TY - JOUR A1 - Zhong, Qi A1 - Mi, Lei A1 - Metwalli, Ezzeldin A1 - Biessmann, Lorenz A1 - Philipp, Martine A1 - Miasnikova, Anna A1 - Laschewsky, Andre A1 - Papadakis, Christine M. A1 - Cubitt, Robert A1 - Schwartzkopf, Matthias A1 - Roth, Stephan V. A1 - Wang, Jiping A1 - Müller-Buschbaum, Peter T1 - Effect of chain architecture on the swelling and thermal response of star-shaped thermo-responsive (poly(methoxy diethylene glycol acrylate)-block-polystyrene)(3) block copolymer films JF - Soft matter N2 - The effect of chain architecture on the swelling and thermal response of thin films obtained from an amphiphilic three-arm star-shaped thermo-responsive block copolymer poly(methoxy diethylene glycol acrylate)-block-polystyrene ((PMDEGA-b-PS)(3)) is investigated by in situ neutron reflectivity (NR) measurements. The PMDEGA and PS blocks are micro-phase separated with randomly distributed PS nanodomains. The (PMDEGA-b-PS)(3) films show a transition temperature (TT) at 33 degrees C in white light interferometry. The swelling capability of the (PMDEGA-b-PS)(3) films in a D2O vapor atmosphere is better than that of films from linear PS-b-PMDEGA-b-PS triblock copolymers, which can be attributed to the hydrophilic end groups and limited size of the PS blocks in (PMDEGA-b-PS)(3). However, the swelling kinetics of the as-prepared (PMDEGA-b-PS)(3) films and the response of the swollen film to a temperature change above the TT are significantly slower than that in the PS-b-PMDEGA-b-PS films, which may be related to the conformation restriction by the star-shape. Unlike in the PS-b-PMDEGA-b-PS films, the amount of residual D2O in the collapsed (PMDEGA-b-PS)(3) films depends on the final temperature. It decreases from (9.7 +/- 0.3)% to (7.0 +/- 0.3)% or (6.0 +/- 0.3)% when the final temperatures are set to 35 degrees C, 45 degrees C and 50 degrees C, respectively. This temperature-dependent reduction of embedded D2O originates from the hindrance of chain conformation from the star-shaped chain architecture. Y1 - 2018 U6 - https://doi.org/10.1039/c8sm00965a SN - 1744-683X SN - 1744-6848 VL - 14 IS - 31 SP - 6582 EP - 6594 PB - Royal Society of Chemistry CY - Cambridge ER - TY - JOUR A1 - Reitenbach, Julija A1 - Geiger, Christina A1 - Wang, Peixi A1 - Vagias, Apostolos N. A1 - Cubitt, Robert A1 - Schanzenbach, Dirk A1 - Laschewsky, André A1 - Papadakis, Christine M. A1 - Müller-Buschbaum, Peter T1 - Effect of magnesium salts with chaotropic anions on the swelling behavior of PNIPMAM thin films JF - Macromolecules : a publication of the American Chemical Society N2 - Poly(N-isopropylmethacrylamide) (PNIPMAM) is a stimuli responsive polymer, which in thin film geometry exhibits a volume-phase transition upon temperature increase in water vapor. The swelling behavior of PNIPMAM thin films containing magnesium salts in water vapor is investigated in view of their potential application as nanodevices. Both the extent and the kinetics of the swelling ratio as well as the water content are probed with in situ time-of-flight neutron reflectometry. Additionally, in situ Fourier-transform infrared (FTIR) spectroscopy provides information about the local solvation of the specific functional groups, while two-dimensional FTIR correlation analysis further elucidates the temporal sequence of solvation events. The addition of Mg(ClO4)2 or Mg(NO3)2 enhances the sensitivity of the polymer and therefore the responsiveness of switches and sensors based on PNIPMAM thin films. It is found that Mg(NO3)2 leads to a higher relative water uptake and therefore achieves the highest thickness gain in the swollen state. Y1 - 2023 U6 - https://doi.org/10.1021/acs.macromol.2c02282 SN - 0024-9297 SN - 1520-5835 VL - 56 IS - 2 SP - 567 EP - 577 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Nieuwenhuis, Sophie A1 - Zhong, Qi A1 - Metwalli, Ezzeldin A1 - Biessmann, Lorenz A1 - Philipp, Martine