TY - JOUR A1 - Wang, Weiwei A1 - Xu, Xun A1 - Li, Zhengdong A1 - Kratz, Karl A1 - Ma, Nan A1 - Lendlein, Andreas T1 - Modulating human mesenchymal stem cells using poly(n-butyl acrylate) networks in vitro with elasticity matching human arteries JF - Clinical hemorheology and microcirculation : blood flow and vessels N2 - Non-swelling hydrophobic poly(n-butyl acrylate) network (cPnBA) is a candidate material for synthetic vascular grafts owing to its low toxicity and tailorable mechanical properties. Mesenchymal stem cells (MSCs) are an attractive cell type for accelerating endothelialization because of their superior anti-thrombosis and immune modulatory function. Further, they can differentiate into smooth muscle cells or endothelial-like cells and secret pro-angiogenic factors such as vascular endothelial growth factor (VEGF). MSCs are sensitive to the substrate mechanical properties, with the alteration of their major cellular behavior and functions as a response to substrate elasticity. Here, we cultured human adipose-derived mesenchymal stem cells (hADSCs) on cPnBAs with different mechanical properties (cPnBA250, Young’s modulus (E) = 250 kPa; cPnBA1100, E = 1100 kPa) matching the elasticity of native arteries, and investigated their cellular response to the materials including cell attachment, proliferation, viability, apoptosis, senescence and secretion. The cPnBA allowed high cell attachment and showed negligible cytotoxicity. F-actin assembly of hADSCs decreased on cPnBA films compared to classical tissue culture plate. The difference of cPnBA elasticity did not show dramatic effects on cell attachment, morphology, cytoskeleton assembly, apoptosis and senescence. Cells on cPnBA250, with lower proliferation rate, had significantly higher VEGF secretion activity. These results demonstrated that tuning polymer elasticity to regulate human stem cells might be a potential strategy for constructing stem cell-based artificial blood vessels. KW - Poly(n-butyl acrylate) KW - mechanical property KW - vascular graft KW - mesenchymal stem cells KW - VEGF Y1 - 2019 U6 - https://doi.org/10.3233/CH-189418 SN - 1386-0291 SN - 1875-8622 VL - 71 IS - 2 SP - 277 EP - 289 PB - IOS Press CY - Amsterdam ER - TY - JOUR A1 - Wanjiku, Barbara A1 - Yamamoto, Kenji A1 - Klossek, Andre A1 - Schumacher, Fabian A1 - Pischon, Hannah A1 - Mundhenk, Lars A1 - Rancan, Fiorenza A1 - Judd, Martyna M. A1 - Ahmed, Muniruddin A1 - Zoschke, Christian A1 - Kleuser, Burkhard A1 - Rühl, Eckart A1 - Schäfer-Korting, Monika T1 - Qualifying X-ray and Stimulated Raman Spectromicroscopy for Mapping Cutaneous Drug Penetration JF - Analytical chemistry N2 - Research on topical drug delivery relies on reconstructed human skin (RHS) in addition to ex vivo human and animal skin, each with specific physiological features. Here, we compared the penetration of dexamethasone from an ethanolic hydroxyethyl cellulose gel into ex vivo human skin, murine skin, and RHS. For comprehensive insights into skin morphology and penetration enhancing mechanisms, scanning transmission X-ray microscopy (STXM), liquid chromatography tandem mass spectrometry (LC-MS/MS), and stimulated Raman spectromicroscopy (SRS) were combined. STXM offers high spatial resolution with label-free drug detection and is therefore sensitive to tissue damage. Despite differences in sample preparation and data analysis, the amounts of dexamethasone in RHS, detected and quantified by STXM and LC-MS/MS, were very similar and increased during the first 100 min of exposure. SRS revealed interactions between the gel and the stratum corneum or, more specifically, its protein and lipid structures. Similar to both types of ex vivo skin, higher protein-to-lipid ratios within the stratum corneum of RHS indicated reduced lipid amounts after 30 min of ethanol exposure. Extended ethanol exposure led to a continued reduction of lipids in the ex vivo matrixes, while protein integrity appeared to be compromised in RHS, which