TY - JOUR A1 - Wang, Jingwen A1 - Rychkov, Dmitry A1 - Nguyen, Quyet Doan A1 - Gerhard, Reimund T1 - Unexpected bipolar space-charge polarization across transcrystalline interfaces in polypropylene electret films JF - Journal of applied physics N2 - A double-layer transcrystalline polypropylene (PP) film with a flat central interface layer between its two transcrystalline layers is obtained by recrystallization from the melt between two polytetrafluoroethylene (PTFE) surfaces on both sides of the PP film. Its electret properties are studied and compared with those of a single-layer transcrystalline PP film re-crystallized in contact with only one PTFE surface. Within experimental uncertainty, the two types of transcrystalline films exhibit the same thermal properties and crystallinities. After thermal poling, however, two hetero-charge layers of opposite polarity are found on the internal interfaces of the double-layer transcrystalline films and may together be considered as micrometer-sized dipoles. The unexpected phenomenon does not occur in single-layer transcrystalline samples without a central interface layer, suggesting that the interfaces between the transcrystalline layers and the micrometer-thick central interface layer may be the origin of deeper traps rather than the crystalline structures in the transcrystallites or the spherulites. The origin of the interfacial charges was also studied by means of an injection-blocking charging method, which revealed that intrinsic charge carriers introduced during recrystallization are most likely responsible for the interfacial charges. It is fascinating that a material as familiar as PP can exhibit such intriguing properties with a special bipolar space-charge polarization across the central interface layer after quasi-epitaxial surface moulding into a double-layer transcrystalline form. In addition to applications in electret (micro-)devices for electro-mechanical transduction, the highly ordered structures may also be employed as a new paradigm for studying charge storage and transport in polymer electrets and in dielectrics for DC electrical insulation. Y1 - 2020 U6 - https://doi.org/10.1063/5.0022071 SN - 0021-8979 SN - 1089-7550 VL - 128 IS - 13 PB - American Institute of Physics, AIP CY - Melville, NY ER - TY - JOUR A1 - Wang, Jingwen A1 - Rychkov, Dmitry A1 - Gerhard, Reimund T1 - Space-charge electret properties of polypropylene films with transcrystalline or spherulitic structures BT - a comparison of functionalities at interfaces JF - Journal of applied physics : AIP's archival journal for significant new results in applied physics / publ. by the American Institute of Physics N2 - Spherulite-related space-charge electret properties of polypropylene (PP) have been widely discussed in the past decades. In the present paper, a less-common crystalline structure in PP-transcrystalline PP-is studied regarding its electret behavior in comparison with the typical spherulitic morphology. Polarized light microscopy and differential scanning calorimetry were employed to characterize the crystallite types and crystallinities of transcrystalline and spherulitic PP. Their electret functionality is investigated by means of thermally stimulated discharge experiments, where the cross-over phenomenon is observed on transcrystalline PP films, whereas surface-potential saturation and undercharging on the surface occur on the spherulitic samples. Besides, an asymmetrical behavior of positive and negative surface-charge stabilities is found on PP with spherulites, the negatively charged spherulitic surfaces show a better charge stability. It is shown that PP electrets are very sensitive to changes in the microscopic crystalline structures and their interfaces as well as in the molecular conformations controlled through adjustments of the respective processing steps. In addition, surface and bulk nanocomposites of PP or low-density polyethylene with inorganic particles are included in the comparison. In view of recent developments in the areas of PP-based electret-fiber filters and cellular-foam ferroelectrets, the observed changes in the charge-storage properties may have particular relevance, as the required film, fiber, or foam processing might significantly modify crystalline morphologies and nano-scale interfaces in PP electrets. Limitations in the charge-storage capabilities of interface structures may also be of interest in the context of high-voltage electrical-insulation materials where reduced space-charge accumulation and slightly increased charge transport can be advantageous. Y1 - 2021 U6 - https://doi.org/10.1063/5.0039867 SN - 0021-8979 SN - 1089-7550 VL - 129 IS - 6 PB - American Institute of Physics CY - Melville ER - TY - JOUR A1 - Wang, Jingwen A1 - Rychkov, Dmitry A1 - Nguyen, Quyet Doan A1 - Gerhard, Reimund T1 - The influence of orthophosphoric-acid surface modification on charge-storage enhancement in polypropylene electrets JF - Journal of applied physics N2 - Bipolar electrets from polypropylene (PP) are essential, e.g., in electret air filters and in cellular-foam ferroelectrets. Therefore, the mechanism of surface-charge stability enhancement on PP electrets via orthophosphoric-acid surface treatment is investigated in detail. It is shown that the significant charge-stability enhancement can be mainly attributed to deeper surface traps originating from deposited chemicals and topographic features on the modified surfaces. Thermally stimulated discharge of chemically treated and non-treated PP films with different surface-charge densities is used to test the limits