TY - THES A1 - Tan, Li T1 - Synthesis, assembly and thermo-responsivity of polymer-functionalized magnetic cobalt nanoparticles T1 - Synthese, Assemblierung und Temperatur-Responsivität von Polymer-funktionalisierten magnetischen Cobalt Nanopartikeln N2 - This thesis mainly covers the synthesis, surface modification, magnetic-field-induced assembly and thermo-responsive functionalization of superparamagnetic Co NPs initially stabilized by hydrophobic small molecules oleic acid (OA) and trioctylphosphine oxide (TOPO), as well as the synthesis of both superparamagnetic and ferromagnetic Co NPs by using end-functionalized-polystyrene as stabilizer. Co NPs, due to their excellent magnetic and catalytic properties, have great potential application in various fields, such as ferrofluids, catalysis, and magnetic resonance imaging (MRI). Superparamagnetic Co NPs are especially interesting, since they exhibit zero coercivity. They get magnetized in an external magnetic field and reach their saturation magnetization rapidly, but no magnetic moment remains after removal of the applied magnetic field. Therefore, they do not agglomerate in the body when they are used in biomedical applications. Normally, decomposition of metallic precursors at high temperature is one of the most important methods in preparation of monodisperse magnetic NPs, providing tunability in size and shape. Hydrophobic ligands like OA, TOPO and oleylamine are often used to both control the growth of NPs and protect them from agglomeration. The as-prepared magnetic NPs can be used in biological applications as long as they are transferred into water. Moreover, their supercrystal assemblies have the potential for high density data storage and electronic devices. In addition to small molecules, polymers can also be used as surfactants for the synthesis of ferromagnetic and superparamagnetic NPs by changing the reaction conditions. Therefore, chapter 2 gives an overview on the basic concept of synthesis, surface modification and self-assembly of magnetic nanoparticles. Various examples were used to illustrate the recent work. The hydrophobic Co NPs synthesized with small molecules as surfactants limit their biological applications, which require a hydrophilic or aqueous environment. Surface modification (e.g., ligand exchange) is a general idea for either phase transition or surface-functionalization. Therefore, in chapter 3, a ligand exchange process was conducted to functionalize the surface of Co NPs. PNIPAM is one of the most popular smart polymers and its lower critical solution temperature (LCST) is around 32 °C, with a reversible change in the conformation structure between hydrophobic and hydrophilic. The novel nanocomposites of superparamagnetic Co NPs and thermo-responsive PNIPAM are of great interest. Thus, well-defined superparamagnetic Co NPs were firstly synthesized through the thermolysis of cobalt carbonyl by using OA and TOPO as surfactants. A functional ATRP initiator, containing an amine (as anchoring group) and a 2-bromopropionate group (SI-ATRP initiator), was used to replace the original ligands. This process is rapid and facial for efficient surface functionalization and afterwards the Co NPs can be dispersed into polar solvent DMF without aggregation. FT-IR spectroscopy showed that the TOPO was completely replaced, but a small amount of OA remained on the surface. A TGA measurement allowed the calculation of the grafting density of the initiator as around 3.2 initiator/nm2. Then, the surface-initiated ATRP was conducted for the polymerization of NIPAM on the surface of Co NPs and rendered the nanocomposites water-dispersible. A temperature-dependent dynamic light scattering study showed the aggregation behavior of PNIPAM-coated Co NPs upon heating and this process was proven to be reversible. The combination of superparamagnetic and thermo-responsive properties in these hybrid nanoparticles is promising for future applications e.g. in biomedicine. In chapter 4, the magnetic-field-induced assembly of superparamagnetic cobalt nanoparticles both on solid substrates and at liquid-air interface was investigated. OA- and TOPO-coated Co NPs were synthesized via the thermolysis of cobalt carbonyl and dispersed into either hexane or toluene. The Co NP dispersion was dropped onto substrates (e.g., TEM grid, silicon wafer) and at liquid-air (water-air or ethylene glycol-air) interface. Due to the attractive dipolar interaction, 1-D chains formed in the presence of an external magnetic field. It is known that the concentration and the strength of the magnetic field can affect the assembly behavior of superparamagnetic Co NPs. Therefore, the influence of these two parameters on the morphology of the assemblies was studied. The formed 1-D chains were shorter and flexible at either lower concentration of the Co NP dispersion or lower strength of the external magnetic field due to thermal fluctuation. However, by increasing either the concentration of the NP dispersion or the strength of the applied magnetic field, these chains became longer, thicker and straighter. The reason could be that a high concentration led to a high fraction of short dipolar chains, and their interaction resulted in longer and thicker chains under applied magnetic field. On the other hand, when the magnetic field increased, the induced moments of the magnetic nanoparticles became larger, which dominated over the thermal fluctuation. Thus, the formed short chains connected to each other and grew in length. Thicker chains were also observed through chain-chain interaction. Furthermore, the induced moments of the NPs tended to direct into one direction with increased magnetic field, thus the chains were straighter. In comparison between the assembly on substrates, at water-air interface and at ethylene glycol-air interface, the assembly of Co NPs in hexane dispersion at ethylene glycol-air interface showed the most regular and homogeneous chain structures due to the better spreading of the dispersion on ethylene glycol subphase than on water subphase and substrates. The magnetic-field-induced assembly of superparamagnetic nanoparticles could provide a powerful approach for applications in data storage and electronic devices. Chapter 5 presented the synthesis of superparamagnetic and ferromagnetic cobalt nanoparticles through a dual-stage thermolysis of cobalt carbonyl (Co2(CO)8) by using polystyrene as surfactant. The amine end-functionalized polystyrene surfactants with different molecular weight were prepared via atom transfer radical polymerization technique. The molecular weight determination of polystyrene was conducted by gel permeation chromatography (GPC) and matrix-assisted laser desorption/ionization time-of-flight (MALDI-ToF) mass spectrometry techniques. The results showed that, when the molecular weight distribution is low (Mw/Mn < 1.2), the measurement by GPC and MALDI-ToF MS provided nearly similar results. For example, the molecular weight of 10600 Da was obtained by MALDI-ToF MS, while GPC gave 10500 g/mol (Mw/Mn = 1.17). However, if the polymer is poly distributed, MALDI-ToF MS cannot provide an accurate value. This was exemplified for a polymer with a molecular weight of 3130 Da measured by MALDI-TOF