TY - THES A1 - Haseeb, Haider T1 - Charge and heat transport across interfaces in nanostructured porous silicon T1 - Ladungs- und Wärmetransport über Grenzflächen in nanostrukturiertem porösem Silizium N2 - This thesis discusses heat and charge transport phenomena in single-crystalline Silicon penetrated by nanometer-sized pores, known as mesoporous Silicon (pSi). Despite the extensive attention given to it as a thermoelectric material of interest, studies on microscopic thermal and electronic transport beyond its macroscopic characterizations are rarely reported. In contrast, this work reports the interplay of both. PSi samples synthesized by electrochemical anodization display a temperature dependence of specific heat 𝐶𝑝 that deviates from the characteristic 𝑇^3 behaviour (at 𝑇<50𝐾). A thorough analysis reveals that both 3D and 2D Einstein and Debye modes contribute to this specific heat. Additional 2D Einstein modes (~3 𝑚𝑒𝑉) agree reasonably well with the boson peak of SiO2 in pSi pore walls. 2D Debye modes are proposed to account for surface acoustic modes causing a significant deviation from the well-known 𝑇^3 dependence of 𝐶𝑝 at 𝑇<50𝐾. A novel theoretical model gives insights into the thermal conductivity of pSi in terms of porosity and phonon scattering on the nanoscale. The thermal conductivity analysis utilizes the peculiarities of the pSi phonon dispersion probed by the inelastic neutron scattering experiments. A phonon mean-free path of around 10 𝑛𝑚 extracted from the presented model is proposed to cause the reduced thermal conductivity of pSi by two orders of magnitude compared to p-doped bulk Silicon. Detailed analysis indicates that compound averaging may cause a further 10-50% reduction. The percolation threshold of 65% for thermal conductivity of pSi samples is subsequently determined by employing theoretical effective medium models. Temperature-dependent electrical conductivity measurements reveal a thermally activated transport process. A detailed analysis of the activation energy 𝐸𝐴𝜎 in the thermally activated transport exhibits a Meyer Neldel compensation rule between different samples that originates in multi-phonon absorption upon carrier transport. Activation energies 𝐸𝐴𝑆 obtained from temperature-dependent thermopower measurements provide further evidence for multi-phonon assisted hopping between localized states as a dominant charge transport mechanism in pSi, as they systematically differ from the determined 𝐸𝐴𝜎 values. N2 - Diese Dissertation befasst sich mit Wärme- und Ladungstransportphänomenen in mesoporösem Silizium (pSi) oder etwas genauer in einkristallinem Silizium, welches mit nanometergroßen Poren durchsetzt ist. Trotz der großen Aufmerksamkeit, die diesem thermoelektrischen Material zuteil wird, wird nur selten über Studien zum mikroskopischen thermischen und elektronischen Transport jenseits seiner makroskopischen Charakterisierung berichtet. Im Gegensatz dazu wird in dieser Studie das Zusammenspiel von beidem untersucht. PSi-Proben, die durch elektrochemische Anodisierung synthetisiert wurden, zeigen eine Temperaturabhängigkeit der spezifischen Wärme 𝐶𝑝, die vom charakteristischen 𝑇3 Verhalten (bei 𝑇<50𝐾) abweicht. Eine gründliche Analyse zeigt, dass sowohl 3D- als auch 2D-Einstein- und Debye-Moden zu dieser spezifischen Wärme beitragen. Zusätzliche 2D-Einstein-Moden (~3 𝑚𝑒𝑉) stimmen gut mit dem Bosonen-Peak von SiO2 in teilweise oxidierten pSi-Porenwänden überein. 2D-Debye-Moden werden vorgeschlagen, um akustische Oberflächenmoden zu erklären, die eine signifikante Abweichung von der bekannten 𝑇3Abhängigkeit von 𝐶𝑝 bei 𝑇<50𝐾 verursachen. Ein neuartiges theoretisches Modell gibt Einblicke in die Wärmeleitfähigkeit von pSi in Bezug auf Porosität und Phononenstreuung auf der Nanoskala. Die Analyse der Wärmeleitfähigkeit nutzt die Besonderheiten der pSi-Phononendispersion, die durch Experimente mit inelastischer Neutronenstreuung untersucht wurden. Ein mittlerer freier Weg der Phononen von etwa 10 𝑛𝑚, der aus dem vorgestellten Modell extrahiert wurde, wird als Ursache für die um zwei Größenordnungen geringere Wärmeleitfähigkeit von pSi im Vergleich zu p-dotiertem Silizium vorgeschlagen. Eine detaillierte Analyse zeigt, dass