle) Methylaryletherspaltung freigesetzt. Eine anschließende partielle saure Hydrolyse der Ethyleinheit führte zu, von Muschelklebeproteinen inspirierten, catechol- und kationen-haltigen Copolymeren. Die modifizierten Copolymere wurde mittels NMR Spektroskopie, UV-VIS Spektroskopie und SEC analysiert. Die catechol- und kationenhaltigen Copolymere und deren Vorläufercopolymere wurden mittels einer Quarzkristallmikrowaage mit Dissipation (QCM-D) hinsichtlich ihrer Adsorptionsfähigkeit an den Oberflächen Gold, Borosilicat, Eisen und Polystyrol untersucht. Exemplarisch wurde gezeigt, dass eine mit catechol und kationenhaltigem Copoly(2-oxazoline) beschichtete Goldoberfläche, stark proteinabweisende Eigenschaften aufweist. KW - poly(2-oxazoline)s KW - adhesive KW - anti-fouling KW - mussel-mimicking KW - klebend KW - Antifouling KW - Muschelnachahmend KW - Poly(2-oxazoline) Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-549836 ER - TY - THES A1 - Tang, Jo Sing Julia T1 - Biofunctional polymers for medical applications T1 - Biofunktionale Polymere für medizinische Anwendungen N2 - Carbohydrates are found in every living organism, where they are responsible for numerous, essential biological functions and processes. Synthetic polymers with pendant saccharides, called glycopolymers, mimic natural glycoconjugates in their special properties and functions. Employing such biomimetics furthers the understanding and controlling of biological processes. Hence, glycopolymers are valuable and interesting for applications in the medical and biological field. However, the synthesis of carbohydrate-based materials can be very challenging. In this thesis, the synthesis of biofunctional glycopolymers is presented, with the focus on aqueous-based, protecting group free and short synthesis routes to further advance in the field of glycopolymer synthesis. A practical and versatile precursor for glycopolymers are glycosylamines. To maintain biofunctionality of the saccharides after their amination, regioselective functionalization was performed. This frequently performed synthesis was optimized for different sugars. The optimization was facilitated using a design of experiment (DoE) approach to enable a reduced number of necessary experiments and efficient procedure. Here, the utility of using DoE for optimizing the synthesis of glycosylamines is discussed. The glycosylamines were converted to glycomonomers which were then polymerized to yield biofunctional glycopolymers. Here, the glycopolymers were aimed to be applicable as layer-by-layer (LbL) thin film coatings for drug delivery systems. To enable the LbL technique, complimentary glycopolymer electrolytes were synthesized by polymerization of the glycomonomers and subsequent modification or by post-polymerization modification. For drug delivery, liposomes were embedded into the glycopolymer coating as potential cargo carriers. The stability as well as the integrity of the glycopolymer layers and liposomes were investigated at physiological pH range. Different glycopolymers were also synthesized to be applicable as anti-adhesion therapeutics by providing advanced architectures with multivalent presentations of saccharides, which can inhibit the binding of pathogene lectins. Here, the synthesis of glycopolymer hydrogel particles based on biocompatible poly(N-isopropylacrylamide) (NiPAm) was established using the free-radical precipitation polymerization technique. The influence of synthesis parameters on the sugar content in the gels and on the hydrogel morphology is discussed. The accessibility of the saccharides to model lectins and their enhanced, multivalent interaction were investigated. At the end of this work, the synthesis strategies for the glycopolymers are generally discussed as well as their potential application in medicine. N2 - Kohlenhydrate sind in jedem Lebewesen zu finden, wo sie für zahlreiche, essenzielle biologische Funktionen und Prozesse verantwortlich sind. Synthetische Polymere, die Saccharide tragen, werden Glykopolymere genannt und können natürliche Glykokonjugate in ihren besonderen Eigenschaften und Funktionen nachahmen. Der Einsatz solcher Biomimetika fördert das Verständnis und die Kontrolle biologischer Prozesse. Daher sind Glykopolymere besonders interessant für Anwendungen im medizinischen und biologischen Bereich. Die Synthese von Materialien auf Kohlenhydratbasis kann jedoch eine große Herausforderung darstellen. In dieser Arbeit wird die Synthese biofunktioneller Glykopolymere vorgestellt, wobei der Schwerpunkt auf wässrigen, schutzgruppenfreien und kurzen Synthesewegen liegt, um weitere Fortschritte auf dem Gebiet der Glykopolymersynthese zu erzielen. Ein praktisches und vielseitiges Ausgangsmaterial für Glykopolymere sind Glykosylamine. Um die Biofunktionalität der Saccharide nach deren Aminierung zu erhalten, wurde eine regioselektive Funktionalisierung durchgeführt. Diese häufig durchgeführte Synthese wurde für verschiedene Zucker optimiert. Die Optimierung wurde durch die Anwendung von statistischer Versuchsplanung (Design of Experiments, DoE) vereinfacht, um die Anzahl der erforderlichen Experimente zu reduzieren und ein effizientes Verfahren zu ermöglichen. Hier wird der Nutzen des DoE-Ansatzes für die Optimierung der Synthese von Glykosylaminen diskutiert. Die Glykosylamine wurden in Glykomonomere umgewandelt, die daraufhin polymerisiert wurden, um biofunktionelle Glykopolymere zu erhalten. Die Glykopolymere sollten als Layer-by-Layer (LbL)-Beschichtungen für Drug-Delivery-Systeme anwendbar sein. Um die LbL-Technik zu ermöglichen, wurden komplementäre Glykopolymerelektrolyte durch Polymerisation der Glykomonomere mit anschließender Modifkation oder durch Postpolymerisationsglykosylierung hergestellt. Für die Verabreichung von Arzneimitteln wurden Liposomen als potenzielle Wirkstoffcarrier in die Glykopolymerbeschichtung eingebettet. Die Stabilität sowie die Unversehrtheit der Glykopolymerschichten und Liposomen wurden im physiologischen pH-Bereich nachgewiesen. Abschließend wurden verschiedene Glykopolymere synthetisiert, die als Anti-Adhäsions-Therapeutika anwendbar sein könnten, indem sie komplexe Architekturen mit multivalenter Präsentation von Sacchariden bereitstellen, welche die Bindung von Pathogenenlektinen hemmen können. Hier wurde die Synthese von Glykopolymer-Hydrogelpartikeln auf der Basis von biokompatiblem Poly(N-isopropylacrylamid) (NiPAm) mit Hilfe einer radikalischen Fällungspolymerisation etabliert. Der Einfluss der Syntheseparameter auf den Zuckergehalt in den Gelen und auf die Hydrogelmorphologie wurde diskutiert. Die Zugänglichkeit der Saccharide für Modell-Lektine und ihre verstärkte, multivalente Interaktion wurden untersucht. Zum Abschluss dieser Arbeit werden die Synthesestrategien für die Glykopolymere sowie deren mögliche Anwendung in der Medizin allgemein diskutiert. KW - glycopolymers KW - Glykopolymere KW - glycoconjugates KW - Glykokonjugate KW - glycogels KW - Glykogele KW - layer-by-layer glycopolymer coating KW - Layer-by-Layer Glykopolymerbeschichtung KW - design of experiments KW - statistische Versuchsplanung (Design of Experiments) KW - glycopolymer electrolytes KW - Glykopolymer-Elektrolyt Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-563639 ER - TY - THES A1 - Dambowsky, Ina T1 - Bioinspirierte Komposite - Strukturbildung durch Verkleben von Nano- oder Mesokristallen mit funktionalisierten Poly(2-oxazolin)en T1 - Bioinspired composites - structure formation by gluing of nano- or mesocrystals with functionalized poly(2-oxazoline)s N2 - Die herausragenden mechanischen Eigenschaften natürlicher anorganisch-organischer Kompositmaterialien wie Knochen oder Muschelschalen entspringen ihrer hierarchischen Struktur, die von der nano- bis hinauf zur makroskopischen Ebene reicht, und einer kontrollierten Verbindung entlang der Grenzflächen der anorganischen und organischen Komponenten. Ausgehend von diesen Schlüsselprinzipien des biologischen Materialdesigns wurden in dieser Arbeit zwei Konzepte für die bioinspirierte Strukturbildung von Kompositen untersucht, die auf dem Verkleben von Nano- oder Mesokristallen mit funktionalisierten Poly(2-oxazolin)-Blockcopolymeren beruhen sowie deren Potenzial zur Herstellung bioinspirierter selbstorganisierter hierarchischer anorganisch-organischer Verbundstrukturen ohne äußere Kräfte beleuchtet. Die Konzepte unterschieden sich in den verwendeten anorganischen Partikeln und in der Art der Strukturbildung. Über einen modularen Ansatz aus Polymersynthese und polymeranaloger Thiol-En-Funktionalisierung wurde erfolgreich eine Bibliothek von Poly(2-oxazolin)en mit unterschiedlichen Funktionalitäten erstellt. Die Blockcopolymere bestehen aus einem kurzen partikelaffinen "Klebeblock", der aus Thiol-En-funktionalisiertem Poly(2-(3-butenyl)-2-oxazolin) besteht, und einem langen wasserlöslichen, strukturbildenden Block, der aus thermoresponsivem und kristallisierbarem Poly(2-isopropyl-2-oxazolin) besteht und hierarchische Morphologien ausbildet. Verschiedene analytische Untersuchungen wie Turbidimetrie, DLS, DSC, SEM oder XRD machten das thermoresponsive bzw. das Kristallisationsverhalten der Blockcopolymere in Abhängigkeit vom eingeführten Klebeblock zugänglich. Es zeigte sich, dass diese Polymere ein komplexes temperatur- und pH-abhängiges Trübungsverhalten aufweisen. Hinsichtlich der Kristallisation änderte der Klebeblock nicht die nanoskopische Kristallstruktur; er beeinflusste jedoch die Kristallisationszeit, den Kristallisationsgrad und die hierarchische Morphologie. Dieses Ergebnis wurde auf das unterschiedliche Aggregationsverhalten der Polymere in Wasser zurückgeführt. Für die Herstellung von Kompositen nutzte Konzept 1 mikrometergroße Kupferoxalat-Mesokristalle, die eine innere Nanostruktur aufweisen. Die Strukturbildung über den anorganischen Teil wurde durch das Verkleben und Anordnen dieser Partikel erstrebt. Konzept 1 ermöglichte homogene freistehende stabile Kompositfilme mit einem hohen anorganischen Anteil. Die Partikel-Polymer-Kombination vereinte jedoch ungünstige Eigenschaften in sich, d. h. ihre Längenskalen waren zu unterschiedlich, was die Selbstassemblierung der Partikel verhinderte. Aufgrund des geringen Aspektverhältnisses von Kupferoxalat blieb auch die gegenseitige Ausrichtung durch äußere Kräfte erfolglos. Im Ergebnis eignet sich das Kupferoxalat-Poly(2-oxazolin)-Modellsystem nicht für die Herstellung hierarchischer Kompositstrukturen. Im Gegensatz dazu verwendet Konzept 2 scheibenförmige Laponit®-Nanopartikel und kristallisierbare Blockcopolymere zur Strukturbildung über die organische Komponente durch polymervermittelte Selbstassemblierung. Komplementäre Analysemethoden (Zeta-Potenzial, DLS, SEM, XRD, DSC, TEM) zeigten sowohl eine kontrollierte Wechselwirkung zwischen den Komponenten in wässriger Umgebung als auch eine kontrollierte Strukturbildung, die in selbstassemblierten Nanokompositen resultiert, deren Struktur sich über mehrere Längenskalen erstreckt. Es wurde gezeigt, dass die negativ geladenen Klebeblöcke spezifisch und selektiv an den positiv geladenen Rändern der Laponit®-Partikel binden und so Polymer-Laponit®-Nanohybridpartikel entstehen, die als Grundbausteine für die Kompositbildung dienen. Die Hybridpartikel sind bei Raumtemperatur elektrosterisch stabilisiert - sterisch durch ihre langen, mit Wasser wechselwirkenden Poly(2-isopropyl-2-oxazolin)-Blöcke und elektrostatisch über die negativ geladenen Laponit®-Flächen. Im Ergebnis ließ sich Konzept 2 und damit die Strukturbildung über die organische Komponente erfolgreich umsetzten. Das Laponit®-Poly(2-oxazolin)-Modellsystem eröffnete den Weg zu selbstassemblierten geschichteten quasi-hierarchischen Nanokompositstrukturen mit hohem anorganischen Anteil. Abhängig von der frei verfügbaren Polymerkonzentration bei der Kompositbildung entstanden zwei unterschiedliche Komposit-Typen. Darüber hinaus entwarf die Arbeit einen Erklärungsansatz für den polymervermittelten Bildungsprozess der Komposit-Strukturen. Insgesamt legt diese Arbeit Struktur-Prozess-Eigenschafts-Beziehungen offen, um selbstassemblierte bioinspirierte Kompositstrukturen zu bilden und liefert neue Einsichten zu einer geeigneten Kombination an Komponenten und Herstellungsbedingungen, die eine kontrollierte selbstassemblierte Strukturbildung mithilfe funktionalisierter Poly(2-oxazolin)-Blockcopolymere erlauben. N2 - Natural inorganic-organic composite materials like nacre and bone feature unique mechanical properties due to their complex hierarchical structure and their controlled connection at the interface of the components, starting from the nanometer scale. Following these key principles of biological material design, this thesis investigates two concepts for bioinspired structure formation of composites based on gluing nano- or mesocrystals with functionalized poly(2-oxazoline) block copolymers and the potential of these materials for fabricating bioinspired self-assembled hierarchical inorganic-organic composite structures without external forces. The concepts differed in the inorganic particles used and in the structure formation pathway. A modular approach of polymer synthesis and polymer analogue thiol-ene modification was successfully used to create a platform of poly(2-oxazoline)s with different functionalities. The block copolymers are composed of a short particle-affine "gluing block" consisting of thiol-ene modified poly(2-(3-butenyl)-2-oxazoline) and a long water soluble, structure forming block that consists of thermoresponsive and crystallizable poly(2-isopropyl-2-oxazoline) that yields hierarchical morphologies. Various analytical investigations such as turbidimetry, DLS, DSC, SEM and XRD revealed the influence of the "gluing block" on the thermoresponsive and crystallization behavior of the block copolymers. It was shown that these polymers have complex temperature- and pH-dependent turbidity behavior. Concerning crystallization, the gluing block did not change the nanoscopic crystal structure but influenced the crystallization time, the degree of crystallization and the hierarchical morphology. This result was attributed to different aggregation behavior of the polymers in water. For the composite fabrication, concept 1 uses micrometer-sized copper oxalate mesocrystals, which exhibit an internal nanostructure and seek structure formation via the inorganic part by the assembly of these particles. Concept 1 enabled homogeneous free-standing stable composite films with high inorganic content. However, the particle-polymer combination combined unfavorable properties, i.e. their length scales were too different, which prevented the particles from self-assembling. Furthermore, due to the small aspect ratio of copper oxalate, mutual alignment via external forces was also unsuccessful. In essence, the copper oxalate-poly(2-oxazoline)-model system is not suitable for the fabrication of hierarchical composite structures. In contrast, concept 2 uses disc-shaped Laponite® nanoparticles and crystallizable block copolymers for structure formation via the organic component by polymer-mediated self-assembly. Complementary analytical methods (zeta potential, DLS, SEM, XRD, DSC, TEM) revealed both controlled interaction between the components in an aqueous environment and a controlled structure formation to yield self-assembled nanocomposites, whose structure spans several length scales. It was shown that the negatively charged gluing blocks bind specifically and selectively to the positively charged Laponite® particle rim, resulting in polymer-Laponite® nanohybrid particles that served as the basic building blocks for composite formation. The hybrid particles are electrosterically stabilized at room temperature – sterically by their long water-interacting poly(2-isopropyl-2-oxazoline) blocks and electrostatically via the negatively charged Laponite® faces. As a result, concept 2 and thus structure formation via the organic component could be successfully achieved. The Laponite®-poly(2-oxazoline)-model system opened the path to self-assembled layered quasi-hierarchical nanocomposite structures with a high inorganic content. Depending on the free available polymer concentration during composite formation, two different composite types were accessible. Additionally, a possible explanation for the polymer-mediated formation process of the self-assembled composite structure was proposed. This thesis contributes insights in understanding the fundamental structure-process-property relationships in order to form self-assembled bioinspired composite structures and provides conditions and suitable compilation of components that allow a controlled self-assembled structure formation via poly(2-oxazoline) block copolymers. KW - bioinspirierte Komposite KW - anorganisch-organische Hybrid-Nanopartikel KW - Selbstassemblierung KW - thermoresponsiv KW - Poly(2-oxazolin)-Blockcopolymer KW - Polymerkristallisation KW - Thiol-En KW - inorganic-organic hybrid nanoparticle KW - self-assembly KW - thermoresponsive KW - poly(2-oxazoline) KW - block copolymer KW - polymer crystallization KW - thiol-ene KW - bioinspired composite Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-523671 ER - TY - THES A1 - Schipper, Florian T1 - Biomass derived carbon for new energy storage technologies N2 - The thesis deals with the production and evaluation of porous carbon materials for energy storage technologies, namely super capacitors and lithium sulfur batteries. N2 - Die Doktorarbeit befasst sich mit der Produktion und Evaluierung poröser Kohlenstoffmaterialien für die Anwendung in Energiespeichertechnologien, namentlich Superkondensatoren und Lithiumschwefelbatterien. T2 - Biomasse basierende Kohlenstoffe für neue Energiespeichertechnologien KW - Batterien KW - Superkondensatoren KW - Energiespeicher KW - Lithium-Schwefel-Batterien KW - Kohlenstoff KW - battery KW - supercapacitors KW - energy storage KW - lithium sulfur battery KW - carbon Y1 - 2014 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-72045 ER - TY - THES A1 - Otte, Fabian T1 - C-Arylglykoside und Chalkone T1 - Aryl C-glycosides and chalcones BT - neue Wege zu heterozyklischen Wirkstoffen durch Ru- und Pd-katalysierte Reaktionen BT - new pathways to heterocyclic drugs by Ru- and Pd-catalyzed reactions N2 - Im bis heute andauernden Zeitalter der wissenschaftlichen Medizin, konnte ein breites Spektrum von Wirkstoffen zur Behandlung diverser Krankheiten zusammengetragen werden. Dennoch hat es sich die organische Synthesechemie zur Aufgabe gemacht, dieses Spektrum auf neuen oder bekannten Wegen und aus verschiedenen Gründen zu erweitern. Zum einen ist das Vorkommen bestimmter Verbindungen in der Natur häufig limitiert, sodass synthetische Methoden immer öfter an Stelle eines weniger nachhaltigen Abbaus treten. Zum anderen kann durch Derivatisierung und Wirkstoffanpassung die physiologische Wirkung oder die Bioverfügbarkeit eines Wirkstoffes erhöht werden. In dieser Arbeit konnten einige Vertreter der bekannten Wirkstoffklassen C-Arylglykoside und Chalkone durch den Schlüsselschritt der Palladium-katalysierten MATSUDA-HECK-Reaktion synthetisiert werden. Dazu wurden im Fall der C-Arylglykoside zunächst ungesättigte Kohlenhydrate (Glykale) über eine Ruthenium-katalysierte Zyklisierungsreaktion dargestellt. Diese wurden im Anschluss mit unterschiedlich substituierten Diazoniumsalzen in der oben erwähnten Palladium-katalysierten Kupplungsreaktion zur Reaktion gebracht. Bei der Auswertung der analytischen Daten konnte festgestellt werden, dass stets die trans-Diastereomere gebildet wurden. Im Anschluss konnte gezeigt werden, dass die Doppelbindungen dieser Verbindungen durch Hydrierung, Dihydroxylierung oder Epoxidierung funktionalisiert werden können. Auf diesem Wege konnte u. a. eine dem Diabetesmedikament Dapagliflozin ähnliche Verbindung hergestellt werden. Im zweiten Teil der Arbeit wurden Arylallylchromanone durch die MATSUDA-HECK-Reaktion von verschiedenen 8-Allylchromanonen mit Diazoniumsalzen dargestellt. Dabei konnte beobachtet werden, dass eine MOM-Schutzgruppe in 7-Position der Moleküle die Darstellung von Produktgemischen unterdrückt und jeweils nur eine der möglichen Verbindungen gebildet wird. Die Lage der Doppelbindung konnte mittels 2D-NMR-Untersuchungen lokalisiert werden. In Kooperation mit der theoretischen Chemie sollte durch Berechnungen untersucht werden, wie die beobachteten Verbindungen entstehen. Durch eine auftretende Wechselwirkung innerhalb des Moleküls konnte allerdings keine explizite Aussage getroffen werden. Im Anschluss sollten die erhaltenen Verbindungen in einer allylischen Oxidation zu Chalkonen umgesetzt werden. Die Ruthenium-katalysierten Methoden zeigten u. a. keine Eignung. Es konnte allerdings eine metallfreie, Mikrowellen-unterstützte Methode erfolgreich erprobt werden, sodass die Darstellung einiger Vertreter dieser physiologisch aktiven Stoffklasse gelang. N2 - The ongoing age of scientific medicine spawned a broad spectrum of drugs for the treatment of various diseases. Nonetheless, it is the task of synthetic organic chemistry to expand this spectrum in new or known pathways and for various reasons. On the one hand, the availability of certain compounds in nature is often limited, so that synthetic methods increasingly take the place of less sustainable extraction. On the other hand, the physiological effect or the bioavailability of a drug can be increased through derivatization and drug adaptation. In this work, several representatives of the known drug classes aryl C-glycosides and chalcones were synthesized by the key step of palladium-catalyzed MATSUDA-HECK reaction. In the case of aryl C-glycosides, unsaturated carbohydrates (glycals) were first prepared by a ruthenium-catalyzed cyclization reaction. These were subsequiently reacted with differently substituted diazonium salts in the above-mentioned palladium-catalyzed coupling reaction. When evaluating the analytical data, it was found that the trans-diastereomers were solitarily formed. Subsequiently, it was shown that the double bonds of these compounds can be functionalized by hydrogenation, dihydroxylation and epoxidation. By applying these methods an aryl C-glycoside similar to the diabetes drug Dapagliflozin was synthesized. The second part of this work, depicts the synthesis of aryl allyl chromanones by the Matsuda-Heck reaction of various 8-allyl chromanones and diazonium salts. It could be observed that a MOM-protection group in the 7-position of the chromanone ring suppresses the expression of product mixtures. In each case only one of the possible compounds is formed. The position of the double bond was localized by 2D NMR studies. In cooperation with theoretical chemistry, calculations were carried out to investigate how the observed compounds were formed. However, an explicit statement could not be made, due to an interaction within the molecule. Finally, the compounds obtained were converted into chalcones in an allylic oxidation reaction. Ru-catalyzed methods showed no suitability. However, a metal-free, microwave-assisted method could be successfully applied so that the synthesis of certain examples of this physiologically active substance class could be shown. KW - C-Arlyglykosid KW - Chalkon KW - Matsuda-Heck-Reaktion KW - Ringschlussmetathese KW - aryl C-glycoside KW - chalcon KW - Matsuda-Heck reaction KW - ring closing metathesis Y1 - 2019 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-434305 ER - TY - THES A1 - Esen, Cansu T1 - Carbon nitride incorporation in polymer networks T1 - Inkorporation von Kohlenstoffnitrid in Polymernetzwerke BT - light-driven integration and utilization of graphitic carbon nitride into macroscale polymeric networks N2 - The urge of light utilization in fabrication of materials is as encouraging as challenging. Steadily increasing energy consumption in accordance with rapid population growth, is requiring a corresponding solution within the same rate of occurrence speed. Therefore, creating, designing and manufacturing materials that can interact with light and in further be applicable as well as disposable in photo-based applications are very much under attention of researchers. In the era of sustainability for renewable energy systems, semiconductor-based photoactive materials have received great attention not only based on solar and/or hydrocarbon fuels generation from solar energy, but also successful stimulation of photocatalytic reactions such as water splitting, pollutant degradation and organic molecule synthesisThe turning point had been reached for water splitting with an electrochemical cell consisting of TiO2-Pt electrode illuminated by UV light as energy source rather than an external voltage, that successfully pursued water photolysis by Fujishima and Honda in 1972. Ever since, there has been a great deal of interest in research of semiconductors (e.g. metal oxide, metal-free organic, noble-metal complex) exhibiting effective band gap for photochemical reactions. In the case of environmental friendliness, toxicity of metal-based semiconductors brings some restrictions in possible applications. Regarding this, very robust and ‘earth-abundant’ organic semiconductor, graphitic carbon nitride has been synthesized and successfully applied in photoinduced applications as novel photocatalyst. Properties such as suitable band gap, low charge carrier recombination and feasibility for scaling up, pave the way of advance combination with other catalysts to gather higher photoactivity based on compatible heterojunction. This dissertation aims to demonstrate a series of combinations between organic semiconductor g-CN and polymer materials that are forged through photochemistry, either in synthesis or in application. Fabrication and design processes as well as applications performed in accordance to the scope of thesis will be elucidated in detail. In addition to UV light, more attention is placed on visible light as energy source with a vision of more sustainability and better scalability in creation of novel materials and solar energy based applications. N2 - Die Nutzung von Licht bei der Herstellung von Materialien ist ebenso vielversprechend wie herausfordernd. Der stetig steigende Energieverbrauch in Kombination mit dem rasanten Bevölkerungswachstum erfordert Lösungen in der entsprechenden Geschwindigkeit. Daher stehen Materialien, die mit Licht interagieren können und darüber hinaus in fotobasierten Anwendungen einsetzbar sind, im Mittelpunkt des Interesses der Forscher. In der Ära der Nachhaltigkeit und erneuerbarer Energiesysteme haben halbleiterbasierte photoaktive Materialien nicht nur aufgrund der Erzeugung von Solarenergie oder der Herstellung von Brennstoffen aus Sonnenenergie große Aufmerksamkeit erhalten, sondern auch aufgrund des erfolgreichen Einsatzes in photokatalytischen Reaktionen wie zum Beispiel der Wasserspaltung, des Schadstoffabbaus und der Synthese organischer Moleküle. Die Wasserspaltung mit einer elektrochemischen Zelle führte hier zu einem Wendepunkt in der Forschung. Die Zelle bestand aus einer TiO2-Pt-Elektrode, welche mit UV-Licht als Energiequelle anstatt einer sonst üblichen externen Spannung betrieben wurde. 1972 führten Fujishima und Honda somit erfolgreich die Photolyse von Wasser durch. Seitdem besteht ein großes Interesse an der Erforschung von Halbleitern (z. B. Metalloxide, metallfreie organische Stoffe, Edelmetallkomplexe), die eine effektive Bandlücke für photochemische Reaktionen aufweisen. Was jedoch die Umweltfreundlichkeit anbelangt, so bringt die Toxizität von Halbleitern auf Metallbasis einige Einschränkungen mit sich. Um diese Toxizität zu vermeiden wurde der sehr robuste und bezüglich seiner Ausgangsstoffe häufig vorkommende organische Halbleiter Graphitkohlenstoffnitrid synthetisiert und erfolgreich in photoinduzierten Anwendungen als neuartiger Photokatalysator eingesetzt. Eigenschaften wie eine geeignete Bandlücke, geringe Ladungsträgerrekombination und die Möglichkeit der Skalierung ebnen somit den Weg für Kombinationen mit anderen Katalysatoren, um eine höhere Photoaktivität auf der Grundlage einer kompatiblen Heteroverbindung zu erreichen. Diese Dissertation zielt darauf ab, eine Reihe von Kombinationen zwischen dem organischen Halbleitern g-CN und Polymermaterialien zu demonstrieren. Diese werden entweder durch photochemische Reaktionen synthetisiert oder in solchen angewendet. Die Herstellungs- und Designprozesse sowie die Anwendungen, die im Rahmen dieser Arbeit durchgeführt wurden, werden im Detail erläutert. Neben UV-Licht wird auch dem sichtbarem Licht als Energiequelle mehr Aufmerksamkeit gewidmet. Durch die Verwendung von sichtbaren Licht können die Materialen in solarenergetischen Anwendungen genutzt werden und die Nachhaltigkeit und Skalierbarkeit der Materialien wird verbessert. KW - polymer chemistry KW - Polymerchemie KW - carbon nitride KW - Kohlenstoffnitriden KW - heterogeneous photocatalysis KW - heterogene Photokatalyse Y1 - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-576253 ER - TY - THES A1 - Galushchinskiy, Alexey T1 - Carbon nitride: a flexible platform for net-oxidative and net-neutral photocatalysis BT - Kohlenstoffnitrid: Eine flexible Plattform für netzoxidative und netzneutrale Photokatalyse N2 - Solar photocatalysis is the one of leading concepts of research in the current paradigm of sustainable chemical industry. For actual practical implementation of sunlight-driven catalytic processes in organic synthesis, a cheap, efficient, versatile and robust heterogeneous catalyst is necessary. Carbon nitrides are a class of organic semiconductors who are known to fulfill these requirements. First, current state of solar photocatalysis in economy, industry and lab research is overviewed, outlining EU project funding, prospective synthetic and reforming bulk processes, small scale solar organic chemistry, and existing reactor designs and prototypes, concluding feasibility of the approach. Then, the photocatalytic aerobic cleavage of oximes to corresponding aldehydes and ketones by anionic poly(heptazine imide) carbon nitride is discussed. The reaction provides a feasible method of deprotection and formation of carbonyl compounds from nitrosation products and serves as a convenient model to study chromoselectivity and photophysics of energy transfer in heterogeneous photocatalysis. Afterwards, the ability of mesoporous graphitic carbon nitride to conduct proton-coupled electron transfer was utilized for the direct oxygenation of 1,3-oxazolidin-2-ones to corresponding 1,3-oxazlidine-2,4-diones. This reaction provides an easier access to a key scaffold of diverse types of drugs and agrochemicals. Finally, a series of novel carbon nitrides based on poly(triazine imide) and poly(heptazine imide) structure was synthesized from cyanamide and potassium rhodizonate. These catalysts demonstrated a good performance in a set of photocatalytic benchmark reactions, including aerobic oxidation, dual nickel photoredox catalysis, hydrogen peroxide evolution and chromoselective transformation of organosulfur precursors. Concluding, the scope of carbon nitride utilization for net-oxidative and net-neutral photocatalytic processes was expanded, and a new tunable platform for catalyst synthesis was discovered. N2 - Die solare Photokatalyse ist eines der führenden Forschungskonzepte im aktuellen Paradigma der nachhaltigen chemischen Industrie. Für die praktische Umsetzung von sonnenlichtgetriebenen katalytischen Prozessen in der organischen Synthese ist ein billiger, effizienter, vielseitiger und robuster heterogener Katalysator erforderlich. Kohlenstoffnitride sind eine Klasse von organischen Halbleitern, von denen bekannt ist, dass sie diese Anforderungen erfüllen. Zunächst wird ein Überblick über den aktuellen Stand der solaren Photokatalyse in Wirtschaft, Industrie und Laborforschung gegeben, wobei die Finanzierung von EU-Projekten, künftige Synthese- und Reformierungsprozesse in großen Mengen, organische Solarchemie in kleinem Maßstab sowie bestehende Reaktorkonstruktionen und -prototypen beschrieben und die Durchführbarkeit des Ansatzes erläutert werden. Anschließend wird die photokatalytische aerobe Spaltung von Oximen in die entsprechenden Aldehyde und Ketone durch anionisches Poly(heptazinimid)-Kohlenstoffnitrid diskutiert. Die Reaktion stellt eine praktikable Methode zur Entschützung und Bildung von Carbonylverbindungen aus Nitrosierungsprodukten dar und dient als geeignetes Modell zur Untersuchung der Chromoselektivität und der Photophysik der Energieübertragung in der heterogenen Photokatalyse. Anschließend wurde die Fähigkeit von mesoporösem graphitischem Kohlenstoffnitrid, protonengekoppelten Elektronentransfer zu leiten, für die direkte Oxygenierung von 1,3-Oxazolidin-2-onen zu den entsprechenden 1,3-Oxazlidin-2,4-Dionen genutzt. Diese Reaktion ermöglicht einen leichteren Zugang zu einem wichtigen Gerüst für verschiedene Arten von Medikamenten und Agrochemikalien. Schließlich wurde eine Reihe neuartiger Kohlenstoffnitride auf der Basis von Poly(triazinimid)- und Poly(heptazinimid)-Strukturen aus Cyanamid und Kaliumrhodizonat synthetisiert. Diese Katalysatoren zeigten eine gute Leistung in einer Reihe von photokatalytischen Benchmark-Reaktionen, einschließlich aerober Oxidation, dualer Nickel-Photoredox-Katalyse, Wasserstoffperoxid-Evolution und chromoselektiver Umwandlung von Organoschwefel-Vorläufern. Abschließend wurde der Anwendungsbereich von Kohlenstoffnitrid für netzoxidative und netzneutrale photokatalytische Prozesse erweitert und eine neue abstimmbare Plattform für die Katalysatorsynthese entdeckt. KW - carbon nitrides KW - Kohlenstoffnitriden KW - heterogeneous photocatalysis KW - heterogene Photokatalyse KW - organic synthesis KW - organische Synthese Y1 - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-610923 ER - TY - THES A1 - Glatzel, Stefan T1 - Cellulose based transition metal nano-composites : structuring and development T1 - Zellulose-basierte Übergangsmetall Nano-Komposite : Strukturierung und Entwicklung N2 - Cellulose is the most abundant biopolymer on earth. In this work it has been used, in various forms ranging from wood to fully processed laboratory grade microcrystalline cellulose, to synthesise a variety of metal and metal carbide nanoparticles and to establish structuring and patterning methodologies that produce highly functional nano-hybrids. To achieve this, the mechanisms governing the catalytic processes that bring about graphitised carbons in the presence of iron have been investigated. It was found that, when infusing cellulose with an aqueous iron salt solution and heating this mixture under inert atmosphere to 640 °C and above, a liquid eutectic mixture of iron and carbon with an atom ratio of approximately 1:1 forms. The eutectic droplets were monitored with in-situ TEM at the reaction temperature where they could be seen dissolving amorphous carbon and leaving behind a trail of graphitised carbon sheets and subsequently iron carbide nanoparticles. These transformations turned ordinary cellulose into a conductive and porous matrix that is well suited for catalytic applications. Despite these significant changes on the nanometre scale the shape of the matrix as a whole was retained with remarkable precision. This was exemplified by folding a sheet of cellulose paper into origami cranes and converting them via the temperature treatment in to magnetic facsimiles of those cranes. The study showed that the catalytic mechanisms derived from controlled systems and described in the literature can be transferred to synthetic concepts beyond the lab without loss of generality. Once the processes determining the transformation of cellulose into functional materials were understood, the concept could be extended to other metals and metal-combinations. Firstly, the procedure was utilised to produce different ternary iron carbides in the form of MxFeyC (M = W, Mn). None of those ternary carbides have thus far been produced in a nanoparticle form. The next part of this work encompassed combinations of iron with cobalt, nickel, palladium and copper. All of those metals were also probed alone in combination with cellulose. This produced elemental metal and metal alloy particles of low polydispersity and high stability. Both features are something that is typically not associated with high temperature syntheses and enables to connect the good size control with a scalable process. Each of the probed reactions resulted in phase pure, single crystalline, stable materials. After showing that cellulose is a good stabilising and separating agent for all the investigated types of nanoparticles, the focus of the work at hand is shifted towards probing the limits of the structuring and pattering capabilities of cellulose. Moreover possible post-processing techniques to further broaden the applicability of the materials are evaluated. This showed that, by choosing an appropriate paper, products ranging from stiff, self-sustaining monoliths to ultra-thin and very flexible cloths can be obtained after high temperature treatment. Furthermore cellulose has been demonstrated to be a very good substrate for many structuring and patterning techniques from origami folding to ink-jet printing. The thereby resulting products have been employed as electrodes, which was exemplified by electrodepositing copper onto them. Via ink-jet printing they have additionally been patterned and the resulting electrodes have also been post functionalised by electro-deposition of copper onto the graphitised (printed) parts of the samples. Lastly in a preliminary test the possibility of printing several metals simultaneously and thereby producing finely tuneable gradients from one metal to another have successfully been made. Starting from these concepts future experiments were outlined. The last chapter of this thesis concerned itself with alternative synthesis methods of the iron-carbon composite, thereby testing the robustness of the devolved reactions. By performing the synthesis with partly dissolved scrap metal and pieces of raw, dry wood, some progress for further use of the general synthesis technique were made. For example by using wood instead of processed cellulose all the established shaping techniques available for wooden objects, such as CNC milling or 3D prototyping, become accessible for the synthesis path. Also by using wood its intrinsic well defined porosity and the fact that large monoliths are obtained help expanding the prospect of using the composite. It was also demonstrated in this chapter that the resulting material can be applied for the environmentally important issue of waste water cleansing. Additionally to being made from renewable resources and by a cheap and easy one-pot synthesis, the material is recyclable, since the pollutants can be recovered by washing with ethanol. Most importantly this chapter covered experiments where the reaction was performed in a crude, home-built glass vessel, fuelled – with the help of a Fresnel lens – only by direct concentrated sunlight irradiation. This concept carries the thus far presented synthetic procedures from being common laboratory syntheses to a real world application. Based on cellulose, transition metals and simple equipment, this work enabled the easy one-pot synthesis of nano-ceramic and metal nanoparticle composites otherwise not readily accessible. Furthermore were structuring and patterning techniques and synthesis routes involving only renewable resources and environmentally benign procedures established here. Thereby it has laid the foundation for a multitude of applications and pointed towards several future projects reaching from fundamental research, to application focussed research and even and industry relevant engineering project was envisioned. N2 - Die vorliegende Arbeit beschäftigt sich mit der Synthese und Strukturierung von Nanokompositen, d.h. mit ausgedehnten Strukturen, welche Nanopartikel enthalten. Im Zuge der Arbeit wurde der Mechanismus der katalytischen Graphitisierung, ein Prozess, bei dem ungeordneter Kohlenstoff durch metallische Nanopartikel in geordneten (graphitischen) Kohlenstoff überführt wird, aufgeklärt. Dies wurde exemplarisch am Beispiel von Zellulose und Eisen durchgeführt. Die untersuchte Synthese erfolgte durch das Lösen eines Eisensalzes in Wasser und die anschließende Zugabe von so viel Zellulose, dass das die gesamte Eisensalzlösung aufgenommen wurde. Die so erhaltene Mischung wurde anschließend unter Schutzgas innerhalb kürzester Zeit auf 800 °C erhitzt. Hierbei zeigte sich, dass zu Beginn der Reaktion Eisenoxidnanopartikel (Rost) auf der Oberfläche der Zellulose entstehen. Beim weiteren Erhöhen der Temperatur werden diese Partikel zu Eisenpartikeln umgewandelt. Diese lösen dann kleine Bereiche der Zellulose auf, wandeln sich in Eisenkarbid um und scheiden graphitischen Kohlenstoff ab. Nach der Reaktion sind die Zellulosefasern porös, jedoch bleibt ihre Faserstruktur vollkommen erhalten. Dies konnte am Beispiel eines Origamikranichs gezeigt werden, welcher nach dem Erhitzen zwar seine Farbe von Weiß zu Schwarz verändert hatte, ansonsten aber seine Form vollkommen beibehält. Aufgrund der eingebetteten Eisenkarbid Nanopartikel war der Kranich außerdem hochgradig magnetisch. Basierend auf dieser Technik wurden außerdem winzige metallische Nanopartikel aus Nickel, Nickel-Palladium, Nickel-Eisen, Kobalt, Kobalt-Eisen und Kupfer, sowie Partikel aus den Verbundkarbiden Eisen-Mangan-Karbid und Eisen-Wolfram-Karbid, jeweils in verschiedenen Mischungsverhältnissen, hergestellt und analysiert. Da die Vorstufe der Reaktion flüssig ist, konnte diese mit Hilfe eines einfachen kommerziellen Tintenstrahldruckers strukturiert auf Zellulosepapier aufgebracht werden. Dies ermöglicht gezielt Leiterbahnen, bestehend aus graphitisiertem Kohlenstoff, in ansonsten ungeordnetem (amorphen) Kohlenstoff zu erzeugen. Diese Methode wurde anschließend auf Systeme mit mehreren Metallen übertragen. Hierbei wurde die Tatsache, dass moderne Drucker vier Tintenpatronen beherbergen, ausgenutzt um Nanopartikel mit beliebigen Mischungsverhältnisse von Metallen zu erzeugen. Dieser Ansatz hat potentiell weitreichende Auswirkungen im Feld der Katalyse, da hiermit hunderte oder gar tausende Mischungen simultan erzeugt und getestet werden können. Daraus würden sich große Zeiteinsparungen (Tage anstelle von Monaten) bei der Entwicklung neuer Katalysatoren ergeben. Der letzte Teil der Arbeit beschäftigt sich mit der umweltfreundlichen Synthese der obengenannten Komposite. Hierbei wurden erfolgreich Altmetall und Holzstücke als Ausgangstoffe verwandt. Zusätzlich wurde gezeigt, dass die gesamte Synthese ohne Verwendung von hochentwickeltem Equipment durchgeführt werden kann. Dazu wurde eine sogenannte Fresnel-Linse genutzt um Sonnenlicht zu bündeln und damit direkt die Reaktionsmischung auf die benötigten 800 °C zu erhitzen. Weiterhin wurde ein selbst gebauter Glasreaktor eingesetzt und gezeigt, wie das entstehende Produkt als Abwasserfilter genutzt werden kann. Die Kombination dieser Ergebnisse bedeutet, dass dieses System sich beispielsweise zum Einsatz in Katastrophenregionen eignen würde, um ohne Strom und besondere Ausrüstung vor Ort Wasserfilter herzustellen. KW - Zellulose KW - Übergangsmetalle KW - Carbide KW - Nanopartikel KW - Komposite KW - Cellulose KW - Transitionmetals KW - Carbides KW - Nanoparticles KW - Composites Y1 - 2013 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-64678 ER - TY - THES A1 - Debsharma, Tapas T1 - Cellulose derived polymers T1 - Polymere aus Cellulose BT - synthesis of functional and degradable polymers from cellulose N2 - Plastics, such as polyethylene, polypropylene, and polyethylene terephthalate are part of our everyday lives in the form of packaging, household goods, electrical insulation, etc. These polymers are non-degradable and create many environmental problems and public health concerns. Additionally, these polymers are produced from finite fossils resources. With the continuous utilization of these limited resources, it is important to look towards renewable sources along with biodegradation of the produced polymers, ideally. Although many bio-based polymers are known, such as polylactic acid, polybutylene succinate adipate or polybutylene succinate, none have yet shown the promise of replacing conventional polymers like polyethylene, polypropylene and polyethylene terephthalate. Cellulose is one of the most abundant renewable resources produced in nature. It can be transformed into various small molecules, such as sugars, furans, and levoglucosenone. The aim of this research is to use the cellulose derived molecules for the synthesis of polymers. Acid-treated cellulose was subjected to thermal pyrolysis to obtain levoglucosenone, which was reduced to levoglucosenol. Levoglucosenol was polymerized, for the first time, by ring-opening metathesis polymerization (ROMP) yielding high molar mass polymers of up to ~150 kg/mol. The poly(levoglucosenol) is thermally stable up to ~220 ℃, amorphous, and is exhibiting a relatively high glass transition temperature of ~100 ℃. The poly(levoglucosenol) can be converted to a transparent film, resembling common plastic, and was found to degrade in a moist acidic environment. This means that poly(levoglucosenol) may find its use as an alternative to conventional plastic, for instance, polystyrene. Levoglucosenol was also converted into levoglucosenyl methyl ether, which was polymerized by cationic ring-opening metathesis polymerization (CROP). Polymers were obtained with molar masses up to ~36 kg/mol. These polymers are thermally stable up to ~220 ℃ and are semi-crystalline thermoplastics, having a glass transition temperature of ~35 ℃ and melting transition of 70-100 ℃. Additionally, the polymers underwent cross-linking, hydrogenation and thiol-ene click chemistry. N2 - Kunststoffe wie Polyethylen, Polypropylen und Polyethylenterephthalat sind ein großer Bestandteil unseres Alltags und finden Verwendung unter anderem als Verpackungsmaterialien, Haushaltswaren und Elektroisolierungen. Diese Polymere werden aus fossilen Ressourcen hergestellt, sind nicht abbaubar und verursachen nicht nur viele Umweltprobleme sondern können auch zu Gesundheitsschäden führen. Aufgrund dessen muss die Verwendung von erneuerbaren Ressourcen geachtet werden, wobei die hergestellten Polymere im Idealfall komplett biologisch abbaubar sind. Obwohl viele biobasierte Polymere, wie Polymilchsäure, Polybutylensuccinatadipat oder Polybutylensuccinat, bekannt sind, hat noch keines das Potential gezeigt, herkömmliche Polymere zu ersetzen. Cellulose ist einer der am häufigsten in der Natur produzierten nachwachsenden Rohstoffe und kann in verschiedene kleine organische Moleküle wie Zucker (Saccharide), Furan und auch Levoglucosenon umgewandelt werden. Ziel dieser Arbeit ist die Verwendung von Levoglucosenon als Monomer für die Synthese von Polymeren. Säurebehandelte Cellulose wurde einer thermischen Pyrolyse unterzogen, um Levoglucosenon zu erhalten, das dann weiter zu Levoglucosenol reduziert wurde. Das Levoglucosenol wurde zum ersten Mal erfolgreich über eine Ringöffnungsmetathese-Polymerisation (ROMP) polymerisiert. Die Molmassen der hergestellten Polymere erreichten Werte von bis zu ~150 kg/mol. Die thermische Analyse von Poly(levoglucosenol) zeigt, dass es bis zu einer Temperatur von ~220 ℃ stabil ist, eine Glasübergangstemperatur bei ~100 ℃ hat und ein amorphes Polymer ist. Weiterhin kann das Poly(levoglucosenol) in feuchter saurer Umgebung in kurzer Zeit abgebaut werden. Aufgrund dieser Eigenschaften kann Poly(levoglucosenol) als Alternative zu konventionellem Kunststoff, wie z.B. Polystyrol, eingesetzt werden kann. Levoglucosenol wurde weiter in Levoglucosenylmethylether umgewandelt. Levoglucosenylmethylether kann mit kationischer Ringöffnungs-Polymerisation (CROP) polymerisiert werden. Es wurden Polymere mit Molmassen von bis zu ~36 kg/mol hergestellt. Die Polymere weisen eine thermische Stabilität bis zu einer Temperatur von ~220 °C auf. Es handelt sich bei den hergestellten Poly(levoglucosenylmethylethern) um teilkristalline Thermoplaste, deren Glasüberganstemperatur bei ~35 °C und der Schmelzbereich bei 70-100 °C liegt. Die Doppelbindungen des Levoglucosenylmethylethers wurden genutzt um das Polymer zu vernetzen und zu funktionalisieren. KW - biomass valorization KW - levoglucosenol KW - ring-opening polymerization KW - degradable polymer KW - sustainable chemistry KW - Biomasseverwertung KW - Levoglucosenol KW - ringöffnende Polymerisation KW - abbaubares Polymer KW - nachhaltige Chemie Y1 - 2019 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-441312 ER - TY - THES A1 - Zarafshani, Zoya T1 - Chain-end functionalization and modification of polymers using modular chemical reactions T1 - Ketten-Ende Funktionalisierung und Modifikation von Polymeren mittels modulare chemischen Reaktionen N2 - Taking advantage of ATRP and using functionalized initiators, different functionalities were introduced in both α and ω chain-ends of synthetic polymers. These functionalized polymers could then go through modular synthetic pathways such as click cycloaddition (copper-catalyzed or copper-free) or amidation to couple synthetic polymers to other synthetic polymers, biomolecules or silica monoliths. Using this general strategy and designing these co/polymers so that they are thermoresponsive, yet bioinert and biocompatible with adjustable cloud point values (as it is the case in the present thesis), the whole generated system becomes "smart" and potentially applicable in different branches. The applications which were considered in the present thesis were in polymer post-functionalization (in situ functionalization of micellar aggregates with low and high molecular weight molecules), hydrophilic/hydrophobic tuning, chromatography and bioconjugation (enzyme thermoprecipitation and recovery, improvement of enzyme activity). Different α-functionalized co/polymers containing cholesterol moiety, aldehyde, t-Boc protected amine, TMS-protected alkyne and NHS-activated ester were designed and synthesized in this work. N2 - In dieser Arbeit wurden mittels der ATRP Methode sowie durch Benutzung funktioneller Initiatoren verschiedene Funktionalitäten an der α- und ω-Position der synthetischen Polymere (Kettenenden) eingeführt. Diese funktionalisierten Polymere können durch modulare synthetische Methoden wie z.B. die “Klick-Zykloaddition” (kupferkatalysiert oder auch kupferfreie Methoden möglich), Amidierung mit anderen synthetischen Polymeren oder Biomolekülen, oder auch mit Silikatmonolithen gekuppelt werden. Den beschriebenen Strategien folgend und unter Benutzung von thermoresponsiven, bioinerten und biokompartiblen (Co-) Polymeren mit einstellbaren Trübungspunkten können mittels Temperaturänderungen leicht steuerbare, „smarte“ Polymersysteme für verschiedene Anwendungen hergestellt werden. Im Rahmen dieser Arbeit wurden speziell Anwendungen wie die Postfunktionalisierung (in situ Funktionalisierung mizellarer Aggregate mit Molekülen, die sowohl niedrige als auch höhere Molekulargewichte aufweisen), hydrophiles/hydrophobes Tuning von Polymeren, Chromatographie an Polymeren sowie Biokonjugation von Polymeren (Enzymthermoprezipitation und -Gewinnung, Enzymaktivitätsmodifizierung) genauer untersucht. Es wurden verschiedene α-funktionalisierte (Co-)Polymere, die Cholesterol, Aldehyde, t-Boc geschützte Amine, TMS-geschützte Alkine und NHS-aktivierte Ester entwickelt und hergestellt und mittels passender ATRP Initiatoren eingeführt. KW - Atom Transfer Radical Polymerization KW - Klick-Chemie KW - Biokonjugation KW - Funktionalisierung KW - Modifizierung von Polymeren KW - ATRP KW - Click chemistry KW - Bioconjugation KW - Functionalization KW - Polymer Modification Y1 - 2012 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-59723 ER - TY - THES A1 - Sapei, Lanny T1 - Characterisation of silica in Equisetum hyemale and its transformation into biomorphous ceramics T1 - Charakterisierung von Siliciumdioxid in Winterschachtelhalmen und dessen Umwandlung in biomorphe Keramiken N2 - Equisetum spp. (horsetail / “Schachtelhalm”) is the only surviving genus of the primitive Sphenopsids vascular plants which reached their zenith during the Carboniferous era. It is an herbaceous plant and is distinguished by jointed stems with fused whorl of nodal leaves. The plant has been used for scouring kitchen utensils and polishing wood during the past time due to its high silica encrustations in the epidermis. Equisetum hyemale (scouring rush) can accumulate silica up to 16% dry weight in its tissue, which makes this plant an interesting candidate as a renewable resource of silica for the synthesis of biomorphous ceramics. The thesis comprises a comprehensive experimental study of silica accumulations in E.hyemale using different characterisation techniques at all hierarchical levels. The obtained results shed light on the local distribution, chemical form, crystallinity, and nanostructure of biogenic silica in E.hyemale which were quite unclear until now. Furthermore, isolation of biogenic silica from E.hyemale to obtain high grade mesoporous silica with high purity is investigated. Finally, syntheses of silicon carbide (b-SiC) by a direct thermoconversion process of E.hyemale is attempted, which is a promising material for high performance ceramics. It is found that silica is deposited continuously on the entire epidermal layer with the highest concentration on the knobs. The highest silicon content is at the knob tips (≈ 33%), followed by epidermal flank (≈ 17%), and inner lower knob (≈ 6%), whereas there is almost no silicon found in the interior parts. Raman spectroscopy reveals the presence of at least two silica modifications in E.hyemale. The first type is pure hydrated amorphous silica restricted to the knob tips. The second type is accumulated on the entire continuous outer layer adjacent to the epidermis cell walls. It is lacking silanol groups and is intimately associated with polysaccharides (cellulose, hemicellulose, pectin) and inorganic compounds. Silica deposited in E.hyemale is found to be mostly amorphous with almost negligible amounts of crystalline silica in the form of a-quartz (< 7%). The silica primary particles have a plate-like shape with a thickness of about 2 nm. Pure mesoporous amorphous silica with an open surface area up to 400 m2/g can be obtained from E.hyemale after leaching the plant with HCl to remove the inorganic impurities followed by a calcination treatment. The optimum calcination temperature appears to be around 500°C. Calcination of untreated E.hyemale causes a collapse of the biogenic silica structure which is mainly attributed to the detrimental action of alkali ions present in the native plant. Finally, pure b-SiC with a surface area of about 12 m2/g is obtained upon direct pyrolysis of HCl-treated E.hyemale samples in argon atmosphere. The original structure of native E.hyemale is substantially retained in the biomorphous b-SiC. The results of this thesis lead to a better understanding of the silicification process and allow to draw conclusions about the role of silica in E.hyemale. In particular, a templating role of the plant biopolymers for the synthesis of the nanostructured silica within the plant body can be deduced. Moreover, the high grade ultrafine amorphous silica isolated from E.hyemale promises applications as adsorbent and catalyst support and as silica source for the fabrication of silica-based composites. The synthesis of biomorphous b-SiC from sustainable and low-cost E.hyemale is still in its initial stage. The present thesis demonstrates the principal possibility of carbothermal synthesis of SiC from E.hyemale with the prospect of potential applications, for instance as refractory materials, catalyst supports, or high performance advanced ceramics. N2 - Equisetum spp. (Schachtelhalm) ist die einzige überlebende Gattung der Schachtelhalmgewächse, die ihren Zenit während der Karbon Ära erreichten. Der Schachtelhalm ist eine krautartige Pflanze und wird durch verbundene Stämme mit fixiertem Wirtel der Knotenblätter unterschieden. Aufgrund seiner hohen Siliciumdioxid Bedeckung in der Epidermis sind Winterschachtelhalmen lange Zeit zur Reinigung von Küchegeräten und zum Polieren von Holz verwendet worden. Der Winterschachtelhalm (auch Scheuerkraut genannt) kann Siliciumdioxid bis zu 16% Trockengewicht in seinem Gewebe ansammeln. Dies macht aus dieser Pflanze einen interessanten Kandidaten als erneubare Ressource von Siliciumdioxid für die Synthese von biomorphen Keramiken. Die vorliegende Doktorarbeit beinhaltet eine ausführliche experimentelle Studie der Siliciumdioxidansammlungen in Winterschachtelhalmen mittels unterschiedlicher Charakterisierungstechniken auf allen hierarchischen Ebenen. Die Ergebnisse der Arbeit werfen neues Licht auf die lokale Verteilung, die chemischen Form, die Kristallinität und die Nanostruktur des biogenen Siliciumdioxids, die bisher ziemlich unklar waren. Außerdem werden Möglichkeiten zur Isolierung des biogenen Siliciumdioxids aus Winterschachtelhalmen untersucht, um hochgradig reines Siliciumdioxid zu erhalten. Auch wird die direkte carbothermale Synthese von Siliciumkarbid (b-SiC) aus Schachtelhalmen untersucht, mit dem Ziel einer kostengünstigen Herstellung von Hochleistungskeramiken aus nachwachsenden Rohstoffen Es wird gezeigt, dass das Siliciumdioxid in einer kontinuierlichen Schicht in der Epidermis vorliegt, mit der höchsten Siliciumkonzentration in den auffälligen knopfartigen Ausbuchtungen. Den höchsten Siliciumgehalt zeigen die Knopfspitzen (≈ 33%), gefolgt von der epidermalen Flanke (≈ 17%) und inneren unteren Teile der Knöpfe (≈ 6%), während es in den inneren Teilen der Pflanze praktisch kein Silicium gibt. Ramanspektroskopie beweist eindeutig, dass mindestens zwei Siliciumdioxid Modifikationen vorhanden sind. Der erste Typ ist reines hydratisiertes amorphes Siliciumdioxid, das auf den Bereich der Knopfspitzen beschränkt ist. Der zweite Typ wird in der gesamten kontinuierlichen äußeren Schicht angesammelt, weist keine Ramanbanden von Silanolgruppen auf, und ist örtlich eng verknüpft mit Banden von Polysacchariden (Zellulose, Hemizellulose, Pektin) sowie anorganischen Verbindungen. Der Großteil des Siliciumdioxids in Winterschachtelhalmen ist amorph mit unwesentlichen Mengen an kristallinem a-Quarz (< 7%). Die primären Siliciumdioxidpartikel haben eine plattenähnliche Form mit einer Dicke von ungefähr 2 nm. Hochreines mesoporöses amorphes Siliciumdioxid mit offener Porosität und innerer Oberfläche bis zu 400 m2/g kann aus Winterschachtelhalmen isoliert werden. Dies wird erreicht indem man die Pflanze mit Salzsäure behandelt um die anorganischen Verunreinigungen zu entfernen, gefolgt von einer Kalzinierung, wobei die optimale Temperatur bei etwa 500°C liegt. Im Gegensatz zu den chemisch vorbehandelten Schachtelhalmen, verursacht die Kalzinierung von unbehandelten Winterschachtelhalmen einen Kollaps der biogenen Siliciumdioxidstruktur, und es werden nur sehr kleine innere Oberflächen erzielt. Dies wird hauptsächlich dem Einfluss der Alkaliionen zugeschrieben die in der unbehandelten Pflanze vorhanden sind. Es wird schließlich gezeigt, dass durch direkte Pyrolyse der HCl-behandelten Winterschachtelhalme in Argonatmosphäre reines b-SiC mit einer Oberfläche von ungefähr 12 m2/g erzeugt werden kann. Die ursprüngliche Struktur von natürlichen Winterschachtelhalmen bleibt dabei im Wesentlichen im biomorphen b-SiC erhalten. Die Ergebnisse dieser Arbeit führen zu einem besseren Verständnis des Silicifizierungsprozesses und erlauben es auch, Aussagen über die mögliche Rolle von Siliciumdioxid in E.hyemale zu treffen. Insbesondere kann den Pflanzenpolymeren die Rolle eines Templates bei der Synthese des biogenen Siliciumdioxids im Pflanzengewebe zugeschrieben werden. Das aus den Pflanzen isolierte ultrafeine amorphe Siliciumdioxid mit hoher Reinheit verspricht potentielle Anwendungen, z.B. als Adsorbent oder Katalysatorsupport, und auch als Füllmaterial für die Herstellung von Komopositmaterialien. Die Synthese von biomorphem b-SiC aus erneubaren und preiswerten Winterschachtelhalmen steht zwar erst am Anfang, jedoch konnte die vorliegende Arbeit die prinzipielle Machbarkeit aufzeigen. Dieses Material scheint sehr vielversprechend für eine Reihe technischer Anwendung, zum Beispiel als Refraktärmaterial, Katalysatorsupport oder neuartige Hochleistungskeramik. KW - Siliciumdioxid KW - Winterschachtelhalm KW - Raman KW - Röntgenbeugung KW - Mikrotomographie KW - silica KW - Equisetum hyemale KW - Raman KW - SAXS KW - microtomography Y1 - 2007 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-15883 ER - TY - THES A1 - Qin, Qing T1 - Chemical functionalization of porous carbon-based materials to enable novel modes for efficient electrochemical N2 fixation T1 - Chemische Funktionalisierung von porösen Materialien auf Kohlenstoffbasis zur Ermöglichung neuartiger Verfahren für eine effiziente elektrochemische N2-Fixierung N2 - The central motivation of the thesis was to provide possible solutions and concepts to improve the performance (e.g. activity and selectivity) of electrochemical N2 reduction reaction (NRR). Given that porous carbon-based materials usually exhibit a broad range of structural properties, they could be promising NRR catalysts. Therefore, the advanced design of novel porous carbon-based materials and the investigation of their application in electrocatalytic NRR including the particular reaction mechanisms are the most crucial points to be addressed. In this regard, three main topics were investigated. All of them are related to the functionalization of porous carbon for electrochemical NRR or other electrocatalytic reactions. In chapter 3, a novel C-TixOy/C nanocomposite has been described that has been obtained via simple pyrolysis of MIL-125(Ti). A novel mode for N2 activation is achieved by doping carbon atoms from nearby porous carbon into the anion lattice of TixOy. By comparing the NRR performance of M-Ts and by carrying out DFT calculations, it is found that the existence of (O-)Ti-C bonds in C-doped TixOy can largely improve the ability to activate and reduce N2 as compared to unoccupied OVs in TiO2. The strategy of rationally doping heteroatoms into the anion lattice of transition metal oxides to create active centers may open many new opportunities beyond the use of noble metal-based catalysts also for other reactions that require the activation of small molecules as well. In chapter 4, a novel catalyst construction composed of Au single atoms decorated on the surface of NDPCs was reported. The introduction of Au single atoms leads to active reaction sites, which are stabilized by the N species present in NDPCs. Thus, the interaction within as-prepared AuSAs-NDPCs catalysts enabled promising performance for electrochemical NRR. For the reaction mechanism, Au single sites and N or C species can act as Frustrated Lewis pairs (FLPs) to enhance the electron donation and back-donation process to activate N2 molecules. This work provides new opportunities for catalyst design in order to achieve efficient N2 fixation at ambient conditions by utilizing recycled electric energy. The last topic described in chapter 5 mainly focused on the synthesis of dual heteroatom-doped porous carbon from simple precursors. The introduction of N and B heteroatoms leads to the construction of N-B motives and Frustrated Lewis pairs in a microporous architecture which is also rich in point defects. This can improve the strength of adsorption of different reactants (N2 and HMF) and thus their activation. As a result, BNC-2 exhibits a desirable electrochemical NRR and HMF oxidation performance. Gas adsorption experiments have been used as a simple tool to elucidate the relationship between the structure and catalytic activity. This work provides novel and deep insights into the rational design and the origin of activity in metal-free electrocatalysts and enables a physically viable discussion of the active motives, as well as the search for their further applications. Throughout this thesis, the ubiquitous problems of low selectivity and activity of electrochemical NRR are tackled by designing porous carbon-based catalysts with high efficiency and exploring their catalytic mechanisms. The structure-performance relationships and mechanisms of activation of the relatively inert N2 molecules are revealed by either experimental results or DFT calculations. These fundamental understandings pave way for a future optimal design and targeted promotion of NRR catalysts with porous carbon-based structure, as well as study of new N2 activation modes. N2 - Die zentrale Motivation der Arbeit war es, mögliche Lösungen und Konzepte zur Verbesserung der Leistung (z.B. Aktivität und Selektivität) der elektrochemischen N2-Reduktionsreaktion (NRR) anzubieten. Da poröse Materialien auf Kohlenstoffbasis in der Regel ein breites Spektrum an strukturellen Eigenschaften aufweisen, könnten sie vielversprechende NRR-Katalysatoren sein. Daher sind das fortgeschrittene Design neuartiger poröser Materialien auf Kohlenstoffbasis und die Untersuchung ihrer Anwendung in der elektrokatalytischen NRR einschließlich der besonderen Reaktionsmechanismen die wichtigsten Punkte, die angegangen werden müssen. In diesem Zusammenhang wurden drei Hauptthemen untersucht. Alle von ihnen stehen im Zusammenhang mit der Funktionalisierung von porösem Kohlenstoff für elektrochemische NRR oder andere elektrokatalytische Reaktionen. In Kapitel 3 wurde ein neuartiger C-TixOy/C-Nanokomposit beschrieben, der durch einfache Pyrolyse von MIL-125(Ti) gewonnen wurde. Ein neuartiger Modus für die N2-Aktivierung wird durch Dotierung von Kohlenstoffatomen aus nahegelegenem porösem Kohlenstoff in das Aniongitter von TixOy erreicht. Durch den Vergleich der NRR-Leistung von M-Ts und die Durchführung von DFT-Berechnungen wird festgestellt, dass die Existenz von (O-)Ti-C-Bindungen in C-dotiertem TixOy die Fähigkeit zur Aktivierung und Reduktion von N2 im Vergleich zu unbesetzten OVs in TiO2 erheblich verbessern kann. Die Strategie, Heteroatome rational in das Aniongitter von Übergangsmetalloxiden zu dotieren, um aktive Zentren zu schaffen, kann viele neue Möglichkeiten eröffnen, die über den Einsatz von edelmetallbasierten Katalysatoren hinausgehen, auch für andere Reaktionen, die ebenfalls die Aktivierung von kleinen Molekülen erfordern. In Kapitel 4 wurde über eine neuartige Katalysatorkonstruktion aus Au-Einzelatomen berichtet, die auf der Oberfläche von NDPCs dekoriert sind. Die Einführung von Au-Einzelatomen führt zu aktiven Reaktionsstellen, die durch die in NDPCs vorhandenen N-Spezies stabilisiert werden. So ermöglichte die Interaktion innerhalb von hergestellten AuSAs-NDPCs-Katalysatoren eine vielversprechende Leistung für die elektrochemische NRR. Für den Reaktionsmechanismus können Au-Einzelstandorte und N- oder C-Spezies als frustrierte Lewis-Paare (FLPs) fungieren, um den Elektronenabgabe- und Rückgabeprozess zur Aktivierung von N2-Molekülen zu verbessern. Diese Arbeit bietet neue Möglichkeiten für das Design von Katalysatoren, um eine effiziente N2-Fixierung unter Umgebungsbedingungen durch die Nutzung recycelter elektrischer Energie zu erreichen. Das letzte in Kapitel 5 beschriebene Thema konzentrierte sich hauptsächlich auf die Synthese von dualem heteroatomdotiertem porösem Kohlenstoff aus einfachen Vorläufern. Die Einführung von N- und B-Heteroatomen führt zur Konstruktion von N-B-Motiven und frustrierten Lewis-Paaren in einer mikroporösen Architektur, die ebenfalls reich an Punktdefekten ist. Dies kann die Adsorptionskraft verschiedener Reaktanden (N2 und HMF) und damit deren Aktivierung verbessern. Infolgedessen weist BNC-2 eine wünschenswerte elektrochemische NRR- und HMF-Oxidationsleistung auf. Gasadsorptionsexperimente wurden als einfaches Werkzeug zur Aufklärung des Zusammenhangs zwischen Struktur und katalytischer Aktivität eingesetzt. Diese Arbeit liefert neue und tiefe Einblicke in das rationale Design und den Ursprung der Aktivität bei metallfreien Elektrokatalysatoren und ermöglicht eine physikalisch tragfähige Diskussion der aktiven Motive, sowie die Suche nach deren weiteren Anwendungen. Während dieser Arbeit, die allgegenwärtigen Probleme der niedrigen Selektivität und Aktivität der elektrochemischen NRR werden durch die Gestaltung poröser Katalysatoren auf Kohlenstoffbasis mit hoher Effizienz und die Erforschung ihrer katalytischen Mechanismen. Die Struktur-Leistungsbeziehungen und Aktivierungsmechanismen der relativ inerten N2-Moleküle werden entweder durch experimentelle Ergebnisse oder DFT-Berechnungen aufgezeigt. Diese grundlegenden Erkenntnisse ebnen den Weg für ein zukünftiges optimales Design und eine gezielte Förderung von NRR-Katalysatoren mit poröser Kohlenstoffstruktur, sowie für die Untersuchung neuer N2-Aktivierungsmodi. KW - N2 fixation KW - porous carbon-based materials KW - ammonia KW - selectivity KW - N2-Fixierung KW - porösen Materialien auf Kohlenstoffbasis KW - Ammoniak KW - Selektivität Y1 - 2019 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-443397 ER - TY - THES A1 - Appajaiah, Anilkumar T1 - Climatic stability of polymer optical fibers (POF) N2 - Optische Polymerfasern stellen ein relativ neues Medium zur Hochgeschwindigkeitsdatenübertragung mittels moduliertem Licht dar. Sie gestatten die Verbreitung großer Datenmengen über Entfernungen bis zu ca. 100 m, ohne eine Beeinflussung durch externe elektromagnetischen Feldern. Jedoch reagieren die Fasern und somit auch ihre optischen Eigenschaften aufgrund des organischchemischen Faseraufbaus empfindlich auf das Klima ihrer Umgebung. Die Ursachen für die Abnahme der optischen Transmission aufgrund von klimatischen Einflüssen (Alterung, Degradation) werden mittels chemisch analytischer Verfahren wie Chemilumineszenz (CL) und Fourier Transform Infrarot (FTIR) Spektroskopie untersucht. Dabei kommen fünf, von verschiedenen Herstellern bezogene, Multimode- POFs aus PMMA in sieben verschiedenen Klimaten zum Einsatz. Drei dieser fünf POFs werden genauer untersucht, um den Einfluss einzelner Parameter festzustellen und optische Langzeitstabilität aufgrund von Kurzzeittests vorherzusagen. Als erstes erfolgt eine Kennzeichnung unbeanspruchter POF Komponenten (Kern, Mantel und nackte POF als Kombination von Kern und Mantel) über ihre physikalischen und chemischen Eigenschaften. Die Glas- und die Schmelztemperaturen liegen im Bereich von 120 °C bis 140 °C, das Molekulargewicht des Kerns bei größenordnungsmäßig 105 g mol-1 ;. FTIR-Messungen zeigen zwar Unterschiede in der chemischen Zusammensetzung der Mäntel aber keine Unterschiede bei den Kernen. Bei zwei der POF Proben , die als Kabel (Kern, Mantel und Schutzhülle) für 3300 Stunden einem Klima aus 92 °C und 95 % relativer Feuchte (r.F.) ausgesetzt waren, verringern sich daraufhin die optische Transmissionen in unterschiedlicher Weise. Die Untersuchung der zugehörigen nackten POFs mittels CL, FTIR, Thermogravimetrie (TG), UV/VIS und Gel Permeation Chromatographie (GPC) lässt eine stärkere Schädigung der Mäntel als der Kerne vermuten. Wahrscheinlich führt eine starke Manteldegradation zu einer erhöhten Absorption und Fehlstellen im Mantel und damit zu einer Transmissionsabnahme. Daher scheint die optische Stabilität der POF stärker durch die thermo-oxidative Stabilität des Mantels bestimmt zu sein als durch die des Kernes. Drei nackte POFs (Kern und Mantel) sind unterschiedlich lang (30 Stunden bis 3000 Stunden) folgenden Klimaten ausgesetzt: 92 °C / 95 % r.F., 92 °C / 50 % r.F., 50 °C / 95 % r.F., 90 °C / geringe Feuchte, 100 °C / geringe Feuchte, 110 °C / geringe Feuchte and 120 °C / geringe Feuchte. Auch in diesen Klimaten ergaben sich probenbedingte unterschiedliche Transmissionsänderungen. Die Ergebnisse deuten stark darauf hin, dass bei gleichzeitig hoher Temperatur und hoher Feuchte physikalische Änderungen wie die Volumenausdehnung die Hauptursachen für die Abnahme der optischen Transmission bilden. Ein weiterer Einflussfaktor ist die chemische Zusammensetzung der Mäntel. Bei Kombination von hoher Temperatur und geringer Feuchte erzeugen in den Anfangsstadien der Alterung physikalische Änderungen Transmissionsabnahmen, vermutlich entstehen Fehlstellen in der Kern-Mantel-Grenzschicht. Hinzukommen in den späteren Stadien wahrscheinlich zunehmende Lichtabsorption in Kern und Mantel. L. Jankowski (Doktorand in der BAM) bestätigt diese Annahme durch parallel ausgeführte optische Simulationsrechnungen. Auch für nackte POFs scheint also die thermo-oxidative Stabilität die optische Stabilität zu bestimmen. Kurzzeitalterungstests sollen Aufschluss über den Einfluss individueller Klimaparameter auf die POF Eigenschaften geben. Es zeigt sich bei dauerhaft hoher Temperatur und variabler Feuchte aufgrund des physikalisch absorbierten Wassers bis zu einem gewissen Grad ein reversibles Verhalten des Transmissionsverlustes. Dieses Verhalten tritt aber nur kaum merkbar auf, wenn bei konstanter hoher Feuchte die Temperatur variiert wird. Bei Raumtemperatur und variabler Feuchte stellt sich jedoch ein voll reversibles Verhalten des Transmissionsverlustes ein. Die hier beschriebenen Untersuchungen sind als Ausgangspunkt für weitergehende Forschungen zu verstehen. Die begrenzte Zurverfügungstellung von POF Basisdaten durch die Hersteller und der zeitaufwendige klimabedingte Alterungsprozess beschränken die Ergebnisse mehr oder weniger auf die untersuchten Proben. Signifikante allgemeine Aussagen erfordern aber beispielsweise zusätzliche statistische Daten der Produktionsschwankungen von POF Eigenschaften. Dennoch besitzen die hier beschriebenen Tests das Potential für eine Annäherung an die optische Langzeitstabilität und deren Vorhersage. N2 - Polymer optical fibers (POFs) are a rather new tool for high-speed data transfer by modulated light. They allow the transport of high amounts of data over distances up to about 100 m without be influenced by external electromagnetic fields. Due to organic chemical nature of POFs, they are sensitive to the climate of their environment and therefore the optical fiber properties are as well. Hence, the optical stability is a key issue for long-term applications of POFs. The causes for a loss of optical transmission due to climatic exposures (aging/degradation) are researched by means of chemical analytical tools such as chemiluminescence (CL) and Fourier transform infrared (FTIR) spectroscopy for five different (with respect to manufacturers) step-index multimode PMMA based POFs and for seven different climatic conditions. Three of the five POF samples are studied more in detail to realize the effects of individual parameters and for forecasting longterm optical stability by short-term exposure tests. At first, the unexposed POF components (core, cladding, and bare POF as combination of core and cladding) are characterized with respect to important physical and chemical properties. The glass transition temperature Tg, and the melting temperature Tm are in the region of 120 °C to 140 °C, the molecular weight (Mw) of cores is in the order of 105 g mol-1. POFs are found to have different chemical compositions of their claddings as could be detected by FTIR, but identical compositions of their cores. Two of the POFs are exposed as cables (core, cladding and jacket) for about 3300 hours to the climate 92 °C / 95 % relative humidity (RH) resulting in a different transmission decrease. Investigating the related unexposed and exposed bare POFs for degradation using CL, FTIR, thermogravimetry (TG), UV/visible transmittance and gel permeation chromatography (GPC) suggest that claddings of POFs are more affected than cores. Probably the observed loss of transmission is mainly due to increased light absorption and imperfections at the core-cladding boundary caused by a large degradation of claddings. Hence, it is highly possible that the optical transmission stability of POFs is governed mainly by the thermo-oxidative stability of the cladding and minor of the core. Three bare POFs (core and cladding only) are exposed for different duration of exposure time (30 hours to 4500 hours) to 92 °C / 95 %RH, 92 °C / 50 %RH, 50 °C / 95 %RH, 90 °C / low humidity, 100 °C / low humidity, 110 °C / low humidity and 120 °C / low humidity. In these climates their transmission variations are found to be different from each other, too. The outcomes strongly inform that under high temperature and high humid climates physical changes such as volume expansion, are the main sources for the loss of optical transmission. Also, the optical transmission stability of POFs is found to be dependent on chemical compositions of claddings. Under high temperature and low humid conditions, a loss of transmission at the early stages of the exposure is mainly caused by physical changes, presumable by corecladding interface imperfections. For the later stages of exposures it is proposed to an additional increase of light absorption by core and cladding owes to degradation. Optical simulation results obtained parallel by Mr. L. Jankowski (a PhD student of BAM) are found to confirm these results. For bare POFs, too, the optical stability of POFs seems to depend on their thermo-oxidative stability. Some short-term exposure tests are conducted to realize influences of individual climatic parameters on the transmission property of POFs. It is found that at stationary high temperature and variable humidity conditions POFs display to a certain amount a reversible transmission loss due to physically absorbed water. But in the case of varying temperature and constant high humidity such reversibility is hardly noticeable. However, at room temperature and varying humidity, POFs display fully reversible transmission loss. The whole research described above has to be regarded as a starting point for further investigations. The restricted distribution of fundamental POF data by the manufacturers and the time consuming aging by climatic exposures restrict the results more or less to the samples, investigated here. Significant general statements require for example additional information concerning the variation of POF properties due to production. Nevertheless the tests, described here, have the capability for approximating and forecasting the long-term optical transmission stability of POFs. -------------- Auch im Druck erschienen: Appajaiah, Anilkumar: Climatic stability of polymer optical fibers (POF) / Anilkumar Appajaiah. - Bremerhaven : Wirtschaftsverl. NW, Verl. für neue Wiss., 2005. - Getr. Zählung [ca. 175 S.]