MS, while GPC showed 2300 g/mol (Mw/Mn = 1.38). The size, size distribution and magnetic properties of the hybrid particles were different by changing either the molecular weight or concentration of the polymer surfactants. The analysis from TEM characterization showed that the size of cobalt nanoparticles stabilized with polystyrene of lower molecular weight (Mn = 2300 g/mol) varied from 12–22 nm, while the size with middle (Mn = 4500 g/mol) and higher molecular weight (Mn = 10500 g/mol) of polystyrene-coated cobalt nanoparticles showed little change. Magnetic measurements exhibited that the small cobalt particles (12 nm) were superparamagnetic, while larger particles (21 nm) were ferromagnetic and assembled into 1-D chains. The grafting density calculated from thermogravimetric analysis showed that a higher grafting density of polystyrene was obtained with lower molecular weight (Mn = 2300 g/mol) than those with higher molecular weight (Mn = 10500 g/mol). Due to the larger steric hindrance, polystyrene with higher molecular weight cannot form a dense shell on the surface of the nanoparticles, which resulted in a lower grafting density. Wide angle X-ray scattering measurements revealed the epsilon cobalt crystalline phases of both superparamagnetic Co NPs coated with polystyrene (Mn = 2300 g/mol) and ferromagnetic Co NPs coated with polystyrene (Mn = 10500 g/mol). Furthermore, a stability study showed that PS-Co NPs prepared with higher polymer concentration and polymer molecular weight exhibited a better stability. N2 - Im Rahmen dieser Arbeit wurden superparamagnetische Cobalt Nanopartikel (NP) synthetisiert, die Selbstassemblierung im Magnetfeld untersucht und die ursprünglichen Liganden Ölsäure (Englisch oleic acid, OA) und Trioctylphosphanoxid (TOPO) ersetzt, um eine Funktionalisierung der Nanopartikel mit einem Temperatur-responsiven Polymer zu erreichen. Außerdem wurden superparamagnetische und ferromagnetische Co NP mit Polystyrol als Stabilisator synthetisiert. Co NP haben aufgrund ihrer herausragenden magnetischen und katalytischen Eigenschaften viele potentielle Anwendungen beispielsweise als Ferrofluide, in der Katalyse und der Magnetresonanztomografie (Englisch magnetic resonance imaging, MRI). Besonders interessant sind dabei superparamagnetische Co NP, die in einem äußeren Magnetfeld magnetisiert werden, aber nach Entfernen des angelegten Magnetfelds keine Magnetisierung mehr aufweisen. Bei biomedizinischen Anwendungen aggregieren sie daher nicht im Körper. Hydrophobe Co NP, die von kleinen Molekülen stabilisiert werden, eignen sich nicht für biologische Anwendungen, für die ein hydrophiles oder wässriges Medium vonnöten ist. Kapitel 3 beschreibt einen Ligandenaustausch zur Funktionalisierung von Co Nanopartikeln und das Herstellen neuer Nanokomposite aus superparamagnetischen Co NP und Temperatur-responsivem PNIPAM. Zunächst wurden wohldefinierte superparamagnetische Co NP mit OA und TOPO als Stabilisatoren durch die Thermolyse von Cobalt Carbonyl synthetisiert. Die ursprünglichen Liganden wurden dann durch einen funktionalen Liganden mit einer Amingruppe (zum Binden an die Oberfläche) und einer 2 Brompropionat-Gruppe (Polymerisationsinitiator) ersetzt. Nach diesem schnellen und einfachen Prozess der Oberflächenfunktionalisierung können die Nanopartikel ohne Aggregation in dem polaren Lösungsmittel DMF dispergiert werden. Nach thermogravimetrischen Messungen konnte die Dichte der Initiatoren mit ungefähr 3,2 Initiatoren / nm2 berechnet werden. Anschließend wurde Oberflächen-initiierte ATRP zur Polymerisation von NIPAM durchgeführt. Temperatur-abhängige Messungen der dynamischen Lichtstreuung der nun in Wasser dispergierbaren Nanokomposite zeigte das reversible Aggregationsverhalten nach Erhitzen über 32 °C. Kapitel 4 behandelt die Untersuchung der Assemblierung von superparamagnetischen OA- und TOPO-stabilisierten Co NP im äußeren Magnetfeld sowohl auf festen Oberflächen als auch der Flüssigkeit-Luft Grenzfläche. Durch die anziehende dipolare Wechselwirkung bildeten sich im äußeren Magnetfeld 1-D Ketten. Der Einfluss der Konzentration der Dispersion und der Stärke des Magnetfelds auf die Morphologie der assemblierten Strukturen wurde untersucht. Bei niedrigerer Konzentration der Dispersion und geringerer Magnetfeldstärke bildeten sich kurze und flexible Ketten. Bei höherer Konzentration oder höherer Magnetfeldstärke wurden die Ketten länger, breiter und gerader. Andererseits sind die induzierten magnetischen Momente bei erhöhter Magnetfeldstärke größer und dominieren über die thermische Fluktuation. Daher verbinden sich die kurzen Ketten zu längeren, und dickere Ketten entstehen durch Interaktion benachbarter Ketten. Außerdem zeigen die induzierten Momente der NP verstärkt in die gleiche Richtung je größer das äußere Magnetfeld ist, weshalb die Ketten gerader werden. Im Vergleich der Assemblierung auf Substraten (TEM-Grids, Siliciumwafer), an der Wasser-Luft und Ethylenglycol-Luft Grenzfläche, zeigte die Assemblierung von Co NP aus Hexan-Dispersion an der Ethylenglycol-Luft Grenzfläche die geordnetsten und homogensten Strukturen. Kapitel 5 präsentierte die Synthese von superparamagnetischen und ferromagnetischen Cobalt Nanopartikeln durch die zwei-stufige Thermolyse von Cobalt Carbonyl (Co2(CO)8) mit Polystyrol als Stabilisator. Polystyrol Polymere mit Amin-Endgruppen wurden durch ATRP-Technik mit unterschiedlichen Molekulargewichten hergestellt. Die Größe, Größenverteilung und magnetischen Eigenschaften der hybriden Partikel haben sich mit dem Molekulargewicht und der Konzentration der Polymer-Stabilisatoren unterschieden. Eine Analyse mit Transmissionselektronenmikroskopie zeigte, dass die Größe der Co NP zwischen 12–22 nm variierte, wenn sie durch Polystyrol geringen Molekulargewichts (Mn = 2300 g/mol) stabilisiert wurden, während sich die Größe der Partikel mit Polystyrol mittleren (Mn = 4500 g/mol) und höheren (Mn = 10500 g/mol) Molekulargewichts kaum unterschied. Messungen der magnetischen Eigenschaften zeigten, dass die kleinen Cobalt Partikel (12 nm) superparamagnetisch waren, während größere Partikel (21 nm) ferromagnetisch waren und zu 1-D Ketten assemblierten. Die Dichte der Polymere auf der Oberfläche wurde nach einer thermogravimetrischen Analyse berechnet. Mit kleinem Molekulargewicht (Mn = 2300 g/mol) wurde eine höhere Dichte erreicht als mit hohem Molekulargewicht (Mn = 10500 g/mol). Durch eine stärker ausgeprägte sterische Hinderung kann ein Polymer hohen Molekulargewichts keine dichte Hülle um die Nanopartikel bilden. Das Vorliegen einer epsilon kristallinen Phase wurde durch Weitwinkel-Röntgenstreuung sowohl für superparamagnetische Co NP (mit PS Mn = 2300 g/mol) als auch ferromagnetische Co NP (mit PS Mn = 10500 g/mol) bestimmt. KW - magnetic nanoparticles KW - assembly KW - polymer KW - cobalt nanoparticles KW - magnetische Nanopartikel KW - Assemblierung KW - Polymer KW - Cobalt Nanopartikeln Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-418153 ER - TY - THES A1 - Lama, Sandy M. G. T1 - Functionalization of Porous Carbon Materials with Heteroatoms and Application as Supports in Industrial Heterogeneous Catalysis T1 - Funktionalisierung von porösen Kohlenstoffmaterialien mit Heteroatomen und Anwendung als Träger in der