TY - JOUR A1 - Morgner, Frank A1 - Bennemann, Mark A1 - Cywiński, Piotr J. A1 - Kollosche, Matthias A1 - Górski, Krzysztof A1 - Pietraszkiewicz, Marek A1 - Geßner, André A1 - Löhmannsröben, Hans-Gerd T1 - Elastic FRET sensors for contactless pressure measurement JF - RSC Advances : an international journal to further the chemical sciences N2 - Contactless pressure monitoring based on Forster resonance energy transfer between donor/acceptor pairs immobilized within elastomers is demonstrated. The donor/acceptor energy transfer is employed by dispersing terbium(III) tris[(2-hydroxybenzoyl)-2-aminoethyl] amine complex (LLC, donor) and CdSe/ZnS quantum dots (QD655, acceptor) in styrene-ethylene/buthylene-styrene (SEBS) and poly(dimethylsiloxane) (PDMS). The continuous monitoring of QD luminescence showed a reversible intensity change as the pressure signal is alternated between two stable states indicating a pressure sensitivity of 6350 cps kPa(-1). Time-resolved measurements show the pressure impact on the FRET signal due to an increase of decay time (270 ms up to 420 ms) for the donor signal and parallel drop of decay time (170 mu s to 155 mu s) for the acceptor signal as the net pressure applied. The LLC/QD655 sensors enable a contactless readout as well as space resolved monitoring to enable miniaturization towards smaller integrated stretchable opto-electronics. Elastic FRET sensors can potentially lead to developing profitable analysis systems capable to outdo conventional wired electronic systems (inductive, capacitive, ultrasonic and photoelectric sensors) especially for point-of-care diagnostics, biological monitoring required for wearable electronics. Y1 - 2017 U6 - https://doi.org/10.1039/c7ra06379b SN - 2046-2069 VL - 7 SP - 50578 EP - 50583 PB - RSC Publishing CY - Cambridge ER - TY - GEN A1 - Heyne, Benjamin A1 - Arlt, Kristin A1 - Geßner, André A1 - Richter, Alexander F. A1 - Döblinger, Markus A1 - Feldmann, Jochen A1 - Taubert, Andreas A1 - Wedel, Armin T1 - Mixed Mercaptocarboxylic Acid Shells Provide Stable Dispersions of InPZnS/ZnSe/ZnS Multishell Quantum Dots in Aqueous Media T2 - Postprints der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe N2 - Highly luminescent indium phosphide zinc sulfide (InPZnS) quantum dots (QDs), with zinc selenide/zinc sulfide (ZnSe/ZnS) shells, were synthesized. The QDs were modified via a post-synthetic ligand exchange reaction with 3-mercaptopropionic acid (MPA) and 11-mercaptoundecanoic acid (MUA) in different MPA:MUA ratios, making this study the first investigation into the effects of mixed ligand shells on InPZnS QDs. Moreover, this article also describes an optimized method for the correlation of the QD size vs. optical absorption of the QDs. Upon ligand exchange, the QDs can be dispersed in water. Longer ligands (MUA) provide more stable dispersions than short-chain ligands. Thicker ZnSe/ZnS shells provide a better photoluminescence quantum yield (PLQY) and higher emission stability upon ligand exchange. Both the ligand exchange and the optical properties are highly reproducible between different QD batches. Before dialysis, QDs with a ZnS shell thickness of ~4.9 monolayers (ML), stabilized with a mixed MPA:MUA (mixing ratio of 1:10), showed the highest PLQY, at ~45%. After dialysis, QDs with a ZnS shell thickness of ~4.9 ML, stabilized with a mixed MPA:MUA and a ratio of 1:10 and 1:100, showed the highest PLQYs, of ~41%. The dispersions were stable up to 44 days at ambient conditions and in the dark. After 44 days, QDs with a ZnS shell thickness of ~4.9 ML, stabilized with only MUA, showed the highest PLQY, of ~34%. T3 - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe - 1026 KW - quantum dots KW - cadmium-free KW - Cd-free KW - InP KW - InPZnS KW - multishell KW - mercaptocarboxylic acids KW - 3-mercaptopropionic acid KW - 11-mercaptoundecanoic acid KW - phase transfer KW - ligand exchange KW - aqueous dispersion KW - QDs Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-486032 SN - 1866-8372 IS - 1026 ER - TY - JOUR A1 - Heyne, Benjamin A1 - Arlt, Kristin A1 - Geßner, André A1 - Richter, Alexander F. A1 - Döblinger, Markus A1 - Feldmann, Jochen A1 - Taubert, Andreas A1 - Wedel, Armin T1 - Mixed Mercaptocarboxylic Acid Shells Provide Stable Dispersions of InPZnS/ZnSe/ZnS Multishell Quantum Dots in Aqueous Media JF - Nanomaterials N2 - Highly luminescent indium phosphide zinc sulfide (InPZnS) quantum dots (QDs), with zinc selenide/zinc