. : Ill., graph. Darst. - (BAM-Dissertationsreihe ; 9) ISBN 3-86509-302-7 T2 - Climatic stability of polymer optical fibers (POF) KW - POF; Reliabilität; Abbau; Chemilumineszenz KW - POF; reliability; degradation; chemiluminescence Y1 - 2004 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-0001661 ER - TY - THES A1 - Gentsch, Rafael T1 - Complex bioactive fiber systems by means of electrospinning T1 - Komplexe Bioaktive Fasersysteme mittels Elektrospinnen N2 - Nanofibrous mats are interesting scaffold materials for biomedical applications like tissue engineering due to their interconnectivity and their size dimension which mimics the native cell environment. Electrospinning provides a simple route to access such fiber meshes. This thesis addresses the structural and functional control of electrospun fiber mats. In the first section, it is shown that fiber meshes with bimodal size distribution could be obtained in a single-step process by electrospinning. A standard single syringe set-up was used to spin concentrated poly(ε-caprolactone) (PCL) and poly(lactic-co-glycolic acid) (PLGA) solutions in chloroform and meshes with bimodal-sized fiber distribution could be directly obtained by reducing the spinning rate at elevated humidity. Scanning electron microscopy (SEM) and mercury porosity of the meshes suggested a suitable pore size distribution for effective cell infiltration. The bimodal fiber meshes together with unimodal fiber meshes were evaluated for cellular infiltration. While the micrometer fibers in the mixed meshes generate an open pore structure, the submicrometer fibers support cell adhesion and facilitate cell bridging on the large pores. This was revealed by initial cell penetration studies, showing superior ingrowth of epithelial cells into the bimodal meshes compared to a mesh composed of unimodal 1.5 μm fibers. The bimodal fiber meshes together with electrospun nano- and microfiber meshes were further used for the inorganic/organic hybrid fabrication of PCL with calcium carbonate or calcium phosphate, two biorelevant minerals. Such composite structures are attractive for the potential improvement of properties such as stiffness or bioactivity. It was possible to encapsulate nano and mixed sized plasma-treated PCL meshes to areas > 1 mm2 with calcium carbonate using three different mineralization methods including the use of poly(acrylic acid). The additive seemed to be useful in stabilizing amorphous calcium carbonate to effectively fill the space between the electrospun fibers resulting in composite structures. Micro-, nano- and mixed sized fiber meshes were successfully coated within hours by fiber directed crystallization of calcium phosphate using a ten-times concentrated simulated body fluid. It was shown that nanofibers accelerated the calcium phosphate crystallization, as compared to microfibers. In addition, crystallizations performed at static conditions led to hydroxyapatite formations whereas in dynamic conditions brushite coexisted. In the second section, nanofiber functionalization strategies are investigated. First, a one-step process was introduced where a peptide-polymer-conjugate (PLLA-b-CGGRGDS) was co-spun with PLGA in such a way that the peptide is enriched on the surface. It was shown that by adding methanol to the chloroform/blend solution, a dramatic increase of the peptide concentration at the fiber surface could be achieved as determined by X-ray photoelectron spectroscopy (XPS). Peptide accessibility was demonstrated via a contact angle comparison of pure PLGA and RGD-functionalized fiber meshes. In addition, the electrostatic attraction between a RGD-functionalized fiber and a silica bead at pH ~ 4 confirmed the accessibility of the peptide. The bioactivity of these RGD-functionalized fiber meshes was demonstrated using blends containing 18 wt% bioconjugate. These meshes promoted adhesion behavior of fibroblast compared to pure PLGA meshes. In a second functionalization approach, a modular strategy was investigated. In a single step, reactive fiber meshes were fabricated and then functionalized with bioactive molecules. While the electrospinning of the pure reactive polymer poly(pentafluorophenyl methacrylate) (PPFPMA) was feasible, the inherent brittleness of PPFPMA required to spin a PCL blend. Blends and pure PPFPMA showed a two-step functionalization kinetics. An initial fast reaction of the pentafluorophenyl esters with aminoethanol as a model substance was followed by a slow conversion upon further hydrophilization. This was analysed by UV/Vis-spectroscopy of the pentaflurorophenol release upon nucleophilic substitution with the amines. The conversion was confirmed by increased hydrophilicity of the resulting meshes. The PCL/PPFPMA fiber meshes were then used for functionalization with more complex molecules such as saccharides. Aminofunctionalized D-Mannose or D-Galactose was reacted with the active pentafluorophenyl esters as followed by UV/Vis spectroscopy and XPS. The functionality was shown to be bioactive using macrophage cell culture. The meshes functionalized with D-Mannose specifically stimulated the cytokine production of macrophages when lipopolysaccharides were added. This was in contrast to D-Galactose- or aminoethanol-functionalized and unfunctionalized PCL/PPFPMA fiber mats. N2 - Biofunktionale Materialien gewinnen immer größere Bedeutung in biomedizinischen Anwendungen wie dem künstlichen Ersatz von Knochen oder Blutgefässe. Weiterhin können diese Stoffe nützlich sein, um die Wechselwirkung zwischen Biomaterialien und biologischen Systemen wie Zellen oder Organismen weiter zu erforschen. In diversen Studien konnten Größen wie dreidimensionaler Strukturaufbau, Oberflächentopographie, Mechanik und die Funktionalisierung mit bioaktiven Substanzen als Einflussfaktoren identifiziert werden, welche auf verschiedenen Größenskalen von makroskopisch bis nanoskopisch untersucht wurden und gegenwärtig erforscht werden. Bioinspiriert von Kollagenfasern, die als Strukturmotiv an verschieden Orten im menschlichen Körper vorkommen (z.B. extrazelluläre Matrix) konnte gezeigt werden, dass Fasermatten, die eine ähnliche Größendimensionen wie die vorher erwähnten Kollagenfasern (Ø ~ 500 nm) aufweisen, eine aussichtsreiche Gerüstmatrix darstellen. Eine einfache Methode Fasermatten in diesen Dimensionen herzustellen ist Elektrospinning, wobei typischerweise eine viskose Polymerlösung durch anlegen eines Hochspannungsfeldes verstreckt wird. Obwohl auf diese Weise hergestellte Fasermatten für gewisse Zelllinien eine ideale Zellwechselwirkung aufweisen, ist die Zellbesiedelung solcher Netzwerke, bedingt auch durch die kleinen Porendurchmesser, problematisch und bedarf meistens weiterer Prozessierungsschritte. Diese Arbeit beschäftigt sich mit der einfachen Herstellung von strukturel und funktional kontrollierten Fasersystem mittels Elektrospinning. Der erste Teil behandelt ein Einschrittverfahren zum Elektrospinnen von bimodalen Fasermatten bestehend aus Nano- und Mikrofasern. In Zellstudien mit Epithelzellen konnte gezeigt werden, dass solche Netzwerke tiefer besiedelt werden als Matten bestehend aus unimodalen 1.5 μm dicken Fasern. Des Weiteren wurden diese Fasermatten für fasergerichtete Kristallisation von Kalziumcarbonat und – phosphat benutzt. In einem zweiten Teil wurden 2 Strategien für die Faserfunktionalisierung mit Peptiden und Zuckermolekülen entwickelt. Zum einen wurde gezeigt, dass funktionale Peptidfasern durch Verspinnung einer Mischung von einem Peptid-Polymer-Konjugat mit einem kommerziellen Polymer hergestellt werden konnten. Zusätzlich wurde ein modularer Ansatz für die Herstellung von reaktiven Fasern ausgearbeitet, die anschließend mit Peptiden oder Zuckern funktionalisiert wurden. Die Bioaktivität der Zucker funktionalisierten Fasern konnte durch Zellversuche erfolgreich bestätigt werden. KW - Elektrospinnen KW - Faser KW - bioaktiv KW - funktional KW - Struktur KW - electrospinning KW - fiber KW - bioactive KW - functional KW - structure Y1 - 2010 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-44900 ER - TY - THES A1 - Rusu, Viorel Marin T1 - Composite materials made of chitosan and nanosized apatite : preparation and physicochemical characterization T1 - - N2 - Taking inspiration from nature, where composite materials made of a polymer matrix and inorganic fillers are often found, e.g. bone, shell of crustaceans, shell of eggs, etc., the feasibility on making composite materials containing chitosan and nanosized hydroxyapatite were investigated. A new preparation approach based on a co-precipitation method has been developed. In its earlier stage of formation, the composite occurs as hydrogel as suspended in aqueous alkaline solution. In order to get solid composites various drying procedures including freeze-drying technique, air-drying at room temperature and at moderate temperatures, between 50oC and 100oC were used. Physicochemical studies showed that the composites exhibit different properties with respect to their structure and composition. IR and Raman spectroscopy probed the presence of both chitosan and hydroxyapatite in the composites. Hydroxyapatite as dispersed in the chitosan matrix was found to be in the nanosize range (15-50 nm) and occurs in a bimodal distribution with respect to its crystallite length. Two types of distribution domains of hydroxyapatite crystallites in the composite matrix such as cluster-like (200-400 nm) and scattered-like domains were identified by the transmission electron microscopy (TEM), X-ray diffraction (XRD) and by confocal scanning laser microscopy (CSLM) measurements. Relaxation NMR experiments on composite hydrogels showed the presence of two types of water sites in their gel networks, such as free and bound water. Mechanical tests showed that the mechanical properties of composites are one order of magnitude less than those of compact bone but comparable to those of porous bone. The enzymatic degradation rates of composites showed slow degradation processes. The yields of degradation were estimated to be less than 10% by loss of mass, after incubation with lysozyme, for a period of 50 days. Since the composite materials were found biocompatible by the in vivo tests, the simple mode of their fabrication and their properties recommend them as potential candidates for the non-load bearing bone substitute materials. N2 - Inspiriert von Natur, bei der Kompositmaterialien aus Polymermatrices und anorganischen Füllstoffen z.B. in Knochen, Krustentieren und Eierschalen vorzufinden sind, wurde die Herstellungsmöglichkeit von Kompositmaterial aus Chitosan und Hydroxyapatitdispersionen untersucht. Basierend auf einem Kopräzipitationsverfahren wurde eine neue Herstellungsmethode entwickelt, die als flexibler Zugang zu einem Spektrum von Komposittypen führt. In den frühen Phasen der Kompositbildung entsteht ein in der wässrigen alkalischen Lösung suspendiertes Hydrogel, das durch Filtration und Zentrifugation isoliert werden kann. IR und Ramanspektroskopie klären das Vorhandensein von Chitosan und Hydroxyapatit im Kompositmaterial. Hydroxyapatit ist als Nanopartikel der Größe von 15-50 nm in bimodaler Verteilung in der Chitosanmatrix dispersiert, und in durch Transmissionselektronenmikroskopie (TEM), X-Ray Diffraction (XRD) und Konfokaler Laserscanmikroskopie (CSLM) nachweisbaren 200-400 nm großen Clustern assembliert. NMR-Relaxationsmessungen an Hydrogelkompositmaterial decken die Existenz zweier Klassen vorkommenden Wassers im Netzwerk auf, gebundenes und freies Wasser. Mechanische Tests zeigen, dass die mechanische Festigkeit etwa eine Größenordnung unter der von massivem Knochen liegt, der Festigkeit von porösem Knochen aber gleichkommt. Enzymatische Abbauraten des Kompostimaterials sind als langsam einzuschätzen. Eine 50-tägige Einwirkzeit von Lysozym führte zu einem Abbau von 10 % der Kompositmasse. Die sich durch in vivo Tests herausstellende Biokompatibilität, die einfachen Herstellungsmöglichkeiten und die physikochemischen Eigenschaften empfehlen dieses Material als vielversprechenden Kandidaten für Knochenersatzmaterial in mäßig belasteten Bereichen. KW - Chitosan KW - Hydroxyapatit KW - Nanopartikel KW - Kompositmaterial KW - Chitosan KW - hydroxyapatite KW - nanoparticles KW - composites Y1 - 2004 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-2316 ER - TY - THES A1 - Kossmann, Janina T1 - Controlled condensation to functional materials – synergetic effect of nitrogen content and pore structure T1 - Kontrollierte Kondensation zu funktionellen Materialien - Synergetische Wirkung von Stickstoffgehalt und Porenstruktur N2 - The development and optimization of carbonaceous materials is of great interest for several applications including gas sorption, electrochemical storage and conversion, or heterogeneous catalysis. In this thesis, the exploration and optimization of nitrogen containing carbonaceous materials by direct condensation of smart chosen, molecular precursors will be presented. As suggested with the concept of noble carbons, the choice of a stable, nitrogen-containing precursor will lead to an even more stable, nitrogen doped carbonaceous material with a controlled structure and electronic properties. Molecules fulfilling this requirement are for example nucleobases. The direct condensation of nucleobases leads to highly nitrogen containing carbonaceous materials without any further post or pretreatment. By using salt melt templating, pore structure adjustment is possible without the use of hazardous or toxic reagents and the template can be reused. Using these simple tools, the synergetic effect of the pore structure and nitrogen content of the materials can be explored. Within this thesis, the influence of the condensation parameters will be correlated to the structure and performance of the materials. First, the influence of the condensation temperature to the porosity and nitrogen content of guanine will be discussed and the exploration of highly CO2 selective structural pores in C1N1 materials will be shown. Further tuning the pore structure of the materials by salt melt templating will be then explored, the potential of the prepared materials as heterogeneous catalysts and their basic catalytic strength will be correlated to their nitrogen content and pore morphology. A similar approach is used to explore the water sorption behavior of uric acid derived carbonaceous materials as potential sorbents for heat transformation applications. Changes in maximum water uptake and hydrophilicity of the prepared materials will be correlated to the nitrogen content and pore architecture. Due to the high thermal stability, porosity, and nitrogen content of ionic liquid derived nitrogen doped carbonaceous materials, a simple impregnation and calcination route can be conducted to obtain copper nano cluster decorated nitrogen-doped carbonaceous materials. The activity as catalyst for the oxygen reduction reaction of the obtained materials will be shown and structure performance relations are discussed. In conclusion, the versatility of nitrogen doped carbonaceous materials with a nitrogen to carbon ratio of up to one will be shown. The possibility to tune the pore structure as well as the nitrogen content by using a simple procedure including salt melt templating as well as the use of molecular precursors and their effect on the performance will be discussed. N2 - Die Entwicklung und Optimierung von kohlenstoffhaltigen Materialien ist von großem Interesse in vielen Anwendungsbereichen, darunter Gassorption, elektrochemische Speicherung und Umwandlung von Energie und in der heterogenen Katalyse. In dieser Arbeit wird die Erforschung und Optimierung von stickstoff‑ und kohlenstoffhaltigen Materialien durch direkte Kondensation ausgewählter, molekularer Ausgangsstoffe vorgestellt. Entsprechend dem Konzept der edlen Kohlenstoffe (noble carbons), führt die Kondensation eines stabilen, stickstoffhaltigen Ausgangsstoffes zu einem noch stabileren, stickstoffdotierten kohlenstoffhaltigen Material mit kontrollierter Struktur und elektronischen Eigenschaften. Moleküle, die diese Anforderung erfüllen, sind zum Beispiel Nukleobasen. Die direkte Kondensation von Nukleobasen führt ohne weitere Nach- oder Vorbehandlungen zu kohlenstoffhaltigen Materialien mit einem sehr hohen Stickstoffanteil. Durch die Verwendung des Salzschmelze-Template Verfahrens ist eine Anpassung der Porenstruktur ohne Verwendung gefährlicher oder toxischer Reagenzien möglich und die Templates können außerdem wiederverwendet werden. Mit diesen einfachen Werkzeugen kann der synergetische Effekt der Porenstruktur und des Stickstoffgehalts der Materialien erforscht werden. Im Rahmen dieser Arbeit wird der Einfluss der Kondensationsparameter auf die Struktur und die Leistung der Materialien in Beziehung gesetzt. Zunächst wird der Einfluss der Kondensationstemperatur auf die Porosität und den Stickstoffgehalt von Guanin erörtert und die Erforschung von CO2-selektiven strukturellen Poren in C1N1-Materialien aufgezeigt. Das Potenzial der hergestellten Materialien als heterogener Katalysator und ihre katalytische Wirkung werden mit ihrem Stickstoffgehalt und ihrer Porenstruktur korreliert. Ein ähnlicher Ansatz wird verwendet, um das Wassersorptionsverhalten von aus Harnsäure hergestellten kohlenstoffhaltigen Materialien als potenzielle Sorptionsmittel für Wärmetransformationsanwendungen zu untersuchen. Die maximale Wasseraufnahme und Hydrophilie der hergestellten Materialien werden mit dem Stickstoffgehalt und der Porenarchitektur korreliert. Aufgrund der hohen thermischen Stabilität, der Porosität und des Stickstoffgehalts der mit ionischer Flüssigkeit hergestellten stickstoffdotierten kohlenstoffhaltigen Materialien können diese des Weiteren als Träger für Metalle dienen. Durch einfache Imprägnierung und Kalzinierung werden Kupfer‑Nanocluster dekorierte stickstoffhaltige Kohlenstoffmaterialen hergestellt und als Katalysator für die in Brennstoffzellen stattfindende Sauerstoff-Reduktionsreaktion genutzt. Zusammenfassend wird die Vielseitigkeit von stickstoffdotierten kohlenstoffhaltigen Materialien mit einem Stickstoff-Kohlenstoff-Verhältnis von bis zu eins aufgezeigt. Es wird die Möglichkeit gezeigt, die Porenstruktur und den Stickstoffgehalt in einem einfachen Verfahren, einschließlich Salzschmelze‑Templating und die Verwendung von molekularen Ausgangsstoffen, zu beeinflussen und somit für gezielte Anwendungen zu variieren. KW - CO2 capture KW - nitrogen containing carbonaceous materials KW - C1N1 KW - heat transformation application KW - oxygen reduction reaction KW - salt melt templating KW - C1N1 KW - CO2-Abscheidung KW - Wärmetransformationsanwendungen KW - Stickstoff‑ und Kohlenstoffhaltige Materialien KW - Sauerstoff-Reduktionsreaktion KW - Salzschmelze-Templating Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-536935 ER - TY - THES A1 - Cheng, Xiao T1 - Controlled solvent vapor annealing of block copolymer films T1 - Kontrolliertes Lösungsmitteldampfglühen von Blockcopolymerfilmen N2 - This project was focused on exploring the phase behavior of poly(styrene)187000-block-poly(2-vinylpyridine)203000 (SV390) with high molecular weight (390 kg/mol) in thin films, in which the self-assembly of block copolymers (BCPs) was realized via thermo-solvent annealing. The advanced processing technique of solvent vapor treatment provides controlled and stable conditions. In Chapter 3, the factors to influence the annealing process and the swelling behavior of homopolymers are presented and discussed. The swelling behavior of BCP in films is controlled by the temperature of the vapor and of the substrate, on one hand, and variation of the saturation of the solvent vapor atmosphere (different solvents), on the other hand. Additional factors like the geometry and material of the chamber, the type of flow inside the chamber etc. also influence the reproducibility and stability of the processing. The slightly selective solvent vapor of chloroform gives 10% more swelling of P2VP than PS in films with thickness of ~40 nm. The tunable morphology in ultrathin films of high molecular weight BCP (SV390) was investigated in Chapter 4. First, the swelling behavior can be precisely tuned by temperature and/or vapor flow separately, which provided information for exploring the multiple-parameter-influenced segmental chain mobility of polymer films. The equilibrium state of SV390 in thin films influenced by temperature was realized at various temperatures with the same degree of swelling. Various methods including characterization with SFM, metallization and RIE were used to identify the morphology of films as porous half-layer with PS dots and P2VP matrix. The kinetic investigations demonstrate that on substrates with either weak or strong interaction the original morphology of the BCP with high molecular weight is changed very fast within 5 min, and the further annealing serves for annihilation of defects. The morphological development of symmetric BCP in films with thickness increasing from half-layer to one-layer influenced by confinement factors of gradient film thicknesses and various surface properties of substrates was studied in Chapter 5. SV390 and SV99 films show bulk lamella-forming morphology after slightly selective solvent vapor (chloroform) treatment. SV99 films show cylinder-forming morphology under strongly selective solvent vapor (toluene) treatment since the asymmetric structure (caused by toluene uptake in PS blocks only) of SV99 block copolymer during annealing. Both kinds of morphology (lamella and cylinder) are influenced by the film thickness. The annealed morphology of SV390 and SV99 influenced by the combination of confined film and substrate property is similar to the morphology on flat silicon wafers. In this chapter the gradients in the film thickness and surface properties of the substrates with regard to their influence on the morphological development in thin BCP films are presented. Directed self-assembly (graphoepitaxy) of this SV390 was also investigated to compare with systematically reported SV99. In Chapter 6 an approach to induced oriented microphase separation in thick block copolymer films via treatment with the oriented vapor flow using mini-extruder is envisaged to be an alternative to existing methodologies, e.g. via non-solvent-induced phase separation. The preliminary tests performed in this study confirm potential perspective of this method, which alters the structure through the bulk of the film (as revealed by SAXS measurements), but more detailed studies have to be conducted in order to optimize the preparation. N2 - Im Rahmen dieser Arbeit wurde das Phasenverhalten von Poly(styrol)_187000 -block-poly(2-Vinylpyridin)_203000 (SV^390 ) hohen Molekulargewichts (390 kg/mol) in dünnen Filmen untersucht, in denen die Selbstassemblierung der Block-Copolymere durch Lösungsmitteltempern erreicht wurde. Das hochentwickelte Verfahren der Behandlung mit Lösungsmitteldampf bietet kontrollierte und stabile Bedingungen. In *Kapitel 3* werden die Faktoren diskutiert, die den Prozess des Temperns und das Schwellverhalten der dünnen Block-Copolymer Filme beeinflussen. Das Schwellverhalten von Block-Copolymeren in Filmen wird einerseits durch die Temperaturen des Lösungsmitteldampfes und des Substrates sowie andererseits dem Sättigungs-Dampfdruck kontrolliert. Zusätzlich beeinflussen auch Faktoren wie die Geometrie und das Material der Kammer sowie die Art der Strömung in der Kammer die Reproduzierbarkeit und Stabilität der Messungen. Der geringfügig selektive Lösungsmitteldampf von Chloroform führt zu 10% stärkerem Schwellen des P2VP-Blocks im Vergleich zu PS in Filmen mit einer Dicke von ca. 40 nm. Die variable Morphologie ultradünner Filme eines Block-Copolymers hohen Molekulargewichts (SV^390 ) wurde in *Kapitel 4* untersucht. Das Schwellverhalten kann durch die Temperatur und den Dampffluss unabhängig voneinander präzise beeinflusst werden. Die Umgebungstemperatur stellt einen limitierenden Faktor für den Bereich der Annealing-Temperatur aufgrund der möglichen Kondensation des Lösungsmitteldampfes dar. Mehrere Methoden, wie zum Beispiel die Charakterisierung mit Rasterkraftmikroskopie, Metallisierung und reaktives Ionenätzen, wurden verwendet, um die Morphologie der Filme als perforierte Lamellen mit PS-Kugeln und P2VP-Matrix zu bestimmen. Eine Analyse der Kinetik der Strukturbildung zeigt, dass sich die ursprüngliche Morphologie von Block-Copolymeren hohen Molekulargewichts sowohl auf Substraten mit schwacher als auch starker Wechselwirkung innerhalb von 5 min ändert und das weitere Tempern zum Ausheilen von Defekten führt. Die morphologische Veränderung von symmetrischen Block-Copolymeren bei Filmdicken zwischen einer halben Domänendicke und einer ganzen Domänendicke wurde in *Kapitel 5* in Abhängigkeit von Gradienten der Filmdicke und verschiedenen Oberflächeneigenschaften der Substrate untersucht. SV^390 und SV^99 Filme zeigen eine lamellare Bulk-Morphologie nach Behandlung mit geringfügig selektivem Lösungsmitteldampf (Chloroform). SV^99 Filme bilden eine zylindrische Morphologie unter Behandlung mit stark selektivem Lösungsmitteldampf (Toluol) aus, weil das SV^99 Block-Copolymer während des Temperns eine asymmetrische Struktur aufweist (Toluol-Aufnahme ausschließlich im Polystyrol-Block). Beide Morphologien (Lamellen und Zylinder) werden durch die Filmdicke beeinflusst. Die Morphologie von SV^390 und SV^99 nach Tempern ist abhängig von der Filmdicke und den Substrat-Eigenschaften und ähnlich der Morphologie auf flachen Silicium-Wafern. In *Kapitel 6* wird ein Ansatz zur induzierten orientierten Mikrophasenseparation in dicken Block-Copolymer Filmen durch Behandlung mit orientiertem Dampffluss unter Verwendung eines Miniextruders vorgestellt, der als Alternative zu existierenden Verfahren wie Nichtlösungsmittel-induzierter Phasenseparation dienen könnte. Die ersten im Rahmen dieser Arbeit durchgeführten Untersuchungen zeigen das Potential der Methode auf, welche die Struktur im gesamten Volumen des Films durchgehend beeinflusst (durch SAXS-Messungen gezeigt). Jedoch sind detailliertere Studien notwendig, um die Prozedur zu optimieren. KW - block copolymer KW - thin films KW - solvo-thermal annealing KW - Block-copolymer KW - dünne Filme KW - Lösungsmittel-thermisches Tempern Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-424179 ER - TY - THES A1 - Bastian, Philipp U. T1 - Core-shell upconversion nanoparticles - investigation of dopant intermixing and surface modification T1 - Kern-Schale Aufkonvertierende Nanopartikel — eine Untersuchung der Dotandenvermischung und Oberflächenmodifikation N2 - Frequency upconversion nanoparticles (UCNPs) are inorganic nanocrystals capable to up-convert incident photons of the near-infrared electromagnetic spectrum (NIR) into higher energy photons. These photons are re-emitted in the range of the visible (Vis) and even ultraviolet (UV) light. The frequency upconversion process (UC) is realized with nanocrystals doped with trivalent lanthanoid ions (Ln(III)). The Ln(III) ions provide the electronic (excited) states forming a ladder-like electronic structure for the Ln(III) electrons in the nanocrystals. The absorption of at least two low energy photons by the nanoparticle and the subsequent energy transfer to one Ln(III) ion leads to the promotion of one Ln(III) electron into higher excited electronic states. One high energy photon will be emitted during the radiative relaxation of the electron in the excited state back into the electronic ground state of the Ln(III) ion. The excited state electron is the result of the previous absorption of at least two low energy photons. The UC process is very interesting in the biological/medical context. Biological samples (like organic tissue, blood, urine, and stool) absorb high-energy photons (UV and blue light) more strongly than low-energy photons (red and NIR light). Thanks to a naturally occurring optical window, NIR light can penetrate deeper than UV light into biological samples. Hence, UCNPs in bio-samples can be excited by NIR light. This possibility opens a pathway for in vitro as well as in vivo applications, like optical imaging by cell labeling or staining of specific organic tissue. Furthermore, early detection and diagnosis of diseases by predictive and diagnostic biomarkers can be realized with bio-recognition elements being labeled to the UCNPs. Additionally, "theranostic" becomes possible, in which the identification and the treatment of a disease are tackled simultaneously. For this to succeed, certain parameters for the UCNPs must be met: high upconversion efficiency, high photoluminescence quantum yield, dispersibility, and dispersion stability in aqueous media, as well as availability of functional groups to introduce fast and easy bio-recognition elements. The UCNPs used in this work were prepared with a solvothermal decomposition synthesis yielding in particles with NaYF4 or NaGdF4 as host lattice. They have been doped with the Ln(III) ions Yb3+ and Er3+, which is only one possible upconversion pair. Their upconversion efficiency and photoluminescence quantum yield were improved by adding a passivating shell to reduce surface quenching. However, the brightness of core-shell UCNPs stays behind the expectations compared to their bulk material (being at least μm-sized particles). The core-shell structures are not clearly separated from each other, which is a topic in literature. Instead, there is a transition layer between the core and the shell structure, which relates to the migration of the dopants within the host lattice during the synthesis. The ion migration has been examined by time-resolved laser spectroscopy and the interlanthanoid resonance energy transfer (LRET) in the two different host lattices from above. The results are presented in two publications, which dealt with core-shell-shell structured nanoparticles. The core is doped with the LRET-acceptor (either Nd3+ or Pr3+). The intermediate shell serves as an insulation shell of pure host lattice material, whose shell thickness has been varied within one set of samples having the same composition, so that the spatial separation of LRET-acceptor and -donor changes. The outer shell with the same host lattice is doped with the LRET-donor (Eu3+). The effect of the increasing insulation shell thickness is significant, although the LRET cannot be suppressed completely. Next to the Ln(III) migration within a host lattice, various phase transfer reactions were investigated in order to subsequently perform surface modifications for bioapplications. One result out of this research has been published using a promising ligand, that equips the UCNP with bio-modifiable groups and has good potential for bio-medical applications. This particular ligand mimics natural occurring mechanisms of mussel protein adhesion and of blood coagulation, which is why the UCNPs are encapsulated very effectively. At the same time, bio-functional groups are introduced. In a proof-of-concept, the encapsulated UCNP has been coupled successfully with a dye (which is representative for a biomarker) and the system’s photoluminescence properties have been investigated. N2 - Frequenzaufkonvertierende Nanopartikel (UCNP) sind anorganische Nanokristalle. Sie können einfallende Photonen des nah-infraroten elektromagnetischen Spektrums (NIR) in höher energetische Photonen im Bereich des sichtbaren Lichtes und sogar des ultravioletten Lichtes (UV) umwandeln und wieder emittieren. Dieser Frequenzaufkonversionsprozess (UC) basiert auf Nanokristallen, die mit dreiwertigen Lanthanoid-Ionen (Ln(III)) dotiert sind. Die elektronisch angeregten Zustände der Ln(III)-Ionen stehen zur Verfügung, mit deren Hilfe Elektronen über eine leiterartige elektronische Struktur der elektronischen Zustände der Ln(III)-Ionen in höher angeregte Zustände gelangen können. Zuvor müssen mindestens zwei niederenergetische Photonen vom Nanopartikel absorbiert werden. Die absorbierte Energie muss über einen oder mehrere Energieübertragungen das gleiche Ln(III)-Ion erreichen um beim strahlenden Relaxieren des Elektrones im angeregten Zustand zurück in den elektronischen Grundzustand des Ln(III)-Ions ein höherenergetisches Photon zu emittieren. Der Frequenzaufkonversionsprozess ist sehr interessant für die Anwendung im biologisch/medizinischen Bereich. Biologische Proben (z.B. organisches Gewebe, Blut, Urin und Stuhl) absorbieren höherenergetische Photonen (UV) stärker als niederenergetische Photonen (NIR). Dank eines natürlich vorkommenden optischen Fensters in biologischen Proben kann NIR-Licht tiefer als UV-Licht eindringen, sodass die UCNPs in biologischen Proben mit NIR-Licht angeregt werden können. Dies ermöglicht in vitro als auch in vivo Anwendungen, z.B. für die optische Bildgebung durch Markieren von Zellen oder durch Einfärben von bestimmten Bereichen organischer Gewebe. Frühzeitige Erkennung von Krankheiten kann durch prädiktive und diagnostisch geeignete Biomarker, die mit Erkennungselementen an den UCNPs detektiert werden, realisiert werden. Demnach ist „Theranostic“ ein mögliches Szenario, das die Identifikation und die gleichzeitige Behandlung einer Krankheit ermöglichen könnte. Um diese Vision zu realisieren, müssen die UCNPs bestimmte Parameter erfüllen: Eine hohe Aufkonversionseffizienz, eine hohe Photolumineszenzquantenausbeute, eine gute Dispergierbarkeit und Stabilität der Dispersion in wässrigen Medien, sowie die Verfügbarkeit von funktionellen Gruppen, um schnell und einfach biologische Erkennungselemente daran zu koppeln. Die UCNPs dieser Arbeit wurden mit Hilfe einer solvothermalen Zersetzungsreaktion durchgeführt. Die Nanopartikel bestanden aus unterschiedlichen Wirtsgittern, entweder aus NaYF4 oder NaGdF4. Die Wirtsgitter wurden mit den Ln(III)-Ionen Yb3+ und Er3+ dotiert. Die Aufkonversionseffizienz, somit auch deren Quantenausbeute, konnte mit einer passivierenden Schale verbessert werden. Dennoch leuchten die Kern-Schale-UCNPs schlechter als es im Vergleich mit μm-großen Partikeln zu erwarten wäre. Die Kern-Schale-Strukturen gehen ineinander über und sind nicht klar voneinander getrennt. Zwischen dem Kern und der Schale existiert eine Übergangsregion, die mit der Wanderung der Ionen des Wirtsgitters und den dotierten Ln(III)-Ionen einhergeht. Diese Beobachtung wird auch in der Literatur diskutiert. Die Ionenwanderung wurde mit Hilfe von zeitaufgelöster Laserspektroskopie und dem Interlanthanoidenergietransfer (LRET) in den beiden erwähnten Wirtsgittern untersucht. Die Ergebnisse sind in zwei Publikationen veröffentlicht, die auf Kern-Schale-Schale-Strukturen basieren. Der Kern ist mit dem LRET-Akzeptor dotiert (Nd3+ oder Pr3+). Die Zwischenschale besteht aus dem gleichen Wirtsgitter ohne Dotierstoffe und dient als Isolationsschale, deren Schalendicke innerhalb einer Experimentierreihe variiert wurde, um eine räumliche Trennung von LRET-Akzeptor und -Donor zu schaffen. Die äußere Schale, aus dem gleichen Wirtsgitter, ist mit dem LRET-donor (Eu3+) dotiert. Der Effekt der wachsenden Isolationsschalendicke ist signifikant. Aber es ist nicht möglich gewesen, den Energietransfer vom Donor auf den Akzeptor komplett zu unterbinden. Neben der Untersuchung der Wanderung von Ln(III)-Ionen in einem Wirtsgitter wurden verschiedene Phasentransferreaktionen durchgeführt, um anschließende Oberflächenmodifikationen anzuwenden, damit die Anwendungen der UCNPs im biologischen Kontext prinzipiell demonstriert werden kann. Ein Ergebnis mit einem sehr vielversprechenden Liganden für die bio-medizinische Anwendung wurde in einer Publikation veröffentlicht. Dieser Ligand imitiert natürliche Mechanismen von Muschelproteinen und von Blutkoagulation, sodass die untersuchten Nanopartikel sehr effektiv eingekapselt werden. Gleichzeitig sind funktionelle Gruppen zur Bio-Funktionalisierung vorhanden. In einer Machbarkeitsstudie wurde der eingekapselte UCNP erfolgreich mit einem Farbstoff (der durch einen Biomarker ersetzt werden kann) gekoppelt und die Photolumineszenzeigenschaften des Systems untersucht. KW - upconversion KW - Aufkonversion KW - Nanopartikel KW - nanoparticle KW - bio-modification KW - Biomodification KW - Ionenmigration KW - ion migration KW - surface modification KW - Oberflächenmodifizierung Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-551607 ER - TY - THES A1 - Eren, Enis Oğuzhan T1 - Covalent anode materials for high-energy sodium-ion batteries T1 - Kovalente Anodenmaterialien für hoch-energetische Natrium-Ionen-Batterien N2 - The reliance on fossil fuels has resulted in an abnormal increase in the concentration of greenhouse gases, contributing to the global climate crisis. In response, a rapid transition to renewable energy sources has begun, particularly lithium-ion batteries, playing a crucial role in the green energy transformation. However, concerns regarding the availability and geopolitical implications of lithium have prompted the exploration of alternative rechargeable battery systems, such as sodium-ion batteries. Sodium is significantly abundant and more homogeneously distributed in the crust and seawater, making it easier and less expensive to extract than lithium. However, because of the mysterious nature of its components, sodium-ion batteries are not yet sufficiently advanced to take the place of lithium-ion batteries. Specifically, sodium exhibits a more metallic character and a larger ionic radius, resulting in a different ion storage mechanism utilized in lithium-ion batteries. Innovations in synthetic methods, post-treatments, and interface engineering clearly demonstrate the significance of developing high-performance carbonaceous anode materials for sodium-ion batteries. The objective of this dissertation is to present a systematic approach for fabricating efficient, high-performance, and sustainable carbonaceous anode materials for sodium-ion batteries. This will involve a comprehensive investigation of different chemical environments and post-modification techniques as well. This dissertation focuses on three main objectives. Firstly, it explores the significance of post-synthetic methods in designing interfaces. A conformal carbon nitride coating is deposited through chemical vapor deposition on a carbon electrode as an artificial solid-electrolyte interface layer, resulting in improved electrochemical performance. The interaction between the carbon nitride artificial interface and the carbon electrode enhances initial Coulombic efficiency, rate performance, and total capacity. Secondly, a novel process for preparing sulfur-rich carbon as a high-performing anode material for sodium-ion batteries is presented. The method involves using an oligo-3,4-ethylenedioxythiophene precursor for high sulfur content hard carbon anode to investigate the sulfur heteroatom effect on the electrochemical sodium storage mechanism. By optimizing the condensation temperature, a significant transformation in the materials’ nanostructure is achieved, leading to improved electrochemical performance. The use of in-operando small-angle X-ray scattering provides valuable insights into the interaction between micropores and sodium ions during the electrochemical processes. Lastly, the development of high-capacity hard carbon, derived from 5-hydroxymethyl furfural, is examined. This carbon material exhibits exceptional performance at both low and high current densities. Extensive electrochemical and physicochemical characterizations shed light on the sodium storage mechanism concerning the chemical environment, establishing the material’s stability and potential applications in sodium-ion batteries. N2 - Die Abhängigkeit von fossilen Brennstoffen hat zu einem abnormalen Anstieg von Treibhausgasen in der Atmosphäre geführt, was zur globalen Klimakrise beiträgt. Als Reaktion darauf hat eine rasche Umstellung auf erneuerbare Energiequellen begonnen, insbesondere Lithium-Ionen-Batterien, die eine entscheidende Rolle in der grünen Energiewende spielen. Bedenken hinsichtlich der Verfügbarkeit und geopolitischen Implikationen von Lithium haben jedoch die Erforschung alternativer wiederaufladbarer Batteriesysteme wie Natrium-Ionen-Batterien angeregt. Natrium ist in der Erdkruste und im Meerwasser deutlich häufiger und gleichmäßiger verteilt, was seine Extraktion im Vergleich zu Lithium einfacher und kostengünstiger macht. Aufgrund der geheimnisvollen Natur ihrer Komponenten sind Natrium-Ionen-Batterien derzeit noch nicht ausreichend fortgeschritten, um Lithium-Ionen-Batterien zu ersetzen. Insbesondere weist Natrium einen stärker metallischen Charakter und einen größeren Ionenradius auf, was zu einem anderen Ionen-Speichermechanismus führt, der in Lithium-Ionen-Batterien verwendet wird. Innovationen in synthetischen, post-synthetischen Methoden und Schnittstellentechnik zeigen deutlich die Bedeutung der Entwicklung hochleistungsfähiger kohlenstoffhaltiger Anodenmaterialien für Natrium-Ionen-Batterien auf. Das Ziel dieser Dissertation ist es, einen systematischen Ansatz zur Herstellung effizienter, leistungsstarker und nachhaltiger kohlenstoffhaltiger Anodenmaterialien für Natrium-Ionen-Batterien zu untersuchen. Diese Dissertation konzentriert sich auf drei Hauptziele. Erstens untersucht sie die Bedeutung von post-synthetischen Methoden bei der Gestaltung von Schnittstellen. Eine konforme Kohlenstoffnitrid-Beschichtung wird durch chemische Gasphasenabscheidung auf einer Kohlenstoffelektrode als künstliche Festelektrolytschnittstelle abgeschieden, was zu einer verbesserten elektrochemischen Leistung führt. Die Wechselwirkung zwischen der künstlichen Kohlenstoffnitrid-Schnittstelle und der Kohlenstoffelektrode trägt zu einer verbesserten anfänglichen kolumbischen Effizienz, Leistung bei hohen Raten und Gesamtkapazität bei. Zweitens wird ein neuartiger Prozess zur Herstellung von schwefelreichem Kohlenstoff als hochleistungsfähiges Anodenmaterial für Natrium-Ionen-Batterien vorgestellt. Die Methode verwendet einen Oligo-3,4-ethylendioxythiophen-Vorläufer für eine harte Kohlenstoffanode mit hohem Schwefelgehalt, um den Effekt des Schwefelheteroatoms auf den elektrochemischen Natriumspeichermechanismus zu untersuchen. Durch Optimierung der Kondensationstemperatur wird eine bedeutende Transformation in der Nanostruktur des Materials erreicht, was zu einer verbesserten elektrochemischen Leistung führt. Der Einsatz von in-operando-Röntgenkleinwinkelstreuung liefert wertvolle Erkenntnisse über die Wechselwirkung zwischen Mikroporen und Natriumionen während der elektrochemischen Prozesse. Letzendlich wird die Entwicklung einer hochkapazitiven harten Kohlenstoffanode, die aus 5-Hydroxymethylfurfural gewonnen wird, untersucht. Dieses Kohlenstoffmaterial zeigt eine außergewöhnliche Leistung sowohl bei niedrigen als auch bei hohen Stromdichten. KW - sodium-ion battery KW - sulfur KW - carbon KW - CN KW - anode KW - in-operando SAXS KW - Kohlenstoffnitrid (CN) KW - Anode KW - Kohlenstoff KW - in-operando SAXS KW - Natrium-Ionen-Batterie KW - Schwefel Y1 - 2024 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-622585 ER - TY - THES A1 - Montenegro, Rivelino V. D. T1 - Crystallization, biomimetics and semiconducting polymers in confined systems T1 - Kristallisation, Biomimetik und halbleitende Polymere in räumlich begrenzten Systemen N2 - populärwissenschaftlicher Abstract: Kristallisation, Biomimetik und halbleitende Polymere in räumlich begrenzten Systemen: Öl und Wasser mischen sich nicht, man kann aber aus beiden Flüssigkeiten Emulsionen herstellen, bei denen Tröpfchen der einen Flüssigkeit in der anderen Flüssigkeit vorliegen. Das heißt, es können entweder Öltröpfchen in Wasser oder Wassertröpfchen in Öl erzeugt werden. Aus täglichen Erfahrungen, z.B. beim Kochen weiß man jedoch, dass sich eine Emulsion durch Schütteln oder Rühren herstellen lässt, diese jedoch nicht besonders stabil ist. Mit Hilfe von hohen Scherenergien kann man nun sehr kleine, in ihrer Größe sehr einheitliche und außerdem sehr stabile Tröpfchen von 1/10000 mm erhalten. Eine solche Emulsion wird Miniemulsion genannt. In der Dissertation wurden nun z.B. Miniemulsionen untersucht, die aus kleinen Wassertröpfchen in einem Öl bestehen. Es konnte gezeigt werden, dass das Wasser in diesen Tröpfchen, also in den räumlich begrenzten Systemen, nicht bei 0 °C, sondern bei -22 °C kristallisierte. Wie lässt sich das erklären? Wenn man einen Eimer Wasser hat, dann bildet sich normalerweise bei 0 °C Eis, da nämlich in dem Wasser einige (manchmal ganz wenige) Keime (z.B. Schutzteilchen, ein Fussel etc.) vorhanden sind, an denen sich die ersten Kristalle bilden. Wenn sich dann einmal ein Kristall gebildet hat, kann das Wasser im gesamten Eimer schnell zu Eis werden. Ultrareines Wasser würde bei -22 °C kristallisieren. Wenn man jetzt die Menge Wasser aus dem Eimer in kleine Tröpfchen bringt, dann hat man eine sehr, sehr große Zahl, nämlich 1017 Tröpfchen, in einem Liter Emulsion vorliegen. Die wenigen Schmutzpartikel verteilen auf sehr wenige Tröpfchen, die anderen Tröpfchen sind ultrarein. Daher kristallisieren sie erst bei -22 °C. Im Rahmen der Arbeit konnte auch gezeigt werden, dass die Miniemulsionen genutzt werden können, um kleine Gelatine-Partikel, also Nanogummibärchen, herzustellen. Diese Nanogummibärchen quellen bei Erhöhung der Temperatur auf ca. 38 °C an. Das kann ausgenutzt werden, um zum Beispiel Medikamente zunächst in den Partikeln im menschlichen Körper zu transportieren, die Medikamente werden dann an einer gewünschten Stelle freigelassen. In der Arbeit wurde auch gezeigt, dass die Gelatine-Partikel genutzt werden können, um die Natur nachzuahnen (Biomimetik). Innerhalb der Partikel kann nämlich gezielt Knochenmaterial aufgebaut werden kann. Die Gelatine-Knochen-Partikel können dazu genutzt werden, um schwer heilende oder komplizierte Knochenbrüche zu beheben. Gelatine wird nämlich nach einigen Tagen abgebaut, das Knochenmaterial kann in den Knochen eingebaut werden. LEDs werden heute bereits vielfältig verwendet. LEDs bestehen aus Halbleitern, wie z.B. Silizium. Neuerdings werden dazu auch halbleitende Polymere eingesetzt. Das große Problem bei diesen Materialien ist, dass sie aus Lösungsmitteln aufgebracht werden. Im Rahmen der Doktorarbeit wurde gezeigt, dass der Prozess der Miniemulsionen genutzt werden kann, um umweltfreundlich diese LEDs herzustellen. Man stellt dazu nun wässrige Dispersionen mit den Polymerpartikeln her. Damit hat man nicht nur das Lösungsmittel vermieden, das hat nun noch einen weiteren Vorteil: man kann nämlich diese Dispersion auf sehr einfache Art verdrucken, im einfachsten Fall verwendet man einfach einen handelsüblichen Tintenstrahldrucker. N2 - The colloidal systems are present everywhere in many varieties such as emulsions (liquid droplets dispersed in liquid), aerosols (liquid dispersed in gas), foam (gas in liquid), etc. Among several new methods for the preparation of colloids, the so-called miniemulsion technique has been shown to be one of the most promising. Miniemulsions are defined as stable emulsions consisting of droplets with a size of 50-500 nm by shearing a system containing oil, water, a surfactant, and a highly water insoluble compound, the so-called hydrophobe 1. In the first part of this work, dynamic crystallization and melting experiments are described which were performed in small, stable and narrowly distributed nanodroplets (confined systems) of miniemulsions. Both regular and inverse systems were examined, characterizing, first, the crystallization of hexadecane, secondly, the crystallization of ice. It was shown for both cases that the temperature of crystallization in such droplets is significantly decreased (or the required undercooling is increased) as compared to the bulk material. This was attributed to a very effective suppression of heterogeneous nucleation. It was also found that the required undercooling depends on the nanodroplet size: with decreasing droplet size the undercooling increases. 2. It is shown that the temperature of crystallization of other n-alkanes in nanodroplets is also significantly decreased as compared to the bulk material due to a very effective suppression of heterogeneous nucleation. A very different behavior was detected between odd and even alkanes. In even alkanes, the confinement in small droplets changes the crystal structure from a triclinic (as seen in bulk) to an orthorhombic structure, which is attributed to finite size effects inside the droplets. An intermediate metastable rotator phase is of less relevance for the miniemulsion droplets than in the bulk. For odd alkanes, only a strong temperature shift compared to the bulk system is observed, but no structure change. A triclinic structure is formed both in bulk and in miniemulsion droplets. 3. In the next part of the thesis it is shown how miniemulsions could be successfully applied in the development of materials with potential application in pharmaceutical and medical fields. The production of cross-linked gelatin nanoparticles is feasible. Starting from an inverse miniemulsion, the softness of the particles can be controlled by varying the initial concentration, amount of cross-link agent, time of cross-linking, among other parameters. Such particles show a thermo-reversible effect, e.g. the particles swell in water above 37 °C and shrink below this temperature. Above 37 °C the chains loose the physical cross-linking, however the particles do not loose their integrity, because of the chemical cross-linking. Those particles have potential use as drug carriers, since gelatin is a natural polymer derived from collagen. 4. The cross-linked gelatin nanoparticles have been used for the biomineralization of hydroxyapatite (HAP), a biomineral, which is the major constituent of our bones. The biomineralization of HAP crystals within the gelatin nanoparticles results in a hybrid material, which has potential use as a bone repair material. 5. In the last part of this work we have shown that layers of conjugated semiconducting polymers can be deposited from aqueous dispersion prepared by the miniemulsion process. Dispersions of particles of different conjugated semiconducting polymers such as a ladder-type poly(para-phenylene) and several soluble derivatives of polyfluorene could be prepared with well-controlled particle sizes ranging between 70 - 250 nm. Layers of polymer blends were prepared with controlled lateral dimensions of phase separation on sub-micrometer scales, utilizing either a mixture of single component nanoparticles or nanoparticles containing two polymers. From the results of energy transfer it is demonstrated that blending two polymers in the same particle leads to a higher efficiency due to the better contact between the polymers. Such an effect is of great interest for the fabrication of opto-electronic devices such as light emitting diodes with nanometer size emitting points and solar cells comprising of blends of electron donating and electron accepting polymers. KW - Confinement KW - miniemulsion KW - crystallization KW - biomimetics and semiconducting polymers Y1 - 2003 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-0000726 ER - TY - THES A1 - Eisold, Ursula T1 - Cumarin- und DBD-Farbstoffe als Fluoreszenzsonden T1 - Coumarin and dbd dyes as fluorescent probes BT - Fluoreszenzimmunassays und Förster-Resonanz-Energietransfer BT - fluorescence immunoassays and Foerster resonance energy transfer N2 - In dieser Arbeit werden drei Themen im Zusammenhang mit den spektroskopischen Eigenschaften von Cumarin- (Cou) und DBD-Farbstoffen ([1,3]Dioxolo[4,5-f][1,3]benzodioxol) behandelt. Der erste Teil zeigt die grundlegende spektroskopische Charakterisierung von 7-Aminocumarinen und ihre potentielle Anwendung als Fluoreszenzsonde für Fluoreszenzimmunassays. Im zweiten Teil werden mit die photophysikalischen Eigenschaften der Cumarine genutzt um Cou- und DBD-funktionalisierte Oligo-Spiro-Ketal-Stäbe (OSTK) und ihre Eigenschaften als Membransonden zu untersuchen. Der letzte Teil beschäftigt sich mit der Synthese und der Charakterisierung von Cou- und DBD-funktionalisierten Polyprolinen als Referenzsysteme für schwefelfunktionalisierte OSTK-Stäbe und ihrer Kopplung an Goldnanopartikel. Immunochemische Analysemethoden sind in der klinischen Diagnostik sehr erfolgreich und werden heute auch für die Nahrungsmittelkontrolle und Überwachung von Umweltfragen mit einbezogen. Dadurch sind sie von großem Interesse für weitere Forschungen. Unter den verschiedenen Immunassays zeichnen sich lumineszenzbasierte Formate durch ihre herausragende Sensitivität aus, die dieses Format für zukünftige Anwendungen besonders attraktiv macht. Die Notwendigkeit von Multiparameterdetektionsmöglichkeiten erfordert einen Werkzeugkasten mit Farbstoffen, um die biochemische Reaktion in ein optisch detektierbares Signal umzuwandeln. Hier wird bei einem Multiparameteransatz jeder Analyt durch einen anderen Farbstoff mit einer einzigartigen Emissionsfarbe, die den blauen bis roten Spektralbereich abdecken, oder eine einzigartige Abklingzeit detektiert. Im Falle eines kompetitiven Immunassayformats wäre für jeden der verschiedenen Farbstoffe ein einzelner Antikörper erforderlich. In der vorliegenden Arbeit wird ein leicht modifizierter Ansatz unter Verwendung einer Cumarineinheit, gegen die hochspezifische monoklonale Antikörper (mAb) erzeugt wurden, als grundlegendes Antigen präsentiert. Durch eine Modifikation der Stammcumarineinheit an einer Position des Moleküls, die für die Erkennung durch den Antikörper nicht relevant ist, kann auf den vollen Spektralbereich von blau bis tiefrot zugegriffen werden. In dieser Arbeit wird die photophysikalische Charakterisierung der verschiedenen Cumarinderivate und ihrer entsprechenden Immunkomplexe mit zwei verschiedenen, aber dennoch hochspezifischen, Antikörpern präsentiert. Die Cumarinfarbstoffe und ihre Immunkomplexe wurden durch stationäre und zeitaufgelöste Absorptions- sowie Fluoreszenzemissionsspektroskopie charakterisiert. Darüber hinaus wurden Fluoreszenzdepolarisationsmessungen durchgeführt, um die Daten zu vervollständigen, die die verschiedenen Bindungsmodi der beiden Antikörper betonten. Im Gegensatz zu häufig eingesetzten Nachweissystemen wurde eine massive Fluoreszenzverstärkung bei der Bildung des Antikörper-Farbstoffkomplexes bis zu einem Faktor von 50 gefunden. Wegen der leichten Emissionsfarbenänderung durch das Anpassen der Cumarinsubstitution in der für die Antigenbindung nicht relevanten Position des Elternmoleküls, ist eine Farbstoff-Toolbox vorhanden, die bei der Konstruktion von kompetitiven Multiparameterfluoreszenzverstärkungsimmunassays verwendet werden kann. Oligo-Spiro-Thio-Ketal-Stäbe werden aufgrund ihres hydrophoben Rückgrats leicht in Doppellipidschichten eingebaut und deshalb als optische Membransonde verwendet. Wegen ihres geringen Durchmessers wird nur eine minimale Störung der Doppellipidschicht verursacht. Durch die Markierung mit Fluoreszenzfarbstoffen sind neuartige Förster-Resonanz-Energietransfersonden mit hoch definierten relativen Orientierungen der Übergangsdipolmomente der Donor- und Akzeptorfarbstoffe zugänglich und macht die Klasse der OSTK-Sonden zu einem leistungsstarken, flexiblen Werkzeugkasten für optische Biosensoranwendungen. Mit Hilfe von stationären und zeitaufgelösten Fluoreszenzexperimenten wurde der Einbau von Cumarin- und DBD markierten OSTK-Stäben in großen unilamellaren Vesikeln untersucht und die Ergebnisse durch Fluoreszenzdepolarisationsmessungen untermauert. Der letzte Teil dieser Arbeit beschäftigt sich mit der Synthese und Charakterisierung von Cou- und DBD-funktionalisierten Polyprolinen und ihrer Kopplung an Goldnanopartikel. Die farbstoffmarkierten Polyproline konnten erfolgreich hergestellt werden. Es zeigten sich deutlich Einflüsse auf die spektroskopischen Eigenschaften der Farbstoffe durch die Bindung an die Polyprolinhelix. Die Kopplung an die 5 nm großen AuNP konnte erfolgreich durchgeführt werden. Die Erfahrungen, die durch die Kopplung der Polyproline an die AuNP, gewonnen wurde, ist die Basis für eine Einzelmolekül-AFM-FRET-Nanoskopie mit OSTK-Stäben. N2 - In this thesis, three topics are discussed in connection with the spectroscopic properties of coumarin (Cou) and DBD ([1,3]dioxolo[4,5-f][1,3]benzodioxole) dyes. The first part shows the basic spectroscopic characterization of 7-aminocumarins and their advantage as a fluorescence probe for fluorescence immunoassays. In the second part, the photophysical properties of the coumarins are used to investigate Cou- and DBD-functionalized oligo-spiro-ketal rods (OSTK) and their properties as membrane probes. The last part deals with the synthesis and characterization of Cou- and DBD-functionalized polyprolines as reference systems for sulfur-functionalized OSTK rods and their coupling to gold nanoparticles. The fact that immunochemical analysis methods are very successful in clinical diagnostics and are now also included for food control and monitoring of environmental questions they are of great interest for further research. Among the various immunoassays, luminescence-based formats are distinguished by their outstanding sensitivity, which makes this format particularly attractive for future applications. The need for multiparameter detection capabilities requires a toolbox of dyes to convert the biochemical response to an optically detectable signal. Here, in the case of a multiparameter approach, each analyte is detected by another dye with a unique emission color which covers the blue to red spectral range or a unique decay time. In the case of a competitive immunoassay format, a single antibody would be required for each of the different dyes. In the present work, a slightly modified approach is presented as a basic antigen using a coumarin moiety against which highly specific antibodies have been produced. By modifying the parent coumarin moiety at a site of the molecule which is not relevant for recognition by the antibody, the full spectral range from blue to deep red can be accessed. This work presents the photophysical characterization of the different cumarine derivatives and their corresponding immuno complexes with two different but nevertheless highly specific monoclonal antibodies (mAb). The coumarin dyes and their immunocomplexes were characterized by steady-state time-resolved absorption and fluorescence emission spectroscopy. In addition, fluorescence depolarization measurements were performed to complete the data emphasizing the different binding modes of the two antibodies. In contrast to frequently used detection systems, a massive fluorescence enhancement was found in the formation of the antibody dye complex up to a factor of 50. Because of the slight change in the emission by adjusting the coumarin substitution in the position of the parent molecule which is not relevant for the antigen binding, a dye toolbox which can be used for the construction of competitive multiparameter fluorescence enhancement immunoassays has been created. Due to their hydrophobic backbone, oligospirothioketal rods (OSTK) are easily incorporated into lipid bilayers and are therefore used as an optical membrane probe. Because of their narrow diameter, only a minimal disturbance of the lipid bilayer is caused. By labeling with fluorescent dyes, novel Förster resonance energy transfer probes are available with highly defined relative orientations of the transition dipole moments of the donor and acceptor dyes, making the class of the OSTK probes into a powerful, flexible toolbox for optical biosensor applications. The incorporation of cumarin and [1,3]-dioxolo[4,5-f][1,3]benzodioxol-labeled OSTK rods in large unilamellar vesicles was investigated using steady-state and time-resolved fluorescence experiments and the results were confirmed by fluorescence depolarization measurements. The last part of this work deals with the synthesis and characterization of Cou- and DBD-functionalized polyprolines and their coupling to gold nanoparticles. The dye-labeled polyprolines were successfully synthesized. Influences on the spectroscopic properties of the dyes by binding to the polyproline helix were found. The coupling to 5 nm AuNP was successfully carried out. The experience gained by the coupling of the polyprolins to the AuNP can be used as a good basis for the investigation of a single molecule FRET AFM nanoscopy using OSTK rods. KW - FRET KW - Förster-Resonanz-Energie-Transfer KW - Förster resonance energy transfer KW - Origo-Spiro-Thio-Ketal-Stäbe KW - oligo spiro thio ketal rods KW - FRET Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-405833 ER - TY - THES A1 - Jordan, Thomas T1 - CxNy-materials from supramolecular precursors for “All-Carbon” composite materials T1 - CxNy-Materialien aus supramolekularen Precursoren für „All-Carbon“-Komposit-Materialien N2 - Among modern functional materials, the class of nitrogen-containing carbons combines non-toxicity and sustainability with outstanding properties. The versatility of this materials class is based on the opportunity to tune electronic and catalytic properties via the nitrogen content and –motifs: This ranges from the electronically conducting N-doped carbon, where few carbon atoms in the graphitic lattice are substituted by nitrogen, to the organic semiconductor graphitic carbon nitride (g-C₃N₄), with a structure based on tri-s-triazine units. In general, composites can reveal outstanding catalytic properties due to synergistic behavior, e.g. the formation of electronic heterojunctions. In this thesis, the formation of an “all-carbon” heterojunction was targeted, i.e. differences in the electronic properties of the single components were achieved by the introduction of different nitrogen motives into the carbon lattice. Such composites are promising as metal-free catalysts for the photocatalytic water splitting. Here, hydrogen can be generated from water by light irradiation with the use of a photocatalyst. As first part of the heterojunction, the organic semiconductor g-C₃N₄ was employed, because of its suitable band structure for photocatalytic water splitting, high stability and non-toxicity. The second part was chosen as C₂N, a recently discovered semiconductor. Compared to g-C₃N₄, the less nitrogen containing C₂N has a smaller band gap and a higher absorption coefficient in the visible light range, which is expected to increase the optical absorption in the composite eventually leading to an enhanced charge carrier separation due to the formation of an electronic heterojunction. The aim of preparing an “all-carbon” composite included the research on appropriate precursors for the respective components g-C₃N₄ and C₂N, as well as strategies for appropriate structuring. This was targeted by applying precursors which can form supramolecular pre-organized structures. This allows for more control over morphology and atom patterns during the carbonization process. In the first part of this thesis, it was demonstrated how the photocatalytic activity of g-C₃N₄ can be increased by the targeted introduction of defects or surface terminations. This was achieved by using caffeine as a “growth stopping” additive during the formation of the hydrogen-bonded supramolecular precursor complexes. The increased photocatalytic activity of the obtained materials was demonstrated with dye degradation experiments. The second part of this thesis was focused on the synthesis of the second component C₂N. Here, a deep eutectic mixture from hexaketocyclohexane and urea was structured using the biopolymer chitosan. This scaffolding resulted in mesoporous nitrogen-doped carbon monoliths and beads. CO₂- and dye-adsorption experiments with the obtained monolith material revealed a high isosteric heat of CO₂-adsorption and showed the accessibility of the monolithic pore system to larger dye molecules. Furthermore, a novel precursor system for C₂N was explored, based on organic crystals from squaric acid and urea. The respective C₂N carbon with an unusual sheet-like morphology could be synthesized by carbonization of the crystals at 550 °C. With this precursor system, also microporous C₂N carbon with a BET surface area of 865 m²/g was obtained by “salt-templating” with ZnCl₂. Finally, the preparation of a g-C₃N₄/C₂N “all carbon” composite heterojunction was attempted by the self-assembly of g-C₃N₄ and C₂N nanosheets and tested for photocatalytic water splitting. Indeed, the composites revealed high rates of hydrogen evolution when compared to bulk g-C₃N₄. However, the increased catalytic activity was mainly attributed to the high surface area of the nanocomposites rather than to the composition. With regard to alternative composite synthesis ways, first experiments indicated N-Methyl-2-pyrrolidon to be suitable for higher concentrated dispersion of C₂N nanosheets. Eventually, the results obtained in this thesis provide precious synthetic contributions towards the preparation and processing of carbon/nitrogen compounds for energy applications. N2 - Eine interessante Materialklasse für technologische Anwendungen sind Kohlenstoff/Stickstoff-Materialien, die sich durch Ungiftigkeit und Umweltfreundlichkeit bei gleichzeitig interessanten katalytischen Eigenschaften auszeichnen. Die Vielseitigkeit dieser Materialkasse basiert auf der Möglichkeit ihre katalytischen und elektronischen Eigenschaften über Stickstoff-Anteil und –Funktionalitäten zu beeinflussen. Die vorliegende Arbeit fokussierte sich auf Komposite zwischen verschiedenen Kohlenstoff/Stickstoff-Derivaten, für welche aufgrund ihrer unterschiedlichen elektronischen Eigenschaften die Bildung elektronischer Heteroübergänge erwartet werden kann. Solche Komposite sind vielversprechende Materialien für die Erzeugung von Wasserstoff durch die photokatalytische Spaltung von Wasser. Für die eine Komponente des Komposits wurde das graphitische Kohlenstoffnitrid g-C₃N₄ eingesetzt, welches durch seine elektronische Struktur und Stabilität ein geeignetes Material für die photokatalytische Wasserspaltung ist. Für die andere Komponente des Komposits wurde eine erst kürzlich erstmalig beschriebene Kohlenstoff/Stickstoff Verbindung eingesetzt, das Kohlenstoffnitrid C₂N. Für dieses Komposit ist eine im Vergleich zu den einzelnen Komponenten stark erhöhte photokatalytische Aktivität zu erwarten. Neben dem Ziel der Herstellung eines solchen Komposits, fokussierte sich diese Arbeit auch darauf, neue Wege zur Synthese und Strukturierung der einzelnen Komponenten zu entwickeln. Dies sollte über supramolekulare Präkursor-Komplexe erfolgen, mit welchen eine erhöhte Einflussnahme auf Karbonisierungsprozesse erlangt werden kann. Im ersten Teil der Arbeit, welcher auf das graphitische Kohlenstoffnitrid g-C₃N₄ fokussiert war, wurde gezeigt wie die photokatalytische Aktivität dieser Komponente durch den gezielten Einbau von Defekten erhöht werden kann. Dies wurde über einen durch Koffein modifizierten supramolekularen Komplex als Präkursor erreicht. Die erhöhte photokatalytische Aktivität wurde über Farbstoff-Zersetzung nachgewiesen. Der zweite Teil der Arbeit war auf die Herstellung und Strukturierung der neuartigen Verbindung C₂N fokussiert. Hier wurde gezeigt, wie eine eutektische Mischung zwischen Hexaketocyclohexan und Harnstoff als C₂N-Präkursor mit dem Polysaccharid Chitosan strukturiert werden kann. Hierbei wurden poröse Stickstoffhaltige Kohlenstoff-Monolithen und -Perlen erhalten, die eine hohe Adsorptionswärme für die CO₂-Adsorption zeigten. Weiterhin wurde ein neuartiger Präkursor für C₂N vorgestellt, eine organisch-kristalline Verbindung zwischen Quadratsäure und Harnstoff. Durch Karbonisation dieser Verbindung bei 550 °C wurde ein Material mit einer Zusammensetzung von C₂N und einer ungewöhnlichen, schichtartigen Morphologie erhalten. Über eine eutektische Salzschmelze mit Zinkchlorid, konnte mit diesem Präkursor-System auch mikroporöser C₂N-Kohlenstoff mit einer BET-Oberfläche von 865 m²/g hergestellt werden. Im letzten Teil dieser Arbeit wurde die Herstellung des g-C₃N₄/C₂N-Komposits versucht, über die Selbstassemblierung von kolloidal dispergierten g-C₃N₄- und C₂N-Nanopartikeln. Die Nanopartikel wurden über Ultraschall-Behandlungen von Dispersionen dieser Komponenten hergestellt. Die erhaltenen Komposite zeigten eine hohe Aktivität zur photokatalytischen Wasserspaltung, wobei dies eher auf die hohe Oberfläche der Nanopartikel als auf ihre Zusammensetzung zurückgeführt wurde. Im Hinblick auf mögliche Alternativen zur Kompositherstellung, wurden erste Experimente zu höher konzentrierten kolloidalen Dispersionen von C₂N in dem organischen Lösungsmittel N-Methyl-2-pyrrolidon durchgeführt. Zusammenfassend, die Ergebnisse die in dieser Arbeit erhalten wurden, liefern einen wertvollen Beitrag zur Synthese und Strukturierung von Kohlenstoff/Stickstoff-Materialien sowie deren Anwendungen im Bereich alternative Energien. KW - carbon nitrides KW - supramolecular chemistry KW - porous materials KW - composite materials KW - photocatalysis KW - Kohlenstoffnitride KW - supramolekulare Chemie KW - poröse Materialien KW - Komposite KW - Photokatalyse Y1 - 2017 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-398855 ER - TY - THES A1 - Luschtinetz, Franziska T1 - Cyaninfarbstoffe als Fluoreszenzsonden in biomimetischen und biologischen Systemen : Fluoreszenz-Korrelations-Spektroskopie und Fluoreszenzanisotropie-Untersuchungen T1 - Cyanine dyes as fluorescent probes in biomimetic and biological systems : fluorescence correlation spectroscopy and fluorescence anisotropy studies N2 - Um Prozesse in biologischen Systemen auf molekularer Ebene zu untersuchen, haben sich vor allem fluoreszenzspektroskopische Methoden bewährt. Die Möglichkeit, einzelne Moleküle zu beobachten, hat zu einem deutlichen Fortschritt im Verständnis von elementaren biochemischen Prozessen geführt. Zu einer der bekanntesten Methoden der Einzelmolekülspektroskopie zählt die Fluoreszenz-Korrelations-Spektroskopie (FCS), mit deren Hilfe intramolekulare und diffusionsgesteuerte Prozesse in einem Zeitbereich von µs bis ms untersucht werden können. Durch die Verwendung von sog. Fluoreszenzsonden können Informationen über deren molekulare Mikroumgebung erhalten werden. Insbesondere für die konfokale Mikroskopie und die Einzelmolekülspektroskopie werden Fluoreszenzfarbstoffe mit einer hohen Photostabilität und hohen Fluoreszenzquantenausbeute benötigt. Aufgrund ihrer hohen Fluoreszenzquantenausbeute und der Möglichkeit, maßgeschneiderte“ Farbstoffe in einem breiten Spektralbereich für die Absorption und Fluoreszenz zu entwickeln, sind Cyaninfarbstoffe von besonderem Interesse für bioanalytische Anwendungen. Als Fluoreszenzmarker finden diese Farbstoffe insbesondere in der klinischen Diagnostik und den Lebenswissenschaften Verwendung. Die in dieser Arbeit verwendeten Farbstoffe DY-635 und DY-647 sind zwei typische Vertreter dieser Farbstoffklasse. Durch Modifizierung können die Farbstoffe kovalent an biologisch relevante Moleküle gebunden werden. Aufgrund ihres Absorptionsmaximums oberhalb von 630nm werden sie insbesondere in der Bioanalytik eingesetzt. In der vorliegenden Arbeit wurden die spektroskopischen Eigenschaften der Cyaninfarbstoffe DY-635 und DY-647 in biomimetischen und biologischen Modellsystemen untersucht. Zur Charakterisierung wurden dabei neben der Absorptionsspektroskopie insbesondere fluoreszenzspektroskopische Methoden verwendet. Dazu zählen die zeitkorrelierte Einzelphotonenzählung zur Ermittlung des Fluoreszenzabklingverhaltens, Fluoreszenz-Korrelations-Spektroskopie (FCS) zur Beobachtung von Diffusions- und photophysikalischen Desaktivierungsprozessen und die zeitaufgelöste Fluoreszenzanisotropie zur Untersuchung der Rotationsdynamik und Beweglichkeit der Farbstoffe im jeweiligen Modellsystem. Das Biotin-Streptavidin-System wurde als Modellsystem für die Untersuchung von Protein-Ligand-Wechselwirkungen verwendet, da der Bindungsmechanismus weitgehend aufgeklärt ist. Nach Bindung der Farbstoffe an Streptavidin wurde eine erhebliche Veränderung in den Absorptions- und Fluoreszenzeigenschaften beobachtet. Es wird angenommen, dass diese spektralen Veränderungen durch Wechselwirkung von benachbarten, an ein Streptavidintetramer gebundenen Farbstoffmolekülen und Bildung von H-Dimeren verursacht wird. Für das System Biotin-Streptavidin ist bekannt, dass während der Bindung des Liganden (Biotin) an das Protein eine Konformationsänderung auftritt. Anhand von zeitaufgelösten Fluoreszenzanisotropieuntersuchungen konnte in dieser Arbeit gezeigt werden, dass diese strukturellen Veränderungen zu einer starken Einschränkung der Beweglichkeit des Farbstoffes DY-635B führen. Liegt eine Mischung von ungebundenem und Streptavidin-gebundenem Farbstoff vor, können die Anisotropieabklingkurven nicht nach einem exponentiellen Verlauf angepasst werden. Es konnte im Rahmen dieser Arbeit gezeigt werden, dass in diesem Fall die Auswertung mit Hilfe des Assoziativen Anisotropiemodells möglich ist, welches eine Unterscheidung der Beiträge aus den zwei verschiedenen Mikroumgebungen ermöglicht. Als zweites Modellsystem dieser Arbeit wurden Mizellen des nichtionischen Tensids Tween-20 eingesetzt. Mizellen bilden eines der einfachsten Systeme, um die Mikroumgebung einer biologischen Membran nachzuahmen. Sind die Farbstoffe in den Mizellen eingelagert, so kommt es zu keiner Veränderung der Mizellgröße. Die ermittelten Werte des Diffusionskoeffizienten der mizellar eingelagerten Farbstoffe spiegeln demzufolge die Translationsbewegung der Tween-20-Mizellen wider. Die Beweglichkeit der Farbstoffe innerhalb der Tween-20-Mizellen wurde durch zeitaufgelöste Fluoreszenzanisotropiemessungen untersucht. Neben der „Wackelbewegung“, entsprechend dem wobble-in-a-cone-Modell, wird zusätzlich noch die laterale Diffusion der Farbstoffe entlang der Mizelloberfläche beschrieben. N2 - To investigate processes in biological systems on a molecular level, particularly fluorescence spectroscopic methods have proven. The possibility to observe single molecules led to significant progress in the understanding of basic biochemical processes. Fluorescence correlation spectroscopy (FCS) is one of the most popular methods of single molecule spectroscopy and is a powerful technique for the investigation of intramolecular and diffusion-controlled processes on a µs to ms time scale. The photophysical characteristics of fluorescent probes are often strongly influenced by their microenvironment. For confocal microscopy and single molecule detection applications fluorescent dyes with properties, such as high photostability and high fluorescence efficiency are highly needed. Due to the high fluorescence efficiency and the high potential to design tailor-made fluorescence probes covering a wide spectral range in absorption and fluorescence, cyanine dyes are highly attractive as fluorescence probes for bioanalytical applications, such as clinical diagnostics and life sciences. The dyes DY-635 and DY-647 are two typical representatives of this class of dyes and can be covalently attached to biologically relevant molecules. Because of their excitation wavelength above 630nm these dyes are especially suited for bioanalytical applications. In this work the spectroscopic properties of DY-635 and DY-647 in biomimetic and biological model systems were studied by absorption and fluorescence spectroscopy techniques: time-correlated single photon counting to determine fluorescence decay behavior, fluorescence correlation spectroscopy (FCS) to observe diffusion and photophysical deactivation processes, and fluorescence anisotropy to study the mobility and rotational behavior of the dyes in the respective model system. The well characterized system biotin-streptavidin was used as a model system for protein-ligand interactions. Binding to streptavidin resulted in significant changes in the steady-state photophysical characteristics of DY-635B and DY-647. These spectral changes are attributed to dye-dye interactions and the formation of H-dimers. Previous studies have demonstrated, that binding of biotin alters the conformation of streptavidin. Based on the evaluation of time-resolved anisotropy data in this study it was shown that these structural changes result in strong hindrance of the rotational freedom of DY-635B. For mixtures of unbound and streptavidin-bound dyes the fluorescence anisotropy decay curves are found to be nonexponential. In this case the concept of an associated anisotropy were applied which allowed discrimination between contributions from different microenvironments. As a second model system, micelles of the nonionic surfactant Tween-20 were used. Micelles are one of the simplest systems to mimic the microenvironment of a biological membrane. Incorporation of the dyes had no effect on the micelle size. The diffusion coefficient of the dyes, obtained by fluorescence correlation spectroscopy (FCS), reflects the translational behavior of Tween-20 micelles. The mobility of the dyes in the Tween-20 micelles was studied by time-resolved fluorescence anisotropy. In addition to a „wobbling“ motion ccording to the wobble-in-a-cone model, a lateral diffusion of the dyes along the micelle surface is described. KW - Cyaninfarbstoffe KW - Fluoreszenz-Korrelations-Spektroskopie KW - Fluoreszenzanisotropie KW - Biotin-Streptavidin KW - Assoziatives Anisotropiemodell KW - cyanine dyes KW - fluorescence correlation spectroscopy KW - fluorescence anisotropy KW - biotin streptavidin KW - associated anisotropy Y1 - 2010 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-48478 ER - TY - THES A1 - Phung, Thi Thuy Nga T1 - Defect chemistry in halide perovskites BT - material characterisation and device integration N2 - Metallhalogenid-Perowskite haben sich aufgrund ihrer hervorragenden optoelektronischen Eigenschaften zu einer attraktiven Materialklasse für die Photovoltaikindustrie entwickelt. Die Langzeitstabilität ist jedoch noch immer ein Hindernis für die industrielle Realisierung dieser Materialklasse. Zunehmend zeigen sich Hinweise dafür, dass intrinsische Defekte im Perowskit die Material-Degradation fördern. Das Verständnis der Defekte im Perowskit ist wichtig, um seine Stabilität und optoelektronische Qualität weiter zu verbessern. Diese Dissertation konzentriert sich daher auf das Thema Defektchemie im Perowskit. Der erste Teil der Dissertation gibt einen kurzen Überblick über die Defekteigenschaften von Halogenid-Perowskiten. Anschließend zeigt der zweite Teil, dass das Dotieren von Methylammoniumbleiiodid mit einer kleinen Menge von Erdalkalimetallen (Sr und Mg) ein höherwertiges, weniger fehlerhaftes Material erzeugt, was zu hohen Leerlaufspannungen sowohl in der n-i-p als auch in der p-i-n Architektur von Solarzellen führt. Es wurde beobachtet, dass die Dotierung in zwei Domänen stattfindet: eine niedrige Dotierungskonzentration führt zum Einschluss der entsprechenden Elemente in das Kristallgitter ermöglicht, während eine hohe Dotierungskonzentration zu einer Phasentrennung führt. Das Material kann im Niedrigdotierungsbereich mehr n-dotiert sein, während es im Hochdotierungsbereich weniger n-dotiert ist. Die Schwelle dieser beiden Regime hängt von der Atomgröße der Dotierelemente ab. Der nächste Teil der Dissertation untersucht die photoinduzierte Degradation von Methylammonium-Bleiiodid. Dieser Abbaumechanismus hängt eng mit der Bildung und Migration von defekten zusammen. Nach der Bildung können sich diese in Abhängigkeit von der Defektdichte und ihrer Verteilung bewegen. Demnach kann eine hohe Defektdichte wie an den Korngrenzen eines Perowskitfilms die Beweglichkeit von ionischen Punktdefekten hemmen. Diese Erkenntnis ließe sich auf das zukünftige Materialdesign in der Photovoltaikindustrie anwenden, da die Perowskit-Solarzellen normalerweise einen polykristallinen Dünnfilm mit hoher Korngrenzendichte verwenden. Die abschließende Studie, die in dieser Dissertation vorgestellt wird, konzentriert sich auf die Stabilität der neuesten „dreifach-kationen“ Perowskit-basierten Solarzellen unter dem Einfluss einer permanent angelegten elektrischen Spannung. Eine längere Betriebsdauer (mehr als drei Stunden permanente Spannung) fördert die Amorphisierung im Halogenid-Perowskiten. Es wird hierbei vermutet, dass sich eine amorphe Phase an den Grenzflächen bildet, insbesondere zwischen der lochselektiven Schicht und dem Perowskit. Diese amorphe Phase hemmt den Ladungstransport und beeinträchtigt die Leistung der Perowskit-Solarzelle erheblich. Sobald jedoch keine Spannung mehr anliegt können sich die Perowskitschichten im Dunkeln bereits nach einer kurzen Pause regenerieren. Die Amorphisierung wird auf die Migration von ionischen Fehlordnungen zurückgeführt, höchstwahrscheinlich auf die Migration von Halogeniden. Dieser Ansatz zeigt ein neues Verständnis des Abbau-Mechanismus in Perowskit-Solarzellen unter Betriebsbedingungen. N2 - Metal halide perovskites have merged as an attractive class of materials for photovoltaic applications due to their excellent optoelectronic properties. However, the long term stability is a roadblock for this class of material’s industrial pathway. Increasing evidence shows that intrinsic defects in perovskite promote material degradation. Consequently, understanding defect behaviours in perovskite materials is essential to further improve device stability and performance. This dissertation, hence, focuses on the topic of defect chemistry in halide perovskites. The first part of the dissertation gives a brief overview of the defect properties in halide perovskite. Subsequently, the second part shows that doping methylammonium lead iodide with a small amount of alkaline earth metals (Sr and Mg) creates a higher quality, less defective material resulted in high open circuit voltages in both n-i-p and p-i-n architecture. It has been found that the mechanism of doping has two distinct regimes in which a low doping concentration enables the inclusion of the dopants into the lattice whereas higher doping concentrations lead to phase segregation. The material can be more n-doped in the low doping regime while being less n-doped in the high doping regime. The threshold of these two regimes is based on the atomic size of the dopants. The next part of the dissertation examines the photo-induced degradation in methylammonium lead iodide. This degradation mechanism links closely to the formation and migration of ionic defects. After they are formed, these ionic defects can migrate, however, not freely depending on the defect concentration and their distribution. In fact, a highly concentrated defect region such as the grain boundaries can inhibit the migration of ionic defects. This has implications for material design as perovskite solar cells normally employ a polycrystalline thin-film which has a high density of grain boundary. The final study presented in this PhD dissertation focuses on the stability of the state-of-the-art triple cation perovskite-based solar devices under external bias. Prolonged bias (more than three hours) is found to promote amorphization in halide perovskite. The amorphous phase is suspected to accumulate at the interfaces especially between the hole selective layer and perovskite. This amorphous phase inhibits the charge collection and severely affects the device performance. Nonetheless, the devices can recover after resting without bias in the dark. This amorphization is attributed to ionic defect migration most likely halides. This provides a new understanding of the potential degradation mechanisms in perovskite solar cells under operational conditions. KW - halide perovskite KW - solar cells KW - defect chemistry KW - ionic defects KW - Defektchemie KW - Halogenid-Perowskite KW - Defekte KW - Solarzellen Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-476529 ER - TY - THES A1 - Altabal, Osamah T1 - Design and fabrication of geometry-assisted on-demand dosing systems N2 - The controlled dosage of substances from a device to its environment, such as a tissue or an organ in medical applications or a reactor, room, machinery or ecosystem in technical, should ideally match the requirements of the applications, e.g. in terms of the time point at which the cargo is released. On-demand dosage systems may enable such a desired release pattern, if the device contain suitable features that can translate external signals into a release function. This study is motivated by the opportunities arising from microsystems capable of an on-demand release and the contributions that geometrical design may have in realizing such features. The goals of this work included the design, fabrication, characterization and experimental proof-of-concept of geometry-assisted triggerable dosing effect (a) with a sequential dosing release and (b) in a self-sufficient dosage system. Structure-function relationships were addressed on the molecular, morphological and, with a particular attention, the device design level, which is on the micrometer scale. Models and/or computational tools were used to screen the parameter space and provide guidance for experiments. N2 - Die kontrollierte Freisetzung von Substanzen aus einem Device in seine Umgebung, wie ein Gewebe oder Organ in medizinischen Anwendungen oder ein Reaktor, ein Raum, ein Gerät oder ein Ökosystem in technischer Nutzung sollte idealerweise den Anforderungen des Einsatzzweckes entsprechen, beispielsweise hinsichtlich des Zeitpunktes an dem die Freisetzung erfolgt. On-demand Freisetzungssysteme könnten eine derartiges gewünschtes Verhalten zeigen, wenn das System die Befähigung besitzt, externe Signale in eine Freisetzungsfunktion zu überführen. Diese Arbeit greift die Möglichkeiten auf, die sich durch den Einsatz und ein gezieltes Design von mikrostrukturierten Systemen für die Realisierung einer on-demand Freisetzung ergeben könnten. Die Ziele der Arbeit umfassen die Konzeptionierung, Herstellung, Charakterisierung sowie den grundsätzlichen Nachweis durch Stimuli induzierten on-demand Freisetzungsfunktion einerseits in Form eines sequentiellen Freigabeverhaltens und anderseits in Form eines autarken (kontaktfrei ausgelösten) Dosiersystems. Struktur-Eigenschafts-Beziehungen wurden auf molekularer, morphologischer und - mit besonderen Augenmerk - auf der Ebene des Device-Designs untersucht. Modelle und/oder Computer-gestützte Verfahren wurden verwendet um geeignete Materialparameter zu identifizieren und einen Leitfaden für die Experimente bereitzustellen. KW - Stress concentration KW - Negative Poisson’s ratio KW - On-demand release KW - Spannungskonzentrationen KW - Negatives Poisson-Verhältnis KW - On-demand Freisetzung Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-532441 ER - TY - THES A1 - Piluso, Susanna T1 - Design of biopolymer-based networks with defined molecular architecture T1 - Design biopolymer-basierter Netzwerke mit definierter molekularer Architektur N2 - In this work, the synthesis of biopolymer-based hydrogel networks with defined architecture is presented. In order to obtain materials with defined properties, the chemoselective copper-catalyzed azide-alkyne cycloaddition (or Click Chemistry) was used for the synthesis of gelatin-based hydrogels. Alkyne-functionalized gelatin was reacted with four different diazide crosslinkers above its sol-gel transition to suppress the formation of triple helices. By variation of the crosslinking density and the crosslinker flexibility, the swelling (Q: 150-470 vol.