industriellen heterogenen Katalyse N2 - Due to a challenging population growth and environmental changes, a need for new routes to provide required chemicals for human necessities arises. An effective solution discussed in this thesis is industrial heterogeneous catalysis. The development of an advanced industrial heterogeneous catalyst is investigated herein by considering porous carbon nano-material as supports and modifying their surface chemistry structure with heteroatoms. Such modifications showed a significant influence on the performance of the catalyst and provided a deeper insight regarding the interaction between the surface structure of the catalyst and the surrounding phase. This thesis contributes to the few present studies about heteroatoms effect on the catalyst performance and emphasizes on the importance of understanding surface structure functionalization in a catalyst in different phases (liquid and gaseous) and for different reactions (hydrogenolysis, oxidation, and hydrogenation/ polymerization). Herein, the heteroatoms utilized for the modifications are hydrogen (H), oxygen (O), and nitrogen (N). The heteroatoms effect on the metal particle size, on the polarity of the support/ the catalyst, on the catalytic performance (activity, selectivity, and stability), and on the interaction with the surrounding phase has been explored. First hierarchical porous carbon nanomaterials functionalized with heteroatoms (N) is synthesized and applied as supports for nickel nanoparticles for hydrogenolysis process of kraft lignin in liquid phase. This reaction has been performed in batch and flow reactors for three different catalysts, two of comparable hierarchical porosity, yet one is modified with N and the other is not, and a third is a prepared catalyst from a commercial carbon support. The reaction production and analyses show that the catalysts with hierarchical porosity perform catalytically much better than in presence of a commercial carbon support with lower surface area. Moreover, the modification with N-heteroatoms enhanced the catalytic performance because the heteroatom modified porous carbon material with nickel nanoparticles catalyst (Ni-NDC) performed highest among the other catalysts. In the flow reactor, Ni-NDC selectively degraded the ether bonds (β-O-4) in kraft lignin with an activity of 2.2 x10^-4 mg lignin mg Ni-1 s-1 for 50 h at 350°C and 3.5 mL min-1 flow, providing ~99 % conversion to shorter chained chemicals (mainly guaiacol derivatives). Then, the functionalization of carbon surface was further studied in selective oxidation of glucose to gluconic acid using < 1 wt. % of gold (Au) deposited on the previously-mentioned synthesized carbon (C) supports with different functionalities (Au-CGlucose, Au-CGlucose-H, Au-CGlucose-O, Au-CGlucoseamine). Except for Au-CGlucose-O, the other catalysts achieved full glucose conversion within 40-120 min and 100% selectivity towards gluconic acid with a maximum activity of 1.5 molGlucose molAu-1 s-1 in an aqueous phase at 45 °C and pH 9. Each heteroatom influenced the polarity of the carbon differently, affecting by that the deposition of Au on the support and thus the activity of the catalyst and its selectivity. The heteroatom effect was further investigated in a gas phase. The Fischer-Tropsch reaction was applied to convert synthetic gas (CO and H2) to short olefins and paraffins using surface-functionalized carbon nanotubes (CNTs) with heteroatoms as supports for ion (Fe) deposition in presence and absence of promoters (Na and S). The results showed the promoted Fe-CNT doped with nitrogen catalyst to be stable up to 180 h and selective to the formation of olefins (~ 47 %) and paraffins (~6 %) with a conversion of CO ~ 92 % at a maximum activity of 94 *10^-5 mol CO g Fe-1 s-1. The more information given regarding this topic can open wide range of applications not only in catalysis, but in other approaches as well. In conclusion, incorporation of heteroatoms can be the next approach for an advanced industrial heterogeneous catalyst, but also for other applications (e.g. electrocatalysis, gas adsorption, or supercapacitors). N2 - Herausforderungen wie Bevölkerungszuwachs und Umweltveränderungen erfordern neue Wege, chemische Substanzen zu erzeugen, um menschliche Anforderungen zu befriedigen. Eine mögliche effektive Lösung dafür, welche in dieser Arbeit diskutiert wird ist die industrielle heterogene Katalyse. Es werden unter dem Einsatz poröser Kohlenstoffträger neue industrielle Katalysatoren untersucht und entwickelt wobei die Oberflächenstruktur dieser Trägermaterialien mit Heteroatomen modifiziert wird. Diese Modifikationen zeigten einen signifikanten Einfluss auf die Eigenschaften der Katalysatoren und erlaubten Rückschlüsse hinsichtlich der Interaktion zwischen Katalysatoroberfläche und umgebender Phase. Die vorliegende Arbeit trägt zu einigen wenigen existierenden Studien bei die sich mit den Einflüssen solcher Heteroatome auf Katalysatoren beschäftigen. Es wird versucht, die Wichtigkeit dieser Oberflächeneigenschaften in Reaktionen (Hydrogenolyse, Oxidation, Hydrierung/ Polymerisation) in verschiedenen Phasen (flüssig oder gasförmig) zu verstehen. Die für die Modifikationen eingesetzten Heteroatome sind Wasserstoff (H), Sauerstoff (O) und Stickstoff (N). Ihr Effekt auf die Größe der Metallpartikel, die Polarität der Träger bzw. Katalysatoren, die eigentlichen katalytischen Eigenschaften und die Interaktion mit der umgebenden Phase wurde untersucht. Zuerst wurden hierarchisch poröse Kohlenstoffmaterialien hergestellt, die mit Stickstoff als Heteroatome funktionalisiert wurden. Diese wurden als Trägermaterialien für Nickel-Nanopartikel in der Hydrogenolyse von Kraft Lignin in flüssiger Phase eingesetzt. Diese Reaktion wurde mit drei unterschiedlichen Katalysatoren in Batch- und Flussreaktoren durchgeführt. Zwei der Katalysatoren hatten vergleichbare hierarchische Porosität. Einer davon war mit Heteroatomen funktionalisiert, einer dagegen nicht. Ein dritter Katalysator wurde mit einem kommerziell erhältlichen Kohlenstoffmaterial hergestellt. Die Reaktion zeigte, dass die Katalysatoren mit hierarchischer Porosität deutlich bessere Eigenschaften zeigen als das kommerzielle Trägermaterial mit geringerer Oberfläche. Darüber hinaus zeigte sich, dass die Modifizierung mit Stickstoffatomen die katalytischen Eigenschaften verbessert, da das modifizierte Kohlenstoffmaterial mit den Nickelpartikeln (Ni-NDC) die besten Ergebnisse aller untersuchten Katalysatoren zeigte. Im Durchflussreaktor wurden von Ni-NDC die Etherbindungen des Kraft Lignins (β-O-4) selektiv mit einer Aktivität von 2.2 x10^-4 mg lignin mg Ni-1 s-1 für 50 h bei 99% Umsatz zu kurzkettigeren Strukturen (hauptsächlich Guajakol-Derivat) gespalten. Außerdem wurde der Einfluss der Funktionalisierung der Kohlenstoffoberfläche in der selektiven Oxidation von Glucose zu Gluconsäure mit 1 Gew.