of the newly formed deep traps in terms of the capacity for hosting surface charges. When the initial surface-charge density is very high, more charges are forced into shallower original traps on the surface or in the bulk of the treated PP samples, reducing the effect of the deeper surface traps brought by the surface modification. The well-known crossover phenomenon (of the surface-charge decay curves) has been observed between modified PP electrets charged to +/- 2kV and to +/- 3kV. Acoustically probed charge distributions in the thickness direction of PP electrets at different stages of thermal discharging indicate that the deep surface trapping sites may have preference for negative charges, resulting in the observed asymmetric charge stability of the modified PP films. Y1 - 2020 U6 - https://doi.org/10.1063/5.0013805 SN - 0021-8979 SN - 1089-7550 VL - 128 IS - 3 PB - American Institute of Physics CY - Melville ER - TY - GEN A1 - Wang, Jingwen A1 - Rychkov, Dmitry A1 - Gerhard, Reimund T1 - Influence of Charge Density on Charge Decay in Chemically Modified Polypropylene Films T2 - 2018 IEEE 2nd International Conference on Dielectrics (ICD) N2 - Previous work has shown that surface modification with orthophosphoric acid can significantly enhance the charge stability on polypropylene (PP) surface by generating deeper traps. In the present study, thermally stimulated potential-decay measurements revealed that the chemical treatment may also significantly increase the number of available trapping sites on the surface. Thus, as a consequence, the so-called "cross-over" phenomenon, which is observed on as-received and thermally treated PP electrets, may be overcome in a certain range of initial charge densities. Furthermore, the discharge behavior of chemically modified samples indicates that charges can be injected from the treated surface into the bulk, and/or charges of opposite polarity can be pulled from the rear electrode into the bulk at elevated temperatures and at the high electric fields that are caused by the deposited charges. In the bulk, a lack of deep traps causes rapid charge decay already in the temperature range around 95 degrees C. KW - polypropylene KW - surface charge stability KW - thermally stimulated discharge KW - cross-over effect KW - chemical modification Y1 - 2018 SN - 978-1-5386-6389-9 U6 - https://doi.org/10.1109/ICD.2018.8514718 PB - IEEE CY - New York ER - TY - GEN A1 - Nguyen, Quyet Doan A1 - Wang, Jingwen A1 - Rychkov, Dmitry A1 - Gerhard, Reimund T1 - Depth Profile and Transport of Positive and Negative Charge in Surface (2-D) and Bulk (3-D) Nanocomposite Films T2 - 2nd International Conference on Electrical Materials and Power Equipment (ICEMPE 2019) N2 - In the present study, the charge distribution and the charge transport across the thickness of 2- and 3-dimensional polymer nanodielectrics was investigated. Chemically surface-treated polypropylene (PP) films and low-density polyethylene nanocomposite films with 3 wt % of magnesium oxide (LDPE/MgO) served as examples of 2-D and 3-D nanodielectrics, respectively. Surface charges were deposited onto the non-metallized surfaces of the one-side metallized polymer films and found to broaden and to thus enter the bulk of the films upon thermal stimulation at suitable elevated temperatures. The resulting space-charge profiles in the thickness direction were probed by means of Piezoelectrically-generated Pressure Steps (PPSs). It was observed that the chemical surface treatment of PP which led to the formation of nano-structures or the use of bulk nanoparticles from LDPE/MgO nanocomposites enhance charge trapping on or in the respective polymer films and also reduce charge transport inside the respective samples. KW - LDPE nanocomposites KW - MgO nanoparticles KW - Space charge KW - Charge transport KW - Charge stability KW - Acoustic probing of electric-field profiles KW - Piezoelectrically generated Pressure Steps (PPSs) Y1 - 2019 SN - 978-1-5386-8434-4 SN - 978-1-5386-8435-1 U6 - https://doi.org/10.1109/ICEMPE.2019.8727256 SP - 298 EP - 300 PB - IEEE CY - New York ER - TY - THES A1 - Wang, Jingwen T1 - Electret properties of polypropylene with surface chemical modification and crystalline reconstruction N2 - As one of the most-produced commodity polymers, polypropylene draws considerable scientific and commercial interest as an electret material. In the present thesis, the influence of the surface chemical modification and crystalline reconstruction on the electret properties of the polypropylene thin films will be discussed. The chemical treatment with orthophosphoric acid can significantly improve the surface charge stability of the polypropylene electrets by introducing phosphorus- and oxygen-containing structures onto the modified surface. The thermally stimulated discharge measurement and charge profiling by means of piezoelectrically generated pressure steps are used to investigate the electret behaviour. It is concluded that deep traps of limited number density are created during the treatment with inorganic chemicals. Hence, the improvement dramatically decreases when the surface-charge density is substantially higher than ±1.2×10^(-3) C·m^(-2). The newly formed traps also show a higher trapping energy for negative charges. The energetic distributions of the traps in the non-treated and chemically treated samples offer an insight regarding the surface and foreign-chemical dominance on the charge storage and transport in the polypropylene electrets. Additionally, different electret properties are observed on the polypropylene films