-%;) and the Young’s and shear moduli (E: 50 kPa - 635 kPa, G’: 0.1 kPa - 16 kPa) could be tuned in the kPa range. In order to understand the network structure, a method based on the labelling of free functional groups within the hydrogel was developed. Gelatin-based hydrogels were incubated with alkyne-functionalized fluorescein to detect the free azide groups, resulting from the formation of dangling chains. Gelatin hydrogels were also incubated with azido-functionalized fluorescein to check the presence of alkyne groups available for the attachment of bioactive molecules. By using confocal laser scanning microscopy and fluorescence spectroscopy, the amount of crosslinking, grafting and free alkyne groups could be determined. Dangling chains were observed in samples prepared by using an excess of crosslinker and also when using equimolar amounts of alkyne:azide. In the latter case the amount of dangling chains was affected by the crosslinker structure. Specifically, 0.1% of dangling chains were found using 4,4’-diazido-2,2’-stilbene-disulfonic acid as cosslinker, 0.06% with 1,8-diazidooctane, 0.05% with 1,12-diazidododecane and 0.022 % with PEG-diazide. This observation could be explained considering the structure of the crosslinkers. During network formation, the movements of the gelatin chains are restricted due to the formation of covalent netpoints. A further crosslinking will be possible only in the case of crosslinker that are flexible and long enough to reach another chain. The method used to obtain defined gelatin-based hydrogels enabled also the synthesis of hyaluronic acid-based hydrogels with tailorable properties. Alkyne-functionalized hyaluronic acid was crosslinked with three different linkers having two terminal azide functionalities. By variation of the crosslinking density and crosslinker type, hydrogels with elastic moduli in the range of 0.5-3 kPa have been prepared. The variation of the crosslinking density and crosslinker type had furthermore an influence also on the hydrolytic and enzymatic degradation of gelatin-based hydrogels. Hydrogels with a low crosslinker amount experienced a faster decrease in mass loss and elastic modulus compared to hydrogels with higher crosslinker content. Moreover, the structure of the crosslinker had a strong influence on the enzymatic degradation. Hydrogels containing a crosslinker with a rigid structure were much more resistant to enzymatic degradation than hydrogels containing a flexible crosslinker. During hydrolytic degradation, the hydrogel became softer while maintaining the same outer dimensions. These observations are in agreement with a bulk degradation mechanism, while the decrease in size of the hydrogels during enzymatic degradation suggested a surface erosion mechanism. Because of the use of small amount of crosslinker (0.002 mol.% 0.02 mol.%) the networks synthesized can still be defined as biopolymer-based hydrogels. However, they contain a small percentage of synthetic residues. Alternatively, a possible method to obtain biopolymer-based telechelics, which could be used as crosslinkers, was investigated. Gelatin-based fragments with defined molecular weight were obtained by controlled degradation of gelatin with hydroxylamine, due to its specific action on asparaginyl-glycine bonds. The reaction of gelatin with hydroxylamine resulted in fragments with molecular weights of 15, 25, 37, and 50 kDa (determined by SDS-PAGE) independently of the reaction time and conditions. Each of these fragments could be potentially used for the synthesis of hydrogels in which all components are biopolymer-based materials. N2 - In dieser Arbeit wird die Synthese Biopolymer-basierter Hydrogelnetzwerke mit definierter Architektur beschrieben. Um Materialien mit definierten und einstellbaren Eigenschaften zu erhalten, wurde die chemoselektive Kupferkatalysierte Azid-Alkin-Cycloadditionsreaktion (auch als Click-Chemie bezeichnet) für die Synthese Gelatine-basierter Netzwerke eingesetzt. Alkin-funktionalisierte Gelatine wurde mit vier verschiedenen Diazid-Quervernetzern oberhalb der Gel-Sol-Übergangstemperatur umgesetzt, um die Formierung tripelhelikaler Bereiche durch Gelatineketten zu unterdrücken. Durch Variation der Menge an Quervernetzer (und damit der Netzdichte) sowie der Länge und Flexibilität der Quervernetzer konnten u.a. die Quellung (Q: 150-470 vol.-%) sowie der Young’s - und Schermodul im kPa Bereich eingestellt werden (E: 50 kPa - 635 kPa, G’: 0.1 kPa - 16 kPa). Um die Netzwerkarchitektur zu verstehen, wurde eine Methode basierend auf dem Labeln unreagierter Azid- und Alkingruppen im Hydrogel entwickelt. Die Gelatine-basierten Hydrogele wurden mit Alkin-funktionalisiertem Fluorescein umgesetzt, um freie Azidgruppen zu detektieren, die bei einem Grafting entstehen. Darüber hinaus wurden die Hydrogele mit Azid-funktionalisiertem Fluorescein reagiert, um die Menge an freien Alkingruppen zu bestimmen, die zudem potentiell für die Anbindung bioaktiver Moleküle geeignet sind. Quervernetzung, Grafting, und die Anzahl freier Alkingruppen konnten dann mit Hilfe der konfokalen Laser Scanning Mikroskopie und der Fluoreszenzmikroskopie qualitativ und quantitativ nachgewiesen werden. Gegraftete Ketten wurden in Systemen nachgewiesen, die mit einem Überschuss an Quervernetzer hergestellt wurden, entstanden aber auch beim Einsatz äquimolarer Mengen Alkin- und Azidgruppen. Im letzteren Fall wurde in Abhängigkeit von der Struktur des Diazids unterschiedliche Anteile gegrafteter Ketten festgestellt. 0.1 mol-% von gegrafteten Ketten wurden für 4,4’-Diazido-2,2’-stilbendisulfonsäure gefunden, 0.06 mol-% für 1,8-Diazidooktan, 0.05 mol% für 1,12-diazidododecan und 0.022 mol-% für PEG-Diazid. Diese Beobachtung kann durch die unterschiedliche Flexibilität der Vernetzer erklärt werden. Während der Netzwerkbildung werden die Bewegungen der Gelatineketten eingeschränkt, so dass kovalente Netzpunkte nur erhalten werden können, wenn der Vernetzer lang und flexibel genug ist, um eine andere Alkingruppe zu erreichen. Die Strategie zur Synthese von Biopolymer-basierten Hydrogelen mit einstellbaren Eigenschaften wurde von Gelatine- auf Hyaluronsäure-basierte Gele übertragen. Alkin-funktionalisierte Hyaluronäure wurde mit drei verschiedenen Diaziden quervernetzt, wobei Menge, Länge, und Flexibilität des Quervernetzers variiert wurden. In dieser Weise wurden sehr weiche Hydrogele mit E-Moduli im Bereich von 0.5-3 kPa hergestellt. Die Variation der Vernetzungsdichte und des Vernetzertyps beeinflusste weiterhin den hydrolytischen und enzymatischen Abbau der Hydrogele. Hydrogele mit einem geringerem Anteil an Quervernetzer wurden schneller abgebaut als solche mit einem höheren Quervernetzeranteil. Darüber hinaus konnte gezeigt werden, dass Hydrogele mit Quervernetzern mit einer rigiden Struktur deutlich langsamer degradierten als Hydrogele mit flexibleren Quervernetzern. Während des hydrolytischen Abbau wurden die Materialien weicher, behielten aber ihre Form bei, was mit einem Bulk-Abbau-Modell übereinstimmt. Während des enzymatischen Abbaus hingegen änderten sich die Materialeigenschaften kaum, jedoch wurden die Proben kleiner. Diese Beobachtung stimmt mit einem Oberflächenabbaumechanismus überein. Da in allen vorgestellten Systemen nur eine kleine Menge synthetischer Vernetzer eingesetzt wurde (0.002 – 0.02 mol%), können die Materialien noch als Biopolymer-basierte Materialien klassifiziert werden. Jedoch enthalten die Materialien synthetische Abschnitte. In Zukunft könnte es interessant sein, einen Zugang zu Materialien zu haben, die ausschließlich aus Biopolymeren aufgebaut sind. Daher wurde der Zugang zu Biopolymer basierten Telechelen untersucht, die potentiell als Vernetzer dienen können. Dazu wurden durch die kontrollierte Spaltung von Gelatine mit Hydroxylamin Gelatinefragmente mit definiertem Molekulargewicht hergestellt. Hydroxalamin reagiert unter Spaltung mit der Amidbindung zwischen Asparagin und Glycin, wobei Aspartylhydroxamate und Aminoendgruppen entstehen. Die Reaktion von Gelatine mit Hydroxylamin ergab Fragmente mit Molekulargewichten von 15, 25, 37, und 50 kDa (bestimmt mit SDS-PAGE), und die Formierung dieser Fragmente war unabhängig von den weiteren Reaktionsbedingungen und der Reaktionszeit. Jedes dieser Fragmente kann potentiell für die Synthese von Hydrogelen eingesetzt werden, die ausschließlich aus Biopolymeren bestehen. KW - Klickchemie KW - Gelatine KW - Hyaluronsäure KW - Abbau KW - Kollagenase KW - Click Chemistry KW - Gelatin KW - Hyaluronic acid KW - Degradation KW - Collagenase Y1 - 2012 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-59865 ER - TY - THES A1 - Mondal, Suvendu Sekhar T1 - Design of isostructural metal-imidazolate frameworks : application for gas storage T1 - Synthese isostruktureller Metall-Imidazolat Frameworks : Anwendung für Gasspeicherung N2 - The sharply rising level of atmospheric carbon dioxide resulting from anthropogenic emissions is one of the greatest environmental concerns facing our civilization today. Metal-organic frameworks (MOFs) are a new class of materials that constructed by metal-containing nodes bonded to organic bridging ligands. MOFs could serve as an ideal platform for the development of next generation CO2 capture materials owing to their large capacity for the adsorption of gases and their structural and chemical tunability. The ability to rationally select the framework components is expected to allow the affinity of the internal pore surface toward CO2 to be precisely controlled, facilitating materials properties that are optimized for the specific type of CO2 capture to be performed (post-combustion capture, precombustion capture, or oxy-fuel combustion) and potentially even for the specific power plant in which the capture system is to be installed. For this reason, significant effort has been made in recent years in improving the gas separation performance of MOFs and some studies evaluating the prospects of deploying these materials in real-world CO2 capture systems have begun to emerge. We have developed six new MOFs, denoted as IFPs (IFP-5, -6, -7, -8, -9, -10, IFP = Imidazolate Framework Potsdam) and two hydrogen-bonded molecular building block (MBB, named as 1 and 2 for Zn and Co based, respectively) have been synthesized, characterized and applied for gas storage. The structure of IFP possesses 1D hexagonal channels. Metal centre and the substituent groups of C2 position of the linker protrude into the open channels and determine their accessible diameter. Interestingly, the channel diameters (range : 0.3 to 5.2 Å) for IFP structures are tuned by the metal centre (Zn, Co and Cd) and substituent of C2 position of the imidazolate linker. Moreover hydrogen bonded MBB of 1 and 2 is formed an in situ functionalization of a ligand under solvothermal condition. Two different types of channels are observed for 1 and 2. Materials contain solvent accessible void space. Solvent could be easily removed by under high vacuum. The porous framework has maintained the crystalline integrity even without solvent molecules. N2, H2, CO2 and CH4 gas sorption isotherms were performed. Gas uptake capacities are comparable with other frameworks. Gas uptake capacity is reduced when the channel diameter is narrow. For example, the channel diameter of IFP-5 (channel diameter: 3.8 Å) is slightly lower than that of IFP-1 (channel diameter: 4.2 Å); hence, the gas uptake capacity and Brunauer-Emmett-Teller (BET) surface area are slightly lower than IFP-1. The selectivity does not depend only on the size of the gas components (kinetic diameter: CO2 3.3 Å, N2 3.6 Å and CH4 3.8 ) but also on the polarizability of the surface and of the gas components. IFP-5 and-6 have the potential applications for the separation of CO2 and CH4 from N2-containing gas mixtures and CO2 and CH4 containing gas mixtures. Gas sorption isotherms of IFP-7, -8, -9, -10 exhibited hysteretic behavior due to flexible alkoxy (e.g., methoxy and ethoxy) substituents. Such phenomenon is a kind of gate effects which is rarely observed in microporous MOFs. IFP-7 (Zn-centred) has a flexible methoxy substituent. This is the first example where a flexible methoxy substituent shows the gate opening behavior in a MOF. Presence of methoxy functional group at the hexagonal channels, IFP-7 acted as molecular gate for N2 gas. Due to polar methoxy group and channel walls, wide hysteretic isotherm was observed during gas uptake. The N2 The estimated BET surface area for 1 is 471 m2 g-1 and the Langmuir surface area is 570 m2 g-1. However, such surface area is slightly higher than azolate-based hydrogen-bonded supramolecular assemblies and also comparable and higher than some hydrogen-bonded porous organic molecules. N2 - Metallorganische Gerüstverbindungen (MOFs) sind eine neue Klasse von porösen Koordinationspolymeren, die aus Metall-Knoten und verbrückenden Liganden bestehen. MOFs können Gasgemische trennen und Gase speichern. Aufgrund ihres modularen Aufbaus können die MOF-Eigenschaften systematisch variiert werden. Ein wichtiges Ziel für das Design von MOFs ist die Synthese von Materialien, die eine hohe selektive Aufnahmefähigkeit und -kapazität für Kohlenstoffdioxid besitzen. Im Rahmen der Arbeit ist es gelungen sechs neue MOFs (IFP-5, -6, -7, -8, -9 und -10) zu synthetisieren. Diese MOFs tragen die Kurzbezeichnung IFP. IFP steht als Abkürzung für Imidazolat-Framework-Potsdam (Imidazolat-basierte Gerüstverbindung Potsdam). In diesen IFPs wurde der Metallknoten (Zink, Cobalt, Cadmium) und der Brückenligand, ein 2-substituiertes Imidazolat-amid-imidat, in der Position variiert, um gute und selektive Sorptionseigenschaften für Kohlenstoffdioxid zu erzielen. Von den synthetisierten Verbindungen hat das IFP-5 die besten Sorptionseigenschaften für Kohlenstoffdioxid. Es konnte weiter gezeigt werden, dass sich die IFP-Struktur bei der Wahl von geeigneten Substituenten 2, wie z.B. Methoxy und Ethoxy auch für das Design von gate-opening (Tür-öffnenden) Effekten eignet. Diese Effekte können wiederum genutzt werden, um selektiv Gasmischungen zu trennen. Wenn man das 4,5-Dicyano-2-methoxy-imidazol in Gegenwart von Zink- und Cobalt-Salzen unter solvothermalen Bedingungen zur Reaktion bringt, erhält man beispiellose supramolekulare Wasserstoffbrückenbindungen zu einem dreidimensionalen Netzwerk, die mit Kanälen verknüpft sind. Diese Kanäle können von Lösungsmittelmolekülen (Wasser und Dimethylformamid) befreit werden und Gase aufnehmen. Insgesamt besteht nun die neue MOF-Klasse der Imidazolat-basierten IFPs aus Vertretern. Das Potential der 2-substituierten 4,5-Dicyanoimidazole ist nicht nur auf die Bildung von porösen Koordinationspolymeren beschränkt, sondern kann auch für die Synthese von bisher unbekannten supramolekularen Strukturen genutzt werden. KW - Metal-organic framework KW - Gas Sorption KW - Cobalt KW - Zinc KW - Ionic Liquid KW - metal-organic framework KW - gas sorption KW - cobalt KW - zinc KW - ionic liquid Y1 - 2013 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-69692 ER - TY - THES A1 - Ilic, Ivan T1 - Design of sustainable cathodes for Li-ion batteries T1 - Design nachhaltiger Kathoden für Li-Ionen-Batterien BT - understanding the redox behaviour of guaiacyl and catecholic groups in lithium organic system N2 - In recent years people have realised non-renewability of our modern society which relays on spending huge amounts of energy mostly produced from fosil fuels, such as oil and coal, and the shift towards more sustainable energy sources has started. However, sustainable sources of energy, such as wind-, solar- and hydro-energy, produce primarily electrical energy and can not just be poured in canister like many fosil fuels, creating necessity for rechragable batteries. However, modern Li-ion batteries are made from toxic heavy metals and sustainable alternatives are needed. Here we show that naturally abundant catecholic and guaiacyl groups can be utilised to replace heavy metals in Li-ion batteries. Foremost vanillin, a naturally occurring food additive that can be sustainably synthesised from industrial biowaste, lignin, was utilised to synthesise materials that showed extraordinary performance as cathodes in Li-ion batteries. Furthermore, behaviour of catecholic and guiacyl groups in Li-ion system was compared, confirming usability of guiacayl containing biopolymers as cathodes in Li-ion batteries. Lastly, naturally occurring polyphenol, tannic acid, was incorporated in fully bioderived hybrid material that shows performance comparable to commercial Li-ion batteries and good stability. This thesis presents an important advancement in understanding of biowaste derived cathode materials for Li-ion batteries. Further research should be conducted to better understand behaviour of guaiacyl groups during Li-ion battery cycling. Lastly, challenges of incorporation of lignin, an industrial biowaste, have to be addressed and lignin should be incorporated as a cathode material in Li-ion batteries. N2 - Diese Dissertation untersucht, wie nachhaltige Kathoden (Kathodenmaterialien) für Lithium-Ionen-Batterien aus Holzabfällen hergestellt werden können. In den letzten Jahren hat die Menschheit erkannt, wie wenig nachhaltig unsere moderne Gesellschaft ist und große Mengen an Energie verbraucht, welche zum größten Teil aus fossilen Brennstoffen gewonnen werden. Daher versucht man jetzt die Energie aus hauptsächlich erneuerbaren Quellen wie Sonne und Wind zu gewinnen. Allerdings kann elektrische Energie nicht einfach wie Öl in einen Kanister gegossen werden, sondern muss in wieder aufladbaren Batterien gespeichert werden. In den letzten Jahren wurden Lithium-Ionen-Batterien entwickelt, die leistungsstark und allgegenwärtig sind, da sie zum Beispiel in Handys und sogar Autos Verwendung finden. Lithium-Ionen-Batterien verwenden jedoch Trägermaterialien aus giftigen Schwermetallen, die abgebaut werden müssen, was sich negativ auf die Umwelt auswirkt. In diesem Zusammenhang ist insbesondere das Schwermetall Kobalt zu erwähnen, welches in den meisten modernen Kathoden verwendet wird. Nach dem Bekanntwerden von Sklaverei und Kinderarbeit beim Kobaltabbau im Kongo, folgten große Kontroversen, da Kobalt praktisch in jedem Gerät führender Unternehmen wie zum Beispiel Apple und Microsoft zu finden ist. Idealerweise müssen wir von nicht erneuerbaren Schwermetallen zu erneuerbaren organischen Molekülen wechseln. Daher verwende ich in meiner Forschung Vanillin, ein Molekül, das hinsichtlich der Elektronenspeicherung ähnliche Eigenschaften wie Schwermetalle aufweist, jedoch viele Vorteile bietet. Erstens erkennt man Vanillin am spezifischen Geruch, da es einer der Hauptbestandteile von Vanille und daher ein natürlich vorkommendes Molekül ist. Zweitens kann es aus Holzabfällen oder aus Abfällen vieler Industrien hergestellt werden, die Holz als Rohstoff verwenden, wie beispielsweise der Papierindustrie. Durch milde chemische Reaktionen in Lösemitteln wie Wasser, Essig und Alkohol haben wir Vanillin zu einem Material modifiziert, welches hervorragende Eigenschaften zur Verwendung in Lithium-Ionen-Batterien hat und die bisher verwendeten Schwermetelle ersetzen kann. Diese Batterien wären somit erneuerbar und können uns der nachhaltigen Welt einen Schritt näher bringen. Darüber hinaus wurde Tanninsäure, ein natürlich vorkommendes Polymer in Holzrinde, verwendet, um vollständig aus Bioabfällen bestehende Batterien herzustellen. KW - biomass KW - electrochemistry KW - energy conversion KW - polymers KW - redox chemistry KW - Biomasse KW - Elektrochemie KW - Energieumwandlung KW - Polymere KW - Redoxchemie Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-483689 ER - TY - THES A1 - Bivigou Koumba, Achille Mayelle T1 - Design, Synthesis and Characterisation of Amphiphilic Symmetrical triblock copolymers by the RAFT process : their self-organisation in dilute and concentrated aqueous solutions T1 - Design, Synthese und Charakterisierung von amphiphilen symmetrischen Triblock-Copolymeren anhand des RAFT Prozesses : ihre Selbstorganisation in wässrigen verdünnten und höher konzentrierten Lösungen N2 - This work presents the synthesis and the self-assembly of symmetrical amphiphilic ABA and BAB triblock copolymers in dilute, semi-concentrated and highly concentrated aqueous solution. A series of new bifunctional bistrithiocarbonates as RAFT agents was used to synthesise these triblock copolymers, which are characterised by a long hydrophilic middle block and relatively small, but strongly hydrophobic end blocks. As hydrophilic A blocks, poly(N-isopropylacrylamide) (PNIPAM) and poly(methoxy diethylene glycol acrylate) (PMDEGA) were employed, while as hydrophobic B blocks, poly(4-tert-butyl styrene), polystyrene, poly(3,5-dibromo benzyl acrylate), poly(2-ethylhexyl acrylate), and poly(octadecyl acrylate) were explored as building blocks with different hydrophobicities and glass transition temperatures. The five bifunctional trithiocarbonates synthesised belong to two classes: the first are RAFT agents, which position the active group of the growing polymer chain at the outer ends of the polymer (Z-C(=S)-S-R-S-C(=S)-Z, type I). The second class places the active groups in the middle of the growing polymer chain (R-S-C(=S)-Z-C(=S)-S-R, type II). These RAFT agents enable the straightforward synthesis of amphiphilic triblock copolymers in only two steps, allowing to vary the nature of the hydrophobic blocks as well as the length of the hydrophobic and hydrophilic blocks broadly with good molar mass control and narrow polydispersities. Specific side reactions were observed among some RAFT agents including the elimination of ethylenetrithiocarbonate in the early stage of the polymerisation of styrene mediated by certain agents of the type II, while the use of the RAFT agents of type I resulted in retardation of the chain extension of PNIPAM with styrene. These results underline the need of a careful choice of RAFT agents for a given task. The various copolymers self-assemble in dilute and semi-concentrated aqueous solution into small flower-like micelles. No indication for the formation of micellar clusters was found, while only at high concentration, physical hydrogels are formed. The reversible thermoresponsive behaviour of the ABA and BAB type copolymer solutions in water with A made of PNIPAM was examined by turbidimetry and dynamic light scattering (DLS). The cloud point of the copolymers was nearly identical to the cloud point of the homopolymer and varied between 28-32 °C with concentrations from 0.01 to 50 wt%. This is attributed to the formation of micelles where the hydrophobic blocks are shielded from a direct contact with water, so that the hydrophobic interactions of the copolymers are nearly the same as for pure PNIPAM. Dynamic light scattering measurements showed the presence of small micelles at ambient temperature. The aggregate size dramatically increased above the cloud point, indicating a change of aggregate morphology into clusters due to the thermosensitivity of the PNIPAM block. The rheological behaviour of the amphiphilic BAB triblock copolymers demonstrated the formation of hydrogels at high concentrations, typically above 30-35 wt%. The minimum concentration to induce hydrogels decreased with the increasing glass transition temperatures and increasing length of the end blocks. The weak tendency to form hydrogels was attributed to a small share of bridged micelles only, due to the strong segregation regime occurring. In order to learn about the role of the nature of the thermoresponsive block for the aggregation, a new BAB triblock copolymer consisting of short polystyrene end blocks and PMDEGA as stimuli-responsive middle block was prepared and investigated. Contrary to PNIPAM, dilute aqueous solutions of PMDEGA and of its block copolymers showed reversible phase transition temperatures characterised by a strong dependence on the polymer composition. Moreover, the PMDEGA block copolymer allowed the formation of physical hydrogels at lower concentration, i.e. from 20 wt%. This result suggests that PMDEGA has a higher degree of water-swellability than PNIPAM. N2 - Die Arbeit behandelt die Synthese und das Selbstorganisationsverhalten von neuen funktionellen symmetrischen "stimuli-responsiven" Triblockcopolymeren ABA und BAB in wässrigen verdünnten und höher konzentrierten Lösungen. Neue symmetrische, bifunktionelle Bistrithiocarbonate wurden als RAFT-Agentien benutzt, um Triblockcopolymere mit langen hydrophilen (A) Innen- und kurzen hydrophoben (B) Außenblöcken zu synthetisieren. Als hydrophile A Blöcke wurden Poly(N-isopropylacrylamid) PNIPAM und Poly(methoxy diethylene glykol acrylat) PMDEGA benutzt, während als hydrophobe Blöcke B Poly(4-tert-butyl styrol), Polystyrol, Poly(3,5-dibromo benzyl acrylat), Poly(2-ethylhexyl acrylat), und Poly(octadecyl acrylat) als Bausteine mit unterschiedlicher Glasübergangstemperatur untersucht wurden. Die Selbstorganisation von ABA und BAB Copolymeren in Wasser mit A Blöcken aus PNIPAM wurde anhand von Trübungsphotometrie, dynamischer Lichtstreuung (DLS) und Rheologie untersucht. Die amphiphilen Blockcopolymere sind direkt wasserlöslich. Bei Konzentrationen von 0.01 bis 50 wt% zeigen Trübungsmessungen bei den Blockcopolymeren wie bei den Homopolymeren eine Übergangstemperatur bei 28-32 °C. Zurückzuführen ist dies auf die Bildung von Mizellen, bei der die hydrophoben Blöcke von einem direkten Kontakt mit Wasser abgeschirmt werden. DLS zeigt kleine Mizellen bei niedrigen Temperaturen und Aggregate mit großem hydrodynamischem Durchmesser bei Temperaturen oberhalb der Übergangstemperatur. Die rheologische Untersuchung von BAB Polymeren zeigt die Bildung von Hydrogelen bei höheren Konzentrationen (über 30-35 wt%). Die minimal benötigte Konzentration, bei der die von Hydrogelen auftreten, nimmt mit wachsender Glasübergangstemperatur ab, und nimmt mit der Länge der hydrophoben Blöcke B zu. Im Unterschied zu PNIPAM zeigen wässrige Lösungen von PMDEGA und seinen Blockcopolymeren reversible Übergangstemperaturen abhängig von der chemischen Struktur. Außerdem bilden PMDEGA Blockcopolymere Hydrogele bei niedriger Konzentration (ab 20 wt%). Dieses Ergebnis deutet darauf hin, dass PMDEGA stärker Wasser bindet als PNIPAM. KW - Design KW - Synthese KW - Charakterisierung KW - Triblock-Copolymere KW - RAFT KW - Design KW - Synthesis KW - Characterisation KW - Triblock Copolymers KW - RAFT Y1 - 2009 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-39549 ER - TY - THES A1 - Meiling, Till Thomas T1 - Development of a reliable and environmentally friendly synthesis for fluorescence carbon nanodots T1 - Entwicklung einer zuverlässigen und umweltfreundlichen Synthese für fluoreszierende Kohlenstoff-Nanopunkte BT - preparation and characterisation of excellent and well-defined carbon nanodots by a fast, simple and cost-efficient synthesis method; with special focus on future exploration and large scale applications BT - Herstellung und Charakterisierung von hochwertigen und klar definierten Kohlenstoff-Nanopunkten mit Hilfe einer schnellen, einfachen, und kosteneffizienten Synthesemethode; mit speziellem Fokus auf ihre zukünftige Erforschung und breite Anwendung N2 - Carbon nanodots (CNDs) have generated considerable attention due to their promising properties, e.g. high water solubility, chemical inertness, resistance to photobleaching, high biocompatibility and ease of functionalization. These properties render them ideal for a wide range of functions, e.g. electrochemical applications, waste water treatment, (photo)catalysis, bio-imaging and bio-technology, as well as chemical sensing, and optoelectronic devices like LEDs. In particular, the ability to prepare CNDs from a wide range of accessible organic materials makes them a potential alternative for conventional organic dyes and semiconductor quantum dots (QDs) in various applications. However, current synthesis methods are typically expensive and depend on complex and time-consuming processes or severe synthesis conditions and toxic chemicals. One way to reduce overall preparation costs is the use of biological waste as starting material. Hence, natural carbon sources such as pomelo peal, egg white and egg yolk, orange juice, and even eggshells, to name a few; have been used for the preparation of CNDs. While the use of waste is desirable, especially to avoid competition with essential food production, most starting-materials lack the essential purity and structural homogeneity to obtain homogeneous carbon dots. Furthermore, most synthesis approaches reported to date require extensive purification steps and have resulted in carbon dots with heterogeneous photoluminescent properties and indefinite composition. For this reason, among others, the relationship between CND structure (e.g. size, edge shape, functional groups and overall composition) and photophysical properties is yet not fully understood. This is particularly true for carbon dots displaying selective luminescence (one of their most intriguing properties), i.e. their PL emission wavelength can be tuned by varying the excitation wavelength. In this work, a new reliable, economic, and environmentally-friendly one-step synthesis is established to obtain CNDs with well-defined and reproducible photoluminescence (PL) properties via the microwave-assisted hydrothermal treatment of starch, carboxylic acids and Tris-EDTA (TE) buffer as carbon- and nitrogen source, respectively. The presented microwave-assisted hydrothermal precursor carbonization (MW-hPC) is characterized by its cost-efficiency, simplicity, short reaction times, low environmental footprint, and high yields of approx. 80% (w/w). Furthermore, only a single synthesis step is necessary to obtain homogeneous water-soluble CNDs with no need for further purification. Depending on starting materials and reaction conditions different types of CNDs have been prepared. The as-prepared CNDs exhibit reproducible, highly homogeneous and favourable PL properties with narrow emission bands (approx. 70nm FWHM), are non-blinking, and are ready to use without need for further purification, modification or surface passivation agents. Furthermore, the CNDs are comparatively small (approx. 2.0nm to 2.4nm) with narrow size distributions; are stable over a long period of time (at least one year), either in solution or as a dried solid; and maintain their PL properties when re-dispersed in solution. Depending on CND type, the PL quantum yield (PLQY) can be adjusted from as low as 1% to as high as 90%; one of the highest reported PLQY values (for CNDs) so far. An essential part of this work was the utilization of a microwave synthesis reactor, allowing various batch sizes and precise control over reaction temperature and -time, pressure, and heating- and cooling rate, while also being safe to operate at elevated reaction conditions (e.g. 230 ±C and 30 bar). The hereby-achieved high sample throughput allowed, for the first time, the thorough investigation of a wide range of synthesis parameters, providing valuable insight into the CND formation. The influence of carbon- and nitrogen source, precursor concentration and -combination, reaction time and -temperature, batch size, and post-synthesis purification steps were carefully investigated regarding their influence on the optical properties of as-synthesized CNDs. In addition, the change in photophysical properties resulting from the conversion of CND solution into solid and back into the solution was investigated. Remarkably, upon freeze-drying the initial brown CND-solution turns into a non-fluorescent white/slightly yellow to brown solid which recovers PL in aqueous solution. Selected CND samples were also subject to EDX, FTIR, NMR, PL lifetime (TCSPC), particle size (TEM), TGA and XRD analysis. Besides structural characterization, the pH- and excitation dependent PL characteristics (i.e. selective luminescence) were examined; giving inside into the origin of photophysical properties and excitation dependent behaviour of CNDs. The obtained results support the notion that for CNDs the nature of the surface states determines the PL properties and that excitation dependent behaviour is caused by the “Giant Red-Edge Excitation Shift” (GREES). N2 - Kohlenstoff-Nanopunkte (CNDs, engl. carbon nanodots) haben im letzten Jahrzehnt insbesondere durch ihre vielversprechenden Eigenschaften immer mehr an Popularität gewonnen. CNDs zeichnen sich insbesondere durch ihre Wasserlöslichkeit, hohe chemische Stabilität, Biokompatibilität, hohe Resistenz gegen Photobleichen, und die Möglichkeit zur Oberflächenfunktionalisierung aus. Diese Eigenschaften machen sie somit ideal für eine breite Palette von Anwendungen: z.B. Abwasserbehandlung, (Foto-) Katalyse, Bioimaging und Biotechnologie, chemische Sensorik, sowie elektrochemische- und optoelektronische Anwendungen (z.B. LEDs). Insbesondere die Möglichkeit, CNDs aus einer Vielzahl organischer Materialien herzustellen, machen sie zu einer möglichen Alternative für herkömmliche organische Farbstoffe und Halbleiter-Quantenpunkte (QDs). Derzeitigen Synthesestrategien erweisen sich jedoch häufig als teuer, komplex und zeitaufwändig; bzw. benötigen toxischen Chemikalien und/oder drastische Reaktionsbedingungen. Eine Möglichkeit, die Herstellungskosten von CNDs zu reduzieren, ist die Verwendung von biologischem Abfall als Ausgangsmaterial. So wurden bereits eine Vielzahl an natürlichen Kohlenstoffquellen, z.B. Pomelo-Schale, Eiweiß und Eigelb, Orangensaft und sogar Eierschalen, für die Darstellung von CNDs verwendet. Während die Verwendung von biologischem Abfall wünschenswert ist, insbesondere um Wettbewerb mit der Nahrungsmittelproduktion zu vermeiden, fehlt den meisten Ausgangsmaterialien jedoch die notwendige Reinheit und strukturelle Homogenität um einheitliche CNDs zu erhalten. So führen bisherige Syntheseansätze oft zu CNDs mit heterogenen photophysikalischen Eigenschaften und unbestimmter Zusammensetzung. Für die Untersuchung des Zusammenhangs zwischen CND Struktur und photophysikalischen Eigenschaften werden aber möglichst homogene und vergleichbare Proben benötigt. In dieser Arbeit wird daher eine neue, zuverlässige, ökonomische und umweltfreundliche Einstufen-Synthese zur Darstellung von CNDs mit klar definierten und reproduzierbaren Photolumineszenz- (PL) -Eigenschaften vorgestellt. Die vorgestellte Methode basiert auf der mikrowellenunterstützten, hydrothermischen Behandlung (MW-hPC, engl. microwaveassisted hydrothermal precursor carbonization) wässriger Lösungen aus Stärke, Carbonsäuren (als Kohlenstoffquelle) und Tris-EDTA (TE) -Puffer (als Stickstoffquelle). Die MW-hPC zeichnet sich insbesondere durch die hohe Reproduzierbarkeit, einfache Handhabung, geringen Reaktionszeiten, geringe Umweltbelastung, Kosteneffizienz und die hohen Ausbeuten von ca. 80% (w/w) aus. Darüber hinaus wird nur ein einziger Syntheseschritt (ohne weitere Aufreinigung) benötigt um homogene, wasserlösliche CNDs zu erhalten. In Abhängig der gewählten Ausgangsmaterialen und Reaktionsbedingungen können verschiedene Typen an CNDs gewonnen werden. Die so gewonnen CNDs sind verhältnismäßig klein (ca. 2.0nm- 2.4nm); besitzen eine geringe Größenverteilung, hochgradig homogenen PL-Eigenschaften, und geringen Halbwertsbreiten (FWHM) von ca. 70nm. Darüber hinaus erwiesen sie sich als nicht blinkend; sind langzeitstabil (min. ein Jahr) sowohl in Lösung als auch als Feststoff; und sind direkt gebrauchsfertig, d.h. benötigen keine weitere Aufreinigung oder Oberflächenpassivierung. In Abhängigkeit vom CND-Typ kann die PL-Quantenausbeute zwischen 1% bis 90% betragen; einer der höchsten Werte der je (für CNDs) erreicht wurde. Ein wesentlicher Bestandteil dieser Arbeit war die Verwendung eines Mikrowellensynthese- Reaktors (MiWR) und die damit einhergehende präzise Kontrolle über die Reaktionstemperatur und -zeit, den Druck, und die Heiz- und Abkühlgeschwindigkeit. Des Weiteren ermöglichte der MiWR unterschiedliche Ansatzgrößen und das sichere Arbeiten bei erhöhten Reaktionsbedingungen (z.B. 230 ±C und 30 bar). Der hierdurch erreichte hohe Probendurchsatz ermöglichte somit erstmals die sorgfältige Untersuchung einer Vielzahl an Syntheseparametern hinsichtlich ihres Einflusses auf die photophysikalischen Eigenschaften der dargestellten CNDs. Die untersuchten Parameter reichen hierbei von der Reaktionstemperatur und -zeit über die Edukt-Konzentration und -Kombination (Kohlenstoff- und Stickstoffquelle) bis hin zur Ansatzgröße. Bemerkenswerterweise, und unabhängig vom CND-Typ, transformieren die ursprünglich braunen CND-Lösungen während der Trocknung zu einem nicht fluoreszierenden, weißen/leicht gelblich bis bräunlichen Feststoff; und regenerieren ihre photophysikalischen Eigenschaften verlustfrei in wässriger Lösung. Im Rahmen dieser Arbeit wurden ausgewählte CND-Proben der EDX-, FTIR-, NMR-, TCSPC-, Partikelgrößen (TEM)-, TGA- und XRD-Analyse unterzogen. Die hierbei gewonnenen Erkenntnisse stützen die Theorie, dass die photophysikalischen Eigenschaften der CNDs durch ihre Oberflächenzustände bestimmt werden und dass die s.g. ”Riesen-Rotkanten-Anregungsverschiebung” (GREES, engl. Giant Red Edge Excitation Shift) eine mögliche Ursache für die häufig beobachtete Anregungswellenlängenabhängigkeit der Emissionswellenlänge (bzw. selektive Lumineszenz) in CNDs ist. KW - carbon dots KW - carbon nanodots KW - fluorescence KW - high quantum yield KW - microwave synthesis KW - white carbon KW - Kohlenstoff-Punkte KW - Kohlenstoff-Nanopunkte KW - Fluoreszenz KW - hohe Quantenausbeute KW - mikrowellengestützte Synthese KW - weißer Kohlenstoff Y1 - 2017 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-410160 ER - TY - THES A1 - Bhattacharryya, Saroj Kumar T1 - Development of detector for analytical ultracentrifuge. - [korr. Fassung] T1 - Detektor-Entwicklung für die analytische Ultrazentrifuge. - [korr. Fassung] N2 - In this work approaches for new detection system development for an Analytical Ultracentrifuge (AUC) were explored. Unlike its counterpart in chromatography fractionation techniques, the use of a Multidetection system for AUC has not yet been implemented to full extent despite its potential benefit. In this study we tried to couple existing fundamental spectroscopic and scattering techniques that are used in day to day science as tool for extracting analyte information. Trials were performed for adapting Raman, Light scattering and UV/Vis (with possibility to work with the whole range of wavelengths) to AUC. Conclusions were drawn for Raman and Light scattering to be a possible detection system for AUC, while the development for a fast fiber optics based multiwavelength detector was completed. The multiwavelength detector demonstrated the capability of data generation matching the literature and reference measurement data and faster data collection than that of the commercial instrument. It became obvious that with the generation of data in 3-D space in the UV/Vis detection system, the user can select the wavelength for the evaluation of experimental results as the data set contains the whole range of information from UV/Vis wavelength. The detector showed the data generation with much faster speed unlike the commercial instruments. The advantage of fast data generation was exemplified with the evaluation of data for a mixture of three colloids. These data were in conformity with measurement results from normal radial experiments and without significant diffusion broadening. Thus conclusions were drawn that with our designed Multiwavelength detector, meaningful data in 3-D space can be collected with much faster speed of data generation. N2 - In der vorliegenden Arbeit wurde die Entwicklung neuer Detektoren für die Analytische Ultrazentrifugation (AUZ) untersucht und vorangetrieben. Im Gegensatz zu chromatgraphischen. Fraktionierungsmethoden werden Multidetektionssysteme bis heute nicht in der AUZ eingesetzt. Hier wird die Möglichkeit geprüft, bekannte spektroskopische sowie Streumethoden simultan zur Probenanalyse in der AUZ einzusetzen mit dem Ziel, simultan komplimentäre Informationen über die Probe zu erhalten. So wurde versucht, Raman- und UV/VIS-Spektroskopie (letztere mit der Möglichkeit, das gesamte Wellenlängenspektrum auszunutzen) und statische Lichtstreuung zu kombinieren, um das Analytverhalten während des Ultrazentrifugationsexperimentes zu untersuchen. Es wurden zum einen die Ramanspektroskopie als Detektionssystem für chemische Funktionalität in der AUZ geprüft und zum anderen gezeigt, daß die statische Kleinwinkel Lichtstreuung als direkter Molmassendetektor für den Einsatz in der AUZ geeignet erscheint. Zum anderen wurde die Entwicklung eines Multi-Wellenlängen-UV/VIS-Detektors abgeschlossen, um seine Eignung für den Einsatz in der AUZ und die damit verbundene Möglichkeiten der schnelleren und umfassenderen Datenerzeugung gegenüber kommerziellen Geräten zu zeigen. Dieser Multiwellendetektor liefert anstelle eines Absorptionswertes für jede radiale Position in der Messzelle direkt ein ganzes UV-Vis Spektrum und erzeugt eine zusaetzliche Dimension der Messdaten, was die Möglichkeiten der Analyse von komplexen Systemen mit multiplen Chromophoren, Teilchengrößenbestimmung über Wellenlängenabhängigkeit der Trübung oder auch der Datenmittelung enorm vergrößert. Desweiteren erlaubt der Detektor die Anwendung von Geschwindigkeitsprofilen zur Analyse extrem polydisperser Systeme. Die Entwicklung des Detektors beruht auf einem auf Linsen basierenden System mit modularem Aufbau. Dabei war die sorgfältige Ausrichtung des optischen Systems ein essentieller Punkt, um seine Eignung zu überprüfen zu können. An einer Mischung von drei Kolloiden, Halbleiternanopartikeln sowie Proteinen und deren Mischungen ist es hier gelungen, die erfolgreiche Entwicklung des UV/VIS-Detektors zu demonstrieren: Die Daten konnten schneller und mit wesentlich mehr Informationsgehalt, als auf allen kommerziellen Geräten generiert werden. Die Sedimentationskoeffizientenverteilungen stimmen dabei mit denen aus herkömmlichen Sedimentationsgeschwindigkeitsexperimenten überein, unterliegen jedoch nicht einer signifikanten diffusionsbedingten Verbreiterung. Es ist in dieser Arbeit somit gelungen, zum einen die Lichtstreuung als aussichtsreiche Methode für ein Detektorsystem in der AUZ aufzuzeigen, und zum anderen einen Multi-Wellenlängen-UV/VIS-Detektor zu entwickeln, der eine Datenerzeugung von bislang noch nicht erreichter Schnelligkeit im dreidimensionalen Raum ermöglicht. KW - Ultrazentrifuge KW - Detektor KW - Detektor-Entwicklung KW - SLS KW - UV/VIS KW - Raman KW - detector development KW - SLS KW - UV/VIS KW - Raman Y1 - 2006 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-8215 ER - TY - THES A1 - Dippel, Sandor T1 - Development of functional hydrogels for sensor applications T1 - Entwicklung funktionalisierter Hydrogele für Sensor Anwendungen N2 - In this work, a sensor system based on thermoresponsive materials is developed by utilizing a modular approach. By synthesizing three different key monomers containing either a carboxyl, alkene or alkyne end group connected with a spacer to the methacrylic polymerizable unit, a flexible copolymerization strategy has been set up with oligo ethylene glycol methacrylates. This allows to tune the lower critical solution temperature (LCST) of the polymers in aqueous media. The molar masses are variable thanks to the excurse taken in polymerization in ionic liquids thus stretching molar masses from 25 to over 1000 kDa. The systems that were shown shown to be effective in aqueous solution could be immobilized on surfaces by copolymerizing photo crosslinkable units. The immobilized systems were formulated to give different layer thicknesses, swelling ratios and mesh sizes depending on the demand of the coupling reaction. The coupling of detector units or model molecules is approached via reactions of the click chemistry pool, and the reactions are evaluated on their efficiency under those aspects, too. These coupling reactions are followed by surface plasmon resonance spectroscopy (SPR) to judge efficiency. With these tools at hand, Salmonella saccharides could be selectively detected by SPR. Influenza viruses were detected in solution by turbidimetry in solution as well as by a copolymerized solvatochromic dye to track binding via the changes of the polymers’ fluorescence by said binding event. This effect could also be achieved by utilizing the thermoresponsive behavior. Another demonstrator consists of the detection system bound to a quartz surface, thus allowing the virus detection on a solid carrier. The experiments show the great potential of combining the concepts of thermoresponsive materials and click chemistry to develop technically simple sensors for large biomolecules and viruses. N2 - Diese Arbeit befasst sich mit der Entwicklung von Sensorsystemen für biologische Analyten wie Bakterien und Viren. Die Sensoren beruhen auf thermoresponsiven Polymeren und die Entwicklung wird Schritt für Schritt ausgehend von der Monomersynthese dargelegt. Die Grundidee ist es alle Einzelschritte so modular wie möglich zu halten. Die Kopplungseinheiten für die späteren Erkennungsgruppen bestehen aus Carboxyl, Alken und Alkinfunktionalitäten, die zuerst mit einem Ethylenglycolspacer mit variabler Länge verknüpft werden und dann mit der polymerisierbaren Methylmethacrylatgruppe versehen werden. Diese koppelbaren Monomere werden mit Di- oder (Oligoethylenglycol)methacrylaten copolymerisiert. Je nach Verhältnis ist so auch die untere kritische Entmischungstemperatur (LCST) einstellbar. Mit der Erweiterung der Polymerisationstechnik um ionische Flüssigkeiten als Lösemittel lassen sich Molmassen von 25 bis über 1000 kDa einstellen. Um die Polymere funktionell zu erweitern, lassen sich auch benzophenonhaltige Monomere zur Vernetzung oder Immobilisierung copolymerisieren. Naphthalsäureimidhaltige Monomere wiederum dienen als Signaleinheit, da sie durch Verändern der Polarität ihrer Umgebung solvatochrom reagieren. Durch Aufschleudern und UV-Vernetzen lassen sich Gelschichten mit guter Schichtdickenkontrolle herstellen. Dabei sind die Substrate nur auf den jeweiligen Zweck beschränkt. Dank des Baukastenprinzips kann auch die Maschenweite oder der Quellgrad der Gele eingestellt werden. Die Polymere oder Hydrogele werden mit Hilfe von effizienten Reaktionen swe sogenannten „Click Chemie“ umgesetzt und die Reaktionen werden durchleuchtet, ob sie diesen Ansprüchen gerecht werden. Je nach Möglichkeit wird das Anknüpfen mittels Oberflächenplasmonenresonanzspektroskopie(SPR) verfolgt, so wie zum Beispiel die Kopplung eines Phagen-Oberflächenproteins und das selektive Binden eines Membransaccharids des Salmonellen Bakteriums. Influenza Viren werden selektiv mit Hilfe eines Erkennungspeptids gebunden und mit Hilfe von Trübungsspektroskopie bzw. dem thermoresponsiven Verhalten des Trägerpolymers nachgewiesen. Ein weiterer dargelegter Ansatz ist das Nachweisen von geringen Virenkonzentrationen mit Hilfe eines Hydrogels oder von Polymeren in Lösung, die jeweils mit einem solvatochromen Farbstoff ausgestattet sind, der auf die Umgebungsänderung durch den Virus reagiert. Die Experimente zeigen das große Potential von geschickt kombinierten thermoresponsiven Materialien, die mittels Funktionalisierung durch Click-Chemie zu technisch einfachen Nachweissystemen für Biomoleküle und sogar ganze Zellen entwickelt werden können. KW - biosensors KW - polymer synthesis KW - lower critical solution temperature KW - surface modification KW - smart materials KW - Biosensoren KW - Polymersynthese KW - untere kritische Entmischungstemperatur KW - schaltbare Materialien Y1 - 2017 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-398252 ER - TY - THES A1 - Karabudak, Engin T1 - Development of MWL-AUC / CCD-C-AUC / SLS-AUC detectors for the analytical ultracentrifuge T1 - Entwicklung von MWL-AUC / CCD-C-AUC / SLS-AUC-Detektoren für die analytische Ultrazentrifuge N2 - Analytical ultracentrifugation (AUC) has made an important contribution to polymer and particle characterization since its invention by Svedberg (Svedberg and Nichols 1923; Svedberg and Pederson 1940) in 1923. In 1926, Svedberg won the Nobel price for his scientific work on disperse systems including work with AUC. The first important discovery performed with AUC was to show the existence of macromolecules. Since that time AUC has become an important tool to study polymers in biophysics and biochemistry. AUC is an absolute technique that does not need any standard. Molar masses between 200 and 1014 g/mol and particle size between 1 and 5000 nm can be detected by AUC. Sample can be fractionated into its components due to its molar mass, particle size, structure or density without any stationary phase requirement as it is the case in chromatographic techniques. This very property of AUC earns it an important status in the analysis of polymers and particles. The distribution of molar mass, particle sizes and densities can be measured with the fractionation. Different types of experiments can give complementary physicochemical parameters. For example, sedimentation equilibrium experiments can lead to the study of pure thermodynamics. For complex mixtures, AUC is the main method that can analyze the system. Interactions between molecules can be studied at different concentrations without destroying the chemical equilibrium (Kim et al. 1977). Biologically relevant weak interactions can also be monitored (K ≈ 10-100 M-1). An analytical ultracentrifuge experiment can yield the following information: • Molecular weight of the sample • Number of the components in the sample if the sample is not a single component • Homogeneity of the sample • Molecular weight distribution if the sample is not a single component • Size and shape of macromolecules & particles • Aggregation & interaction of macromolecules • Conformational changes of macromolecules • Sedimentation coefficient and density distribution Such an extremely wide application area of AUC allows the investigation of all samples consisting of a solvent and a dispersed or dissolved substance including gels, micro gels, dispersions, emulsions and solutions. Another fact is that solvent or pH limitation does not exist for this method. A lot of new application areas are still flourishing, although the technique is 80 years old. In 1970s, 1500 AUC were operational throughout the world. At those times, due to the limitation in detection technologies, experimental results were obtained with photographic records. As time passed, faster techniques such as size exclusion chromatography (SEC), light scattering (LS) or SDS-gel electrophoresis occupied the same research fields with AUC. Due to these relatively new techniques, AUC began to loose its importance. In the 1980s, only a few AUC were in use throughout the world. In the beginning of the 1990s a modern AUC -the Optima XL-A - was released by Beckman Instruments (Giebeler 1992). The Optima XL-A was equipped with a modern computerized scanning absorption detector. The addition of Rayleigh Interference Optics is introduced which is called XL-I AUC. Furthermore, major development in computers made the analysis easier with the help of new analysis software. Today, about 400 XL-I AUC exist worldwide. It is usually applied in the industry of pharmacy, biopharmacy and polymer companies as well as in academic research fields such as biochemistry, biophysics, molecular biology and material science. About 350 core scientific publications which use analytical ultracentrifugation are published every year (source: SciFinder 2008 ) with an increasing number of references (436 reference in 2008). A tremendous progress has been made in method and analysis software after digitalization of experimental data with the release of XL-I. In comparison to the previous decade, data analysis became more efficient and reliable. Today, AUC labs can routinely use sophisticated data analysis methods for determination of sedimentation coefficient distributions (Demeler and van Holde 2004; Schuck 2000; Stafford 1992), molar mass distributions (Brookes and Demeler 2008; Brookes et al. 2006; Brown and Schuck 2006), interaction constants (Cao and Demeler 2008; Schuck 1998; Stafford and Sherwood 2004), particle size distributions with Angstrom resolution (Cölfen and Pauck 1997) and the simulations determination of size and shape distributions from sedimentation velocity experiments (Brookes and Demeler 2005; Brookes et al. 2006). These methods are also available in powerful software packages that combines various methods, such as, Ultrascan (Demeler 2005), Sedift/Sedphat (Schuck 1998; Vistica et al. 2004) and Sedanal (Stafford and Sherwood 2004). All these powerful packages are free of charge. Furthermore, Ultrascans source code is licensed under the GNU Public License (http://www.gnu.org/copyleft/gpl.html). Thus, Ultrascan can be further improved by any research group. Workshops are organized to support these software packages. Despite of the tremendous developments in data analysis, hardware for the system has not developed much. Although there are various user developed detectors in research laboratories, they are not commercially available. Since 1992, only one new optical system called “the fluorescence optics” (Schmidt and Reisner, 1992, MacGregor et al. 2004, MacGregor, 2006, Laue and Kroe, in press) has been commercialized. However, except that, there has been no commercially available improvement in the optical system. The interesting fact about the current hardware of the XL-I is that it is 20 years old, although there has been an enormous development in microelectronics, software and in optical systems in the last 20 years, which could be utilized for improved detectors. As examples of user developed detector, Bhattacharyya (Bhattacharyya 2006) described a Multiwavelength-Analytical Ultracentrifuge (MWL-AUC), a Raman detector and a small angle laser light scattering detector in his PhD thesis. MWL-AUC became operational, but a very high noise level prevented to work with real samples. Tests with the Raman detector were not successful due to the low light intensity and thus high integration time is required. The small angle laser light scattering detector could only detect latex particles but failed to detect smaller particles and molecules due to low sensitivity of the detector (a photodiode was used as detector). The primary motivation of this work is to construct a detector which can measure new physico-chemical properties with AUC with a nicely fractionated sample in the cell. The final goal is to obtain a multiwavelength detector for the AUC that measures complementary quantities. Instrument development is an option for a scientist only when there is a huge potential benefit but there is no available commercial enterprise developing appropriate equipment, or if there is not enough financial support to buy it. The first case was our motivation for developing detectors for AUC. Our aim is to use today’s technological advances in microelectronics, programming, mechanics in order to develop new detectors for AUC and improve the existing MWL detector to routine operation mode. The project has multiple aspects which can be listed as mechanical, electronical, optical, software, hardware, chemical, industrial and biological. Hence, by its nature it is a multidisciplinary project. Again by its nature it contains the structural problem of its kind; the problem of determining the exact discipline to follow at each new step. It comprises the risk of becoming lost in some direction. Having that fact in mind, we have chosen the simplest possible solution to any optical, mechanical, electronic, software or hardware problem we have encountered and we have always tried to see the overall picture. In this research, we have designed CCD-C-AUC (CCD Camera UV/Vis absorption detector for AUC) and SLS-AUC (Static Light Scattering detector for AUC) and tested them. One of the SLS-AUC designs produced successful test results, but the design could not be brought to the operational stage. However, the operational state Multiwavelength Analytical Ultracentrifuge (MWL-AUC) AUC has been developed which is an important detector in the fields of chemistry, biology and industry. In this thesis, the operational state Multiwavelength Analytical Ultracentrifuge (MWL-AUC) AUC is to be introduced. Consequently, three different applications of MWL-AUC to the aforementioned disciplines shall be presented. First of all, application of MWL-AUC to a biological system which is a mixture of proteins lgG, aldolase and BSA is presented. An application of MWL-AUC to a mass-produced industrial sample (β-carotene gelatin composite particles) which is manufactured by BASF AG, is presented. Finally, it is shown how MWL-AUC will impact on nano-particle science by investigating the quantum size effect of CdTe and its growth mechanism. In this thesis, mainly the relation between new technological developments and detector development for AUC is investigated. Pioneering results are obtained that indicate the possible direction to be followed for the future of AUC. As an example, each MWL-AUC data contains thousands of wavelengths. MWL-AUC data also contains spectral information at each radial point. Data can be separated to its single wavelength files and can be analyzed classically with existing software packages. All the existing software packages including Ultrascan, Sedfit, Sedanal can analyze only single wavelength data, so new extraordinary software developments are needed. As a first attempt, Emre Brookes and Borries Demeler have developed mutliwavelength module in order to analyze the MWL-AUC data. This module analyzes each wavelength separately and independently. We appreciate Emre Brookes and Borries Demeler for their important contribution to the development of the software. Unfortunately, this module requires huge amount of computer power and does not take into account the spectral information during the analysis. New software algorithms are needed which take into account the spectral information and analyze all wavelengths accordingly. We would like also invite the programmers of Ultrascan, Sedfit, Sedanal and the other programs, to develop new algorithms in this direction. N2 - Die analytische Chemie versucht die chemische Zusammensetzung, chemische und physikalische Eigenschaften von biologischen oder künstlichen Materialien zu bestimmen. Mit der Entwicklung deren Methoden können genauere Informationen über die Umweltverschmutzung, das Ozonloch, Proteinfunktionen und Wechselwirkungen im menschlichen Körper erlangt werden. Es sind eine Vielzahl von analytischen Techniken vorhanden, die durch Verbesserungen in der Mikroelektronik, Mechanik, Informatik und Nanotechnologie einer markanten Entwicklung unterworfen wurden. In dieser Arbeit wurde versucht die Detektionskapazität der analytischen Ultrazentrifuge zu erhöhen. Die analytische Ultrazentrifuge (AUZ) ist eine gut bekannte, sehr leistungsstarke Trennungsmethode. AUZ benutzt die Zentrifugalkraft zum Trennen von Stoffen. Die Probe kann für die Messung gelöst oder in einer Flüssigkeit dispergiert werden. Makromoleküle, Proteine und kolloidale Systeme in Lösung können in einer AUZ Zelle zwischen 1000-60000 Rotationen pro Minute zentrifugiert werden, wie beispielsweise in der kommerziellen Beckmann AUZ. Die Rotationsbeschleunigung entspricht 73-262mal der Erdschwerebeschleunigung (= 9.81 m s-2) für eine radiale Position von 6.5 Zentimeter. Diese Kraft ist der Schlüsselfaktor für die Fähigkeit der AUZ sogar kleine Moleküle und Ionen zu trennen. Die Experimente wurden bei kontrollierter Rotationsgeschwindigkeit und Temperatur ausgeführt. Drei verschiedene, neue Detektoren wurden im Rahmen dieser Arbeit konstruiert und getestet. Diese Detektoren haben die analytischen Informationen sehr verbessert. Dies wurde für Proteine, halbleitende Nanopartikel sowie auch für industrielle Produkte gezeigt. KW - Ultrazentrifuge KW - Detektorentwicklung KW - Multi-Wellenlängen KW - Nanopartikel KW - Open Source KW - ultracentrifuge KW - detector development KW - multiwavelength KW - nanoparticles KW - open source Y1 - 2009 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-39921 ER - TY - THES A1 - Matthes, Annika T1 - Die Dehydro-Diels-Alder-Reaktion (DDA-Reaktion) als neue Methode zur Darstellung von Naphthalenophanen T1 - The Dehydro-Diels-Alder reaction (DDA reaction) as new strategy for the development of Naphthalenophanes BT - ein neuer Zugang zu gespannten Ringsystemen und zur asymmetrischen Synthese von Biarylen BT - a new approach for strained ring systems and for the asymmetric synthesis of biaryls N2 - Die Dissertation beschreibt die Herstellung von ringförmigen Verbindungen (Naphthalenophanen) mit Hilfe der Dehydro-Diels-Alder-Reaktion, wobei immer Enantiomerenpaare auftreten. Es wird der diastereoselektive Aufbau von Naphthalenophanen und der enantiomeren reine Aufbau von Biarylen untersucht. Desweiteren werden die physikalischen Eigenschaften der erhaltenen Verbindungen, wie die Phosphoreszenz, Trennbarkeit der entstehenden Enantiomere und die Ringspannung beschrieben. N2 - The dissertation describes the synthesis of cyclic compounds (Naphthalenophanes) using the Dehydro-Diels-Alder reaction. The diastereoselective assembling of Naphthalenophanes and the development of pure enantiomeres were researched. All synthesised products are pairs of enantiomeres. Furthermore the physical properties like the phosphorescence, separability of the enantiomeres and the ring strain energy were specified. KW - Naphthalenophane KW - Biaryle KW - Ringspannung KW - asymmetrische Synthese KW - Rotationsbarriere KW - Naphthalenophanes KW - Biaryles KW - strain energy KW - asymmetric synthesis KW - barrier of rotation energy Y1 - 2013 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-65264 ER - TY - THES A1 - Audörsch, Stephan T1 - Die Synthese von (2Z,4E)-Diencarbonsäureestern und ihre Anwendung in der Totalsynthese von Polyacetylenen T1 - Synthesis of (2Z,4E)-dienoic acid ester and their application in the total synthesis of natural occurring polyacetylenes N2 - Z,E-Diene sind ein häufig auftretendes Strukturmerkmal in Naturstoffen. Aus diesem Grund ist die einfache Darstellung dieser Struktureinheit von großen Interesse in der organischen Chemie. Das erste Ziel der vorliegenden Arbeit war daher die Weiterentwicklung der Ringschlussmetathese-/ baseninduzierten Ringöffnungs-/ Veresterungssequenz (RBRV-Sequenz) zur Synthese von (2Z,4E)-Diencarbonsäureethylestern ausgehend von Butenoaten. Dazu wurde zunächst die RBRV-Sequenz optimiert. Diese aus drei Schritten bestehende Sequenz konnte in einem Eintopf-Verfahren angewendet werden. Die Ringschlussmetathese gelang mit einer Katalysatorbeladung von 1 mol% des GRUBBS-Katalysators der zweiten Generation in Dichlormethan. Für die baseninduzierte Ringöffnung des β,γ-ungesättigten δ Valerolactons wurde NaHMDS verwendet. Die Alkylierung der Carboxylatspezies gelang mit dem MEERWEIN-Reagenz. Die Anwendbarkeit der Sequenz wurde für verschiedene Substrate demonstriert. Die Erweiterung der Methode auf α-substituierte Butenoate unterlag starken Einschränkungen. So konnte der Zugang für α Hydroxyderivate realisiert werden. Bei der Anwendung der RBRV-Sequenz auf die α-substituierten Butenoate wurde festgestellt, dass diese sich nur in moderaten Ausbeuten umsetzen ließen und zudem nicht selektiv zu den (2E,4E)-konfigurierten α-substituierten-Dienestern reagierten. Der Einsatz von Eninen unter den Standardbedingungen der RBRV-Sequenz gelang nicht. Erst nach Modifizierung der Sequenz (höhere Katalysatorbeladung, Wechsel des Lösungsmittels) konnten die [3]Dendralen-Produkte in geringen Ausbeuten erhalten werden. Im zweiten Teil der Arbeit wurde der Einsatz von (2Z,4E)-Diencarbonsäureethylestern in der Totalsynthese von Naturstoffen untersucht. Dazu wurden zunächst die Transformationsmöglichkeiten der Ester geprüft. Es konnte gezeigt werden, dass sich (2Z,4E)-Diencarbonsäureethylester insbesondere zur Synthese von (2Z,4E)-Aldehyden sowie zum Aufbau der (3Z,5E)-Dien-1-in-Struktur eignen. Anhand dieser Ergebnisse wurde im Anschluss die RBRV-Sequenz in der Totalsynthese eingesetzt. Dazu wurde zunächst der (2Z,4E)-Dienester Microsphaerodiolin in seiner ersten Totalsynthese auf drei verschiedene Routen hergestellt. Im Anschluss wurden sechs verschiedene Polyacetylene mit einer (3Z,5E)-Dien-1-in-Einheit hergestellt. Schlüsselschritte in ihrer Synthese waren immer die RBRV-Sequenz zum Aufbau der Z,E-Dien-Einheit, die Transformation des Esters in ein terminales Alkin sowie die CADIOT-CHODKIEWICZ-Kupplung zum Aufbau unsymmetrischer Polyine. Alle sechs Polyacetylene wurden zum ersten Mal in einer Totalsynthese synthetisiert. Drei Polyacetylene wurden ausgehend von (S)-Butantriol enantiomerenrein dargestellt. Anhand ihrer Drehwerte konnte eine Revision der von YAO und Mitarbeitern vorgenommen Zuordnung der Absolutkonfiguration der Naturstoffe vorgenommen werden. N2 - Z,E-Dienes are a common motif in natural products. Therefore their simple preparation is of high interest. The first part of this work focuses on the improvement of the one-pot sequence “RBRV” consisting of three steps: ring closing metathesis, base induced ring opening and esterification of butenoates. This method yields (2Z,4E) dienoic acid esters. As optimized conditions were found the use of Grubbs catalysts 2nd Generation in dichloromethane, NaHMDS as base and Meerwein’s reagent as alkylating agent. The extension of this method on α-substituted butenoates was subject to many restrictions. The synthesis of precursors was realized for α-hydroxy derivates only. Application of these substrates in the RBRV sequence gave the desired products in moderate yield and diminished selectivity. The use of enines was demonstrated as well. For these substrates changes of the conditions were necessary. The products, [3]dendralenes, were obtained in low yield and excellent selectivity. The second part of this thesis focuses on the application of the RBRV-sequence in the total synthesis of natural products with a Z,E-diene unit. For this purpose it was demonstrated how the ester function can be transformed. As result it was shown that especially Z,E-diene-alkynes can be easily synthesized from Z,E-diene esters. Based on these results the RBRV was used in the synthesis of some natural products. These include Microsphaerodiolin, Atractylodemayne A, C and F as well as three other, unnamed, polyacetylenes. All of them have been synthesized for the first time. Three of them were synthesized in enatioselective manner utilizing enantiopure 1,2,4-butane triole as starting material. KW - Polyacetylene KW - Totalsynthese KW - 2Z,4E-Diencarbonsäureester KW - organische Chemie KW - polyacetylenes KW - total synthesis KW - organic chemistry Y1 - 2016 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-92366 ER - TY - THES A1 - Wolf, Gunter T1 - Diffusionsuntersuchungen an (polymer-modifizierten) Mikroemulsionen mittels Feldgradientenimpuls-NMR-Spektroskopie T1 - Diffusion studies in (polymer-modified) microemulsions using pulsed field gradient NMR spectroscopy N2 - Aufgrund des großen Verhältnisses von Oberfläche zu Volumen zeigen Nanopartikel interessante, größenabhängige Eigenschaften, die man im ausgedehnten Festkörper nicht beobachtet. Sie sind daher von großem wissenschaftlichem und technologischem Interesse. Die Herstellung kleinster Partikel ist aus diesem Grund überaus wünschenswert. Dieses Ziel kann mit Hilfe von Mikroemulsionen als Templatphasen bei der Herstellung von Nanopartikeln erreicht werden. Mikroemulsionen sind thermodynamisch stabile, transparente und isotrope Mischungen von Wasser und Öl, die durch einen Emulgator stabilisiert sind. Sie können eine Vielzahl verschiedener Mikrostrukturen bilden. Die Kenntnis der einer Mikroemulsion zugrunde liegenden Struktur und Dynamik ist daher von außerordentlicher Bedeutung, um ein gewähltes System potentiell als Templatphase zur Nanopartikelherstellung einsetzen zu können. In der vorliegenden Arbeit wurden komplexe Mehrkomponentensysteme auf der Basis einer natürlich vorkommenden Sojabohnenlecithin-Mischung, eines gereinigten Lecithins und eines Sulfobetains als Emulgatoren mit Hilfe der diffusionsgewichteten 1H-NMR-Spektroskopie unter Verwendung gepulster Feldgradienten (PFG) in Abhängigkeit des