A1 - Miasnikova, Anna A1 - Laschewsky, Andre A1 - Papadakis, Christine M. A1 - Cubitt, Robert A1 - Wang, Jiping A1 - Müller-Buschbaum, Peter T1 - Hydration and Dehydration Kinetics: Comparison between Poly(N-isopropyl methacrylamide) and Poly(methoxy diethylene glycol acrylate) Films JF - Langmuir N2 - Thermoresponsive films of poly(N-isopropyl methacrylamide) (PNIPMAM) and poly(methoxy diethylene glycol acrylate) (PMDEGA) are compared with respect to their hydration and dehydration kinetics using in situ neutron reflectivity. Both as-prepared films present a homogeneous single-layer structure and have similar transition temperatures of the lower critical solution temperature type (TT, PNIPMAM 38 degrees C and PMDEGA 41 degrees C). After hydration in unsaturated D2O vapor at 23 degrees C, a D2O enrichment layer is observed in PNIPMAM films adjacent to the Si substrate. In contrast, two enrichment layers are present in PMDEGA films (close to the vapor interface and the Si substrate). PNIPMAM films exhibit a higher hydration capability, ascribed to having both donor (N-H) and acceptor (C=O) units for hydrogen bonds. "While the swelling of the PMDEGA films is mainly caused by the increase of the enrichment layers, the thickness of the entire PNIPMAM films increases with time. The observed longer relaxation time for swelling of PNIPMAM films is attributed to the much higher glass transition temperature of PNIPMAM. When dehydrating both films by increasing the temperature above the TT, they react with a complex response consisting of three stages (shrinkage, rearrangement, and reswelling). PNIPMAM films respond faster than PMDEGA films. After dehydration, both films still contain a large amount of D2O, and no completely dry film state is reached for a temperature above their TTs. Y1 - 2019 U6 - https://doi.org/10.1021/acs.langmuir.9b00535 SN - 0743-7463 VL - 35 IS - 24 SP - 7691 EP - 7702 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Zhong, Qi A1 - Metwalli, Ezzeldin A1 - Rawolle, Monika A1 - Kaune, Gunar A1 - Bivigou Koumba, Achille Mayelle A1 - Laschewsky, Andre A1 - Papadakis, Christine M. A1 - Cubitt, Robert A1 - Wang, Jiping A1 - Müller-Buschbaum, Peter T1 - Influence of Hydrophobic Polystyrene Blocks on the Rehydration of Polystyrene-block-poly(methoxy diethylene glycol acrylate)-block-polystyrene Films Investigated by in Situ Neutron Reflectivity JF - Macromolecules : a publication of the American Chemical Society N2 - The rehydration of thermoresponsive polystyrene-block-poly(methoxy diethylene glycol acrylate)-block-polystyrene (PS-b-PMDEGA-b-PS) films forming a lamellar microphase-separated structure is investigated by in situ neutron reflectivity in a D2O vapor atmosphere. The rehydration of collapsed PS-b-PMDEGA-b-PS films is realized by a temperature change from 45 to 23 degrees C and comprises (1) condensation and absorption of D2O, (2) evaporation of D2O, and (3) reswelling of the film due to internal rearrangement. The hydrophobic PS layers hinder the absorption of condensed D2O, and a redistribution of embedded D2O between the hydrophobic PS layers and the hydrophilic PMDEGA layers is observed. In contrast, the rehydration of semiswollen PS-b-PMDEGA-b-PS films (temperature change from 35 to 23 degrees C) shows two prominent differences: A thicker D2O layer condenses on the surface, causing a more enhanced evaporation of D2O. The rehydrated films differ in film thickness and volume fraction of D2O, which is due to the different thermal protocols, although the final temperature is identical. Y1 - 2016 U6 - https://doi.org/10.1021/acs.macromol.5b02279 SN - 0024-9297 SN - 1520-5835 VL - 49 SP - 317 EP - 326 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Hu, Neng A1 - Lin, Li A1 - Metwalli, Ezzeldin A1 - Bießmann, Lorenz A1 - Philipp, Martine A1 - Hildebrand, Viet A1 - Laschewsky, André A1 - Papadakis, Christine