% Gold (Au) auf den vorher angesprochenen Kohlenstoffträgermaterialien mit unterschiedlichen Oberflächenfunktionalitäten (Au-CGlucose, Au-CGlucose-H, Au-CGlucose-O, Au-CGlucoseamine) untersucht. Mit Ausnahme von Au-CGlucose-O erreichten alle Katalysatoren innerhalb von 40-120 min 100% Glucose Umsatz bei 100%iger Selektivität zu Gluconsäure und einer maximalen katalytischen Aktivität von 1.5 molGlucose molAu-1 s-1 in wässriger Phase bei 45°C und pH 9. Die unterschiedlichen Heteroatome wirkten sich unterschiedlich auf die Polarität der Kohlenstoffe und damit auch auf die Abscheidung der Goldpartikel auf die Trägermaterialien und die Katalysatoraktivität und -selektivität aus. Der Einfluss der Heteroatome wurde außerdem in einer Gasphasenreaktion untersucht. Die Fischer-Tropsch Reaktion kam zum Einsatz um Synthesegas (CO und H2) mit Hilfe von Katalysatoren bestehend aus Eisen (Fe) auf Heteroatomfunktionalisierten Kohlenstoffnanoröhrchen (engl. Carbon nanotubes, CNTs) in Gegenwart und Abwesenheit von Promotoren (Na und S) zu kurzkettigen Olefinen und Paraffinen umzuwandeln. Die Ergebnisse zeigten dass die Fe-CNT Katalysatoren mit Promotoren und stickstoffdotierten Trägern bis zu 180 h stabil waren und Olefine (~ 47 %) sowie Paraffine (~6 %) mit guten Selektivitäten bei einem CO Umsatz von 92% und einer maximalen Aktivität von 94 *10^-5 mol CO gFe-1 s-1 hergestellt werden konnten. Je mehr Informationen zu diesem Thema zur Verfügung gestellt werden, kann dies zu einer großen Bandbreite von Anwendungen nicht nur in der Katalyse, sondern auch in anderen Ansätzen beitragen. Zusammenfassend kann der Einbau von Heteroatomen der nächste Ansatz für einen fortgeschrittenen industriellen heterogenen Katalysator sein, aber auch für andere Anwendungen (z.B. Elektrokatalyse, Gasadsorption oder Superkondensatoren). KW - catalysis KW - carbon material KW - carbon supports KW - glucose oxidation KW - Kraft lignin hydrogenolysis KW - Fischer-Tropsch Synthesis KW - Syngas Hydrogenation KW - gold-carbon catalysts KW - nickel-carbon catalysts KW - iron-carbon nanotube catalysts KW - hierarchical porosity KW - heteroatom modification KW - catalyst functionalization KW - Katalyse KW - Kohlenstoffmaterial KW - Kohlenstoffträger KW - Glukoseoxidation KW - Kraftlignin KW - Hydrogenolyse KW - Fischer-Tropsch-Synthese KW - Syngashydrierung KW - Gold-Kohlenstoff-Katalysatoren KW - Nickel-Kohlenstoff-Katalysatoren KW - Eisen-Kohlenstoff-Nanoröhrchen-Katalysatoren KW - hierarchische Porosität KW - Heteroatom-Modifikation KW - Funktionalisierung von Katalysatoren Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-415797 ER - TY - THES A1 - Lee, Hui-Chun T1 - Toward ultimate control of polymerization and catalytic property T1 - In Richtung ultimative Kontrolle der Polymerisation und der katalytischen Eigenschaft BT - a combination of metal-organic frameworks and ATRP BT - eine Kombination von Metall-organischen Gerüsten und ATRP N2 - Reversible-deactivation radical polymerization (RDRP) is without any doubt one of the most prevalent and powerful strategies for polymer synthesis, by which well-defined living polymers with targeted molecular weight (MW), low molar dispersity (Ɖ) and diverse morphologies can be prepared in a controlled fashion. Atom transfer radical polymerization (ATRP) as one of the most extensive studied types of RDRP has been particularly emphasized due to the high accessibility to hybrid materials, multifunctional copolymers and diverse end group functionalities via commercially available precursors. However, due to catalyst-induced side reactions and chain-chain coupling termination in bulk environment, synthesis of high MW polymers with uniform chain length (low Ɖ) and highly-preserved chain-end fidelity is usually challenging. Besides, owing to the inherited radical nature, the control of microstructure, namely tacticity control, is another laborious task. Considering the applied catalysts, the utilization of large amounts of non-reusable transition metal ions which lead to cumbersome purification process, product contamination and complicated reaction procedures all delimit the scope ATRP techniques. Metal-organic frameworks (MOFs) are an emerging type of porous materials combing the properties of both organic polymers and inorganic crystals, characterized with well-defined crystalline framework, high specific surface area, tunable porous structure and versatile nanochannel functionalities. These promising properties of MOFs have thoroughly revolutionized academic research and applications in tremendous aspects, including gas processing, sensing, photoluminescence, catalysis and compartmentalized polymerization. Through functionalization, the microenvironment of MOF nanochannel can be precisely devised and tailored with specified functional groups for individual host-guest interactions. Furthermore, properties of high transition metal density, accessible catalytic sites and crystalline particles all indicate MOFs as prominent heterogeneous catalysts which open a new avenue towards unprecedented catalytic performance. Although beneficial properties in catalysis, high agglomeration and poor dispersibility restrain the potential catalytic capacity to certain degree. Due to thriving development of MOF sciences, fundamental polymer science is undergoing a significant transformation, and the advanced polymerization strategy can eventually refine the intrinsic drawbacks of MOF solids reversely. Therefore, in the present thesis, a combination of low-dimensional polymers with crystalline MOFs is demonstrated as a robust and comprehensive approach to gain the bilateral advantages from polymers (flexibility, dispersibility) and MOFs (stability, crystallinity). The utilization of MOFs for in-situ polymerizations and catalytic purposes can be realized to synthesize intriguing polymers in a facile and universal process to expand the applicability of conventional ATRP methodology. On the other hand, through the formation of MOF/polymer composites by surface functionalization, the MOF particles with environment-adjustable dispersibility and high catalytic property can be as-prepared. In the present thesis, an approach via combination of confined porous textures from MOFs and controlled radical polymerization is proposed to advance synthetic polymer chemistry. Zn2(bdc)2(dabco) (Znbdc) and the initiator-functionalized Zn MOFs, ZnBrbdc, are utilized as a reaction environment for in-situ polymerization of various size-dependent methacrylate monomers (i.e. methyl, ethyl, benzyl and isobornyl methacrylate) through (surface-initiated) activators regenerated by electron transfer (ARGET/SI-ARGET) ATRP, resulting in polymers with control over dispersity, end functionalities and tacticity with respect to distinct molecular size. While the functionalized MOFs are applied, due to the strengthened compartmentalization effect, the accommodated polymers with molecular weight up to 392,000 can be achieved. Moreover, a significant improvement in end-group fidelity and stereocontrol can be observed. The results highlight a combination of MOFs and ATRP is a promising and universal methodology to synthesize versatile well-defined polymers with high molecular weight, increment in isotactic trial and the preserved chain-end functionality. More than being a host only, MOFs can act as heterogeneous catalysts for metal-catalyzed polymerizations. A Cu(II)-based MOF, Cu2(bdc)2(dabco), is demonstrated as a heterogeneous, universal catalyst for both thermal or visible light-triggered ARGET ATRP with expanded monomer range. The accessible catalytic metal