Zusatzes des Polykations Poly-(diallyl-dimethyl-ammoniumchlorid) (PDADMAC) untersucht. Der zentrale Gegenstand dieser Untersuchungen war die strukturelle und dynamische Charakterisierung der verwendeten Mikroemulsionen hinsichtlich ihrer potentiellen Anwendbarkeit als Templatphasen für die Herstellung möglichst kleiner Nanopartikel. Die konzentrations- und zeit-abhängige NMR-Diffusionsmessung stellte sich dabei als hervorragend geeignete und genaue Methode zur Untersuchung der Mikrostruktur und Dynamik in den vorliegenden Systemen heraus. Die beobachtete geschlossene Wasser-in-Öl- (W/O-) Mikrostruktur der Mikroemulsionen zeigt deutlich deren potentielle Anwendbarkeit in der Nanopartikelsynthese. Das Gesamtdiffusionsverhalten des Tensides wird durch variierende Anteile aus der Verschiebung gesamter Aggregate, der Monomerdiffusion im Medium bzw. der medium-vermittelten Oberflächendiffusion bestimmt. Dies resultierte in einigen Fällen in einer anormalen Diffusionscharakteristik. In allen Systemen liegen hydrodynamische und direkte Wechselwirkungen zwischen den Tensidaggregaten vor. Der Zusatz von PDADMAC zu den Mikroemulsionen resultiert in einer Stabilisierung der flüssigen Grenzfläche der Tensidaggregate aufgrund der Adsorption des Polykations auf den entgegengesetzt geladenen Tensidfilm und kann potentiell zu Nanopartikeln mit kleineren Dimensionen und schmaleren Größenverteilungen führen. N2 - Owing to their large surface-to-volume ratio nanoparticles show interesting size-dependent properties that are not observable in bulk materials. Thus, they are of great scientific and technological interest. Thereby, the highly desirable preparation of as small particles as possible might be easily achieved using microemulsions as template phases. Microemulsions are thermodynamically stable, transparent and isotropic mixtures of water and oil stabilized by an emulsifying agent. However, microemulsions may form a great variety of different microstructures. Thus, it is of utmost importance to know the underlying microstructure and microdynamics of a chosen microemulsion system in order to use it as a template phase for nanoparticle formation. In the present study complex multi-component microemulsion systems based on a naturally occurring soybean lecithin mixture, purified lecithin and sulfobetaine as emulsifiers were investigated by diffusion-weighted pulsed field gradient (PFG) 1H NMR spectroscopy in the presence and absence of the polycation poly-(diallyldimethylammonium chloride) (PDADMAC). The central topic of this study was to structurally and dynamically characterize the present microemulsions with respect to their potential use in nanoparticle formation. The concentration- and time-dependent NMR diffusion measurements turned out to be a suitable and accurate tool to investigate the microstructure and microdynamics of the systems under investigation. They reveal closed water-in-oil (W/O) microemulsion microstructures which prove the potential suitability of the respective systems as template phases for the preparation of nano-sized particles. The overall diffusion behavior of surfactants were found to be governed by varying contributions from displacements of entire aggregates, monomer diffusion in the medium and bulk-mediated surface diffusion, respectively. In some cases this led to a marked anomalous diffusion characteristics. In all systems interactions between aggregates are dominated by hydrodynamic and direct forces. The addition of PDADMAC to the microemulsion systems results in a stabilization of the liquid interface of surfactant aggregates due to the adsorption of the polycation at the oppositely charged surfactant film and may potentially lead to nanoparticles of smaller dimensions and narrower size distributions. KW - Mikroemulsion KW - Mikrostruktur KW - Magnetische Kernresonanz KW - PFG-NMR-Spektroskopie KW - Selbstdiffusion KW - Anomale Diffusion KW - Polykation KW - Inverse Micelle KW - Wasser-in-Öl-Mikroemulsion KW - Tensiddynamik KW - medium-vermittelte Oberflächendiffusion KW - Levy-Bewegung KW - water-in-oil microemulsion KW - surfactant dynamics KW - bulk-mediated surface diffusion KW - Levy walk Y1 - 2005 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-6259 ER - TY - THES A1 - Bäckemo, Johan Dag Valentin T1 - Digital tools and bioinspiration for the implementation in science and medicine T1 - Digitale Werkzeuge und Bioinspiration für die Umsetzung in der Wissenschaft und der Medizin N2 - Diese Doktorarbeit untersucht anhand dreier Beispiele, wie digitale Werkzeuge wie Programmierung, Modellierung, 3D-Konstruktions-Werkzeuge und additive Fertigung in Verbindung mit einer auf Biomimetik basierenden Design\-strategie zu neuen Analysemethoden und Produkten führen können, die in Wissenschaft und Medizin Anwendung finden. Das Verfahren der Funkenerosion (EDM) wird häufig angewandt, um harte Metalle zu verformen oder zu formen, die mit normalen Maschinen nur schwer zu bearbeiten sind. In dieser Arbeit wird eine neuartige Krümmungsanalysemethode als Alternative zur Rauheitsanalyse vorgestellt. Um besser zu verstehen, wie sich die Oberfläche während der Bearbeitungszeit des EDM-Prozesses verändert, wurde außerdem ein digitales Schlagmodell erstellt, das auf einem ursprünglich flachen Substrat Krater auf Erhebungen erzeugte. Es wurde festgestellt, dass ein Substrat bei etwa 10.000 Stößen ein Gleichgewicht erreicht. Die vorgeschlagene Krümmungsanalysemethode hat das Potenzial, bei der Entwicklung neuer Zellkultursubstrate für die Stammzellenforschung eingesetzt zu werden. Zwei Arten, die in dieser Arbeit aufgrund ihrer interessanten Mechanismen analysiert wurden, sind die Venusfliegenfalle und der Bandwurm. Die Venusfliegenfalle kann ihr Maul mit einer erstaunlichen Geschwindigkeit schließen. Der Schließmechanismus kann für die Wissenschaft interessant sein und ist ein Beispiel für ein so genanntes mechanisch bi-stabiles System - es gibt zwei stabile Zustände. Der Bandwurm ist bei Säugetieren meist im unteren Darm zu finden und heftet sich mit seinen Saugnäpfen an die Darmwände. Wenn der Bandwurm eine geeignete Stelle gefunden hat, stößt er seine Haken aus und heftet sich dauerhaft an die Wand. Diese Funktion könnte in der minimalinvasiven Medizin genutzt werden, um eine bessere Kontrolle der Implantate während des Implantationsprozesses zu ermöglichen. Für beide Projekte wurde ein mathematisches Modell, das so genannte Chained Beam Constraint Model (CBCM), verwendet, um das nichtlineare Biegeverhalten zu modellieren und somit vorherzusagen, welche Strukturen ein mechanisch bi-stabiles Verhalten aufweisen könnten. Daraufhin konnten zwei Prototypen mit einem 3D-Drucker gedruckt und durch Experimente veranschaulicht werden, dass sie beide ein bi-stabiles Verhalten aufweisen. Diese Arbeit verdeutlicht das hohe Anwendungspotenzial für neue Analysenmethoden in der Wissenschaft und für neue Medizinprodukte in der minimalinvasiven Medizin. N2 - Biomimicry is the art of mimicking nature to overcome a particular technical or scientific challenge. The approach studies how evolution has found solutions to the most complex problems in nature. This makes it a powerful method for science. In combination with the rapid development of manufacturing and information technologies into the digital age, structures and material that were before thought to be unrealizable can now be created with simple sketch and the touch of a button. This doctoral thesis had as its primary goal to investigate how digital tools, such as programming, modelling, 3D-Design tools and 3D-Printing, with the help from biomimicry, could lead to new analysis methods in science and new medical devices in medicine. The Electrical Discharge Machining (EDM) process is applied commonly to deform or mold hard metals that are difficult to work using normal machinery. A workpiece submerged in an electrolyte is deformed while being in close vicinity to an electrode. When high voltage is put between the workpiece and the electrode it will cause sparks that create cavitations on the substrate which in turn removes material and is flushed away by the electrolyte. Usually, such surfaces are analysed based on roughness, in this work another method using a novel curvature analysis method is presented as an alternative. In addition, to better understand how the surface changes during process time of the EDM process, a digital impact model was created which created craters on ridges on an originally flat substrate. These substrates were then analysed using the curvature analysis method at different processing times of the modelling. It was found that a substrate reaches an equilibrium at around 10000 impacts. The proposed curvature analysis method has potential to be used in the design of new cell culture substrates for stem cell. The Venus flytrap can shut its jaws at an amazing speed. The shutting mechanism may be interesting to use in science and is an example of a so-called mechanical bi-stable system – there are two stable states. In this work two truncated pyramid structures were modelled using a non-linear mechanical model called the Chained Beam Constraint Model (CBCM). The structure with a slope angle of 30 degrees is not bi-stable and the structure with a slope angle of 45 degrees is bi-stable. Developing this idea further by using PEVA, which has a shape-memory effect, the structure which is not bi-stable could be programmed to be bi-stable and then turned off again. This could be used as an energy storage system. Another species which has interesting mechanism is the tapeworm. Some species of this animal has a crown of hooks and suckers located on its side. The parasite commonly is found in mammals in the lower intestine and attaches to the walls by using its suckers. When the tapeworm has found a suitable spot, it ejects its hooks and permanently attaches to the wall. This function could be used in minimally invasive medicine to have better control of implants during the implantation process. By using the CBCM model and a 3D-printer capable of tuning how hard or soft a printed part is, a design strategy was developed to investigate how one could create a device that mimics the tapeworm. In the end a prototype was created which was able attach to a pork loin at an under pressure of 20 kPa and to ejects its hooks at an under pressure of 50 kPa or above. These three projects is an exhibit of how digital tools and biomimicry can be used together to come up with applicable solutions in science and in medicine. KW - bioinspiration KW - non-linear mechanics KW - modelling KW - shape-memory KW - additive manufacturing KW - Bioinspiration KW - nichtlineare Mechanik KW - Modellierung KW - Formgedächtnis KW - additive Fertigung Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-571458 ER - TY - THES A1 - Chandrakanth Shetty, Sunidhi T1 - Directed chemical communication in artificial eukaryotic cells T1 - Gezielte chemische Kommunikation in künstlichen eukaryotischen Zellen N2 - Eukaryotic cells can be regarded as complex microreactors capable of performing various biochemical reactions in parallel which are necessary to sustain life. An essential prerequisite for these complex metabolic reactions to occur is the evolution of lipid membrane-bound organelles enabling compartmental- ization of reactions and biomolecules. This allows for a spatiotemporal control over the metabolic reactions within the cellular system. Intracellular organi- zation arising due to compartmentalization is a key feature of all living cells and has inspired synthetic biologists to engineer such systems with bottom-up approaches. Artificial cells provide an ideal platform to isolate and study specific re- actions without the interference from the complex network of biomolecules present in biological cells. To mimic the hierarchical architecture of eukaryotic cells, multi-compartment assemblies with nested liposomal structures also re- ferred to as multi-vesicular vesicles (MVVs) have been widely adopted. Most of the previously reported multi-compartment systems adopt bulk method- ologies which suffer from low yield and poor control over size. Microfluidic strategies help circumvent these issues and facilitate a high-throughput and robust technique to assemble MVVs of uniform size distribution. In this thesis, firstly, the bulk methodologies are explored to build MVVs and implement a synthetic signalling cascade. Next, a polydimethylsiloxane (PDMS)-based microfluidic platform is introduced to build MVVs and the significance of PEGylated lipids for the successful encapsulation of inner com- partments to generate stable multi-compartment systems is highlighted. Next, a novel two-inlet channel PDMS-based microfluidic device to create MVVs encompassing a three-step enzymatic reaction cascade is presented. A directed reaction pathway comprising of the enzymes α-glucosidase (α-Glc), glucose oxidase (GOx), and horseradish peroxidase (HRP) spanning across three compartments via reconstitution of size-selective membrane proteins is described. Furthermore, owing to the monodispersity of our MVVs due to microfluidic strategies, this platform is employed to study the effect of com- partmentalization on reaction kinetics. Further integration of cell-free expression module into the MVVs would allow for gene-mediated signal transduction within artificial eukaryotic cells. Therefore, the chemically inducible cell-free expression of a membrane protein alpha-hemolysin and its further reconstitution into liposomes is carried out. In conclusion, the present thesis aims to build artificial eukaryotic cells to achieve size-selective chemical communication that also show potential for applications as micro reactors and as vehicles for drug delivery. N2 - Eukaryontische Zellen können als komplexe Mikroreaktoren betrachtet werden, die in der Lage sind, verschiedene biochemische Reaktionen parallel durchzuführen, die für die Aufrechterhaltung des Lebens notwendig sind. Eine wesentliche Voraussetzung für die Durchführung dieser komplexen Stoffwechselreaktionen ist die Entwicklung von Organellen mit Lipidmembranen, die eine Kompartimentierung von Reaktionen und Biomolekülen ermöglichen. Dies ermöglicht eine räumlich-zeitliche Kontrolle über die Stoffwechselreaktionen innerhalb des zellulären Systems. Die durch die Kompartimentierung entstehende intrazelluläre Organisation ist ein Schlüsselmerkmal aller lebenden Zellen und hat synthetische Biologen dazu inspiriert, solche Systeme mit Bottom-up-Ansätzen zu entwickeln. Künstliche Zellen bieten eine ideale Plattform, um spezifische Reaktionen zu isolieren und zu untersuchen, ohne dass das komplexe Netzwerk von Biomolekülen, das in biologischen Zellen vorhanden ist, stört. Um die hierarchische Architektur eukaryontischer Zellen zu imitieren, haben sich Multikompartiment-Anordnungen mit verschachtelten liposomalen Strukturen, die auch als multivesikuläre Vesikel (MVV) bezeichnet werden, durchgesetzt. Die meisten der bisher vorgestellten Multikompartiment-Systeme basieren auf Bulk-Methoden, die eine geringe Ausbeute und eine schlechte Kontrolle über die Größe aufweisen. Mikrofluidische Strategien helfen, diese Probleme zu umgehen und ermöglichen eine robuste Technik mit hohem Durchsatz, um MVVs mit einheitlicher Größenverteilung herzustellen. In dieser Dissertation werden zunächst die Bulk-Methoden zum Aufbau von MVVs und zur Implementierung einer synthetischen Signalkaskade untersucht. Anschließend wird eine auf Polydimethylsiloxan (PDMS) basierende mikrofluidische Plattform zur Herstellung von MVVs vorgestellt und die Bedeutung von PEGylierten Lipiden für die erfolgreiche Verkapselung der inneren Kompartimente zur Erzeugung stabiler Multikompartiment-Systeme hervorgehoben. Es wird ein neuartiges mikrofluidisches Gerät mit zwei Einlasskanälen auf PDMS-Basis zur Herstellung von MVVs vorgestellt, das eine dreistufige enzymatische Reaktionskaskade umfasst. Es wird ein gerichteter Reaktionsweg beschrieben, der die Enzyme α-Glucosidase (α-Glc), Glucoseoxidase (GOx) und Meerrettichperoxidase (HRP) umfasst und sich über drei Kompartimente erstreckt, die durch die Rekonstitution von größenselektiven Membranproteinen entstehen. Aufgrund der Monodispersität unserer MVVs durch mikrofluidische Strategien nutze ich diese Plattform außerdem, um die Auswirkungen der Kompartimentierung auf die Reaktionskinetik zu untersuchen. Eine weitere Integration von zellfreien Expressionsmodulen in MVVs würde eine genvermittelte Signaltransduktion in künstlichen eukaryotischen Zellen ermöglichen. Daher wird die chemisch induzierbare zellfreie Expression eines Membranproteins alpha-Hämolysin und seine weitere Rekonstitution in Liposomen durchgeführt. Zusammenfassend lässt sich sagen, dass die vorliegende Arbeit darauf abzielt, künstliche eukaryotische Zellen zu bauen, um eine größenselektive chemische Kommunikation zu erreichen, und das Potenzial für Anwendungen als Mikroreaktoren und als Vehikel für die Verabreichung von Medikamenten aufweisen. KW - microfluidics KW - synthetic biology KW - Mikrofluidik KW - synthetische Biologie Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-533642 ER - TY - THES A1 - Mostafa, Amr T1 - DNA origami nanoforks: A platform for cytochrome c single molecule surface enhanced Raman spectroscopy N2 - This thesis presents a comprehensive exploration of the application of DNA origami nanofork antennas (DONAs) in the field of spectroscopy, with a particular focus on the structural analysis of Cytochrome C (CytC) at the single-molecule level. The research encapsulates the design, optimization, and application of DONAs in enhancing the sensitivity and specificity of Raman spectroscopy, thereby offering new insights into protein structures and interactions. The initial phase of the study involved the meticulous optimization of DNA origami structures. This process was pivotal in developing nanoscale tools that could significantly enhance the capabilities of Raman spectroscopy. The optimized DNA origami nanoforks, in both dimer and aggregate forms, demonstrated an enhanced ability to detect and analyze molecular vibrations, contributing to a more nuanced understanding of protein dynamics. A key aspect of this research was the comparative analysis between the dimer and aggregate forms of DONAs. This comparison revealed that while both configurations effectively identified oxidation and spin states of CytC, the aggregate form offered a broader range of detectable molecular states due to its prolonged signal emission and increased number of molecules. This extended duration of signal emission in the aggregates was attributed to the collective hotspot area, enhancing overall signal stability and sensitivity. Furthermore, the study delved into the analysis of the Amide III band using the DONA system. Observations included a transient shift in the Amide III band's frequency, suggesting dynamic alterations in the secondary structure of CytC. These shifts, indicative of transitions between different protein structures, were crucial in understanding the protein’s functional mechanisms and interactions. The research presented in this thesis not only contributes significantly to the field of spectroscopy but also illustrates the potential of interdisciplinary approaches in biosensing. The use of DNA origami-based systems in spectroscopy has opened new avenues for research, offering a detailed and comprehensive understanding of protein structures and interactions. The insights gained from this research are expected to have lasting implications in scientific fields ranging from drug development to the study of complex biochemical pathways. This thesis thus stands as a testament to the power of integrating nanotechnology, biochemistry, and spectroscopic techniques in addressing complex scientific questions. N2 - Diese Dissertation präsentiert eine umfassende Untersuchung der Anwendung von DNA-Origami-Nanogabelantennen (DONAs) im Bereich der Spektroskopie, mit einem besonderen Fokus auf der strukturellen Analyse von Cytochrom C (CytC) auf Einzelmolekülebene. Die Forschung umfasst das Design, die Optimierung und die Anwendung von DONAs zur Steigerung der Sensitivität und Spezifität der Raman-Spektroskopie und bietet somit neue Einblicke in Proteinstrukturen und -interaktionen. Die erste Phase der Studie beinhaltete die sorgfältige Optimierung von DNA-Origami-Strukturen. Dieser Prozess war entscheidend für die Entwicklung von Nanowerkzeugen, die die Fähigkeiten der Raman-Spektroskopie erheblich verbessern könnten. Die optimierten DNA-Origami-Nanogabeln, sowohl in Dimer- als auch in Aggregatform, zeigten eine verbesserte Fähigkeit, molekulare Schwingungen zu detektieren und zu analysieren, was zu einem nuancierteren Verständnis der Proteindynamik beitrug. Ein Schlüsselaspekt dieser Forschung war die vergleichende Analyse zwischen den Dimer- und Aggregatformen von DONAs. Dieser Vergleich zeigte, dass beide Konfigurationen effektiv Oxidations- und Spin-Zustände von CytC identifizieren konnten, wobei die Aggregatform aufgrund ihrer längeren Signalemission und der erhöhten Anzahl von Molekülen ein breiteres Spektrum an detektierbaren molekularen Zuständen bot. Die verlängerte Dauer der Signalemission in den Aggregaten wurde auf den kollektiven Hotspot-Bereich zurückgeführt, der die Gesamtsignalstabilität und -empfindlichkeit erhöhte. Darüber hinaus ging die Studie auf die Analyse der Amid-III-Bande unter Verwendung des DONA-Systems ein. Zu den Beobachtungen gehörte eine vorübergehende Verschiebung der Frequenz der Amid-III-Bande, was auf dynamische Veränderungen in der Sekundärstruktur von CytC hindeutete. Diese Verschiebungen, die auf Übergänge zwischen verschiedenen Proteinstrukturen hindeuteten, waren entscheidend für das Verständnis der funktionellen Mechanismen und Interaktionen des Proteins. Die in dieser Dissertation präsentierte Forschung leistet nicht nur einen bedeutenden Beitrag zum Gebiet der Spektroskopie, sondern veranschaulicht auch das Potenzial interdisziplinärer Ansätze in der Biosensorik. Der Einsatz von DNA-Origami-basierten Systemen in der Spektroskopie hat neue Wege für die Forschung eröffnet und bietet ein detailliertes und umfassendes Verständnis von Proteinstrukturen und -interaktionen. Die aus dieser Forschung gewonnenen Erkenntnisse werden voraussichtlich langfristige Auswirkungen auf wissenschaftliche Bereiche haben, die von der Arzneimittelentwicklung bis hin zur Untersuchung komplexer biochemischer Prozesse reichen. Diese Dissertation steht somit als Zeugnis für die Kraft der Integration von Nanotechnologie, Biochemie und spektroskopischen Techniken bei der Beantwortung komplexer wissenschaftlicher Fragen. KW - DNA origami KW - DNA origami nanoantennas (DONA) KW - SERS KW - Cytochrome C Y1 - 2024 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-635482 ER - TY - THES A1 - Choi, Youngeun T1 - DNA origami structures as versatile platforms for nanophotonics T1 - DNA Origami Struktruen als Vielseitige Plattform für Nanophotonik N2 - Nanophotonics is the field of science and engineering aimed at studying the light-matter interactions on the nanoscale. One of the key aspects in studying such optics at the nanoscale is the ability to assemble the material components in a spatially controlled manner. In this work, DNA origami nanostructures were used to self-assemble dye molecules and DNA coated plasmonic nanoparticles. Optical properties of dye nanoarrays, where the dyes were arranged at distances where they can interact by Förster resonance energy transfer (FRET), were systematically studied according to the size and arrangement of the dyes using fluorescein (FAM) as the donor and cyanine 3 (Cy 3) as the acceptor. The optimized design, based on steady-state and time-resolved fluorometry, was utilized in developing a ratiometric pH sensor with pH-inert coumarin 343 (C343) as the donor and pH-sensitive FAM as the acceptor. This design was further applied in developing a ratiometric toxin sensor, where the donor C343 is unresponsive and FAM is responsive to thioacetamide (TAA) which is a well-known hepatotoxin. The results indicate that the sensitivity of the ratiometric sensor can be improved by simply arranging the dyes into a well-defined array. The ability to assemble multiple fluorophores without dye-dye aggregation also provides a strategy to amplify the signal measured from a fluorescent reporter, and was utilized here to develop a reporter for sensing oligonucleotides. By incorporating target capturing sequences and multiple fluorophores (ATTO 647N dye molecules), a reporter for microbead-based assay for non-amplified target oligonucleotide sensing was developed. Analysis of the assay using VideoScan, a fluorescence microscope-based technology capable of conducting multiplex analysis, showed the DNA origami nanostructure based reporter to have a lower limit of detection than a single stranded DNA reporter. Lastly, plasmonic nanostructures were assembled on DNA origami nanostructures as substrates to study interesting optical behaviors of molecules in the near-field. Specifically, DNA coated gold nanoparticles, silver nanoparticles, and gold nanorods, were placed on the DNA origami nanostructure aiming to study surface-enhanced fluorescence (SEF) and surface-enhanced Raman scattering (SERS) of molecules placed in the hotspot of coupled plasmonic structures. N2 - Nanophotonik bezeichnet die Untersuchung von Licht in Wechselwirkung mit Materie im Nanometermaßstab. Die exakte Kontrolle über den Aufbau und die räumliche Anordnung der beteiligten Komponenten ist ein entscheidender Faktor für die Erforschung der Optik nanoskalierter Systeme. Eine mögliche Lösung bietet die selbstorganisatorische Eigenschaft von DNA-Origami-Nanostrukturen, die im Rahmen dieser Dissertation, insbesondere zur Kopplung verschiedener Farbstoffe bzw. plasmonisch aktiver Nanopartikel, verwendet wurden. Im ersten Teil dieser Dissertation wurden unterschiedliche Förster-Resonanzenergietransfer- (FRET) Farbstoff-Matrizen, bestehend aus Fluorescein (FAM) als FRET-Donor und Cyanine 3 (Cy 3) als FRET-Akzeptor, hergestellt und nachfolgend hinsichtlich des Einflusses ihrer Gesamtgröße und ihrer Anordnung via statischer und zeitaufgelöster Fluoreszenzspektroskopie untersucht. Daraufhin erfolgte die Weiterentwicklung der ermittelten optimalen Anordnung der Farbstoffe in einen ratiometrischen pH-Sensor, bestehend aus dem pH stabilen Coumarin 343 (C343) als FRET-Donor und dem pH sensitiven FAM als FRET-Akzeptor. Die erhaltenen Ergebnisse zeigten, dass sich die Sensitivität ratiometrischer Sensoren, insbesondere durch die wohldefinierte Anordnung der beteiligten Farbstoffe in der Matrize, deutlich steigern lassen. Selbige Anordnung konnte auch erfolgreich zur Entwicklung eines Giftstoffsensors, zum Nachweis des Hepatoxins Thioacetamid (TAA), verwendet werden. Die Möglichkeit der Anordnung mehrerer Farbstoffe, unter Vermeidung ungewollter Farbstoff-Aggregation, ermöglicht außerdem die Verstärkung der Signale sogenannter Fluoreszenzreporter. Dies führte, im Rahmen dieser Arbeit, zur erfolgreichen Entwicklung eines auf Mikroperlen basierenden Oligonukleotid-Sensors, welcher ohne die Notwendigkeit einer vorherigen Zielverstärkung (z.B. durch Polymerase-Kettenreaktion) auskommt. Die anschließende Analyse mittels VideoScan, einer Multiplex-Analyse-Technik basierend auf der Fluoreszenzmikroskopie, ergab deutlich niedrigere Nachweisgrenzen für auf DNA-Origami basierende Reporter im Vergleich zu DNA-Einzelstrang basierenden Reportern. Abschließend erfolgte die Verwendung der DNA-Origamis als Substrat für die präzise räumliche Anordnung verschiedener plasmonisch aktiver Nanopartikel zur Untersuchung des optischen Verhaltens von Zielmolekülen im plasmonischen Nahfeld. Die Untersuchung der oberflächenverstärkten Fluoreszenz (SEF) und oberflächenverstärkten Raman-Streuung (SERS) von Molekülen im plasmonischer Hotspots erfolgte insbesondere mit Fokus auf den Einfluss der unterschiedlichen Anordnung von Gold-Nanostäbchen, Gold-Nanopartikel, und Silber-Nanopartikel. KW - DNA origami KW - Förster resonance energy transfer KW - plasmonics KW - DNA Origami KW - Förster-Resonanzenergietransfer KW - Plasmonik Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-421483 ER - TY - THES A1 - Prinz, Julia T1 - DNA origami substrates as a versatile tool for surface-enhanced Raman scattering (SERS) T1 - DNA Origami-Substrate als ein vielseitiges Werkzeug für die oberflächenverstärkte Raman-Streuung (SERS) N2 - Surface-enhanced Raman scattering (SERS) is a promising tool to obtain rich chemical information about analytes at trace levels. However, in order to perform selective experiments on individual molecules, two fundamental requirements have to be fulfilled. On the one hand, areas with high local field enhancement, so-called “hot spots”, have to be created by positioning the supporting metal surfaces in close proximity to each other. In most cases hot spots are formed in the gap between adjacent metal nanoparticles (NPs). On the other hand, the analyte has to be positioned directly in the hot spot in order to profit from the highest signal amplification. The use of DNA origami substrates provides both, the arrangement of AuNPs with nm precision as well as the ability to bind analyte molecules at predefined positions. Consequently, the present cumulative doctoral thesis aims at the development of a novel SERS substrate based on a DNA origami template. To this end, two DNA-functionalized gold nanoparticles (AuNPs) are attached to one DNA origami substrate resulting in the formation of a AuNP dimer and thus in a hot spot within the corresponding gap. The obtained structures are characterized by correlated atomic force microscopy (AFM) and SERS imaging which allows for the combination of structural and chemical information. Initially, the proof-of principle is presented which demonstrates the potential of the novel approach. It is shown that the Raman signal of 15 nm AuNPs coated with dye-modified DNA (dye: carboxytetramethylrhodamine (TAMRA)) is significantly higher for AuNP dimers arranged on a DNA origami platform in comparison to single AuNPs. Furthermore, by attaching single TAMRA molecules in the hot spot between two 5 nm AuNPs and optimizing the size of the AuNPs by electroless gold deposition, SERS experiments at the few-molecule level are presented. The initially used DNA origami-AuNPs design is further optimized in many respects. On the one hand, larger AuNPs up to a diameter of 60 nm are used which are additionally treated with a silver enhancement solution to obtain Au-Ag-core-shell NPs. On the other hand, the arrangement of both AuNPs is altered to improve the position of the dye molecule within the hot spot as well as to decrease the gap size between the two particles. With the optimized design the detection of single dye molecules (TAMRA and cyanine 3 (Cy3)) by means of SERS is demonstrated. Quantitatively, enhancement factors up to 10^10 are estimated which is sufficiently high to detect single dye molecules. In the second part, the influence of graphene as an additional component of the SERS substrate is investigated. Graphene is a two-dimensional material with an outstanding combination of electronical, mechanical and optical properties. Here, it is demonstrated that single layer graphene (SLG) replicates the shape of underlying non-modified DNA origami substrates very well, which enables the monitoring of structural alterations by AFM imaging. In this way, it is shown that graphene encapsulation significantly increases the structural stability of bare DNA origami substrates towards mechanical force and prolonged exposure to deionized water. Furthermore, SLG is used to cover DNA origami substrates which are functionalized with a 40 nm AuNP dimer. In this way, a novel kind of hybrid material is created which exhibits several advantages compared to the analogue non-covered SERS substrates. First, the fluorescence background of dye molecules that are located in between the AuNP surface and SLG is efficiently reduced. Second, the photobleaching rate of the incorporated dye molecules is decreased up to one order of magnitude. Third, due to the increased photostability of the investigated dye molecules, the performance of polarization-dependent series measurements on individual structures is enabled. This in turn reveals extensive information about the dye molecules in the hot spot as well as about the strain induced within the graphene lattice. Although SLG can significantly influence the SERS substrate in the aforementioned ways, all those effects are strongly related to the extent of contact with the underlying AuNP dimer. N2 - Desoxyribonukleinsäure (engl. deoxyribonucleic acid (DNA)) ist nicht nur Träger der Erbinformation, sondern wird auch seit den frühen 80er Jahren als Gerüstmaterial in der Nanotechnologie verwendet. Im Jahr 2006 wurde die bis dato entwickelte DNA-Nanotechnologie durch die Erfindung der sogenannten DNA Origami-Technik weiter revolutioniert. Diese erlaubt die Konstruktion vielfältiger zwei- und dreidimensionaler Strukturen durch gezielte DNA-Selbstassemblierung. Basierend auf der grundlegenden Watson-Crick Basenpaarung innerhalb eines DNA-Doppelstrangs können die gewünschten Zielstrukturen dabei mit hoher Genauigkeit vorhergesagt werden. Neben der Entwicklung vielfältiger DNA-Konstrukte eignen sich DNA Origami-Substrate zudem hervorragend zur Bindung funktionaler Einheiten mit der Präzision im Bereich von Nanometern. Somit lassen sich beispielsweise Goldnanopartikel (AuNPs) präzise anordnen. Dies ist von höchstem Interesse im Zusammenhang mit der oberflächenverstärkten Ramanstreuung (engl. surface-enhanced Raman scattering (SERS)). SERS basiert darauf, die naturgemäß schwache Ramanstreuung eines Analyten um mehrere Größenordnungen zu verstärken, indem der Analyt nahe einer Metalloberfläche positioniert wird. Die Verstärkung der Ramanstreuung beruht hierbei hauptsächlich auf der Wechselwirkung des Analyten mit dem elektromagnetischen Feld der Metalloberfläche und kann im Zwischenraum zweier benachbarter Metallstrukturen besonders stark ausgeprägt sein. Die vorliegende kumulative Dissertation beschäftigt sich mit der Entwicklung einer DNA Origami-basierten Sensoroberfläche für die Anwendung von SERS-Experimenten. Hierbei werden jeweils zwei AuNPs in gezieltem Abstand an ein DNA Origami-Substrat gebunden und das verstärkte Ramansignal eines Analyten im Zwischenraum des AuNP-Dimers detektiert. Zunächst wird das allgemeine Prinzip in Form eines Wirksamkeitsnachweises vorgestellt, in welchem der Farbstoff Carboxytetramethylrhodamin (TAMRA) als Analyt verwendet wird. Die darauf aufbauenden Experimente zielen auf eine Verringerung der Nachweisgrenze bis hin zur Einzelmoleküldetektion ab. Im Zuge dessen werden vielseitige Optimierungsschritte durchgeführt, die die Größe, die Anordnung sowie die Ummantelung der AuNPs mit einer dünnen Silberschicht betreffen. Es wird gezeigt, dass durch die Optimierung aller Parameter die Detektion einzelner TAMRA- und Cyanin 3 (Cy3)-Moleküle mittels SERS möglich ist. Weiterhin wird Graphen, ein erst im Jahr 2004 entdecktes Material bestehend aus einer einzigen Schicht Kohlenstoffatome, als weiterer Bestandteil der untersuchten Nanostrukturen eingeführt. Graphen zeichnet sich durch eine bislang einzigartige Kombination aus optischen, elektronischen und mechanischen Eigenschaften aus und hat sich daher innerhalb kürzester Zeit zu einem vielfältigen Forschungsschwerpunkt entwickelt. In der vorliegenden Dissertation wird zunächst die erhöhte strukturelle Stabilität von Graphen bedeckten DNA Origami-Substraten im Hinblick auf mechanische Beanspruchung sowie auf die Inkubation in deionisiertem Wasser demonstriert. In weiterführenden Betrachtungen werden auch DNA Origami-Substrate, die mit AuNP-Dimeren funktionalisiert sind, mit Graphen bedeckt, und somit eine neuartige Hybridstruktur erzeugt. Es wird gezeigt, dass Graphen den Fluoreszenzuntergrund der untersuchten Farbstoffmoleküle deutlich reduziert und zusätzlich deren Photostabilität gegenüber der eintreffenden Laserstrahlung effektiv verbessert. KW - DNA origami KW - surface-enhanced Raman scattering KW - DNA nanostructures KW - graphene KW - single-molecule detection KW - DNA Origami KW - oberflächenverstärkte Raman-Streuung KW - DNA Nanostrukturen KW - Graphen KW - Einzelmoleküldetektion Y1 - 2016 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-104089 ER - TY - THES A1 - Kasparova, Pavla T1 - Doppelthydrophile Blockcopolymere als Mineralisationstemplate N2 - Die vorliegende Arbeit beschäftigt sich mit der Synthese und den Eigenschaften von doppelthydrophilen Blockcopolymeren und ihrer Anwendung in einem biomimetischen Mineralisationsprozeß von Calciumcarbonat und Bariumsulfat. Doppelthydrophile Blockcopolymere bestehen aus einem hydrophilen Block, der nicht mit Mineralien wechselwirkt und einem zweiten Polyelektrolyt-Block, der stark mit Mineraloberflächen wechselwirkt. Diese Blockcopolymere wurden durch ringöffnende Polymerisation von N-carboxyanhydriden (NCA′s) und a-methoxy-ω-amino[poly(ethylene glycol)] PEG-NH2 als Initiator hergestellt. Die hergestellten Blockcopolymere wurden als effektive Wachstumsmodifikatoren für die Kristallisation von Calciumcarbonat und Bariumsulfat Mineralien eingesetzt. Die so erhaltenen Mineralpartikel (Kugeln, Hantel, eiförmige Partikel) wurden durch Lichtmikroskopie in Lösung, SEM und TEM charakterisiert. Röntgenweitwinkelstreuung (WAXS) wurde verwendet, um die Modifikation von Calciumcarbonat zu ermitteln und die Größe der Calciumcarbonat- und Bariumsulfat-Nanopartikel zu ermitteln. N2 - This work describes the synthesis and characterization of double hydrophilic block copolymers and their use in a biomimetic mineralization process of Calcium Carbonate and Barium Sulfate. Double hydrophilic block copolymers consist of a hydrophilic block that does not interact with minerals and another hydrophilic polyelectrolyte block that strongly interacts with mineral surfaces. These polymers were synthesised via ring opening polymerisation of N-carboxyanhydride (NCA), and the first hydrophilic block a-methoxy-ω-amino[poly(ethylene glycol)] PEG-NH2 was used as an initiator. The prepared block copolymers were used as effective crystal growth modifiers to control the crystallization of Calcium Carbonate and Barium Sulfate minerals. The resulting mineral particles (spheres, dumbbells, egg-like particles) were characterised by light microscopy in solution, by SEM, and by TEM. X-Ray scattering measurements (WAXS) were used to prove the modification of Calcium Carbonate particles and to calculate the size of Calcium Carbonate and Barium Sulfate nanoparticles. KW - Blockcopolymere ; Polyaminosäuren ; Hydrophile Verbindungen ; Chemische Synthese ; Ringöffnungspolymerisation | Calciumcarbonat ; Biomineralisation KW - Doppelthydrophile Blockcopolymere KW - N-carboxyanhydrid KW - NCA KW - poly(L-Asparaginsäure) KW - poly(L-Glutaminsäure) KW - poly(L-Serin) KW - poly(O-phospho-L-Serin) KW - Ca KW - Double hydrophilic block copolymers KW - N-carboxyanhydride KW - NCA KW - poly(L-aspartic acid) KW - poly(L-glutamic acid) KW - poly(L-serine) KW - poly(O-phospho-L-serine) Y1 - 2002 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-0000483 ER - TY - THES A1 - Won, Jooyoung T1 - Dynamic and equilibrium adsorption behaviour of ß-lactoglobulin at the solution/tetradecane interface: Effect of solution concentration, pH and ionic strength T1 - Dynamik und Gleichgewicht der Adsorption von ß-Lactoglobulin an der Grenzfläche Lösung / Tetradecan (W/TD) N2 - Proteins are amphiphilic and adsorb at liquid interfaces. Therefore, they can be efficient stabilizers of foams and emulsions. β-lactoglobulin (BLG) is one of the most widely studied proteins due to its major industrial applications, in particular in food technology. In the present work, the influence of different bulk concentration, solution pH and ionic strength on the dynamic and equilibrium pressures of BLG adsorbed layers at the solution/tetradecane (W/TD) interface has been investigated. Dynamic interfacial pressure (Π) and interfacial dilational elastic modulus (E’) of BLG solutions for various concentrations at three different pH values of 3, 5 and 7 at a fixed ionic strength of 10 mM and for a selected fixed concentration at three different ionic strengths of 1 mM, 10 mM and 100 mM are measured by Profile Analysis Tensiometer PAT-1 (SINTERFACE Technologies, Germany). A quantitative data analysis requires additional consideration of depletion due to BLG adsorption at the interface at low protein bulk concentrations. This fact makes experiments more efficient when oil drops are studied in the aqueous protein solutions rather than solution drops formed in oil. On the basis of obtained experimental data, concentration dependencies and the effect of solution pH on the protein surface activity was qualitatively analysed. In the presence of 10 mM buffer, we observed that generally the adsorbed amount is increasing with increasing BLG bulk concentration for all three pH values. The adsorption kinetics at pH 5 result in the highest Π values at any time of adsorption while it exhibits a less active behaviour at pH 3. Since the experimental data have not been in a good agreement with the classical diffusion controlled model due to the conformational changes which occur when the protein molecules get in contact with the hydrophobic oil phase in order to adapt to the interfacial environment, a new theoretical model is proposed here. The adsorption kinetics data were analysed with the newly proposed model, which is the classical diffusion model but modified by assuming an additional change in the surface activity of BLG molecules when adsorbing at the interface. This effect can be expressed through the adsorption activity constant in the corresponding equation of state. The dilational visco-elasticity of the BLG adsorbed interfacial layers is determined from measured dynamic interfacial tensions during sinusoidal drop area variations. The interfacial tension responses to these harmonic drop oscillations are interpreted with the same thermodynamic model which is used for the corresponding adsorption isotherm. At a selected BLG concentration of 2×10-6 mol/l, the influence of the ionic strength using different buffer concentration of 1, 10 and 100 mM on the interfacial pressure was studied. It is affected weakly at pH 5, whereas it has a strong impact by increasing buffer concentration at pH 3 and 7. In conclusion, the structure formation of BLG adsorbed layer in the early stage of adsorption at the W/TD interface is similar to those of the solution/air (W/A) surface. However, the equation of state at the W/TD interface provides an adsorption activity constant which is almost two orders of magnitude higher than that for the solution/air surface. At the end of this work, a new experimental tool called Drop and Bubble Micro Manipulator DBMM (SINTERFACE Technologies, Germany) has been introduced to study the stability of protein covered bubbles against coalescence. Among the available protocols the lifetime between the moment of contact and coalescence of two contacting bubble is determined for different BLG concentrations. The adsorbed amount of BLG is determined as a function of time and concentration and correlates with the observed coalescence behaviour of the contacting bubbles. N2 - Die vorliegende Arbeit ist ein Beitrag zum Verständnis des Überganges von der qualitativen zur quantitativen Beschreibung der Adsorption von Proteinen an der Wasser/Öl- Grenzfläche. Dabei wird die Adsorption des Molkeproteins ß-Lactoglobulin (BLG) an der Wasser/Tetradekan (W/TD) Grenzfläche untersucht. Die Proteinadsorption an Grenzflächen zwischen zwei nicht mischbaren Flüssigkeiten ist ein Zeitprozess. Die Tropfenprofil-Analysen-Tensiometrie (PAT) hat sich als optimale Methode erwiesen, um den Prozess der Bildung von Proteinadsorptionsschichten an Flüssig-/flüssig-Grenzflächen quantitativ zu untersuchen. Die gemessenen dynamischen Grenzflächenspannungen können genutzt werden, um die adsorbierte Menge von Protein an Grenzflächen zu bestimmen. Zusätzlich erlaubt die Methode, durch periodische Tropfenoszillationen, die Messung der Dilatations-Viskoelastizität. Die experimentellen Ergebnisse zeigen deutlich, dass die Adsorption von Proteinen mit der Konzentration ansteigt. Der Adsorptionsprozess von Proteinen ist ähnlich dem von Tensiden, allerdings wird seine Beschreibung wesentlich komplizierter, durch die zusätzliche Möglichkeit der Konformationsänderungen der Proteinmoleküle an der Grenzfläche. Ein kürzlich im Rahmen dieser Dissertation entwickeltes Modell zur Adsorptionskinetik von Proteinen wurde genutzt, um experimentelle Daten für BLG zu interpretieren. Dieses kinetische Modell erlaubt es, den Mechanismus der Proteinadsorption an der Wasser/Öl-Grenzfläche zu beschreiben, was durch ältere Modelle bisher nicht möglich war. Im neu entwickelten Modell wurde die klassische Diffusionstheorie so modifiziert, dass eine Änderung der Adsorptionsaktivität der adsorbierenden Proteinmoleküle berücksichtigt wird. Die Änderung der Adsorptionsaktivität geschieht durch den Kontakt adsorbierter BLG-Moleküle an der Wasser/Öl-Grenzfläche. Es wird nach diesem neuen Modell angenommen, dass die Adsorptionsaktivität eine Funktion der Adsorptionszeit ist. Die ansteigende Adsorptionaktivität ist erforderlich, um den Adsorptionsprozess von BLG über den gesamten Zeitbereich quantitativ zu beschrieben. Mit diesem neuen Modell wurde es möglich, die experimentellen Daten zur Adsorptionskinetik sowie zur Dilatationsrheologie von Adsorptionsschichten bei unterschiedlichen BLG-Konzentrationen, pH-Werten und Ionenstärken an der Grenzfläche Lösung/Tetradekan quantitativ zu beschreiben. Die Ergebnisse dienen als Ausgangspunkt für weitere Entwicklungen zur Verbesserung des Verständnisses der Stabilität von Schäumen und Emulsionen, die durch die Dynamik der Adsorption von Molekülen wie BLG signifikant beeinflusst wird. KW - beta-lactoglobulin KW - water/tetradecane interface KW - drop profile analysis tensiometry KW - dynamic interfacial tensions KW - protein adsorption KW - pH effect KW - ionic strength effect KW - protein stabilized foams KW - drop and bubble coalescence KW - interfacial dynamics KW - capillary pressure tensiometry KW - drop-drop interaction KW - bubble-bubble interaction KW - ß-Lactoglobulin KW - Flüssig-/flüssig-Grenzflächen KW - Wasser/Öl-Grenzfläche KW - Grenzfläche Lösung/Tetradecan KW - Dynamik der Adsorption KW - Gleichgewicht der Adsorption KW - Proteinadsorption KW - Tropfenprofil-Analysen-Tensiometrie KW - Tropfenoszillationen KW - Dilatations-Viskoelastizität KW - klassische Diffusionstheorie KW - Konformationsänderungen KW - Adsorptionsaktivität KW - Wirkung des pH-Werten KW - Wirkung des Ionenstärken KW - Stabilität von Schäumen KW - Stabilität von Emulsionen Y1 - 2016 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-99167 ER - TY - THES A1 - Vorndran, Katja Marianne T1 - Einfache Decarbonylierungen und stereoselektive Oxidationen von Cyclohexadienen und Cyclohexenen N2 - Zusammenfassend konnte im Rahmen dieser Arbeit das Synthesepotential von Cyclohexadienen und Cyclohexenen deutlich erweitert werden. Die Darstellung der 1-Alkylcyclohexa-2,5-dien-1-carbonsäuren erfolgte mittels Birch-Reduktion in flüssigem Ammoniak und anschließender Umsetzung der intermediär entstehenden Dianionen mit Alkylhalogeniden. So konnte ausgehend von verschiedenen Benzoesäurederivaten eine Reihe interessanter Cyclohexadiene in sehr guten Ausbeuten synthetisiert werden. Erstmals gelangen säurekatalysierte Decarbonylierungen von Cyclohexadiencarbonsäuren, was die einfache Synthese substituierter Aromaten in ausgezeichneten Ausbeuten ermöglichte. In dieser Arbeit wird der Reaktionsmechanismus vorgestellt, welcher durch den Nachweis von Kohlenmonoxid in der Gasphase der Reaktionslösung durch IR-Spektroskopie untermauert wird. Bei der säurekatalysierten Umsetzung von 3-alkylsubstituierten Cyclohexadien-carbonsäuren entstanden neben den erwarteten Aromaten Lactone in ca. 50% Ausbeute. Schließlich zeigen die untersuchten Singulettsauerstoff-En-Reaktionen, der im ersten Teil dargestellten Cyclohexadiene und Lactone, durchweg hohe Regioselektivitäten und lieferten durch elektrostatische Wechselwirkungen und konformative Effekte zum Teil sehr gute Diastereoselektivitäten. Die auxiliarkontrollierte Photooxygenierungen von Cyclohexenon welches mit verschiedenen Weinsäureestern ketalisiert wurde, zeigten jedoch keine bevorzugte p-Facialität des Singulettsauerstoffs. N2 - In this dissertation thesis it was possible to extend the synthetical potential of cyclohexadienes and cyclohexenes with partially newly developed and very efficient synthetic pathways. The alkylcyclohexadiene carboxylic acids were synthesized in good yields via well known Birch-reduction procedure in liquid ammonia from a broad variety of substituted benzoic acid derivatives. A wide range of alkylhalides were subsequently added to the resulting dianion. We were able to decarbonylize the cyclohexadienes through acid catalyses, which leads to ipso-substituted aromatics in excellent yields. The study presents the postulated mechanism, which is supported by the proof of carbon monoxide in the gas phase of the reactionmixture with IR-spectroscopy. When 3-alkylsubstituted cyclohexadiene carboxylic acids were subjected to the acid catalyses they gave lactones in up to 50% yield as side products of the aromatization product.The cyclohexadienes and lactones were used as substrates in singlet oxygen-en-reactions with photochemically induced singulet oxygen. The products showed high regioselectivitiy and partially high diastereoselectivity which is caused by electrostatic interaction and conformativ effects of the reaction intermediates. Experiments to induce auxiliary controlled photooxygenations of cyclohexenones, which were ketalysed with different chiral tartaric acid esters leaded to poor diastereoselectivity and a diverse mixture of isomers. KW - Cyclohexadienderivate ; Chemische Synthese ; Birch-Reduktion ; Decarbonylierung | Cyclohexadienderivate ; Photooxidation ; Stereoselektive Reaktion ; KW - Decarbonylierung KW - Birch-Reduktion KW - Photooxygenierung KW - Singulettsauerstoff KW - Cyclohexadien KW - Decarbonylation KW - Birch-Reduction KW - Photooxygenation KW - Singletoxygen KW - Cylcohexadiene Y1 - 2001 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-0000331 ER - TY - THES A1 - Herfurth, Christoph T1 - Einstufen-Synthese und Charakterisierung amphiphiler Sternpolymere als multifunktionale assoziative Verdicker T1 - One-step synthesis and characterisation of amphiphilic star polymers as multifunctional associative thickeners N2 - Typische assoziative Verdicker für wässrige Systeme basieren auf linearen, doppelt hydrophob endmodifizierten Poly(ethylenglykolen) (PEGs). Diese Polymere aggregieren aufgrund ihrer Struktur in wässriger Lösung und bilden ein Netzwerk aus verbrückten Polymer-Mizellen. Dabei kann ein Polymer-Molekül maximal zwei Mizellen miteinander verbinden. Bisher ist unklar, wie die Anzahl der Endgruppen eines verzweigten, mehrfach hydrophob endmodifizierten hydrophilen Polymers die Struktur und Dynamik solcher Netzwerke beeinflusst. Die Synthese verzweigter Polymere auf PEG-Basis erfolgt mittels lebender ionischer Polymerisation und ist experimentell aufwändig. Das Einführen hydrophober Endgruppen erfordert zusätzliche Synthese-Schritte. In dieser Arbeit wurden hydrophile Sternpolymere mit hydrophoben Endgruppen in einem Schritt hergestellt. Dazu wurde die Technik der radikalischen Polymerisation unter Kettenübertragung durch reversible Addition und anschließende Fragmentierung (reversible addition-fragmentation chain transfer, RAFT) genutzt. Die Synthese der Sternpolymere erfolgte von einem multifunktionalen Kern, der die R-Gruppe der RAFT-Kettenüberträger (chain transfer agents, CTAs) bildete. Die dazu benötigten CTAs wurden so konzipiert, dass mit ihrer Hilfe sowohl die Anzahl der Arme des Sternpolymers (von 2 bis 4), als auch die Länge der hydrophoben Endgruppe (C4, C12, C18) variiert werden konnte. Der große Vorteil der RAFT-Polymerisation ist, dass sie viele polare Monomere für die Synthese der hydrophilen Arme des Sternpolymers toleriert. In dieser Arbeit wurden als Modell-Monomere Oligo(ethylenglykol)methylether-acrylat (OEGA) und N,N-Dimethylacrylamid (DMA) eingesetzt. Beide Monomere bilden nicht-ionische hydrophile Polymere. Poly(OEGA) ist ein Kammpolymer, das auf PEG basiert. Poly(DMA) besitzt dagegen eine deutlich kompaktere Struktur. Die erhaltenen amphiphilen Sternpolymere wurden umfassend molekular charakterisiert. Die Molmassen wurden mit verschiedenen GPC-Systemen bestimmt und der Grad der Endgruppenfunktionalisierung wurde mittels UV/Vis- und 1H-NMR-Spektroskopie überprüft. Die Polymerisation von OEGA zeigt mit den CTAs einige Charakteristika der Polymerisation mit reversibler Deaktivierung (RDRP, auch „kontrollierte radikalische Polymerisation“), wird aber durch Kettenübertragung zum Monomer bzw. Polymer gestört. Diese Nebenreaktion ist auf die Struktur des Monomers als Oligoether zurückzuführen. Bei allen untersuchten Polymerisationen von DMA mit den multifunktionalen CTAs steigt die Molmasse linear mit dem Umsatz. Die erhaltenen Polymere zeigen durchweg monomodale und enge Molmassenverteilungen (PDI ≤ 1,2). Die Molmassen lassen sich in einem weiten Bereich von 25 kg/mol bis 150 kg/mol einstellen und die Endgruppen der Polymere bleiben zu 90 % erhalten. Während die Polymerisation von DMA sowohl mit den di- als auch den trifunktionalen CTAs innerhalb von 3 h zu quantitativen Umsätzen verläuft, wird der quantitative Umsatz des Monomers bei der Polymerisation mit tetrafunktionalen CTAs erst nach 4 h erreicht. Diese Verzögerung ist auf eine Retardierung in der Anfangsphase der Polymerisation zurückzuführen, die sich aus der besonderen Struktur der tetrafunktionalen CTAs erklärt. Auf dem System zur Polymerisation von DMA aufbauend ließen sich Gradienten-Block-Copolymere in Eintopfreaktionen herstellen. Dazu wurde nach Erreichen des quantitativen Umsatzes von DMA ein zweites Monomer zur Reaktionsmischung gegeben. Mit Ethylacrylat (EtA) wurden so lineare amphiphile symmetrische Triblock-Copolymere erhalten. Dabei wurde die Länge des hydrophoben Blocks durch unterschiedliche Mengen an EtA variiert. Mit N,N-Diethylacrylamid (DEA) wurden lineare symmetrische Triblock-Copolymere sowie 3-Arm Stern-Diblock-Copolymere hergestellt, die über einen thermisch schaltbaren zweiten Block verfügen. Bei diesen Polymeren lässt sich die Länge des hydrophoben Teils in situ durch Veränderung der Temperatur variieren. Das Verhalten der amphiphilen Sternpolymere in wässriger Lösung und in Mikroemulsion wurde im Rahmen einer Kooperation an der TU Berlin mit Hilfe von Kleinwinkel-Neutronenstreuung (SANS), dynamischer Lichtstreuung (DLS) und Rheologie untersucht. Die Polymere wirken durch Assoziation der hydrophoben Endgruppen als effektive Verdicker sowohl allein in wässriger Lösung als auch in Mikroemulsion. Die Struktur des gebildeten Netzwerks hängt dabei von der Konzentration des Polymers in der Lösung und der Länge der Endgruppe (Hydrophobie) ab. Die dynamischen Eigenschaften der Lösungen werden außerdem durch die Anzahl der Arme der Polymere bestimmt. N2 - Typically, associative thickeners for aqueous system consist of linear, hydrophobically α,ω-end-capped poly(ethylene glycols) (PEGs). Owing to their structure, these polymers aggregate in aqueous solution, forming a network of bridged micelles. Thus, one polymer molecule can link not more than two micelles. Until now it is unclear whether the structure and dynamics of such networks are influenced by the number of end groups of a branched multiply hydrophobically end-capped hydrophilic polymers. Branched PEG-based polymers are synthesized using the laborious and limited techniques of living ionic polymerization. Introducing hydrophobic end groups demands a multiple-step process. This work presents the one-step synthesis of hydrophilic star polymers with hydrophobic end groups, using reversible addition fragmentation chain transfer (RAFT) polymerization. This radical polymerization method is easy to use and tolerates a large number of polar monomers for the synthesis of the hydrophilic arms of the star polymers. The arms of the polymer were grown from a multifunctional core that formed the R-group of the chain transfer agents (CTAs). The CTAs where tailored to be able to vary the number of arms of the star polymers from 2 to 4 and to vary the length (and therefore the hydrophobicity) of the end groups (C4, C12, C18). Two different polar monomers where used as model monomers: Oligo(ethylene glycol)methyl ether acrylate (OEGA) and N,N-Dimethylacrylamide (DMA). Both monomers yield non-ionic hydrophilic polymers. While poly(OEGA) is a comb polymer based on PEG, poly(DMA) exhibits a more compact structure. The amphiphilic star polymers were characterized extensively. The molar masses were determined using GPC in various solvents and the degree of end functionalisation was monitored using 1H NMR and UV/Vis spectroscopy. The polymerization of OEGA shows some of the expected characteristics of reversible deactivation radical polymerization (RDRP). However, chain transfer to monomer and polymer is a prominent side reaction, limiting the use of this monomer for the fabrication of well-defined material. This reaction can be attributed to the structure of the monomer being an oligoether. For all examined polymerizations of DMA with the multifunctional CTAs the molar mass increased linearly with conversion. The molar mass distributions were monomodal and narrow (PDI ≤ 1.2). Expected values were reached for molar masses from 25 to 150 kg/mol and the end group functionality was about 90 % in all cases. While the polymerization of DMA using di- and trifunctional CTAs proceeded to quantitative conversion within 3 h, an initial retardation period of about 60 min was observed for the polymerization using tetrafunctional CTAs. This retardation was attributed to the peculiar molecular structure of these CTAs. Owing to the well-controlled features of the polymerization of DMA using the multifunctional CTAs, this system was used to obtain tapered block copolymers in a one-pot process. These structures were achieved by adding a second monomer to the reaction mixture after the quantitative conversion of DMA. Using ethyl acrylate (EtA), linear amphiphilic symmetrical triblock copolymers were synthesized. The length of the hydrophobic block was tailored by the addition of varying amounts of EtA. With N,N-Diethylacrylamide as a second monomer, linear symmetric triblock copolymers as well as 3-arm star diblock copolymers were obtained that contain a thermosensitve block. Altering the temperature of aqueous solutions of these polymers varies the length of the hydrophobic block in situ. At the TU Berlin, the behavior of the polymers was studied in aqueous solution as well as in microemulsion. The solutions were characterized by small angle neutron scattering (SANS), dynamic light scattering (DLS) and rheology. The end groups of the polymers aggregate, making the polymers efficient thickeners both in aqueous solution and in microemulsion. The structure of the formed network depends on the concentration of the polymer in solution and on the length of the end group. The dynamic properties of the solutions are governed additionally by the number of arms. KW - RAFT-Polymerisation KW - Sternpolymere KW - Synthese KW - Amphiphile Polymere KW - Assoziative Verdicker KW - RAFT polymerisation KW - star polymers KW - synthesis KW - amphiphilic polymers KW - associative thickeners Y1 - 2012 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-62446 ER - TY - THES A1 - Schutjajew, Konstantin T1 - Electrochemical sodium storage in non-graphitizing carbons - insights into mechanisms and synthetic approaches towards high-energy density materials T1 - Elektrochemische Natriumspeicherung in nicht-graphitisierbaren Kohlenstoffen - Untersuchungen zu Mechanismen und synthetische Ansätze für die Darstellung von Materialien mit hohen Energiedichten N2 - To achieve a sustainable energy economy, it is necessary to turn back on the combustion of fossil fuels as a means of energy production and switch to renewable sources. However, their temporal availability does not match societal consumption needs, meaning that renewably generated energy must be stored in its main generation times and allocated during peak consumption periods. Electrochemical energy storage (EES) in general is well suited due to its infrastructural independence and scalability. The lithium ion battery (LIB) takes a special place, among EES systems due to its energy density and efficiency, but the scarcity and uneven geological occurrence of minerals and ores vital for many cell components, and hence the high and fluctuating costs will decelerate its further distribution. The sodium ion battery (SIB) is a promising successor to LIB technology, as the fundamental setup and cell chemistry is similar in the two systems. Yet, the most widespread negative electrode material in LIBs, graphite, cannot be used in SIBs, as it cannot store sufficient amounts of sodium at reasonable potentials. Hence, another carbon allotrope, non-graphitizing or hard carbon (HC) is used in SIBs. This material consists of turbostratically disordered, curved graphene layers, forming regions of graphitic stacking and zones of deviating layers, so-called internal or closed pores. The structural features of HC have a substantial impact of the charge-potential curve exhibited by the carbon when it is used as the negative electrode in an SIB. At defects and edges an adsorption-like mechanism of sodium storage is prevalent, causing a sloping voltage curve, ill-suited for the practical application in SIBs, whereas a constant voltage plateau of relatively high capacities is found immediately after the sloping region, which recent research attributed to the deposition of quasimetallic sodium into the closed pores of HC. Literature on the general mechanism of sodium storage in HCs and especially the role of the closed pore is abundant, but the influence of the pore geometry and chemical nature of the HC on the low-potential sodium deposition is yet in an early stage. Therefore, the scope of this thesis is to investigate these relationships using suitable synthetic and characterization methods. Materials of precisely known morphology, porosity, and chemical structure are prepared in clear distinction to commonly obtained ones and their impact on the sodium storage characteristics is observed. Electrochemical impedance spectroscopy in combination with distribution of relaxation times analysis is further established as a technique to study the sodium storage process, in addition to classical direct current techniques, and an equivalent circuit model is proposed to qualitatively describe the HC sodiation mechanism, based on the recorded data. The obtained knowledge is used to develop a method for the preparation of closed porous and non-porous materials from open porous ones, proving not only the necessity of closed pores for efficient sodium storage, but also providing a method for effective pore closure and hence the increase of the sodium storage capacity and efficiency of carbon materials. The insights obtained and methods developed within this work hence not only contribute to the better understanding of the sodium storage mechanism in carbon materials of SIBs, but can also serve as guidance for the design of efficient electrode materials. N2 - Eine nachhaltige Energiewirtschaft kann nur durch die Abkehr von fossilen Brennstoffen als Energiequellen und den ausschließlichen Einsatz erneuerbarer Quellen für die Energieerzeugung erreicht werden. Da diese jedoch naturgemäß nur diskontinuierlich zur Verfügung stehen und sich die tageszeitliche Verfügbarkeit kaum mit dem Bedarf deckt, muss erneuerbar gewonnene Energie zwischengespeichert werden. Dies kann mittels elektrochemischer Energiespeicher geschehen, wobei sich die Lithium-Ionen-Batterie (LIB) aufgrund ihrer hohen Energiedichte und Effizienz besonders dafür eignet. Da jedoch Ressourcen, welche für entscheidende Zellkomponenten der LIB benötigt werden, knapper werden und oft in geopolitisch komplizierten Regionen vorkommen, muss auch dafür eine Alternative gefunden werden. Die Natrium-Ionen-Batterie (NIB) bietet sich als Nachfolger für LIBs an, da sich die Zellchemie der beiden Systeme ähnelt und somit Kenntnisse direkt aus der LIB-Forschung übernommen werden können. Es erweist sich allerdings als problematisch, dass das kommerziell wichtigste negative Elektrodenmaterial in LIBs, Graphit, nicht für die Anwendung in NIBs eignet und daher eine andere Kohlenstoffmodifikation, sogenannter nicht-graphitisierbarer Kohlenstoff, oder aus dem Englischen hard carbon (HC), verwendet werden muss. HC ist durch eine besondere Art der Fehlordnung geprägt und besteht im Wesentlichen aus Regionen, in denen die Kohlenstoffschichten parallel zueinander verlaufen und aus Regionen, in denen die Schichten innere Hohlräume, sogenannte geschlossene Poren bilden. Die Lade-Entladekurve von HCs ist geprägt von diesen Strukturmerkmalen, sodass sie in einen linear-abflachenden, aus dem Englischen sloping Bereich, und einen Plateaubereich unterteilt werden kann. Die Speicherung im für Energieanwendungen relevanteren Plateaubereich erfolgt durch Abscheidung quasimetallischer Natriumstrukturen in eingangs erwähnten geschlossenen Poren, bei geringen, konstanten Spannungen, wie zahlreiche Forschungsarbeiten unter Berufung auf verschiedene Strukturcharakterisierungsmethoden � uberzeugend nahelegen. Jedoch ist über den Einfluss der Größe und Form der geschlossenen Poren sowie derer chemischer Eigenschaften auf die Natriumspeicherung nur wenig bekannt. Eben diese Fragestellung soll in der vorliegenden Arbeit behandelt werden. Durch die Herstellung von Materialien mit genau definierter und bekannter Morphologie, Porenstruktur sowie chemischer Beschaffenheit wird die Bedeutung dieser Merkmale für die Natriumabscheidung bei geringen Potentialen beleuchtet. Mittels elektrochemischer Impedanzspektroskopie wird desweiteren der Natriumspeichermechanismus detailliert untersucht und die Kinetik der reversiblen Natriumspeicherung mit der der irreversiblen Metallabscheidung verglichen, wobei eine bemerkenswerte Ähnlichkeit der beiden Prozesse zu beobachten ist. Abschließend ist die gezielte Herstellung geschlossenporiger Materialien aus offenporigen Vorläufermaterialien gelungen, welche es nicht nur ermöglicht, geschlossen- und offenporige Materialien ansonsten gleicher Porenstruktur zu vergleichen und die Notwendigkeit geschlossener Poren nachzuweisen, sondern auch die Speicherkapazität und Effizienz der Elektrodenmaterialien zu erhöhen. Insgesamt tragen die im Rahmen der vorliegenden Dissertation gewonnenen Erkenntisse nicht nur zum tiefergehenden Verständnis des Natriumspeichermechanismus in HCs bei, sondern es werden auch synthetische und analytische Methoden vorgestellt, die der weiteren Forschung auf diesem Gebiet dienen werden. KW - sodium-ion batteries KW - energy storage KW - carbon KW - Natrium-Ionen-Akkumulator KW - Energiespeicher KW - Kohlenstoff Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-541894 ER - TY - THES A1 - Zühlke, Martin T1 - Elektrosprayionisation Ionenmobilitätsspektrometrie T1 - Electrospray ionization Ion mobility spectrometry BT - Entwicklung, Charakterisierung und Anwendung zur HPLC-Detektion und zum Reaktionsmonitoring BT - development, characterization and application for HPLC detection and reaction monitoring N2 - Die Elektrosprayionisation (ESI) ist eine der weitverbreitetsten Ionisationstechniken für flüssige Pro-ben in der Massen- und Ionenmobilitäts(IM)-Spektrometrie. Aufgrund ihrer schonenden Ionisierung wird ESI vorwiegend für empfindliche, komplexe Moleküle in der Biologie und Medizin eingesetzt. Überdies ist sie allerdings für ein sehr breites Spektrum an Substanzklassen anwendbar. Die IM-Spektrometrie wurde ursprünglich zur Detektion gasförmiger Proben entwickelt, die hauptsächlich durch radioaktive Quellen ionisiert werden. Sie ist die einzige analytische Methode, bei der Isomere in Echtzeit getrennt und über ihre charakteristische IM direkt identifiziert werden können. ESI wurde in den 90ger Jahren durch die Hill Gruppe in die IM-Spektrometrie eingeführt. Die Kombination wird bisher jedoch nur von wenigen Gruppen verwendet und hat deshalb noch ein hohes Entwick-lungspotential. Ein vielversprechendes Anwendungsfeld ist der Einsatz in der Hochleistungs-flüssigkeitschromatographie (HPLC) zur mehrdimensionalen Trennung. Heutzutage ist die HPLC die Standardmethode zur Trennung komplexer Proben in der Routineanalytik. HPLC-Trennungsgänge sind jedoch häufig langwierig und der Einsatz verschiedener Laufmittel, hoher Flussraten, von Puffern, sowie Laufmittelgradienten stellt hohe Anforderungen an die Detektoren. Die ESI-IM-Spektrometrie wurde in einigen Studien bereits als HPLC-Detektor eingesetzt, war dort bisher jedoch auf Flussratensplitting oder geringe Flussraten des Laufmittels beschränkt. In dieser kumulativen Doktorarbeit konnte daher erstmals ein ESI IM-Spektrometer als HPLC-Detektor für den Flussratenbereich von 200-1500 μl/min entwickelt werden. Anhand von fünf Publi-kationen wurden (1) über eine umfassende Charakterisierung die Eignung des Spektrometers als HPLC-Detektor festgestellt, (2) ausgewählte komplexe Trenngänge präsentiert und (3) die Anwen-dung zum Reaktionsmonitoring und (4, 5) mögliche Weiterentwicklungen gezeigt. Erfolgreich konnten mit dem selbst-entwickelten ESI IM-Spektrometer typische HPLC-Bedingungen wie Wassergehalte im Laufmittel von bis zu 90%, Pufferkonzentrationen von bis zu 10 mM, sowie Nachweisgrenzen von bis zu 50 nM erreicht werden. Weiterhin wurde anhand der komplexen Trennungsgänge (24 Pestizide/18 Aminosäuren) gezeigt, dass die HPLC und die IM-Spektrometrie eine hohe Orthogonalität besitzen. Eine effektive Peakkapazität von 240 wurde so realisiert. Auf der HPLC-Säule koeluierende Substanzen konnten über die Driftzeit getrennt und über ihre IM identifi-ziert werden, sodass die Gesamttrennzeiten erheblich minimiert werden konnten. Die Anwend-barkeit des ESI IM-Spektrometers zur Überwachung chemischer Synthesen wurde anhand einer dreistufigen Reaktion demonstriert. Es konnten die wichtigsten Edukte, Zwischenprodukte und Produkte aller Stufen identifiziert werden. Eine quantitative Auswertung war sowohl über eine kurze HPLC-Vortrennung als auch durch die Entwicklung eines eigenen Kalibrierverfahrens, welches die Ladungskonkurrenz bei ESI berücksichtigt, ohne HPLC möglich. Im zweiten Teil der Arbeit werden zwei Weiterentwicklungen des Spektrometers präsentiert. Eine Möglichkeit ist die Reduzierung des Drucks in den intermediären Bereich (300 - 1000 mbar) mit dem Ziel der Verringerung der benötigten Spannungen. Mithilfe von Streulichtbildern und Strom-Spannungs-Kurven wurden für geringe Drücke eine verminderte Freisetzung der Analyt-Ionen aus den Tropfen festgestellt. Die Verluste konnten jedoch über höhere elektrische Feldstärken ausgeglichen werden, sodass gleiche Nachweisgrenzen bei 500 mbar und bei 1 bar erreicht wurden. Die zweite Weiterentwicklung ist ein neuartiges Ionentors mit Pulsschaltung, welches eine Verdopplung der Auflösung auf bis zu R > 100 bei gleicher Sensitivität ermöglichte. Eine denkbare Anwendung im Bereich der Peptidanalytik wurde mit beachtlichen Auflösungen der Peptide von R = 90 gezeigt. N2 - Electrospray ionization (ESI) is one of the most widespread ionization techniques for liquid samples in mass and ion mobility (IM) spectrometry. Due to its gentle ionization, ESI is often used for sensitive, complex molecules in biology and medicine. However, it is also applicable to a wide range of substance classes. IM spectrometry was originally developed for the detection of gaseous samples, which are mainly ionized by radioactive sources. It is the only analytical method in which isomers can be separated in real time and directly identified by their characteristic IM. ESI was introduced to IM spectrometry by the Hill Group in the 90s. So far, the combination was only used by a limited number of groups and therefore there is still a large development potential. A highly promising field of application is highperformance liquid chromatography (HPLC) for multidimensional separations. At present, HPLC is the standard method for the separation of complex samples in routine analysis. However, HPLC separations are often time-consuming and the use of different solvents, high flow rates, buffers, as well as solvent gradients impose high demands on the detectors. ESI IM spectrometry was already used as an HPLC detector in a number of studies. However, these studies were restricted to splitting or low flow rates of the mobile phase. In this cumulative thesis, an ESI IM spectrometer was developed as an HPLC detector for the flow rate range of 200-1500 μl/min for the first time. Based on five publications, (1) the suitability of the spectrometer as an HPLC detector was comprehensively characterized, (2) selected complex separations are presented, and (3) the application to the reaction monitoring as well as (4, 5) possible further developments are shown. With the in-house developed ESI IM spectrometer, typical HPLC conditions such as water contents in the mobile phase of up to 90%, buffer concentrations of up to 10 mM, as well as detection limits of up to 50 nM, were achieved successfully. Furthermore, on the basis of a complex separation (24 pesticides/18 amino acids), it could be demonstrated that HPLC and IM spectrometry possess a high degree of orthogonality. An effective peak capacity of 240 was thus realized. Substances coeulating on the HPLC column could be separated in the drift time and were identified by their IM. Thus, the overall separation times could be significantly reduced. The applicability of the ESI IM spectrometer for the monitoring of chemical syntheses was demonstrated for a three-stage reaction. The main starting materials, intermediates and products of all stages could be identified. A quantitative evaluation was possible both by means of a short HPLC pre-separation as well as by a newly developed calibration procedure, which takes charge competition during ESI into account, without HPLC. In the second part of the thesis, two further developments of the spectrometer are presented. One possibility is a reduction of the pressure to the intermediate range (300 - 1000 mbar) with the aim of reducing the required voltages. With the help of scattered light images and current-voltage curves, a reduced release of analyte ions from the droplets was determined at low pressures. However, these losses could be compensated for by higher electric field strengths. Therefore, the same detection limits were achieved at 500 mbar and at 1 bar. The second development is a novel ion gate with pulse switching, which allows a doubling of the resolution up to R > 100 with equal sensitivity. A possible application in the field of peptide analysis was demonstrated, achieving a considerable resolutions of R = 90 for the peptides. KW - HPLC KW - HPLC KW - Ionenmobilitätsspektrometrie KW - Elektrosprayionisation KW - ion mobility spectrometry KW - electrospray ionization (ESI) Y1 - 2017 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-407452 ER - TY - THES A1 - Erbe, Andreas T1 - Ellipsometrische Lichtstreuung als neue Methode zur Charakterisierung der Grenzfläche von Kolloiden N2 - Die ellipsometrische Lichtstreuung wird als eine neue, leistungsfähige Methode zur Charakterisierung von Schichten um kolloidale Partikel vorgestellt. Theoretische Grundlage der Methode ist die Mie-Theorie der Lichtstreuung. Experimentell wurde die Polarisationsoptik eines Null-Ellipsometers in den Strahlengang eines Lichtstreuaufbaus eingebaut. Wie in der Reflexionsellipsometrie um den Brewsterwinkel herum erhält man in der ellipsometrischen Streuung einen Winkelbereich, in dem die Methode empfindlich auf Schichten an der Oberfläche der Partikel ist. An verschiedenen Systemen wurde die Tauglichkeit der ellipsometrischen Streuung zur Charakterisierung von Schichten auf Partikeln demonstriert. So wurden Dicke und Brechungsindex einer thermosensitiven Schicht von Poly(N-isopropylacrylamid) auf einem Poly(methylmethacrylat)-Kern bestimmt. Damit ist es möglich, experimentell den Schichtbrechungsindex und damit den Quellungsgrad zu bestimmen. Des Weiteren wurde der Einfluss der NaCl-Konzentration auf die Polyelektrolythülle von Poly(methylmethacrylat)-Poly(styrolsulfonat)-Blockcopolymer-Partikeln untersucht. Die Polyelektrolytketten liegen im hier untersuchten Beispiel nicht gestreckt vor. Als drittes wurde die Verteilung von niedermolekularen Ionen um elektrostatisch stabilisierte Poly(styrol)-Latexpartikel in Wasser untersucht. Hier wurde gezeigt, dass die beobachteten Schichtdicken und Schichtbrechungsindizes viel größer sind, als nach der klassischen Poisson-Boltzmann-Theorie zu erwarten ist. Des Weiteren wurde die Doppelbrechung von unilamellaren Lipidvesikeln bestimmt. Außerdem wurden Messungen der dynamische Lichtstreuung im Intensitätsminimum der Ellipsometrie durchgeführt. Dabei wird ein Prozess mit einer Korrelationszeit, die unabhängig vom Streuvektor, aber abhängig von der verwendeten Wellenlänge ist, sichtbar. Die Natur dieses Prozesses konnte hier nicht vollständig geklärt werden. N2 - Ellipsometric light scattering is introduced as a new and powerful technique to characterize layers on colloidal particles. For the experiments, the polarization optics used reflection ellipsometry was installed in the beam of a light scattering setup. Using the priciples of null ellipsometry, a small range of scattering angles is obtained, were the method is sensitive to layers on the surface of colloidal particles. This is an analogy to the layer sensitivity of reflection ellipsometry at planer interfaces close to the Brewster angle. The