M. A1 - Cubitt, Robert A1 - Zhong, Qi A1 - Müller-Buschbaum, Peter T1 - Kinetics of water transfer between the LCST and UCST thermoresponsive blocks in diblock copolymer thin films monitored by in situ neutron reflectivity JF - Advanced materials interfaces N2 - The kinetics of water transfer between the lower critical solution temperature (LCST) and upper critical solution temperature (UCST) thermoresponsive blocks in about 10 nm thin films of a diblock copolymer is monitored by in situ neutron reflectivity. The UCST-exhibiting block in the copolymer consists of the zwitterionic poly(4((3-methacrylamidopropyl)dimethylammonio)butane-1-sulfonate), abbreviated as PSBP. The LCST-exhibiting block consists of the nonionic poly(N-isopropylacrylamide), abbreviated as PNIPAM. The as-prepared PSBP80-b-PNIPAM(400) films feature a three-layer structure, i.e., PNIPAM, mixed PNIPAM and PSBP, and PSBP. Both blocks have similar transition temperatures (TTs), namely around 32 degrees C for PNIPAM, and around 35 degrees C for PSBP, and with a two-step heating protocol (20 degrees C to 40 degrees C and 40 degrees C to 80 degrees C), both TTs are passed. The response to such a thermal stimulus turns out to be complex. Besides a three-step process (shrinkage, rearrangement, and reswelling), a continuous transfer of D2O from the PNIPAM to the PSBP block is observed. Due to the existence of both, LCST and UCST blocks in the PSBP80-b-PNIPAM(400 )film, the water transfer from the contracting PNIPAM, and mixed layers to the expanding PSBP layer occurs. Thus, the hydration kinetics and thermal response differ markedly from a thermoresponsive polymer film with a single LCST transition. KW - block copolymer KW - dual thermoresponsive KW - kinetic water transfer KW - neutron KW - reflectivity KW - thin film Y1 - 2022 U6 - https://doi.org/10.1002/admi.202201913 SN - 2196-7350 VL - 10 IS - 3 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Wang, Peixi A1 - Geiger, Christina A1 - Kreuzer, Lucas A1 - Widmann, Tobias A1 - Reitenbach, Julija A1 - Liang, Suzhe A1 - Cubitt, Robert A1 - Henschel, Cristiane A1 - Laschewsky, André A1 - Papadakis, Christine M. A1 - Müller-Buschbaum, Peter T1 - Poly(sulfobetaine)-based diblock copolymer thin films in water/acetone atmosphere: modulation of water hydration and co-nonsolvency-triggered film contraction JF - Langmuir : the ACS journal of surfaces and colloids N2 - The water swelling and subsequent solvent exchange including co-nonsolvency behavior of thin films of a doubly thermo-responsive diblock copolymer (DBC) are studied viaspectral reflectance, time-of-flight neutron reflectometry, and Fourier transform infrared spectroscopy. The DBC consists of a thermo-responsive zwitterionic (poly(4-((3-methacrylamidopropyl) dimethylammonio) butane-1-sulfonate)) (PSBP) block, featuring an upper critical solution temperature transition in aqueous media but being insoluble in acetone, and a nonionic poly(N-isopropylmethacrylamide) (PNIPMAM) block, featuring a lower critical solution temperature transition in water, while being soluble in acetone. Homogeneous DBC films of 50-100 nm thickness are first swollen in saturated water vapor (H2OorD2O), before they are subjected to a contraction process by exposure to mixed saturated water/acetone vapor (H2OorD2O/acetone-d6 = 9:1 v/v). The affinity of the DBC film toward H2O is stronger than for D2O, as inferred from the higher film thickness in the swollen state and the higher absorbed water content, thus revealing a pronounced isotope sensitivity. During the co-solvent-induced switching by mixed water/acetone vapor, a two-step film contraction is observed, which is attributed to the delayed expulsion of water molecules and uptake of acetone molecules. The swelling kinetics are compared for both mixed vapors (H2O/acetone-d6 and D2O/acetone-d6) and with those of the related homopolymer films. Moreover, the