TY - THES A1 - Zimmermann, Marc T1 - Multifunctional patchy silica particles via microcontact printing T1 - Multifunktionale Patchy Silika Partikel mithilfe des Mikrokontaktdruckverfahrens N2 - This research addressed the question, if it is possible to simplify current microcontact printing systems for the production of anisotropic building blocks or patchy particles, by using common chemicals while still maintaining reproducibility, high precision and tunability of the Janus-balance Chapter 2 introduced the microcontact printing materials as well as their defined electrostatic interactions. In particular polydimethylsiloxane stamps, silica particles and high molecular weight polyethylenimine ink were mainly used in this research. All of these components are commercially available in large quantities and affordable, which gives this approach a huge potential for further up-scaling developments. The benefits of polymeric over molecular inks was described including its flexible influence on the printing pressure. With this alteration of the µCP concept, a new method of solvent assisted particle release mechanism enabled the switch from two-dimensional surface modification to three-dimensional structure printing on colloidal silica particles, without changing printing parameters or starting materials. This effect opened the way to use the internal volume of the achieved patches for incorporation of nano additives, introducing additional physical properties into the patches without alteration of the surface chemistry. The success of this system and its achievable range was further investigated in chapter 3 by giving detailed information about patch geometry parameters including diameter, thickness and yield. For this purpose, silica particles in a size range between 1µm and 5µm were printed with different ink concentrations to change the Janus-balance of these single patched particles. A necessary intermediate step, consisting of air-plasma treatment, for the production of trivalent particles using "sandwich" printing was discovered and comparative studies concerning the patch geometry of single and double patched particles were conducted. Additionally, the usage of structured PDMS stamps during printing was described. These results demonstrate the excellent precision of this approach and opens the pathway for even greater accuracy as further parameters can be finely tuned and investigated, e.g. humidity and temperature during stamp loading. The performance of these synthesized anisotropic colloids was further investigated in chapter 4, starting with behaviour studies in alcoholic and aqueous dispersions. Here, the stability of the applied patches was studied in a broad pH range, discovering a release mechanism by disabling the electrostatic bonding between particle surface and polyelectrolyte ink. Furthermore, the absence of strong attractive forces between divalent particles in water was investigated using XPS measurements. These results lead to the conclusion that the transfer of small PDMS oligomers onto the patch surface is shielding charges, preventing colloidal agglomeration. However, based on this knowledge, further patch modifications for particle self-assembly were introduced including physical approaches using magnetic nano additives, chemical patch functionalization with avidin-biotin or the light responsive cyclodextrin-arylazopyrazoles coupling as well as particle surface modification for the synthesis of highly amphiphilic colloids. The successful coupling, its efficiency, stability and behaviour in different solvents were evaluated to find a suitable coupling system for future assembly experiments. Based on these results the possibility of more sophisticated structures by colloidal self-assembly is given. Certain findings needed further analysis to understand their underlying mechanics, including the relatively broad patch diameter distribution and the decreasing patch thickness for smaller silica particles. Mathematical assumptions for both effects are introduced in chapter 5. First, they demonstrate the connection between the naturally occurring particle size distribution and the broadening of the patch diameter, indicating an even higher precision for this µCP approach. Second, explaining the increase of contact area between particle and ink surface due to higher particle packaging, leading to a decrease in printing pressure for smaller particles. These