theoretical basis for ellipsometric scattering is the Mie theory with its modern supplements. The feasibility of characterizing layers on colloidal particles was demonstrated with several systems. First, layer thickness and layer refractive index of poly(N-isopropylacrylamide) layers on a poly(methylmethacrylate) core were determined. This was the first time that the refractive index and with that the degree of swelling of a layer was directly determined in an scattering experiment. Second, polyelectrolyte layers on Poly(methylmethacrylate)-Poly(styrenesulfonate)-blockcopolymer particles were characterized. The influence of the salt concentration on the parameters of the layer was determined. The results show that the polyelectrolyte chains in the system investigated are not streched. Third, layers of ions around electrostatically-stabilized poly(styrene) particles were characterized. The layer thickness and layer refractive index in these examples are shown to be much larger than predicted by the classical Poisson-Boltzmann-theory. In addition, the birefringence of lipid vesicles was determined. Another interesting application of the ellipsometric scattering is the dynamic light scattering with ellipsometric optics. Its results show a characteristic process with a correlation time independent of the scattering vector, but wavelength dependent. The origin of this mode is not yet completely clarified. T2 - Ellipsometrische Lichtstreuung als neue Methode zur Charakterisierung der Grenzfläche von Kolloiden KW - Ellipsometrie KW - Lichtstreuung KW - Grenzfläche KW - Kolloide KW - Ionenverteilung KW - Lipide KW - Polyelektrolyte KW - ellipsometry KW - light scattering KW - interface KW - colloids KW - ion distribution KW - lipids KW - polyelectrolytes Y1 - 2004 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-0001565 ER - TY - THES A1 - Kozempel, Steffen T1 - Emulgatorfreie Emulsionspolymerisation : Monomerlösungszustand und Teilchenbildung T1 - Emulsifier-free emulsion polymerization : monomer solution state and particle formation N2 - Polymere sind zweifelsohne der Werkstoff in unserer Zeit. Ein bedeutender Anteil der heute industriell produzierten Polymere wird durch Emulsionspolymerisation hergestellt. Obwohl die Emulsionspolymerisation breite Anwendung findet, sind die involvierten Mechanismen von Teilchenbildung und -wachstum noch heute Gegenstand heftiger Kontroversen. Ein Spezialfall der Emulsionspolymerisation ist die emulgatorfreie Emulsionspolymerisation. Hierbei handelt es sich um ein scheinbar einfacheres System der Emulsionspolymerisation, weil diese Methode ohne Zusatz von Emulgatoren auskommt. Die Teilchenbildung ist ein fundamentaler Vorgang im Verlauf der Emulsionspolymerisation, da sie zur Ausbildung der polymeren Latexphase führt. Detaillierte Kenntnisse zum Mechanismus der Nukleierung ermöglichen eine bessere Kontrolle des Reaktionsverlaufes und damit der Eigenschaften des Endproduktes der Emulsionspolymerisation, dem Polymer-Latex. Wie bereits vorangegangene Arbeiten auf dem Gebiet der emulgatorfreien Emulsionspolymerisation von Styrol sowie Methylmethacrylat und Vinylacetat zeigen konnten, verläuft die Teilchenbildung in diesen Systemen über den Mechanismus der aggregativen Nukleierung. Im Zusammenhang mit den Ergebnissen der genannten Arbeiten tauchte dabei immer wieder ein interessanter Effekt im Bereich der Partikelnukleierung auf. Dieses als JUMBO-Effekt bezeichnete Phänomen zeigte sich reproduzierbar in einem Anstieg der Transmission im Bereich der Teilchenbildung von emulgatorfreien Emulsionspolymerisationen von Styrol, MMA und VAc. Nach der Initiierung der Polymerisation in einer wässrigen Monomerlösung durch Kaliumperoxodisulfat steigt die Durchlässigkeit bei 546 nm auf über 100 % an. Für diese „Abnahme der optischen Dichte“ wurden verschiedene Erklärungsmöglichkeiten vorgeschlagen, jedoch blieb ein Nachweis der Ursache für den JUMBO-Effekt bisher aus. Dieser Mangel an Aufklärung eines offenbar grundlegenden Phänomens in der emulgatorfreien Emulsionspolymerisation bildet den „Nukleus“ für die vorlie¬gende Arbeit. Durch die vorliegende Dissertation konnte das Verständnis für Phänomene der Teilchenbildung in der emulgatorfreien Emulsionspolymerisation von Styrol mit KPS erweitert werden. In diesem Rahmen wurde das Online-Monitoring des Polymerisationsvorganges verbessert und um verschiedene Methoden erweitert: Zur simultanen Erfassung von Trübungsdaten bei verschiedenen Wellenlängen konnte ein modernes Spektrometer in Kombination mit einer Lichtleitersonde in die Reaktionsapparatur integriert werden. Es wurde ein verbesserter Algorithmus zur Datenbearbeitung für die Partikelgrößenbestimmung mittels faseroptischer dynamischer Lichtstreuung entwickelt. Es wurden Online-Partikelgrößenanalysen mittels statischer Vielwinkellichtstreuung bei Polymerisationen direkt in entsprechenden Lichtstreuküvetten durchgeführt. Diese zur Beschreibung des untersuchten Systems eingeführten Methoden sowie ein zeitlich vollständiges Monitoring des gesamten Polymerisationsverlaufes, beginnend mit der Zugabe von Monomer zu Wasser, führten zu neuen Erkenntnissen zur emulgatorfreien Emulsionspolymerisation. Es wurden große Monomeraggregate, die sog. Nanotröpfchen, in wässriger Lösung (emulgatorfrei) nachgewiesen. Diese Aggregate bilden sich spontan und treten verstärkt in entgastem Wasser auf. Die Existenz von Nanotröpfchen in Verbindung mit Trübungs- und gaschromatografischen Messungen lässt auf eine molekular gelöste „Wirkkonzentration“ von Styrol in Wasser schließen, die bedeutend geringer ist als die absolute Sättigungskonzentration. Es konnten Hinweise auf eine Reaktion höherer Ordnung im System Wasser/Styrol/KPS gefunden werden. Es konnte gezeigt werden, dass eine präzise Einstellung der Nukleierungsdauer über die Zeit der Equilibrierung von Wasser mit Styrol möglich ist. Der JUMBO-Effekt, dem in dieser Arbeit ein besonderes Interesse galt, konnte in gewisser Weise entmystifiziert werden. Es konnte gezeigt werden, dass die Durchlässigkeit der Reaktionsmischung bereits beim Lösen von Styrol in Wasser durch Bildung von Styrolaggregaten abnimmt. Der darauf folgende kurzzeitige Transmissionsanstieg im Zusammenhang mit der Nukleierung erreicht dabei nicht mehr 100 % des Referenzwertes von reinem Wasser. Alle experimentellen Daten sprechen für die Nanotröpfchen als Ursache des JUMBO-Effekts. Wie die Ergebnisse dieser Arbeit zeigen, ist selbst das relativ „einfache“ System der emulgatorfreien Emulsionspolymerisation komplizierter als angenommen. Die Existenz von großen Styrolaggregaten in wässriger Lösung erfordert eine neue Betrachtungsweise des Reaktionssystems, in die auch der Lösungszustand des Monomers mit einbezogen werden muss. N2 - Polymers are doubtless the material of today. Large amounts of industrially produced polymers are made via emulsion polymerization. Although emulsion polymerization is widely used commercially, the mechanisms of particle formation and -growth involved are still intensely controversial. A special case of the emulsion polymerization is the emulsifier-free emulsion polymerization. This apparently easier procedure is performed without addition of emulsifier. Particle formation is a fundamental event in the progression of emulsion polymerization because it leads to the formation of a polymeric latex phase. Explicit knowledge concerning the mechanism of nucleation facilitates better control of the reaction process and therefore of the properties of the final polymeric latex product. Other contributions in emulsifier-free emulsion polymerization of styrene could already proof that particle formation in the present system proceeds via aggregative nucleation. In the context of the results of these contributions, an interesting effect was always detected in the time range of particle nucleation. This so-called “JUMBO-effect” appeared highly reproducible as an increase of transmittance during nucleation period in the emulsifier-free emulsion polymerization of styrene. After initiation of the polymerization in an aqueous monomer solution with potassiumperoxodisulfate the transmittance at 546 nm increases to more than 100 %. For this “decrease in optical density” various possible explanations have been suggested, but a proof for any of them is still to be found. This lack of insight into an apparently fundamental phenomenon in emulsifier-free emulsion polymerization arises as the “nucleus” of the present thesis. Within this work the understanding of the phenomena of particle formation in emulsifier-free emulsion polymerization of styrene with potassiumperoxodisulfate could be enhanced. In this frame the online monitoring of the polymerization process could be improved and expanded to several methods: For the simultaneous recording of UV-spectra respectively turbidity data at various wavelengths a modern spectrometer in combination with a fibre optical probe could be integrated into the reaction vessel. An improved algorithm for data treatment of particle size determination via fibre optical dynamic light scattering was developed. We implemented online particle size determinations via multi angle laser light scattering directly in light scattering cuvettes. These newly introduced methods, in combination with temporally complete monitoring of the whole polymerization progression, starting with the addition of monomer to water, lead to novel insight into emulsifier-free emulsion polymerization of styrene: Big monomer aggregates, so called “nano droplets”, could be detected in an aqueous solution of styrene. These aggregates form spontaneously and appear especially in degassed water. Polymerisation as the origin of the nano droplets can be excluded. In context with turbidity and gas chromatographic measurements, the existence of nano droplets leads us to conclude that there is a molecularly dissolved “effective” concentration of styrene in water which is much lower than the absolute concentration reported in the literature. We could find some hints for a higher reaction order in the system water/styrene/potassiumpersulfate. The induced decomposition of the peroxodisulfate ion in the presence of styrene and ethylbenzene shows an additional reaction of the initiator with aromatic compounds besides the thermolytical cleavage. Furthermore it could be shown that it is possible to precisely adjust the duration of nucleation with the solubilisation time of styrene in water. This kind of control can be useful for other applications. The JUMBO-effect, which was a major topic of this thesis, could be partly de-mystified. It could be shown that the turbidity of the reaction mixture already increases during the dissolution process of styrene due to the formation of aggregates. The turbidity decrease which is depicted by the JUMBO-effect in the time range of nucleation never reaches 100 % of the reference water. An interference of the used measuring wavelength with the domain size of density fluctuations according to the theory of spinodal decomposition could not be verified. The experimental data suggest rather the nano droplets as origin of the JUMBO-effect. The results of the present thesis show clearly that the relatively “simple” system of the emulsifier-free emulsion polymerisation (water/styrene/potassiumpersulfate) is more complex than expected. The existence of big styrene aggregates in aqueous solution requires a new approach of the reaction system, which also includes the solution state of the monomer. KW - Emulsionspolymerisation KW - Styrol KW - emulatorfrei KW - Lösungszustand KW - Teilchenbildung KW - Nukleierung KW - emulsion polymerization KW - styrene KW - nucleation KW - particle formation KW - emulsifier-free Y1 - 2005 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-6106 ER - TY - THES A1 - Ledendecker, Marc T1 - En route towards advanced catalyst materials for the electrocatalytic water splitting reaction T1 - Innovative Katalysatormaterialien für die elektrokatalytische Wasserspaltung BT - mechanistic insights into the formation of metal carbides, phosphides, sulfides and nitrides BT - mechanistische Einblicke in die Bildung von Metallcarbiden, -phosphiden, -sulfiden und –nitriden N2 - The thesis on hand deals with the development of new types of catalysts based on pristine metals and ceramic materials and their application as catalysts for the electrocatalytic water splitting reaction. In order to breathe life into this technology, cost-efficient, stable and efficient catalysts are imploringly desired. In this manner, the preparation of Mn-, N-, S-, P-, and C-containing nickel materials has been investigated together with the theoretical and electrochemical elucidation of their activity towards the hydrogen (and oxygen) evolution reaction. The Sabatier principle has been used as the principal guideline towards successful tuning of catalytic sites. Furthermore, two pathways have been chosen to ameliorate the electrocatalytic performance, namely, the direct improvement of intrinsic properties through appropriate material selection and secondly the increase of surface area of the catalytic material with an increased amount of active sites. In this manner, bringing materials with optimized hydrogen adsorption free energy onto high surface area support, catalytic performances approaching the golden standards of noble metals were feasible. Despite varying applied synthesis strategies (wet chemistry in organic solvents, ionothermal reaction, gas phase reaction), one goal has been systematically pursued: to understand the driving mechanism of the growth. Moreover, deeper understanding of inherent properties and kinetic parameters of the catalytic materials has been gained. N2 - Wasserstoff ist einer der vielversprechendsten Energieträger aufgrund seiner hohen massenbezogenen Energiedichte. In diesem Zusammenhang erlaubt die elektrokatalytische Wasserspaltung die einfache und saubere Herstellung von Wasserstoff. Allerdings erfordert die Trennung der relativ starken Wasserstoff-Sauerstoff Bindungen beträchtliche Energie und teure Edelmetalle wie Platin oder Iridium zeigen die höchste katalytische Aktivität mit geringer Überspannung und hohen Stromdichten was zu einem guten Wirkungsgrad führt. Aus dieser Motivation heraus befasst sich die vorliegende Arbeit mit der Entwicklung neuer Katalysatoren, die auf Metalllegierungen und Keramiken basieren, sowie ihrer Anwendung für die elektrokatalytische Wasserspaltung. Besonderes Augenmerk wurde auf die Herstellung von kostengünstigen mangan-, stickstoff-, schwefel-, phosphor- und kohlenstoffhaltigen Nickelwerkstoffen gelegt und deren Aktivität experimentell und theoretisch erforscht. Nickel wurde aufgrund seines relativ günstigen Preises und hohen Vorkommens gewählt. Das Prinzip von Sabatier – die Wechselwirkung zwischen Adsorbat und Substrat sollte weder zu stark noch zu schwach sein – wurde als Leitfaden für die Entwicklung effizienter Katalysatoren benutzt. Trotz unterschiedlich angewendeter Synthesestrategien (Synthese in organischen Lösungsmitteln, ionothermale Reaktion oder Gasphasenreaktion), wurde zusätzlich systematisch ein weiteres Ziel verfolgt: Die Wachstums- und Entstehungsmechanismen dieser Materialen zu ergründen. Darüber hinaus wurde ein tieferes Verständnis der inhärenten Eigenschaften und kinetischen Parameter der katalytischen Materialien gewonnen. KW - Wasserspaltung KW - Katalysatoren KW - Keramik KW - Legierungen KW - Materialwissenschaft KW - HER KW - OER KW - water splitting reaction KW - ceramics KW - metal alloys KW - material science KW - HER KW - OER Y1 - 2016 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-93296 ER - TY - THES A1 - Nagel, Alessandro T1 - Energie induzierte Nanopartikel-Substrat Interaktionen T1 - Energy induced nanoparticle substrate interactions N2 - Im Rahmen dieser Arbeit wurden Energie induzierte Nanopartikel-Substrat Interaktionen untersucht. Dazu wurden Goldnanopartikelanordnungen (AuNPA) auf verschiedenen Silizium-basierten Substraten hergestellt und der Einfluss eines Energieeintrages, genauer gesagt einer thermischen Behandlung oder des Metall-assistierten chemischen Ätzens (MaCE) getestet. Die Nanopartikelanordnungen, welche für die thermische Behandlung eingesetzt wurden, wurden nass-chemisch in Toluol synthetisiert, mit Thiol-terminiertem Polystyrol funktionalisiert und mittels Schleuderbeschichtung auf verschiedenen Substraten (drei Gläser und ein Siliziumwafer) in quasi-hexagonalen Mustern angeordnet. Diese AuNP-Anordnungen wurden mit Temperaturen zwischen 475 °C – 792 °C über verschiedene Zeiträume thermisch behandelt. Generell sanken die Nanopartikel in die Substrate ein, und es wurde festgestellt, dass mit Erhöhung der Glasübergangstemperatur der Substrate die Einsinktiefe der Nanopartikel abnahm. Die AuNPA auf Siliziumwafern wurden auf Temperaturen von 700 °C – 900 °C erhitzt. Die Goldnanopartikel sanken dabei bis zu 2,5 nm in das Si-Substrat ein. Ein Sintern der Nanopartikel fand ab einer Temperatur über 660 °C statt. Welcher Sintermechanismus der dominante ist konnte abschließend nicht eindeutig geklärt werden. Für die Untersuchung des Einflusses des zweiten Energieeintrages mittels MaCE wurden AuNPA sowie Goldkern-Silberschale-Anordnungen auf Siliziumsubstraten genutzt. Die AuNPA wurden mit Hilfe von Poly-N-Isopropylacrylamid Mikrogelen und Natriumcitrat-stabilisierten Goldnanopartikeln (Na-AuNP) bzw. Tetrachloridogoldsäure (TCG) präpariert. Es ergaben sich Nanopartikelanordnungen mit hemisphärischen Partikeln (aus Na-AuNP) und zum anderen Nanopartikelanordnungen mit sphärischen Partikeln (aus TCG). Durch eine anschließende Silberwachstumsreaktion konnten dann die dazugehörigen Goldkern-Silberschale Nanopartikelanordnungen erhalten werden. Beim MaCE konnten signifikante Unterschiede im Verhalten dieser vier Nanopartikelanordnungen festgestellt werden, z.B. mussten bei den hemisphärischen Partikelanordnungen höhere Wasserstoffperoxidkonzentrationen (0,70 M – 0,91 M) als bei den sphärischen Partikelanordnungen (0,08 M – 0,32 M) für das Ätzen eingesetzt werden, um ein Einsinken der Nanopartikel in das Substrat zu erreichen. N2 - In this work, energy-induced nanoparticle-substrate interactions were investigated. For this purpose, gold nanoparticle arrays (AuNPA) were fabricated on different silicon-based substrates and the influence of energy input, more specifically thermal treatment or metal-assisted chemical etching (MaCE), was tested. The nanoparticle arrays used for thermal treatment were wet-chemically synthesized in toluene, functionalized with thiol-terminated polystyrene and arranged in quasi-hexagonal patterns on different substrates (three glasses and one silicon wafer) by spin coating. These AuNP arrays were thermally treated with temperatures ranging from 475 °C - 792 °C for different time periods. In general, the nanoparticles sank into the substrates, and it was found that as the glass transition temperature of the substrates increased, the sinking depth of the nanoparticles decreased. The AuNPA on silicon wafers were heated to temperatures of 700 °C - 900 °C. The gold nanoparticles sank into the Si substrate by up to 2.5 nm. Sintering of the nanoparticles occurred at temperatures above 660 °C. It could not be clarified conclusively which sintering mechanism is dominant. For the investigation of the influence of the second energy input by means of MaCE, AuNPA as well as gold core-silver shell arrays on silicon substrates were used. The AuNPA were prepared using poly-N-isopropylacrylamide microgels and sodium citrate-stabilized gold nanoparticles (Na-AuNP) and tetrachloridoauric acid (TCG), respectively. Nanoparticle arrays with hemispherical particles (from Na-AuNP) or nanoparticle arrays with spherical particles (from TCG) resulted. A subsequent silver growth reaction was utilized for obtaining the corresponding gold core-silver shell nanoparticle assemblies. MaCE showed significant differences in the behavior of these four nanoparticle arrays, e.g., higher hydrogen peroxide concentrations (0.70 M - 0.91 M) had to be used for etching the hemispherical particle arrays than for the spherical particle arrays (0.08 M - 0.32 M) to achieve sinking of the nanoparticles into the substrate. KW - Nanopartikel Substrat Interaktionen KW - nanoparticle substrate interactions KW - Sintern von Nanopartikeln KW - nanoparticle sintering KW - kolloidale Lithographie KW - colloidal lithography Y1 - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-596396 ER - TY - THES A1 - Stahlhut, Frank T1 - Entwicklung neuer triphiler, fluorkohlenstofffreier Blockcopolymere und Untersuchung ihrer Eigenschaften für Multikompartiment-Mizellen T1 - Synthesis of new triphilic fluorocarbon -free block copolymers and analysis of their suitability as multicompartment micelles N2 - Neue Systeme für triphile, fluorkohlenstofffreie Blockcopolymere in Form von Acrylat-basierten thermoresponsiven Blockcopolymeren sowie Acrylat- bzw. Styrol-basierten Terblock-Polyelektrolyten mit unterschiedlich chaotropen Kationen des jeweiligen polyanionischen Blocks wurden entwickelt. Multikompartiment-Mizellen, mizellare Aggregate mit ultrastrukturiertem hydrophobem Mizellkern die biologischen Strukturen wie dem Humanalbumin nachempfunden sind, sollten bei der Selbstorganisation in wässriger Umgebung entstehen. Durch Verwendung apolarer und polarer Kohlenwasserstoff-Domänen anstelle von fluorophilen Fluorkohlenstoff-Domänen sollte erstmals anhand solcher triphilen Systeme nachgewiesen werden, ob diese in der Lage zur selektiven Aufnahme hydrophober Substanzen in unterschiedliche Domänen des Mizellkerns sind. Mit Hilfe von sequentieller RAFT-Polymerisation wurden diese neuen triphilen Systeme hergestellt, die über einen permanent hydrophilen, eine permanent stark hydrophoben und einen dritten Block verfügen, der durch externe Einflüsse, speziell die Induzierung eines thermischen Coil-to-globule-Übergangs bzw. die Zugabe von organischen, hydrophoben Gegenionen von einem wasserlöslichen in einen polar-hydrophoben Block umgewandelt werden kann. Als RAFT-Agens wurde 4-(Trimethylsilyl)benzyl(3-(trimethylsilyl)-propyl)-trithiocarbonat mit zwei unterschiedlichen TMS-Endgruppen verwendet, das kontrollierte Reaktions-bedingungen sowie die molekulare Charakterisierung der komplexen Copolymere ermöglichte. Die beiden Grundtypen der linearen ternären Blockcopolymere wurden jeweils in zwei 2 Modell-Systeme, die geringfügig in ihren chemischen Eigenschaften sowie in dem Blocklängenverhältnis von hydrophilen und hydrophoben Polymersegmenten variierten, realisiert und unterschiedliche Permutation der Blöcke aufwiesen. Als ersten Polymertyp wurden amphiphile thermoresponsive Blockcopolymere verwendet. Modell-System 1 bestand aus dem permanent hydrophoben Block Poly(1,3-Bis(butylthio)-prop-2-yl-acrylat), permanent hydrophilen Block Poly(Oligo(ethylenglykol)monomethyletheracrylat) und den thermoresponsiven Block Poly(N,N‘-Diethylacrylamid), dessen Homopolymer eine LCST-Phasenübergang (LCST, engl.: lower critical solution temperature) bei ca. 36°C aufweist. Das Modell-System 2 bestand aus dem permanent hydrophilen Block Poly(2-(Methylsulfinyl)ethylacrylat), dem permanent hydrophoben Block Poly(2-Ethylhexylacrylat) und wiederum Poly(N,N‘-Diethylacrylamid). Im ternären Blockcopolymer erhöhte sich, je nach Blocksequenz und relativen Blocklängen, der LCST-Übergang auf 50 – 65°C. Bei der Untersuchung der Selbstorganisation für die Polymer-Systeme dieses Typs wurde die Temperatur variiert, um verschieden mizellare Überstrukturen in wässriger Umgebung zu erzeugen bzw. oberhalb des LCST-Übergangs Multikompartiment-Mizellen nachzuweisen. Die Unterschiede in der Hydrophilie bzw. den sterischen Ansprüche der gewählten hydrophilen Blöcke sowie die Variation der jeweiligen Blocksequenzen ermöglichte darüber hinaus die Bildung verschiedenster Morphologien mizellarer Aggregate. Der zweite Typ basierte auf ein Terblock-Polyelektrolyt-System mit Polyacrylaten bzw. Polystyrolen als Polymerrückgrat. Polymere ionische Flüssigkeiten wurden als Vorlage der Entwicklung zweier Modell-Systeme genommen. Eines der beiden Systeme bestand aus dem permanent hydrophilen Block Poly(Oligo(ethylenglykol)monomethyletheracrylat, dem permanent hydrophoben Block Poly(2-Ethylhexylacrylat) sowie dem Polyanion-Block Poly(3-Sulfopropylacrylat). Die Hydrophobie des Polyanion-Blocks variierte durch Verwendung großer organischer Gegenionen, nämlich Tetrabutylammonium, Tetraphenylphosphonium und Tetraphenylstibonium. Analog wurde in einem weiteren System aus dem permanent hydrophilen Block Poly(4-Vinylbenzyltetrakis(ethylenoxy)methylether), dem permanent hydrophoben Block Poly(para-Methylstyrol) und Poly(4-Styrolsulfonat) mit den entsprechenden Gegenionen gebildet. Aufgrund unterschiedlicher Kettensteifigkeit in beiden Modell-Systemen sollte es bei der Selbstorganisation der mizellarer Aggregate zu unterschiedlichen Überstrukturen kommen. Mittels DSC-Messungen konnte nachgewiesen werden, dass für alle Modell-Systeme die Blöcke in Volumen-Phase miteinander inkompatibel waren, was eine Voraussetzung für Multikompartimentierung von mizellaren Aggregaten ist. Die Größe mizellarer Aggregate sowie der Einfluss externer Einflüsse wie der Veränderung der Temperatur bzw. der Hydrophobie und Größe von Gegenionen auf den hydrodynamischen Durchmesser mittels DLS-Untersuchungen wurden für alle Modell-Systeme untersucht. Die Ergebnisse zu den thermoresponsiven ternären Blockcopolymeren belegten , dass sich oberhalb der Phasenübergangstemperatur des thermoresponsiven Blocks die Struktur der mizellaren Aggregate änderte, indem der p(DEAm)-Block scheinbar kollabierte und so zusammen mit den permanent hydrophoben Block den jeweiligen Mizellkern bildete. Nach gewisser Equilibrierungszeit konnten bei Raumtemperatur dir ursprünglichen mizellaren Strukturen regeneriert werden. Hingegen konnte für die Terblock-Polyelektrolyt-Systeme bei Verwendung der unterschiedlich hydrophoben Gegenionen kein signifikanter Unterschied in der Größe der mizellaren Aggregate beobachtet werden. Zur Abbildung der mizellaren Aggregate mittels kryogene Transmissionselektronenmikroskopie (cryo-TEM) der mizellaren Aggregate war mit Poly(1,3-Bis(butylthio)-prop-2-yl-acrylat) ein Modell-System so konzipiert, dass ein erhöhter Elektronendichtekontrast durch Schwefel-Atome die Visualisierung ultrastrukturierter hydrophober Mizellkerne ermöglichte. Dieser Effekt sollte in den Terblock-Polyelektrolyt-Systemen auch durch die Gegenionen Tetraphenylphosphonium und Tetraphenylstibonium nachgestellt werden. Während bei den thermoresponsiven Systemen auch oberhalb des Phasenübergangs kein Hinweis auf Ultrastrukturierung beobachtet wurde, waren für die Polyelektrolyt-Systeme, insbesondere im Fall von Tetraphenylstibonium als Gegenion Überstrukturen zu erkennen. Der Nachweis der Bildung von Multikompartiment-Mizellen war für beide Polymertypen mit dieser abbildenden Methode nicht möglich. Die Unterschiede in der Elektronendichte einzelner Blöcke müsste möglicherweise weiter erhöht werden um Aussagen diesbezüglich zu treffen. Die Untersuchung von ortsspezifischen Solubilisierungsexperimenten mit solvatochromen Fluoreszenzfarbstoffen mittels „steady-state“-Fluoreszenzspektroskopie durch Vergleich der Solubilisierungsorte der Terblockcopolymere bzw. –Polyelektrolyte mit den jeweiligen Solubilisierungsorten von Homopolymer- und Diblock-Vorstufen sollten den qualitativen Nachweis der Multikompartimentierung erbringen. Aufgrund der geringen Mengen an Farbstoff, die für die Solubilisierungsexperimente eingesetzt wurden zeigten DLS-Untersuchungen keine störenden Effekte der Sonden auf die Größe der mizellaren Aggregate. Jedoch erschwerten Quench-Effekte im Falle der Polyelektrolyt Modell-Systeme eine klare Interpretation der Daten. Im Falle der Modell-Systeme der thermoresponsiven Blockcopolymere waren dagegen deutliche solvatochrome Effekte zwischen der Solubilisierung in den mizellaren Aggregaten unterhalb und oberhalb des Phasenübergangs zu erkennen. Dies könnte ein Hinweis auf Multikompartimentierung oberhalb des LCST-Übergangs sein. Ohne die Informationen einer Strukturanalyse wie z.B. der Röntgen- oder Neutronenkleinwinkelstreuung (SAXS oder SANS), kann nicht abschließend geklärt werden, ob die Solubilisierung in mizellaren hydrophoben Domänen des kollabierten Poly(N,N‘-Diethylacrylamid) erfolgt oder in einer Mischform von mizellaren Aggregaten mit gemittelter Polarität. N2 - New systems for triphilic fluorine-carbon-free block copolymers in the form of acrylate-based thermoresponsive block copolymers and acrylate- and styrene-based ternary block polyelectrolytes with different chaotropic cations of the respective polyanionic blocks have been developed. Multicompartment micelles, micellar aggregates with ultrastructured hydrophobic micelle core which are bio-inspired by biological structures like human serum albumin, should occur during the self-assembly in aqueous environment. By having nonpolar and polar hydrocarbon domains instead of fluorocarbon domains in these triphilic systems, it should be possible to demonstrate for the first time, whether they are capable of selectively uptaking hydrophobic substances in different hydrophobic domains of the micelle core. These new triphilic systems were prepared by using sequential RAFT polymerization. These polymers are based on a permanently hydrophilic polymer block; a permanent highly hydrophobic block and a third block which is sensitive to the result of external influences, especially the induction of a thermal coil-to-globule transition in the case of thermoresponsive block copolymers or adding organic hydrophobic counter ions in the case of block polyelectrolytes. The third block for each system can be converted from a water-soluble in a polar hydrophobic block due to external stimulus. The RAFT agent, 4- (trimethylsilyl) benzyl (3- (trimethylsilyl) propyl) trithiocarbonate, has two different TMS-labeled end groups, which enable controlled polymerization conditions and the exact molecular characterization of the complex copolymers. Each of the two basic types of linear ternary block copolymers, which were prepared for this work, were implemented in two 2 model systems that varied slightly in their chemical properties, as well as in the block length ratio of hydrophilic and hydrophobic polymer segments and different block sequences. The first polymer type is based on amphiphilic thermoresponsive block copolymers. Model system 1 consisted of the permanent hydrophobic block p(1,3-bis (butylthio) prop-2-yl acrylate), the permanently hydrophilic block p(oligo (ethylene glycol) mono methyl ether acrylate) and the thermoresponsive block p(N,N–diethyl acrylamide) whose homopolymer has a LCST (lower critical solution temperature) like phase transition approximately about 36°C. The model system 2 consisted of the permanent hydrophilic block p(2- (methylsulfinyl) ethyl acrylate), the permanently hydrophobic block p(2-ethylhexyl acrylate) and again p(N,N–diethyl acrylamide). The LCST is increased in ternary block copolymers to 50 - 65°C, depending on the block sequence and relative block lengths. To study the self-assembly of these two polymer systems, their aqueous micellar solutions where analyzed above and below LCST to produce different micellar superstructures in an aqueous environment and to prove the occurrence of multicompartment micelles above LCST. The differences in the hydrophilicity or the individual steric requirements of the chosen hydrophilic blocks as well as the variation of the respective block sequences lead additionally to different morphologies of micellar aggregates. The second type of polymers is based on ternary block polyelectrolytes with polyacrylates and polystyrenes as polymer backbone respectively. Polymeric ionic liquids were taken as role model for the development of two model systems of block polyelectrolytes. One of the two systems consisting of the permanently hydrophilic p(oligo (ethylene glycol) mono methyl ether acrylate), the permanent hydrophobic block p(2-ethylhexyl acrylate) and the polyanion block p(3-sulfopropyl acrylate) (= model system 3). The hydrophobicity of the polyanion blocks varied largely by using organic counter ions, namely tetrabutyl ammonium, tetraphenyl phosphonium and tetraphenyl stibonium. Analogously, model system 4 consists of a permanently hydrophilic block p(4-vinylmethoxybenzyltetrakis (oxyethylene) ether), a permanently hydrophobic block p(para-methyl styrene) and p(4-styrene sulfonate) formed with the corresponding counter ions. Due to different chain stiffness in both model systems there should be different superstructures of micellar aggregates in aqueous solution. DSC (differential scanning calorimetry) measurements could demonstrate that the all polymer blocks for each modell system were incompatible with each other in bulk phase. This property is a prerequisite for ultra-structured hydrophobic cores of micellar aggregates. The influence of external factors such as change of temperature or change of hydrophobicity and size of counter ions on the size of micellar aggregates for all model systems was examined by DLS measurements. The results on the thermoresponsive ternary block copolymers showed that above the phase transition temperature of the thermo-responsive block the structure of micellar aggregates changed because the p(N,N–diethyl acrylamide) block apparently collapsed formed a subdivided micellar core together with the permanently hydrophobic block. Some equilibration time for the thermoresponsive block copolymer systems were needed to ensure that heoriginal micellar structures could be regenerated after cooling heated auqeous micellar solutions to room temperature. However, for the ternary block polyelectrolytes, there was no significant difference in the size of the micellar aggregates due to the exchange of counter ions which differ by their hydrophobicity. For imaging the micellar aggregates and especially multicompartment micelles by means of cryogenic transmission electron microscopy (cryo-TEM), the model system 1 with p(1,3-bis (butylthio) -prop-2-yl acrylate) as permanently hydrophobic block was specifically designed so that the increased electron density contrast by sulfur atoms should enable the visualization of multicompartment micelles. This effect should be readjusted in the ternary block polyelectrolyte systems by the counter ions tetraphenyl phosphonium and tetraphenyl stibonium. While in the thermoresponsive block copolymer systems it was possible to observe new kinds of micellar aggregates above LCST, there was no indication on ultrastructuring in the micellar cores for all analyzed systems. Otherwise by using tetraphenyl stibonium counter ions in block polyelectrolyte systems, some kind of ultrastructured micellar aggregates with seemingly subdivided micellar cores could be observed. The detection of the formation of multicompartment micelles was not possible for both types of polymers with this direct imaging method. The differences in the electron density of individual blocks might have to be further increased to make statements concerning the self-assembly into multicompartment micelles. Site-specific solubilization experiments with solvatochromic fluorescent dyes by using steady-state fluorescence spectroscopy should provide the qualitative evidence of multicompartment micelles. The selective solubilization areas of different kinds of substances in self-assembled structures of all ternary block copolymers and ternary polyelectrolytes were compared with the solubilization areas in their respective homopolymer and diblock precursors. Because of the small amounts of dye that have been used for the solubilization DLS measurements showed no interfering effects of the probes on the size of the micellar aggregates. However, quenching effects made a clear interpretation of the data in the case of polyelectrolyte model systems difficult. In the case of model systems 1 and 2 a change of the solubilization areas of fluorescent dyes due to the occurrence significant solvatochromic effects (stokes shifts) above LCST could be observed. The effect was reversibel. This could be an indication that the micellar aggregates self-assemble into multicompartment micelles above the LCST transition. Without the information of a structural analysis such as the small angle x-ray scattering or small angle neutron scattering (SAXS or SANS), it cannot be conclusively clarified whether the solubilization occurs in micellar hydrophobic domains of the collapsed p(N,N–diethyl acrylamide), or in a mixed form of micellar aggregates with mixed polarity. KW - Blockcopolymere KW - RAFT KW - Multikompartiment-Mizellen KW - cryo-TEM KW - Solubilisierung KW - Fluoereszenzsonden KW - block copolymers KW - triphilic KW - RAFT KW - multicompartment micelles KW - cryo-TEM KW - fluorescent dyes KW - fluorescence probe experiments KW - triphil Y1 - 2016 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-96299 SP - iv, 191 ER - TY - THES A1 - Heinke, David T1 - Entwicklung biokompatibler superparamagnetischer Nanopartikel für den Einsatz als in vivo-Diagnostikum insbesondere im Magnetic Particle Imaging T1 - Development of biocompatible and superparamagnetic nanoparticles for use as in vivo diagnostics especially in magnetic particle imaging N2 - Magnetische Eisenoxidnanopartikel werden bereits seit geraumer Zeit erfolgreich als MRT-Kontrastmittel in der klinischen Bildgebung eingesetzt. Durch Optimierung der magnetischen Eigenschaften der Nanopartikel kann die Aussagekraft von MR-Aufnahmen verbessert und somit der diagnostische Wert einer MR-Anwendung weiter erhöht werden. Neben der Verbesserung bestehender Verfahren wird die bildgebende Diagnostik ebenso durch die Entwicklung neuer Verfahren, wie dem Magnetic Particle Imaging, vorangetrieben. Da hierbei das Messsignal von den magnetischen Nanopartikeln selbst erzeugt wird, birgt das MPI einen enormen Vorteil hinsichtlich der Sensitivität bei gleichzeitig hoher zeitlicher und räumlicher Auflösung. Da es aktuell jedoch keinen kommerziell vertriebenen in vivo-tauglichen MPI-Tracer gibt, besteht ein dringender Bedarf an geeigneten innovativen Tracermaterialien. Daraus resultierte die Motivation dieser Arbeit biokompatible und superparamagnetische Eisenoxidnanopartikel für den Einsatz als in vivo-Diagnostikum insbesondere im Magnetic Particle Imaging zu entwickeln. Auch wenn der Fokus auf der Tracerentwicklung für das MPI lag, wurde ebenso die MR-Performance bewertet, da geeignete Partikel somit alternativ oder zusätzlich als MR-Kontrastmittel mit verbesserten Kontrasteigenschaften eingesetzt werden könnten. Die Synthese der Eisenoxidnanopartikel erfolgte über die partielle Oxidation von gefälltem Eisen(II)-hydroxid und Green Rust sowie eine diffusionskontrollierte Kopräzipitation in einem Hydrogel. Mit der partiellen Oxidation von Eisen(II)-hydroxid und Green Rust konnten erfolgreich biokompatible und über lange Zeit stabile Eisenoxidnanopartikel synthetisiert werden. Zudem wurden geeignete Methoden zur Formulierung und Sterilisierung etabliert, wodurch zahlreiche Voraussetzungen für eine Anwendung als in vivo-Diagnostikum geschaffen wurden. Weiterhin ist auf Grundlage der MPS-Performance eine hervorragende Eignung dieser Partikel als MPI-Tracer zu erwarten, wodurch die Weiterentwicklung der MPI-Technologie maßgeblich vorangetrieben werden könnte. Die Bestimmung der NMR-Relaxivitäten sowie ein initialer in vivo-Versuch zeigten zudem das große Potential der formulierten Nanopartikelsuspensionen als MRT-Kontrastmittel. Die Modifizierung der Partikeloberfläche ermöglicht ferner die Herstellung zielgerichteter Nanopartikel sowie die Markierung von Zellen, wodurch das mögliche Anwendungsspektrum maßgeblich erweitert wurde. Im zweiten Teil wurden Partikel durch eine diffusionskontrollierte Kopräzipitation im Hydrogel, wobei es sich um eine bioinspirierte Modifikation der klassischen Kopräzipitation handelt, synthetisiert, wodurch Partikel mit einer durchschnittlichen Kristallitgröße von 24 nm generiert werden konnten. Die Bestimmung der MPS- und MR-Performance elektrostatisch stabilisierter Partikel ergab vielversprechende Resultate. In Vorbereitung auf die Entwicklung eines in vivo-Diagnostikums wurden die Partikel anschließend erfolgreich sterisch stabilisiert, wodurch der kolloidale Zustand in MilliQ-Wasser über lange Zeit aufrechterhalten werden konnte. Durch Zentrifugation konnten die Partikel zudem erfolgreich in verschiedene Größenfraktionen aufgetrennt werden. Dies ermöglichte die Bestimmung der idealen Aggregatgröße dieses Partikelsystems in Bezug auf die MPS-Performance. N2 - Magnetic nanoparticles have long been successfully implemented in the clinic as contrast agents for magnetic resonance imaging (MRI). Through optimization of the nanoparticles’ magnetic properties, an improvement in the resulting diagnostic images can be achieved, which in turn increases the diagnostic value of the MRI procedure. The advancement of diagnostic imaging is brought about not only through the improvement of established diagnostic techniques, but also through the development of new methodologies such as Magnetic Particle Imaging (MPI). In MPI, the measured signal arises directly from the magnetic particles and, thus, the technique holds great promise in terms of sensitivity and spatial resolution. Since there are currently no commercially available MPI tracers for in vivo use, the development of optimal tracer materials that are biocompatible and, thus, suitable for in vivo application, is becoming increasingly important. Therefore, the aim of this work was to develop biocompatible superparamagnetic iron oxide nanoparticles for application as an in vivo diagnostic agent in particular for MPI. Even though the focus lay on the development of an MPI tracer, the MR performance of the generated magnetic nanoparticles was also addressed, since such particles can be also be used as an MRI contrast agent with improved contrast efficacy. Synthesis of the superparamagnetic iron oxide nanoparticles was performed either via partial oxidation of precipitated iron (II) hydroxide and green rust or through a diffusion-controlled co-precipitation reaction in a hydrogel. The partial oxidation synthetic route gave rise to biocompatible and colloidally stable iron oxide nanoparticles. Furthermore, suitable methods for the formulation and sterilization of these particles were developed, enabling many of the prerequisites for successful in vivo application to be addressed. The resulting outstanding magnetic particle spectra (MPS) performance of the synthesized nanoparticles enables their suitability as an effective MPI tracer, assisting the advancement of the MPI technology. Moreover, the MR relaxivity values of the particles as well as results obtained from a preliminary in vivo MRI experiment revealed the high potential of the formulated nanoparticle suspensions for application as MRI contrast agents. In addition, chemical modification of the particle surface was performed, which enables the fabrication of target-specific nanoparticles as well as magnetic labeling of certain cell types e.g. stem cells. Nanoparticle synthesis via a diffusion-controlled co-precipitation strategy in a hydrogel, which is a bioinspired modification of the classical co-precipitation reaction, resulted in particles with a mean crystal diameter of 24 nm. Measurement of the MPS and MR performances of such electrostatically-stabilized particles revealed promising results. So as to promote the development of these particles for use as in vivo diagnostic agents, the particles were sterically stabilized and were found to be colloidally stable on the long-term in aqueous solution. Through centrifugation, the particles were successfully separated in batches of varying mean particle sizes, allowing for the determination of the ideal size of this particle system in terms of the MPS performance. KW - Magnetic Particle Imaging KW - Magnetresonanztomograpgie KW - magnetic resonance imaging KW - iron oxide nanoparticle KW - Eisenoxidnanopartikel Y1 - 2017 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-406196 ER - TY - THES A1 - Büchele, Dominique T1 - Entwicklung einer robusten Online-Methode zur Bestimmung von Nährelementen in Ackerböden mit einem Energie-dispersiven RFA-Sensor N2 - Im Rahmen der vom Bundesministerium für Bildung und -forschung geförderten Forschungsinitiative „BonaRes – Boden als nachhaltige Ressource der Bioökonomie“ soll sich das Teilprojekt „I4S – integrated system for site-specific soil fertility management“ der Entwicklung eines integrierten Systems zum ortsspezifischen Management der Bodenfruchtbarkeit widmen. Hierfür ist eine Messplattform zur Bestimmung relevanter Bodeneigenschaften und der quantitativen Analyse ausgewählter Makro- und Mikronährstoffe geplant. In der ersten Phase dieses Projekts liegt das Hauptaugenmerk auf der Kalibrierung und Validierung der verschiedenen Sensoren auf die Matrix Boden, der Probennahme auf dem Acker und der Planung sowie dem Aufbau der Messplattform. Auf dieser Plattform sollen in der zweiten Phase des Projektes die verschiedenen Bodensensoren installiert, sowie Modelle und Entscheidungsalgorithmen zur Steuerung der Düngung und dementsprechend Verbesserung der Bodenfunktionen erstellt werden. Ziel der vorliegenden Arbeit ist die Grundlagenuntersuchung und Entwicklung einer robusten Online-Analyse mittels Energie-dispersiver Röntgenfluoreszenzspektroskopie (EDRFA) zur Quantifizierung ausgewählter Makro- und Mikronährstoffe in Böden für eine kostengünstige und flächendeckende Kartierung von Ackerflächen. Für die Entwicklung eines Online-Verfahrens wurde ein dem Stand der Technik entsprechender Röntgenfluoreszenzmesskopf in Betrieb genommen und die dazugehörigen Geräteparameter auf die Matrix Boden optimiert. Die Bestimmung der analytischen Qualitäts-merkmale wie Präzision und Nachweisgrenzen fand für eine Auswahl an Nährelementen von Aluminium bis Zink statt. Um eine möglichst Matrix-angepasste Kalibrierung zu erhalten, wurde sowohl mit zertifizierten Referenzmaterialien (CRM), als auch mit Ackerböden kalibriert. Da einer der größten Nachteile der Röntgenfluoreszenzanalyse die Beeinflussung durch Matrixeffekte ist, wurde neben der klassischen univariaten Datenauswertung auch die chemometrische multivariate Methode der Partial Least Squares Regression (PLSR) eingesetzt. Die PLSR bietet dabei den Vorteil, Matrixeffekte auszugleichen, wodurch robustere Kalibriermodelle erhalten werden können. Zusätzlich wurde eine Hauptkomponentenanalyse (PCA) durchgeführt, um Gemeinsamkeiten und Ausreißer innerhalb des Probensets zu identifizieren. Es zeigte sich, dass eine Klassifizierung der Böden anhand ihrer Textur Sand, Schluff, Lehm und Ton möglich ist. Aufbauend auf den Ergebnissen idealer Bodenproben (zu Tabletten gepresste luftgetrocknete Proben mit Korngrößen < 0,5 mm) wurde im Verlauf dieser Arbeit die Probenvorbereitung immer weiter reduziert und der Einfluss verschiedener Kenngrößen untersucht. Diese Einflussfaktoren können die Dichte und die Homogenität der Probe, sowie Korngrößeneffekte und die Feuchtigkeit sein. Anhand des RMSE (Wurzel der mittleren Fehlerquadratsumme) und unter Berücksichtigung der Residuen werden die jeweils erstellten Kalibriermodelle miteinander verglichen. Um die Güte der Modelle zu bewerten, wurden diese mit einem Testset validiert. Hierfür standen 662 Bodenproben von 15 verschiedenen Standorten in Deutschland zur Verfügung. Da die Ergebnisse an gepressten Tabletten für die Elemente Al, Si, K, Ca, Ti, Mn, Fe und Zn den Anforderungen für eine spätere Online-Analyse entsprechen, wurden im weiteren Verlauf dieser Arbeit Kalibriermodelle mit losen Bodenproben erstellt. Auch hier konnten gute Ergebnisse durch ausreichende Nachweisgrenzen und eine niedrige gemittelte Messabweichung bei der Vorhersage unbekannter Testproben erzielt werden. Es zeigte sich, dass die Vorhersagefähigkeit mit der multivariaten PLSR besser ist als mit der univariaten Datenauswertung, insbesondere für die Elemente Mn und Zn. Der untersuchte Einfluss der Feuchtigkeit und der Korngrößen auf die Quantifizierung der Elementgehalte war vor allem bei leichteren Elementen deutlich zu sehen. Es konnte schließlich eine multivariate Kalibrierung unter Berücksichtigung dieser Faktoren für die Elemente Al bis Zn erstellt werden, so dass ein Einsatz an Böden auf dem Acker möglich sein sollte. Eine höhere Messunsicherheit muss dabei einkalkuliert werden. Für eine spätere Probennahme auf dem Feld wurde zudem der Unterschied zwischen statischen und dynamischen Messungen betrachtet, wobei sich zeigte, dass beide Varianten genutzt werden können. Zum Abschluss wurde der hier eingesetzte Sensor mit einem kommerziell erhältlichen Hand-Gerät auf sein Quantifizierungspotential hin verglichen. Der Sensor weist anhand seiner Ergebnisse ein großes Potential als Online-Sensor für die Messplattform auf. Die Ergebnisse unter Laborbedingungen zeigen, dass eine robuste Analyse Ackerböden unter Berücksichtigung der Einflussfaktoren möglich ist. N2 - As part of the research initiative "BonaRes – soil as sustainable resource of the bioeconomy", funded by the Federal Ministry of Education and Research, the subproject I4S is responsible for the development of an integrated system for site-specific soil fertility management. For this purpose, a measuring platform for the determination of relevant soil properties and the quantitative analysis of selected macro- and micronutrients is planned. In the first part of this project, the focus will be on calibration and validation of different sensors on the matrix soil, sampling on the field as well as designing and construction of the measurement platform. In the second part of the project, the soil sensors were installed and models as well as decision making algorithms for the control of fertilization and corresponding improvement of soil functions were established. The aim of the present work is the investigation and development of a robust online-analysis with energy-dispersive X-ray fluorescence spectroscopy (EDXRF) for the quantification of selected macro- and micronutrients in soils for a low-cost and area-wide mapping of arable land. For the development of an online method, a state-of-the-art X-ray fluorescence sensor was launched, and the corresponding device parameters were optimized for the matrix soil. The determination of the analytical figures of merit such as precision and detection limit took place for a selection of nutrients Al, Si, P, S, K, Ca, Ti, Mn, Fe, Cu and Zn. In order to obtain a matrix-specific calibration, certified reference materials (CRM) as well as a selection of agricultural soils was used. Since one of the biggest disadvantages of X-ray fluorescence analysis is the influence of matrix effects, the multivariate method of partial least squares regression (PLSR) in addition to the classical univariate data analysis was applied. PLSR offers the advantage of compensating matrix effects, resulting in more robust calibration models. Furthermore, a principal component analysis (PCA) was performed to identify similarities and outliers within the sample set. A classification of the soils based on their texture sand, silt, loam and clay was possible. Based on the results of ideal soil samples: pelleted air-dried samples with particle sizes < 0.5 mm, the sample preparation was reduced, and the influence of different properties was investigated. These factors can be the density and homogeneity of the sample, as well as grain size and moisture. Based on the parameter RMSE and considering the residuals, the created calibration models were compared with each other. To evaluate the quality of the models, validation with a test set was done. For this purpose, 662 soil samples from 15 different locations in Germany were available. Since the results on pressed pellets for the elements Al, Si, K, Ca, Ti, Mn, Fe and Zn correspond to the requirements for later online-analysis, further calibration models with loose soil samples were prepared. Again, good results could be achieved with sufficient detection limits and a low mean error in the prediction of unknown test samples. The predictive capability of the multivariate PLSR is better than that of the univariate data analysis, especially for the elements Mn and Zn. The influence of moisture and grain sizes on the quantification of elemental contents is clearly visible, especially for lighter elements. A multivariate calibration for the elements Si to Zn was possible, so that it is possible to measure soils in the field. A higher measurement uncertainty must be considered. For any subsequent sampling on the field, the difference between static and dynamic measurements was also considered showing that both variants could be used. Finally, the used sensor was compared with a commercially available handheld device for its quantification potential. Based on the results, the sensor has great potential as an online-sensor on the platform. The results under laboratory conditions show that the robust analysis of arable soils is possible considering the influencing factors. T2 - Development of a robust online-method for determination of nutrients in agricultural soils using an EDXRF-sensor KW - Chemometrie KW - Boden KW - RFA KW - PCA KW - PLSR KW - ICP-OES KW - Nährelemente KW - Soil KW - Chemometrics KW - Nutrients KW - XRF KW - PCA KW - PLSR KW - ICP-OES Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-483735 ER - TY - THES A1 - Salffner, Katharina T1 - Entwicklung eines breitbandigen Cavity-Ring-Down-Spektrometers unter Verwendung nahinfraroter, inkohärenter Strahlung T1 - Development of a broadband cavity ring-down spectrometer using incoherent near-infrared radiation N2 - In der vorliegenden Arbeit werden verschiedene Spektrometer für die Analyse von Gasen bzw. Gasgemischen vorgestellt und deren Design, Aufbau, Charakterisierung und Optimierung beschrieben. Das Resultat der Optimierung und Weiterentwicklungen ist ein spektral breitbandiges Cavity-Ring-Down-Spektrometer (CRD-Spektrometer). Ausgangspunkt der hier vorgestellten Arbeit ist ein Spektrometer auf Basis klassischer Absorptionsspektroskopie in einer Multireflexionszelle. Für dieses Spektrometer wurde als Strahlquelle ein Superkontinuumlaser verwendet. Der Vorteil dieses Spektrometers liegt in seiner Kompaktheit. Mit diesem Spektrometer wurden Absorptionsspektren von mehreren Reingasen und einem Gasgemisch über einen Wellenlängenbereich von 1500 nm – 1700 nm aufgenommen. Der qualitative Vergleich mit zu erwartenden Spektren, welche auf der HITRAN-Datenbank basieren, zeigte eine gute Übereinstimmung. Die quantitative Interpretierbarkeit der Daten war jedoch stark eingeschränkt aufgrund des hohen zufälligen und systematischen Fehlers der Messungen. Als Konsequenz aus der als nicht zufriedenstellend bewerteten quantitativen Interpretierbarkeit der Daten wurde eine alternative Messmethode gesucht, welche eine höhere Sensitivität und Genauigkeit ermöglicht. Die Wahl fiel auf die Cavity-Ring-Down-Spektroskopie, eine resonatorgestützte Variante der Absorptionsspektroskopie. Wesentliche Vorteile dieser Technik sind a) die Unabhängigkeit von Leistungsschwankungen der Strahlquelle, b) ein effektiver Absorptionsweg von bis zu mehreren Kilometern, welcher sich unmittelbar auf die Sensitivität der Messungen auswirkt, c) die Ermittlung absoluter Absorberkonzentrationen, ohne die Notwendigkeit einer Kalibrierung oder den Vergleich mit einer Referenzzelle und d) die Vernachlässigbarkeit von Absorptionen außerhalb des Resonators. Als notwendiger Zwischenschritt auf dem Weg zu einem breitbandigen CRD-Spektrometer wurde zunächst ein monochromatisches CRD-Spektrometer designt, aufgebaut und charakterisiert. Für die effektive Einkopplung von Strahlungsenergie in einen Resonator ist die Anpassung der Strahlparameter an die Mode des Resonators notwendig. Voraussetzung dieser Anpassung ist die Kenntnis der Strahlparameter, welche experimentell ermittelt wurden. Im Laufe des Aufbaus des Spektrometers ergab sich, dass trotz der Modenanpassung die Einkopplung der Strahlungsenergie in den Resonator gestört wurde. Daraufhin wurden systematisch mögliche Ursachen dieser Störung untersucht und das Spektrometer optimiert. Mit diesem optimierten Spektrometer wurden Spektren gemessen, welche sowohl qualitativ als auch quantitativ gut mit den zu erwartenden Spektren übereinstimmen. Als Nachweisgrenze dieses Spektrometers wurde ein Wert für den Absorptionskoeffizienten alpha von 10^-8 cm-1 bestimmt. Mit dem monochromatischen CRD-Spektrometer war es zudem möglich, isotopenspezifische Messungen durchzuführen. Für das breitbandige Spektrometer wurde als Strahlquelle eine ASE-Diode (amplified spontaneous emission) verwendet. Dabei handelt es sich um eine inkohärente Strahlquelle. Mittels Messungen nach dem Prinzip der Cavity-Enhanced-Absorptionsspektroskopie wurde die generelle Funktionalität des resonatorgestützten Spektrometers überprüft. Anschließend wurden die wellenlängenabhängigen Abklingsignale des leeren und des mit einem CO2-Luft-Gemisch gefüllten Resonators gemessen und ebenfalls mit den zu erwartenden Spektren verglichen. Qualitativ stimmen die experimentellen Spektren gut mit den zu erwartenden Spektren überein. Für die quantitative Interpretation der Daten wurde ein spezieller Algorithmus entwickelt, der die spektrale Auflösung des Systems berücksichtigt. Mit dem vorgestellten Spektrometer ist so die qualitative und quantitative Interpretation der Spektren möglich. Die Nachweisgrenze des breitbandigen Cavity-Ring-Down-Spektrometers wurde zu einem Wert von alpha = 8x10^-7 cm-1 bestimmt. Der systematischen und der zufällige Fehler der Messungen lagen bei Werten von ca. 1%. Bei diesem Spektrometer handelt es sich um einen Prototyp. Mittels Optimierung des Systems lassen sich sowohl der Wert der Nachweisgrenze als auch die Fehler der Messungen verbessern. N2 - This thesis presents the design, set-up, characterisation and optimization of various spectrometers to be used for the analysis of gases and gas mixtures. The result of this optimization and its further development is a spectrally broadband cavity ring-down spectrometer (CRD spectrometer), which uses an incoherent light source that emits in the near-infrared. The starting point of the development was a spectrometer which is based on classic absorption spectroscopy inside a multipass cell. This spectrometer uses a supercontinuum laser as light source. The advantage of this spectrometer is its compactness. With this spectrometer, the spectra of various gases and a gas mixture were detected in the spectral range of 1500 nm to 1700 nm. The experimentally derived spectra are in good qualitative accordance to expected spectra based on the HITRAN database. Nevertheless, the qualitative interpretation of the data reveals significant systematic and random errors. As a consequence, a different spectroscopic approach was chosen. The method of choice was cavity ring-down spectroscopy. The advantages of this technique are a) the independence from power fluctuations of the light source, b) an effective absorption path length of up to several kilometres, c) absolute measurement of absorber concentration and d) independence of absorption outside of the cavity. As an important intermediate step on the way to the broadband CRD spectrometer, a monochromatic CRD spectrometer was designed, set up and characterised. To effectively couple light into the cavity, the beam parameters have to be matched to the cavity’s mode. Prerequisite of this mode matching is the knowledge of the beam parameters, which were determined experimentally. Despite this mode matching, the coupling of the light into the cavity turned out to be instable. The cause of that disturbance was systematically investigated, which let to an optimization of the system. The spectra measured with this optimized system were in very good qualitative and quantitative agreement with the expected spectra. The limit of detection of this spectrometer was determined to an absorption coefficient alpha of 10^-8 cm-1. Furthermore, isotope-selective measurements were performed. The light source of the broadband CRD spectrometer is an amplified spontaneous emission diode, which is an incoherent light source. The general functionality of the spectrometer was first tested by means of CEAS measurements (cavity enhanced absorption spectroscopy). Afterwards, the wavelength dependent ring-down signals of the empty cavity and the cavity filled with a CO2 air mixture were detected. The qualitative comparison with the expected data shows very good agreement. For the quantitative interpretation of the experimental data, a special algorithm was developed. Thereby the data measured with the presented spectrometer can be interpreted both qualitatively and quantitatively. The limit of detection of the broadband CRD spectrometer was determined to a value of alpha = 8x10^-7 cm-1. The systematic and the random error are in the range of 1 %. The presented spectrometer is a prototype. Therefore the systematic and random error will be improved by further optimization of the spectrometer. KW - Spektroskopie KW - Nahinfrarot (NIR) KW - Breitband KW - Cavity Ring-Down KW - Gassensorik KW - spectroscopy KW - near-infrared (NIR) KW - broadband KW - cavity ring-down KW - gas sensing Y1 - 2013 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-68952 ER - TY - THES A1 - Melchert, Christian T1 - Entwicklung multi-stimuli sensitiver Materialien auf der Basis von flüssigkristallinen Elastomeren T1 - Development of multi-stimuli sensitive materials based on liquid-crystalline elastomers N2 - Aufgrund der zunehmenden technischen Ansprüche der Gesellschaft sind sich aktiv bewegende Polymere in den Mittelpunkt aktueller Forschung gerückt. Diese spielen bei Anwen-dungen im Bereich von künstlichen Muskeln und Implantaten für die minimal invasive Chirurgie eine wichtige Rolle. Vor allem Formänderungs- und Formgedächtnispolymere stehen dabei im wissenschaftlichen Fokus. Während die kontaktlose Deformation einer permanenten Form in eine temporäre metastabile Form, charakteristisch für Formände-rungspolymere ist, kann bei Formgedächtnis-Materialien die temporäre Form, aufgrund der Ausbildung reversibler, temporärer Netzpunkte, fixiert werden. Ein Polymermaterial, das eine Kombination beider Funktionen aufweist würde zu einem Material führen welches kontaktlos in eine temporäre Form deformiert und in dieser fixiert werden kann. Zusätzlich würde aufgrund der kontaktlosen Deformation die Reversibilität dieser Funktion gewähr-leistet sein. Ein solches Material ist bislang noch nicht beschrieben worden. In dieser Arbeit wird untersucht, ob durch die Kopplung zweier separat schaltbarer, be-kannter Funktionen eine neue schaltbare Funktion erzielt werden kann. Daher wurden multi-stimuli sensitive Materialien entwickelt die eine Kopplung des Formänderungs- und des Formgedächtniseffektes aufweisen. Dazu wurden zwei Konzepte entwickelt, die sich hinsichtlich der Reihenfolge der verwendeten Stimuli unterscheiden. Im ersten Konzept wurden flüssigkristalline Elastomere basie-rend auf Azobenzenderivaten aufgebaut und hinsichtlich der Kombination des licht-induzierten Formänderungseffektes mit dem thermisch-induzierten Formgedächtniseffekt untersucht. Diese orientierten Netzwerke weisen oberhalb der Glasübergangstemperatur (Tg) eine kontaktlose Verformung (Biegung) durch Bestrahlung mit UV-Licht des geeigneten Wellenlängenbereichs auf, wodurch eine temporäre Form erhalten wurde. Hierbei spielt der Vernetzungsgrad eine entscheidende Rolle bezüglich der Ausprägung dieser Biegung. Eine fixierte, temporäre Form konnte durch gleichzeitiges Abkühlen des Materials unterhalb von Tg während der Bestrahlung mit UV-Licht erhalten werden. Nach erneutem Aufheizen über Tg konnte die Originalform wiederhergestellt werden. Dieser Vorgang konnte reversibel durchgeführt werden. Damit wurde gezeigt, dass eine neue schaltbare Funktion erzielt wurde, die auf der Kopplung des lichtinduzierten Formänderungs- mit dem thermisch-induzierten Formgedächtniseffekt basiert. Die Abstimmung der einzelnen Funktion wird in diesem Konzept über die Morphologie des Systems gewährleistet. Diese neue Funktion ermöglicht eine kontaktlose Deformation des Materials in eine temporäre Form, welche fixiert werden kann. Im zweiten Konzept wurde eine Kopplung des thermisch induzierten Formänderungs- mit dem licht-induzierten Formgedächtniseffekt angestrebt. Um dies zu realisieren wurden nematisch, flüssigkristalline Hauptkettenelastomere (NMC-LCE) entwickelt, die eine nied-rige Übergangstemperatur der nematischen in die isotrope Phase (TNI), als auch einen aus-geprägten thermisch induzierten Formänderungseffekt aufweisen. Zusätzlich wurde eine photosensitive Schicht aufgebaut, die Cinnamylidenessigsäuregruppen in der Seitenkette eines Polysiloxanrückgrates aufweist. Die Reversibilität der photoinduzierten [2+2]-Cycloaddition konnte für dieses photosensitive Polymer beobachtet werden, wodurch die-ses Polymersystem in der Lage ist reversible temporäre Netzpunkte, aufgrund der Bestrah-lung mit UV-Licht, auszubilden. Die kovalente Anbindung der photosensitiven Schicht an die Oberfläche des flüssigkristallinen Kerns wurde erfolgreich durchgeführt, wodurch ein Multi-Komponenten-System aufgebaut wurde. Die Kombination des thermisch-induzierten Formänderungs- mit dem licht-induzierten Formgedächtniseffektes wurde anhand dieses Systems untersucht. Während die Einzelkomponenten die erforderliche Funktion zeigten, ist hier noch Arbeit in der Abstimmung beider Strukturen zu leisten. Insbesondere die Variation der Schichtdicken beider Komponenten steht im Fokus zukünftiger Arbeiten. In dieser Arbeit wurde durch die Kopplung von zwei separat schaltbaren, bekannten Funktionen eine neue schaltbare Funktion erzielt. Dies setzt voraus, dass die Einzelkomponenten hinsichtlich einer Funktion schaltbar sind und in einem Material integriert werden können. Des Weiteren müssen die beiden Funktionen mit unterschiedlichen Stimuli geschaltet werden. Ein wichtiger Schritt bei der Kopplung der Funktionen, ist die Abstimmung der beiden Komponenten. Dies kann über die Variation der Morphologie oder der Struktur erzielt werden. Anhand der Vielzahl der vorhandenen stimuli-sensitiven Materialien sind verschiedene Kopplungsmöglichkeiten vorhanden. Demnach wird erwartet, dass auf diesem Gebiet weitere neue Funktionen erzielt werden können. N2 - Actively moving polymers are high scientific significance due to their ability to move actively in response to an external stimulus. Most notably shape-change and shape-memory polymers are in the focus of current research. Shape-changing polymers exhibit a non-contact deformation from a permanent into a temporary shape, which is just stable as long the material is exposed to an external stimulus. In contrast shape-memory polymers are capable of a fixed temporary shape due to the formation of additional temporary netpoints, while the deformation is proceed by applying mechanical stress. A polymeric material, which combines both functions would result into a material that possesses the advantages of the shape-change, as well as the shape-memory effect. In this work, the coupling of two known functions is investigated which results into a new switchable function. Therefore, two different concepts were developed requiring different material structures. For the first concept monodomain, smectic liquid-crystalline elastomers (LCE) containing azobenzene moieties were prepared and the coupling of the light-induced shape-change with the thermally-induced shape-memory effect was investigated. These oriented LCE's exhibit a non-contact deformation into a temporary shape, above the glass transition temperature (Tg), due to the irradiation with UV-light. The temporary shape could be fixed by cooling the material below Tg, while the irradiation with light was kept constant. The permanent shape could be recovered by additional heating above Tg. This process could be repeated several times. Therefore, a new switchable function was developed, which based on the coupling of the light-induced shape-change with the thermally induced shape-memory effect. The second concept required a multi-component system and the coupling of the thermally-induced shape-memory withe the light-induced shape-change effect was investigated. The multi component system consists of a LCE-core and a photosensitive layer. Nematic, main-chain elastomers were prepared, which possess of low transition temperatures and high actuation performances. The photosensitive layer consists of cinnamylidene acetic moieties, that were attached to a siloxane backbone, while the photoreversibility of the light-induced [2+2]-cycloaddition was shown. Furthermore, the photosensitive layer was covalently attached to the surface of the LCE-core. While both components showed their functionality, the coupling of the thermally-induced shape-change with the light-induced shape-memory effect was not successful up to now. The Adjustment of both components on each other has to be improved. Mainly the variation of the layer thickness of both structural components should be in the focus of future work. KW - multi-stimuli sensitive Materialien KW - aktive Polymere KW - Formgedächtnispolymere KW - [2+2]-Cycloaddition KW - flüssigkristalline Netzwerke KW - multi-stimuli sensitiv materials KW - active polymers KW - shape-memory polymers KW - [2+2]-cycloaddition KW - liquid-crystalline elastomers Y1 - 2012 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-62866 ER - TY - THES A1 - Kölsch, Jonas David T1 - Entwicklung neuer farbstoffmarkierter Polymere zur Visualisierung des LCST-Phasenübergangs in wässriger Lösung T1 - Development of new dye labeled polymers for visualisation of LCST transition in water N2 - Ziel der Arbeit war die Entwicklung von farbstoffmarkierten Polymeren, die einen temperaturgetriebenen Knäuel-Kollaps-Phasenübergang in wässriger Lösung ("thermo-responsive Polymere") zeigen und diesen in ein optisches Signal übersetzen können. Solche Polymere unterliegen innerhalb eines kleinen Temperaturintervalls einer massiven Änderung ihres Verhaltens, z B. ihrer Konformation und ihres Quellungsgrads. Diese Änderungen sind mit einem Wechsel der Löseeigenschaften von hydrophil zu hydrophob verbunden. Als Matrixpolymere wurden Poly-N-isopropylacrylamid (polyNIPAm), Poly(oligoethylen-glykolacrylat) (polyOEGA) und Poly(oligoethylenglykolmethacrylat) (polyOEGMA) ein-gesetzt, in die geeignete Farbstoffen durch Copolymerisation eingebaut wurden. Als besonders geeignet, um den Phasenübergang in ein optisches Signal zu übersetzen, erwiesen sich hierfür kompakte, solvatochrome Cumarin- und Naphthalimidderivate. Diese beeinträchtigten weder das Polymerisationsverhalten noch den Phasenübergang, reagierten aber sowohl bezüglich Farbe als auch Fluoreszenz stark auf die Polarität des Lösemittels. Weiterhin wurden Systeme entwickelt, die mittels Energietransfer (FRET) ein an den Phasenübergang gekoppeltes optisches Signal erzeugen. Hierbei wurde ein Cumarin als Donor- und ein Polythiophen als Akzeptorfarbstoff eingesetzt. Es zeigte sich, dass trotz scheinbarer Ähnlichkeit bestimmte Polymere ausgeprägt auf einen Temperaturstimulus mit Änderung ihrer spektralen Eigenschaften reagieren, andere aber nicht. Hierfür wurden die molekularen Ursachen untersucht. Als wahrscheinliche Gründe für das Ausbleiben einer spektralen Änderung in Oligo(ethylenglykol)-basierten Polymeren sind zum einen die fehlende Dehydratationseffektivität infolge des Fehlens eines selbstgenügenden Wasserstoffbrückenbindungsmotivs zu nennen und zum anderen die sterische Abschirmung der Farbstoffe durch die Oligo(ethylenglykol)-Seitenketten. Als Prinzipbeweis für die Nützlichkeit solcher Systeme für die Bioanalytik wurde ein System entwickelt, dass die Löslichkeitseigenschaft eines thermoresponsiven Polymers durch Antikörper-Antigen-Reaktion änderte. Die Bindung selbst kleiner Mengen eines Antikörpers ließ sich so direkt optisch auslesen und war bereits mit dem bloßen Auge zu erkennen. N2 - This work is based on different dye labeled thermo responsive polymers. These polymers are useful tool for the visualisation of the LCST phase transition in water. KW - LCST KW - Farbstoff KW - Polymer KW - Fluoreszens KW - LCST KW - dye KW - polymer KW - fluorescence Y1 - 2014 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-72531 ER - TY - THES A1 - Buller, Jens T1 - Entwicklung neuer stimuli-sensitiver Hydrogelfilme als Plattform für die Biosensorik T1 - Development of new stimuli-sensitive hydrogel films designed as platform for biosensors N2 - Diese Arbeit befasst sich mit der Synthese und der Charakterisierung von thermoresponsiven Polymeren und ihrer Immobilisierung auf festen Oberflächen als nanoskalige dünne Schichten. Dabei wurden thermoresponsive Polymere vom Typ der unteren kritischen Entmischungstemperatur (engl.: lower critical solution temperature, LCST) verwendet. Sie sind bei niedrigeren Temperaturen im Lösungsmittel gut und nach Erwärmen oberhalb einer bestimmten kritischen Temperatur nicht mehr löslich; d. h. sie weisen bei einer bestimmten Temperatur einen Phasenübergang auf. Als Basismaterial wurden verschiedene thermoresponsive und biokompatible Polymere basierend auf Diethylenglykolmethylethermethacrylat (MEO2MA) und Oligo(ethylenglykol)methylethermethacrylat (OEGMA475, Mn = 475 g/ mol) über frei radikalische Copolymerisation synthetisiert. Der thermoresponsive Phasenübergang der Copolymere wurde in wässriger Lösung und in gequollenen vernetzten dünnen Schichten beobachtet. Außerdem wurde untersucht, inwiefern eine selektive Proteinbindung an geeignete funktionalisierte Copolymere die Phasenübergangstemperatur beeinflusst. Die thermoresponsiven Copolymere wurden über photovernetzbare Gruppen auf festen Oberflächen immobilisiert. Die nötigen lichtempfindlichen Vernetzereinheiten wurden mittels des polymerisierbaren Benzophenonderivates 2 (4 Benzoylphenoxy)ethylmethacrylat (BPEM) in das Copolymer integriert. Dünne Filme der Copolymere mit ca. 100 nm Schichtdicke wurden über Rotationsbeschichtung auf Siliziumwafer aufgeschleudert und anschließend durch Bestrahlung mit UV Licht vernetzt und auf der Oberfläche immobilisiert. Die Filme sind stabiler je größer der Vernetzeranteil und je größer die Molmasse der Copolymere ist. Bei einem Waschprozess nach der Vernetzung wird beispielsweise aus einem Film mit moderater Molmasse und geringem Vernetzeranteil mehr unvernetztes Copolymer ausgewaschen als bei einem höhermolekularen Copolymer mit hohem Vernetzeranteil. Die Quellbarkeit der Polymerschichten wurde mit Ellipsometrie untersucht. Sie ist größer je geringer der Vernetzeranteil in den Copolymeren ist. Schichten aus thermoresponsiven OEG Copolymeren zeigen einen Volumenphasenübergang vom Typ der LCST. Der thermoresponsive Kollaps der Schichten ist komplett reversibel, die Kollapstemperatur kann über die Zusammensetzung der Copolymere eingestellt werden. Für einen Vergleich dieser Eigenschaften mit dem gut charakterisierten und derzeit wohl am häufigsten untersuchten thermoresponsiven Polymer Poly(N-isopropylacrylamid) (PNIPAM) wurden zusätzlich photovernetzte Schichten aus PNIPAM hergestellt und ebenfalls ellipsometrisch vermessen. Im Vergleich zu PNIPAM verläuft der Phasenübergang der Schichten aus den Copolymeren mit Oligo(ethylenglykol)-seitenketten (OEG Copolymere) über einen größeren Temperaturbereich. Mit Licht einer Wellenlänge > 300 nm wurden die photosensitiven Benzophenongruppen selektiv angeregt. Bei der Verwendung kleinerer Wellenlängen vernetzten die Copolymerschichten auch ohne die Anwesenheit der lichtempfindlichen Benzophenongruppen. Dieser Effekt ließ sich zur kontrollierten Immobilisierung und Vernetzung der OEG Copolymere einsetzen. Als weitere Methode zur Immobilisierung der Copolymere wurde die Anbindung über Amidbindungen untersucht. Dazu wurden OEG Copolymere mit dem carboxylgruppenhaltigen 2 Succinyloxyethylmethacrylat (MES) auf mit 3 Aminopropyldimethylethoxysilan (APDMSi) silanisierte Siliziumwafer rotationsbeschichtet, und mit dem oligomeren α, ω Diamin Jeffamin® ED 900 vernetzt. Die Vernetzungsreaktion erfolgte ohne weitere Zusätze durch Erhitzen der Proben. Die Hydrogelschichten waren anschließend stabil und zeigten neben thermoresponsivem auch pH responsives Verhalten. Um zu untersuchen, ob die Phasenübergangstemperatur durch eine Proteinbindung beeinflusst werden kann, wurde ein polymerisierbares Biotinderivat 2 Biotinyl-aminoethylmethacrylat (BAEMA) in das thermoresponsive Copolymer eingebaut. Der Einfluss des biotinbindenen Proteins Avidin auf das thermoresponsive Verhalten des Copolymers in Lösung wurde untersucht. Die spezifische Bindung von Avidin an das biotinylierte Copolymer verschob die Übergangstemperatur deutlich zu höheren Temperaturen. Kontrollversuche zeigten, dass dieses Verhalten auf eine selektive Proteinbindung zurückzuführen ist. Thermoresponsive OEG Copolymere mit photovernetzbaren Gruppen aus BPEM und Biotingruppen aus BAEMA wurden über Rotationsbeschichtung auf Gold- und auf Siliziumoberflächen aufgetragen und durch UV Strahlung vernetzt. Die spezifische Bindung von Avidin an die Copolymerschicht wurde mit Oberflächenplasmonenresonanz und Ellipsometrie untersucht. Die Bindungskapazität der Schichten war umso größer, je kleiner der Vernetzeranteil, d. h. je größer die Maschenweite des Netzwerkes war. Die Quellbarkeit der Schichten wurde durch die Avidinbindung erhöht. Bei hochgequollenen Systemen verursachte eine Mehrfachbindung des tetravalenten Avidins allerdings eine zusätzliche Quervernetzung des Polymernetzwerkes. Dieser Effekt wirkt der erhöhten Quellbarkeit durch die Avidinbindung entgegen und lässt die Polymernetzwerke schrumpfen. N2 - This work describes the synthesis and characterization of thermoresponsive polymers and their immobilisation on solid substrates as nanoscale thin films. The used polymers were of the lower critical solution temperature (LCST) type. They are well soluble in a solvent below a and get insoluble above a certain temperature, thus they exhibit a