sites enable the Cu(II) MOF to polymerize various monomers, including benzyl methacrylate (BzMA), styrene, methyl methacrylate (MMA), 2-(dimethylamino)ethyl methacrylate (DMAEMA) in the fashion of ARGET ATRP. Furthermore, due to the robust frameworks, surpassing the conventional homogeneous catalyst, the Cu(II) MOF can tolerate strongly coordinating monomers and polymerize challenging monomers (i.e. 4-vinyl pyridine, 2-vinyl pyridine and isoprene), in a well-controlled fashion. Therefore, a synthetic procedure can be significantly simplified, and catalyst-resulted chelation can be avoided as well. Like other heterogeneous catalysts, the Cu(II) MOF catalytic complexes can be easily collected by centrifugation and recycled for an arbitrary amount of times. The Cu(II) MOF, composed of photostimulable metal sites, is further used to catalyze controlled photopolymerization under visible light and requires no external photoinitiator, dye sensitizer or ligand. A simple light trigger allows the photoreduction of Cu(II) to the active Cu(I) state, enabling controlled polymerization in the form of ARGET ATRP. More than polymerization application, the synergic effect between MOF frameworks and incorporated nucleophilic monomers/molecules is also observed, where the formation of associating complexes is able to adjust the photochemical and electrochemical properties of the Cu(II) MOF, altering the band gap and light harvesting behavior. Owing to the tunable photoabsorption property resulting from the coordinating guests, photoinduced Reversible-deactivation radical polymerization (PRDRP) can be achieved to further simplify and fasten the polymerization. More than the adjustable photoabsorption ability, the synergistic strategy via a combination of controlled/living polymerization technique and crystalline MOFs can be again evidenced as demonstrated in the MOF-based heterogeneous catalysts with enhanced dispersibility in solution. Through introducing hollow pollen pivots with surface immobilized environment-responsive polymer, PDMAEMA, highly dispersed MOF nanocrystals can be prepared after associating on polymer brushes via the intrinsic amine functionality in each DMAEMA monomer. Intriguingly, the pollen-PDMAEMA composite can serve as a “smart” anchor to trap nanoMOF particles with improved dispersibility, and thus to significantly enhance liquid-phase photocatalytic performance. Furthermore, the catalytic activity can be switched on and off via stimulable coil-to-globule transition of the PDMAEMA chains exposing or burying MOF catalytic sites, respectively. N2 - Die sogenannte „Reversible-Deactivation Radical Polymerization (RDRP)“ ist eine der am häufigsten genutzten und leistungsstärksten Methoden für die Polymersynthese, mit Hilfe derer genau definierte Polymere mit gezieltem Molekulargewicht (MW), niedriger molarer Dispersität (Ɖ) und verschiedenen Morphologien hergestellt werden können. Die sogenannte „Atom Transfer Radical Polymerization (ATRP) ist eine der am intensivsten untersuchten RDRP Methoden, da sie eine hohe Zugänglichkeit zu Hybridmaterialien, multifunktionellen Copolymeren und diversen Endgruppenfunktionalitäten ermöglicht. Jedoch ist die Synthese von Polymeren mit hohem Molekulargewicht, niedriger Dispersität, exakten Endgruppen und der Steuerung der Taktizität für gewöhnlich schwierig. Außerdem führt die Verwendung von großen Mengen an nichtwiederverwendbaren Übergangsmetallionen zu einem umständlichen Reinigungsprozess, wobei Produktverunreinigungen und komplizierte Reaktionsverfahren die Anwendungsbereiche der ATRP Techniken weiter begrenzen. “Metal-organic frameworks (MOFs)“ sind eine vielversprechende Art von porösen Materialien, die die Eigenschaften von organischen Polymeren und anorganischen Kristallen in sich vereinen und sich durch ein kristallines Gerüst, hohe spezifische Oberflächen, einstellbare poröse Strukturen und vielseitige Nanokanal-Funktionalitäten auszeichnen. Diese vielversprechenden Eigenschaften von MOFs haben die akademische Forschung und ihre Anwendung vielseitig revolutioniert, einschließlich der Photolumineszenz, Katalyse und kompartimentierter Polymerisation. Durch gezielte Funktionalisierung kann die Mikroumgebung von MOF-Nanokanälen mit spezifischen funktionellen Gruppen für individuelle Schlüssel-Schloss-Wechselwirkungen präzise entworfen und maßgeschneidert werden. Darüber hinaus weist die hohe Übergangsmetalldichte, zugängliche katalytische Zentren und die kristallinen Partikel auf MOFs als herausragende heterogene Katalysatoren hin, welche eine vielversprechende Möglichkeit für zukünftige Anwendungen erlauben. Ungeachtet der vorteilhaften Eigenschaften in der Katalyse halten eine hohe Agglomerationstendenz und die schlechte Dispergierbarkeit die potentiellen katalytischen Vorteile bis zu einem gewissen Grad zurück. In der vorliegenden Arbeit wurde eine Kombination von niederdimensionalen Polymeren mit kristallinen MOFs als robuster und umfassender Ansatz zur Erzielung der bilateralen Vorteile von Polymeren (Flexibilität, Dispergierbarkeit) und MOFs (Stabilität, Kristallinität) gezeigt. Die Verwendung von MOFs für in-situ-Polymerisationen und katalytische Zwecke kann realisiert werden, um verblüffende Polymere in einem einfachen und universellen Prozess zu synthetisieren, um die Anwendbarkeit herkömmlicher ATRP Methoden zu erweitern. MOFs können nicht nur als Gerüst dienen, sondern auch selbst als heterogene Katalysatoren für metall-katalysierte Polymerisationen, bedingt durch thermische Behandlung oder sichtbares Licht, fungieren. Auf der anderen Seite können MOF / Polymer-Komposite durch Oberflächenfunktionalisierung hergestellt werden, welche sich schließlich durch einstellbare Dispergierbarkeit und guter katalytischer Eigenschaften auszeichnen. KW - metal organic framework KW - controlled polymerization KW - environmental response KW - liquid-phase catalysis KW - confined polymerization KW - ATRP KW - visible light photocatalysis KW - metallorganischen Gerüstverbindungen KW - kontrollierte Polymerisation KW - Umweltreaktion KW - Flüssigphasenkatalyse KW - begrenzte Polymerisation KW - ATRP KW - sichtbares Licht Photokatalyse Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-414973 ER - TY - THES A1 - Nizardo, Noverra Mardhatillah T1 - Thermoresponsive block copolymers with UCST-behavior aimed at biomedical environments T1 - Thermoresponsive Blockcopolymere mit UCST-Verhalten unter biomedizinisch relevanten Bedingungen N2 - Thermoresponsive block copolymers of presumably highly biocompatible character exhibiting upper critical solution temperature (UCST) type phase behavior were developed. In particular, these polymers were designed to exhibit UCST-type cloud points (Tcp) in physiological saline solution (9 g/L) within the physiologically interesting window of 30-50°C. Further, their use as carrier for controlled release purposes was explored. Polyzwitterion-based block copolymers were synthesized by atom transfer radical polymerization (ATRP) via a macroinitiator approach with varied molar masses and co-monomer contents. These block copolymers can self-assemble in the amphiphilic state to form micelles, when the thermoresponsive block experiences a coil-to-globule transition upon cooling. Poly(ethylene glycol) methyl