die Porosität selbst eine weitere Verringerung der Wärmeleitfähigkeit um 10-50% verursachen kann. Die Perkolationsschwelle von 65 % für die Wärmeleitfähigkeit von pSi-Proben wird anschließend mit Hilfe eines theoretischen Ansatzes für effektive Medien bestimmt. Temperaturabhängige Messungen der elektrischen Leitfähigkeit lassen einen thermisch aktivierten Transportprozess erkennen. Eine detaillierte Analyse der Aktivierungsenergie 𝐸𝐴𝜎 im thermisch aktivierten Transport zeigt eine Meyer-Neldel-Kompensationsregel zwischen verschiedenen Proben, die auf Multiphononenabsorption beim Ladungsträgertransport zurückzuführen ist. Aktivierungsenergien 𝐸𝐴𝑆, die aus temperaturabhängigen Seebeck-Messungen gewonnen wurden, liefern weitere Beweise für Multiphononen-unterstütztes Springen zwischen lokalisierten Zuständen als dominanten Ladungstransportmechanismus in pSi, da sie sich systematisch von den ermittelten 𝐸𝐴𝜎 Werten unterscheiden. KW - mesoporous KW - silicon KW - Meyer-Neldel-rule KW - nanomaterials KW - Meyer-Neldel-Regel KW - mesoporös KW - Nanomaterialien KW - Silizium Y1 - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-611224 ER - TY - THES A1 - Borisova, Dimitriya T1 - Feedback active coatings based on mesoporous silica containers T1 - Rückkopplungsaktive Beschichtungen basierend auf mesoporösen Silika-Behältern N2 - Metalle werden oft während ihrer Anwendung korrosiven Bedingungen ausgesetzt, was ihre Alterungsbeständigkeit reduziert. Deswegen werden korrosionsanfällige Metalle, wie Aluminiumlegierungen mit Schutzbeschichtungen versehen, um den Korrosionsprozess aktiv oder passiv zu verhindern. Die klassischen Schutzbeschichtungen funktionieren als physikalische Barriere zwischen Metall und korrosiver Umgebung und bieten einen passiven Korrosionsschutz nur, wenn sie unbeschädigt sind. Im Gegensatz dazu kann die Korrosion auch im Fall einer Beschädigung mittels aktiver Schutzbeschichtungen gehemmt werden. Chromathaltige Beschichtungen bieten heutzutage den besten aktiven Korrosionsschutz für Aluminiumlegierungen. Aufgrund ihrer Giftigkeit wurden diese weltweit verboten und müssen durch neue umweltfreundliche Schutzbeschichtungen ersetzt werden. Ein potentieller Ersatz sind Schutzbeschichtungen mit integrierten Nano- und Mikrobehältern, die mit ungiftigem Inhibitor gefüllt sind. In dieser Arbeit werden die Entwicklung und Optimierung solcher aktiver Schutzbeschichtungen für die industriell wichtige Aluminiumlegierung AA2024-T3 dargestellt Mesoporöse Silika-Behälter wurden mit dem ungiftigen Inhibitor (2-Mercaptobenzothiazol) beladen und dann in die Matrix anorganischer (SiOx/ZrOx) oder organischer (wasserbasiert) Schichten dispergiert. Zwei Sorten von Silika-Behältern mit unterschiedlichen Größen (d ≈ 80 and 700 nm) wurden verwendet. Diese haben eine große spezifische Oberfläche (≈ 1000 m² g-1), eine enge Porengrößenverteilung mit mittlerer Porenweite ≈ 3 nm und ein großes Porenvolumen (≈ 1 mL g-1). Dank dieser Eigenschaften können große Inhibitormengen im Behälterinneren adsorbiert und gehalten werden. Die Inhibitormoleküle werden bei korrosionsbedingter Erhöhung des pH-Wertes gelöst und freigegeben. Die Konzentration, Position und Größe der integrierten Behälter wurden variiert um die besten Bedingungen für einen optimalen Korrosionsschutz zu bestimmen. Es wurde festgestellt, dass eine gute Korrosionsschutzleistung durch einen Kompromiss zwischen ausreichender Inhibitormenge und guten Barriereeigenschaften hervorgerufen wird. Diese Studie erweitert das Wissen über die wichtigsten Faktoren, die den Korrosionsschutz beeinflussen. Somit wurde die Entwicklung effizienter, aktiver Schutzbeschichtungen ermöglicht, die auf mit Inhibitor beladenen Behältern basieren. N2 - Metals are often used in environments that are conducive to corrosion, which leads to a reduction in their mechanical properties and durability. Coatings are applied to corrosion-prone metals such as aluminum alloys to inhibit the destructive surface process of corrosion in a passive or active way. Standard anticorrosive coatings function as a physical barrier between the material and the corrosive environment and provide passive protection only when intact. In contrast, active protection prevents