phase transition at a critical temperature. Different thermoresponsive biocompatible copolymers based on oligo(ethylene glycol) methyl ether methacrylate (OEGMA475) and di(ethylene glycol) methyl ether methacrylate (MEO2MA) were synthesized by free radical polymerization. The phase transition was observed in solution and in thin immobilized copolymer layers. Further regarding the phase transition the influence of selective protein binding onto functionalized copolymers was studied. Solid surfaces were modified with thermoresponsive copolymers based on MEO2MA, OEGMA475 and 2 (4 benzoylphenoxy)ethyl methacrylate (BPEM) as photo crosslinkable groups. Thin films of 100 nm thickness were spin-casted onto silicon wafers and subsequently crosslinked and immobilized by irradiation with UV-light. Their stability is controlled by the crosslinker ratio and by the molar mass of the copolymers. For instance a washing process after crosslinking removes more unbound polymer if the polymer contains less crosslinker and has a lower molecular weight. The swellability of the films was investigated by ellipsometry. It gets higher with lower crosslinker ratio. Layers of thermoresponsive copolymers exhibited a swelling/ deswelling phase transition of the lower critical solution temperature (LCST) type. The transition is completely reversible and the transition temperature can be adjusted by the composition of the copolymers. Compared to similarly synthesized photo-crosslinked layers of the well investigated thermoresponsive copolymer poly-(N-isopropyl acrylamide) (PNIPAM) the phase transition exceeds a larger temperature range. The photo-crosslinking of the OEG copolymers was accomplished in a controlled manner with light of wavelengths > 300 nm. Light of smaller wavelengths crosslinked the copolymer layers even without the presence of photosensitive groups. This effect could be exploited for a controlled immobilization and crosslinking of the OEG copolymers. As further method for crosslinking the formation of amide bonds was investigated. Therefore OEG copolymers containing 2 succinyloxyethyl methacrylate (MES) were spin-casted onto silicon substrates silanized with (3 aminopropyl)dimethylethoxysilane (APDMSi) and crosslinked with oligomeric α, ω diamine Jeffamin® ED 900. The crosslinking reaction was carried out by annealing the dry substrate. No further additives were added for the reaction. After annealing the hydrogel layers were stable against washing and showed thermoresponsive and pH responsive behaviour. In order to investigate whether the phase transition can be affected by specific protein binding, a polymerizable biotin derivative biotinyl-2-aminoethyl methacrylate (BAEMA) was integrated into the base thermoresponsive OEG copolymer. The influence of avidin on its thermoresponsive behaviour was investigated. The specific binding of avidin to the bioitinylated copolymer caused a marked shift of the transition temperature to higher temperatures. Control experiments proved that this effect can be ascribed to a specific protein binding. Thermoresponsive OEG Copolymers with photo-crosslinkable groups from BPEM and biotin groups from BAEMA were spin casted onto gold and silicon substrates and subsequently crosslinked by irradiation with UV light. The specific binding of Avidin onto the copolymer layer was investigated by surface plasmon resonance spectroscopy and ellipsometry. The binding capacity was higher if the mesh size of the hydrogel layers was higher. Upon binding of the Avidin the swellability of the layers was increased. At temperatures below the phase transition for loosely crosslinked copolymer layers an additional crosslinking effect of Avidin was observed. This effect counteracts the swelling of the hydrogel and leads to a shrinkage of the hydrogel layer. KW - Thermoresponsiv KW - OEGMA KW - MEO2MA KW - Protein KW - Hydrogel KW - Film KW - thermoresponsive KW - OEGMA KW - MEO2MA KW - protein KW - hydrogel KW - film Y1 - 2013 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-66261 ER - TY - THES A1 - Gabriel, Christina T1 - Entwicklung neuer Stärkederivate für die Anwendung als wasserbasierte Filmbildner in Farben und Lacken T1 - Development of new starch derivatives for application as water-based film formers in paints and varnishes N2 - In den letzten Jahrzehnten fand auch in der Beschichtungsindustrie ein Umdenken hin zu umweltfreundlicheren Farben und Lacken statt. Allerdings basieren auch neue Lösungen meist nicht auf Biopolymeren und in einem noch geringeren Anteil auf wasserbasierten Beschichtungssystemen aus nachwachsenden Rohstoffen. Dies stellt den Anknüpfungspunkt dieser Arbeit dar, in der untersucht wurde, ob das Biopolymer Stärke das Potenzial zum wasserbasierten Filmbildner für Farben und Lacke besitzt. Dabei müssen angelehnt an etablierte synthetische Marktprodukte die folgenden Kriterien erfüllt werden: Die wässrige Dispersion muss mindestens einen 30%igen Feststoffgehalt haben, bei Raumtemperatur verarbeitet werden können und Viskositäten zwischen 10^2-10^3 mPa·s aufweisen. Die finale Beschichtung muss einen geschlossenen Film bilden und sehr gute Haftfestigkeiten zu einer spezifischen Oberfläche, in dieser Arbeit Glas, besitzen. Als Grundlage für die Modifizierung der Stärke wurde eine Kombination von molekularem Abbau und chemischer Funktionalisierung ausgewählt. Da nicht bekannt war, welchen Einfluss die Stärkeart, die gewählte Abbaureaktion als auch verschiedene Substituenten auf die Dispersionsherstellung und deren Eigenschaften sowie die Beschichtungseigenschaften ausüben könnten, wurden die strukturellen Parameter getrennt voneinander untersucht. Das erste Themengebiet beinhaltete den oxidativen Abbau von Kartoffel- und Palerbsenstärke mittels des Hypochlorit-Abbaus (OCl-) und des ManOx-Abbaus (H2O2, KMnO4). Mit beiden Abbaureaktionen konnten vergleichbare gewichtsmittlere Molmassen (Mw) von 2·10^5-10^6 g/mol (GPC-MALS) hergestellt werden. Allerdings führten die gewählten Reaktionsbedingungen beim ManOx-Abbau zur Bildung von Gelpartikeln. Diese lagen im µm-Bereich (DLS und Kryo-REM-Messungen) und hatten zur Folge, dass die ManOx-Proben deutlich erhöhte Viskositäten (c: 7,5 %; 9-260 mPa·s) im Vergleich zu den OCl--Proben (4-10 mPa·s) bei scherverdünnendem Verhalten besaßen und die Eigenschaften von viskoelastischen Gelen (G‘ > G‘‘) zeigten. Des Weiteren wiesen sie reduzierte Heißwasserlöslichkeiten (95 °C, vorrangig: 70-99 %) auf. Der OCl--Abbau führte zu hydrophileren (Carboxylgruppengehalt bis zu 6,1 %; ManOx: bis zu 3,1 %), nach 95 °C-Behandlung vollständig wasserlöslichen abgebauten Stärken, die ein Newtonsches Fließverhalten mit Eigenschaften einer viskoelastischen Flüssigkeit (G‘‘ > G‘) hatten. Die OCl--Proben konnten im Vergleich zu den ManOx-Produkten (10-20 %) zu konzentrierteren Dispersionen (20-40 %) verarbeitet werden, die gleichzeitig die Einschränkung von anwendungsrelevanten Mw auf < 7·10^5 g/mol zuließen (Konzentration sollte > 30 % sein). Außerdem führten nur die OCl--Proben der Kartoffelstärke zu transparenten (alle anderen waren opak) geschlossenen Beschichtungsfilmen. Somit hebt sich die Kombination von OCl--Abbau und Kartoffelstärke mit Hinblick auf die Endanwendung ab. Das zweite Themengebiet umfasste Untersuchungen zum Einfluss von Ester- und Hydroxyalkylether-Substituenten auf Basis einer industriell abgebauten Kartoffelstärke (Mw: 1,2·10^5 g/mol) vor allem auf die Dispersionsherstellung, die rheologischen Eigenschaften der Dispersionen und die Beschichtungseigenschaften in Kombination mit Glassubstraten. Dazu wurden Ester und Ether mit DS/MS-Werten von 0,07-0,91 synthetisiert. Die Derivate konnten zu wasserbasierten Dispersionen mit Konzentrationen von 30-45 % verarbeitet werden, wobei bei hydrophoberen Modifikaten ein Co-Lösemittel, Diethylenglycolmonobutylether (DEGBE), eingesetzt werden musste. Die Feststoffgehalte sanken dabei für beide Derivatklassen vor allem mit zunehmender Alkylkettenlänge. Die anwendungsrelevanten Viskositäten (323-1240 mPa·s) stiegen auf Grund von Wechselwirkungen tendenziell mit DS/MS und Alkylkettenlänge an. Hinsichtlich der Beschichtungseigenschaften erwiesen sich die Ester vergleichend zu den Ethern als die bevorzugte Substituentenklasse, da nur die Ester geschlossene, defektfreie und mehrheitlich transparente Beschichtungsfilme bildeten, die exzellente bis sehr gute Haftfestigkeiten (ISO Klasse: 0 und 1) auf Glas besaßen. Die Ether bildeten mehrheitlich brüchige Filme. Basierend auf der Kombination der Ergebnisse aus Lösemittelaustausch, den rheologischen Untersuchungen und zusätzlichen Oberflächenspannungsmessungen (30-61 mN/m) konnte geschlossen werden, dass wahrscheinlich fehlende oder schlechte Haftfestigkeiten vorrangig akkumuliertem Wasser in den Beschichtungsfilmen (visuell: trüb oder weiß) geschuldet sind, während die Brüchigkeit vermutlich auf Wechselwirkungen (H-Brücken Wechselwirkungen, hydrophobe Wechselwirkungen) zwischen den Polymeren zurückgeführt werden kann. Insgesamt scheint die Kombination aus Kartoffelstärke basierend auf dem OCl--Abbau mit Mw < 7·10^5 g/mol und einem Estersubstituenten eine gute Wahl für wasserbasierte Dispersionen mit hohen Feststoffkonzentrationen (> 30 %), guter Filmbildung und exzellenten Haftungen auf Glas zu sein. N2 - In the last few decades, the coating industry, like many other industries, has changed its thinking towards more environmentally friendly paints and varnishes. However, even new solutions are usually not based on biopolymers and, to an even lesser extent, on water-based coating systems made from renewable raw materials. This is the starting point of this work, which aimed to investigate whether the biopolymer starch has the potential to be a water-based film former for paints and varnishes. Based on established synthetic market products, the following criteria must be fulfilled: The aqueous dispersion must have a solid content of at least 30%, be processable at room temperature and have viscosities of 10^2-10^3 mPa·s. The final coating must form a continuous film and have very good adhesion to a specific substrate, in this thesis glass. A combination of molecular degradation and chemical functionalisation was selected as the basis for the modification of the starch. Since it was not known what influence the type of starch, the chosen degradation reaction as well as different substituents could have on the dispersion production and its properties as well as on the coating properties, the structural parameters were investigated separately. The first part dealt with the oxidative degradation of potato and smooth pea starch by hypochlorite degradation (OCl-) and ManOx degradation (H2O2, KMnO4). With both degradation reactions comparable weight average molar masses (Mw) of 2·10^5-10^6 g/mol (SEC-MALS) could be synthesized. However, the selected reaction conditions led to the formation of gel particles during ManOx degradation. These were in the µm-range (DLS and cryo-REM measurements) and resulted in ManOx samples having significantly higher viscosities (c: 7.5%; 9-260 mPa·s) compared to OCl- samples (4-10 mPa·s) with shear-thinning behaviour and showing the properties of viscoelastic gels (G' > G''). Furthermore, they exhibited reduced hot water solubilities (95 °C, primarily: 70-99%). OCl- degradation led to more hydrophilic (carboxyl group content up to 6.1%; ManOx: up to 3.1%), after 95 °C treatment completely water-soluble degraded starches, which had Newtonian flow behaviour with properties of a viscoelastic liquid (G'' > G'). Compared to the ManOx products (10-20%), the OCl- samples could be processed to more concentrated dispersions (20-40%), which at the same time allowed the restriction of application-relevant Mw to < 7·10^5 g/mol (concentration should be > 30%). In addition, only the OCl- samples of the potato starch led to transparent (all others were opaque) continuous coating films. Thus, the combination of OCl- degradation and potato starch stands out with regard to the final application. The second part included investigations on the influence of ester and hydroxyalkyl ether substituents on the basis of an industrially degraded potato starch (Mw: 1.2·10^5 g/mol), particularly on dispersion preparation, rheological properties of the dispersions and the coating properties in combination with glass substrates. For this purpose, esters and ethers with DS/MS values of 0.07-0.91 were synthesized. The derivatives could be prepared to water-based dispersions with concentrations of 30-45%, whereby a co-solvent, diethylene glycol monobutyl ether (DEGBE), had to be used for more hydrophobic derivatives. The solid content of both derivative classes decreased most of all with increasing alkyl chain length. The application-relevant viscosities (323-1240 mPa·s) tended to increase due to interactions with DS/MS and alkyl chain length. With regard to the coating properties, esters proved to be the preferred substituent class compared to ethers, since only the esters formed continuous, defect free and mostly transparent coating films which had excellent to very good adhesion (ISO class: 0 and 1) on glass. The majority of ethers formed brittle films. Based on the combination of the results from solvent exchange, rheological investigations and additional surface tension measurements (30-61 mN/m), it could be concluded that probably missing or poor adhesion was primarily due to accumulated water in the coating films (visually: turbid or white), while the brittleness can probably be attributed to interactions (H-bridge interactions, hydrophobic interactions) between the polymers. Overall, the combination of potato starch based on OCl- degradation with Mw < 7·10^5 g/mol and an ester substituent seems to be a good choice for water-based dispersions with high solid concentrations (> 30%), good film formation and excellent adhesion to glass. KW - Stärke KW - starch KW - Filmbildner KW - film former KW - Beschichtung KW - coating Y1 - 2019 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-432942 ER - TY - THES A1 - Schulze, Sven T1 - Entwicklung und Charakterisierung optischer Biosensorplattformen basierend auf photonischen Kristallen und Faser-Bragg-Gitter T1 - Development and characterization of optical biosensor platforms based on photonic crystalls and fiber Bragg gratings N2 - In dieser Arbeit steht die Entwicklung einer Sensorplattform für biochemische Anwendungen, welche auf einem optischen Detektionsprinzips beruht, im Vordergrund. Während der Entwicklung wurden zwei komplementäre Konzeptideen behandelt, zum einen ein Sensor, der auf photonischen Kristallen und Wellenleiterstrukturen basiert und zum anderen einen faserbasierten Sensor, der chemisch modifizierte Faser-Bragg-Gitter enthält. Das optische Detektionsprinzip in beiden Sensorideen ist die resultierende Brechungsindexänderung als messbare physikochemische Kenngröße. Das aus der Natur bekannte Phänomen der photonischen Kristalle, das u. a. bei Opalen und bei Schmetterlingen zu finden ist, wurde bereits 1887 von Lord Rayleigh beschrieben. Er beschrieb die optischen Eigenschaften von periodischen mehrschichtigen Filmen, welche als vereinfachtes Modell eines eindimensionalen photonischen Kristalls verstanden werden können. Die Periodizität der Brechungsindexänderung resultiert in einem optischen Filter für Frequenzen in einem bestimmten spektralen Bereich, weshalb dann dort keine Lichtausbreitung mehr möglich ist. Wird dieses System aber durch eine Defektstelle in der Brechungsindexperiodizität gestört, sodass daraus zwei perfekt periodische Systeme entstehen, ist die Lichtausbreitung für eine bestimmte Frequenz dennoch möglich. In der Folge resultiert daraus ein schmalbandiges Signal im Transmissionsspektrum. Die erlaubte Frequenz ist dabei u. a. abhängig vom Brechungsindexunterschied des periodischen Systems, d.h. Veränderung des Brechungsindexes einer Schicht führt zu einer spektralen Verschiebung der erlaubten Frequenz, dadurch kann dieses Sensorkonzept für biochemische Sensorik ausgenutzt werden [1]. Diese Entwicklung des auf photonischen Kristallen basierenden Sensors war eine Kooperation mit dem Industriepartner „Nanoplus GmbH“. In der Doktorarbeit wurden Simulationen und praktischen Arbeiten zur Designentwicklung des Sensors und die Arbeiten an einem ersten Modellaufbau für die biochemischen Anwendungen durchgeführt. Für den faserbasierten Sensor wurden Faser-Bragg-Gitter in den Faserkern hineingeschrieben. Hill et al. entdeckten 1978, dass solche Gitterstrukturen genau wie photonische Kristalle als optische Filter fungieren [2]. Die Gitter bestehen dabei aus Änderungen des Brechungsindexes im Faserkern. Im Laufe der nächsten vierzig Jahren wurden verschiedene Einschreibetechniken und Gitterstrukturen entwickelt, weshalb die Eigenschaften der jeweiligen Gitterstrukturen variieren. Eine solche Gitterstruktur sind u. a. die Faser-Bragg-Gitter, deren Gitterperiode, d. h. die Abstände der Brechungsindexmodifikationen, sich im Nanometer- bis Mikrometerbereich befinden. Aufgrund der kleinen Gitterperiode wird eine rückwärtsführende Welle im Kern für eine bestimmte Frequenz bzw. Wellenlänge, der Bragg-Wellenlänge, erzeugt. Im Endeffekt resultiert daraus ein schmalbandiges Signal sowohl im Transmissionsspektrum, als auch im Reflexionsspektrum. Die Resonanzwellenlänge ist dabei proportional zu der Gitterperiode und dem effektiven Brechungsindex, welcher vom Brechungsindex des Kerns und des kernumgebenen Materials abhängig ist. Letztlich eignet sich diese Technik für physikochemische Sensorik. Im Rahmen dieser Arbeit wurden die Gitter mit Hilfe einer relativen neuen Herstellungsmethode in die Fasern geschrieben [3]. Anschließend stand die Entwicklung eines Biosensors im Vordergrund, wobei zunächst ein Protokoll zum Ätzen der Faser mit Flusssäure entwickelt worden ist, dass das System sensitiv zum umgebenen Brechungsindex macht. Am Ende wurde ein Modellaufbau realisiert, indem ein Modellsystem, hier die Detektion vom C-reaktiven Protein mittels spezifischen einzelsträngigen DNS-Aptameren, erfolgreich getestet und quantifiziert worden ist. 1 Mandal, S.; Erickson, D. Nanoscale Optofluidic Sensor Arrays. Opt. Express 2008, 16 (3), 1623–1631. 2 Hill, K. O.; Fujii, Y.; Johnson, D. C.; Kawasaki, B. S. Photosensitivity in Optical Fiber Waveguides: Application to Reflection Filter Fabrication. Appl. Phys. Lett. 1978, 32 (10), 647–649. 3 Martínez, A.; Dubov, M.; Khrushchev, I.; Bennion, I. Direct Writing of Fibre Bragg Gratings by Femtosecond Laser. Electron. Lett. 2004, 40 (19), 1170. N2 - In this thesis, the development of a sensor platform for biochemical applications based on an optical detection principle is in the foreground. Two complementary concept ideas address during development, one based on photonic crystals next to waveguide structures and on the other with a fiber-based sensor containing chemically modified fiber Bragg gratings. The optical detection principle in both sensor ideas is the resulting refractive index change as a measurable physicochemical parameter. Lord Rayleigh described the well-known phenomenon of photonic crystals, which can be found among others in opals and butterflies, already in 1887. He described the optical properties of periodic multilayer films, which can be understood as a simplified model of a one-dimensional photonic crystal. The periodicity of the refractive index change results in an optical filter for frequencies in a certain spectral range, which is why no light propagation is possible there. However, if this is disturbed by a defect point in the refractive index periodicity, resulting in two perfectly periodic systems, the light propagation for a given frequency is still possible. This results in a narrowband signal in the transmission spectrum. The permitted frequency is dependent, inter alia, on the refractive index difference of the periodic system, that is, changing the refractive index of a layer leads to a spectral shift of the permitted frequency, thereby this sensor concept can be exploit for biochemical sensors [1]. This development of the sensor based on photonic crystals was a cooperation with the industrial partner “Nanoplus GmbH“. In the doctoral thesis, simulations and practical work for the design development of the sensor and the work on a first model set-up for the biochemical applications were carried out. For the fiber-based sensor, fiber Bragg gratings were written into the fiber core. Hill et al. discovered in 1978 that such lattice structures act as optical filters just like photonic crystals [2]. The gratings consist of changes in the refractive index in the fiber core. Over the next forty years, various inscription techniques and lattice structures have been developed, which is why the properties of the respective lattice structures vary. Such a lattice structure include the fiber Bragg gratings whose grating period, that is, the distances of the refractive index modifications, are in the nanometer to micrometer range. Due to the small grating period, a backward wave is generated in the core for a particular frequency, the Bragg wavelength. Ultimately, this results in a narrowband signal in both in the transmission spectrum, as well as in the reflection spectrum. The resonant wavelength is proportional to the grating period and the effective refractive index, which depends on the refractive index of the core and the core-surrounded material. Ultimately, this technique is suitable for physicochemical sensors. In this thesis, the gratings were written into the fibers using a relatively new manufacturing method [3]. Subsequently, the development of a biosensor was in the the foreground, whereby first a protocol for the etching of the fiber with hydrofluoric acid was developed, which makes the system sensitive to the surrounded refractive index. In the end, a model design was realized by successfully testing and quantifying a model system, here the detection of the C-reactive protein by means of specific single-stranded DNA aptamers. 1 Mandal, S.; Erickson, D. Nanoscale Optofluidic Sensor Arrays. Opt. Express 2008, 16 (3), 1623–1631. 2 Hill, K. O.; Fujii, Y.; Johnson, D. C.; Kawasaki, B. S. Photosensitivity in Optical Fiber Waveguides: Application to Reflection Filter Fabrication. Appl. Phys. Lett. 1978, 32 (10), 647–649. 3 Martínez, A.; Dubov, M.; Khrushchev, I.; Bennion, I. Direct Writing of Fibre Bragg Gratings by Femtosecond Laser. Electron. Lett. 2004, 40 (19), 1170. KW - Faser-Bragg-Gitter KW - fiber Bragg graiting KW - photonischer Kristall KW - photonic crystall KW - point-by-point-inscription method KW - Punkt-für-Punkt-Einschreibemethode KW - Faserätzen KW - fiber etching KW - optischer Fasersensor KW - fiber optical sensor KW - Aptamere KW - aptamers KW - C-reaktives Protein KW - c-reactive protein KW - Biomarker KW - biomarker Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-422139 ER - TY - THES A1 - Grothe, Dorian C. T1 - Entwicklung und Synthese von Materialien für Polyelektrolytmembranen mit ionischen Flüssigkeiten zum Einsatz in Lithium-Ionen-Batterien T1 - Development and synthesis of materials for poly electrolyte membranes with ionic liquids for application in Lithium-ion batteries N2 - Für den Einsatz in Autobatterien gibt es besondere Anforderungen an den Elektrolyten im Bereich der Energie- und Leistungsdichten, um beispielsweise thermische Verluste gering zu halten. Hochleitfähige Elektrolyte mit Leitfähigkeiten im Millisiemensbereich sind hier ebenso notwendig wie auch sichere, d.h. möglichst nicht brennbare und einen niedrigen Dampfdruck besitzende Materialien. Um diese Vorgaben zu erreichen, ist es notwendig, einen polymeren Separator zu entwickeln, welcher auf brennbare organische Lösungsmittel verzichtet und damit eine drastische Steigerung der Sicherheit gewährleistet. Gleichzeitig müssen hierbei die Leistungsvorgaben bezüglich der Leitfähigkeit erfüllt werden. Zu diesem Zweck wurde ein Konzept basierend auf der Kombination von einer polymeren sauerstoffreichen Matrix und einer ionischen Flüssigkeit entwickelt und verifiziert. Dabei wurden folgende Erkenntnisse gewonnen: 1. Es wurden neuartige diacrylierte sauerstoffreiche Matrixkomponenten mit vielen Carbonylfunktionen, für eine gute Lithiumleitfähigkeit, synthetisiert. 2. Es wurden mehrere neue ionische Flüssigkeiten sowohl auf Imidazolbasis als auch auf Ammoniumbasis synthetisiert und charakterisiert. 3. Die Einflüsse der Kationenstruktur und der Einfluss der Gegenionen im Bezug auf Schmelzpunkte und Leitfähigkeiten wurden untersucht. 4. Aus den entwickelten Materialien wurden Blendsysteme hergestellt und mittels Impedanzspektrometrie untersucht: Leitfähigkeiten von 10-4S/cm bei Raumtemperatur sind realisierbar. 5. Die Blendsysteme wurden auf ihre thermische Stabilität hin untersucht: Stabilitäten bis 250°C sind erreichbar. Dabei wird keine kristalline Struktur beobachtet. N2 - Within the field of energy storage and charge transfer, the lithium polymer batteries are one of the leading technologies, due to their low manufacture cost and their possible variety of packaging shapes. Despite their good thermal stability and very good weight to energy ratio, lithium ion batteries use as a electrolyte system a mixture of ethylene carbonate and diethyl carbonate as solvent which have a high risk of deflagration when they come in contact with water. Thus the developement of new materials for lithium-ion-batteries are necessary. For the electrolyte there are special requirements in terms of energy- and power density e.g. in order to minimize thermal loss. High conductivity electrolytes with conductivities in the range of milisiemens are as essential as safe materials, like non flammable non-volatile materials. To fulfill these requirements it is important to develop a polymeric lithium ion conductor, which is free of flammable organic solvents in order to ensure safety. Simultaneously it is also ,mandatory to achieve high performances in terms of ion-conductivity. Therefore a concept based on a combination of an oxygen rich polymeric matrix and ionic liquids was developed and verified. Following results were achieved . 1. Synthesis of new diacryalted oxygen rich matrix components with many carbonylfunctions for a good lithium ion transport. 2. Synthesis and characterization of new ionic liquids based on imidazol or ammonium compounds. 3. Investigation of the influences of the cation structure and counter ions for melting points and ion conductivity. 4. Creation of Blendsystems with the developed materials 5. Thermal investigations of these solid-state-electrolytes with DSC and TGA measurements, resulting in thermal stabilities up to 250°C.No crystallization were observed. 6. investigation of these solid-state-electrolytes via AC-impedance spectrometry, resulting in conductivities of 10-4S/cm at room temperature. KW - Lithium-Ionen-Batterie KW - ionische Flüssigkeiten KW - Festelektrolyten KW - AC Impedanz KW - Lithium ion battery KW - ionic liquids KW - solid-state-electrolyte KW - AC -Impedance Y1 - 2012 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-63690 ER - TY - THES A1 - Chao, Madlen T1 - Entwicklung und Validierung eines Online-LIBS-Verfahrens für die Bestimmung von Nährelementen in Böden N2 - In den letzten Jahrzehnten ist die Nachfrage nach kostengünstigen und flächendeckenden Kartierungsmöglichkeiten im Hinblick auf eine ertragssteigernde und umweltfreundlichere Bewirtschaftung von landwirtschaftlichen Nutzflächen stark gestiegen. Hierfür eignen sich spektroskopische Methoden wie die Röntgenfluoreszenzanalyse (RFA), Raman- und Gammaspektroskopie sowie die laserinduzierte Plasmaspektroskopie (LIBS). In Abhängigkeit von der Funktionsweise der jeweiligen Methoden werden Informationen zu verschiedensten Bodeneigenschaften wie Nährelementgehalt, Textur und pH-Wert erhalten. Ziel dieser Arbeit ist die Entwicklung eines Online-LIBS-Verfahrens zur Nährelementbestimmmung und Kartierung von Ackerflächen. Die LIBS ist eine schnelle und simultane Multielementanalyse bei der durch das Fokussieren eines hochenergetischen Laserpulses Probenmaterial von der Probenoberfläche ablatiert wird und in ein Plasma überführt wird. Beim Abkühlen des Plasmas wird Strahlung emittiert, welche Rückschlüsse über die elementare Zusammensetzung der Probe gibt. Diese Arbeit ist im Teilprojekt I4S (Intelligenz für Böden) im Forschungsprogramm BonaRes (Boden als nachhaltige Ressource für die Bioökonomie) des Bundesministerium für Bildung und Forschung (BMBF) entstanden. Es wurden insgesamt 651 Bodenproben von verschiedenen Test-Agrarflächen unterschiedlichster Standorte Deutschlands gemessen, ausgewertet und zu Validierungszwecken mit entsprechender Referenzanalytik wie die Optische Emissionsspektroskopie mittels induktiv gekoppeltem Plasma (ICP-OES) und die wellenlängendispersive Röntgenfluoreszenzanalyse (WDRFA) charakterisiert. Für die Quantifizierung wurden zunächst die Messparameter des LIBS-Systems auf die Bodenmatrix optimiert und für die Elemente geeignete Linien ausgewählt sowie deren Nachweisgrenzen bestimmt. Es hat sich gezeigt, dass eine absolute Quantifizierung basierend auf einem univariaten Ansatz aufgrund der starken Matrixeffekte und der schlechten Reproduzierbarkeit des Plasmas nur eingeschränkt möglich ist. Bei Verwendung eines multivariaten Ansatz wie der Partial Least Squares Regression (PLSR) für die Kalibrierung konnten für die Nährelemente im Vergleich zur univariaten Variante Analyseergebnisse mit höherer Güte und geringeren Messunsicherheiten ermittelt werden. Die Untersuchungen haben gezeigt, dass das multivariate Modell weiter verbessert werden kann, indem mit einer Vielzahl von gut analysierten Böden verschiedener Standorte, Bodenarten und einem breiten Gehaltsbereich kalibriert wird. Mithilfe der Hauptkomponentenanalyse (PCA) wurde eine Klassifizierung der Böden nach der Textur realisiert. Weiterhin wurde auch eine Kalibrierung mit losem Bodenmaterial erstellt. Trotz der Signalabnahme konnten für die verschiedenen Nährelemente Kalibriergeraden mit ausreichender, analytischer Güte erstellt werden. Für den Einsatz auf dem Acker wurde außerdem der Einfluss von Korngröße und Feuchtigkeit auf das LIBS-Signal untersucht. Die unterschiedlichen Korngrößen haben nur einen geringen Einfluss auf das LIBS-Signal und das Kalibriermodell lässt sich durch entsprechende Proben leicht anpassen. Dagegen ist der Einfluss der Feuchtigkeit deutlich stärker und hängt stark von der Bodenart ab, sodass für jede Bodenart ein separates Kalibriermodell für verschiedene Feuchtigkeitsgehalte erstellt werden muss. Mithilfe der PCA kann der Feuchtigkeitsgehalt im Boden grob abgeschätzt werden und die entsprechende Kalibrierung ausgewählt werden. Diese Arbeit liefert essentielle Informationen für eine Echtzeit-Analyse von Nährelementen auf dem Acker mittels LIBS und leistet einen wichtigen Beitrag zu einer fortschrittlichen und zukunftsfähigen Nutzung von Ackerflächen. N2 - In the last few decades, the demand for affordable and extensive mapping of agricultural fields has risen in order to make the cultivation of these areas more yielding and environmentally friendly. Spectroscopic methods like X-ray fluorescence spectroscopy (XRF), Raman spectroscopy, gamma-ray spectroscopy and laser-induced breakdown spectroscopy (LIBS) are generally suitable for this purpose. Depending on the functionality of each method, information about soil properties such as nutrient content, texture and pH value are obtained. The aim of this thesis is the development of an online LIBS analysis method for the determination of the nutrient content in soil and the mapping of agricultural areas. LIBS is a fast and simultaneous multi-element analysis, in which material is ablated from the sample’s surface and turned into plasma by focused, highly energetic laser pulses. While the plasma cools down, radiation is emitted, which is characteristic for the elemental composition of the sample. The work in this thesis has been done as part of the project I4S (intelligence for soil) within the research programme BonaRes (soil as a sustainable resource for the bioeconomy) funded by the Federal Ministry of Education and Research (BMBF) in Germany. Overall, 651 soil samples of different agricultural areas within Germany have been selected, measured and evaluated with LIBS. For validation purposes the samples have been also analysed with inductively coupled plasma optical emission spectrometry (ICP-OES) and wavelength-dispersive X-ray fluorescence (WDXRF). For the quantification of the nutrient content, the measuring parameters of the LIBS system have been optimised for the soil matrix, suitable spectral lines have been chosen for each element and their limits of detection have been determined. It has been shown that an absolute quantification based on a univariate approach is challenging due to strong matrix effects and poor reproducibility of the plasma. By utilising a multivariate approach such as partial least squares regression (PLSR) for the calibration, better results with lower measurement uncertainties have been obtained for the quantification of the nutrient content. The multivariate model has been improved further by cali-brating with data from soils of different origin, type and nutrient content. With the help of principal component analysis (PCA) a classification of soils according to their textures is realised. Further-more, another model is calibrated with loose soil as opposed to the pressed pellets that have been used before. Despite decreases in signal intensity, calibration models with sufficient accuracy have been achieved. For the application on the field, the influence of different grain size distributions and moisture have been investigated. First tests of different grain size distributions have indicated that the grain size has only a small effect on the LIBS signal and calibration models can be easily ad-justed with the help of appropriate samples. However, the influence of moisture is much larger and depends on the soil type, which is why for each soil type a separate calibration model for different moisture contents has to be created. With the help of PCA, the moisture content can be estimated and, thus, the correct calibration model can be chosen. This thesis provides essential information for the real-time analysis of nutrient content on agricultural fields with LIBS and makes an important contribution to an advanced and sustainable usage of agricultural land. T2 - Development and validation of an online-LIBS method for the determination of nutrients in soils KW - LIBS KW - PLSR KW - PCA KW - Nährelemente KW - Boden KW - Doppelpuls KW - Chemometrie KW - Düngeempfehlung KW - Kartierung KW - Precision Agriculture KW - ICP-OES KW - RFA KW - XRF Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-476772 ER - TY - THES A1 - Grunert, Bianca T1 - Entwicklung von Markierungsreagenzien für die bildgebende Diagnostik T1 - Development of cell labeling probes for diagnostic imaging N2 - Die intrazelluläre Markierung mit geeigneten Reagenzien ermöglicht ihre bildgebende Darstellung in lebenden Organismen. Dieses Verfahren (auch „Zell-Tracking“ genannt) wird in der Grundlagenforschung zur Entwicklung zellulärer Therapien, für die Erforschung pathologischer Prozesse, wie der Metastasierung, sowie für Therapiekontrollen eingesetzt. Besondere Bedeutung haben in den letzten Jahren zelluläre Therapien mit Stammzellen erlangt, da sie großes Potential bei der Regeneration von Geweben bei Krankheiten wie Morbus Parkinson oder Typ-1-Diabetes versprechen. Für die Entwicklung einer zellulären Therapie sind Informationen über den Verbleib der applizierten Zellen in vivo (Homing-Potential), über ihre Zellphysiologie sowie über die Entstehung möglicher Entzündungen notwendig. Das Ziel der vorliegenden Arbeit war daher die Synthese von Markierungsreagenzien, die nicht nur eine effiziente Zellmarkierung ermöglichen, sondern einen synergistischen Effekt hinsichtlich des modalitätsübergreifenden Einsatzes in den bildgebenden Verfahren MRT und Laser-Ablation(LA)-ICP-MS erlauben. Die MRT-Bildgebung ermöglicht die nicht invasive Nachverfolgung markierter Zellen in vivo und die LA-ICP-MS die anschließende ex vivo Analytik zur Darstellung der Elementverteilung (Bioimaging) in einer Biopsieprobe oder in einem Gewebeschnitt. Für diese Zwecke wurden zwei verschiedene Markierungsreagenzien mit dem kontrastgebenden Element Gadolinium synthetisiert. Gadolinium eignet sich aufgrund seines hohen magnetischen Moments hervorragend für die MRT-Bildgebung und da es in Biomolekülen nicht natürlich vorkommt, konnten die Reagenzien gleichermaßen für die Zellmarkierung und das Bioimaging mit der LA-ICP-MS untersucht werden. Für die Synthese eines makromolekularen Reagenzes wurde das kommerziell verfügbare Dendrimer G5-PAMAM über bifunktionelle Linker mit dem Chelator DOTA funktionalisiert, um anschließend Gadolinium zu komplexieren. Ein zweites, nanopartikuläres Reagenz wurde über eine Solvothermal-Synthese erhalten, bei der Ln:GdVO4-Nanokristalle mit einer funktionellen Polyacrylsäure(PAA)-Hülle dargestellt wurden. Die Dotierung der Ln:GdVO4-PAA Nanokristalle mit verschiedenen Lanthanoiden (Ln=Eu, Tb) zeigte ihre prinzipielle Multiplexfähigkeit in der LA-ICP-MS. Beide Markierungsreagenzien zeichneten sich durch gute Bioverträglichkeiten und r1-Relaxivitäten aus, was zudem ihr Potential für Anwendungen als präklinische „blood-pool“ MRT-Kontrastmittel belegte. Die Untersuchung der Zellmarkierung erfolgte anhand einer Tumorzelllinie und einer Stammzelllinie, wobei beide Zellarten erfolgreich intrazellulär mit beiden Reagenzien markiert wurden. Nach der Zellmarkierung veranschaulichte die in vitro MRT-Bildgebung von Zell-Phantomen eine deutlichere Kontrastverstärkung der Zellen nach der Markierung mit den Nanokristallen im Vergleich zum kommerziellen Kontrastmittel Magnevist®. Die hohe Effizienz der Zellmarkierung mit den Nanokristallen und die damit verbundenen hohen Signalintensitäten in einer einzelnen Zelle erlaubten beim Bioimaging mit der LA-ICP-MS, Messungen bis zu einer Auflösung von 4 µm Laser Spot Size. Nach der Zellmarkierung mit den DOTA(Gd3+)-funktionalisierten G5-PAMAM Dendrimeren waren hingegen Aufnahmen mit der LA-ICP-MS nur bis zu einer Auflösung von 12 µm Laser Spot Size möglich. Insgesamt waren die Ln:GdVO4-PAA Nanokristalle mit größerer Ausbeute und kostengünstiger herstellbar als die DOTA(Gd3+)-funktionalisierten G5-PAMAM Dendrimere und zeigten zudem eine effizientere Zellmarkierung. Die Ln:GdVO4-PAA Nanokristalle erscheinen somit für das Zell-Tracking als besonders vielversprechend. Darauf aufbauend wurden die Nanokristalle zur Etablierung der Antikörper-Konjugation ausgewählt, was sie für die molekulare in vivo Bildgebung sowie für die Immuno-Bildgebung von Gewebeschnitten oder Biopsie-Proben mit der LA-ICP-MS anwendbar macht. N2 - Labeling of intracellular structures using appropriate reagents allows diagnostic imaging of such structures in living organisms. This procedure, also known as ‘cell-tracking’, can be applied in various fields of basic research, e.g. for development of cellular therapies, understanding of pathological processes such as metastasis as well as monitoring of therapeutic strategies. In recent years, cellular therapies involving stem cells have gained increasing importance for they promise great potential in the regeneration of damaged tissue associated with various diseases such as Parkinson’s disease or Type 1 diabetes. However, to enable the development of a cell-based therapy, information regarding the in vivo ability of administered cells to migrate to the organ of their origin (homing potential), the cell physiology and the risk of potential inflammation is essential. The objective of the present thesis was the synthesis of labeling reagents that not only enable efficient cell labeling, but also allow tracking of the labeled cells via magnetic resonance imaging (MRI) and laser ablation inductively coupled plasma mass spectroscopy (LA-ICP-MS). MRI offers the ability to non-invasively track the labeled cells in vivo, whereas LA-ICP-MS allows subsequent ex vivo analysis of biopsy samples. To this end, two different types of labeling reagents were synthesized containing the contrast-enhancing element gadolinium (Gd). Gd is perfectly suited for MRI due to its high magnetic moment and, since it does not occur naturally in biomolecules, the Gd-containing labelling reagents could additionally be investigated with regard to their cell labeling and bioimaging efficacy using LA-ICP-MS. Synthesis of a macromolecular labeling reagent was performed by functionalization of the commercially available dendrimer G5-PAMAM with the chelator DOTA, which subsequently allows complexation of Gd3+-ions. A second nanoparticulate labeling reagent was synthesized via a solvothermal route which yielded in Ln:GdVO4 nanocrystals having a functional shell of polyacrylic acid. Doping of these nanocrystals with different lanthanides (Ln=Eu, Tb) demonstrated their fundamental capability for multiple implementation with LA-ICP-MS. All synthesized labeling reagents showed suitable biocompatibility and r1-relativities, indicating their potential for application as in vivo preclinical MR imaging agents. The cell labeling efficacy of the synthesized reagents was investigated in both cancer and stem cell lines, whereby both cell types showed efficient intracellular uptake. After cell labelling, in vitro MRI of cell phantoms indicated that the nanocrystalline-labelled cells portrayed a significantly higher contrast enhancement, in comparison to labelling with the commercially available MRI agent, Magnevist. Bioimaging of the nanocrystalline-labelled cells with LA-ICP-MS enabled resolutions of up to 4 µm laser spot size to be achieved since the high labelling efficacy allowed high signal intensities to be observed. On the other hand, measurements of dendrimer-labelled cells could be performed up to resolutions of 12 µm laser spot size. Evaluation of the different labelling reagents showed that the one based on nanocrystals could be synthesized more cost effectively, with greater yields and resulted in a higher cell labelling efficacy, demonstrating a superior aptitude for cell-tracking applications. Consequently, the nanocrystalline labeling reagent was selected for conjugation with antibodies, which in turn enables in vitro ICP-MS-based immunohistochemistry detection as well as in vivo molecular imaging. KW - Zellmarkierung KW - Magnetresonanztomographie KW - Laserablation-ICP-MS KW - cell labeling probe KW - magnetic resonance imaging Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-422830 ER - TY - THES A1 - Erler, Alexander T1 - Entwicklung von online-Detektionsverfahren für landwirtschaftlich relevante Analyten N2 - Die Entwicklung nachhaltiger Bewirtschaftungs- und Produktionsmethoden ist eine der zentralen Fragestellungen der modernen Agrarwirtschaft. Die vorliegende Arbeit beschäftigt sich mit zwei Forschungsthemen, die das Konzept Nachhaltigkeit beinhalten. In beiden Fällen werden analytische Grundlagen für die Entwicklung entsprechender landwirtschaftlicher Arbeitsmethoden gelegt. Das erste Thema ist an den sogenannten Präzisionsackerbau angelehnt. Bei diesem wird die Bearbeitung von Agrarflächen ortsabhängig ausgeführt. Das heißt, die Ausbringung von Saatgut, Dünger, Bewässerung usw. richtet sich nach den Eigenschaften des jeweiligen Standortes und wird nicht pauschal gleichmäßig über ein ganzes Feld verteilt. Voraussetzung hierfür ist eine genaue Kenntnis der Bodeneigenschaften. In der vorliegenden Arbeit sollten diese Parameter mittels der analytischen Technik der Laser-induzierten Breakdown Spektroskopie (LIBS), die eine Form der Elementaranalyse darstellt, bestimmt werden. Bei den hier gesuchten Bodeneigenschaften handelte es sich um die Gehalte von Nährstoffen sowie einige sekundäre Parameter wie den Humusanteil, den pH-Wert und den pflanzenverfügbaren Anteil einzelner Nährstoffe. Diese Eigenschaften wurden durch etablierte Referenzanalysen bestimmt. Darauf aufbauend wurden die Messergebnissen der LIBS-Untersuchungen durch verschiedene Methoden der sogenannten multivariaten Datenanalyse (MVA) ausgewertet. Daraus sollten Modelle zur Vorhersage der Bodenparameter in zukünftigen LIBS-Messungen erarbeitet werden. Die Ergebnisse dieser Arbeit zeigten, dass mit der Kombination von LIBS und MVA sämtliche Bodenparameter erfolgreich vorhergesagt werden konnten. Dies beinhaltete sowohl die tatsächlich messbaren Elemente als auch die sekundären Eigenschaften, welche durch die MVA mit den Elementgehalten in Zusammenhang gebracht wurden. Das zweite Thema beschäftigt sich mit der Vermeidung von Verlusten durch Schädlingsbefall bei der Getreidelagerung. Hier sollten mittels der Ionenmobilitätsspektrometrie (IMS) Schimmelpilzkontaminationen detektiert werden. Dabei wurde nach den flüchtigen Stoffwechselprodukten der Pilze gesucht. Die durch Referenzmessungen mit Massenspektrometern identifizierten Substanzen konnten durch IMS im Gasvolumen über den Proben, dem sogenannten Headspace, nachgewiesen werden. Dabei wurde nicht nur die Anwesenheit einer Kontamination festgestellt, sondern diese auch charakterisiert. Die freigesetzten Substanzen bildeten spezifische Muster, anhand derer die Pilze identifiziert werden konnten. Hier wurden sowohl verschiedene Gattungen als auch einzelne Arten unterschieden. Die Messungen fanden auf verschiedenen Nährböden statt um den Einfluss dieser auf die Stoffwechselprodukte zu beobachten. Auch die sekundären Stoffwechselprodukte der Schimmelpilze, die Mykotoxine, konnten durch IMS detektiert werden. Beide in dieser Arbeit vorgestellten Forschungsthemen konnten erfolgreich abgeschlossen werden. Sowohl LIBS als auch IMS erwiesen sich für den Nachweis der jeweiligen Analyten als geeignet, und der Einsatz moderner computergestützter Auswertemethoden ermöglichte die genaue Charakterisierung der gesuchten Parameter. Beide Techniken können in Form von mobilen Geräten verwendet werden und zeichnen sich durch eine schnelle und sichere Analyse aus. In Kombination mit entsprechenden Modellen der MVA sind damit alle Voraussetzungen für Vor-Ort-Untersuchungen und damit für den Einsatz in der Landwirtschaft erfüllt. N2 - The basis of modern agriculture is sustainable cultivation and production. Two of the research subjects of this thesis are related to this topic. The aim of both is the development of an analytical method for sustainable agriculture. The first topic is an application for precision agriculture, which is the side specific cultivation of agricultural areas. The local properties of each m² of the field are determined and used for sowing, fertilizing or irrigation instead of using standardized quantities for the entire field. This practice requires detailed knowledge of the soil properties. In this work, some of these soil properties were determined by laser-induced breakdown spectroscopy (LIBS), which is a form of elementary analysis. The evaluated properties are the total amounts of several elemental nutrients as well as some secondary parameters, such as pH value, humus-content and the plant available contents of a number of nutrients. Soil samples with reference values from established analytical methods were used. Various methods of multivariate analysis (MVA) were used for developing different calibration models based on the LIBS data. These models can be used to predict soil properties from future LIBS experiments on soils. The results of the combination of LIBS and MVA were reliable predictions for the total amounts of elements, which can directly be correlated to LIBS signals in the measurements, as well as the secondary parameters, which can only be correlated with the LIBS spectra by MVA. The second topic of this thesis was the detection of pest infestations of stored grains for preventing economic losses. Ion mobility spectrometry (IMS) was used to detect mould fungus contaminations. The target substances were volatile metabolites emitted by the fungi. Reference measurements by mass spectrometry (MS) identified the substances found in the headspace of the samples, which are also detected by IMS. In addition to the detection of a contamination, an identification of the contaminant was also possible because the substances emitted by the fungi formed specific patterns. Therefore, it was possible to discriminate not only various fungus genera but also individual species. Additionally, the influence of different growth media used for fungus cultivation on the metabolites emitted was investigated. In addition to the detection of volatile metabolites, the direct detection of mycotoxins by IMS could also be demonstrated. The goals of both research topics presented in this thesis were successfully achieved. LIBS and IMS could be used to detect the respective analytes and a characterization of the target parameters was possible using computer-assisted data processing. Common features of both techniques are the availability of mobile instrumentation and a fast and reliable analytical performance. In combination with MVA-based prediction models, they fulfil the requirements for in-field analysis, which potentially makes them well suited to a wide range of applications in modern agriculture. KW - Ionenmobilitätsspektrometrie KW - Laser induzierte Breakdown Spektroskopie KW - Schimmelpilze KW - Bodenanalytik KW - ion mobility spectrometry KW - laser induced breakdown spectroscopy KW - mold fungi KW - soil analysis Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-473406 ER - TY - THES A1 - Menski, Antonia Isabell T1 - Europium als strukturelle Sonde zur Analyse neuartiger Materialien T1 - Europium as a structural probe for the analysis of novel materials N2 - Im Rahmen dieser Arbeit wird anhand von neuartigen Materialien das Potential der Europium-Lumineszenz für die strukturelle Analyse dargestellt. Bei diesen Materialien handelt es sich zum einen um Nanopartikel mit Matrizes aus mehreren Metall-Mischoxiden und Dotierungen durch die Sonde Europium und zum anderen um Metallorganische Netzwerke (MOFs), die mit Neodym , Samarium- und Europium-Ionen beladen sind. Die Synthese der aus der Kombination von Metalloxiden enthaltenen Nanopartikel ist unter milden Bedingungen mithilfe von speziell dafür hergestellten Reagenzien erfolgt und hat zu sehr kleinen, amorphen Nanopartikeln geführt. Durch eine nachfolgende Temperaturbehandlung hat sich die Kristallinität erhöht. Damit verbunden haben sich auch die Kristallstruktur sowie die Position des Dotanden Europium verändert. Während die etablierte Methode der Röntgendiffraktometrie einen Blick auf das Kristallgitter als Gesamtes ermöglicht, so trifft die Lumineszenz des Europiums durch die Sichtbarkeit einzelner Stark-Aufspaltungen Aussagen über dessen lokale Symmetrien. Die Symmetrie wird durch Sauerstofffehlstellen verändert, welche die Sauerstoffleitfähigkeit der Nanopartikel beeinflussen. Diese ist für die Anwendung als Katalysatoren in industriellen Prozessen und ebenso als Sensoren und Therapeutika in biologischen Systemen von Bedeutung. Zur ersten katalytischen Charakterisierung werden die Proben mittels Temperatur-programmierter Reduktion untersucht. Des Weiteren werden die Mischoxid-Nanopartikel auch hinsichtlich ihrer Verwendbarkeit als Matrix in Aufkonversionsprozessen untersucht. Die Metallorganischen Netzwerke eignen sich aufgrund ihrer mikroporösen Struktur für Anwendungen in der Speicherung gleichermaßen von Nutzgasen wie auch von Schadstoffen. Ebenfalls ist eine biologische Anwendung denkbar, die insbesondere den Bereich der drug delivery-Reagenzien betrifft. Erfolgt in die mikroporösen Strukturen der Metallorganischen Netzwerke die Einlagerung von Lanthanoid-Ionen, so können diese bei der entsprechenden Kombination als Weißlicht-Emittierer fungieren. Dabei ist neben den Verhältnissen zwischen den Lanthanoid-Ionen auch die genaue Position innerhalb des Netzwerks sowie die Distanz zu anderen Ionen von Interesse. Zur Untersuchung dieser Fragestellungen wird die Umgebungssensitivität der Europium-Lumineszenz ausgenutzt. Die auf diese Weise festgestellte Formiat-Bildung hängt von zahlreichen Parametern ab. Insgesamt stellt sich die im Rahmen dieser Arbeit verwendete Methodik des Einsatzes von Europium als strukturelle Sonde in höchstem Maße vielseitig dar und zeigt seine größte Stärke in der Kombination mit weiteren Methoden der Strukturanalytik. Die auf diese Weise genauestens charakterisierten neuartigen Materialien können nun gezielt und anwendungsfokussiert weiterentwickelt werden. N2 - In this work the potential of the luminescence of europium for structural analysis using novel materials is presented. These materials are on the one hand side nanoparticles made of various metal mixed oxide and doped by europium as a structural probe and on the other hand side the so-called metal organic frameworks (MOFs) loaded with neodymium, samarium and europium ions. The synthesis of the metal mixed oxide nanoparticles is done under mild conditions using reagents that have been specifically produced for this application. It leads to very small and amorphous nanoparticles. The crystallinity is increased by downstreamed temperature treatment. Related to that, the crystal structure and the position of the europium dopant have changed. While the well-established method of X-ray-diffraction offers an insight to the whole crystal lattice, the luminescence of europium gives information about the local symmetry of single europium ions using the visibility of single Stark-splittings. The symmetry is changed by oxygen vacancies which have an influence on the oxygen conductivity of the nanoparticles. This property is important for the application in industrial catalysts as well as in sensors and therapeutic agents in biological systems. For basic catalytical characterisation the samples are examined using the method of temperature-programmed reduction. Furthermore, the metal mixed oxide nanoparticles are also evaluated concerning the usability of the matrix in upconversion-processes. The metal organic frameworks are suitable for the storage of technical gases and pollutants due to their microporous structure. An application in the biological context can be seen especially in the field of drug delivery agents. By intercalation of certain combinations of lanthanide ions in the microporous structure of the metal organic frameworks, white light emitters can be developed. In this application the ratio between the lanthanide ions as well as their exact position within the framework and the distance between the single ions are of interest. For unravelling the regarding open questions, the environment-sensitive luminescence of the europium is used. The determined formate formation depends on several parameters. To sum up, the method of using europium as a structural probe as shown in this work is highly versatile and proves its worth in combination with further methods of structural analysis. Furthermore, an advanced development of the novel materials with focus on specific applications is now well prepared due to precise characterisation. KW - Spektroskopie KW - Nanomaterialien KW - Ceroxid KW - metallorganische Netzwerke KW - spectroscopy KW - nanomaterials KW - cerium oxide KW - metal organic frameworks Y1 - 2019 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-427141 ER - TY - THES A1 - Riebe, Daniel T1 - Experimental and theoretical investigations of molecular ions by spectroscopy as well as ion mobility and mass spectrometry T1 - Experimentelle und theoretische Untersuchungen molekularer Ionen durch Spektroskopie sowie Ionenmobilitäts- und Massenspektrometrie N2 - The aim of this thesis was the elucidation of different ionization methods (resonance-enhanced multiphoton ionization – REMPI, electrospray ionization – ESI, atmospheric pressure chemical ionization – APCI) in ion mobility (IM) spectrometry. In order to gain a better understanding of the ionization processes, several spectroscopic, mass spectrometric and theoretical methods were also used. Another focus was the development of experimental techniques, including a high resolution spectrograph and various combinations of IM and mass spectrometry. The novel high resolution 2D spectrograph facilitates spectroscopic resolutions in the range of commercial echelle spectrographs. The lowest full width at half maximum of a peak achieved was 25 pm. The 2D spectrograph is based on the wavelength separation of light by the combination of a prism and a grating in one dimension, and an etalon in the second dimension. This instrument was successfully employed for the acquisition of Raman and laser-induced breakdown spectra. Different spectroscopic methods (light scattering and fluorescence spectroscopy) permitting a spatial as well as spectral resolution, were used to investigate the release of ions in the electrospray. The investigation is based on the 50 nm shift of the fluorescence band of rhodamine 6G ions of during the transfer from the electrospray droplets to the gas phase. A newly developed ionization chamber operating at reduced pressure (0.5 mbar) was coupled to a time-of-flight mass spectrometer. After REMPI of H2S, an ionization chemistry analogous to H2O was observed with this instrument. Besides H2S+ and its fragments, H3S+ and protonated analyte ions could be observed as a result of proton-transfer reactions. For the elucidation of the peaks in IM spectra, a combination of IM spectrometer and linear quadrupole ion trap mass spectrometer was developed. The instrument can be equipped with various ionization sources (ESI, REMPI, APCI) and was used for the characterization of the peptide bradykinin and the neuroleptic promazine. The ionization of explosive compounds in an APCI source based on soft x-radiation was investigated in a newly developed ionization chamber attached to the ion trap mass spectrometer. The major primary and secondary reactions could be characterized and explosive compound ions could be identified and assigned to the peaks in IM spectra. The assignment is based on the comparison of experimentally determined and calculated IM. The methods of calculation currently available exhibit large deviations, especially in the case of anions. Therefore, on the basis of an assessment of available methods, a novel hybrid method was developed and characterized. N2 - Ziel dieser Arbeit war die Aufklärung unterschiedlicher Ionisationsmethoden (Resonanz-verstärkte Mehrphotonenionisation – REMPI, Elektrosprayionisation – ESI, chemische Ionisation bei Atmosphärendruck – APCI) in der Ionenmobilitäts (IM)-Spektrometrie. Um ein besseres Verständnis der Ionisationsprozesse zu erhalten, wurden zusätzlich ver¬schiedene spektroskopische, massenspektrometrische und theoretische Methoden eingesetzt. Ein weiterer Schwerpunkt war die Entwicklung neuer experimenteller Techniken, darunter ein hochauflösender Spektrograph und verschiedene Kombinationen von IM- und Massenspektrometern. Der neuartige, hochauflösende 2D Spektrograph ermöglicht spektroskopische Auflösungen im Bereich kommerzieller Echelle-Spektrographen. Die geringste erreichte Halbwertsbreite eines Peaks betrug 25 pm. Der 2D Spektrograph beruht auf der Wellenlängenseparation von Licht durch eine Kombination aus einem Prisma und einem Gitter in der einen Dimension und einem Etalon in der zweiten Dimension. Das Instrument wurde erfolgreich zur Aufnahme von Raman- und laserinduzierten Plasmaspektren ein¬gesetzt. Verschiedene spektroskopische Methoden (Lichtstreuung und Fluoreszenzspektroskopie), die sowohl eine räumliche, als auch eine spektrale Auflösung erlauben, wurden zur Untersuchung der Freisetzung der Ionen im Elektrospray angewandt. Die Untersuchung beruht auf der Verschiebung der Fluoreszenzbande von Rhodamin 6G-Ionen um 50 nm beim Übergang aus den Elektrospray-Tropfen in die Gasphase. Eine neuent¬wickelte Ionisationskammer bei reduziertem Druck (0,5 mbar) wurde an ein Flugzeit-Massenspektrometer gekoppelt. Darin wurde nach REMPI von H2S eine zum H2O analoge Ionisationschemie beobachtet. Neben H2S+ und seinen Fragmenten wurden als Ergebnis von Proto-nen-Transferreaktionen H3S+ und protonierte Analytionen beobachtet. Zur Aufklärung der Peaks in IM-Spektren wurde eine Kopplung von IM-Spektrometer und linearem Quadrupol-Ionenfallen-Massenspektrometer entwickelt. Die Kopplung kann mit verschiedenen Ionisationsquellen (ESI, REMPI, APCI) ausgestattet werden und wurde zur Charakterisierung des Peptids Bradykinin und des Neuroleptikums Promazin angewendet. Die Ionisation von Sprengstoffen in einer APCI-Quelle, die auf weicher Röntgenstrahlung beruht, wurde in einer neu entwickelten, an das Ionenfallen-Massenspektrometer gekoppelten Ionisationskammer untersucht. Dabei konnten die wichtigsten Primär- und Sekundärreaktionen charakterisiert, sowie Sprengstoffionen identifiziert und den Peaks in den IM-Spektren zugeordnet werden. Diese Zuordnung beruht auf dem Vergleich von experimentell bestimmten und berechneten IM. Da die aktuell verfügbaren Berechnungsmethoden insbesondere für Anionen zu große Abweichungen zu den experimentell bestimmten IM aufweisen, wurde auf Basis der Bewertung verfügbarer Methoden eine neue Hybridmethode entwickelt und charakterisiert. KW - ion mobility spectrometry KW - mass spectrometry KW - explosives KW - X-ray KW - photoionization KW - ion mobility calculations KW - Ionenmobilitätsspektrometrie KW - Massenspektrometrie KW - Sprengstoffe KW - Röntgenstrahlung KW - Photoionisation KW - Ionenmobilitäts-Berechnungen Y1 - 2016 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-94632 ER - TY - THES A1 - Kopetzki, Daniel T1 - Exploring hydrothermal reactions : from prebiotic synthesis to green chemistry T1 - Hydrothermalreaktionen : von präbiotischer Synthese zu nachhaltiger Chemie N2 - In this thesis chemical reactions under hydrothermal conditions were explored, whereby emphasis was put on green chemistry. Water at high temperature and pressure acts as a benign solvent. Motivation to work under hydrothermal conditions was well-founded in the tunability of physicochemical properties with temperature, e.g. of dielectric constant, density or ion product, which often resulted in surprising reactivity. Another cornerstone was the implementation of the principles of green chemistry. Besides the use of water as solvent, this included the employment of a sustainable feedstock and the sensible use of resources by minimizing waste and harmful intermediates and additives. To evaluate the feasibility of hydrothermal conditions for chemical synthesis, exemplary reactions were performed. These were carried out in a continuous flow reactor, allowing for precise control of reaction conditions and kinetics measurements. In most experiments a temperature of 200 °C in combination with a pressure of 100 bar was chosen. In some cases the temperature was even raised to 300 °C. Water in this subcritical range can also be found in nature at hydrothermal vents on the ocean floor. On the primitive earth, environments with such conditions were however present in larger numbers. Therefore we tested whether biologically important carbohydrates could be formed at high temperature from the simple, probably prebiotic precursor formaldehyde. Indeed, this formose reaction could be carried out successfully, although the yield was lower compared to the counterpart reaction under ambient conditions. However, striking differences regarding selectivity and necessary catalysts were observed. At moderate temperatures bases and catalytically active cations like Ca2+ are necessary and the main products are hexoses and pentoses, which accumulate due to their higher stability. In contrast, in high-temperature water no catalyst was necessary but a slightly alkaline solution was sufficient. Hexoses were only formed in negligible amounts, whereas pentoses and the shorter carbohydrates accounted for the major fraction. Amongst the pentoses there was some preference for the formation of ribose. Even deoxy sugars could be detected in traces. The observation that catalysts can be avoided was successfully transferred to another reaction. In a green chemistry approach platform chemicals must be produced from sustainable resources. Carbohydrates can for instance be employed as a basis. They can be transformed to levulinic acid and formic acid, which can both react via a transfer hydrogenation to the green solvent and biofuel gamma-valerolactone. This second reaction usually requires catalysis by Ru or Pd, which are neither sustainable nor low-priced. Under hydrothermal conditions these heavy metals could be avoided and replaced by cheap salts, taking advantage of the temperature dependence of the acid dissociation constant. Simple sulfate was recognized as a temperature switchable base. With this additive high yield could be achieved by simultaneous prevention of waste. In contrast to conventional bases, which create salt upon neutralization, a temperature switchable base becomes neutral again when cooled down and thus can be reused. This adds another sustainable feature to the high atom economy of the presented hydrothermal synthesis. In a last study complex decomposition pathways of biomass were investigated. Gas chromatography in conjunction with mass spectroscopy has proven to be a powerful tool for the identification of unknowns. It was observed that several acids were formed when carbohydrates were treated with bases at high temperature. This procedure was also applied to digest wood. Afterwards it was possible to fermentate the solution and a good yield of methane was obtained. This has to be regarded in the light of the fact that wood practically cannot be used as a feedstock in a biogas factory. Thus the hydrothermal pretreatment is an efficient means to employ such materials as well. Also the reaction network of the hydrothermal decomposition of glycine was investigated using isotope-labeled compounds as comparison for the unambiguous identification of unknowns. This refined analysis allowed the identification of several new molecules and pathways, not yet described in literature. In summary several advantages could be taken from synthesis in high-temperature water. Many catalysts, absolutely necessary under ambient conditions, could either be completely avoided or replaced by cheap, sustainable alternatives. In this respect water is not only a green solvent, but helps to prevent waste and preserves resources. N2 - In dieser Arbeit wurden chemische Reaktionen unter Hydrothermalbedingungen untersucht. Darunter versteht man Wasser als Reaktionsmedium, welches eine Temperatur über 100 °C aufweist. Der flüssige Zustand wird dabei durch erhöhten Druck aufrecht erhalten. Typischerweise wurden die Reaktionen bei 200 °C und einem Druck von 100 bar durchgeführt, also dem 100-fachen des Normaldrucks. Dieses System kann man auch mit einem Dampfdrucktopf vergleichen, wobei durch die erhöhten Temperaturen chemische Reaktionen sehr schnell ablaufen und überraschende Reaktivität auftritt. Die Motivation, Wasser als Lösemittel zu benutzen, ist auch in seiner Umweltfreundlichkeit gegenüber klassischen organischen Lösemitteln begründet. Da solche Hydrothermalbedingungen auf der frühen Erde häufiger anzutreffen waren, wurde untersucht, ob wichtige Biomoleküle bei solch hoher Temperatur gebildet werden können. In der Tat konnten Zucker aus der sehr einfachen Verbindung Formaldehyd synthetisiert werden. Hierzu war lediglich eine leicht basische Lösung nötig und keine der bei moderaten Temperaturen essentiellen Katalysatoren. Zucker stellen zudem den größten Teil der pflanzlichen Biomasse dar und können daher als Grundlage für eine nachhaltige Chemie dienen. Sie können relativ einfach zu Lävulin- und Ameisensäure umgesetzt werden. Aus diesen wiederum kann die wichtige Basischemikalie gamma-Valerolacton hergestellt werden. Der Schlüsselschritt, die Reduktion von Lävulinsäure, erforderte bisher die Zuhilfenahme seltener Edelmetalle wie Ruthenium. Es konnte nun gezeigt werden, dass unter Hydrothermalbedingungen diese Rolle von einfachen Salzen, z. B. Natriumsulfat, übernommen werden kann. Hierbei macht man sich zunutze, dass sie nur bei hoher Temperatur basisch wirken, nicht aber wenn die Lösung wieder abgekühlt ist. Neben Kohlenhydraten besteht Biomasse auch aus Aminosäuren, von denen Glycin die einfachste darstellt. Unter Abspaltung von CO2 können aus ihnen synthetisch wichtige Amine hergestellt werden. Diese Reaktion findet unter Hydrothermalbedingungen statt, daneben treten jedoch noch andere Produkte auf. Unbekannte Verbindungen wurden mittels Massenspektroskopie identifiziert, wobei die Masse des Moleküls und bestimmter Molekülfragmente bestimmt wurde. Dies erlaubte es, bisher noch unbekannte Reaktionswege aufzuklären. Zusammenfassend lässt sich sagen, dass Wasser unter Hydrothermalbedingungen eine interessante Alternative zu organischen Lösemitteln darstellt. Desweiteren können bestimmte Katalysatoren, die bei moderaten Temperaturen nötig sind, entweder vollständig eingespart oder ersetzt werden. In dieser Hinsicht ist Wasser nicht nur ein umweltfreundliches Lösemittel, sondern trägt dazu bei, Abfall zu vermeiden und Ressourcen zu schonen. KW - hydrothermal KW - Formose KW - Valerolacton KW - Lävulinsäure KW - hydrothermal KW - formose KW - valerolactone KW - levulinic acid Y1 - 2011 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-52581 ER - TY - THES A1 - Deshpande, Atul Suresh T1 - Fabrication of porous metal oxides for catalytic application using templating techniques T1 - Herstellung poröser Metalloxide für katalytische Anwendungen unter Verwendung von Templatierungsverfahren N2 - Nanostrukturierte Materialien zeichnen sich dadurch aus, dass sie aus sehr kleinen Baueinheiten zusammengesetzt sind. Typischerweise liegt die Grössenordnung dieser Bausteine im Bereich von einigen Nanometern. Ein Nanometer entspricht 10-9 Meter. Dadurch bekommen nanostrukturierte Materialien oft verbesserte, vielfach sogar ganz neue Eigenschaften, die für viele heutige wie auch zukünftige Anwendungen von Vorteil sind. Ein Weg, um solche nanostrukturierte Materialien herzustellen, ist die sogenannte „Templatierungsmethode“. Das Templat besteht aus einem einzelnen Molekül, einer Ansammlung von Molekülen oder aus einem festen Objekt. Beim Aufbau des nanostrukturierten Materials wirkt das Templat als Schablone oder als Gussform und beeinflusst damit die Struktur des Endproduktes. Normalerweise besteht dieser Prozess aus mehreren Schritten. Zuerst wird der Raum um das Templat mit dem Ausgangsstoff umhüllt oder ausgefüllt, dann wird der Ausgangsstoff chemisch in das gewünschte Endprodukt umgewandelt, wobei das Templat die Endform kontrolliert und am Schluss wird das Templat entfernt. Das geschieht meistens durch Erhitzen. Als Ausgangsstoff können dabei einzelne Moleküle verwendet werden, die sich leicht in das Endprodukt umwandeln lassen, oder aber vorgeformte Partikelchen, die nur noch zur entsprechenden Form angeordnet werden müssen. In dieser Arbeit wurden poröse Metalloxid-Kügelchen hergestellt, die aus einem Gemisch aus Titanoxid und entweder Aluminium-, Gallium- oder Indiumoxid bestehen. Als Template wurden poröse Kunststoffkügelchen eingesetzt, die man sonst für Chromatographiezwecke braucht. Bei der Synthese wurden die Poren der Kunststoffkügelchen mit dem Ausgangsmaterial gefüllt und mit Wasser in ein amorphes Netzwerk umgewandelt. Danach werden die Kügelchen erhitzt, wobei das Kunststofftemplat zersetzt wird. Gleichzeitig wird das amorphe Gerüst in stabile, kristalline Wände umgewandelt, die die Form der Kügelchen auch dann noch behalten, wenn das Templat verschwunden ist. Mit einem ähnlichen Prozess wurden auch Kügelchen aus Cer-Zirkonoxid erhalten. Als Ausgangsstoff wurden dabei aber vorgeformte Cer-Zirkonoxid-Nanopartikel eingesetzt, die in die Poren der Kunststofftemplatkügelchen hinein diffundieren. Diese Cer-Zirkonoxid-Nanopartikel lassen sich auch für die Herstellung von porösen Pulvern verwenden, wobei dann nicht Polymerkügelchen, sondern hochgeordnete Ansammlungen von Block Copolymeren als Template verwendet werden. Form, Struktur und Eigenschaften all dieser Materialien wurden systematisch unter Anwendung verschiedenster Analysemethoden untersucht. Die auf Titanoxid-basierten Kügelchen wurden auch auf ihre photokatalytische Verwendung zum Abbau von umweltschädlichem 2-Chlorophenol untersucht. Die Cer-Zirkonoxid-Kügelchen wurden für die Herstellung von Wasserstoff aus Methanol getestet. Wasserstoff gilt als hoffungsvoller, sauberer Energieträger der Zukunft und kommt in Brennstoffzellen zum Einsatz. N2 - Nanostructured materials are the materials having structural features on the scale of nanometers i.e. 10-9 m. the structural features can enhance the natural properties of the materials or induce additional properties, which are useful for day to technology as well as the future technologies One way to synthesize nanostructured materials is using templating techniques. The templating process involves use of a certain “mould” or “scaffold” to generate the structure. The mould is called as the template, can be a single molecule or assembly of molecule or a larger object, which has its own structure. The product material can be obtained by filling the space around the template with a “precursor”, transformation of precursor into the desired material and then removal of template to get product. The precursor can be any chemical moiety that can be easily transformed in to the desired material. Alternatively the desired material is processed into very tiny bricks or “nano building blocks (NBB)” and the product is obtained by arrangement of the NBB by using a scaffold. We synthesized porous metal oxide spheres of namely TiO2-M2O3: titanium dioxide- M-oxide (M = aluminum, gallium and indium) TiO2-M2O3 and cerium oxide-zirconium oxide solid solution. We used porous polymeric beads as templates. These beads used for chromatographic purposes. For the synthesis of TiO2-M2O3 we used metal- alkoxides as precursor. The pore of beads were filled with precursor and then reacted with water to give transformation of the precursor to amorphous oxide network. The network is crystallized and template is removed by heat treatment at high temperatures. In a similar way we obtained porous spheres of CexZr1-xO2. For this we synthesized nanoparticle of CexZr1-xO2 and used then for the templating process to obtain porous CexZr1-xO2 spheres. Additionally, using the same nanoparticles we synthesized nano-porous powder using self-assembly process between a block-copolymers scaffold and nanoparticles. Morphological and physico-chemical properties of these materials were studies systematically by using various analytical techniques TiO2-M2O3 material were tested for photocatalytic degradation of 2-Chlorophenol a poisonous pollutant. While CexZr1-xO2 spheres were tested for methanol steam reforming reaction to generate hydrogen, which is a fuel for future generation power sources like fuel cells. All the materials showed good catalytic performance. KW - porous materials KW - metal oxides KW - catalytic application Y1 - 2004 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-0001324 ER - TY - THES A1 - Borisova, Dimitriya T1 - Feedback active coatings based on mesoporous silica containers T1 - Rückkopplungsaktive Beschichtungen basierend auf mesoporösen Silika-Behältern N2 - Metalle werden oft während ihrer Anwendung korrosiven Bedingungen ausgesetzt, was ihre Alterungsbeständigkeit reduziert. Deswegen werden korrosionsanfällige Metalle, wie Aluminiumlegierungen mit Schutzbeschichtungen versehen, um den Korrosionsprozess aktiv oder passiv zu verhindern. Die klassischen Schutzbeschichtungen funktionieren als physikalische Barriere zwischen Metall und korrosiver Umgebung und bieten einen passiven Korrosionsschutz nur, wenn sie unbeschädigt sind. Im Gegensatz dazu kann die Korrosion auch im Fall einer Beschädigung mittels aktiver Schutzbeschichtungen gehemmt werden. Chromathaltige Beschichtungen bieten heutzutage den besten aktiven Korrosionsschutz für Aluminiumlegierungen. Aufgrund ihrer Giftigkeit wurden diese weltweit verboten und müssen durch neue umweltfreundliche Schutzbeschichtungen ersetzt werden. Ein potentieller Ersatz sind Schutzbeschichtungen mit integrierten Nano- und Mikrobehältern, die mit ungiftigem Inhibitor gefüllt sind. In dieser Arbeit werden die Entwicklung und Optimierung solcher aktiver Schutzbeschichtungen für die industriell wichtige Aluminiumlegierung AA2024-T3 dargestellt Mesoporöse Silika-Behälter wurden mit dem ungiftigen Inhibitor (2-Mercaptobenzothiazol) beladen und dann in die Matrix anorganischer (SiOx/ZrOx) oder organischer (wasserbasiert) Schichten dispergiert. Zwei Sorten von Silika-Behältern mit unterschiedlichen Größen (d ≈ 80 and 700 nm) wurden verwendet. Diese haben eine große spezifische Oberfläche (≈ 1000 m² g-1), eine enge Porengrößenverteilung mit mittlerer Porenweite ≈ 3 nm und ein großes Porenvolumen (≈ 1 mL g-1). Dank dieser Eigenschaften können große Inhibitormengen im Behälterinneren adsorbiert und gehalten werden. Die Inhibitormoleküle werden bei korrosionsbedingter Erhöhung des pH-Wertes gelöst und freigegeben. Die Konzentration, Position und Größe der integrierten Behälter wurden variiert um die besten Bedingungen für einen optimalen Korrosionsschutz zu bestimmen. Es wurde festgestellt, dass eine gute Korrosionsschutzleistung durch einen Kompromiss zwischen ausreichender Inhibitormenge und guten Barriereeigenschaften hervorgerufen wird. Diese Studie erweitert das Wissen über die wichtigsten Faktoren, die den Korrosionsschutz beeinflussen. Somit wurde die Entwicklung effizienter, aktiver Schutzbeschichtungen ermöglicht, die auf mit Inhibitor beladenen Behältern basieren. N2 - Metals are often used in environments that are conducive to corrosion, which leads to a reduction in their mechanical properties and durability. Coatings are applied to corrosion-prone metals such as aluminum alloys to inhibit the destructive surface process of corrosion in a passive or active way. Standard anticorrosive coatings function as a physical barrier between the material and the corrosive environment and provide passive