led to declining protein signals. In conclusion, LC-MS/MS proved the predictive capability of STXM for label-free drug detection. Combining STXM with SRS precisely dissected the penetration enhancing effects of ethanol. Further studies on topical drug delivery should consider the potential of these complementary techniques. Y1 - 2019 U6 - https://doi.org/10.1021/acs.analchem.9b00519 SN - 0003-2700 SN - 1520-6882 VL - 91 IS - 11 SP - 7208 EP - 7214 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Weis, Philipp A1 - Hess, Andreas A1 - Kircher, Gunnar A1 - Huang, Shilin A1 - Auernhammer, Günter K. A1 - Koynov, Kaloian A1 - Butt, Hans-Jürgen A1 - Wu, Si T1 - Effects of Spacers on Photoinduced Reversible Solid-to-Liquid Transitions of Azobenzene-Containing Polymers JF - Chemistry - a European journal N2 - Photoisomerization in some azobenzene-containing polymers (azopolymers) results in reversible solid-to-liquid transitions because trans- and cis-azopolymers have different glass transition temperatures. This property enables photoinduced healing and processing of azopolymers with high spatiotemporal resolution. However, a general lack of knowledge about the influence of the polymer structure on photoinduced reversible solid-to-liquid transitions hinders the design of such novel polymers. Herein, the synthesis and photoresponsive behavior of new azopolymers with different lengths of spacers between the polymer backbone and the azobenzene group on the side chain are reported. Azopolymers with no and 20 methylene spacers did not show photoinduced solid-to-liquid transitions. Azopolymers with 6 or 12 methylene spacers showed photoinduced solid-to-liquid transitions. This study demonstrates that spacers are essential for azopolymers with photoinduced reversible solid-to-liquid transitions, and thus, gives an insight into how to design azopolymers for photoinduced healing and processing. KW - azobenzenes KW - isomerization KW - photochemistry KW - polymers KW - self-healing Y1 - 2019 U6 - https://doi.org/10.1002/chem.201902273 SN - 0947-6539 SN - 1521-3765 VL - 25 IS - 46 SP - 10946 EP - 10953 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Wolf, Thomas J. A. A1 - Sanchez, David M. A1 - Yang, J. A1 - Parrish, R. M. A1 - Nunes, J. P. F. A1 - Centurion, M. A1 - Coffee, R. A1 - Cryan, J. P. A1 - Gühr, Markus A1 - Hegazy, Kareem A1 - Kirrander, Adam A1 - Li, R. K. A1 - Ruddock, J. A1 - Shen, Xiaozhe A1 - Vecchione, T. A1 - Weathersby, S. P. A1 - Weber, Peter M. A1 - Wilkin, K. A1 - Yong, Haiwang A1 - Zheng, Q. A1 - Wang, X. J. A1 - Minitti, Michael P. A1 - Martinez, Todd J. T1 - The photochemical ring-opening of 1,3-cyclohexadiene imaged by ultrafast electron diffraction JF - Nature chemistry N2 - The ultrafast photoinduced ring-opening of 1,3-cyclohexadiene constitutes a textbook example of electrocyclic reactions in organic chemistry and a model for photobiological reactions in vitamin D synthesis. Although the relaxation from the photoexcited electronic state during the ring-opening has been investigated in numerous studies, the accompanying changes in atomic distance have not been resolved. Here we present a direct and unambiguous observation of the ring-opening reaction path on the femtosecond timescale and subangstrom length scale using megaelectronvolt ultrafast electron diffraction. We followed the carbon-carbon bond dissociation and the structural opening of the 1,3-cyclohexadiene ring by the direct measurement of time-dependent changes in the distribution of interatomic distances. We observed a substantial acceleration of the ring-opening motion after internal conversion to the ground state due to a steepening of the electronic potential gradient towards the product minima. The ring-opening motion transforms into rotation of the terminal ethylene groups in the photoproduct 1,3,5-hexatriene on the subpicosecond timescale. KW - Organic chemistry KW - Photochemistry KW - Physical chemistry KW - Theoretical chemistry Y1 - 2019 