sulfide (ZnSe/ZnS) shells, were synthesized. The QDs were modified via a post-synthetic ligand exchange reaction with 3-mercaptopropionic acid (MPA) and 11-mercaptoundecanoic acid (MUA) in different MPA:MUA ratios, making this study the first investigation into the effects of mixed ligand shells on InPZnS QDs. Moreover, this article also describes an optimized method for the correlation of the QD size vs. optical absorption of the QDs. Upon ligand exchange, the QDs can be dispersed in water. Longer ligands (MUA) provide more stable dispersions than short-chain ligands. Thicker ZnSe/ZnS shells provide a better photoluminescence quantum yield (PLQY) and higher emission stability upon ligand exchange. Both the ligand exchange and the optical properties are highly reproducible between different QD batches. Before dialysis, QDs with a ZnS shell thickness of ~4.9 monolayers (ML), stabilized with a mixed MPA:MUA (mixing ratio of 1:10), showed the highest PLQY, at ~45%. After dialysis, QDs with a ZnS shell thickness of ~4.9 ML, stabilized with a mixed MPA:MUA and a ratio of 1:10 and 1:100, showed the highest PLQYs, of ~41%. The dispersions were stable up to 44 days at ambient conditions and in the dark. After 44 days, QDs with a ZnS shell thickness of ~4.9 ML, stabilized with only MUA, showed the highest PLQY, of ~34%. KW - quantum dots KW - cadmium-free KW - Cd-free KW - InP KW - InPZnS KW - multishell KW - mercaptocarboxylic acids KW - 3-mercaptopropionic acid KW - 11-mercaptoundecanoic acid KW - phase transfer KW - ligand exchange KW - aqueous dispersion KW - QDs Y1 - 2020 U6 - https://doi.org/10.3390/nano10091858 SN - 2079-4991 VL - 10 IS - 9 PB - MDPI CY - Basel ER - TY - JOUR A1 - Tiseanu, Carmen A1 - Pârvulescu, Victor I. A1 - Kumke, Michael Uwe A1 - Dobroiu, Svako A1 - Geßner, André A1 - Simon, Simion T1 - Effects of support and ligand on the photoluminescence properties of siliceous grafted europium complexes N2 - Europium ions were introduced in SiO2 and MCM-41 via two different pathways: (1) grafting the europium complexes with two alkoxide structures, 3-(2-imidazolin-1-yl)-propyl-triethoxysilane (IPTES) and aminopropyltrimethoxysilane (APTMS), and (2) functionalization of the SiO2 support with silicon 4- carboxylbutyltriethoxide followed by subsequent addition of the europium ions. The new materials were characterized using nitrogen adsorption isotherms at -196 degrees C, thermogravimetric analysis, scanning electron microscopy, transmission electron microscopy, powder X-ray diffraction, Fourier transform infrared, NMR, DR-UV-vis, steady-state emission and excitation, and time-resolved photoluminescence spectroscopy. Spectral changes found in the time-resolved photoluminscence spectra strongly point to the distribution of europium ions on a range of environments in both SiO2 and MCM-41 supports. The average europium photoluminescence lifetimes decrease within the order: Eu3+-IPTES/SiO2 (550 mu s) > Eu3+-APTMS/SiO2 (425 mu s) > Eu3+-APTMS/MCM-41 (370 mu s) > Eu3+-IPTES/MCM-41 (320 mu s) > Eu3+-CABES/SiO2 (240 mu s). The photoluminescence quantum efficiency has the largest value, of 22%, for Eu3+-IPTES/SiO2, while the most reduced value, of 9%, was measured for Eu3+-CABES/SiO2. Y1 - 2009 UR - http://pubs.acs.org/journal/jpccck U6 - https://doi.org/10.1021/Jp808411e SN - 1932-7447 ER - TY - JOUR A1 - Tiseanu, Carmen A1 - Lorenz-Fonfria, Victor A. A1 - Geßner, André A1 - Kumke, Michael Uwe A1 - Gagea, Bogdan T1 - Comparative luminescence study of terbium-exchanged zeolites silylated with alkoxysilanes N2 - Terbium-exchanged ZSM-5, MOR and (H)BEA zeolites were silylated with phenyl-, vinyl- and hexadecyl trimethoxysilanes via a post-synthesis grafting. All samples were investigated by means of PXRD, FT-IR, TGA, physical adsorption, DR-UV-Vis and time-resolved photoluminescence spectroscopy. From the comparison of the photoluminescence decays of terbium-exchanged in parent (non-silylated) and silylated zeolites, it resulted that the silylation efficiency of the various alkoxysilanes is determined by the type of zeolite and follows the sequences: phenyl > vinyl > hexadecyl > parent for ZSM-5, hexadecyl a parts per thousand phenyl a parts per thousand vinyl > parent for MOR and hexadecyl > phenyl a parts per thousand vinyl > a parts per thousand parent for BEA zeolites, respectively. Y1 - 2009 UR - http://www.springerlink.com/content/100190 U6 - https://doi.org/10.1007/s10854-008-9597-1 SN - 0957-4522 ER -