concomitant variations of the local environment around the hydrophilic groups located in the PSBP and PNIPMAM blocks are followed. The first contraction step turns out to be dominated by the behavior of the PSBP block, where as the second one is dominated by the PNIPMAM block. The unusual swelling and contraction behavior of the latter block is attributed to its co-nonsolvency behavior. Furthermore, we observe cooperative hydration effects in the DBC films, that is, both polymer blocks influence each other's solvation behavior. Y1 - 2022 U6 - https://doi.org/10.1021/acs.langmuir.2c00451 SN - 0743-7463 SN - 1520-5827 VL - 38 IS - 22 SP - 6934 EP - 6948 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Zhong, Qi A1 - Metwalli, Ezzeldin A1 - Rawolle, Monika A1 - Kaune, Gunar A1 - Bivigou Koumba, Achille Mayelle A1 - Laschewsky, André A1 - Papadakis, Christine M. A1 - Cubitt, Robert A1 - Müller-Buschbaum, Peter T1 - Rehydration of Thermoresponsive Poly(monomethoxydiethylene glycol acrylate) Films Probed in Situ by Real-Time Neutron Reflectivity JF - Macromolecules : a publication of the American Chemical Society N2 - The rehydration of thermoresponsive poly(monomethoxydiethylene glycol acrylate) (PMDEGA) films exhibiting a lower critical solution temperature (LCST) type demixing phase transition in aqueous environments, induced by a decrease in temperature, is investigated in situ with real-time neutron reflectivity. Two different starting conditions (collapsed versus partially swollen chain conformation) are compared. In one experiment, the temperature is reduced from above the demixing temperature to well below the demixing temperature. In a second experiment, the starting temperature is below the demixing temperature, but within the transition regime, and reduced to the same final temperature. In both cases, the observed rehydration process can be divided into three stages: first condensation of water from the surrounding atmosphere, then absorption of water by the PMDEGA film and evaporation of excess water, and finally, rearrangement of the PMDEGA chains. The final rehydrated film is thicker and contains more absorbed water as compared with the initially swollen film at the same temperature well below the demixing temperature. Y1 - 2015 U6 - https://doi.org/10.1021/acs.macromol.5b00645 SN - 0024-9297 SN - 1520-5835 VL - 48 IS - 11 SP - 3604 EP - 3612 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Zhong, Qi A1 - Metwalli, Ezzeldin A1 - Rawolle, Monika A1 - Kaune, Gunar A1 - Bivigou Koumba, Achille Mayelle A1 - Laschewsky, André A1 - Papadakis, Christine M. A1 - Cubitt, Robert A1 - Müller-Buschbaum, Peter T1 - Structure and Thermal Response of Thin Thermoresponsive Polystyrene-block-poly(methoxydiethylene glycol acrylate)-block-polystyrene Films JF - Macromolecules : a publication of the American Chemical Society N2 - Thin thermoresponsive films of the triblock copolymer polystyrene-block-poly(methoxydiethylene glycol acrylate)-block-polystyrene (P(S-b-MDEGA-b-S)) are investigated on silicon substrates. By spin coating, homogeneous and smooth films are prepared for a range of film thicknesses from 6 to 82 nm. Films are stable with respect to dewetting as investigated with optical microscopy and atomic force microscopy. P(S-b-MDEGA-b-S) films with a thickness of 39 nm exhibit a phase transition of the lower critical solution temperature (LCST) type at 36.5 degrees C. The swelling and the thermoresponsive behavior of the films with respect to a sudden thermal stimulus are probed with in-situ neutron reflectivity. In undersaturated water vapor swelling proceeds without thickness increase. The thermoresponse proceeds in three steps: First, the film rejects water as the temperature is above LCST. Next, it stays constant for 600 s, before the collapsed film takes up water again. With ATR-FTIR measurements, changes of bound water in the film