U6 - https://doi.org/10.1038/s41557-019-0252-7 SN - 1755-4330 SN - 1755-4349 VL - 11 IS - 6 SP - 504 EP - 509 PB - Nature Publ. Group CY - London ER - TY - JOUR A1 - Xiong, Tao A1 - Saalfrank, Peter T1 - Vibrationally Broadened Optical Spectra of Selected Radicals and Cations Derived from Adamantane: A Time-Dependent Correlation Function Approach JF - The journal of physical chemistry : A, Molecules, spectroscopy, kinetics, environment & general theory N2 - Diamondoids are hydrogen-saturated molecular motifs cut out of diamond, forming a class of materials with tunable optoelectronic properties. In this work, we extend previous work on neutral, closed-shell diamondoids by computing with hybrid density functional theory and time-dependent correlation functions vibrationally broadened absorption spectra of cations and radicals derived from the simplest diamondoid, adamantane, namely, the neutral 1- and 2-adamantyl radicals (C10H15), the 1- and 2-adamantyl cations (C10H15+), and the adamantane radical cation (C10H16+). For selected cases, we also report vibrationally broadened emission, photoelectron, and resonance Raman spectra. Furthermore, the effect of the damping factor on the vibrational fine-structure is studied. The following trends are found: (1) Low-energy absorptions of the adamantyl radicals and cations, and of the adamantane cation, are all strongly red-shifted with respect to adamantane; (2) also, emission spectra are strongly red-shifted, whereas photoelectron spectra are less affected for the cases studied; (3) vibrational fine-structures are reduced compared to those of adamantane; (4) the spectroscopic signals of 1- and 2-adamantyl species are significantly different from each other; and (5) reducing the damping factor has only a limited effect on the vibrational fine-structure in most cases. This suggests that removing hydrogen atoms and/or electrons from adamantane leads to new optoelectronic properties, which should be detectable by vibronic spectroscopy. Y1 - 2019 U6 - https://doi.org/10.1021/acs.jpca.9b03305 SN - 1089-5639 SN - 1520-5215 VL - 123 IS - 41 SP - 8871 EP - 8880 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Yan, Runyu A1 - Josef, Elinor A1 - Huang, Haijian A1 - Leus, Karen A1 - Niederberger, Markus A1 - Hofmann, Jan P. A1 - Walczak, Ralf A1 - Antonietti, Markus A1 - Oschatz, Martin T1 - Understanding the charge storage mechanism to achieve high capacity and fast ion storage in sodium-ion capacitor anodes by using electrospun nitrogen-doped carbon fibers JF - Advanced functional materials N2 - Microporous nitrogen-rich carbon fibers (HAT-CNFs) are produced by electrospinning a mixture of hexaazatriphenylene-hexacarbonitrile (HAT-CN) and polyvinylpyrrolidone and subsequent thermal condensation. Bonding motives, electronic structure, content of nitrogen heteroatoms, porosity, and degree of carbon stacking can be controlled by the condensation temperature due to the use of the HAT-CN with predefined nitrogen binding motives. The HAT-CNFs show remarkable reversible capacities (395 mAh g(-1) at 0.1 A g(-1)) and rate capabilities (106 mAh g(-1) at 10 A g(-1)) as an anode material for sodium storage, resulting from the abundant heteroatoms, enhanced electrical conductivity, and rapid charge carrier transport in the nanoporous structure of the 1D fibers. HAT-CNFs also serve as a series of model compounds for the investigation of the contribution of sodium storage by intercalation and reversible binding on nitrogen sites at different rates. There is an increasing contribution of intercalation to the charge storage with increasing condensation temperature which becomes less active at high rates. A hybrid sodium-ion capacitor full cell combining HAT-CNF as the anode and salt-templated porous carbon as the cathode provides remarkable performance in the voltage range of 0.5-4.0 V (95 Wh kg(-1) at 0.19 kW kg(-1) and 18 Wh kg(-1) at 13 kW kg(-1)). KW - carbon fibers KW - nitrogen-doped carbon KW - sodium-ion capacitors KW - sodium storage mechanism Y1 - 2019 U6 - https://doi.org/10.1002/adfm.201902858 SN - 1616-301X SN - 1616-3028 VL - 29 IS - 26 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Yang, Guang A1 - Zheng, Wei A1 - Tao, Guoqing A1 - Wu, Libin A1 - Zhou, Qi-Feng A1 - Kochovski, Zdravko A1 - Ji, Tan A1 - Chen, Huaijun A1 - Li, Xiaopeng A1 - Lu, Yan A1 - Ding, Hong-ming A1 - Yang, Hai-Bo A1 - Chen, Guosong A1 - Jiang, Ming T1 - Diversiform and Transformable Glyco-Nanostructures Constructed from Amphiphilic Supramolecular Metallocarbohydrates through Hierarchical Self-Assembly: The Balance between Metallacycles and Saccharides JF - ACS nano N2 - During the past decade, self-assembly of saccharide-containing amphiphilic molecules toward bioinspired functional glycomaterials has attracted continuous attention due to their various applications in fundamental and practical areas. However, it still remains a great challenge to prepare hierarchical glycoassemblies with controllable and diversiform structures because of the complexity of saccharide structures and carbohydrate-carbohydrate interactions. Herein, through hierarchical self-assembly of modulated amphiphilic supramolecular metallocarbohydrates, we successfully prepared various well-defined glyco-nanostructures in aqueous solution, including vesicles, solid spheres, and opened vesicles depending on the molecular structures of metallocarbohydrates. More attractively, these glyco-nanostructures can further transform into other morphological structures in aqueous solutions such as worm-like micelles, tubules, and even tupanvirus-like vesicles (TVVs). It is worth mentioning that distinctive anisotropic structures including the opened vesicles (OVs) and TVVs were rarely reported in glycobased nano-objects. This intriguing diversity was mainly controlled by the subtle structural trade-off of the two major components of the amphiphiles, i.e., the saccharides and metallacycles. To further understand this precise structural control, molecular simulations provided deep physical insights on the morphology evolution and balancing of the contributions from saccharides and metallacycles. Moreover, the multivalency of glyco-nanostructures with different shapes and sizes was demonstrated by agglutination with a diversity of sugarbinding protein receptors such as the plant lectins Concanavalin A (ConA). This modular synthesis strategy provides access to systematic tuning of molecular structure and self-assembled architecture, which undoubtedly will broaden our horizons on the controllable fabrication of biomimetic glycomaterials such as biological membranes and supramolecular lectin inhibitors. KW - glycomaterials KW - diversiform structures KW - hierarchical self-assembly KW - metallocarbohydrates KW - anisotropic structures Y1 - 2019 U6 - https://doi.org/10.1021/acsnano.9b07134 SN - 1936-0851 SN - 1936-086X VL - 13 IS - 11 SP - 13474 EP - 13485 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Yu, Hongtao A1 - Quan, Ting A1 - Mei, Shilin A1 - Kochovski, Zdravko A1 - Huang, Wei A1 - Meng, Hong A1 - Lu, Yan T1 - Prompt Electrodeposition of Ni Nanodots on Ni Foam to Construct a High-Performance Water-Splitting Electrode BT - Efficient, Scalable, and Recyclable JF - Nano-Micro Letters N2 - HighlightsFacile electrodeposition for fabricating active Ni nanodots (NiNDs) on Ni foam (NF) is shown.Binder- and heteroatom-free recyclable NiO/NiNDs@NF electrodes are efficiently made.NiO/NiNDs@NF bifunctional catalytic electrodes are used for water splitting. AbstractIn past decades, Ni-based catalytic materials and electrodes have been intensively explored as low-cost hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) catalysts for water splitting. With increasing demands for Ni worldwide, simplifying the fabrication process, increasing Ni recycling, and reducing waste are tangible sustainability goals. Here, binder-free, heteroatom-free, and recyclable Ni-based bifunctional