ether (mPEG) was used as the permanently hydrophilic block to stabilize the colloids formed, and polyzwitterions as the thermoresponsive block to promote the temperature-triggered assembly-disassembly of the micellear aggregates at low temperature. Three zwitterionic monomers were used for this studies, namely 3-((2-(methacryloyloxy)ethyl)dimethylammonio)propane-1-sulfonate (SPE), 4-((2-(methacryloyl- oxy)ethyl)dimethylammonio)butane-1-sulfonate (SBE), and 3-((2-(methacryloyloxy)ethyl)- dimethylammonio)propane-1-sulfate) (ZPE). Their (co)polymers were characterized with respect to their molecular structure by proton nuclear magnetic resonance (1H-NMR) and gel permeation chromatography (GPC). Their phase behaviors in pure water as well as in physiological saline were studied by turbidimetry and dynamic light scattering (DLS). These (co)polymers are thermoresponsive with UCST-type phase behavior in aqueous solution. Their phase transition temperatures depend strongly on the molar masses and the incorporation of co-monomers: phase transition temperatures increased with increasing molar masses and content of poorly water-soluble co-monomer. In addition, the presence of salt influenced the phase transition dramatically. The phase transition temperature decreased with increasing salt content in the solution. While the PSPE homopolymers show a phase transition only in pure water, the PZPE homopolymers are able to exhibit a phase transition only in high salinity, as in physiological saline. Although both polyzwitterions have similar chemical structures that differ only in the anionic group (sulfonate group in SPE and sulfate group in ZPE), the water solubility is very different. Therefore, the phase transition temperatures of targeted block copolymers were modulated by using statistical copolymer of SPE and ZPE as thermoresponsive block, and varying the ratio of SPE to ZPE. Indeed, the statistical copolymers of P(SPE-co-ZPE) show phase transitions both in pure water as well as in physiological saline. Surprisingly, it was found that mPEG-b-PSBE block copolymer can display “schizophrenic” behavior in pure water, with the UCST-type cloud point occurring at lower temperature than the LCST-type one. The block copolymer, which satisfied best the boundary conditions, is block copolymer mPEG114-b-P(SPE43-co-ZPE39) with a cloud point of 45°C in physiological saline. Therefore, it was chosen for solubilization studies of several solvatochromic dyes as models of active agents, using the thermoresponsive block copolymer as “smart” carrier. The uptake and release of the dyes were explored by UV-Vis and fluorescence spectroscopy, following the shift of the wavelength of the absorbance or emission maxima at low and high temperature. These are representative for the loaded and released state, respectively. However, no UCST-transition triggered uptake and release of these dyes could be observed. Possibly, the poor affinity of the polybetaines to the dyes in aqueous environtments may be related to the widely reported antifouling properties of zwitterionic polymers. N2 - Neue thermisch-responsive Blockcopolymere mit vermutlich hoher biokompatibilität wurden entwickelt, die ein Phasenverhalten mit oberer kritischer Lösungstemperatur (UCST) in wässriger zeigen. Insbesondere wurden diese Polymere so gestaltet, dass sie Trübungspunkte des UCST-Übergangs (Tcp) in physiologischer Kochsalzlösung (9 g/l) innerhalb des physiologischen interessanten Temperaturfensters von 30-50°C zeigen. Außerdem wurde ihre Eignung als Träger für kontrollierte Freisetzungszwecke untersucht. Diese Polyzwitterionen-basierte Blockcopolymere wurden durch „Atom transfer radikal polymerisation“ (ATRP) unter Verwendung eines Makroinitiators mit verschiedenen Molmassen und Anteilen von Comonomeren dargestellt. Diese Blockcopolymere können sich im amphiphilen Zustand zu Mizellen selbstorganisieren, wenn der thermisch-responsive Block beim Abkühlen einen Übergang vom Knäulen zur Kügel erfährt. Poly (ethylenglycol) methylether (mPEG) wurde als permanent hydrophiler Blockverwendet, der die gebildeten Kolloide stabilisiert, und Polyzwitterionen als thermisch-responsiver Block, der bei niedriger Temperatur die temperaturinduzierte Bildung von Mizellen bewirkt. Drei zwitterionische Monomere wurden für diese Untersuchungen verwendet, 3-((2-(meth- acryloyloxy)ethyl)dimethylammonio)propane-1-sulfonate (SPE), 4-((2-(methacryloyloxy)- ethyl)dimethylammonio)butane-1-sulfonate (SBE), und 3-((2-(methacryloyloxy)ethyl) dimethylammonio)propane-1-sulfate) (ZPE). Die (Co)Polymere wurden durch protonen-kernmagnetische Resonanz (1H-NMR) und Gelpermeationschromatographie (GPC) charakterisiert. Ihr Phasenübergangsverhalten im Wasser sowie in physiologischer Kochsalzlösung wurde durch Trübheitsmessungen und dynamische Lichtstreuung (DLS) untersucht. Diese (Co)Polymere sind thermisch-responsiv mit einem UCST-Übergang als Phasenverhalten in wässriger Lösung. Die Übergangstemperaturen hängen stark von den Molmassen und von dem Anteil der Co-Monomeren ab: Eine Vergrößerung der Molmasse und des Anteils an schwerwasserlöslichem Comonomer führt zu einer Erhöhung der Phasenübergangstemperaturen. Des Weiteren beeinflusst ein Salzzusatz den Phasenübergang sehr stark. Während die PSPE-Homopolymere nur in Wasser einen Phasenübergang aufweisen, zeigen die PZPE-Homopolymere nur bei hohem Salzgehalt, wie in physiologischer Kochsalzlösung, einen Phasenübergang. Obwohl beide Polyzwitterionen ähnliche chemische Strukturen besitzen und sich nur in der anionischen Gruppe (Sulfonatgruppe in SPE und Sulfatgruppe in ZPE) unterscheiden, ist die Wasserlöslichkeit sehr verschieden. Daher wurden die Phasenübergangstemperaturen der Blockcopolymere durch Verwendung von statistischen Copolymeren aus SPE und ZPE als thermisch-responsivem Block mittels des Verhältnisses von SPE zu ZPE moduliert. Solche statistischen Copolymere P(SPE-co-ZPE) zeigen Phasenübergänge sowohl in Wasser als auch in physiologischer Kochsalzlösung. Darüber hinaus wurde überraschenderweise gefunden, dass PSBE-basierte Blockcopolymer z. T. "schizophrenes" Verhalten in Wasser besitzen, wobei der Trübungspunkt des UCST-Übergangs niedriger als der des LCST-Übergangs liegt. Das Blockcopolymer mPEG114-b-P(SPE43-co-ZPE39) erfüllte am besten die Zielsetzung mit einem Trübungspunkt von 45°C in physiologischer Kochsalzlösung. Deswegen wurde es für Solubilisierungsexperimente verschiedener solvatochromer Farbstoffe als Modelle von Wirkstoffen ausgewählt, wobei die Eignung des thermisch-responsiven Blockcopolymers als "intelligenter" Träger untersucht wurde. Die Aufnahme und Freisetzung der Farbstoffe wurden durch UV-Vis- und Fluoreszenzspektroskopie anhand der Verschiebung der Wellenlänge der Extinktions- oder Emissionsmaxima bei niedriger und hoher Temperatur verfolgt. Diese Temperaturen entsprechen dem aggregierten bzw. gelösten Zustand des Polymeren. Jedoch wurde keine Aufnahme und Freisetzung dieser Farbstoffe durch UCST-Übergang beobachtet. Möglicherweise hängt die schwache Affinität der Polybetaine zu den Farbstoffen in wässrigen Systemen mit den bekannten Antifouling-Eigenschaften von zwitterionischen Polymeren zusammen. KW - block copolymer KW - thermoresponsive KW - polyzwitterion KW - upper critical