caused by different thermal stimuli are studied. Hydrogen bonds only form between C=O and water in the swollen film. Above the LCST most hydrogen bonds with water are broken, but some amount of bound water remains inside the film in agreement with the neutron reflectivity data. Grazing-incidence small-angle X-ray scattering (GISAXS) shows that the inner lateral structure is not significantly influenced by the different thermal stimuli. Y1 - 2013 U6 - https://doi.org/10.1021/ma400627u SN - 0024-9297 VL - 46 IS - 10 SP - 4069 EP - 4080 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Wang, Weijia A1 - Kaune, Gunar A1 - Perlich, Jan A1 - Paradakis, Christine M. A1 - Bivigou Koumba, Achille Mayelle A1 - Laschewsky, André A1 - Schlage, K. A1 - Röhlsberger, Ralf A1 - Roth, Stephan V. A1 - Cubitt, Robert A1 - Müller-Buschbaum, Peter T1 - Swelling and switching kinetics of gold coated end-capped poly(N-isopropylacrylamide) thin films N2 - Thin thermoresponsive hydrogel films of poly(N-isopropylacrylamide) end-capped with n-butyltrithiocarbonate(nbc- PNIPAM) oil si I icon supports with a gold layer on top, causing an asymmetric confinement, are investigated. For two different gold layer thicknesses (nominally 0.4 and 5 rim), the swelling and switching kinetics are probed with in situ neutron reflectivity. With a temperature jump from 23 to 40 degrees C the film is switched from a swollen into a collapsed state. For the thin gold layer this switching is faster as compared to the thick gold layer. The switching is a two-step process of water release and a subsequent structural relaxation. fit swelling and deswelling cycles, aging of the films is probed. After five cycles, the film exhibits enhanced water storage capacity. Grazing-incidence small-angle X-ray scattering (GISAXS) shows that these gold coated nbc-PNIPAM films do not age with respect to the inner structure but slightly roughen at the gold surface. As revealed by atomic force microscopy, the morphology of the gold layer is changed by the water uptake and release. Y1 - 2010 UR - http://pubs.acs.org/journal/mamobx U6 - https://doi.org/10.1021/Ma902637a SN - 0024-9297 ER - TY - JOUR A1 - Zhong, Qi A1 - Metwalli, Ezzeldin A1 - Kaune, Gunar A1 - Rawolle, Monika A1 - Bivigou Koumba, Achille Mayelle A1 - Laschewsky, André A1 - Papadakis, Christine M. A1 - Cubitt, Robert A1 - Müller-Buschbaum, Peter T1 - Switching kinetics of thin thermo-responsive hydrogel films of poly(monomethoxy-diethyleneglycol-acrylate) probed with in situ neutron reflectivity JF - Soft matter N2 - The switching kinetics of thin thermo-responsive hydrogel films of poly(monomethoxy-diethyleneglycol-acrylate) (PMDEGA) are investigated. Homogeneous and smooth PMDEGA films with a thickness of 35.9 nm are prepared on silicon substrates by spin coating. As probed with white light interferometry, PMDEGA films with a thickness of 35.9 nm exhibit a phase transition temperature of the lower critical solution temperature (LCST) type of 40 degrees C. In situ neutron reflectivity is performed to investigate the thermo-responsive behavior of these PMDEGA hydrogel films in response to a sudden thermal stimulus in deuterated water vapor atmosphere. The collapse transition proceeds in a complex way which can be seen as three steps. The first step is the shrinkage of the initially swollen film by a release of water. In the second step the thickness remains constant with water molecules embedded in the film. In the third step, perhaps due to a conformational rearrangement of the collapsed PMDEGA chains, water is reabsorbed from the vapor atmosphere, thereby giving rise to a relaxation process. Both the shrinkage and relaxation processes can be described by a simple model of hydrogel deswelling. Y1 - 2012 U6 - https://doi.org/10.1039/c2sm25401h SN - 1744-683X VL - 8 IS - 19 SP - 5241 EP - 5249 PB - Royal Society of Chemistry CY - Cambridge ER -