catalytic electrodes were fabricated via a one-step quick electrodeposition method. Typically, active Ni nanodot (NiND) clusters are electrodeposited on Ni foam (NF) in Ni(NO3)(2) acetonitrile solution. After drying in air, NiO/NiND composites are obtained, leading to a binder-free and heteroatom-free NiO/NiNDs@NF catalytic electrode. The electrode shows high efficiency and long-term stability for catalyzing hydrogen and oxygen evolution reactions at low overpotentials ((10)(HER)=119mV and (50)(OER)=360mV) and can promote water catalysis at 1.70V@10mAcm(-2). More importantly, the recovery of raw materials (NF and Ni(NO3)(2)) is quite easy because of the solubility of NiO/NiNDs composites in acid solution for recycling the electrodes. Additionally, a large-sized (S similar to 70cm(2)) NiO/NiNDs@NF catalytic electrode with high durability has also been constructed. This method provides a simple and fast technology to construct high-performance, low-cost, and environmentally friendly Ni-based bifunctional electrocatalytic electrodes for water splitting. KW - Electrodeposition KW - Ni nanodots KW - Bifunctional catalysts KW - Water splitting KW - Large-size Y1 - 2019 U6 - https://doi.org/10.1007/s40820-019-0269-x SN - 2311-6706 SN - 2150-5551 VL - 11 IS - 41 PB - Shanghai JIAO TONG univ press CY - Shanghai ER - TY - JOUR A1 - Yuan, Jinkai A1 - Neri, Wilfrid A1 - Zakri, Cecile A1 - Merzeau, Pascal A1 - Kratz, Karl A1 - Lendlein, Andreas A1 - Poulin, Philippe T1 - Shape memory nanocomposite fibers for untethered high-energy microengines JF - Science N2 - Classic rotating engines are powerful and broadly used but are of complex design and difficult to miniaturize. It has long remained challenging to make large-stroke, high-speed, high-energy microengines that are simple and robust. We show that torsionally stiffened shape memory nanocomposite fibers can be transformed upon insertion of twist to store and provide fast and high-energy rotations. The twisted shape memory nanocomposite fibers combine high torque with large angles of rotation, delivering a gravimetric work capacity that is 60 times higher than that of natural skeletal muscles. The temperature that triggers fiber rotation can be tuned. This temperature memory effect provides an additional advantage over conventional engines by allowing for the tunability of the operation temperature and a stepwise release of stored energy. Y1 - 2019 U6 - https://doi.org/10.1126/science.aaw3722 SN - 0036-8075 SN - 1095-9203 VL - 365 IS - 6449 SP - 155 EP - 158 PB - American Assoc. for the Advancement of Science CY - Washington ER - TY - JOUR A1 - Zaitsev-Doyle, John J. A1 - Puchert, Anke A1 - Pfeifer, Yannik A1 - Yan, Hao A1 - Yorke, Briony A. A1 - Müller-Werkmeister, Henrike A1 - Uetrecht, Charlotte A1 - Rehbein, Julia A1 - Huse, Nils A1 - Pearson, Arwen R. A1 - Sans, Marta T1 - Synthesis and characterisation of alpha-carboxynitrobenzyl photocaged l-aspartates for applications in time-resolved structural biology JF - RSC Advances N2 - We report a new synthetic route to a series of a-carboxynitrobenzyl photocaged L-aspartates for application in time-resolved structural biology. The resulting compounds were characterised in terms of UV/Vis absorption properties, aqueous solubility and stability, and photocleavage rates (tau = ms to ms) and quantum yields (phi = 0.05 to 0.14). Y1 - 2019 U6 - https://doi.org/10.1039/c9ra00968j SN - 2046-2069 VL - 9 IS - 15 SP - 8695 EP - 8699 PB - Royal Society of Chemistry CY - Cambridge ER - TY - JOUR A1 - Zehbe, Kerstin A1 - Lange, Alyna A1 - Taubert, Andreas T1 - Stereolithography Provides Access to 3D Printed lonogels with High Ionic Conductivity JF - Energy Fuels N2 - New ionogels (IGs) were prepared by combination of a series of sulfonate-based ionic liquids (ILs), 1-methyl-3-(4-sulfobutyl)imidazolium para-toluenesulfonate [BmimSO(3)][pTS], 1-methyl-1-butylpiperidiniumsulfonate para-toluenesul-fonate [BmpipSO(3)] [pTS], and 1-methyl-3-(4-sulfobutyl) imidazolium