TY - JOUR A1 - Debsharma, Tapas A1 - Behrendt, Felix Nicolas A1 - Laschewsky, Andre A1 - Schlaad, Helmut T1 - Ring-opening metathesis polymerization of biomass-derived levoglucosenol JF - Angewandte Chemie : a journal of the Gesellschaft Deutscher Chemiker N2 - The readily available cellulose-derived bicyclic compound levoglucosenol was polymerized through ring-opening metathesis polymerization (ROMP) to yield polylevoglucosenol as a novel type of biomass-derived thermoplastic polyacetal, which, unlike polysaccharides, contains cyclic as well as linear segments in its main chain. High-molar-mass polyacetals with apparent weight-average molar masses of up to 100kgmol(-1) and dispersities of approximately 2 were produced despite the non-living/controlled character of the polymerization due to irreversible deactivation or termination of the catalyst/active chain ends. The resulting highly functionalized polyacetals are glassy in bulk with a glass transition temperature of around 100 degrees C. In analogy to polysaccharides, polylevoglucosenol degrades slowly in an acidic environment. KW - degradable polymers KW - metathesis KW - ring-opening polymerization KW - sustainable chemistry KW - thermoplastics Y1 - 2019 U6 - https://doi.org/10.1002/anie.201814501 SN - 1433-7851 SN - 1521-3773 VL - 58 IS - 20 SP - 6718 EP - 6721 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Naolou, Toufik A1 - Lendlein, Andreas A1 - Neffe, Axel T. T1 - Amides as non-polymerizable catalytic adjuncts enable the ring-opening polymerization of lactide with ferrous acetate under mild conditions JF - Frontiers in Chemistry N2 - Sn-based catalysts are effective in the ring-opening polymerization (ROP) but are toxic. Fe(OAc)(2) used as an alternative catalyst is suitable for the ROP of lactide only at higher temperatures (>170 degrees C), associated with racemization. In the ROP of ester and amide group containing morpholinediones with Fe(OAc)(2) to polydepsipeptides at 135 degrees C, ester bonds were selectively opened. Here, it was hypothesized that ROP of lactones is possible with Fe(OAc)(2) when amides are present in the reactions mixture as Fe-ligands could increase the solubility and activity of the metal catalytic center. The ROP of lactide in the melt with Fe(OAc)(2) is possible at temperatures as low as 105 degrees C, in the presence of N-ethylacetamide or N-rnethylbenzamide as non-polymerizable catalytic adjuncts (NPCA), with high conversion (up to 99 mol%) and yield (up to 88 mol%). Polydispersities of polylactide decreased with decreasing reaction temperature to <= 1.1. NMR as well as polarimetric studies showed that no racemization occurred at reaction temperatures <= 145 degrees C. A kinetic study demonstrated a living chain-growth mechanism. MALDI analysis revealed that no side reactions (e.g., cyclization) occurred, though transesterification took place. KW - ring-opening polymerization KW - polyester KW - catalyst KW - iron KW - amide ligand Y1 - 2019 U6 - https://doi.org/10.3389/fchem.2019.00346 SN - 2296-2646 VL - 7 PB - Frontiers Research Foundation CY - Lausanne ER - TY - THES A1 - Debsharma, Tapas T1 - Cellulose derived polymers T1 - Polymere aus Cellulose BT - synthesis of functional and degradable polymers from cellulose N2 - Plastics, such as polyethylene, polypropylene, and polyethylene terephthalate are part of our everyday lives in the form of packaging, household goods, electrical insulation, etc. These polymers are non-degradable and create many environmental problems and public health concerns. Additionally, these polymers are produced from finite fossils resources. With the continuous utilization of these limited resources, it is important to look towards renewable sources along with biodegradation of the produced polymers, ideally. Although many bio-based polymers are known, such as polylactic acid, polybutylene succinate adipate or polybutylene succinate, none have yet shown the promise of replacing conventional polymers like polyethylene, polypropylene and polyethylene terephthalate. Cellulose is one of the most abundant renewable resources produced in nature. It can be transformed into