or slows down corrosion even when the main barrier is damaged. The most effective industrially used active corrosion inhibition for aluminum alloys is provided by chromate conversion coatings. However, their toxicity and worldwide restriction provoke an urgent need for finding environmentally friendly corrosion preventing systems. A promising approach to replace the toxic chromate coatings is to embed particles containing nontoxic inhibitor in a passive coating matrix. This work presents the development and optimization of effective anticorrosive coatings for the industrially important aluminum alloy, AA2024-T3 using this approach. The protective coatings were prepared by dispersing mesoporous silica containers, loaded with the nontoxic corrosion inhibitor 2-mercaptobenzothiazole, in a passive sol-gel (SiOx/ZrOx) or organic water-based layer. Two types of porous silica containers with different sizes (d ≈ 80 and 700 nm, respectively) were investigated. The studied robust containers exhibit high surface area (≈ 1000 m² g-1), narrow pore size distribution (dpore ≈ 3 nm) and large pore volume (≈ 1 mL g-1) as determined by N2 sorption measurements. These properties favored the subsequent adsorption and storage of a relatively large amount of inhibitor as well as its release in response to pH changes induced by the corrosion process. The concentration, position and size of the embedded containers were varied to ascertain the optimum conditions for overall anticorrosion performance. Attaining high anticorrosion efficiency was found to require a compromise between delivering an optimal amount of corrosion inhibitor and preserving the coating barrier properties. This study broadens the knowledge about the main factors influencing the coating anticorrosion efficiency and assists the development of optimum active anticorrosive coatings doped with inhibitor loaded containers. KW - Korrosion KW - Beschichtungen KW - Aluminiumlegierung KW - Silika KW - Nanopartikel KW - mesoporös KW - corrosion KW - coating KW - aluminum alloy KW - silica nanoparticles KW - mesoporous Y1 - 2012 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-63505 ER - TY - THES A1 - Göbel, Ronald T1 - Hybridmaterialien aus mesoporösen Silica und ionischen Flüssigkeiten T1 - Hybrid materials of mesoporous silica and ionic liquids N2 - Die vorliegende Arbeit beschäftigt sich mit der Synthese und Charakterisierung mesoporöser monolithischer Silica und deren Hybridmaterialien mit Ionischen Flüssigkeiten (ILs, ionic liquids). Zur Synthese der Silicaproben wurde ein Sol-Gel-Verfahren, ausgehend von einer Präkursorverbindung wie Tetramethylorthosilicat angewendet. Der Katalysator mit der geringsten Basizität führte zum Material mit der kleinsten Porengröße und der größten spezifischen Oberfläche. Eine Kombination von porösen Silica mit ILs führt zur Materialklasse der Silica-Ionogele. Diese Hybridmaterialien verbinden die Eigenschaften eines porösen Festkörpers mit denen einer IL (Leitfähigkeit, weites elektrochemisches Fenster, gute thermische Stabilität) und bieten vielfältige Einsatzmöglichkeiten z.B. in der Katalyse- Solar- und Sensortechnik. Um diese Materialien für ihren Verwendungszweck zu optimieren, bedarf es deren umfassenden Charakterisierung. Daher wurde in der vorliegenden Arbeit das thermische Verhalten von Silica-Ionogelen unter Verwendung verschiedener 1-Ethyl-3-methylimidazolium [Emim]-basierter ILs untersucht. Interessanterweise zeigen die untersuchten ILs deutliche Änderungen in ihrem thermischen Verhalten, wenn diese in porösen Materialien eingeschlossen werden (Confinement). Während sich die untersuchten reinen ILs durch klar unterscheidbare Phasenübergänge auszeichnen, konnten für die entsprechenden Hybridmaterialien deutlich schwächer ausgeprägte Übergänge beobachtet werden. Einzelne Phasenübergänge wurden unterdrückt (Glas- und Kristallisationsübergänge), während z.B. Schmelzübergänge in verbreiterten Temperaturbereichen, zum Teil als einzeln getrennte Schmelzpeaks beobachtet wurden. Diese Untersuchungen belegen deutliche Eigenschaftsänderungen der ILs in eingeschränkten Geometrien. Über Festkörper-NMR-Spektroskopie konnte außerdem gezeigt werden, daß die ILs in den mesoporösen