with the spherulitic and transcrystalline structures. It indicates the dependence of the charge storage and transport on the crystallite and molecular orientations in the crystalline phase. In general, a more diverse crystalline growth in the spherulitic samples can result in a more complex energetic trap distribution, in comparison to that in a transcrystalline polypropylene. The double-layer transcrystalline polypropylene film with a crystalline interface in the middle can be obtained by crystallising the film in contact with rough moulding surfaces on both sides. A layer of heterocharges appears on each side of the interface in the double-layer transcrystalline polypropylene electrets after the thermal poling. However, there is no charge captured within the transcrystalline layers. The phenomenon reveals the importance of the crystalline interface in terms of creating traps with the higher activation energy in polypropylene. The present studies highlight the fact that even slight variations in the polypropylene film may lead to dramatic differences in its electret properties. N2 - Als eines der meistproduzierten Polymere stößt Polypropylen (PP) auch als Elektretmaterial auf großes wissenschaftliches und kommerzielles Interesse. In der vorliegenden Arbeit wird der Einfluss chemischer Oberflächen-Modifikationen und kristalliner Rekonstruktionen auf die Elektreteigenschaften von dünnen Polypropylen-Schichten untersucht und diskutiert. Die nasschemische Behandlung mit Orthophosphorsäure kann die Oberflächenladungsstabilität der PP-Elektrete deutlich verbessern, indem phosphor- und sauerstoffhaltige Strukturen auf der modifizierten Oberfläche erzeugt und verankert werden. Aus thermisch stimulierten Entladungsexperimenten und Ladungsmessungen mit piezoelektrisch erzeugten Druckstufen ergibt sich, dass die Oberflächenbehandlung eine begrenzte Anzahl tiefer Haftstellen vor allem für negative Ladungen erzeugt. Daher nimmt die Verbesserung drastisch ab, wenn die Oberflächenladungsdichte einen wesentlich höheren Wert als ±1.2×10-3 C·m-2 hat. Die energetischen Verteilungen der Ladungsfallen in unbehandelten und in chemisch behandelten Proben ermöglichen Rückschlüsse auf die Oberfläche und auf die wesentliche Rolle der aufgebrachten chemischen Spezies für Ladungsspeicherung und -transport in PP-Elektreten. Darüber hinaus werden an dünnen Polypropylenfolien mit entweder sphärolithischen oder transkristallinen Strukturen deutlich unterschiedliche Elektreteigenschaften beobachtet, was den starken Einfluss von Kristallstruktur und Molekülorientierung auf Ladungsspeicherung und -transport in der kristallinen Phase anzeigt. Generell führt das vielfältigere kristalline Wachstum in sphärolithischen Proben oft zu komplexeren energetischen Verteilungen der Ladungsfallen als in transkristallinen PP-Schichten. Zweischichtige transkristalline PP-Folien mit einer kristallinen Grenzfläche in der Mitte können durch beidseitige Kristallisation auf rauen Formgussoberflächen erzeugt werden. Auf jeder Seite der Grenzfläche in der Mitte der zweischichtigen transkristallinen PP-Elektrete findet sich nach thermischer Polung eine Schicht von Heteroladungen, während innerhalb der transkristallinen Schichten keine Ladungen beobachtet werden. Daraus wird die Bedeutung der kristallinen Grenzfläche für das Auftreten von Ladungsfallen mit hohen Aktivierungsenergien in Polypropylen deutlich. Die vorliegenden Studien zeigen, dass bereits geringe Variationen in der Nanostruktur der Polypropylenfolien zu dramatisch unterschiedlichen Elektreteigenschaften führen können. KW - electret KW - polypropylene KW - charge storage and transport KW - surface chemical treatment KW - transcrystalline polypropylene KW - Elektret KW - Polypropylen KW - Ladungsspeicherung und -transport KW - chemische Oberflächen-Modifikationen KW - transkristallines Polypropylen Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-470271 ER - TY - JOUR A1 - Wang, Jingwen A1 - Rychkov, Dmitry A1 - Gerhard, Reimund T1 - Chemical modification with orthophosphoric acid enhances surface-charge stability on polypropylene electrets JF - Applied physics letters N2 - The low surface-charge stability of polypropylene (PP) frequently limits its application as an electret material. In this paper, we demonstrate how the treatment of PP-film surfaces with orthophosphoric acid (H3PO4) enhances their charge stability. To discriminate between the effects of chemical modification and thermal treatment, as-received and annealed PP films are used as reference samples. The electret properties of treated and non-treated PP films are characterized with thermally stimulated discharge (TSD) and isothermal surface-potential decay (ISPD) experiments, from which considerable improvement in thermal and temporal charge stability is observed for samples modified with H3PO4. The half-value temperature (T-1/2) observed on TSD curves of chemically treated PP increases to 131 and 145 degrees C for positive and negative charges, respectively. The enhancement might be attributed to the phosphoric compounds detected on the H3PO4-modified surfaces via attenuated-total-reflection infrared spectroscopy. Deeper surface traps formed at the "foreign" phosphorus-containing structures are able to capture the charges over longer time periods and at higher temperatures, thus leading to significant improvements in the temporal and thermal surface-charge stabilities of PP electrets. Published by AIP Publishing. Y1 - 2017 U6 - https://doi.org/10.1063/1.4983348 SN - 0003-6951 SN - 1077-3118 VL - 110 PB - American Institute of Physics CY - Melville ER -