calculations ultimately lead to the development of a new mechanical microcontact printing approach, using centrifugal forces for high pressure control and excellent parallel alignment of printing substrates. First results with this device and the comparison with previously conducted by-hand experiments conclude this research. It furthermore displays the advantages of such a device for future applications using a mechanical printing approach, especially for accessing even smaller nano particles with great precision and excellent yield. In conclusion, this work demonstrates the successful adjustment of the µCP approach using commercially available and affordable silica particles and polyelectrolytes for high flexibility, reduced costs and higher scale-up value. Furthermore, its was possible to increase the modification potential by introducing three-dimensional patches for additional functionalization volume. While keeping a high colloidal stability, different coupling systems showed the self-assembly capabilities of this toolbox for anisotropic particles. N2 - Diese Forschungsarbeit befasste sich mit der Frage, ob es möglich ist, bekannte Mikrokontaktdruckverfahren, zur Herstellung von anisotropen Bausteinen (Patchy Partikel), weiter zu vereinfachen. Dabei sollten gängige Chemikalien verwendet werden ohne einen Verlust in Reproduzierbarkeit, hoher Präzision und Feineinstellung der Janus-Balance zu erleiden. In Kapitel 2 wurden die verwendeten Mikrokontaktdruckmaterialien sowie deren elektrostatische Wechselwirkungen vorgestellt. Insbesondere handelte es sich dabei um Polydimethylsiloxan Stempel, Silikapartikel und hoch molekulare Polyethylenimin Tinte. All diese Produkte sind kommerziel in großen und bezahlbaren Mengen erhältlich. Nicht nur die Vorteile von polymeren Tinten im Gegensatz zu molekularen Tinten wurde beschrieben, sondern auch die hohe Flexibilität dieses Verfahrens bezüglich der verwendeten Druckkraft. Mit dieser Anpassung des Mikrokontaktdrucks, wurde eine neue Methode der Lösungsmittel unterstützten Partikelablösung ermöglicht, mit deren Hilfe ein einfaches Schalten zwischen zwei dimensionaler Oberflächenfunktionalisierung und drei dimensionalem Strukturdrucks möglich war, ohne Druckparameter oder Startchemikalien zu verändern. Dadurch konnte neu erschaffenes internes Volumen verwendet werden um Nanoadditive einzuführen und so zusätzliche physikalische Eigenschaften zu integrieren, ohne die Oberflächenchemie der Patches verändert wurde. Der Erfolg dieses Systems und seine erreichbaren Grenzen wurde gründlichst in Kapitel 3 erforscht, indem detaillierte Geometrieparameter der Patches einschließlich Durchmesser, Dicke und Ausbeute, erworben wurden. Hierfür wurden Silikapartikel in einem Größenbereich von 1µm bis 5µm mit unterschiedlichen Tintenkonzentrationen bedruckt, um Veränderungen erforschen zu können. Ein notwendiger Luftplasma Ätzschritt für die Produktion von trivalenten Partikeln, mit Hilfe des sogenannten ,,Sandwich‘‘-Drucks, wurde erläutert und vergleichende Untersuchen von einfach und zweifach modifizierten Bausteinen wurden durchgeführt. Zusätzlich dazu, wurde die Verwendung von strukturierten Stempel beschrieben. Die Ergebnisse verdeutlichen die exzellente Genauigkeit dieser Methode und öffnet den Weg um eine hoch höhere Präzision zu erreichen da weitere Parametere genau eingestellt und untersucht werden können, z.B. Luftfeuchtigkeit und Temperature während der Stempelbeladung. Die Performance der herstellten anisotropen Partikel wurde in Kapitel 4 mit Verhaltensstudien in alkoholischen und wässrigen Dispersionen getestet. Dabei wurde die Stabilität der Oberflächenfunktionalisierungen in einem breiten pH Bereich untersucht. Dadurch wurde ein Ablösungsmechanismus bei sehr hohen bzw. niedrigen pH-Werten entdeckt, der zur Deaktivierung elektrostatischer Wechselwirkungen zwischen Partikeloberfläche und Polyelektrolyte Tinte führte. Desweitern wurden die Abwesenheit starker Wechselwirkung der divalenten Partikel in Wasser mit Hilfe von XPS untersucht. Das Resultat zeigte, dass der Transfer kleinster PDMS Oligomere auf die Patchoberfläche zu einer Ladungsabschirmung führte. Dadurch konnte Agglomeration verhindert werden. Aufgrund dieser Ergebnisse wurden weitere Modifikationen für Partikelassemblierung durchgeführt. Hierfür wurde die Einführung von magnetischen Nanoadditiven, die Funktionalisierung mit Avidin-Biotin sowie dem Lichtschaltbaren