various small molecules, such as sugars, furans, and levoglucosenone. The aim of this research is to use the cellulose derived molecules for the synthesis of polymers. Acid-treated cellulose was subjected to thermal pyrolysis to obtain levoglucosenone, which was reduced to levoglucosenol. Levoglucosenol was polymerized, for the first time, by ring-opening metathesis polymerization (ROMP) yielding high molar mass polymers of up to ~150 kg/mol. The poly(levoglucosenol) is thermally stable up to ~220 ℃, amorphous, and is exhibiting a relatively high glass transition temperature of ~100 ℃. The poly(levoglucosenol) can be converted to a transparent film, resembling common plastic, and was found to degrade in a moist acidic environment. This means that poly(levoglucosenol) may find its use as an alternative to conventional plastic, for instance, polystyrene. Levoglucosenol was also converted into levoglucosenyl methyl ether, which was polymerized by cationic ring-opening metathesis polymerization (CROP). Polymers were obtained with molar masses up to ~36 kg/mol. These polymers are thermally stable up to ~220 ℃ and are semi-crystalline thermoplastics, having a glass transition temperature of ~35 ℃ and melting transition of 70-100 ℃. Additionally, the polymers underwent cross-linking, hydrogenation and thiol-ene click chemistry. N2 - Kunststoffe wie Polyethylen, Polypropylen und Polyethylenterephthalat sind ein großer Bestandteil unseres Alltags und finden Verwendung unter anderem als Verpackungsmaterialien, Haushaltswaren und Elektroisolierungen. Diese Polymere werden aus fossilen Ressourcen hergestellt, sind nicht abbaubar und verursachen nicht nur viele Umweltprobleme sondern können auch zu Gesundheitsschäden führen. Aufgrund dessen muss die Verwendung von erneuerbaren Ressourcen geachtet werden, wobei die hergestellten Polymere im Idealfall komplett biologisch abbaubar sind. Obwohl viele biobasierte Polymere, wie Polymilchsäure, Polybutylensuccinatadipat oder Polybutylensuccinat, bekannt sind, hat noch keines das Potential gezeigt, herkömmliche Polymere zu ersetzen. Cellulose ist einer der am häufigsten in der Natur produzierten nachwachsenden Rohstoffe und kann in verschiedene kleine organische Moleküle wie Zucker (Saccharide), Furan und auch Levoglucosenon umgewandelt werden. Ziel dieser Arbeit ist die Verwendung von Levoglucosenon als Monomer für die Synthese von Polymeren. Säurebehandelte Cellulose wurde einer thermischen Pyrolyse unterzogen, um Levoglucosenon zu erhalten, das dann weiter zu Levoglucosenol reduziert wurde. Das Levoglucosenol wurde zum ersten Mal erfolgreich über eine Ringöffnungsmetathese-Polymerisation (ROMP) polymerisiert. Die Molmassen der hergestellten Polymere erreichten Werte von bis zu ~150 kg/mol. Die thermische Analyse von Poly(levoglucosenol) zeigt, dass es bis zu einer Temperatur von ~220 ℃ stabil ist, eine Glasübergangstemperatur bei ~100 ℃ hat und ein amorphes Polymer ist. Weiterhin kann das Poly(levoglucosenol) in feuchter saurer Umgebung in kurzer Zeit abgebaut werden. Aufgrund dieser Eigenschaften kann Poly(levoglucosenol) als Alternative zu konventionellem Kunststoff, wie z.B. Polystyrol, eingesetzt werden kann. Levoglucosenol wurde weiter in Levoglucosenylmethylether umgewandelt. Levoglucosenylmethylether kann mit kationischer Ringöffnungs-Polymerisation (CROP) polymerisiert werden. Es wurden Polymere mit Molmassen von bis zu ~36 kg/mol hergestellt. Die Polymere weisen eine thermische Stabilität bis zu einer Temperatur von ~220 °C auf. Es handelt sich bei den hergestellten Poly(levoglucosenylmethylethern) um teilkristalline Thermoplaste, deren Glasüberganstemperatur bei ~35 °C und der Schmelzbereich bei 70-100 °C liegt. Die Doppelbindungen des Levoglucosenylmethylethers wurden genutzt um das Polymer zu vernetzen und zu funktionalisieren. KW - biomass valorization KW - levoglucosenol KW - ring-opening polymerization KW - degradable polymer KW - sustainable chemistry KW - Biomasseverwertung KW - Levoglucosenol KW - ringöffnende Polymerisation KW - abbaubares Polymer KW - nachhaltige Chemie Y1 - 2019 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-441312 ER -