TY - JOUR A1 - Schöne, Anne-Christin A1 - Roch, Toralf A1 - Schulz, Burkhard A1 - Lendlein, Andreas T1 - Evaluating polymeric biomaterial-environment interfaces by Langmuir monolayer techniques JF - Interface : journal of the Royal Society N2 - Polymeric biomaterials are of specific relevance in medical and pharmaceutical applications due to their wide range of tailorable properties and functionalities. The knowledge about interactions of biomaterials with their biological environment is of crucial importance for developing highly sophisticated medical devices. To achieve optimal in vivo performance, a description at the molecular level is required to gain better understanding about the surface of synthetic materials for tailoring their properties. This is still challenging and requires the comprehensive characterization of morphological structures, polymer chain arrangements and degradation behaviour. The review discusses selected aspects for evaluating polymeric biomaterial-environment interfaces by Langmuir monolayer methods as powerful techniques for studying interfacial properties, such as morphological and degradation processes. The combination of spectroscopic, microscopic and scattering methods with the Langmuir techniques adapted to polymers can substantially improve the understanding of their in vivo behaviour. KW - Langmuir monolayer KW - biodegradable polymers KW - air - water interface KW - protein Langmuir layers Y1 - 2017 U6 - https://doi.org/10.1098/rsif.2016.1028 SN - 1742-5689 SN - 1742-5662 VL - 14 PB - Royal Society CY - London ER - TY - JOUR A1 - Schöne, Anne-Christin A1 - Richau, Klaus A1 - Kratz, Karl A1 - Schulz, Burkhard A1 - Lendlein, Andreas T1 - Influence of Diurethane Linkers on the Langmuir Layer Behavior of Oligo[(rac-lactide)-co-glycolide]-based Polyesterurethanes JF - Macromolecular rapid communications N2 - Three oligo[(rac-lactide)-co-glycolide] based polyesterurethanes (OLGA-PUs) containing different diurethane linkers are investigated by the Langmuir monolayer technique and compared to poly[(rac-lactide)-co-glycolide] (PLGA) to elucidate the influence of the diurethane junction units on hydrophilicity and packing motifs of these polymers at the air-water interface. The presence of diurethane linkers does not manifest itself in the Langmuir layer behavior both in compression and expansion experiments when monomolecular films of OLGA-PUs are spread on the water surface. However, the linker retard the evolution of morphological structures at intermediate compression level under isobaric conditions (with a surface pressure greater than 11 mN m(-1)) compared to the PLGA, independent on the chemical structure of the diurethane moiety. The layer thicknesses of both OLGA-PU and PLGA films decrease in the high compression state with decreasing surface pressure, as deduced from ellipsometric data. All films must be described with the effective medium approximation as water swollen layers. KW - Brewster angle microscopy KW - Langmuir monolayer KW - poly[(rac-lactide)-co-glycolide] KW - polyesterurethanes KW - spectroscopic ellipsometry Y1 - 2015 U6 - https://doi.org/10.1002/marc.201500316 SN - 1022-1336 SN - 1521-3927 VL - 36 IS - 21 SP - 1910 EP - 1915 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Rottke, Falko O. A1 - Schulz, Burkhard A1 - Richau, Klaus A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - An ellipsometric approach towards the description of inhomogeneous polymer-based Langmuir layers JF - Beilstein journal of nanotechnology N2 - The applicability of nulling-based ellipsometric mapping as a complementary method next to Brewster angle microscopy (BAM) and imaging ellipsometry (IE) is presented for the characterization of ultrathin films at the air-water interface. First, the methodology is demonstrated for a vertically nonmoving Langmuir layer of star-shaped, 4-arm poly(omega-pentadecalactone) (PPDL-D4). Using nulling-based ellipsometric mapping, PPDL-D4-based inhomogeneously structured morphologies with a vertical dimension in the lower nm range could be mapped. In addition to the identification of these structures, the differentiation between a monolayer and bare water was possible. Second, the potential and limitations of this method were verified by applying it to more versatile Langmuir layers of telechelic poly[(rac-lactide)-co-glycolide]-diol (PLGA). All ellipsometric maps were converted into thickness maps by introduction of the refractive index that was derived from independent ellipsometric experiments, and the result was additionally evaluated in terms of the root mean square roughness, R-q. Thereby, a three-dimensional view into the layers was enabled and morphological inhomogeneity could be quantified. KW - ellipsometric mapping KW - Langmuir monolayer KW - polyester KW - root mean square roughness KW - spectroscopic ellipsometry Y1 - 2016 U6 - https://doi.org/10.3762/bjnano.7.107 SN - 2190-4286 VL - 7 SP - 1156 EP - 1165 PB - Beilstein-Institut zur Förderung der Chemischen Wissenschaften CY - Frankfurt, Main ER - TY - JOUR A1 - Machatschek, Rainhard Gabriel A1 - Lendlein, Andreas T1 - Fundamental insights in PLGA degradation from thin film studies JF - Journal of controlled release : official journal of the Controlled Release Society and of the Japanese Society of Drug Delivery Systems N2 - Poly(lactide-co-glycolide)s are commercially available degradable implant materials, which are typically selected based on specifications given by the manufacturer, one of which is their molecular weight. Here, we address the question whether variations in the chain length and their distribution affect the degradation behavior of Poly[(rac-lactide)-co-glycolide]s (PDLLGA). The hydrolysis was studied in ultrathin films at the air-water interface in order to rule out any morphological effects. We found that both for purely hydrolytic degradation as well as under enzymatic catalysis, the molecular weight has very little effect on the overall degradation kinetics of PDLLGAs. The quantitative analysis suggested a random scission mechanism. The monolayer experiments showed that an acidic micro-pH does not accelerate the degradation of PDLLGAs, in contrast to alkaline conditions. The degradation experiments were combined with interfacial rheology measurements, which showed a drastic decrease of the viscosity at little mass loss. The extrapolated molecular weight behaved similar to the viscosity, dropping to a value near to the solubility limit of PDLLGA oligomers before mass loss set in. This observation suggests a solubility controlled degradation of PDLLGA. Conclusively, the molecular weight affects the degradation of PDLLGA devices mostly in indirect ways, e.g. by determining their morphology and porosity during fabrication. Our study demonstrates the relevance of the presented Langmuir degradation method for the design of controlled release systems. KW - PDLLGA KW - Degradation KW - Langmuir monolayer Y1 - 2019 U6 - https://doi.org/10.1016/j.jconrel.2019.12.044 SN - 0168-3659 SN - 1873-4995 VL - 319 SP - 276 EP - 284 PB - Elsevier CY - New York ER -