Cyclodextrin-Arylazopyrazol Komplexen und die Partikeloberflächenfunktionalisierung zur Herstellung amphiphiler Teilchen untersucht. Die Effizienz der Kopplung, deren Stabilität sowie das Verhalten in unterschiedlichen Lösungsmittel wurde beschrieben. Basierend auf diesen Ergebnissen können noch anspruchsvollere Strukturen durch kolloidale Selbstassemblierung erzeugt werden. Einige Ergebnisse dieser Arbeit benötigten zusätzlicher Analyse um die zugrundeliegenden Mechaniken verstehen zu können. Dazu gehörte die relative hohe Streuung des Durchmessers für unterschiedliche Partikelsysteme, sowie das Ausdünnen des Patches mit kleineren Silikapartikeln. Mathematische Modelle in Kapitel 5 beschreiben beide Effekte. Dadurch war es möglich einen Zusammenhang zwischen der natürlichen Partikelgrößenverteilung sowie der Verbreitung des Patchdurchmessers festzustellen. Des Weiteren konnte eine Verkleinerung der Druckkraft durch eine Erhöhung der Packungsdichte für kleine Partikel beschrieben werden, wodurch eine Erklärung der Ausdünnung möglich war. All diese Berechnung führten schlussendlich zur Entwicklung eines neuen mechanischen Mikrokontaktdruckverfahrens, welches mit Hilfe von Zentrifugalkräften eine hohe Druckkontrolle und eine exzellente parallele Ausrichtung zwischen den Substraten ermöglicht. Erste Ergebnisse, sowie deren Vergleich mit bisher erhaltenen Resultaten schließen diese Forschung ab. Des Weiteren zeigt es die Vorteile einer solchen Vorrichtung für kommende Applikationen, besonders um noch kleinere Nanopartikel mit einer hohen Präzision modifizieren zu können. Zusammenfassend ist zu sagen, dass diese Forschung die erfolgreiche Anpassung des Mikrokontaktdruckverfahrens mit kommerziell erhältlichen und bezahlbaren Silikapartikeln und Polyelektrolyten demonstriert, um hohe Flexibilität, reduzierte Kosten und ein erweitertes Skalierungspotential zu bieten. Zusätzlich ist es gelungen, die Funktionalisierungsdichte zu erhöhen, indem drei dimensionaler Strukturdruck bisher ungenutztes Volumen schaffen konnte. Während eine hohe kolloidale Stabilität erhalten blieb, ist es gelungen unterschiedliche Kopplungssysteme zu nutzen, um das Selbstorganisationspotential dieser Toolbox für anisotrope Partikel aufzuzeigen. KW - patchy particles KW - microcontact printing KW - silica particles KW - anisotropic colloids KW - polyelectrolytes KW - Patchy Partikel KW - Mikrokontaktdruck KW - Silika Partikel KW - Anisotrope Kolloide KW - Polyelektrolyte Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-427731 ER - TY - THES A1 - Haase, Martin F. T1 - Modification of nanoparticle surfaces for emulsion stabilization and encapsulation of active molecules for anti-corrosive coatings T1 - Nanopartikel Oberflächenmodifikationen zur Emulsionsstabilisierung und Verkapselung von Wirkstoffen für Antikorrosionsbeschichtungen N2 - Within this work, three physicochemical methods for the hydrophobization of initially hydrophilic solid particles are investigated. The modified particles are then used for the stabilization of oil-in-water (o/w) emulsions. For all introduced methods electrostatic interactions between strongly or weakly charged groups in the system are es-sential. (i) Short chain alkylammonium bromides (C4 – C12) adsorb on oppositely charged solid particles. Macroscopic contact angle measurements of water droplets under air and hexane on flat silica surfaces in dependency of the surface charge density and alkylchain-length allow the calculation of the surface energy and give insights into the emulsification properties of solid particles modified with alkyltrimethylammonium bromides. The measure-ments show an increase of the contact angle with increasing surface charge density, due to the enhanced adsorp-tion of the oppositely charged alkylammonium bromides. Contact angles are higher for longer alkylchain lengths. The surface energy calculations show that in particular the surface-hexane or surface-air interfacial en-ergy is being lowered upon alkylammonium adsorption, while a significant increase of the surface-water interfa-cial energy occurs only at long alkyl chain lengths and high surface charge densities. (ii) The thickness and the charge density of an adsorbed weak polyelectrolyte layer (e.g. PMAA, PAH) influence the wettability of nanoparticles (e.g. alumina, silica, see Scheme 1(b)). Furthermore, the isoelectric point and the pH range of colloidal stability of