protection only when intact. In contrast, active protection prevents or slows down corrosion even when the main barrier is damaged. The most effective industrially used active corrosion inhibition for aluminum alloys is provided by chromate conversion coatings. However, their toxicity and worldwide restriction provoke an urgent need for finding environmentally friendly corrosion preventing systems. A promising approach to replace the toxic chromate coatings is to embed particles containing nontoxic inhibitor in a passive coating matrix. This work presents the development and optimization of effective anticorrosive coatings for the industrially important aluminum alloy, AA2024-T3 using this approach. The protective coatings were prepared by dispersing mesoporous silica containers, loaded with the nontoxic corrosion inhibitor 2-mercaptobenzothiazole, in a passive sol-gel (SiOx/ZrOx) or organic water-based layer. Two types of porous silica containers with different sizes (d ≈ 80 and 700 nm, respectively) were investigated. The studied robust containers exhibit high surface area (≈ 1000 m² g-1), narrow pore size distribution (dpore ≈ 3 nm) and large pore volume (≈ 1 mL g-1) as determined by N2 sorption measurements. These properties favored the subsequent adsorption and storage of a relatively large amount of inhibitor as well as its release in response to pH changes induced by the corrosion process. The concentration, position and size of the embedded containers were varied to ascertain the optimum conditions for overall anticorrosion performance. Attaining high anticorrosion efficiency was found to require a compromise between delivering an optimal amount of corrosion inhibitor and preserving the coating barrier properties. This study broadens the knowledge about the main factors influencing the coating anticorrosion efficiency and assists the development of optimum active anticorrosive coatings doped with inhibitor loaded containers. KW - Korrosion KW - Beschichtungen KW - Aluminiumlegierung KW - Silika KW - Nanopartikel KW - mesoporös KW - corrosion KW - coating KW - aluminum alloy KW - silica nanoparticles KW - mesoporous Y1 - 2012 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-63505 ER - TY - THES A1 - Nothofer, Heinz-Georg T1 - Flüssigkristalline Polyfluorene N2 - Eine Reihe 9,9-dialkylsubstituierter Polyfluorene mit linearen und verzweigtkettigen Alkylsubstituenten und einem Molekulargewicht von bis zu 200000 g/mol wurde synthetisiert und charakterisiert. Darüber hinaus wurden einige dieser Polymere mit einer geeigneten 'Lochtransport'-Funktionalität (Triphenylamin-Derivate) ausgestattet, um die Ladungstransporteigenschaften und das Molekulargewicht dieser Substanzen zu kontrollieren. Die thermische Orientierung dieser neuen Polymere auf geriebenen Polyimid-Schichten führte zu hoch anisotropen Filmen mit großen dichroischen Verhältnissen (Absorption parallel und senkrecht zur Reibungsrichtung gemessen). Ferner wurde eine Gruppe chiraler Polyfluorene synthetisiert und hinsichtlich ihrer chiroptischen Eigenschaften untersucht. Der mit diesen chiralen, konjugierten Polymeren erreichte Grad der Anisotropie in Absorption (CD), circular polarisierter Photolumineszenz (CPPL) und Elektrolumineszenz (CPEL) überstieg die bis dahin bekannten Werte um einen Faktor von 200. N2 - A series of 9,9-dialkyl-poly(fluorene-2,7-diyl)s containing linear and branched alkyl substituents with a molecular weight of up to 200000 g/mol has been synthesized and characterized. Moreover, some of the polymers were end capped with a suitable hole transport functionality, such as a triphenylamine derivative, to improve their charge transport properties and to control the molecular weight. The thermal alignment of these novel polymers on a rubbed polyimide layer led to highly anisotropic film formation with large dichroic ratios (absorption parallel and perpendicular to the rubbing direction). Additionally a set of chiral polyfluorenes has been synthesized and investigated with respect to their chiroptical properties. The degrees of anisotropy in absorption (CD), circular polarized photoluminescence (CPPL) and electroluminescence (CPEL) found with these chiral conjugated polymers exceeded the yet known values by a factor of 200. KW - Polyfluoren KW - konjugierte Polymere KW - Elektrolumineszenz KW - OLED KW - Circularpolarisation Y1 - 2001 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-0000039 ER - TY - THES A1 - Melani, Giacomo T1 - From structural fluctuations to vibrational spectroscopy of adsorbates on surfaces T1 - Von Strukturfluktuationen bis zur Schwingungsspektroskopie von Adsorbaten auf Oberflächen BT - a theoretical study of H2O on α-Al2O3(0001) BT - eine theoretische Untersuchung von H2O auf α-Al2O3 (0001) N2 - Aluminum oxide is an Earth-abundant geological material, and its interaction with water is of crucial importance for geochemical and environmental processes. Some aluminum oxide surfaces are also known to be useful in heterogeneous catalysis, while the surface chemistry of aqueous oxide interfaces determines the corrosion, growth and dissolution of such materials. In this doctoral work, we looked mainly at the (0001) surface of α-Al 2 O 3 and its reactivity towards water. In particular, a great focus of this work is dedicated to simulate and address the vibrational spectra of water adsorbed on the α-alumina(0001) surface in various conditions and at different coverages. In fact, the main source of comparison and inspiration for this work comes from the collaboration with the “Interfacial Molecular Spectroscopy” group led by Dr. R. Kramer Campen at the Fritz-Haber Institute of the MPG in Berlin. The expertise of our project partners in surface-sensitive Vibrational Sum Frequency (VSF) generation spectroscopy was crucial to develop and adapt specific simulation schemes used in this work. Methodologically, the main approach employed in this thesis is Ab Initio Molecular Dynamics (AIMD) based on periodic Density Functional Theory (DFT) using the PBE functional with D2 dispersion correction. The analysis of vibrational frequencies from both a static and a dynamic, finite-temperature perspective offers the ability to investigate the water / aluminum oxide interface in close connection to experiment. The first project presented in this work considers the characterization of dissociatively adsorbed deuterated water on the Al-terminated (0001) surface. This particular structure is known from both experiment and theory to be the thermodynamically most stable surface termination of α-alumina in Ultra-High Vacuum (UHV) conditions. Based on experiments performed by our colleagues at FHI, different adsorption sites and products have been proposed and identified for D 2 O. While previous theoretical investigations only looked at vibrational frequencies of dissociated OD groups by staticNormal Modes Analysis (NMA), we rather employed a more sophisticated approach to directly assess vibrational spectra (like IR and VSF) at finite temperature from AIMD. In this work, we have employed a recent implementation which makes use of velocity-velocity autocorrelation functions to simulate such spectral responses of O-H(D) bonds. This approach allows for an efficient and qualitatively accurate estimation of Vibrational Densities of States (VDOS) as well as IR and VSF spectra, which are then tested against experimental spectra from our collaborators. In order to extend previous work on unimolecularly dissociated water on α-Al 2 O 3 , we then considered a different system, namely, a fully hydroxylated (0001) surface, which results from the reconstruction of the UHV-stable Al-terminated surface at high water contents. This model is then further extended by considering a hydroxylated surface with additional water molecules, forming a two-dimensional layer which serves as a potential template to simulate an aqueous interface in environmental conditions. Again, employing finite-temperature AIMD trajectories at the PBE+D2 level, we investigated the behaviour of both hydroxylated surface (HS) and the water-covered structure derived from it (known as HS+2ML). A full range of spectra, from VDOS to IR and VSF, is then calculated using the same methodology, as described above. This is the main focus of the second project, reported in Chapter 5. In this case, comparison between theoretical spectra and experimental data is definitely good. In particular, we underline the nature of high-frequency resonances observed above 3700 cm −1 in VSF experiments to be associated with surface OH-groups, known as “aluminols” which are a key fingerprint of the fully hydroxylated surface. In the third and last project, which is presented in Chapter 6, the extension of VSF spectroscopy experiments to the time-resolved regime offered us the opportunity to investigate vibrational energy relaxation at the α-alumina / water interface. Specifically, using again DFT-based AIMD simulations, we simulated vibrational lifetimes for surface aluminols as experimentally detected via pump-probe VSF. We considered the water-covered HS model as a potential candidate to address this problem. The vibrational (IR) excitation and subsequent relaxation is performed by means of a non-equilibrium molecular dynamics scheme. In such a scheme, we specifically looked at the O-H stretching mode of surface aluminols. Afterwards, the analysis of non-equilibrium trajectories allows for an estimation of relaxation times in the order of 2-4 ps which are in overall agreement with measured ones. The aim of this work has been to provide, within a consistent theoretical framework, a better understanding of vibrational spectroscopy and dynamics for water on the α-alumina(0001) surface,ranging from very low water coverage (similar to the UHV case) up to medium-high coverages, resembling the hydroxylated oxide in environmental moist conditions. N2 - Das Hauptziel dieser Doktorarbeit war die Untersuchung der Wechselwirkung zwischen Aluminiumoxid (α-Al2O3) und Wasser, wobei die (0001)-Oberfläche von α-Al2O3 im Fokus der Betrachtungen stand. Infolge der Entwicklung moderner oberflächensensitiver spektroskopischer Methoden, insbesondere in der Schwingungsspektroskopie, ist es inzwischen experimentell möglich, die Oberflächenchemie dieser Oxidmaterialien zu untersuchen und atomistische Informationen über ihre wässrigen Grenzflächen zu erhalten. Unsere Gruppe hat mit der Interfacial Molecular Spectroscopy Gruppe des Fritz-Haber-Instituts der MPG in Berlin zusammengearbeitet, deren Expertise in der oberflächensensitiven Vibrational Sum Frequency (VSF) Generation liegt. Diese Technik gestattet den spezifischen Nachweis von Adsorbatvibrationen, beispielsweise des Produkts der Wasserdissoziation und -adsorption. Zur theoretischen Untersuchung dieses Systems wurden verschiedene Berechnungsmethoden genutzt, wobei bevorzugt die Ab-initio-Molekulardynamik (AIMD) zum Einsatz kam. Darüber hinaus konzentrierten wir uns auf die Simulation von Schwingungsfrequenzen und -spektren für verschiedene Systeme unter Verwendung eines neuen, effizienten Algorithmus, der auf Grundlage klassischer Zeitkorrelationsfunktionen entwickelt wurde. Das erste Projekt untersuchte die einfachsten Adsorptionsprodukte von Wasserreaktionen auf der Al-terminierten α-Al2O3(0001)-Oberfläche, die unter Ultrahochvakuumbedingungen (UHV) als stabilste Struktur bekannt ist. Mit AIMD-basierten Methoden haben wir verschiedene Spezies simuliert, die aus unimolekular adsorbiertem Wasser stammen, und ihre Schwingungsfrequenzen im Vergleich zum Experiment bestimmt. In einem zweiten Projekt widmeten wir uns einer Situation, in der eine vollständig hydroxylierte α-Aluminiumoxid-Oberfläche mit einer ebenfalls vollständig hydroxylierten, aber um eine zusätzliche Wasserschicht erweiterten α-Aluminiumoxid-Oberfläche wechselwirkt. Diese beiden Strukturen dienen als Grundlage zur weitergehenden Untersuchung von Aluminiumoxid-Oberflächen mit größeren Wasser-Bedeckungsgraden unter Umgebungsbedingungen. Wiederum simulierten wir vollständige Schwingunsspektren (einschließlich IR und VSF). Hierzu wurden etablierte Methoden genutzt, die auf der Verwendung von Zeitkorrelationsfunktionen basieren, jedoch von uns im Rahmen dieser Doktorarbeit weiterentwickelt wurden. Schließlich haben wir in einem dritten Projekt in Zusammenarbeit mit Experimentatoren die Schwingungsrelaxation an der Wasser / α-Al2O3-Grenzfläche beschrieben. Motiviert durch Pump-Probe-VSF-Experimente zur Bestimmung der Schwingungslebensdauer adsorbierter OH-Spezies entwickelten und verwendeten wir einen AIMD-Ansatz zur Simulation der Anregungs- und Relaxationsprozesse. Auf Grundlage von Nichtgleichgewichtstrajektorien konnten wir auch eine Relaxationszeitskala für OH-Gruppen ermitteln, die zwischen 2 und 4 Pikosekunden beträgt und gut mit experimentellen Werten übereinstimmt. KW - theoretical chemistry KW - molecular dynamics KW - DFT KW - vibrational spectroscopy KW - theoretische Chemie KW - Molekulardynamik KW - DFT KW - Schwingungsspektroskopie Y1 - 2019 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-441826 ER - TY - THES A1 - Mbaya Mani, Christian T1 - Functional nanoporous carbon-based materials derived from oxocarbon-metal coordination complexes T1 - Funktionale nanoporöse Kohlenstoffmaterialien auf Basis von Oxokohlenstoff-Metal Koordinationskomplexe N2 - Nanoporous carbon based materials are of particular interest for both science and industry due to their exceptional properties such as a large surface area, high pore volume, high electroconductivity as well as high chemical and thermal stability. Benefiting from these advantageous properties, nanoporous carbons proved to be useful in various energy and environment related applications including energy storage and conversion, catalysis, gas sorption and separation technologies. The synthesis of nanoporous carbons classically involves thermal carbonization of the carbon precursors (e.g. phenolic resins, polyacrylonitrile, poly(vinyl alcohol) etc.) followed by an activation step and/or it makes use of classical hard or soft templates to obtain well-defined porous structures. However, these synthesis strategies are complicated and costly; and make use of hazardous chemicals, hindering their application for large-scale production. Furthermore, control over the carbon materials properties is challenging owing to the relatively unpredictable processes at the high carbonization temperatures. In the present thesis, nanoporous carbon based materials are prepared by the direct heat treatment of crystalline precursor materials with pre-defined properties. This synthesis strategy does not require any additional carbon sources or classical hard- or soft templates. The highly stable and porous crystalline precursors are based on coordination compounds of the squarate and croconate ions with various divalent metal ions including Zn2+, Cu2+, Ni2+, and Co2+, respectively. Here, the structural properties of the crystals can be controlled by the choice of appropriate synthesis conditions such as the crystal aging temperature, the ligand/metal molar ratio, the metal ion, and the organic ligand system. In this context, the coordination of the squarate ions to Zn2+ yields porous 3D cube crystalline particles. The morphology of the cubes can be tuned from densely packed cubes with a smooth surface to cubes with intriguing micrometer-sized openings and voids which evolve on the centers of the low index faces as the crystal aging temperature is raised. By varying the molar ratio, the particle shape can be changed from truncated cubes to perfect cubes with right-angled edges. These crystalline precursors can be easily transformed into the respective carbon based materials by heat treatment at elevated temperatures in a nitrogen atmosphere followed by a facile washing step. The resulting carbons are obtained in good yields and possess a hierarchical pore structure with well-organized and interconnected micro-, meso- and macropores. Moreover, high surface areas and large pore volumes of up to 1957 m2 g-1 and 2.31 cm3 g-1 are achieved, respectively, whereby the macroscopic structure of the precursors is preserved throughout the whole synthesis procedure. Owing to these advantageous properties, the resulting carbon based materials represent promising supercapacitor electrode materials for energy storage applications. This is exemplarily demonstrated by employing the 3D hierarchical porous carbon cubes derived from squarate-zinc coordination compounds as electrode material showing a specific capacitance of 133 F g-1 in H2SO4 at a scan rate of 5 mV s-1 and retaining 67% of this specific capacitance when the scan rate is increased to 200 mV s-1. In a further application, the porous carbon cubes derived from squarate-zinc coordination compounds are used as high surface area support material and decorated with nickel nanoparticles via an incipient wetness impregnation. The resulting composite material combines a high surface area, a hierarchical pore structure with high functionality and well-accessible pores. Moreover, owing to their regular micro-cube shape, they allow for a good packing of a fixed-bed flow reactor along with high column efficiency and a minimized pressure drop throughout the packed reactor. Therefore, the composite is employed as heterogeneous catalyst in the selective hydrogenation of 5-hydroxymethylfurfural to 2,5-dimethylfuran showing good catalytic performance and overcoming the conventional problem of column blocking. Thinking about the rational design of 3D carbon geometries, the functions and properties of the resulting carbon-based materials can be further expanded by the rational introduction of heteroatoms (e.g. N, B, S, P, etc.) into the carbon structures in order to alter properties such as wettability, surface polarity as well as the electrochemical landscape. In this context, the use of crystalline materials based on oxocarbon-metal ion complexes can open a platform of highly functional materials for all processes that involve surface processes. N2 - Nanoporöse Kohlenstoffmaterialien zeichnen sich u. a. durch ihre außergewöhnlichen Eigenschaften aus wie z. B. hohe Oberfläche, hohes Porenvolumen, hohe elektrische Leitfähigkeit und auch hohe chemische und thermische Stabilität. Aufgrund dessen finden sie Anwendung in den unterschiedlichsten Bereichen von der Speicherung elektrischer Energie bis hin zur Katalyse und Gasspeicherung. Die klassische Synthese von porösen Kohlenstoffmaterialien basiert u. a. auf der Nutzung von sogenannten anorganischen bzw. organischen Templaten und/oder chemischen Aktivierungsagenzien. Allerdings gelten diese Methoden eher als kompliziert, kostspielig und umweltschädlich. Außerdem wird eine gezielte Kontrolle der Produkteigenschaften durch die zahlreichen Prozesse erschwert, die sich bei den hohen Karbonisierungstemperaturen abspielen und folglich die Materialeigenschaften unvorhersehbar verändern können. In der vorliegenden Arbeit wird ein alternatives Konzept für die Synthese von nanoporösen Kohlenstoffmaterialien mit gezielt einstellbaren Eigenschaften vorgestellt. Diese basiert auf der Nutzung von kristallinen Vorläufermaterialien, die aus der Koordination von den Anionen der Quadratsäure bzw. der Krokonsäure mit verschiedenen Metallionen (Zn2+, Cu2+, Ni2+ und Co2+) resultieren. Diese haben den Vorteil, dass Eigenschaften wie z. B. die Partikelmorphologie und Porosität gezielt durch die Wahl geeigneter Syntheseparameter (z. B. Temperatur, molares Verhältnis, Metallion und Ligand) eingestellt werden können. Beispielsweise führen Koordinationskomplexe von der Quadratsäure mit Zn2+ in Wasser zu porösen 3D würfelförmigen Mikrokristallen, die durch einfache thermische Behandlung unter Schutzgasatmosphäre zu den entsprechenden Kompositen umgewandelt werden. Ein anschließender Waschschritt führt zu den entsprechenden Kohlenstoffmaterialien unter Erhalt der makroskopischen Struktur der kristallinen Vorläufermaterialien. In diesem Zusammenhang weisen die resultierenden Kohlenstoffe ebenfalls eine 3D Würfelform mit einer hierarchischen Porenstruktur bestehend aus vernetzten Mikro-, Meso- und Makroporen auf. Ferner besitzen die Kohlenstoffe hohe Oberflächen und Porenvolumen von bis zu 1.957 m2 g-1 bzw. 2,31 cm3 g-1. Um die Vorteile dieser Eigenschaften zu demonstrieren, werden sie als Elektrodenmaterial für Superkondensatoren getestet und zeigen dabei vielversprechende Kapazitäten. Außerdem, werden sie auch als Trägermaterial für die Immobilisierung von Nickel-Nanopartikel verwendet und als heterogene Katalysatoren in der selektiven Hydrierung von 5-hydroxymethylfurfural zu 2,5-dimethylfuran in einem Festbettreaktor eingesetzt. Dabei wird eine gute Katalysatorleistung (Produktivität) bei minimalem Druckabfall in der Reaktorsäule erreicht. KW - squaric acid KW - Quadratsäure KW - mesocrystals KW - Mesokristalle KW - nanoporöser Kohlenstoffpartikel KW - nanoporous carbon particles KW - Nanopartikel KW - nanoparticles KW - Koordinationskomplexe KW - coordination complexes KW - oxocarbon KW - Oxo-Kohlenstoff Y1 - 2017 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-407866 ER - TY - THES A1 - Wohlgemuth, Stephanie-Angelika T1 - Functional nanostructured hydrothermal carbons for sustainable technologies : heteroatom doping and superheated vapor T1 - Funktionelle, Nanostrukturierte Hydrothermal-Kohlenstoffe für Nachhaltige Technnologien: Heteroatom-Dotierung und Überkritischer Dampf N2 - The underlying motivation for the work carried out for this thesis was the growing need for more sustainable technologies. The aim was to synthesize a “palette” of functional nanomaterials using the established technique of hydrothermal carbonization (HTC). The incredible diversity of HTC was demonstrated together with small but steady advances in how HTC can be manipulated to tailor material properties for specific applications. Two main strategies were used to modify the materials obtained by HTC of glucose, a model precursor representing biomass. The first approach was the introduction of heteroatoms, or “doping” of the carbon framework. Sulfur was for the first time introduced as a dopant in hydrothermal carbon. The synthesis of sulfur and sulfur/nitrogen doped microspheres was presented whereby it was shown that the binding state of sulfur could be influenced by varying the type of sulfur source. Pyrolysis may additionally be used to tune the heteroatom binding states which move to more stable motifs with increasing pyrolysis temperature. Importantly, the presence of aromatic binding states in the as synthesized hydrothermal carbon allows for higher heteroatom retention levels after pyrolysis and hence more efficient use of dopant sources. In this regard, HTC may be considered as an “intermediate” step in the formation of conductive heteroatom doped carbon. To assess the novel hydrothermal carbons in terms of their potential for electrochemical applications, materials with defined nano-architectures and high surface areas were synthesized via templated, as well as template-free routes. Sulfur and/or nitrogen doped carbon hollow spheres (CHS) were synthesized using a polystyrene hard templating approach and doped carbon aerogels (CA) were synthesized using either the albumin directed or borax-mediated hydrothermal carbonization of glucose. Electrochemical testing showed that S/N dual doped CHS and aerogels derived via the albumin approach exhibited superior catalytic performance compared to solely nitrogen or sulfur doped counterparts in the oxygen reduction reaction (ORR) relevant to fuel cells. Using the borax mediated aerogel formation, nitrogen content and surface area could be tuned and a carbon aerogel was engineered to maximize electrochemical performance. The obtained sample exhibited drastically improved current densities compared to a platinum catalyst (but lower onset potential), as well as excellent long term stability. In the second approach HTC was carried out at elevated temperatures (550 °C) and pressure (50 bar), corresponding to the superheated vapor regime (htHTC). It was demonstrated that the carbon materials obtained via htHTC are distinct from those obtained via ltHTC and subsequent pyrolysis at 550 °C. No difference in htHTC-derived material properties could be observed between pentoses and hexoses. The material obtained from a polysaccharide exhibited a slightly lower degree of carbonization but was otherwise similar to the monosaccharide derived samples. It was shown that in addition to thermally induced carbonization at 550 °C, the SHV environment exhibits a catalytic effect on the carbonization process. The resulting materials are chemically inert (i.e. they contain a negligible amount of reactive functional groups) and possess low surface area and electronic conductivity which distinguishes them from carbon obtained from pyrolysis. Compared to the materials presented in the previous chapters on chemical modifications of hydrothermal carbon, this makes them ill-suited candidates for electronic applications like lithium ion batteries or electrocatalysts. However, htHTC derived materials could be interesting for applications that require chemical inertness but do not require specific electronic properties. The final section of this thesis therefore revisited the latex hard templating approach to synthesize carbon hollow spheres using htHTC. However, by using htHTC it was possible to carry out template removal in situ because the second heating step at 550 °C was above the polystyrene latex decomposition temperature. Preliminary tests showed that the CHS could be dispersed in an aqueous polystyrene latex without monomer penetrating into the hollow sphere voids. This leaves the stagnant air inside the CHS intact which in turn is promising for their application in heat and sound insulating coatings. Overall the work carried out in this thesis represents a noteworthy development in demonstrating the great potential of sustainable carbon materials. N2 - Das Ziel der vorgelegten Arbeit war es, mit Hilfe der Hydrothermalen Carbonisierung (HTC) eine Palette an verschiedenen Materialien herzustellen, deren physikalische und chemische Eigenschaften auf spezifische Anwendungen zugeschnitten werden können. Die Motivation hierfür stellt die Notwendigkeit, Alternativen zu Materialien zu finden, die auf fossilen Brennstoffen basieren. Dabei stellen vor allem nachhaltige Energien eine der größten Herausforderungen der Zukunft dar. HTC ist ein mildes, nachhaltiges Syntheseverfahren welches prinzipiell die Nutzung von biologischen Rohstoffen (z. B. landwirtschaftlichen Abfallprodukten) für die Herstellung von wertvollen, Kohlenstoff-basierten Materialien erlaubt. Es wurden zwei verschiedene Ansätze verwendet, um hydrothermalen Kohlenstoff zu modifizieren. Zum einen wurde HTC unter „normalen“ Bedingungen ausgeführt, d. h. bei 180 °C und einem Druck von etwa 10 bar. Der Zucker Glukose diente in allen Fällen als Kohlenstoff Vorläufer. Durch Zugabe von stickstoff und /oder schwefelhaltigen Additiven konnte dotierte Hydrothermalkohle hergestellt werden. Dotierte Kohlenstoffe sind bereits für ihre positiven Eigenschaften, wie verbesserte Leitfähigkeit oder erhöhte Stabilität, bekannt. Zusätzlich zu Stickstoff dotierter Hydrothermalkohle, die bereits von anderen Gruppen hergestellt werden konnte, wurde in dieser Arbeit zum ersten Mal Schwefel in Hydrothermalkohle eingebaut. Außerdem wurden verschiedene Ansätze verwendet, um Oberfläche und definierte Morphologie der dotierten Materialien zu erzeugen, welche wichtig für elektrochemische Anwendungen sind. Schwefel- und/oder stickstoffdotierte Kohlenstoff Nanohohlkugeln sowie Kohlenstoff Aerogele konnten hergestellt werden. Mit Hilfe von einem zusätzlichen Pyrolyseschritt (d. h. Erhitzen unter Schutzgas) konnte die Leitfähigkeit der Materialien hergestellt werden, die daraufhin als Nichtmetall-Katalysatoren für Wasserstoff-Brennstoffzellen getestet wurden. Im zweiten Ansatz wurde HTC unter extremen Bedingungen ausgeführt, d. h. bei 550 °C und einem Druck von ca. 50 bar, welches im Wasser Phasendiagram dem Bereich des Heißdampfes entspricht. Es konnte gezeigt werden, dass die so erhaltene Hydrothermalkohle ungewöhnliche Eigenschaften besitzt. So hat die Hochtemperatur-Hydrothermalkohle zwar einen hohen Kohlenstoffgehalt (mehr als 90 Massenprozent), enthält aber auch viele Wasserstoffatome und ist dadurch schlecht leitfähig. Da damit elektrochemische Anwendungen so gut wie ausgeschlossen sind, wurde die Hochtemperatur-Hydrothermalkohle für Anwendungen vorgesehen, welche chemische Stabilität aber keine Leitfähigkeit voraussetzen. So wurden beispielsweise Hochtemperatur-Kohlenstoff-Nanohohlkugeln synthetisiert, die großes Potential als schall- und wärmeisolierende Additive für Beschichtungen darstellen. Insgesamt konnten erfolgreich verschiedenste Materialien mit Hilfe von HTC hergestellt werden. Es ist zu erwarten, dass sie in Zukunft zu nachhaltigen Technologien und damit zu einem weiteren Schritt weg von fossilen Brennstoffen beitragen werden. KW - Hydrothermale Karbonisierung KW - Heteroatom-Dotierung KW - Aerogele KW - Hohlkugeln KW - Elektrokatalyse KW - Hydrothermal Carbonization KW - Heteroatom Doping KW - Aerogels KW - Hollow Spheres KW - Electrocatalysis Y1 - 2012 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-60120 ER - TY - THES A1 - Perovic, Milena T1 - Functionalization of nanoporous carbon materials for chiral separation and heterogeneous oxidation catalysis N2 - The impact that catalysis has on global economy and environment is substantial, since 85% of all chemical industrial processes are catalytic. Among those, 80% of the processes are heterogeneously catalyzed, 17% make use of homogeneous catalysts, and 3% are biocatalytic processes. Especially in the pharmaceutical and agrochemical industry, a significant part of these processes involves chiral compounds. Obtaining enantiomerically pure compounds is necessary and it is usually accomplished by asymmetric synthesis and catalysis, as well as chiral separation. The efficiency of these processes may be vastly improved if the chiral selectors are positioned on a porous solid support, thereby increasing the available surface area for chiral recognition. Similarly, the majority of commercial catalysts are also supported, usually comprising of metal nanoparticles (NPs) dispersed on highly porous oxide or nanoporous carbon material. Materials that have exceptional thermal and chemical stability, and are electrically conductive are porous carbons. Their stability in extreme pH regions and temperatures, the possibility to tailor their pore architecture and chemical functionalization, and their electric conductivity have already established these materials in the fields of separation and catalysis. However, their heterogeneous chemical structure with abundant defects make it challenging to develop reliable models for the investigation of structure-performance relationships. Therefore, there is a necessity for expanding the fundamental understanding of these robust materials under experimental conditions to allow for their further optimization for particular applications. This thesis gives a contribution to our knowledge about carbons, through different aspects, and in different applications. On the one hand, a rather exotic novel application was investigated by attempts in synthesizing porous carbon materials with an enantioselective surface. Chapter 4.1 described an approach for obtaining mesoporous carbons with an enantioselective surface by direct carbonization of a chiral precursor. Two enantiomers of chiral ionic liquids (CIL) based on amino acid tyrosine were used as carbon precursors and ordered mesoporous silica SBA-15 served as a hard template for obtaining porosity. The chiral recognition of the prepared carbons has been tested in the solution by isothermal titration calorimetry with enantiomers of Phenylalanine as probes, as well as chiral vapor adsorption with 2-butanol enantiomers. Measurements in both solution and the gas phase revealed the differences in the affinity of carbons towards two enantiomers. The atomic efficiency of the CIL precursors was increased in Chapter 4.2, and the porosity was developed independently from the development of chiral carbons, through the formation of stable composites of pristine carbon and CIL-derived coating. After the same set of experiments for the investigation of chirality, the enantiomeric ratios of the composites reported herein were even higher than in the previous chapter. On the other hand, the structure‒activity relationship of carbons as supports for gold nanoparticles in a rather traditional catalytic model reaction, on the interface between gas, liquid, and solid, was studied. In Chapter 5.1 it was shown on the series of catalysts with different porosities that the kinetics of ᴅ-glucose oxidation reaction can be enhanced by increasing the local concentration of the reactants around the active phase of the catalyst. A large amount of uniform narrow mesopores connected to the surface of the Au catalyst supported on ordered mesoporous carbon led to the water confinement, which increased the solubility of the oxygen in the proximity of the catalyst and thereby increased the apparent catalytic activity of this catalyst. After increasing the oxygen concentration in the internal area of the catalyst, in Chapter 5.2 the concentration of oxygen was increased in the external environment of the catalyst, by the introduction of less cohesive liquids that serve as efficient solvent for oxygen, perfluorinated compounds, near the active phase of the catalyst. This was achieved by a formation of catalyst particle-stabilized emulsions of perfluorocarbon in aqueous ᴅ-glucose solution, that further promoted the catalytic activity of gold-on-carbon catalyst. The findings reported within this thesis are an important step in the understanding of the structure-related properties of carbon materials. N2 - Die Auswirkungen, die die Katalyse auf die globale Wirtschaft und Umwelt hat, sind beträchtlich, da 85% aller chemischen Industrieprozesse katalytisch sind. Vor allem in der pharmazeutischen und agrochemischen Industrie ist ein bedeutender Teil dieser Prozesse mit chiralen Verbindungen verbunden, Moleküle, die als Bild und Spiegelbild dargestellt werden können. Es ist notwendig, chiral reine Verbindungen zu erhalten, und die Prozesse, um dies zu erreichen, sind effizienter, wenn poröse chirale Materialien aufgrund ihrer größeren Oberfläche verwendet werden. In ähnlicher Weise besteht die Mehrzahl der kommerziellen Katalysatoren in der Regel aus Metallnanopartikeln, die auf hochporösem Oxid- oder nanoporösem Kohlenstoffmaterial dispergiert sind. Materialien, die eine außergewöhnliche thermische und chemische Stabilität aufweisen und elektrisch leitfähig sind, sind poröse Kohlenstoffe. Ihre Anwendung ist jedoch aufgrund ihrer heterogenen, defektreichen Struktur sehr anspruchsvoll. Daher besteht die Notwendigkeit, das grundlegende Verständnis dieser Materialien unter experimentellen Bedingungen zu erweitern, um ihre weitere Optimierung für bestimmte Anwendungen zu ermöglichen. Diese Arbeit leistet einen Beitrag zu unserem Wissen über Kohlenstoffe durch eine eher exotische neue Anwendung der chiralen Trennung und eine eher traditionelle katalytische Anwendung. In Kapitel 4 wurden zwei Ansätze zur Gewinnung nanoporöser Kohlenstoffe mit chiraler Oberfläche unter Verwendung chiraler ionischer Flüssigkeitsvorläufer beschrieben. Ihre chirale Erkennung wurde in der Lösung und in der Gasphase untersucht. Kapitel 5 konzentrierte sich auf die Struktur-Aktivitäts-Beziehung von Kohlenstoffmaterialien als Träger von Goldnanopartikeln in einer katalytischen Modellreaktion der Glukoseoxidation mit molekularem Sauerstoff. Die in dieser Arbeit berichteten Ergebnisse sind ein wichtiger Schritt zum Verständnis der strukturbezogenen Eigenschaften von Kohlenstoffmaterialien. T2 - Funktionalisierung von nanoporösen Kohlenstoffmaterialien für die chirale Trennung und heterogene Oxidationskatalyse KW - Porous carbon KW - heterogeneous catalysis KW - chiral separation KW - functionalization KW - glucose oxidation KW - poröse Kohlenstoffmaterialien KW - chirale Trennung KW - Funktionalisierung KW - Glukose Oxidation KW - heterogene Katalyse Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-486594 ER - TY - THES A1 - Lama, Sandy M. G. T1 - Functionalization of Porous Carbon Materials with Heteroatoms and Application as Supports in Industrial Heterogeneous Catalysis T1 - Funktionalisierung von porösen Kohlenstoffmaterialien mit Heteroatomen und Anwendung als Träger in der industriellen heterogenen Katalyse N2 - Due to a challenging population growth and environmental changes, a need for new routes to provide required chemicals for human necessities arises. An effective solution discussed in this thesis is industrial heterogeneous catalysis. The development of an advanced industrial heterogeneous catalyst is investigated herein by considering porous carbon nano-material as supports and modifying their surface chemistry structure with heteroatoms. Such modifications showed a significant influence on the performance of the catalyst and provided a deeper insight regarding the interaction between the surface structure of the catalyst and the surrounding phase. This thesis contributes to the few present studies about heteroatoms effect on the catalyst performance and emphasizes on the importance of understanding surface structure functionalization in a catalyst in different phases (liquid and gaseous) and for different reactions (hydrogenolysis, oxidation, and hydrogenation/ polymerization). Herein, the heteroatoms utilized for the modifications are hydrogen (H), oxygen (O), and nitrogen (N). The heteroatoms effect on the metal particle size, on the polarity of the support/ the catalyst, on the catalytic performance (activity, selectivity, and stability), and on the interaction with the surrounding phase has been explored. First hierarchical porous carbon nanomaterials functionalized with heteroatoms (N) is synthesized and applied as supports for nickel nanoparticles for hydrogenolysis process of kraft lignin in liquid phase. This reaction has been performed in batch and flow reactors for three different catalysts, two of comparable hierarchical porosity, yet one is modified with N and the other is not, and a third is a prepared catalyst from a commercial carbon support. The reaction production and analyses show that the catalysts with hierarchical porosity perform catalytically much better than in presence of a commercial carbon support with lower surface area. Moreover, the modification with N-heteroatoms enhanced the catalytic performance because the heteroatom modified porous carbon material with nickel nanoparticles catalyst (Ni-NDC) performed highest among the other catalysts. In the flow reactor, Ni-NDC selectively degraded the ether bonds (β-O-4) in kraft lignin with an activity of 2.2 x10^-4 mg lignin mg Ni-1 s-1 for 50 h at 350°C and 3.5 mL min-1 flow, providing ~99 % conversion to shorter chained chemicals (mainly guaiacol derivatives). Then, the functionalization of carbon surface was further studied in selective oxidation of glucose to gluconic acid using < 1 wt. % of gold (Au) deposited on the previously-mentioned synthesized carbon (C) supports with different functionalities (Au-CGlucose, Au-CGlucose-H, Au-CGlucose-O, Au-CGlucoseamine). Except for Au-CGlucose-O, the other catalysts achieved full glucose conversion within 40-120 min and 100% selectivity towards gluconic acid with a maximum activity of 1.5 molGlucose molAu-1 s-1 in an aqueous phase at 45 °C and pH 9. Each heteroatom influenced the polarity of the carbon differently, affecting by that the deposition of Au on the support and thus the activity of the catalyst and its selectivity. The heteroatom effect was further investigated in a gas phase. The Fischer-Tropsch reaction was applied to convert synthetic gas (CO and H2) to short olefins and paraffins using surface-functionalized carbon nanotubes (CNTs) with heteroatoms as supports for ion (Fe) deposition in presence and absence of promoters (Na and S). The results showed the promoted Fe-CNT doped with nitrogen catalyst to be stable up to 180 h and selective to the formation of olefins (~ 47 %) and paraffins (~6 %) with a conversion of CO ~ 92 % at a maximum activity of 94 *10^-5 mol CO g Fe-1 s-1. The more information given regarding this topic can open wide range of applications not only in catalysis, but in other approaches as well. In conclusion, incorporation of heteroatoms can be the next approach for an advanced industrial heterogeneous catalyst, but also for other applications (e.g. electrocatalysis, gas adsorption, or supercapacitors). N2 - Herausforderungen wie Bevölkerungszuwachs und Umweltveränderungen erfordern neue Wege, chemische Substanzen zu erzeugen, um menschliche Anforderungen zu befriedigen. Eine mögliche effektive Lösung dafür, welche in dieser Arbeit diskutiert wird ist die industrielle heterogene Katalyse. Es werden unter dem Einsatz poröser Kohlenstoffträger neue industrielle Katalysatoren untersucht und entwickelt wobei die Oberflächenstruktur dieser Trägermaterialien mit Heteroatomen modifiziert wird. Diese Modifikationen zeigten einen signifikanten Einfluss auf die Eigenschaften der Katalysatoren und erlaubten Rückschlüsse hinsichtlich der Interaktion zwischen Katalysatoroberfläche und umgebender Phase. Die vorliegende Arbeit trägt zu einigen wenigen existierenden Studien bei die sich mit den Einflüssen solcher Heteroatome auf Katalysatoren beschäftigen. Es wird versucht, die Wichtigkeit dieser Oberflächeneigenschaften in Reaktionen (Hydrogenolyse, Oxidation, Hydrierung/ Polymerisation) in verschiedenen Phasen (flüssig oder gasförmig) zu verstehen. Die für die Modifikationen eingesetzten Heteroatome sind Wasserstoff (H), Sauerstoff (O) und Stickstoff (N). Ihr Effekt auf die Größe der Metallpartikel, die Polarität der Träger bzw. Katalysatoren, die eigentlichen katalytischen Eigenschaften und die Interaktion mit der umgebenden Phase wurde untersucht. Zuerst wurden hierarchisch poröse Kohlenstoffmaterialien hergestellt, die mit Stickstoff als Heteroatome funktionalisiert wurden. Diese wurden als Trägermaterialien für Nickel-Nanopartikel in der Hydrogenolyse von Kraft Lignin in flüssiger Phase eingesetzt. Diese Reaktion wurde mit drei unterschiedlichen Katalysatoren in Batch- und Flussreaktoren durchgeführt. Zwei der Katalysatoren hatten vergleichbare hierarchische Porosität. Einer davon war mit Heteroatomen funktionalisiert, einer dagegen nicht. Ein dritter Katalysator wurde mit einem kommerziell erhältlichen Kohlenstoffmaterial hergestellt. Die Reaktion zeigte, dass die Katalysatoren mit hierarchischer Porosität deutlich bessere Eigenschaften zeigen als das kommerzielle Trägermaterial mit geringerer Oberfläche. Darüber hinaus zeigte sich, dass die Modifizierung mit Stickstoffatomen die katalytischen Eigenschaften verbessert, da das modifizierte Kohlenstoffmaterial mit den Nickelpartikeln (Ni-NDC) die besten Ergebnisse aller untersuchten Katalysatoren zeigte. Im Durchflussreaktor wurden von Ni-NDC die Etherbindungen des Kraft Lignins (β-O-4) selektiv mit einer Aktivität von 2.2 x10^-4 mg lignin mg Ni-1 s-1 für 50 h bei 99% Umsatz zu kurzkettigeren Strukturen (hauptsächlich Guajakol-Derivat) gespalten. Außerdem wurde der Einfluss der Funktionalisierung der Kohlenstoffoberfläche in der selektiven Oxidation von Glucose zu Gluconsäure mit 1 Gew.% Gold (Au) auf den vorher angesprochenen Kohlenstoffträgermaterialien mit unterschiedlichen Oberflächenfunktionalitäten (Au-CGlucose, Au-CGlucose-H, Au-CGlucose-O, Au-CGlucoseamine) untersucht. Mit Ausnahme von Au-CGlucose-O erreichten alle Katalysatoren innerhalb von 40-120 min 100% Glucose Umsatz bei 100%iger Selektivität zu Gluconsäure und einer maximalen katalytischen Aktivität von 1.5 molGlucose molAu-1 s-1 in wässriger Phase bei 45°C und pH 9. Die unterschiedlichen Heteroatome wirkten sich unterschiedlich auf die Polarität der Kohlenstoffe und damit auch auf die Abscheidung der Goldpartikel auf die Trägermaterialien und die Katalysatoraktivität und -selektivität aus. Der Einfluss der Heteroatome wurde außerdem in einer Gasphasenreaktion untersucht. Die Fischer-Tropsch Reaktion kam zum Einsatz um Synthesegas (CO und H2) mit Hilfe von Katalysatoren bestehend aus Eisen (Fe) auf Heteroatomfunktionalisierten Kohlenstoffnanoröhrchen (engl. Carbon nanotubes, CNTs) in Gegenwart und Abwesenheit von Promotoren (Na und S) zu kurzkettigen Olefinen und Paraffinen umzuwandeln. Die Ergebnisse zeigten dass die Fe-CNT Katalysatoren mit Promotoren und stickstoffdotierten Trägern bis zu 180 h stabil waren und Olefine (~ 47 %) sowie Paraffine (~6 %) mit guten Selektivitäten bei einem CO Umsatz von 92% und einer maximalen Aktivität von 94 *10^-5 mol CO gFe-1 s-1 hergestellt werden konnten. Je mehr Informationen zu diesem Thema zur Verfügung gestellt werden, kann dies zu einer großen Bandbreite von Anwendungen nicht nur in der Katalyse, sondern auch in anderen Ansätzen beitragen. Zusammenfassend kann der Einbau von Heteroatomen der nächste Ansatz für einen fortgeschrittenen industriellen heterogenen Katalysator sein, aber auch für andere Anwendungen (z.B. Elektrokatalyse, Gasadsorption oder Superkondensatoren). KW - catalysis KW - carbon material KW - carbon supports KW - glucose oxidation KW - Kraft lignin hydrogenolysis KW - Fischer-Tropsch Synthesis KW - Syngas Hydrogenation KW - gold-carbon catalysts KW - nickel-carbon catalysts KW - iron-carbon nanotube catalysts KW - hierarchical porosity KW - heteroatom modification KW - catalyst functionalization KW - Katalyse KW - Kohlenstoffmaterial KW - Kohlenstoffträger KW - Glukoseoxidation KW - Kraftlignin KW - Hydrogenolyse KW - Fischer-Tropsch-Synthese KW - Syngashydrierung KW - Gold-Kohlenstoff-Katalysatoren KW - Nickel-Kohlenstoff-Katalysatoren KW - Eisen-Kohlenstoff-Nanoröhrchen-Katalysatoren KW - hierarchische Porosität KW - Heteroatom-Modifikation KW - Funktionalisierung von Katalysatoren Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-415797 ER - TY - THES A1 - Behrends, Nicole T1 - Funktionalisierte OS(T)K-Stäbe und Sensorfluorophore zur optischen Sensorik T1 - Functionalized OS(T)K-rods and dyes for optical sensor systems N2 - Im Rahmen dieser Arbeit wurden zum einen erste Oligospiro(thio)ketal (OS(T)K)-basierte Modellsysteme (molekulare Sonden) für abstandsabhängige Messungen mittels Förster-Resonanz-Energietransfer (FRET) und zum anderen Sensorfluorophore, basierend auf einem DBD-Fluorophor und BAPTA, zur Messung der intrazellulären Calcium-Konzentration dargestellt. Für die Synthese von molekularen Sonden für abstandsabhängige Messungen wurden verschiedenste einfach- und doppelt-markierte OS(T)K-Stäbe entwickelt und spektroskopisch untersucht. Die OS(T)K-Stäbe, sogenannte molekulare Stäbe, dienten als starre Abstandshalter zwischen den Fluorophoren. Als Fluorophore wurden Derivate von 6,7-Dihydroxy-4-methylcoumarin (Donor) und Acyl-DBD (Akzeptor) verwendet, die zusammen ein FRET-Paar bilden. Die Fluorophore wurden so funktionalisiert, dass sie sowohl unbeweglich bzw. „starr“, als auch beweglich bzw. „flexibel“ an den OS(T)K-Stab gebunden werden konnten. Für die Synthese der OS(T)K-Stäbe wurden ebenfalls eine Reihe an unterschiedlich langen und kurzen Stabbausteinen synthetisiert. Auf diese Weise wurden eine Vielzahl an verschiedensten einfach- und doppelt-markierten OS(T)K-Stäben dargestellt, deren Fluorophore sowohl „starr“ als auch „flexibel“ gebunden sind. Die dargestellten Stäbe wurden in verschiedensten Lösungsmitteln spektroskopisch untersucht, um anschließend das Verhalten in Vesikel, die eine biomimetische Umgebung darstellen, zu beurteilen. Es wurde festgestellt, dass sich die Stäbe erfolgreich in die Vesikelmembran einlagerten und hohe FRET-Effizienzen aufweisen. Des Weiteren wurde ein FRET-Paar dargestellt, das sich durch 2-Photonenabsorpion im NIR-Bereich anregen lässt. Es wurde in den lebenden Zellen mittels Fluoreszenzlebenszeitmikroskopie (FLIM) untersucht. Zur Untersuchung von intrazellulärem Calcium wurden zwei verschiedene DBD-Fluorophore über einen kurzen Linker mit dem Calcium-Chelator BAPTA verknüpft. Die dargestellten Fluorophore wurden sowohl in vitro als auch in vivo auf ihre Calcium-Sensitivität überprüft. Mittels FLIM wurden in lebenden Zellen die Fluoreszenzlebenszeitverteilungen der Fluorophore nach Calcium-Konzentrationsänderungen detektiert. N2 - In this work, Oligospiro(thio)ketal (OS(T)K)-based model systems (molecular probes) for distance-dependent measurements by Förster resonance energy transfer (FRET) and sensor dyes, based on [1,3]dioxolo[4,5-f][1,3]benzodioxole (DBD) dyes and BAPTA, for measuring the intracellular calcium concentration, were presented. For synthesis of molecular probes, for distance-dependent measurements, various single and double-labeled OS(T)K rods were developed and examined spectroscopically. The OS(T)K rods, called molecular rods, served as rigid spacers between the fluorophores. The FRET pairs consist of a Coumarin (Cou) dye as donor and a DBD dye as acceptor. Cou and DBD were functionalized in such a way that they could be connected both "rigid" as well as "flexible" to the OS(T)K rod. For synthesis of the OS(T)K rods, a number of different long and short rod units were synthesized. In this way, a variety of different single- and double-labeled OS(T)K rods were presented. The rods were spectroscopically analyzed in various solvents to subsequently evaluate the behavior in large unilamellar vesicles (LUVs) that represent a biomimetic system for cell membranes. It was found that the rods successfully incorporated in the vesicle membrane. Furthermore, a FRET pair was shown that can be excited by 2-photon absorption in the NIR region. It was examined in living cells by fluorescence lifetime microscopy (FLIM). To study intracellular calcium, two different DBD dyes were linked via a short linker to the calcium chelator BAPTA. The dyes were examined for their calcium sensitivity both in vitro and in vivo. Using FLIM, the fluorescence lifetime distributions of the dyes were detected in living cells after calcium concentration changes. KW - DBD KW - Coumarin KW - FRET KW - BAPTA KW - Calcium KW - 2P-FRET KW - OSK KW - OSTK KW - molekulare Stäbe KW - DBD KW - coumarin KW - FRET KW - BAPTA KW - calcium KW - 2P-FRET KW - OSK KW - OSTK KW - molecular rods Y1 - 2017 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-404213 ER - TY - THES A1 - Greß, Anja T1 - Funktionalisierte Poly(2-oxazoline) : kontrollierte Synthese, bioinspirierte Strukturbildung und Anwendungen T1 - Functionalized Poly(2-oxazolines) : controlled synthesis, bioinspired structure formation and applications N2 - Funktionalisierte Poly(2-oxazoline) als neue Materialien stellen sowohl unter strukturellen Gesichtspunkten als auch im Hinblick auf potentielle Anwendungen eine interessante Polymerklasse dar. Die Ausbildung von hierarchischen Strukturen mit Poly(2-oxazolinen) über intermolekulare Wasserstoffbrückenbindungen ist hierbei ein bisher nicht beachteter Aspekt. Über einen bioinspirierten Ansatz sollten gezielt funktionelle Gruppen, die für einen hierarchischen Aufbau, z.B. in Proteinen, verantwortlich sind, in vereinfachter Weise auf die synthetische Substanzklasse der Poly(2-oxazoline) übertragen werden. Die vorliegende Arbeit beschäftigt sich mit der modularen Synthese neuer, funktionalisierter Poly(2-oxazolin) Homo- und Copolymere. Ausgehend von der Synthese von 2-(3-Butenyl)-2-oxazolin wurden definierte Präpolymere in einer kationischen Isomerisierungspolymerisation unter kontrolliert/„lebenden“ Bedingungen hergestellt. In einer anschließenden „Thio-Click“ (Thiol-En-Reaktion) Modifizierungsreaktion wurden die gewünschten funktionellen Gruppen quantitativ eingeführt. Hydroxylierte Poly(2-oxazoline) wurden hinsichtlich ihres Aggregationsverhaltens in Wasser untersucht. Bereits die jeweiligen Homopolymere bildeten aufgrund von intermolekularen Wasserstoffbrückenbindungen supramolekulare tubuläre Nanofasern aus. Durch Einsatz verschiedener analytischer Methoden konnte die innere Struktur der Nanoröhren beschrieben und ein entsprechendes Modell aufgestellt werden. Die dargestellten funktionellen Poly(2-oxazoline) wurden hinsichtlich ihrer Anwendung als potentielle, synthetische „antifreeze additives“ untersucht. Alle Polymere besitzen eine ausgeprägte Tendenz zur Nukleierung von Wasser und führen daher zu signifikanten Änderungen der Eismorphologie. Des weiteren wurde ein carboxyliertes Derivat zur biomimetischen Mineralisation von Kalziumcarbonat eingesetzt und nach phänomenologischen Gesichtspunkten untersucht. N2 - Functionalized poly(2-oxazoline)s are a promising class of materials concerning their self-assembly behavior as well as for future applications. Hierarchical structure formation based on hydrogen bonding interactions has not been investigated yet. Applying a bioinspired approach, functional groups promoting hierarchical structure formation are introduced to poly(2-oxazoline)s. This work is focused on the modular synthesis of new functionalized poly(2-oxazoline) homo and copolymers. Starting from the synthesis of the new monomer 2-(3-butenyl)-2-oxazolin, well-defined precursor materials were prepared via cationic isomerization polymerization. Next, the polymers were quantitatively modified with the aimed functional groups using a “thio-click” (thiol-ene) reaction. The aggregation behaviour of hydroxylated poly(2-oxazolines) in water was investigated. Homo- as well as block copolymers can form supramolecular hollow nanofibers via intermolecular hydrogen bonding. Using a variety of different analytical methods, the structure of the nanotubes was determined and a formation model was proposed. Furthermore, the functionalized poly(2-oxazoline)s were investigated as synthetic mimics of natural anti-freeze additives. It was found, that these polymers show the tendency to nucleate water, thus influencing the morphology of ice. Finally, a carboxylated derivative was applied as an additive for the mineralization of calcium carbonate. KW - intermolekulare Wechselwirkungen KW - Poly(2-oxazoline) KW - Selbstorganisation KW - Thio-Click Modifizierung KW - Gefrierschutzadditiv KW - intermolecular interactions KW - poly(2-oxazolines) KW - self-assembly KW - Thio-click modification KW - antifreeze additive Y1 - 2008 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-18646 ER - TY - THES A1 - Walther, Sebastian T1 - Funktionalisierung von Ölsäuremethylester und Alkydharzen für die photoinduzierte radikalische Polymerisation im UV Bereich N2 - Die vorliegende Arbeit behandelt die Synthese und Charakterisierung von funktionalisierten Alkydharzen und die photoinduzierte Polymerisation dieser unter Einsatz einer Quecksilberdampflampe oder einer UV LED mit unterschiedlicher Lichtintensität. Der Fokus dieser Arbeit bestand in der gezielten Substitution der internalen Doppelbindungen der Fettsäureester durch reaktivere Gruppen, wie Acrylate oder Methacrylate, welche für Alkydharze in dieser Form so in der Literatur nicht beschrieben sind. Untersuchungen des Polymerisationsverhaltens dieser funktionalisierten Harze wurden mit der Photo DSC durchgeführt, wobei Bis – (4 – methoxybenzoyl) diethylgermanium als Photoinitiator diente. Die Ergebnisse haben gezeigt, dass die Harze radikalisch polymerisiert werden können und eine geringere Abhängigkeit von der Umgebungsatmosphäre (Luftsauerstoff bzw. Stickstoff) vorliegt. Dies ist so in der Literatur für funktionalisierte Alkydharze nicht bekannt. Abmischungen von unterschiedlichen Monomeren und funktionalisierten Harzen bewirkten eine Steigerung der Viskosität sowie eine Verringerung der Sauerstoffinhibierung im Zuge der photoinduzierten Polymerisation unter Luftsauerstoff für die Quecksilberdampflampe und der UV LED. Zur Untersuchung der sauerstoffinhibierenden Wirkung der Harze sind Synthesen unterschiedlicher, funktionalisierter Ölsäuremethylester als Modellsubstanzen durchgeführt worden. Ein verbessertes Polymerisationsverhalten und eine geringe Abhängigkeit von der Umgebungsatmosphäre konnte für die Modelle nachgewiesen werden. Zur Aufklärung des verbesserten Polymerisationsverhaltens sind gezielt Substituenten (Imidazol, Brom, Alkohol, Acetat) in den funktionalisierten Ölsäuremethylester eingebaut worden, um den Einfluss dieser aufzuzeigen. Im Rahmen dieser Synthesen sind neuartige Strukturen synthetisiert worden, welche so in der Literatur nicht beschrieben sind. Die Gegenüberstellung der Polymerisationszeit, der Umsatz der (Meth-)Acrylatgruppen sowie die Zeit zum Erreichen der maximalen Polymerisationsgeschwindigkeit unter Verwendung von unterschiedlichen UV Lichtquellen hat einen Einfluss der Substituenten auf das Polymerisationsverhalten gezeigt. N2 - The present work deals with the synthesis and characterization of functionalized alkyl resins and the photoinduced polymerization of them with different UV light sources. The focus of this work was the targeted substitution of the internal double bonds of fatty acid esters by more reactive groups such as acrylates or methacrylates, which are not described in the literature for alkyd resins in this form. Differences in the basic polymerizability of these functionalized resins were carried out with the Photo DSC, with Bis – (4 – methoxybenzoyl) diethylgermane serving as the photoinitiator. The results showed that the resins could be radically polymerized and also had a lower dependence on the ambient atmosphere. This is not described in the literature for functionalized alkyd resins. Blends of different monomers and the functionalized resins also showed that in addition to the increase in viscosity and the polymerizability of the monomers was improved under atmospheric oxygen. The reference used was methyl oleate, which had been functionalized via the same routes of synthesis and polymerized photochemically. In the context of these syntheses, novel monomers have been synthesized which are thus unknown in the literature.
The reference substances confirmed the behavior of the functionalized resins and showed improved polymerization behavior under atmospheric oxygen. To elucidate these properties, different functionalized methyl oleate have been synthesized to investigate the influence of the substituents on the polymerizability under atmospheric oxygen. In particular, the polymerization time, the conversion of the (meth) acrylate groups and the time to reach the maximum polymerization rate played a decisive role. T2 - Functionalization of methyl oleate and alkyd resins for the photoinduced radical polymerization in the UV region KW - UV KW - Alkydharze KW - Fettsäuren KW - Funktionalisierte Ölsäuremethylester KW - Polymerisation KW - Druckfarben KW - Alkyd resin KW - printing inks KW - fatty acids KW - functionalized methyl oleate KW - polymerization KW - UV Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-421467 ER - TY - THES A1 - Olejko, Lydia T1 - Förster resonance energy transfer (FRET)-based nanophotonics using DNA origami structures T1 - Förster-Resonanzenergietransfer (FRET) basierende Nanophotonik auf DNA Origami Strukturen N2 - The field of nanophotonics focuses on the interaction between electromagnetic radiation and matter on the nanometer scale. The elements of nanoscale photonic devices can transfer excitation energy non-radiatively from an excited donor molecule to an acceptor molecule by Förster resonance energy transfer (FRET). The efficiency of this energy transfer is highly dependent on the donor-acceptor distance. Hence, in these nanoscale photonic devices it is of high importance to have a good control over the spatial assembly of used fluorophores. Based on molecular self-assembly processes, various nanostructures can be produced. Here, DNA nanotechnology and especially the DNA origami technique are auspicious self-assembling methods. By using DNA origami nanostructures different fluorophores can be introduced with a high local control to create a variety of nanoscale photonic objects. The applications of such nanostructures range from photonic wires and logic gates for molecular computing to artificial light harvesting systems for artificial photosynthesis. In the present cumulative doctoral thesis, different FRET systems on DNA origami structures have been designed and thoroughly analyzed. Firstly, the formation of guanine (G) quadruplex structures from G rich DNA sequences has been studied based on a two-color FRET system (Fluorescein (FAM)/Cyanine3 (Cy3)). Here, the influences of different cations (Na+ and K+), of the DNA origami structure and of the DNA sequence on the G-quadruplex formation have been analyzed. In this study, an ion-selective K+ sensing scheme based on the G-quadruplex formation on DNA origami structures has been developed. Subsequently, the reversibility of the G-quadruplex formation on DNA origami structures has been evaluated. This has been done for the simple two-color FRET system which has then been advanced to a switchable photonic wire by introducing additional fluorophores (FAM/Cy3/Cyanine5 (Cy5)/IRDye®700). In the last part, the emission intensity of the acceptor molecule (Cy5) in a three-color FRET cascade has been tuned by arranging multiple donor (FAM) and transmitter (Cy3) molecules around the central acceptor molecule. In such artificial light harvesting systems, the excitation energy is absorbed by several donor and transmitter molecules followed by an energy transfer to the acceptor leading to a brighter Cy5 emission. Furthermore, the range of possible excitation wavelengths is extended by using several different fluorophores (FAM/Cy3/Cy5). In this part of the thesis, the light harvesting efficiency (antenna effect) and the FRET efficiency of different donor/transmitter/acceptor assemblies have been analyzed and the artificial light harvesting complex has been optimized in this respect. N2 - Nanotechnologie hat in den letzten Jahrzehnten durch die Herstellung von Materialien mit außergewöhnlichen Eigenschaften für Anwendungen im Bereich der Medizin und Materialwissenschaften immer mehr an Popularität gewonnen. Die Herstellungsmethoden von Nanostrukturen sind weit gefächert. Auch Desoxyribonukleinsäure (DNS bzw. engl. DNA, deoxyribonucleic acid) kann für die Herstellung von Strukturen im Nanometerbereich genutzt werden. Diese sogenannte DNA-Nanotechnologie wurde in den frühen 1980er Jahren von Nadrian C. Seeman begründet. Ungefähr 30 Jahre später wurde eine neue Methodik für die Herstellung von DNA-Nanostrukturen von Paul W. K. Rothemund entwickelt, die er „scaffold DNA origami“ (Gerüst-DNA-Origami) nannte. DNA-Origami-Nanostrukturen können relativ einfach hergestellt werden und eignen sich perfekt für die Anordnung unterschiedlicher Moleküle (zum Beispiel Fluorophore) mit hoher räumlicher Kontrolle und Präzision. Daher können sie als Substrate genutzt werden, um verschiedene Förster-Resonanzenergietransfer (FRET) Systeme zu entwerfen und zu untersuchen. FRET ist ein strahlungsloser Energietransfer, bei dem die Anregungsenergie von einem Donor- auf ein Akzeptor-Molekül übertragen wird. In dieser kumulativen Doktorarbeit wurden verschiedene FRET-Systeme auf DNA-Origami-Nanostrukturen entwickelt und mithilfe der Fluoreszenzspektroskopie untersucht. Hierbei wurde zuerst die durch einwertige Kationen (Kalium oder Natrium) induzierte Guanin-Quadruplex-Faltung von freier Telomer-DNA und Telomer-DNA auf DNA-Origami-Strukturen mittels FRET analysiert. Diese Untersuchungen haben gezeigt, dass die freie umgedrehte menschliche Telomer-Sequenz (RevHumTel, 5'-(GGG ATT)4) generell sensitiver auf K+ als auf Na+ reagiert. Durch die Immobilisierung der Telomer-DNA auf DNA-Origami-Strukturen kann eine vollständige Selektivität für K+ erreicht werden. Interessanterweise wird die Ionenselektivität aufgehoben, wenn die menschliche Telomer-Sequenz (HumTel, 5'-(TTA GGG)4) verwendet wird. Basierend auf der G-Quadruplex-Faltung konnten schaltbare FRET-Systeme entwickelt werden, da sich die G-Quadruplexe wieder entfalten, wenn die Kationen mithilfe von zum Beispiel Kryptanden entfernt werden. In den hier untersuchten FRET-Systemen konnte zwischen hoher FRET-Effizienz (gefalteter G-Quadruplex) und niedriger FRET-Effizienz (entfalteter DNA Einzelstrang) durch Zugabe KCl bzw. cryptand gewechselt werden. Da sich DNA-Origami-Strukturen recht einfach modifizieren lassen, wurde das ursprüngliche zwei-Farben-FRET-System durch Hinzufügen eines weiteren etwas rotverschobenen Farbstoffes erweitert (drei-Farben-FRET-Kaskade). Schließlich konnte ein schaltbarer photonischer Draht durch Einfügen eines vierten Farbstoffes entwickelt werden. Die Emissionsintensität des finalen Akzeptors ist in einer einfachen drei-Farben-FRET-Kaskade (ein Donor, ein Transmitter und ein Akzeptor) verhältnismäßig gering und kann durch das Anordnen von mehreren Donor- und Transmitter-Molekülen um ein zentrales Akzeptor-Molekül herum stark erhöht werden. In diesen sogenannten künstlichen Lichtsammelkomplexen absorbieren die Donor-Moleküle das Anregungslicht und übertragen dieses über mehrere FRET-Stufen zum Akzeptor-Molekül. Dadurch wird der Wellenlängenbereich der elektromagnetischen Strahlung, welcher vom Akzeptor absorbiert werden kann, vergrößert und die Emissionsintensität des Akzeptors verstärkt. In diesem Teil der Arbeit wurde die Anzahl der Farbstoffe und die Anordnung dieser unterschiedlichen Farbstoffe variiert und die Lichtsammeleffizienz und FRET-Effizienz bestimmt. Hierbei wurden diese Parameter optimiert und aufgrund der gefundenen Ergebnisse konnten Design-Regeln für solche künstlichen Lichtsammelkomplexe aufgestellt werden. KW - DNA origami KW - FRET KW - Förster resonance energy transfer KW - DNA Origami KW - FRET KW - Förster-Resonanzenergietransfer Y1 - 2017 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-396747 ER - TY - THES A1 - Feldbusch, Elvira T1 - Geochemische Charakterisierung eines Formationsfluids im Unteren Perm T1 - Geochemical characterization of a formation fluid of Lower Permian reservoir BT - Herkunft, betriebsbedingte Prozesse und Rolle organischer Verbindungen im geothermischen Kreislauf BT - origin, operational processes and role of organic compounds in the geothermal cycle N2 - Diese Arbeit befasst sich mit der ganzheitlichen Betrachtung der Fluideigenschaften eines unterpermischen Reservoirs am Geothermie Forschungsstandort Groß Schönebeck (GrSk) bei Reservoirbedingungen und im Betrieb der Geothermieanlage. Die Untersuchungen zur Fluidherkunft ergeben, dass es sich um ein konnates Wasser meteorischen Ursprungs ohne den Einfluss der darüberliegenden Zechsteinwässer handelt. Die Ionen und Isotopenverhältnisse im Formationswasser gelöster Komponenten in GrSk belegen einen gemeinsamen Genesepfad mit Wässern anderer Rotliegend-Reservoire des Nordostdeutschen Beckens (NEGB). Die Isotopenverhältnisse von ⁸⁷Sr/⁸⁶Sr ≈ 0,7158 und von δ³⁴SV CDT ≈ 4,1 ‰ des Sulfats weisen auf die Anreicherung des Fluids mit schweren Isotopen durch die Fluid Gestein-Wechselwirkung mit Vulkaniten und Rotliegend Sandsteinen des Unteren Perms hin. Das im Formationswasser bei Reservoirbedingungen gelöste Gas (Gas/Wasser ≤ 2 bei STP) enthält Stickstoff (δ¹⁵NAir ≈ 0,6 ‰) und thermogenes Methan (δ¹³CV-PDB ≈ - 18 ‰) aus organischen Karbonablagerungen (Kerogen Typ - III Kohlen) hoher Reife. Die Isotopenverhältnisse der Edelgase belegen eine krustale Herkunft des Gasgemisches. Die berechnete Verweilzeit τ (⁴He) der Gase im Reservoir liegt zwischen 275 und 317 Ma und überschreitet damit bei gegebener Konzentration von Mutternukliden im Reservoirgestein das allgemein angenommene Zeitalter der Sedimentgruppe. Das lässt sich durch eine Zuwanderung von Gasen aus älteren Sedimentfolgen erklären. Die Veränderungen der physikochemischen Fluidparameter während des Anlagenbetriebs sind hauptsächlich temperaturbedingt. Bei stabilen Produktionsbedingungen und einer Temperatur von ca. 100 °C stabilisieren sich auch die Fluideigenschaften. Bei In situ Bedingungen übertage beträgt die Dichte ρ = 1,1325 ± 0,0002 g ∙ mL⁻¹, das Redoxpotential Eh = -105,5 ± 1,3 mV und der pH = 6,61 ± 0,002. Die relative Zusammensetzung der Gasphase bei stabilen Produktionsbedingungen zeigt dagegen eine geringe Erhöhung des Stickstoffanteils sowie des Anteils der Kohlenwasserstoffe (Ethan, Propan, usw.) und Abnahme des relativen Methananteils im Laufe des Betriebs. Die quantitative Untersuchung der sekundären mineralischen Ausfällungen im Fluid mittels sequentieller Extraktion zeigte, dass Schwermetalle als eine Hauptkomponente der Fluidfestphase größtenteils in Verbindung mit organischen Molekülen vorliegen. Experimente zum Einfluss organischer Verbindungen unterschiedlicher Substanzklassen auf eine Mobilisierung der Schwermetalle aus dem Reservoirgestein ergaben, dass die Verbindungen wie Fettsäuren und PAK (polyzyklische aromatische Kohlenwasserstoffe) die Freisetzung von Kupfer, Nickel, Chrom und Blei verhindern bzw. zu derer Immobilisierung beitragen. Im Gegensatz dazu wird die Mobilität von Zink in Anwesenheit von diesen Verbindungen erhöht. Niedermolekulare Monocarbonsäuren und stickstoffhaltige Heteroaromaten tragen, mit Ausnahme von Blei, zur Freisetzung bzw. Mobilisierung von Schwermetallen aus dem Reservoirgestein bei. Die gewonnenen Erkenntnisse dieser Arbeit bestätigen das Risiko massiver Ausfällungen auf der kalten Seite der Geothermieanlage bei Inbetriebnahme des Kraftwerks, wenn keine an den Fluidchemismus angepassten Präventionsmethoden eingesetzt werden. Die Isotopenzusammensetzung der Fluidkomponenten sowie geringfügige Schwankungen der Gaszusammensetzung im kontinuierlichen Anlagenbetrieb lässt eine Kommunikation des unterpermischen Reservoirs mit dem darunter liegenden Oberkarbon vermuten, was eine nachträgliche Veränderung der Fluidzusammensetzung beim Dauerbetrieb der Anlage bedeuten kann. N2 - This work represents a holistic study of the properties of fluid from the Lower Permian reservoirs of the geothermal research site Gross Schönebeck at reservoir and at wellhead conditions during fluid circulation. Investigations of the fluid origin show that the formation water represents a connate water of meteoric origin without any evidence of influences from overlying Zechstein. The tracers of formation water as well as the isotopic signatures of relevant components reveal a common genesis path with waters of other Rotliegend reservoirs of the Northeast German Basin (NEGB). The isotope ratios of ⁸⁷Sr/⁸⁶Sr ≈ 0,7158 and sulphate δ³⁴SV-CDT ≈ 4,1 ‰ indicate strong water rock interaction with Lower Permian Rotliegend sandstones and volcanic rocks, resulting in an enrichment with 87Sr and 34S. The fluid dissolves about gas/water ≤ 2 (at STP) of formation gas at reservoir conditions. Major components are nitrogen (δ¹⁵NAir ≈ 0,6 ‰) and methane (δ¹³CV PDB ≈ - 18 ‰) of thermogenic origin from carboniferous organic matter with kerogen Type III coals of high maturity. The noble gases represent a gas mixture of crustal origin with a residence time τ (⁴He) in the reservoir of 275 - 317 Ma. This value exceeds commonly accepted age and parent radionuclide content of the stratigraphic group. This indicates migration of gases from older sediment layers. The changes of physico-chemical fluid properties above ground during plant operation are primarily temperature-affected. At steady operating conditions with a stable temperature of ~ 100 °C fluid properties stabilise with an in-situ density ρ = 1,1325 ± 0,0002 g ∙ mL⁻¹, redox potential Eh = -105,5 ± 1,3 mV and pH = 6,61 ± 0,002. The composition of formation gas at steady operating conditions shows a slight increase of nitrogen content and lower concentrated hydrocarbons (ethane, propane, etc.). Methane content decreases during fluid production, which could be an indicator for gas migration from different reservoir sections. A quantitative examination of secondary mineral precipitations in the fluid by means of sequential extractions indicates that heavy metals are largely bonded on the organic matter. Experiments on the impact different classes of organic components on the mobilisation of heavy metals from the reservoir rock demonstrated that the most heavy metals (Cu, Pb, Cr and Ni) can hardly be mobilized by fatty acids and polycyclic aromatic hydrocarbons or can be precipitated from the fluid. Zinc showed the opposite behaviour with these organic compounds. Organic components such as monocarboxylic acids and nitrogen heterocycles contribute to removing of heavy metals from the reservoir rock, with exception of lead. The findings of this work confirm the risk of considerable precipitation on the cold side of the geothermal plant during commissioning of the power station unless prevention methods adapted for the fluid chemistry are applied. The isotopic composition of fluid components as well as a minor fluctuation of gas composition during continuous plant operation indicates a potential communication of the Lower Permian reservoir with the underlying Upper Carboniferous formation. This may lead to a subsequent change of the fluid composition during a long-term operation of the plant in GrSk. KW - Groß Schönebeck KW - Rotliegend KW - Formationsfluid KW - Schwermetalle KW - Herkunft KW - geothermal KW - origin KW - formation fluid KW - heavy metals KW - onsite monitoring Y1 - 2015 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-87402 ER - TY - THES A1 - Strunk, David T1 - Gewinnung phenolischer Komponenten aus dem Birkenstamm als Rohstoffquelle für die Synthese eines neuen substituierten Phenylmethacrylats und dessen Polymerisation T1 - Extraction of phenolic components from the birch trunk as a source of raw material for the synthesis of a new substituted phenyl methacrylate and its polymerization N2 - In der vorliegenden Arbeit werden Wege zur Gewinnung verschiedener phenolischer Substanzen wie Lignin, Diarylheptanoide und 4-(3-Oxobutyl)phenol (Himbeerketon) aus dem Stamm der Hängebirke (Betula pendula) aufgezeigt. Durch Methacrylierung des 4-(3-Oxobutyl)phenols wurde ein Monomer erzeugt, welches mittels freier radikalischer Masse- und Lösungspolymerisation, sowie enzymatischer Polymerisation polymerisiert werden kann. Eine erste Isolierung von Bestandteilen wurde durch Extraktion von Innenholz bzw. Rinde mit Methanol erzielt. Die in Methanol unlöslichen Bestandteile des Innenholzes und der Rinde wurden anschließend mit ausgewählten ionischen Flüssigkeiten extrahiert. Es wurde ein Verfahren zum selektiven Trennen der mit diesen ionischen Flüssigkeiten extrahierten Bestandteile in Cellulose, Hemicellulose, Lignin und mit Ethylacetat extrahierbare Bestandteile entwickelt. Hierdurch war es möglich, sowohl die verwendeten ionischen Flüssigkeiten als auch das Innenholz und die Rinde hinsichtlich ihres Extraktionsverhaltens miteinander zu vergleichen. Ferner wurden verschiedene Strategien aufgezeigt, um insgesamt drei Spezies an Diarylheptanoiden aus dem methanolischen Extrakt der Rinde zu isolieren. Eines der gefundenen Diarylheptanoide (5 Hydroxy-1,7-bis(4-hydroxyphenyl)-3-heptanon) wurde via Retroaldolreaktion in 4 (3 Oxobutyl)phenol (Himbeerketon) und 3 (4 Hydroxyphenyl)propanal gespalten. Es wurde die Verwendung des 4-(3-Oxobutyl)phenol als Monomerbestandteil untersucht. Hierfür wurde 4-(3-Oxobutyl)phenylmethacrylat synthetisiert und Wege zur Reinigung mittels Säulenchromatographie und Umkristallisation aufgezeigt. Anschließend wurde Poly(4-(3-oxobutyl)phenylmethacrylat) (PObMA) und Polybenzylmethacrylats (PBzMA) aus Massen- und Lösungspolymerisation hergestellt. Die Ausbeuten an PObpMA im Vergleich zum PBzMA liegen bei gleichen Reaktionsbedingungen auf gleichem Niveau. Im Kontrast hierzu ist der Polymerisationsgrad aus freier radikalischer Polymerisation in Masse des PObpMA im Vergleich zum PBzMA um den Faktor 3,7 größer. Die Glasübergangstemperaturen des PObpMA liegen bei gleichen Reaktionsbedingungen sowohl bei freier radikalischer Polymerisation in Masse, als auch bei Lösungspolymerisation über denen des PBzMA. Darüber hinaus wurde die Polymerisation von 4-(3-Oxobutyl)phenylmethacrylat und Benzylmethacrylat mit einem Initiatorsystem bestehend aus Meerrettichperoxidase, Acetylaceton und Wasserstoffperoxid bei Raumtemperatur beschrieben. Die mit enzymatischem Initiatorsystem erzeugten Produkte zeigten starke Übereinstimmung mit Produkten aus Lösungspolymerisationen, welche mit Azobis(isobutyronitril) initiiert wurden. N2 - In the present work ways of obtaining various phenolic substances such as lignin, diarylheptanoids and 4-(3-oxobutyl)-phenol (raspberry ketone) from the trunk of the silver birch (Betula pendula) are shown. By methacrylating of 4-(3-oxobutyl)-phenol, a monomer was generated which can be polymerized by free radical mass and solution polymerization, as well as by enzymatic polymerization. A first separation of constituents was achieved by extraction of wood or bark with methanol. The methanol-insoluble components of the interior wood and the bark were then extracted with selected ionic liquids. A process has been developed for selectively separating the ingredients extracted with these ionic liquids into cellulose, hemicellulose, lignin and ethyl acetate extractables. This made it possible to compare both the ionic liquids used as well as the interior wood and the bark with respect to their extraction behavior with each other. Furthermore, different strategies were shown to isolate a total of three species of diarylheptanoids from the methanolic extract of the bark. One of the found diarylheptanoids (5-hydroxy-1,7-bis-(4-hydroxyphenyl)-3-heptanone) was cleaved by retroaldolysis in 4-(3-oxobutyl)-phenol (raspberry ketone) and 3-(4-hydroxyphenyl)-propanal. The use of 4- (3-oxobutyl) phenol as a monomer component was investigated. For this purpose, 4-(3-oxobutyl)-phenyl methacrylate was synthesized and ways of purification by column chromatography and recrystallization were shown. Subsequently, poly-(4-(3-oxobutyl)-phenyl methacrylate) (PObMA) and polybenzyl methacrylate (PBzMA) were prepared by mass and solution polymerization. The