solution temperature KW - self-assembly KW - Blockcopolymer KW - thermoresponsiv KW - Polyzwitterion KW - obere kritische Lösetemperatur KW - Selbstorganisation Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-412217 ER - TY - THES A1 - Chaleawlert-Umpon, Saowaluk T1 - Sustainable electrode materials based on lignin T1 - Ligninbasierte nachhaltige Elektrodenmaterialien N2 - The utilization of lignin as renewable electrode material for electrochemical energy storage is a sustainable approach for future batteries and supercapacitors. The composite electrode was fabricated from Kraft lignin and conductive carbon and the charge storage contribution was determined in terms of electrical double layer (EDL) and redox reactions. The important factors at play for achieving high faradaic charge storage capacity contribute to high surface area, accessibility of redox sites in lignin and their interaction with conductive additives. A thinner layer of lignin covering the high surface area of carbon facilitates the electron transfer process with a shorter pathway from the active sites of nonconductive lignin to the current collector leading to the improvement of faradaic charge storage capacity. Composite electrodes from lignin and carbon would be even more sustainable if the fluorinated binder can be omitted. A new route to fabricate a binder-free composite electrode from Kraft lignin and high surface area carbon has been proposed by crosslinking lignin with glyoxal. A high molecular weight of lignin is obtained to enhance both electroactivity and binder capability in composite electrodes. The order of the processing step of crosslinking lignin on the composite electrode plays a crucial role in achieving a stable electrode and high charge storage capacity. The crosslinked lignin based electrodes are promising since they allow for more stable, sustainable, halogen-free and environmentally benign devices for energy storage applications. Furthermore, improvement of the amount of redox active groups (quinone groups) in lignin is useful to enhance the capacity in lithium battery applications. Direct oxidative demethylation by cerium ammonium nitrate has been carried out under mild conditions. This proves that an increase of quinone groups is able to enhance the performance of lithium battery. Thus, lignin is a promising material and could be a good candidate for application in sustainable energy storage devices. N2 - Die Verwendung von Lignin als erneuerbares Ausgangsmaterial für Elektroden ist ein nachhaltiger Ansatz für die Herstellung der nächsten Generation von Batterien und Superkondensatoren. In dieser Arbeit werden Verbundelektroden auf der Basis von Kraft-Lignin und leitfähigem Kohlenstoff hergestellt und getestet. Die Beiträge des Aufbaus einer elektrischen Doppelschicht (EDL) und der Redoxreaktionen zur Kapazität der Elektrode werden diskutiert. Die wichtigsten Faktoren um eine hohe faradaysche Kapazität der aktiven Gruppen in Lignin zu erreichen sind eine große Oberfläche, die Zugänglichkeit der redoxaktiven Gruppen, sowie die Wechselwirkung mit leitfähigen Additiven. Dabei verringert eine dünnere Ligninschicht auf der Oberfläche des leitfähigen Kohlenstoffs den Elektronentransportweg zwischen den redoxaktiven Gruppen und dem Stromabnehmer und wirkt sich somit positiv auf die faradaysche Kapazität aus. Traditionelle Verbundelektroden enthalten in der Regel fluorierte Bindemittel, was deren Nachhaltigkeit in Frage stellt. Die Verwendung von Glyoxal als Quervernetzer für Lignin stellt eine Alternative zur Herstellung von bindemittelfreien ligninbasierten Verbundelektroden dar. Durch die Quervernetzung wird Lignin mit hohem Molekulargewicht erhalten, was sich insbesondere vorteilhaft auf die Stabilität der Elektroden auswirkt. Für das Erreichen einer hohen Kapazität spielt allerdings die Reihenfolge der Produktionsschritte eine entscheidende Rolle, was hier auch diskutiert wird. Eine Erhöhung der Anzahl an redoxativen Gruppen, insbesondere Chinon-Funktionalitäten, im Lignin führt darüber hinaus zur Erhöhung der Kapazität in primären Lithiumbatterien. Die direkte oxidative Demethylierung von Phenylethern mit Hilfe von Cerammoniumnitrat wurde in dieser Arbeit unter milden Reaktionsbedingungen durchgeführt und die verbesserte Kapazität in Lithiumbatterien aufgrund der erhöhten Anzahl an redoxaktiven Gruppen aufgezeigt. Abschließend kann Lignin, quervernetzt oder oxidiert, als vielversprechender Wegbereiter für nachhaltige Materialen in der Energiespeicherung angesehen werden. KW - lignin KW - energy storage KW - sustainable energy storage materials KW - Lignin KW - Energiespeicher KW - nachhaltige Energiespeichermaterialien Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-411793 ER - TY - THES A1 - Li, Lina T1 - Preparation of novel photoactive materials T1 - Herstellung von neuen photoaktiven Materialien BT - different pre-compositions, post-modifications and improved performance BT - verschiedene Vorzusammensetzungen, Post-Modifikationen und verbesserte Leistung N2 - Photocatalysis is considered significant in this new energy era, because the inexhaustibly abundant, clean, and safe energy of the sun can be harnessed for sustainable, nonhazardous, and economically development of our society. In the research of photocatalysis, the current focus was held by the design and modification of photocatalyst. As one of the most promising photocatalysts, g-C3N4 has gained considerable attention for its eye-catching properties. It has been extensively explored in photocatalysis applications, such as water splitting, organic pollutant degradation, and CO2 reduction. Even so, it also has its own drawbacks which inhibit its further application. Inspired by that, this thesis will mainly present and discuss the process and achievement on the preparation of some novel photocatalysts and their photocatalysis performance. These materials were all synthesized via the alteration of classic g-C3N4 preparation method, like using different pre-compositions for initial supramolecular complex and functional group post-modification. By taking place of cyanuric acid, 2,5-Dihydroxy-1,4-benzoquinone and chloranilic acid can form completely new supramolecular complex with melamine. After heating, the resulting products of the two complex shown 2D sheet-like and 1D fiber-like morphologies, respectively, which maintain at even up to high temperature of 800 °C. These materials cover crystals, polymers and N-doped carbons with the increase of synthesis temperature. Based on their different pre-compositions, they show different dye degradation performances. For CLA-M-250, it shows the highest photocatalytic activity and strong oxidation capacity. It shows not only great photo-performance in RhB degradation, but also oxygen production in water splitting. In the post-modification method, a novel photocatalysis solution was proposed to modify carbon nitride scaffold with cyano group, whose content can be well controlled by the input of sodium thiocyanate. The cyanation modification leads to narrowed band gap as well as improved photo-induced charges separation. Cyano group grafted carbon nitride thus shows dramatically enhanced performance in the photocatalytic coupling reaction between styrene and