particle-polyelectrolyte composites depend on the thickness of the weak polye-lectrolyte layer. Silica nanoparticles with adsorbed PAH and alumina nanoparticles with adsorbed PMAA be-come interfacially active and thus able to stabilize o/w emulsions when the degree of dissociation of the polye-lectrolyte layer is below 80 %. The average droplet size after emulsification of dodecane in water depends on the thickness and the degree of dissociation of the adsorbed PE-layer. The visualization of the particle-stabilized o/w emulsions by cryogenic SEM shows that for colloidally stable alumina-PMAA composites the oil-water interface is covered with a closely packed monolayer of particles, while for the colloidally unstable case closely packed aggregated particles deposit on the interface. (iii) By emulsifying a mixture of the corrosion inhibitor 8-hydroxyquinoline (8-HQ) and styrene with silica nanoparticles a highly stable o/w emulsion can be obtained in a narrow pH window. The amphoteric character of 8-HQ enables a pH dependent electrostatic interaction with silica nanoparticles, which can render them interfa-cially active. Depending on the concentration and the degree of dissociation of 8-HQ the adsorption onto silica results from electrostatic or aromatic interactions between 8-HQ and the particle-surface. At intermediate amounts of adsorbed 8-HQ the oil wettability of the particles becomes sufficient for stabilizing o/w emulsions. Cryogenic SEM visualization shows that the particles arrange then in a closely packed shell consisting of partly of aggregated domains on the droplet interface. For further increasing amounts of adsorbed 8-HQ the oil wet-tability is reduced again and the particles ability to stabilize emulsions decreases. By the addition of hexadecane to the oil phase the size of the droplets can be reduced down to 200 nm by in-creasing the silica mass fraction. Subsequent polymerization produces corrosion inhibitor filled (20 wt-%) poly-styrene-silica composite particles. The measurement of the release of 8-hydroxyquinoline shows a rapid increase of 8-hydroxyquinoline in a stirred aqueous solution indicating the release of the total content in less than 5 min-utes. The method is extended for the encapsulation of other organic corrosion inhibitors. The silica-polymer-inhibitor composite particles are then dispersed in a water based alkyd emulsion, and the dispersion is used to coat flat aluminium substrates. After drying and cross-linking the polmer-film Confocal Laser Scanning Micros-copy is employed revealing a homogeneous distribution of the particles in the film. Electrochemical Impedance Spectroscopy in aqueous electrolyte solutions shows that films with aggregated particle domains degrade with time and don’t provide long-term corrosion protection of the substrate. However, films with highly dispersed particles have high barrier properties for corrosive species. The comparison of films containing silica-polystyrene composite particles with and without 8-hydroxyquinoline shows higher electrochemical impedances when the inhibitor is present in the film. By applying the Scanning Vibrating Electrode Technique the localized corrosion rate in the fractured area of scratched polymer films containing the silica-polymer-inhibitor composite particles is studied. Electrochemical corrosion cannot be suppressed but the rate is lowered when inhibitor filled composite particles are present in the film. By depositing six polyelectrolyte layers on particle stabilized emulsion droplets their surface morphology changes significantly as shown by SEM visualization. When the oil wettability of the outer polyelectrolyte layer increases, the polyelectrolyte coated droplets can act as emulsion stabilizers themselves by attaching onto bigger oil droplets in a closely packed arrangement. In the presence of 3 mM LaCl3 8-HQ hydrophobized silica particles aggregate strongly on the oil-water inter-face. The application of an ultrasonic field can remove two dimensional shell-compartments from the droplet surface, which are then found in the aqueous bulk phase. Their size ranges up to 1/4th of the spherical particle shell. N2 - Im Rahmen dieser Arbeit wurden drei Oberflächenmodifikationen zur Hydrophobierung von ursprünglich hydrophilen Feststoffpartikeln entwickelt. Die so modifizierten Partikel werden dann zur Stabilisierung von Öl-in-Wasser Emulsionen verwendet. Für sämtliche entwickelte