methylsulfonate [BmimSO(3)H][MeSO3] with a commercial stereolithography photoreactive resin. The article describes both the fundamental properties of the ILs and the resulting IGs. The IGs obtained from the ILs and the resin show high ionic conductivity of up to ca. 0.7.10(-4) S/cm at room temperature and 3.4-10(-3) S/cm at 90 degrees C. Moreover, the IGs are thermally stable to about 200 degrees C and mechanically robust. Finally, and most importantly, the article demonstrates that the IGs can be molded three-dimensionally using stereolithography. This provides, for the first time, access to IGs with complex 3D shapes with potential application in battery or fuel cell technology. Y1 - 2019 U6 - https://doi.org/10.1021/acs.energyfuels.9b03379 SN - 0887-0624 SN - 1520-5029 VL - 33 IS - 12 SP - 12885 EP - 12893 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Zhang, Pengfei A1 - Behl, Marc A1 - Peng, Xingzhou A1 - Balk, Maria A1 - Lendlein, Andreas T1 - Chemoresponsive Shape-Memory Effect of Rhodium-Phosphine Coordination Polymer Networks JF - Chemistry of materials : a publication of the American Chemical Society N2 - Chemoresponsive polymers are of technological significance for smart sensors or systems capable of molecular recognition. An important key requirement for these applications is the material’s structural integrity after stimulation. We explored whether covalently cross-linked metal ion–phosphine coordination polymers (MPN) can be shaped into any temporary shape and are capable of recovering from this upon chemoresponsive exposure to triphenylphosphine (Ph3P) ligands, whereas the MPN provide structural integrity. Depending on the metal-ion concentration used during synthesis of the MPN, the degree of swelling of the coordination polymer networks could be adjusted. Once the MPN was immersed into Ph3P solution, the reversible ligand-exchange reaction between the metal ions and the free Ph3P in solution causes a decrease of the coordination cross-link density in MPN again. The Ph3P-treated MPN was able to maintain its original shape, indicating a certain stability of shape even after stimulation. In this way, chemoresponsive control of the elastic properties (increase in volume and decrease of mechanical strength) of the MPN was demonstrated. This remarkable behavior motivated us to explore whether the MPN are capable of a chemoresponsive shape-memory effect. In initial experiments, shape fixity of around 60% and shape recovery of almost 90% were achieved when the MPN was exposed to Ph3P in case of rhodium. Potential applications for chemoresponsive shape-memory systems could be shapable semiconductors, e.g., for lighting or catalysts, which provide catalytic activity on demand. Y1 - 2019 U6 - https://doi.org/10.1021/acs.chemmater.9b00363 SN - 0897-4756 SN - 1520-5002 VL - 31 IS - 15 SP - 5402 EP - 5407 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Zhang, Quanchao A1 - Rudolph, Tobias A1 - Benitez, Alejandro J. A1 - Gould, Oliver E. C. A1 - Behl, Marc A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Temperature-controlled reversible pore size change of electrospun fibrous shape-memory polymer actuator based meshes JF - Smart materials and structures N2 - Fibrous membranes capable of dynamically responding to external stimuli are highly desirable in textiles and biomedical materials, where adaptive behavior is required to accommodate complex environmental changes. For example, the creation of fabrics with temperature-dependent moisture permeability or self-regulating membranes for air filtration is dependent on the development of materials that exhibit a reversible stimuli-responsive pore size change. Here, by imbuing covalently crosslinked poly(ε-caprolactone) (cPCL) fibrous meshes with a reversible bidirectional shape-memory polymer actuation (rbSMPA) we create a material capable of temperature-controlled changes in porosity. Cyclic thermomechanical testing was used to characterize the mechanical properties of the meshes, which were composed of randomly arranged microfibers with diameters of 2.3 ± 0.6 μm giving an average pore size of approx. 