sodium benzenesulfinate under green light irradiation, which is in stark contrast with the inactivity of pristine g-C3N4. N2 - Die Sonne stellt eine Quelle für unerschöpfliche, saubere und sichere Energie dar, die für eine nachhaltige, ungefährliche und ökonomische Entwicklung unserer Gesellschaft genutzt werden kann, daher wird Photokatalyse heutzutage als äußerst vielversprechend angesehen. Bei der Erforschung der Photokatalyse lag der Fokus auf dem Design und der Modifizierung von Photokatalysatoren. Als einer der vielversprechendsten Photokatalysatoren hat sich g-C3N4 erwiesen. Es wurde ausführlich für Anwendungen wie z.B. Wasserspaltung, den Abbau organischer Schadstoffe und CO2-Reduktion untersucht. Trotzdem hat es auch Nachteile, die eine weitere Anwendung erschweren. Deshalb wird in dieser Arbeit hauptsächlich die Herstellung und Eigenschaften von neuartigen auf auf g-C3N4 basierenden Photokatalysatoren vorgestellt und diskutiert. Diese Materialien wurden mittels Verfahren hergestellt, bei denen die klassische g-C3N4-Herstellungsmethode geändert wurde, wie z.B. durch die Verwendung unterschiedlicher Zusammensetzungen und durch die Modifizierung von funktionellen Gruppen. Im Vergleich zu g-C3N4 weisen diese neu hergestellten Materialien unterschiedliche photokatalytische Eigenschaften auf. KW - photocatalysis KW - Photokatalyse KW - CN materials KW - CN-Materialien KW - supramolecular KW - Supramolekular KW - post-modification KW - Post-Modifikationen Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-410952 ER - TY - THES A1 - Strunk, David T1 - Gewinnung phenolischer Komponenten aus dem Birkenstamm als Rohstoffquelle für die Synthese eines neuen substituierten Phenylmethacrylats und dessen Polymerisation T1 - Extraction of phenolic components from the birch trunk as a source of raw material for the synthesis of a new substituted phenyl methacrylate and its polymerization N2 - In der vorliegenden Arbeit werden Wege zur Gewinnung verschiedener phenolischer Substanzen wie Lignin, Diarylheptanoide und 4-(3-Oxobutyl)phenol (Himbeerketon) aus dem Stamm der Hängebirke (Betula pendula) aufgezeigt. Durch Methacrylierung des 4-(3-Oxobutyl)phenols wurde ein Monomer erzeugt, welches mittels freier radikalischer Masse- und Lösungspolymerisation, sowie enzymatischer Polymerisation polymerisiert werden kann. Eine erste Isolierung von Bestandteilen wurde durch Extraktion von Innenholz bzw. Rinde mit Methanol erzielt. Die in Methanol unlöslichen Bestandteile des Innenholzes und der Rinde wurden anschließend mit ausgewählten ionischen Flüssigkeiten extrahiert. Es wurde ein Verfahren zum selektiven Trennen der mit diesen ionischen Flüssigkeiten extrahierten Bestandteile in Cellulose, Hemicellulose, Lignin und mit Ethylacetat extrahierbare Bestandteile entwickelt. Hierdurch war es möglich, sowohl die verwendeten ionischen Flüssigkeiten als auch das Innenholz und die Rinde hinsichtlich ihres Extraktionsverhaltens miteinander zu vergleichen. Ferner wurden verschiedene Strategien aufgezeigt, um insgesamt drei Spezies an Diarylheptanoiden aus dem methanolischen Extrakt der Rinde zu isolieren. Eines der gefundenen Diarylheptanoide (5 Hydroxy-1,7-bis(4-hydroxyphenyl)-3-heptanon) wurde via Retroaldolreaktion in 4 (3 Oxobutyl)phenol (Himbeerketon) und 3 (4 Hydroxyphenyl)propanal gespalten. Es wurde die Verwendung des 4-(3-Oxobutyl)phenol als Monomerbestandteil untersucht. Hierfür wurde 4-(3-Oxobutyl)phenylmethacrylat synthetisiert und Wege zur Reinigung mittels Säulenchromatographie und Umkristallisation aufgezeigt. Anschließend wurde Poly(4-(3-oxobutyl)phenylmethacrylat) (PObMA) und Polybenzylmethacrylats (PBzMA) aus Massen- und Lösungspolymerisation hergestellt. Die Ausbeuten an PObpMA im Vergleich zum PBzMA liegen bei gleichen Reaktionsbedingungen auf gleichem Niveau. Im Kontrast hierzu ist der Polymerisationsgrad aus freier radikalischer Polymerisation in Masse des PObpMA im Vergleich zum PBzMA um den Faktor 3,7 größer. Die Glasübergangstemperaturen des PObpMA liegen bei gleichen Reaktionsbedingungen sowohl bei freier radikalischer Polymerisation in Masse, als auch bei Lösungspolymerisation über denen des PBzMA. Darüber hinaus wurde die Polymerisation von 4-(3-Oxobutyl)phenylmethacrylat und Benzylmethacrylat mit einem Initiatorsystem bestehend aus Meerrettichperoxidase, Acetylaceton und Wasserstoffperoxid bei Raumtemperatur beschrieben. Die mit enzymatischem Initiatorsystem erzeugten Produkte zeigten starke Übereinstimmung mit Produkten aus Lösungspolymerisationen, welche mit Azobis(isobutyronitril) initiiert wurden. N2 - In the present work ways of obtaining various phenolic substances such as lignin, diarylheptanoids and 4-(3-oxobutyl)-phenol (raspberry ketone) from the trunk of the silver birch (Betula pendula) are shown. By methacrylating of 4-(3-oxobutyl)-phenol, a monomer was generated which can be polymerized by free radical mass and solution polymerization, as well as by enzymatic polymerization. A first separation of constituents was achieved by extraction of wood or bark with methanol. The methanol-insoluble components of the interior wood and the bark were then extracted with selected ionic liquids. A process has been developed for selectively separating the ingredients extracted with these ionic liquids into cellulose, hemicellulose, lignin and ethyl acetate extractables. This made it possible to compare both the ionic liquids used as well as the interior wood and the bark with respect to their extraction behavior with each other. Furthermore, different strategies were shown to isolate a total of three species of diarylheptanoids from the methanolic extract of the bark. One of the found diarylheptanoids (5-hydroxy-1,7-bis-(4-hydroxyphenyl)-3-heptanone) was cleaved by retroaldolysis in 4-(3-oxobutyl)-phenol (raspberry ketone) and 3-(4-hydroxyphenyl)-propanal. The use of 4- (3-oxobutyl) phenol as a monomer component was investigated. For this purpose, 4-(3-oxobutyl)-phenyl methacrylate was synthesized and ways of purification by column chromatography and recrystallization were shown. Subsequently, poly-(4-(3-oxobutyl)-phenyl methacrylate) (PObMA) and polybenzyl methacrylate (PBzMA) were prepared by mass and solution polymerization. The yields of PObpMA compared to PBzMA are at the same level when the same reaction conditions were used. In contrast, the degree of polymerization by free radical polymerization in mass of PObpMA compared to PBzMA is greater by a factor of 3.7. The glass transition temperatures of the PObpMA are both in free radical polymerization in bulk, as well as in solution polymerization over those of PbzMA when the same reaction conditions were used. Moreover, the polymerization of 4-(3-oxobutyl)-phenyl methacrylate and benzyl methacrylate at room temperature with an initiator system consisting of horseradish peroxidase, acetylacetone and hydrogen peroxide has been described. Products produced with enzymatic initiator system showed strong similarity with products from solution polymerizations initiated with Azobis(isobutyronitrile). KW - Birke KW - Rinde KW - Ionische Flüssigkeit KW - birch KW - bark KW - ionic liquiod KW - Diarylheptanoide KW - Himbeerketon KW - raspberry ketone Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-409228 ER -