Silicamaterialien eine unerwartet hohe Mobilität aufweisen. Die ILs können als quasi-flüssig bezeichnet werden und zeigen die nach bestem Wissen höchste Mobilität, die bisher für vergleichbare Hybridmaterialien beobachtet wurde. Durch Verwendung von funktionalisierten Präkursoren, sowie der Wahl der Reaktionsbedingungen, kann die Oberfläche der Silicamaterialien chemisch funktionalisiert werden und damit die Materialeigenschaften in der gewünschten Weise beeinflußt werden. In der vorliegenden Arbeit wurde der Einfluß der Oberflächenfunktionalität auf das thermische Verhalten hin untersucht. Dazu wurden zwei verschiedene Möglichkeiten der Funktionalisierung angewendet und miteinander verglichen. Bei der in-situ-Funktionalisierung wird die chemische Funktionalität während der Sol-Gel-Synthese über ein entsprechend funktionalisiertes Silan mit in das Silicamaterial einkondensiert. Eine postsynthetische Funktionalisierung erfolgt durch Reaktion der Endgruppen eines Silicamaterials mit geeigneten Reaktionspartnern. Um den Einfluß der physikalischen Eigenschaften der Probe auf die Reaktion zu untersuchen, wurden pulverisierte und monolithische Silicamaterialien miteinander verglichen. Im letzten Teil der Arbeit wurde die Vielfältigkeit, mit der Silicamaterialien postsynthetisch funktionalisiert werden können demonstriert. Durch die Kenntnis von Struktur-Eigenschaftsbeziehungen können die Eigenschaften von Silica-Ionogelen durch die geeignete Kombination von fester und mobiler Phase in der gewünschten Weise verändert werden. Die vorliegende Arbeit soll einen Beitrag zur Untersuchung dieser Beziehungen leisten, um das Potential dieser interessanten Materialien für Anwendungen nutzen zu können. N2 - This work describes the synthesis and characterization of mesoporous monolithic silica and its hybrid materials with ionic liquids (ILs). For synthesis of the silica samples a sol-gel method was used. The catalyst with the weakest basicity leads to the material with the smallest pore size and the largest specific surface area. Combination of porous silica with ILs yields silica-ionogels. These hybrid materials combine the properties of porous solids with the properties of ILs (which is e.g. high conductivity, wide electrochemical stability window, and good thermal stability) and therefore offer a variety of possible applications like catalysis, solar and sensing. To optimize these materials for specific applications there is a need to understand their structure-composition-property relations. For this reason the thermal behavior of silica-ionogels was studied using different 1-ethyl-3-methylimidazolium [Emim]-based ILs. Interestingly the ILs show a clear change in their thermal behavior upon confinement in porous silica. Whereas the pure ILs show distinct phase transitions, the hybrid materials exhibit considerably weaker phase transitions. Phase transitions are suppressed (glass- and crystallization phase transitions); melting transitions show multiple melting peaks. Furthermore solid-state NMR also shows that ILs in mesoporous silica exhibit unusual high mobility. The confined ILs can therefore be classified as quasi-liquid and represents to our best knowledge the highest mobility observed so far in ionogels. By using functionalized silane precursors and different reaction conditions the silica surface was chemically functionalized which further changes the material properties. In a final approach a post-synthetic functionalization was performed by reaction of the selected groups of a silica material with suitable reactants. To study the effect of the physical appearance on the characteristics of the final material, powdered and monolithic samples were studied. In the last part of the work the versatility of post-synthetic silica functionalization was demonstrated. The current work contributes to a better understanding of structure-property correlations, to improve the potential of these interesting materials for possible applications. KW - Silica KW - ionische Flüssigkeiten KW - mesoporös KW - Hybridmaterialien KW - Sol-Gel KW - silica KW - ionic liquids KW - mesoporous KW - hybrid materials KW - sol-gel Y1 - 2011 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-54022 ER -