Methoden sind elektrostatische Wechselwirkungen zwischen stark oder schwach dissoziierten chemischen Gruppen essentiell. (i) Kurzkettige Alkyltrimethylammonium Bromide (C4-C12) adsorbieren auf entgegengesetzt geladenen Partikeln. Makroskopische Kontaktwinkelmessungen von Wasser Tropfen in Luft und Hexan auf flachen Siliziumoxid Oberflächen mit variabler Oberflächenladungsdichte und Alkylkettenlänge ermöglichen die Berechnung der Oberflächenenergie und geben Einblicke in die Emulgationseigenschaften von so modifizierten Feststoffpartikeln. Die Messungen zeigen einen Anstieg des Kontakwinkels mit steigender Oberflächenladungsdichte, bedingt durch die verstärkte Adsorption von entgegengesetzt geladenen Alkyltrimethylammonium Bromiden. Die Kontaktwinkel sind zudem größer für längerkettige Alkyltrimethylammonium Bromide. Die Berechnungen der Oberflächenenergie zeigen, dass besonders die Feststoff-Hexan oder Feststoff-Luft Grenzflächenenergie durch die Adsorption verringert wird, wohingegen die Feststoff-Wasser Oberflächenenergie nur bei längeren Alkylkettenlängen und hohen Oberflächenladungsdichten signifikant ansteigt. (ii) Die Schichtdicke und Ladungsdichte von adsorbierten schwachen Polyelektrolyten (z.B. PMAA, PAH) beeinflusst die Benetzbarkeit von Nanopartikeln (z.B. Aluminiumoxid, Siliziumoxid). Der isoelektrische Punkt und der pH Bereich für kolloidale Stabilität solcher Polyelektrolyt modifizierter Partikel hängt von der Dicke der Polyelektrolytschicht ab. Siliziumoxid und Aluminiumoxid Nanopartikel mit adsorbierten PAH bzw. PMAA werden Grenzflächenaktiv und dadurch befähigt Öl-in-Wasser Emulsionen zu stabilisieren, wenn der Dissoziationsgrad der Polyelektrolytschicht geringer als 80 % ist. Die durchschnittliche Tropfengröße von Dodecan-in-Wasser Emulsionen ist abhängig von der Polyelektrolytschichtdicke und dem Dissoziationsgrad. Die Visualisierung von Partikel stabilisierten Öl-in-Wasser Emulsionen durch kryogene REM zeigt, dass im Falle von kolloidal stabilen Aluminiumoxid-PMAA Partikeln die Öl-Tröpfchen mit einer dichtgepackten Partikelhülle belegt sind, während für kolloidal destabilisierte Partikel eine Hülle aus aggregierten Partikeln gefunden wird. (iii) Durch das Emulgieren einer Lösung des Korrosionsinhibitors 8-Hydroxychinolins (8HQ) in Styrol mit Siliziumoxid Nanopartikeln können stabile Öl-in-Wasser Emulsionen in einem pH Fenster von 4 - 6 hergestellt werden. Der amphoterische Charakter von 8HQ ermöglicht eine pH abhängige elektrostatische Wechselwirkung mit den Siliziumdioxid Nanopartikeln, welche diese Grenzflächenaktiv werden lässt. In Abhängigkeit der Konzentration und des Dissoziationsgrads von 8HQ folgt die Adsorption auf Siliziumdioxid aus elektrostatischen oder aromatischen Wechselwirkungen zwischen 8HQ und der Partikeloberfläche. Bei mittleren adsorbierten Mengen wird die Öl Benetzbarkeit der Partikel ausreichend erhöht um Öl-in-Wasser Emulsionen zu stabilisieren. Kryogene REM zeigt, dass die Partikel dann in dicht gepackte Hüllen, mit teilweise aggregierten Domänen auf der Öltröpfchenoberfläche vorliegen. Durch weiter ansteigende adsorbierte 8HQ Mengen wird die Öl-Benetzbarkeit wieder zurückgesetzt und die Emulgationsfähigkeit der Partikel aufgehoben. Durch die Zugabe von Hexadecan zur Öl Phase kann die Tropfengröße durch Erhöhung des Siliziumdioxid Anteils auf 200 nm herabgesetzt werden. Anschließende Polymerisation des Styrols generiert Korrosionsinhibitor gefüllte (20 Gew-%) Polystyrol-Silizumoxid Komposite. Die Messung der Freisetzungsrate von 8HQ zeigt einen schnellen Anstieg der 8HQ Konzentration in einer gerührten wässrigen Lösung innerhalb von 5 Minuten. Die Verkapselungsmethode wird auch für andere organische Korrosionsinhibitoren erweitert. Die Komposite werden dann in einer wasserbasierten Alkydpräpolymeremulsion dispergiert und diese Mischung wird zur Beschichtung von flachen Aluminiumplatten genutzt. Nach Trocknung und Quervernetzung des Films wird Konfokale Laser Mikroskopie dazu verwendet um die räumliche Verteilung der Composite im Film zu visualisieren. Elektrochemische Impedanzspektroskopie zeigt, dass die Barriereeigenschaften des Films durch die Anwesenheit der Komposite verbessert sind. Raster Vibrationselektroden Messungen zeigen, dass die Korrosionsrate in einem Kratzer des Films durch die Anwesenheit der Inhibitor efüllten Komposite reduziert ist. Durch die Ablagerung von 6 Polyelektroytschichten auf Feststoffstabilisierten