yields of PObpMA compared to PBzMA are at the same level when the same reaction conditions were used. In contrast, the degree of polymerization by free radical polymerization in mass of PObpMA compared to PBzMA is greater by a factor of 3.7. The glass transition temperatures of the PObpMA are both in free radical polymerization in bulk, as well as in solution polymerization over those of PbzMA when the same reaction conditions were used. Moreover, the polymerization of 4-(3-oxobutyl)-phenyl methacrylate and benzyl methacrylate at room temperature with an initiator system consisting of horseradish peroxidase, acetylacetone and hydrogen peroxide has been described. Products produced with enzymatic initiator system showed strong similarity with products from solution polymerizations initiated with Azobis(isobutyronitrile). KW - Birke KW - Rinde KW - Ionische Flüssigkeit KW - birch KW - bark KW - ionic liquiod KW - Diarylheptanoide KW - Himbeerketon KW - raspberry ketone Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-409228 ER - TY - THES A1 - Chea, Sany T1 - Glycomaterials: From synthesis of glycoconjugates to potential biomedical applications T1 - Glykomaterialien: Von der Synthese von Glykokonjugaten zu potenziellen biomedizinischen Anwendungen N2 - The importance of carbohydrate structures is enormous due to their ubiquitousness in our lives. The development of so-called glycomaterials is the result of this tremendous significance. These are not exclusively used for research into fundamental biological processes, but also, among other things, as inhibitors of pathogens or as drug delivery systems. This work describes the development of glycomaterials involving the synthesis of glycoderivatives, -monomers and -polymers. Glycosylamines were synthesized as precursors in a single synthesis step under microwave irradiation to significantly shorten the usual reaction time. Derivatization at the anomeric position was carried out according to the methods developed by Kochetkov and Likhorshetov, which do not require the introduction of protecting groups. Aminated saccharide structures formed the basis for the synthesis of glycomonomers in β-configuration by methacrylation. In order to obtain α-Man-based monomers for interactions with certain α-Man-binding lectins, a monomer synthesis by Staudinger ligation was developed in this work, which also does not require protective groups. Modification of the primary hydroxyl group of a saccharide was accomplished by enzyme-catalyzed synthesis. Ribose-containing cytidine was transesterified using the lipase Novozym 435 and microwave irradiation. The resulting monomer synthesis was optimized by varying the reaction partners. To create an amide bond instead of an ester bond, protected cytidine was modified by oxidation followed by amide coupling to form the monomer. This synthetic route was also used to isolate the monomer from its counterpart guanosine. After obtaining the nucleoside-based monomers, they were block copolymerized using the RAFT method. Pre-synthesized pHPMA served as macroCTA to yield cytidine- or guanosine-containing block copolymer. These isolated block copolymers were then investigated for their self-assembly behavior using UV-Vis, DLS and SEM to serve as a potential thermoresponsive drug delivery system. N2 - Die Bedeutung von Kohlenhydratstrukturen ist immens, da sie in unserem Leben allgegenwärtig sind. Die Entwicklung sogenannter Glykomaterialien ist das Ergebnis dieser großen Bedeutung. Diese werden nicht nur zur Erforschung grundlegender biologischer Prozesse eingesetzt, sondern unter anderem auch als Hemmstoffe für Krankheitserreger oder als Wirkstofftransportsysteme. Die vorliegende Arbeit beschreibt die Entwicklung von Glycomaterialien durch die Synthese von Glycoderivaten, -monomeren und -polymeren. Glycosylamine wurden als Vorstufen in einem einzigen Syntheseschritt unter Mikrowellenbestrahlung synthetisiert, um die übliche Reaktionszeit deutlich zu verkürzen. Die Derivatisierung an der anomeren Position wurde nach den von Kochetkov und Likhorshetov entwickelten Methoden durchgeführt, die keine Einführung von Schutzgruppen erfordern. Die aminierten Saccharidstrukturen bildeten die Grundlage für die Synthese von Glycomonomeren in β-Konfiguration durch Methacrylierung. Um α-Man-basierte Monomere für Interaktionen mit bestimmten α-Man-bindenden Lektinen zu erhalten, wurde in dieser Arbeit eine Monomersynthese durch Staudinger-Ligation entwickelt, die ebenfalls keine Schutzgruppen erfordert. Die Modifizierung der primären Hydroxylgruppe eines Saccharids wurde durch enzymkatalysierte Synthese erreicht. Ribosehaltiges Cytidin wurde mit Hilfe der Lipase Novozym 435 und Mikrowellenbestrahlung umgeestert. Die resultierende Monomersynthese wurde durch Variation der Reaktionspartner optimiert. Um eine Amidbindung anstelle einer Esterbindung zu erzeugen, wurde geschütztes Cytidin durch Oxidation und anschließende Amidkupplung modifiziert, um das Monomer zu bilden. Dieser Syntheseweg wurde auch zur Isolierung des Monomers aus seinem Gegenstück Guanosin verwendet. Nach der Gewinnung der nukleosidbasierten Monomere wurden diese mit Hilfe der RAFT-Methode blockcopolymerisiert. Vorsynthetisiertes pHPMA diente als MakroCTA, um Cytidin- oder Guanosin-haltige Blockcopolymere zu erhalten. Diese isolierten Blockcopolymere wurden dann mit UV-Vis, DLS und SEM auf ihr Selbstorganisationsverhalten untersucht, um als potenzielles thermoresponsives Drug-Delivery-System zu dienen. KW - polymer chemistry KW - glyco chemistry KW - glycomonomer KW - glycopolymer KW - lectin KW - drug delivery KW - thermoresponsive KW - glycoconjugate KW - Glykochemie KW - Glykokonjugat KW - Glykomonomer KW - Glykopolymer KW - Lektin KW - Polymerchemie KW - thermoresponsiv KW - Drug Delivery Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-574240 ER - TY - THES A1 - Heck, Christian T1 - Gold and silver nanolenses self-assembled by DNA origami T1 - Gold- und Silbernanolinsen, selbstassembliert durch DNA-Origami N2 - Nanolenses are linear chains of differently-sized metal nanoparticles, which can theoretically provide extremely high field enhancements. The complex structure renders their synthesis challenging and has hampered closer analyses so far. Here, the technique of DNA origami was used to self-assemble DNA-coated 10 nm, 20 nm, and 60 nm gold or silver nanoparticles into gold or silver nanolenses. Three different geometrical arrangements of gold nanolenses were assembled, and for each of the three, sets of single gold nanolenses were investigated in detail by atomic force microscopy, scanning electron microscopy, dark-field scattering and Raman spectroscopy. The surface-enhanced Raman scattering (SERS) capabilities of the single nanolenses were assessed by labelling the 10 nm gold nanoparticle selectively with dye molecules. The experimental data was complemented by finite-difference time-domain simulations. For those gold nanolenses which showed the strongest field enhancement, SERS signals from the two different internal gaps were compared by selectively placing probe dyes on the 20 nm or 60 nm gold particles. The highest enhancement was found for the gap between the 20 nm and 10 nm nanoparticle, which is indicative of a cascaded field enhancement. The protein streptavidin was labelled with alkyne groups and served as a biological model analyte, bound between the 20 nm and 10 nm particle of silver nanolenses. Thereby, a SERS signal from a single streptavidin could be detected. Background peaks observed in SERS measurements on single silver nanolenses could be attributed to amorphous carbon. It was shown that the amorphous carbon is generated in situ. N2 - Nanolinsen sind Strukturen aus linear angeordneten, unterschiedlich großen metallischen Nanopartikeln. Elektromagnetische Felder können durch sie theoretisch extrem verstärkt werden, aufgrund ihres komplexen Aufbaus sind sie bislang aber wenig erforscht. Im Rahmen dieser Dissertation wurden Nanolinsen mit Hilfe der DNA-Origami-Technik aus DNA-beschichteten 10 nm-, 20 nm- und 60 nm-Gold- oder Silbernanopartikeln hergestellt. Für Goldnanolinsen sind die Partikel dabei in drei unterschiedlichen Geometrien angeordnet worden. Einzelne Goldnanolinsen wurden mittels Rasterkraftmikroskopie, Rasterelektronenmikroskopie, Dunkelfeld- und Ramanspektroskopie untersucht. Um die Raman-Verstärkung quantifizieren zu können, trugen dabei jeweils die 10 nm-Goldpartikel Farbstoffmoleküle in ihrer Beschichtung. Die Interpretation der Messdaten wurde durch numerische Simulationen unterstützt. Nanolinsen zeichnen sich durch eine stufenweise Feldverstärkung aus. Dieser Effekt konnte experimentell bestätigt werden, indem selektiv die 20 nm- oder 60 nm-Partikel von Goldnanolinsen mit Farbstoffen markiert und die resultierenden Raman-Signale verglichen wurden. Ein mit Alkingruppen markiertes Protein ist ortsselektiv in Silbernanolinsen integriert worden. Es war möglich, das für das Alkin charakteristische oberflächenverstärkte Raman-Signal im Spektrum einer einzelnen Nanolinse und damit eines einzelnen Proteins zu beobachten. Bei den Messungen mit Silbernanolinsen sind für amorphe Kohlenstoffspezies charakterstische Hintergrundsignale beobachtet worden. Durch zeitabhängige Messungen konnte gezeigt werden, dass diese Spezies erst in situ gebildet werden. KW - DNA origami KW - gold nanoparticles KW - silver nanoparticles KW - SERS KW - self-assembly KW - plasmonics KW - nanolenses KW - DNA-Origami KW - Goldnanopartikel KW - Silbernanopartikel KW - SERS KW - Selbstassemblierung KW - Plasmonik KW - Nanolinsen Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-409002 ER - TY - THES A1 - Mathieu-Gaedke, Maria T1 - Grafting-to and grafting-from proteins - synthesis and characterization of protein-polymer conjugates on the way to biohybrid membrane materials T1 - Grafting-to und Grafting-from - Synthese und Charakterisierung von Protein-Polymer-Konjugaten auf dem Weg zu biohybriden Membranen N2 - The incorporation of proteins in artificial materials such as membranes offers great opportunities to avail oneself the miscellaneous qualities of proteins and enzymes perfected by nature over millions of years. One possibility to leverage proteins is the modification with artificial polymers. To obtain such protein-polymer conjugates, either a polymer can be grown from the protein surface (grafting-from) or a pre-synthesized polymer attached to the protein (grafting-to). Both techniques were used to synthesize conjugates of different proteins with thermo-responsive polymers in this thesis. First, conjugates were analyzed by protein NMR spectroscopy. Typical characterization techniques for conjugates can verify the successful conjugation and give hints on the secondary structure of the protein. However, the 3-dimensional structure, being highly important for the protein function, cannot be probed by standard techniques. NMR spectroscopy is a unique method allowing to follow even small alterations in the protein structure. A mutant of the carbohydrate binding module 3b (CBM3bN126W) was used as model protein and functionalized with poly(N-isopropylacrylamide). Analysis of conjugates prepared by grafting-to or grafting-from revealed a strong impact of conjugation type on protein folding. Whereas conjugates prepared by grafting a pre-formed polymer to the protein resulted in complete preservation of protein folding, grafting the polymer from the protein surface led to (partial) disruption of the protein structure. Next, conjugates of bovine serum albumin (BSA) as cheap and easily accessible protein were synthesized with PNIPAm and different oligoethylene glycol (meth)acrylates. The obtained protein-polymer conjugates were analyzed by an in-line combination of size exclusion chromatography and multi-angle laser light scattering (SEC-MALS). This technique is particular advantageous to determine molar masses, as no external calibration of the system is needed. Different SEC column materials and operation conditions were tested to evaluate the applicability of this system to determine absolute molar masses and hydrodynamic properties of heterogeneous conjugates prepared by grafting-from and grafting-to. Hydrophobic and non-covalent interactions of conjugates lead to error-prone values not in accordance to expected molar masses based on conversions and extents of modifications. As alternative to this method, conjugates were analyzed by sedimentation velocity analytical ultracentrifugation (SV-AUC) to gain insights in the hydrodynamic properties and how they change after conjugation. Within a centrifugal field, a sample moves and fractionates according to the mass, density, and shape of its individual components. Conjugates of BSA with PNIPAm were analyzed below and above the cloud point temperature of the thermo-responsive polymer component. It was identified that the polymer characteristics were transferred to the conjugate molecule which than showed a decreased ideality – defined as increased deviation from a perfect sphere model – below and increased ideality above the cloud point temperature. This effect can be attributed to an arrangement of the polymer chain pointing towards the solvent (expanded state) or snuggling around the protein surface depending on the applied temperature. The last project dealt with the synthesis of ferric hydroxamate uptake protein component A (FhuA)-polymer conjugates as building blocks for novel membrane materials. The shape of FhuA can be described as barrel and removal of a cork domain inside the protein results in a passive channel aimed to be utilized as pores in the membrane system. The polymer matrix surrounding the membrane protein is composed of a thermo-responsive and a UV-crosslinkable part. Therefore, an external trigger for covalent immobilization of these building blocks in the membrane and switchability of the membrane between different states was incorporated. The overall performance of membranes prepared by a drying-mediated self-assembly approach was evaluated by permeability and size exclusion experiments. The obtained membranes displayed an insufficiency in interchain crosslinking and therefore a lack in performance. Furthermore, the aimed switch between a hydrophilic and hydrophobic state of the polymer matrix did not occur. Correspondingly, size exclusion experiments did not result in a retention of analytes larger than the pores defined by the dimension of the used FhuA variant. Overall, different paths to generate protein-polymer conjugates by either grafting-from or grafting-to the protein surface were presented paving the way to the generation of new hybrid materials. Different analytical methods were utilized to describe the folding and hydrodynamic properties of conjugates providing a deeper insight in the overall characteristics of these seminal building blocks. N2 - Der Einbau von Proteinen in künstliche Materialien wie zum Beispiel Membranen ist eine vielversprechende Möglichkeit sich die besonderen Eigenschaften dieser Biomakromoleküle zunutze zu machen. Eine Möglichkeit, solche Membranen herzustellen, ist die Nutzung von Protein-Polymer-Konjugaten als universelle Bausteine. Für die Synthese solcher Konjugate stehen zwei Ansätze zur Verfügung. Bei grafting-to wird ein endgruppenfunktionalisiertes Polymer an das Protein angebunden. Dagegen wird bei grafting-from das Protein in einem ersten Schritt mit Initiatoren funktionalisiert und in einem zweiten Schritt das Polymer ausgehend von diesen sogenannten Makroinitiatoren synthetisiert. Innerhalb der hier vorliegenden Dissertation wurden vier Hauptprojekte bearbeitet, die sich entweder mit der tiefergehenden Charakterisierung von Protein-Polymer-Konjugaten oder deren Nutzung als Bausteine für Biohybrid-Membranen beschäftigten. Im ersten Projekt wurde der Einfluss der Konjugation auf die Proteinstruktur mittels NMR-Spektroskopie untersucht. Viele Analysemethoden geben Aufschluss über die Erhaltung großer, lokal ausgebildeter Strukturelemente nach Modifizierung. Kleine strukturelle Änderungen bleiben dort meist unerkannt. NMR-Spektroskopie ist eine der wenigen Methoden, die auch solche kleinen Änderungen aufzeigen kann. Innerhalb dieser Dissertation konnte gezeigt werden, dass die Modifizierung von Proteinen mit Polymeren je nach Konjugationsmethode einen enormen Einfluss auf die Proteinstruktur hat. Während Konjugate, die durch grafting-to hergestellt wurden, nahezu keine strukturellen Änderungen aufwiesen, führte die Modifizierung mit Initiatoren bereits zu deutlichen Änderungen, die sich nach der Polymerisation verstärkten. Das zweite Projekt widmetete sich der Analyse der hydrodynamischen Eigenschaften und der absoluten Molmassenbestimmung von Konjugaten mittels einer Kombination aus Größenausschlusschromatographie und Mehrwinkellichtstreuung. Während der Chromatographie werden die Konjugate entsprechend ihrer Größe aufgetrennt und anschließend durch Lichtstreuung vermessen. Damit diese Vermessung zu realistischen Werten führt, muss die vorangehende Chromatographie gewisse Anforderungen erfüllen. Eine davon ist, dass die Probe die Säule rein entsprechend ihrer Größe passiert und keine anderen Wechselwirkungen auftreten. Leider konnte diese Anforderung unter den getesteten Bedingungen nicht erfüllt werden, sodass die erhaltenen hydrodynamischen Werte und Molmassen stark fehlerbehaftet waren. Als Alternative zu dieser Methode wurden im dritten Projekt Konjugate in einer analytischen Ultrazentrifuge untersucht. Im Zentrifugalfeld wird eine Probe entsprechend der Größe, Masse und Dichte der Einzelbestandteile getrennt und detektiert. Solche Messungen wurden an Konjugaten modifiziert mit einem temperaturschaltbaren Polymer durchgeführt. Bei Temperaturen unterhalb des Schaltpunkts des Polymers sedimentierten die Konjugate langsamer als oberhalb dieses Punkts. Da sich die Molmasse während des Prozesses nicht ändert, kann dieses Verhalten auf die Form des Konjugats und den Einfluss des Polymers zurückgeführt werden. Die Messungen werden so interpretiert, dass das Polymer unterhalb der Schalttemperatur vom Protein weg zeigt und wie eine Art Fallschirm fungiert. Oberhalb der Temperatur schmiegt es sich an das Protein, ähnlich einem Fallschirmspringer, der die Arme an den Körper zieht. Das letzte Projekt strebte die Immobilisierung von Membranproteinen als funktionelle Poren in Membranmaterialien an. Dazu wurden Membranprotein-Polymer-Konjugate mit einem thermoresponsiven, UV-verlinkbaren Polymer hergestellt, welches einerseits durch einen externen Auslöser für eine kovalente Immobilisierung der Bausteine in der Membran und andererseits durch einen zweiten Auslöser die Membraneigenschaften modulieren sollte. Die Performance der hergestellten Membranen wurde durch Permeabilitäts- und Größenausschlussexperimente bewertet. Allerdings fand der angestrebte Wechsel zwischen einem hydrophilen und einem hydrophoben Zustand der Polymermatrix unter den getesteten Bedingungen nicht statt. Dementsprechend führten Größenausschlussexperimente nicht zu einer Retention von Analyten, die theoretisch größer sind als die durch die Dimension der verwendeten FhuA-Variante definierten Poren. Insgesamt wurden verschiedene Wege zur Synthese von Protein-Polymer-Konjugaten durch grafting-from und grafting-to vorgestellt. Die entwickelten Methoden und gewonnenen Erkenntnisse sind ein wichtiger Schritt auf dem Weg zu neuen Hybridmaterialien. Verschiedene analytische Methoden wurden eingesetzt, um die Faltung und die hydrodynamischen Eigenschaften der Konjugate zu untersuchen, was einen tieferen Einblick in die allgemeinen Eigenschaften dieser zukunftsträchtigen Bausteine ermöglicht. KW - Protein-Polymer-Konjugat KW - Proteincharakterisierung KW - kontrollierte radikalische Polymerisationen KW - Transmembranprotein KW - Analytische Ultrazentrifugation KW - SEC-MALS KW - Protein-NMR-Spektroskopie KW - Biohybrid-Membran KW - protein-polymer conjugate KW - protein characterization KW - controlled radical polymerization KW - transmembrane protein KW - analytical ultracentrifugation KW - SEC-MALS KW - protein NMR spectroscopy KW - biohybrid membrane materials Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-542921 ER - TY - THES A1 - Hentrich, Doreen T1 - Grenzflächen-kontrollierte Mineralisation von Calciumphosphat T1 - Interface-controlled mineralization of calcium phosphate N2 - In der vorliegenden Arbeit konnte gezeigt werden, dass die beiden verwendeten Amphiphile mit Cholesterol als hydrophoben Block, gute Template für die Mineralisation von Calciumphosphat an der Wasser/Luft-Grenzfläche sind. Mittels Infrarot-Reflexions-Absorptions-Spektroskopie (IRRAS), Röntgenphotoelektronenspektroskopie (XPS), Energie dispersiver Röntgenspektroskopie (EDXS), Elektronenbeugung (SAED) und hochauflösende Transmissionselektronenmikroskopie (HRTEM) konnte die erfolgreiche Mineralisation von Calciumphosphat für beide Amphiphile an der Wasser/Luft-Grenzfläche nachgewiesen werden. Es konnte auch gezeigt werden, dass das Phasenverhalten der beiden Amphiphile und die bei der Mineralisation von Calciumphosphat gebildeten Kristallphasen nicht identisch sind. Beide Amphiphile üben demnach einen unterschiedlichen Einfluss auf den Mineralisationsverlauf aus. Beim CHOL-HEM konnte sowohl nach 3 h als auch nach 5 h Octacalciumphosphat (OCP) als einzige Kristallphase mittels XPS, SAED, HRTEM und EDXS nachgewiesen werden. Das A-CHOL hingegen zeigte bei der Mineralisation von Calciumphosphat nach 1 h zunächst eine nicht eindeutig identifizierbare Vorläuferphase aus amorphen Calciumphosphat, Brushit (DCPD) oder OCP. Diese wandelte sich dann nach 3 h und 5 h in ein Gemisch, bestehend aus OCP und ein wenig Hydroxylapatit (HAP) um. Die Schlussfolgerung daraus ist, dass das CHOL-HEM in der Lage ist, dass während der Mineralisation entstandene OCP zu stabilisieren. Dies geschieht vermutlich durch die Adsorption des Amphiphils bevorzugt an der OCP Oberfläche in [100] Orientierung. Dadurch wird die Spaltung entlang der c-Achse unterdrückt und die Hydrolyse zum HAP verhindert. Das A-CHOL ist hingegen sterisch anspruchsvoller und kann wahrscheinlich aufgrund seiner Größe nicht so gut an der OCP Kristalloberfläche adsorbieren verglichen zum CHOL HEM. Das CHOL-HEM kann also die Hydrolyse von OCP zu HAP besser unterdrücken als das A-CHOL. Da jedoch auch beim A-CHOL nach einer Mineralisationszeit von 5 h nur wenig HAP zu finden ist, wäre auch hier ein Stabilisierungseffekt der OCP Kristalle möglich. Um eine genaue Aussage darüber treffen zu können, sind jedoch zusätzliche Kontrollexperimente notwendig. Es wäre zum einen denkbar, die Mineralisationsexperimente über einen längeren Zeitraum durchzuführen. Diese könnten zeigen, ob das CHOL-HEM die Hydrolyse vom OCP zum HAP komplett unterdrückt. Außerdem könnte nachgewiesen werden, ob beim A-CHOL das OCP weiter zum HAP umgesetzt wird oder ob ein Gemisch beider Kristallphasen erhalten bleibt. Um die Mineralisation an der Wasser/Luft-Grenzfläche mit der Mineralisation in Bulklösung zu vergleichen, wurden zusätzlich Mineralisationsexperimente in Bulklösung durchgeführt. Dazu wurden Nitrilotriessigsäure (NTA) und Ethylendiamintetraessigsäure (EDTA) als Mineralisationsadditive verwendet, da NTA unter anderem der Struktur der hydrophilen Kopfgruppe des A-CHOLs ähnelt. Es konnte gezeigt werden, dass ein Vergleich der Mineralisation an der Grenzfläche mit der Mineralisation in Bulklösung nicht ohne weiteres möglich ist. Bei der Mineralisation in Bulklösung wird bei tiefen pH-Werten DCPD und bei höheren pH-Werten HAP gebildet. Diese wurde mittels Röntgenpulverdiffraktometrie Messungen nachgewiesen und durch Infrarotspektroskopie bekräftigt. Die Bildung von OCP wie an der Wasser/Luft-Grenzfläche konnte nicht beobachtet werden. Es konnte auch gezeigt werden, dass beide Additive NTA und EDTA einen unterschiedlichen Einfluss auf den Verlauf der Mineralisation nehmen. So unterscheiden sich zum einen die Morphologien des gebildeten DCPDs und zum anderen wurde beispielsweise in Anwesenheit von 10 und 15 mM NTA neben DCPD auch HAP bei einem Ausgangs-pH-Wert von 7 nachgewiesen. Da unser Augenmerk speziell auf der Mineralisation von Calciumphosphat an der Wasser/Luft-Grenzfläche liegt, könnten Folgeexperimente wie beispielsweise GIXD Messungen durchgeführt werden. Dadurch wäre es möglich, einen Überblick über die gebildeten Kristallphasen nach unterschiedlichen Reaktionszeiten direkt auf dem Trog zu erhalten. Es konnte weiterhin gezeigt werden, dass auch einfache Amphiphile in der Lage sind, die Mineralisation von Calciumphosphat zu steuern. Amphiphile mit Cholesterol als hydrophoben Block bilden offensichtlich besonders stabile Monolagen an der Wasser/Luft-Grenzfläche. Eine Untersuchung des Einflusses ähnlicher Amphiphile mit unterschiedlichen hydrophilen Kopfgruppen auf das Mineralisationsverhalten von Calciumphosphat wäre durchaus interessant. N2 - In the current thesis two amphiphiles were used as templates for the mineralization of calcium phosphate at the air-water interface. Both amphiphiles have a cholesteryl group as hydrophobic block and only differ in their hydrophilic unit. The amphiphile CHOL-HEM has one carboxylic acid as the hydrophilic unit and the amphiphile A-CHOL contains a Newkome type dendron as hydrophilic block. The successful mineralization of calcium phosphate at the air-water interface could be prove by infrared reflection absorption spectroscopy, X-ray photoelectron spectroscopy, energy-dispersive X-ray spectroscopy, selected area electron diffraction and high resolution transmission electron microscopy. Furthermore, the study shows that the two amphiphiles have a different influence on the mineralization leading to different calcium phosphate phases. The crystal phase formed in case of the CHOL-HEM is octacalcium phosphate (OCP). For the A-CHOL a precursor phase after 1 h mineralization time was formed which could not be identified clearly. The precursor phase could be amorphous calcium phosphate, dicalcium hydrogen phosphate dihydrate (DCPD) or OCP. This phase transformed into a mixture of OCP and a small amount of hydroxyapatite (HAP). In conclusion, it can be demonstrated that the CHOL-HEM is able to stabilize the OCP. This could happen by the adsorption of the amphiphile at the OCP crystal surface in [100] direction and therefore the splitting along the c-axis is hampered and the hydrolysis into HAP will be prevented. The hydrophilic block of the A-CHOL is much bigger and sterically more demanding. For that reason, the A-CHOL cannot adsorb at the OCP crystal surface as good as the CHOL-HEM. The CHOL-HEM can prevent the hydrolysis from OCP into HAP much more efficiently. Due to the fact, that after 5 h mineralization time using A-CHOL as template just a small amount of HAP could be identified suggests that also this amphiphile shows a stabilizing effect on the OCP crystals. To prove this, additional control experiments would be necessary. The A-CHOL shows a better control in terms of the orientation of the mineralized crystals, which could be mostly identified as OCP crystals in [110] and HAP crystals in [-110] orientation. For the CHOL-HEM no preferred orientation could be determined for the formed OCP crystals. Additional mineralization experiments in bulk solution using ethylenediaminetetraacetic acid disodium salt dihydrate (EDTA) and nitrilotriacetic acid (NTA) as mineralization additives were performed. The structure of the NTA is similar to the hydrophilic unit of the A-CHOL. The study shows that the comparison of the mineralization at the air-water interface with the mineralization in bulk solution is not easily possible. For the mineralization in bulk solution at low pH values DCPD and at high pH values HAP is formed. These two phases could be identified using X-ray powder diffraction and infrared spectroscopy. The formation of OCP like for the mineralization at the air-water interface could not be observed. Both additives, EDTA and NTA show a different influence on the mineralization progress and show for example different morphologies of the precipitated DCPD. KW - Calciumphosphat KW - Mineralisation KW - Wasser-Luft-Grenzfläche KW - calcium phosphate KW - mineralization KW - air-water interface Y1 - 2017 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-398236 ER - TY - THES A1 - Sczech, Ronny T1 - Haftvermittlung von Polyelektrolyten zwischen Celluloseoberflächen T1 - Adhesion of polyelectrolytes between cellulose surfaces N2 - Der Adhäsionsprozess an Cellulosefasern sollte bis hin zur molekularen Ebene aufgeklärt werden. Zuerst wurde eine definierte Celluloseoberfläche durch Aufschleudern hergestellt und eingehend charakterisiert wurde. Die Beschaffenheit der Oberfläche ist stark abhängig von der Konzentration Celluloselösung, die für das Aufschleudern benutzt wurde. Für geringe Konzentrationen bildete sich ein Netzwerk von Cellulosefibrillen über die Siliziumoberfläche aus. In einem mittleren Bereich wurden geschlossene Filme mit Dicken zwischen 1,5 und ca. 10 nm erhalten. Diese Filme wiesen eine Rauhigkeit unter 2 nm auf, was der Größe eines Cellulosemoleküls entspräche. Mit höheren Konzentrationen wurden die Filme dicker und auch rauer. Die molekular glatten Cellulosefilme wurden zur Untersuchung der Adhäsionseigenschaften zwischen Celluloseoberflächen und ihrer Modifikation durch den Einfluss von Haftvermittlern (Polyelektrolyte) eingesetzt. Dafür wurde das Haftungsvermögen von Celluloseperlen auf der glatten Celluloseoberfläche analysiert. Die Adhäsion der Celluloseperlen hängt dabei von der Menge und von der Art des adsorbierten Polyelektrolyts ab. Geringe Polyelektrolytkonzentrationen ermöglichen wegen der teilweisen Bedeckung der Celluloseoberflächen eine Verstärkung der Haftvermittlung (Adhäsion). Höhere Konzentrationen an Polyelektrolyten bedecken die Celluloseoberfläche komplett, so dass die Symmetrie der Polyelektrolytadsorption entscheidend wird. Wenn Celluloseperlen und glatte Celluloseoberfläche gleichzeitig mit Polyelektrolyten beschichtet werden verringert sich bei hohen Konzentrationen die Adhäsion erheblich. Ein hohes Maß an Adhäsion wird dagegen erreicht, wenn nur eine der beiden gegenüberliegende Celluloseoberflächen separat beschichtet und dann in Kontakt mit der anderen gebracht Oberfläche wurde. Der Einfluss einer äußeren Kraft auf die haftenden Celluloseperlen wurde untersucht, um eine Aussage über die auftretenden Adhäsionskräfte machen zu können. Dafür wurde eine spezielle Strömungszelle entwickelt, mit der die Bewegung von Celluloseperlen beobachtet werden kann. Je nach Ausrichtung der Strömungszelle bewegten sich die Celluloseperlen unterschiedlich schnell. War die Strömungszelle horizontal ausgerichtet, wirkte zusätzlich zur Adhäsionskraft noch die Gravitation auf die Oberfläche, so dass hier eine wesentlich langsamere Durchschnittsgeschwindigkeit ermittelt wurde als für die Messungen in vertikaler Ausrichtung. Die Zugabe von verschiedenen Polyelektrolyten bei den Messungen mit der Strömungszelle hatte einen erheblichen Einfluss auf die Beweglichkeit der haftenden Celluloseperlen. Bei geringen Polyelektrolytkonzentrationen wurde das Potential der einzelnen Polyelektrolyten zur effektiven Haftvermittlung durch eine signifikant geringere Durchschnittsgeschwindigkeit der rollenden Celluloseperlen sichtbar. Aus der kritischen Anfangsgeschwindigkeit der rollenden Celluloseperlen wurde die Adhäsionsarbeit errechnet, die für die Bewegung nötig ist. N2 - The process of adhesion of cellulose fibres should be revealed down to a molecular level. Therefore, a well defined cellulose surface was prepared and then characterized. Cellulose was deposited on silicon wafer surfaces via spin coating from a solution of cellulose in dimethylacetamide (including 7% (w/w) lithium chloride). The resulting cellulose layers were analyzed by ellipsometry, AFM, FTIR, ICP-MS, x-ray reflectivity, and contact angle measurements. The texture of the prepared cellulose surfaces depends strongly on the used cellulose solution for spin coating process. For cellulose concentrations below 0.07wt% the wafer surfaces are covered with a network of cellulose fibrils. For concentrations between 0.07 and 0.5 wt%, closed films with thicknesses between 1.5 and ca. 10 nm are obtained. These films are molecularly smooth (rms roughness < 2nm). Higher concentrations result in thicker films with significantly rougher surfaces (rms roughness >2nm). The cellulose layers were used to investigate cellulose/cellulose adhesion and their modification by polyelectrolytes. To this end the sticking behavior of cellulose beads was analyzed. It is demonstrated that the adhesion of the beads depends on the type, amount, and adsorption symmetry of adsorbed polyelectrolyte. Low, incomplete polyelectrolyte coverage always enhances adhesion, whereas for high coverage the symmetry of the polyelectrolyte coating is very important. In this case, adhesion is enhanced if only one surface is covered with polyelectrolyte prior to contact. If both surfaces were fully covered with polyelectrolytes before contact adhesion is decreased. Flexible and cationic polyelectrolytes are the most potent candidates for this usage. The influence of an external force on the adhered cellulose beads was investigated to extimate the occurring adhesion forces. A special flow chamber was developed, in order to track the movements of cellulose beads rolling over a flat cellulose film. A constant water stream was applied as external force. The alignment of the flow chamber in reference to lab floor has an considerable influence on the speed of the rolling cellulose beads. If the flow chamber was aligned in the horizontal position, then gravity acts in addition to the adhesion force onto the surface. Thus, here were measured a substantial lower average speed of cellolude beads as it was measured for the vertical alignment of the flow chamber. The influence of gravity on the rolling friction of the cellulose beads could be prooved by modelling the rolling friction to HERTZ’s law and by evaluating statistically the movement vectors of the cellulose beads. As an another result of this findings one can estimate the occurring adhesion forces and energies. The addition of different polyelectrolytes to the water stream used in measurements with the flow chamber had a substantial influence on the mobility of adhered cellulose beads. At high concentrations of polyelectrolyte sticked so many beads at the cellulose surface, that it was not possible to interpret the data reasonable. Low concentrations enables the potential of the invidual polyelectrolyte to be a effictive binding agent. Here, a significant lower average speed of cellulose beads rolling over a cellulose surface was observed by all used polyelectrolytes but most by a flexible and cationic one. KW - Polyelektrolyt KW - Haftvermittler KW - Cellulose KW - Nassfestigkeit KW - Oberflächen KW - Adhäsion KW - surfaces KW - adhesion Y1 - 2005 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-7338 ER - TY - THES A1 - John, Daniela T1 - Herstellung anisotroper Kolloide mittels templatgesteuerter Assemblierung und Kontaktdruckverfahren T1 - Generation of anisotropic colloids via templated-assisted assembly and contact printing N2 - Diese Arbeit befasste sich mit neuen Konzepten zur Darstellung anisotroper Partikelsysteme durch Anordnung von funktionalisierten Partikeln unter Zuhilfenahme etablierter Methoden wie der templatgestützten Assemblierung von Partikeln und dem Mikrokontaktdruck. Das erste Teilprojekt beschäftigte sich mit der kontrollierten Herstellung von Faltenstrukturen im Mikro- bis Nanometerbereich. Die Faltenstrukturen entstehen durch die Relaxation eines Systems bestehend aus zwei übereinander liegender Schichten unterschiedlicher Elastizität. In diesem Fall wurden Falten auf einem elastischen PDMS-Substrat durch Generierung einer Oxidschicht auf der Substratoberfläche mittels Plasmabehandlung erzeugt. Die Dicke der Oxidschicht, die über verschiedene Parameter wie Behandlungszeit, Prozessleistung, Partialdruck des plasmaaktiven Gases, Vernetzungsgrad, Deformation sowie Substratdicke einstellbar war, bestimmte Wellenlänge und Amplitude der Falten. Das zweite Teilprojekt hatte die Darstellung komplexer, kolloidaler Strukturen auf Basis supramolekularer Wechselwirkungen zum Ziel. Dazu sollte vor allem die templatgestützte Assemblierung von Partikeln sowohl an fest-flüssig als auch flüssig-flüssig Grenzflächen genutzt werden. Für Erstere sollten die in Teilprojekt 1 hergestellten Faltenstrukturen als Templat, für Letztere Pickering-Emulsionen zur Anwendung kommen. Im ersten Fall wurden verschiedene, modifizierte Silicapartikel und Magnetitnanopartikel, deren Größe und Oberflächenfunktionalität (Cyclodextrin-, Azobenzol- und Arylazopyrazolgruppen) variierte, in Faltenstrukturen angeordnet. Die Anordnung hing dabei nicht nur vom gewählten Verfahren, sondern auch von Faktoren wie der Partikelkonzentration, der Oberflächenladung oder dem Größenverhältnis der Partikel zur Faltengeometrie ab. Die Kombination von Cyclodextrin (CD)- und Arylazopyrazol-modifizierten Partikeln ermöglichte, auf Basis einer Wirt-Gast-Wechselwirkung zwischen den Partikeltypen und einer templatgesteuerten Anordnung, die Bildung komplexer und strukturierter Formen in der Größenordnung mehrerer Mikrometer. Dieses System kann einerseits als Grundlage für die Herstellung verschiedener Janus-Partikel herangezogen werden, andererseits stellt die gerichtete Vernetzung zweier Partikelsysteme zu größeren Aggregaten den Grundstein für neuartige, funktionale Materialien dar. Neben der Anordnung an fest-flüssig Grenzflächen konnte außerdem nachgewiesen werden, dass Azobenzol-funktionalisierte Silicapartikel in der Lage sind, Pickering-Emulsionen über mehrere Monate zu stabilisieren. Die Stabilität und Größe der Emulsionsphase kann über Parameter, wie das Volumenverhältnis und die Konzentration, gesteuert werden. CD-funktionalisierte Silicapartikel besaßen dagegen keine Grenzflächenaktivität, während es CD-basierten Polymeren wiederum möglich war, durch die Ausbildung von Einschlusskomplexen mit den hydrophoben Molekülen der Ölphase stabile Emulsionen zu bilden. Dagegen zeigte die Kombination zwei verschiedener Partikelsysteme keinen oder einen destabilisierenden Effekt bezüglich der Ausbildung von Emulsionen. Im letzten Teilprojekt wurde die Herstellung multivalenter Silicapartikel mittels Mikrokontaktdruck untersucht. Die Faltenstrukturen wurden dabei als Stempel verwendet, wodurch es möglich war, die Patch-Geometrie über die Wellenlänge der Faltenstrukturen zu steuern. Als Tinte diente das positiv geladene Polyelektrolyt Polyethylenimin (PEI), welches über elektrostatische Wechselwirkungen auf unmodifizierten Silicapartikeln haftet. Im Gegensatz zum Drucken mit flachen Stempeln fiel dabei zunächst auf, dass sich die Tinte bei den Faltenstrukturen nicht gleichmäßig über die gesamte Substratfläche verteilt, sondern hauptsächlich in den Faltentälern vorlag. Dadurch handelte es sich bei dem Druckprozess letztlich nicht mehr um ein klassisches Mikrokontaktdruckverfahren, sondern um ein Tiefdruckverfahren. Über das Tiefdruckverfahren war es dann aber möglich, sowohl eine als auch beide Partikelhemisphären gleichzeitig und mit verschiedenen Funktionalitäten zu modifizieren und somit multivalente Silicapartikel zu generieren. In Abhängigkeit der Wellenlänge der Falten konnten auf einer Partikelhemisphäre zwei bis acht Patches abgebildet werden. Für die Patch-Geometrie, sprich Größe und Form der Patches, spielten zudem die Konzentration der Tinte auf dem Stempel, das Lösungsmittel zum Ablösen der Partikel nach dem Drucken sowie die Stempelhärte eine wichtige Rolle. Da die Stempelhärte aufgrund der variierenden Dicke der Oxidschicht bei verschiedenen Wellenlängen nicht kontant ist, wurden für den Druckprozess meist Abgüsse der Faltensubstrate verwendet. Auf diese Weise war auch die Vergleichbarkeit bei variierender Wellenlänge gewährleistet. Neben dem erfolgreichen Nachweis der Modifikation mittels Tiefdruckverfahren konnte auch gezeigt werden, dass über die Komplexierung mit PEI negativ geladene Nanopartikel auf die Partikeloberfläche aufgebracht werden können. N2 - This work dealt with new concepts of formation of anisotropic particle systems by using well-known methods such as template-assisted self-assembly of particles and microcontact printing. The first part paid attention to the controlled preparation of wrinkles in a micro or nanometer range. Wrinkles result from the relaxation of a system consisting of two layers with different elasticity. In this case, wrinkles were generated on top of an elastic PDMS substrate via plasma oxidation to a rigid surface. The thickness of the oxidized layer determined wavelength and amplitude of the wrinkles and could be varied by different parameters: time, power, partial pressure of plasma active gas, level of cross-linking, displacement and thickness of the PDMS substrate. The aim of the second part was the generation of complex, colloidal structures based on supramolecular interactions. For this, the template-assisted self-assembly of particles at solid-liquid and liquid-liquid interfaces should be used. Concerning the assembly at solid-liquid interfaces, we utilized the wrinkle structures generated in part 1 and, concerning the assembly at liquid-liquid interfaces, Pickering emulsions were chosen. In the first case, modified particles (silica and magnetite), that size and functionality (cyclodextrine, azobenzene and arylazopyrazol groups) varied, were assembled in wrinkle structures. The assembly depended not only on the chosen method, concentration, surface charge and size ratio between wrinkles and particles. The combination of cyclodextrine (CD)- and aryazopyralzol-modified particles enabled to build complex and regular structures based on supramolecular interactions between the two particles types and template-assisted self-assembly of these particles. On the one hand, this system generated Janus particles and on the other hand, the controlled agglomeration of two different particle types laid the foundation of new functional materials. Beside the assembly at solid-liquid interfaces, azobenzene-functionalized particles could be used for stabilizing Pickering emulsions. Formed emulsions were stable over a period of several months while parameters such as volume ratio and concentration influenced this stability as well as the volume of the emulsion phase. However, CD-functionalized silica particles possessed no interfacial activity to stabilize emulsions, whereas CD-based polymers could stabilize emulsions by forming inclusion complexes with hydrophobic molecules of the oil phase. On the other hand, the combination of CD-based and azobenzene-functionalized particle systems showed no or a destabilizing effect with regard to the formation of emulsions. In the last part, the generation of multivalent silica particles using a microcontact printing technique were analyzed. Wrinkles were used as stamps which induced the possibility to control the patch geometry by varying their wavelength. The positively charged polyelectrolyte (PEI) served as ink because it can stick to the silica surface by electrostatic interactions. Having a closer look at the printing process, a deviation to printing with flat stamps was found. In contrast to printing with flat stamps, ink solution, in case of wrinkles structures, did not spread over the whole substrate equally but laid mainly in the wrinkle groves. Due to this, the printing process is no longer a classical microcontact printing process but an intaglio printing process. Using the intaglio printing process, it was possible to modify both hemispheres of the particles at the same time and with different functionalities as well as generate multivalent silica particles. Depending on the wrinkle wavelength, two to eight patches per hemisphere could be achieved. The geometry of patches, means their size and arrangement, depended on the concentration of the ink on the stamps, the solvent to removing the particles from the stamps and the hardness of the stamps. Due to a varied thickness of the oxidized layer at different wrinkle wavelengths, the hardness of the stamps is not constant; that is why, casted wrinkles were utilized for the printing process. In this way, we ensure the comparability of printing using different wavelengths. Beside the successful proof of modification using intaglio printing, we could also show that negatively charged nanoparticles could be applied on the particle surface by embedding them into PEI before. KW - Faltenstrukturen KW - Anisotrope Kolloide KW - Kontaktdruck KW - Templatgesteuerte Assemblierung KW - wrinkles KW - patchy particles KW - particle assembly KW - printing Y1 - 2017 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-398270 ER - TY - THES A1 - Struszczyk, Marcin Henryk T1 - Herstellung von Chitosan und einige Anwendungen N2 - 1. Die Deacetylierung von crabshell – Chitosan führte gleichzeitig zu einem drastischen Abfall der mittleren viscosimetrischen Molmasse ( Mv), insbesondere wenn die Temperatur und die Konzentration an NaOH erhöht werden. Diese Parameter beeinflussten jedoch nicht den Grad der Deacetylierung (DD). Wichtig ist jedoch die Quelle des Ausgangsmaterials: Chitin aus Pandalus borealis ist ein guter Rohstoff für die Herstellung von Chitosan mit niedrigem DD und gleichzeitig hoher mittlerer Mv, während Krill-Chitin (Euphausia superba) ein gutes Ausgangsmaterial zur Herstellung von Chitosan mit hohem DD und niedrigem Mv ist. Chitosan, das aus Insekten (Calliphora erythrocephala), unter milden Bedingungen (Temperatur: 100°C, NaOH-Konzentration: 40 %, Zeit: 1-2h ) hergestellt wurde, hatte die gleichen Eigenschaften hinsichtlich DD und Mv wie das aus Krill hergestellte Chitosan. Der Bedarf an Zeit, Energie und NaOH ist für die Herstellung von Insekten-Chitosan geringer als für crabshell-Chitosan vergleichbare Resultaten für DD und Mv. 2. Chitosan wurde durch den Schimmelpilz Aspergillus fumigatus zu Chitooligomeren fermentiert. Die Ausbeute beträgt 25%. Die Chitooligomere wurden mit Hilfe von HPLC und MALDI-TOF-Massenspektrmetrie identifiziert. Die Fermentationsmischung fördert die Immunität von Pflanzen gegen Bakterien und Virusinfektion. Die Zunahme der Immunität schwankt jedoch je nach System Pflanze-Pathogen. Die Fermentation von Chitosan durch Aspergillus fumigatus könnte eine schnelle und billige Methode zur Herstellung von Chitooligomeren mit guter Reinheit und Ausbeute sein. Eine partiell aufgereinigte Fermentationsmischung dieser Art könnte in der Landwirtschaft als Pathogeninhibitor genutzt werden. Durch kontrollierte Fermentation, die Chitooligomere in definierter Zusammensetzung (d.h. definierter Verteilung des Depolymerisationsgrades) liefert, könnte man zu Mischungen kommen, die für die jeweilige Anwendung eine optimale Bioaktivität besitzen. 3. Die aus Chitosan-Dispersionen hergestellten MCChB-Filme weisen bessere mechanische Eigenschaften (Bruchfestigkeit, Dehnung) und eine höhere Wasseraufnahmefähigkeit auf als Filme, die nach herkömmlichen Methoden aus sauerer Lösung hergestellt werden. Die Einführung von Proteinen ändert die mechanischen Eigenschaften der MCChB-Filme abhängig von der Art, der Proteine sowie des DD und der Mv des eingesetzte Chitosan. Die Zugabe von Protein beschleunigt den biologischen Abbau der MCChB-Filme. Aus den untersuchten MCChB-Filmen mit Proteinzusatz können leichte, reißfeste und dennoch elastische Materialen hergestellt werden. 4. Mit Hilfe von MCChB-Dispersion kann Papier modifiziert werden. Dadurch werden die mechanischen Eigenschaften verbessert und die Wasseraufnahme wird verringert. Die Zugabe von Proteinen verringert das Wasseraufnahmevermögen noch weiter. Ein geringes Wasseraufnahmevermögen ist der bedeutendste Faktor bei der Papierherstellung. Auch Papier, das mit einem MCChB-Protein-Komplexe modifiziert wurde, zeigt gute mechanische Eigenschaften. 5. Wird Chitosan durch unmittelbare Einführung von MCChB auf Cellulose-Fasern aufgebracht, so erhält man eine netzartige Struktur, während durch Ausfällung aufgebrachtes Chitosan eine dünne Schicht auf den Cellulose-Fasern bildet. Die netzartige Struktur erleichtert die Bioabbaubarkeit, während die Schichtstruktur diese erschwert. 6. Die guten mechanischen Eigenschaften, die geringe Wasseraufnahmefähigkeit und die mit Cellulose vergleichbare Bioabbaubarkeit von Papier, das mit MCChB modifiziert wurde, lassen MCChB für die Veredlung von Papier nützlich erscheinen. N2 - 1. Deacetylation of the crustacean chitosan causes drastically decrease in the Mv with increasing reaction temperature and time as well as the concentration of sodium hydroxide. However, the DD are relatively less affected. Pandalus borealis is a good source for production of chitosan having high Mv and low DD, whereas chitosan of medium to low Mv can ideally be prepared using krill chitin. Insect chitosan is prepared under milder condition as compared with the crustacean chitosan, showed similar Mv and DD. Moreover, the consumption of time, energy and sodium hydroxide is much lower than for crustacean chitosan used. The properties of chitin (type of source, crystallinity, DD, Mv, swelling properties, particle size) affect the deacetylated polymer parameters. 2. Fermentation of chitosan using fungus Aspergillus fumigatus resulted in a composition of oligosaccharides with controlled molecular weight and yield at least 25 wt%. The product of fermentation effectively inhibited the viral and/or bacterial infection of the plant. This method can be an excellent, inexpensive system for preparation of bioactive agent. The preliminary purified fermentation mixture due to its antiviral and antibacterial behaviour is capable to be used as a natural, plant protection agent. The controlled degradation of chitosan connected with the production of various oligosaccharides having specified molecular weight allows obtaining the product with optimum bioactivity for suitable applications. 3. The films formed form microcrystalline chitosan (MCChB) gel-like dispersion demonstrate the better mechanical properties and higher swelling behaviour than typical films prepared using acidic solution of chitosan. The introduction of proteins significantly changes the mechanical strength and swelling behaviour. Addition of proteins causes the increase in their biodecomposition. The blended films containing proteins could be the base for formation of the resistant materials showed excellent elongation at break. 4. The application of MCChB in a paper formation as a modificator of the fibre-water interactions allows producing the paper sheets indicating the high increase in the mechanical properties and significant decrease in swelling properties. The introduction of MCChB with proteins causes a slight decrease in paper mechanical strength, if determined at low relative humidity. However, the mechanical strength measured at high relative humidity differ less than for paper sheet containing only MCChB. 5. Direct introduction of MCChB to a paper pulp forms the "web-like" structure of cellulose fibres and MCChB. The "web-like" structure of MCChB enables the faster biodecomposition of formed paper sheets. The precipitation of MCChB as wells as introduction of MCChB with proteins causes the "coat-like" structure. MCChB creates a thin layers coated the cellulose fibres lowering a biodecomposition rate. 6. The properties of paper sheets modified by MCChB such as: similar to cellulose biodegradation, excellent mechanical properties at rel. high humidity and the decrease in swelling properties as well as various possibilities to introduce MCChB allow to apple microcrystalline chitosan with or without proteins as the modificator of the fibre-water interactions in paper. KW - Chitosan / Präparative Chemie / Verpackungsmaterial / Mikrobielle Abbaubarkeit / Chitosan / Proteine Y1 - 2000 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-0000319 ER - TY - THES A1 - Chung, Kang Ko T1 - Heteroatom-containing carbons for high energy density supercapacitor T1 - Heteroatomhaltige Kohlenstoffe für Superkondensatoren mit hohen Energiedichten N2 - The supercapacitor is one of the most important energy storage devices as its construction allows for addressing many of the drawbacks related to batteries, but the low energy density of current systems is a major issue. In this doctoral dissertation, with a view to attaining high energy density supercapacitor systems that can be comparable to those for batteries, new heteroatom-containing carbons in the form of particles and three-dimensional films were investigated. A nitrogen-containing material, acrodam, was chosen as the carbon precursor due to the inexpensiveness, high carbonization yield, oligomerizability, etc. The carbon particles were prepared from acrodam together with caesium acetate as a meltable flux agent, and disclosed excellent properties in hydroquinone-loaded sulphuric acid electrolyte with high energy densities (up to 133.0 Wh kg–1) and sufficient cycle stabilities. These properties are already now comparable to those of batteries. Besides, conductive carbon three-dimensional films were fabricated using acrodam oligomer as the precursor by the inexpensive spin coating method. The films were found to be homogeneous, flat, void- and crack-free, and high conductivities (up to 334 S cm–1) could be obtained at the carbonization temperature of 1000 ºC. Furthermore, a porous carbon three-dimensional film could be formed using an organic template at the first attempt. This finding demonstrates the film’s potentiality for various applications such as supercapacitor electrode; the essential absence of contact resistance within the network should contribute to effective transportation of electron within the electrode. The progress made in this dissertation will open a new way to further enhancement of energy density for supercapacitor as well as other applications that exceeds the current properties. N2 - Der Superkondensator ist einer der wichtigsten Energiespeicher da seine Konstruktion die Lösung vieler Nachteile von Batterien erlaubt. Allerdings weisen derzeitige Systeme noch zu geringe Energiedichten auf. Um Superkondensatoren mit Energiedichten vergleichbar zu Batterien zu ermöglichen, wurden in der vorliegenden Dissertation neue, heteroatomhaltige Kohlenstoffe in Form von Partikeln und Filmen untersucht. Aufgrund geringer Kosten, hohen Ausbeuten, Polymerisierbarkeit usw. wurde die stickstoffhaltige Substanz Acrodam als Kohlenstoffvorstufe verwendet. Die Kohlenstoffpartikel wurden ausgehend von Acrodam zusammen mit Cäsiumacetat als schmelzbares Flussmittel hergestellt und wiesen ausgezeichnete Eigenschaften in Hydrochinon geladenen Schwefelsäure-Elektrolyten mit hohen Energiedichten (bis zu 133,0 Wh kg–1) und guten Zyklusstabilitäten auf. Diese Eigenschaften sind bereits jetzt vergleichbar mit denen von Batterien. Weiterhin wurden unter Verwendung von Acrodamoligomeren als Vorstufe und mit Hilfe der kostengünstigen Rotationsbeschichtung leitfähige, dreidimensionale Kohlenstofffilme hergestellt. Bei einer Karbonisierungstemperatur von 1000 °C konnten die Materialien als homogene, flache, Hohlraum-und Riss-freie Filme erhalten werden, die eine hohe Leitfähigkeit (bis zu 334 S cm–1) aufwiesen. Darüber hinaus konnte mit einem organischen Templat ein dreidimensionaler, poröser Kohlenstoff geformt werden. Dies zeigt das Potential der Filme für verschiedene Anwendungen wie Superkondensatorelektroden; die Abwesenheit von Übergangswiderständen im Netzwerk sollte zu einem effizienten Transport von Elektronen in der Elektrode beitragen. Die Ergebnisse dieser Dissertation werden neue Wege zur Verbesserung der Energiedichte von Superkondensatoren sowie weiteren Anwendungen eröffnen. KW - supercapacitor KW - carbon KW - heteroatom KW - energy density Y1 - 2013 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-69826 ER - TY - THES A1 - Braun, Max T1 - Heterogeneous Catalysis for the Conversion of Fructose to Chemicals and Fuel in a Continuous Flow Process T1 - Umsetzung von Fruktose zu Chemikalien und Treibstoff mittels heterogener Katalysatoren in einem kontinuierlichen Prozess N2 - Die Umsetzung von Zucker (Kohlenhydrate) in einem kontinuierlichen Prozess eröffnet Möglichkeiten der Synthese diverser Chemikalien und Treibstoff aus erneuerbaren Ressourcen, welche heute überwiegend aus fossilen Quellen stammen. Passend zum Konzept der Bioraffinerie und der „grünen Chemie“, liegt der Fokus dieser Arbeit auf der Umsetzung von in Ethanol gelöster Fruktose in einem kontinuierlichen Verfahren, mit Hilfe eigens entwickelter heterogener Katalysatoren. Die Dehydratisierung von Fruktose wird mit einem heterogenen Säurekatalysator realisiert, während die Folgeprodukte mittels einer Hydrodesoxygenierung umgesetzt werden. Für den zweiten Schritt kommen Metallkatalysatoren auf Basis von Nickel und Wolframcarbid (WC) zum Einsatz, wodurch der Einsatz teurer Edelmetalle vermieden werden kann. Hauptprodukte des zweistufigen Verfahrens sind 2,5-Dimethylfuran (DMF) und Ethyllevulinat (EL). Beide Moleküle sind vielversprechende alternative Treibstoffe, bzw. können gebräuchlichen Treibstoffen beigemischt werden, um deren Einsatz zu reduzieren und schrittweise zu substituieren. Alternativ können die Zwischenprodukte der Dehydratisierung, sowie DMF und EL weiter zu Chemikalien umgesetzt werden, welche in der Polymersynthese, als Lösungsmittel oder als Grundchemikalien eingesetzt werden können. Die Entwicklung der jeweiligen Katalysatoren für Dehydratisierungs- und Hydrodesoxygenierungsreaktionen erfolgt auf Basis von karbonisierter Biomasse, sowie Wolframcarbid. Die jeweiligen Reaktivitäten werden durch Standardreaktionen getestet, wobei sich Wolframcarbid in Nanopartikelform, in Kombination mit Wasserstoff als sehr aktiv erwiesen hat. Der selbst entwickelte aktivierte Kohlenstoff, das kommerzielle Amberlyst 15, sowie Wolframcarbid mit zusätzlichen Nickel-Nanopartikeln werden für weiterführende Reaktionen in einem kontinuierlichen Prozess herangezogen und kombiniert. Um den Umsatz von Fruktose zu DMF in einer „zwei Reaktoren Anlage“ zu ermöglichen, wird eine Erweiterung eines kommerziellen Reaktorsystems um einen weiteren Reaktor vorgenommen. Die Verweilzeit in der Reaktoranlage beträgt somit ca. 14 Minuten, wobei 11 Minuten auf die erste Säule (Dehydratisierung) und 3 Minuten auf die zweite Säule (Hydrodesoxygenierung) entfallen. In diesem kontinuierlichen und zweistufigen System lassen sich Ausbeuten von 38.5 % DMF und 47 % EL erzielen. Ein kontinuierlicher Lauf von sieben Stunden zeigt die Stabilität der eingesetzten Katalysatoren, auch wenn eine geringe Deaktivierung des Dehydratisierungskatalysators beobachtet werden kann. Der Ni@WC Katalysator zeigte hingegen keine Abnahme der Nickel Konzentration und somit kommt es zu keiner Auswaschung des Metalls. Das gebildete EL wurde hingegen nicht umgesetzt und verbleibt unverändert in Lösung. Das zweistufige System wurde schließlich in einem Mischkatalysatorsystem kombiniert, wobei auf aktivierten und sulfonierten Kohlenstoff zurückgegriffen wurde. Dieser zeigte bereits eine Transferhydrodesoxygenierungsaktivität. Diese Beobachtung ist deshalb bemerkenswert, da erst seit kurzem bekannt ist, dass Graphenstrukturen an sich katalytisch aktiv sein können. Um diese Aktivität weiter zu steigern, wurde der aktivierte Kohlenstoff mit 10 wt% Ni@WC gemischt, sodass beide Katalysatoren in einer Säule vorliegen. Die ursprünglichen 2 % DMF Ausbeute mit reinem aktivierten Kohlenstoff können somit auf 12 % gesteigert werden, da das Folgeprodukt EL hierbei vermieden wird und das Zwischenprodukt „HMF Derivat“ direkt zu DMF weiter reagieren kann. Dieses Ergebnis zeigt das Potential der „ein Reaktor Umsetzung“, weshalb eine kontinuierliche Durchflussreaktoranlage im Litermaßstab als Scale-Up des vorhergehenden Labormaßstabs realisiert wurde. Der 800 mm x 28.5 mm Reaktor bedient eine maximale Flussrate von 50 mL min-1, Drücke von 100 bar und Temperaturen bis zu 500 °C. N2 - The valorization of carbohydrates is one of the most promising fields in green chemistry, as it enables to produce bulk chemicals and fuels out of renewable and abundant resources, instead of further exploiting fossil feedstocks. The focus in this thesis is the conversion of fructose, using dehydration and hydrodeoxygenation reactions. The main goal is to find an easy continuous process, including the solubility of the sugar in a green solvent, the conversion over a solid acid as well as over a metal@tungsten carbide catalyst. At the beginning of this thesis, solid acid catalysts are synthesized by using carbohydrate material like glucose and starch at high temperatures (up to 600 °C). Additionally a third carbon is synthesized, using an activation method based on Ca(OH)2. After carbonization and further sulfonation, using fuming sulfuric acid, the three resulting catalysts are characterized together with sulfonated carbon black and Amberlyst 15 as references. In order to test all solid acid catalysts in reaction, a 250 mm x 4.6 mm stainless steel column is used as a fixed-bed continuous reactor. The temperature (110 °C to 250 °C) and residence time (2 to 30 minutes) is varied, and a direct relationship between contact time and selectivity is determined. The reaction mechanism, as well as the product distribution is showing a dehydration step of fructose towards 5-hydroxymethylfurfural (HMF). These furan-ring molecules are considered as “sleeping giants”, due to the possibility of using them as fuel, but also for upgrading them to chemicals like terephthalic acid or p-xylene. Consecutive reactions are producing levulinic acid, as well as condensation products with ethanol and formic acid. The activated carbon is additionally showing a 2 % yield of 2,5-Dimethylfuran (DMF) production, pointing towards the extraordinary properties of this catalyst. Without a metal catalyst present, what is normally necessary for hydrogenation reactions, a transferhydrogenation (with formic acid) is observed. The active catalyst was therefore carbon itself, what activated the hydrogen on its surface. This phenomenon was just very rarely observed so far. Expensive noble metals are the material of choice, when it comes to hydrogenation reactions nowadays and cheaper alternatives are necessary. By postulating a similar electronic structure of tungsten carbide (WC) to platinum by Lewy and Boudart, research is focusing on the replacement of Pt. The production of nano-sized tungsten carbide particles (7.5 ± 2.5 nm, 70 m2 g-1) is enabled by the so called “urea glass route” and its catalytic performances are compared to commercial material. It is shown, that the activity is strongly dependent on the size of the particles as well as the surface area. Nano-sized tungsten carbide is showing activity for hydrogenation reactions under mild conditions (maximum 150 °C, 30 bar). This material therefore opens up new possibilities for replacing the rare and expensive platinum with tungsten carbide based catalysts. Additionally different metal nanoparticles of palladium, copper and nickel are deposited on top of WC to further promote its reactivity. The nickel nanoparticles are strongly connected to WC and showed the best activity as well as selectivity for upgrading HMF with hydrodeoxygenation. The Ni@WC is not leaching and is showing very good hydrodeoxygenation properties with DMF yields up to 90 percent. Copper@WC is not showing good activity and palladium@WC enables undesired consecutive reactions, hydrogenating the furan ring system. In order to enable the upgrade of fructose to DMF directly in a continuous system, the current H CUBE Pro TM hydrogenation system is customized with a second reaction column. A 250 mm x 4.6 mm stainless steel reactor column is connected ahead of the hydrogen insertion, enabling the dehydration of fructose to HMF derivatives, before pumping these products into the second column for hydrogenation. The overall residence time in the two column reactor system is 14 minutes. The overall results are an almost full conversion with a yield of 38.5 % DMF and 47 % yield of EL. The main disadvantage is the formation of higher mass products, so called humins, which start depositing on top of the catalysts, blocking their active sites. In general it can be stated, that a two column system goes along with a higher investment as well as more maintenance costs, compared to a one column catalytic approach. To develop a catalyst, which is on the one hand able to dehydrate as well as hydrodeoxygenate the reactants, is aimed for at the last part of the thesis. The activated carbon however shows already activity for hydrodeoxygenation without any metal present and offers itself therefore as an alternative to overcome the temperature instability of Amberlyst 15 (max. 120 °C) for a combined DMF production directly from fructose. The activity for the upgrade to DMF is increased from 2 % to 12 % DMF yield in one mixed continuous column. In order to scale up the entire one column approach, an 800 mm x 28.5 mm inner diameter column was planned and manufactured. The system is scaled up and assembled, whereas this flow reactor system is able to be run with 50 mL min-1 maximum flow rate, to stand a pressure of maximum 100 bar and be heated to around 500 °C. The tubing and connections, as well as the used devices are planned according to be safe and easy in use. The scaled-up approach offers a reaction column 120 times bigger (510 ml) then the first extension of the commercial system. This further extension offers the possibility of ranging between 1 and 1000 mL min-1, making it possible to use the approach in pilot plant applications. KW - Biorefinery KW - Catalysis KW - Hydroxymethylfurfural KW - Upgrade of Fructose KW - Bioraffinerie KW - Katalyse KW - Hydroxymethylfurfural KW - Aufarbeitung von Fruktose Y1 - 2017 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-410370 ER - TY - THES A1 - Göbel, Ronald T1 - Hybridmaterialien aus mesoporösen Silica und ionischen Flüssigkeiten T1 - Hybrid materials of mesoporous silica and ionic liquids N2 - Die vorliegende Arbeit beschäftigt sich mit der Synthese und Charakterisierung mesoporöser monolithischer Silica und deren Hybridmaterialien mit Ionischen Flüssigkeiten (ILs, ionic liquids). Zur Synthese der Silicaproben wurde ein Sol-Gel-Verfahren, ausgehend von einer Präkursorverbindung wie Tetramethylorthosilicat angewendet. Der Katalysator mit der geringsten Basizität führte zum Material mit der kleinsten Porengröße und der größten spezifischen Oberfläche. Eine Kombination von porösen Silica mit ILs führt zur Materialklasse der Silica-Ionogele. Diese Hybridmaterialien verbinden die Eigenschaften eines porösen Festkörpers mit denen einer IL (Leitfähigkeit, weites elektrochemisches Fenster, gute thermische Stabilität) und bieten vielfältige Einsatzmöglichkeiten z.B. in der Katalyse- Solar- und Sensortechnik. Um diese Materialien für ihren Verwendungszweck zu optimieren, bedarf es deren umfassenden Charakterisierung. Daher wurde in der vorliegenden Arbeit das thermische Verhalten von Silica-Ionogelen unter Verwendung verschiedener 1-Ethyl-3-methylimidazolium [Emim]-basierter ILs untersucht. Interessanterweise zeigen die untersuchten ILs deutliche Änderungen in ihrem thermischen Verhalten, wenn diese in porösen Materialien eingeschlossen werden (Confinement). Während sich die untersuchten reinen ILs durch klar unterscheidbare Phasenübergänge auszeichnen, konnten für die entsprechenden Hybridmaterialien deutlich schwächer ausgeprägte Übergänge beobachtet werden. Einzelne Phasenübergänge wurden unterdrückt (Glas- und Kristallisationsübergänge), während z.B. Schmelzübergänge in verbreiterten Temperaturbereichen, zum Teil als einzeln getrennte Schmelzpeaks beobachtet wurden. Diese Untersuchungen belegen deutliche Eigenschaftsänderungen der ILs in eingeschränkten Geometrien. Über Festkörper-NMR-Spektroskopie konnte außerdem gezeigt werden, daß die ILs in den mesoporösen Silicamaterialien eine unerwartet hohe Mobilität aufweisen. Die ILs können als quasi-flüssig bezeichnet werden und zeigen die nach bestem Wissen höchste Mobilität, die bisher für vergleichbare Hybridmaterialien beobachtet wurde. Durch Verwendung von funktionalisierten Präkursoren, sowie der Wahl der Reaktionsbedingungen, kann die Oberfläche der Silicamaterialien chemisch funktionalisiert werden und damit die Materialeigenschaften in der gewünschten Weise beeinflußt werden. In der vorliegenden Arbeit wurde der Einfluß der Oberflächenfunktionalität auf das thermische Verhalten hin untersucht. Dazu wurden zwei verschiedene Möglichkeiten der Funktionalisierung angewendet und miteinander verglichen. Bei der in-situ-Funktionalisierung wird die chemische Funktionalität während der Sol-Gel-Synthese über ein entsprechend funktionalisiertes Silan mit in das Silicamaterial einkondensiert. Eine postsynthetische Funktionalisierung erfolgt durch Reaktion der Endgruppen eines Silicamaterials mit geeigneten Reaktionspartnern. Um den Einfluß der physikalischen Eigenschaften der Probe auf die Reaktion zu untersuchen, wurden pulverisierte und monolithische Silicamaterialien miteinander verglichen. Im letzten Teil der Arbeit wurde die Vielfältigkeit, mit der Silicamaterialien postsynthetisch funktionalisiert werden können demonstriert. Durch die Kenntnis von Struktur-Eigenschaftsbeziehungen können die Eigenschaften von Silica-Ionogelen durch die geeignete Kombination von fester und mobiler Phase in der gewünschten Weise verändert werden. Die vorliegende Arbeit soll einen Beitrag zur Untersuchung dieser Beziehungen leisten, um das Potential dieser interessanten Materialien für Anwendungen nutzen zu können. N2 - This work describes the synthesis and characterization of mesoporous monolithic silica and its hybrid materials with ionic liquids (ILs). For synthesis of the silica samples a sol-gel method was used. The catalyst with the weakest basicity leads to the material with the smallest pore size and the largest specific surface area. Combination of porous silica with ILs yields silica-ionogels. These hybrid materials combine the properties of porous solids with the properties of ILs (which is e.g. high conductivity, wide electrochemical stability window, and good thermal stability) and therefore offer a variety of possible applications like catalysis, solar and sensing. To optimize these materials for specific applications there is a need to understand their structure-composition-property relations. For this reason the thermal behavior of silica-ionogels was studied using different 1-ethyl-3-methylimidazolium [Emim]-based ILs. Interestingly the ILs show a clear change in their thermal behavior upon confinement in porous silica. Whereas the pure ILs show distinct phase transitions, the hybrid materials exhibit considerably weaker phase transitions. Phase transitions are suppressed (glass- and crystallization phase transitions); melting transitions show multiple melting peaks. Furthermore solid-state NMR also shows that ILs in mesoporous silica exhibit unusual high mobility. The confined ILs can therefore be classified as quasi-liquid and represents to our best knowledge the highest mobility observed so far in ionogels. By using functionalized silane precursors and different reaction conditions the silica surface was chemically functionalized which further changes the material properties. In a final approach a post-synthetic functionalization was performed by reaction of the selected groups of a silica material with suitable reactants. To study the effect of the physical appearance on the characteristics of the final material, powdered and monolithic samples were studied. In the last part of the work the versatility of post-synthetic silica functionalization was demonstrated. The current work contributes to a better understanding of structure-property correlations, to improve the potential of these interesting materials for possible applications. KW - Silica KW - ionische Flüssigkeiten KW - mesoporös KW - Hybridmaterialien KW - Sol-Gel KW - silica KW - ionic liquids KW - mesoporous KW - hybrid materials KW - sol-gel Y1 - 2011 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-54022 ER - TY - THES A1 - Fellinger, Tim-Patrick T1 - Hydrothermal and ionothermal carbon structures T1 - Hydrothermale und ionothermale Kohlenstoffstrukturen BT - from carbon negative materials to energy applications N2 - The needs for sustainable energy generation, but also a sustainable chemistry display the basic motivation of the current thesis. By different single investigated cases, which are all related to the element carbon, the work can be devided into two major topics. At first, the sustainable synthesis of “useful” carbon materials employing the process of hydrothermal carbonisation (HC) is described. In the second part, the synthesis of heteroatom - containing carbon materials for electrochemical and fuel cell applications employing ionic liquid precursors is presented. On base of a thorough review of the literature on hydrothermolysis and hydrothermal carbonisation of sugars in addition to the chemistry of hydroxymethylfurfural, mechanistic considerations of the formation of hydrothermal carbon are proposed. On the base of these reaction schemes, the mineral borax, is introduced as an additive for the hydrothermal carbonisation of glucose. It was found to be a highly active catalyst, resulting in decreased reaction times and increased carbon yields. The chemical impact of borax, in the following is exploited for the modification of the micro- and nanostructure of hydrothermal carbon. From the borax - mediated aggregation of those primary species, widely applicable, low density, pure hydrothermal carbon aerogels with high porosities and specific surface areas are produced. To conclude the first section of the thesis, a short series of experiments is carried out, for the purpose of demonstrating the applicability of the HC model to “real” biowaste i.e. watermelon waste as feedstock for the production of useful materials. In part two cyano - containing ionic liquids are employed as precursors for the synthesis of high - performance, heteroatom - containing carbon materials. By varying the ionic liquid precursor and the carbonisation conditions, it was possible to design highly active non - metal electrocatalyst for the reduction of oxygen. In the direct reduction of oxygen to water (like used in polymer electrolyte fuel cells), compared to commercial platinum catalysts, astonishing activities are observed. In another example the selective and very cost efficient electrochemical synthesis of hydrogen peroxide is presented. In a last example the synthesis of graphitic boron carbon nitrides from the ionic liquid 1 - Ethyl - 3 - methylimidazolium - tetracyanoborate is investigated in detail. Due to the employment of unreactive salts as a new tool to generate high surface area these materials were first time shown to be another class of non - precious metal oxygen reduction electrocatalyst. N2 - Die Notwendigkeit einer nachhaltigen Energiewirtschaft, sowie der nachhaltigen Chemie stellen die Motivation der vorgelegten Arbeit. Auf Grundlage separater Untersuchungen, die jeweils in engem Bezug zum Element Kohlenstoff stehen, kann die Arbeit in zwei Themenfelder geordnet werden. Der erste Teil behandelt die nachhaltige Herstellung nützlicher Kohlenmaterialien mit Hilfe des Verfahrens der hydrothermalen Carbonisierung. Im zweiten Teil wird die Synthese von Bor und Stickstoff angereicherten Kohlen aus ionischen Flüssigkeiten für elektrochemische Anwendungen abgehandelt. Insbesondere geht es um die Anwendung in Wasserstoff-Brennstoffzellen. Als Ergebnis einer sorgfältigen Literatur¬zusammenfassung der Bereiche Hydrothermolyse, hydrothermale Carbonisierung und Chemie des Hydroxymethylfurfurals wird ein chemisch-mechanistisches Modell zur Entstehung der Hydrothemalkohle vorgestellt. Auf der Basis dieses Modells wird ein neues Additiv zur hydrothermalen Carbonisierung von Zuckern vorgestellt. Die Verwendung des einfachen Additivs, genauer Borax, erlaubt eine wesentlich verkürzte und zu niedrigeren Temperaturen hin verschobene Prozessführung mit höheren Ausbeuten. Anhand des mechanistischen Modells wird ein Einfluss auf die Reaktion von Zuckern mit der reaktiven Kohlenvorstufe (Hydroxymethylfurfural) identifiziert. Die chemische Wirkung des Minerals Borax in der hydrothermalen Carbonisierung wird im Folgenden zur Herstellung vielfältig anwendbarer, hochporöser Kohlen mit einstellbarer Partikelgröße genutzt. Zum Abschluss des ersten Teils ist in einer Serie einfacher Experimente die Anwendbarkeit des mechanischen Modells auf die Verwendung „echter“ Biomasse in Form von Wassermelonenabfall gezeigt. Im zweiten Teil werden verschiedene cyano-haltige ionische Flüssigkeiten zur ionothermalen Synthese von Hochleistungskohlen verwendet. Durch Variation der ionischen Flüssigkeiten und Verwendung unterschiedlicher Synthesebedingungen wird die Herstellung hochaktiver, metallfreier Katalysatoren für die elektrochemische Reduktion von Sauerstoff erreicht. In der direkten Reduktion von Sauerstoff zu Wasser (wie sie in Brennstoffzellen Anwendung findet) werden, verglichen zu konventionellen Platin-basierten elektrochemischen Katalysatoren, erstaunliche Aktivitäten erreicht. In einem anderen Beispiel wird die selektive Herstellung von Wasserstoffperoxid zu sehr geringen Kosten vorgestellt. Abschließend wird anhand der Verwendung der ionischen Flüssigkeit 1-Ethyl-3-methylimidazolium-tetracyanoborat eine detaillierte Betrachtung zur Herstellung von graphitischem Borcarbonitrid vorgestellt. Unter Verwendung unreaktiver Salze, als einfaches Werkzeug zur Einführung großer inneren Oberflächen wird erstmals die elektrokatalytische Aktivität eines solchen Materials in der elektrochemischen Sauerstoffreduktion gezeigt. KW - Hydrothermalkohle KW - ionische Flüssigkeiten KW - poröse Materialien KW - Elektrokatalyse KW - hydrothermal carbon KW - ionic liquids KW - porous materials KW - electrocatalysis Y1 - 2011 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-57825 ER -