10 μm. When subjected to programming strains of εm = 300% and 100% reversible strain changes of εʹrev = 22% ± 1% and 6% ± 1% were measured, with switching temperature ranges of 10 °C–30 °C and 45 °C–60 °C for heating and cooling, respectively. The rbSMPA of cPCL fibrous meshes generated a microscale reversible pore size change of 11% ± 3% (an average of 1.5 ± 0.6 μm), as measured by scanning electron microscopy. The incorporation of a two-way shape-memory actuation capability into fibrous meshes is anticipated to advance the development and application of smart membrane materials, creating commercially viable textiles and devices with enhanced performance and novel functionality. KW - reversible shape-memory effect KW - fiber meshes KW - electrospinning Y1 - 2019 U6 - https://doi.org/10.1088/1361-665X/ab10a1 SN - 0964-1726 SN - 1361-665X VL - 28 IS - 5 PB - IOP Publ. Ltd. CY - Bristol ER - TY - JOUR A1 - Zhang, Su-Yun A1 - Guo, Wen-Bin A1 - Tang, Ying-Ying A1 - Xu, Jin-Qiu A1 - He, Zhang-Zhen T1 - Observation of Spin Relaxation in a Vanadate Chloride with Quasi-One-Dimensional Linear Chain JF - Crystal growth & design : integrating the fields of crystal engineering and crystal growth for the synthesis and applications of new materials N2 - A new cobalt(II) vanadate chloride, Pb2Co(OH)(V2O7)Cl, has been synthesized under mild hydrothermal conditions. It contains quasi-one-dimensional (1D) linear chains built by edge-sharing of (CoO6)-O-II octahedra. The cobalt(II) oxide chains are further interconnected by (V2O7)(4-) dimers into a three-dimensional (3D) anionic framework with Pb2+ and Cl- ions residing in Co4V8 12-member ring tunnels. The intrachain Co center dot center dot center dot Co distance is 3.041 angstrom, while the interchain distances are 8.742 and 9.256 angstrom. Magnetic measurements suggest the ferromagnetic intrachain and the antiferromagnetic interchain interactions with a specific value of J(intra)/J(inter) = 1.7 x 10(3). Zero-field heat capacity demonstrates the magnetic long-range ordering at 5.5 K. Alternating current (AC) magnetic susceptibility under zero external direct current (DC) fields displays two slow magnetic relaxations at low temperatures, giving characteristic relaxations (tau(0)) of 1.2(3) x 10(-12) and 1.9(4) x 10(-10) s with effective energy barriers (Delta(r)) of 76.1(2) and 48.4(5) K. The energy barrier between the spin up and spin-down states can be ascribed to the ferromagnetic spin chain and the Ising-like magnetic anisotropy in Pb2Co(OH)(V2O7)Cl. Y1 - 2019 U6 - https://doi.org/10.1021/acs.cgd.8b01839 SN - 1528-7483 SN - 1528-7505 VL - 19 IS - 4 SP - 2228 EP - 2234 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Zhang, Su-Yun A1 - Kochovski, Zdravko A1 - Lee, Hui-Chun A1 - Lu, Yan A1 - Zhang, Hemin A1 - Zhang, Jie A1 - Sun, Jian-Ke A1 - Yuan, Jiayin T1 - Ionic organic cage-encapsulating phase-transferable metal clusters JF - Chemical science N2 - Exploration of metal clusters (MCs) adaptive to both aqueous and oil phases without disturbing their size is promising for a broad scope of applications. The state-of-the-art approach via ligand-binding may perturb MCs' size due to varied metal–ligand binding strength when shuttling between solvents of different polarity. Herein, we applied physical confinement of a series of small noble MCs (<1 nm) inside ionic organic cages (I-Cages), which by means of anion exchange enables reversible transfer of MCs between aqueous and hydrophobic solutions without varying their ultrasmall size. Moreover, the MCs@I-Cage hybrid serves as a recyclable, reaction-switchable catalyst featuring high activity in liquid-phase NH3BH3 (AB) hydrolysis reaction with a turnover frequency (TOF) of 115 min−1. Y1 - 2019 U6 - https://doi.org/10.1039/c8sc04375b SN - 2041-6520 SN - 2041-6539 VL - 10 IS - 5 SP - 1450 EP - 1456 PB - Royal Society of Chemistry CY - Cambridge ER - TY - JOUR A1 - Zu, Fengshuo A1 - Amsalem, Patrick A1 - Egger, David A. A1 - Wang, Rongbin A1 - Wolff, Christian Michael A1 - Fang, Honghua A1 - Loi, Maria Antonietta A1 - Neher, Dieter A1 - Kronik, Leeor A1 - Duhm, Steffen A1 - Koch, Norbert T1 - Constructing the Electronic Structure of CH3NH3PbI3 and CH3NH3PbBr3 Perovskite Thin Films from Single-Crystal Band Structure Measurements JF - The journal of physical chemistry letters N2 - Photovoltaic cells based on halide perovskites, possessing remarkably high power conversion efficiencies have been reported. To push the development of such devices further, a comprehensive and reliable understanding of their electronic properties is essential but presently not available. To provide a solid foundation for understanding the electronic properties of polycrystalline thin films, we employ single-crystal band structure data from angle-resolved photoemission measurements. For two prototypical perovskites (CH3NH3PbBr3 and CH3NH3PbI3), we reveal the band dispersion in two high-symmetry directions and identify the global valence band maxima. With these benchmark data, we construct "standard" photoemission spectra from polycrystalline thin film samples and resolve challenges discussed in the literature for determining the valence band onset with high reliability. Within the framework laid out here, the consistency of relating the energy level alignment in perovskite-based photovoltaic and optoelectronic devices with their functional parameters is substantially enhanced. Y1 - 2019 U6 - https://doi.org/10.1021/acs.jpclett.8b03728 SN - 1948-7185 VL - 10 IS - 3 SP - 601 EP - 609 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Zude, Manuela A1 - Hashim, Norhashila A1 - Hass, Roland A1 - Polley, Nabarun A1 - Regen, Christian T1 - Validation study for measuring absorption and reduced scattering coefficients by means of laser-induced backscattering imaging JF - Postharvest Biology and Technology N2 - Decoupling of optical properties appears challenging, but vital to get better insight of the relationship between light and fruit attributes. In this study, nine solid phantoms capturing the ranges of absorption (μa) and reduced scattering (μs’) coefficients in fruit were analysed non-destructively using laser-induced backscattering imaging (LLBI) at 1060 nm. Data analysis of LLBI was carried out on the diffuse reflectance, attenuation profile obtained by means of Farrell’s diffusion theory either calculating μa [cm−1] and μs’ [cm−1] in one fitting step or fitting only one optical variable and providing the other one from a destructive analysis. The nondestructive approach was approved when calculating one unknown coefficient non-destructively, while no ability of the method was found to analysis both, μa and μs’, non-destructively. Setting μs’ according to destructive photon density wave (PDW) spectroscopy and fitting μa resulted in root mean square error (rmse) of 18.7% in comparison to fitting μs’ resulting in rmse of 2.6%, pointing to decreased measuring uncertainty, when the highly variable μa was known. The approach was tested on European pear, utilizing destructive PDW spectroscopy for setting one variable, while LLBI was applied for calculating the remaining coefficient. Results indicated that the optical properties of pear obtained from PDW spectroscopy as well as LLBI changed concurrently in correspondence to water content mainly. A destructive batch-wise analysis of μs’ and online analysis of μa may be considered in future developments for improved fruit sorting results, when considering fruit with high variability of μs’. KW - Absorption KW - European pear KW - Fruit quality KW - Phantoms KW - Reduced scattering coefficient KW - Scattering KW - Spatially resolved spectroscopy Y1 - 2019 U6 - https://doi.org/10.1016/j.postharvbio.2019.04.002 SN - 0925-5214 SN - 1873-2356 VL - 153 SP - 161 EP - 168 PB - Elsevier CY - Amsterdam ER -