Emulsionströpfchen verändert sich deren Oberflächenmorphologie deutlich (gezeigt durch REM). Wenn die Ölbenetzbarkeit der äußeren Polyelektrolytschicht ansteigt, dann können solche Polyelektolytbeschichteten Feststoffstabilisierte Emulsionströpfchen selber als Emulsionsstabilisatoren verwendet werden. Diese lagern sich dann in einer dicht gepackten Schicht auf der Oberfläche von größeren Emulsionstropfen ab. In der Gegenwart von 3 mM LaCl3 aggregieren 8HQ modifizierte Siliziumoxid Partikel stark auf der Öl-Wasser Grenzfläche. Der Einsatz von Ultraschall kann aggregierte Schalenbestandteile von der Tropfenoberfläche wegreißen. Diese Wracks können bis zu einem Viertel der Kugelhülle ausmachen und liegen dann als kolloidale Schalen im Wasser vor. KW - Nanopartikel KW - Emulsionen KW - Polyelektrolyte KW - Korrosion KW - Adsorption KW - nanoparticles KW - emulsions KW - polyelectrolytes KW - corrosion KW - adsorption Y1 - 2011 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-55413 ER - TY - THES A1 - Note, Carine T1 - Influence of hydrophobically modified polyelectrolytes on nanoparticle synthesis in self-organized systems and in water T1 - Einfluss von hydrophob modifizierten Polyelektrolyten auf die Nanopartikelsynthese in selbst-organisierten Systemen und in Wasser N2 - The formation of colloids by the controlled reduction, nucleation, and growth of inorganic precursor salts in different media has been investigated for more than a century. Recently, the preparation of ultrafine particles has received much attention since they can offer highly promising and novel options for a wide range of technical applications (nanotechnology, electrooptical devices, pharmaceutics, etc). The interest derives from the well-known fact that properties of advanced materials are critically dependent on the microstructure of the sample. Control of size, size distribution and morphology of the individual grains or crystallites is of the utmost importance in order to obtain the material characteristics desired. Several methods can be employed for the synthesis of nanoparticles. On the one hand, the reduction can occur in diluted aqueous or alcoholic solutions. On the other hand, the reduction process can be realized in a template phase, e.g. in well-defined microemulsion droplets. However, the stability of the nanoparticles formed mainly depends on their surface charge and it can be influenced with some added protective components. Quite different types of polymers, including polyelectrolytes and amphiphilic block copolymers, can for instance be used as protecting agents. The reduction and stabilization of metal colloids in aqueous solution by adding self-synthesized hydrophobically modified polyelectrolytes were studied in much more details. The polymers used are hydrophobically modified derivatives of poly(sodium acrylate) and of maleamic acid copolymers as well as the commercially available branched poly(ethyleneimine). The first notable result is that the polyelectrolytes used can act alone as both reducing and stabilizing agent for the preparation of gold nanoparticles. The investigation was then focused on the influence of the hydrophobic substitution of the polymer backbone on the reduction and stabilization processes. First of all, the polymers were added at room temperature and the reduction process was investigated over a longer time period (up to 8 days). In comparison, the reduction process was realized faster at higher temperature, i.e. 100°C. In both cases metal nanoparticles of colloidal dimensions can be produced. However, the size and shape of the individual nanoparticles mainly depends on the polymer added and the temperature procedure used. In a second part, the influence of the prior mentioned polyelectrolytes was investigated on the phase behaviour as well as on the properties of the inverse micellar region (L2 phase) of quaternary systems consisting of a surfactant, toluene-pentanol (1:1) and water. The majority of the present work has been made with the anionic surfactant sodium dodecylsulfate (SDS) and the cationic surfactant cetyltrimethylammonium bromide (CTAB) since they can interact with the oppositely charged polyelectrolytes and the microemulsions formed using these surfactants present a large water-in-oil region. Subsequently, the polymer-modified microemulsions were used as new templates for the synthesis of inorganic particles, ranging from metals to complex crystallites, of very small size. The water droplets can indeed act as nanoreactors for the nucleation and growth of the particles, and the added polymer can influence the droplet size, the droplet-droplet interactions, as well as the stability of the surfactant film by the formation of polymer-surfactant complexes. One further advantage of the polymer-modified microemulsions is the possibility to stabilize the primary formed nanoparticles via a polymer adsorption (steric and/or electrostatic stabilization). Thus, the polyelectrolyte-modified nanoparticles formed can be redispersed without flocculation after solvent evaporation. N2 - Die Bildung von Kolloiden durch kontrollierte Reduktion, durch Keimbildung und durch Wachstum anorganischer Precurser in unterschiedlichen Medien wird seit mehr als einem Jahrhundert intensiv beforscht. Vor kurzem hat die Herstellung ultrafeiner Partikel viel Aufmerksamkeit errungen, da sich hieraus vielversprechende neue Möglichkeiten für ein breites Spektrum an technischen Anwendungen (Nanotechnologie, elektrooptische Materialen, Pharmazeutik, usw.) ergeben. Das Interesse leitet sich von der weithin bekannten Tatsache ab, dass die Eigenschaften der „advanced materials“ von der Mikrostruktur der Probe deutlich abhängig sind. Die gezielte Steuerung der Größe, der Größenverteilung und der Morphologie der einzelnen Keime oder Kristallite ist von größter Wichtigkeit, um die gewünschten Eigenschaften zu erreichen. Verschiedene Methoden können für die Synthese von Nanopartikel verwendet werden. Einerseits kann eine Reduktion in verdünnten wässrigen oder alkoholischen Lösungen stattfinden, andererseits kann der Reduktionsprozess in einer Templatphase, z.B. in definierten Mikroemulsionströpfchen stattfinden. Die Stabilität der produzierten Nanopartikel hängt hauptsächlich von ihrer Oberflächenladung ab, welche durch schützende Komponenten zusätzlich beeinflusst werden kann. Verschiedene Arten von Polymeren, einschließlich Polyelektrolyte und amphiphile Blockcopolymere, können als solche Komponenten benutzt werden. Die Reduktion und Stabilisierung von Metallkolloiden in der wässrigen Lösung durch Addition von hydrophob modifizierten Polyelektrolyten werden bereits ausführlich studiert. Die verwendeten Polymere sind hydrophob modifizierte Derivate des Natrium-Polyacrylat, der Maleinsäure Copolymere sowie das verzweigte Poly(ethylenimin). Erstaunlicherweise genügt bereits die Anwesenheit die verwendeten Polyelektrolyte zu Reduzierung und Stabilisierung der Goldnanopartikel. Darüber hinaus wurde der Einfluss der hydrophoben Seitenkette des Polymer auf den Reduktions- und Stabilisierungsprozess bei unterschiedliche Reaktionstemperatur untersucht. In beiden Fällen können Metallnanopartikel kolloidaler Größe hergestellt werden, jedoch hängt die Größe und die Form der einzelnen Nanopartikel hauptsächlich vom dem zugefügten Polymer und vom verwendeten Temperaturverfahren ab. Im zweiten Teil wurde der Einfluss der vorher erwähnten Polyelektrolyte auf das Phaseverhalten sowie auf die Eigenschaften der inversen mizellaren Region (L2 Phase) der quaternären Systeme untersucht, die aus einem Tensid, Toluol-Pentanol – Gemisch (1:1) sowie Wasser bestehen. Dabei wurden hauptsächlich ionische Tenside, wie z.B. das anionische Natriumdodecylsulfate (SDS) und das kationische Cetyltrimethylammonium-bromid (CTAB) verwendet, da sie mit den geladenen Polyelektrolyten wechselwirken können. Darüber hinaus wurden die polymer-modifizierten Mikroemulsionen als neue Template für die Synthese von anorganischen Nanopartikeln verwendet. Die Wassertröpfchen können in der Tat als Nanoreaktoren für die Keimbildung und das Wachstum der Partikel dienen, und das zugefügte Polymer kann die Tröpfchengröße, die Tröpfchen-Tröpfchen Wechselwirkungen, sowie die Stabilität des Tensidfilms durch Polyelektrolyt-Tensid Komplexbildung beeinflussen. Ein weiterer Vorteil der polymer-modifizierten Mikroemulsionen ist die Stabilizierung der produzierten Primärteilchen über eine Polymeradsorption (durch sterische bzw. elektrostatische Stabilisierung), welche eine Redispergierung der Polyelektrolyte-modifiziert Nanopartikel, nach Lösungsmittel-verdampfung, ohne Aggregation der Partikel erlaubt. KW - Mikroemulsion KW - Nanopartikel KW - Polyelektrolyte KW - microemulsion KW - polyelectrolyte KW - nanoparticle Y1 - 2006 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-11670 ER -