TY - THES A1 - Saatchi, Mersa T1 - Study on manufacturing of multifunctional bilayer systems N2 - Layered structures are ubiquitous in nature and industrial products, in which individual layers could have different mechanical/thermal properties and functions independently contributing to the performance of the whole layered structure for their relevant application. Tuning each layer affects the performance of the whole layered system. Pores are utilized in various disciplines, where low density, but large surfaces are demanded. Besides, open and interconnected pores would act as a transferring channel for guest chemical molecules. The shape of pores influences compression behavior of the material. Moreover, introducing pores decreases the density and subsequently the mechanical strength. To maintain defined mechanical strength under various stress, porous structure can be reinforced by adding reinforcement agent such as fiber, filler or layered structure to bear the mechanical stress on demanded application. In this context, this thesis aimed to generate new functions in bilayer systems by combining layers having different moduli and/or porosity, and to develop suitable processing techniques to access these structures. Manufacturing processes of layered structures employ often organic solvents mostly causing environmental pollution. In this regard, the studied bilayer structures here were manufactured by processes free of organic solvents. In this thesis, three bilayer systems were studied to answer the individual questions. First, while various methods of introducing pores in melt-phase are reported for one-layer constructs with simple geometry, can such methods be applied to a bilayer structure, giving two porous layers? This was addressed with Bilayer System 1. Two porous layers were obtained from melt-blending of two different polyurethanes (PU) and polyvinyl alcohol (PVA) in a co-continuous phase followed by sequential injection molding and leaching the PVA phase in deionized water. A porosity of 50 ± 5% with a high interconnectivity was obtained, in which the pore sizes in both layers ranged from 1 µm to 100 µm with an average of 22 µm in both layers. The obtained pores were tailored by applying an annealing treatment at relevant high temperatures of 110 °C and 130 °C, which allowed the porosity to be kept constant. The disadvantage of this system is that a maximum of 50% porosity could be reached and removal of leaching material in the weld line section of both layers is not guaranteed. Such a construct serves as a model for bilayer porous structure for determining structure-property relationships with respect to the pore size, porosity and mechanical properties of each layer. This fabrication method is also applicable to complex geometries by designing a relevant mold for injection molding. Secondly, utilizing scCO2 foaming process at elevated temperature and pressure is considered as a green manufacturing process. Employing this method as a post-treatment can alter the history orientation of polymer chains created by previous fabrication methods. Can a bilayer structure be fabricated by a combination of sequential injection molding and scCO2 foaming process, in which a porous layer is supported by a compact layer? Such a construct (Bilayer System 2) was generated by sequential injection molding of a PCL (Tm ≈ 58 °C) layer and a PLLA (Tg ≈ 58 °C) layer. Soaking this structure in the autoclave with scCO2 at T = 45 °C and P = 100 bar led to the selective foaming of PCL with a porosity of 80%, while the PLA layer was kept compact. The scCO2 autoclave led to the formation of a porous core and skin layer of the PCL, however, the degree of crystallinity of PLLA layer increased from 0 to 50% at the defined temperature and pressure. The microcellular structure of PCL as well as the degree of crystallinity of PLLA were controlled by increasing soaking time. Thirdly, wrinkles on surfaces in micro/nano scale alter the properties, which are surface-related. Wrinkles are formed on a surface of a bilayer structure having a compliant substrate and a stiff thin film. However, the reported wrinkles were not reversible. Moreover, dynamic wrinkles in nano and micro scale have numerous examples in nature such as gecko foot hair offering reversible adhesion and an ability of lotus leaves for self-cleaning altering hydrophobicity of the surface. It was envisioned to imitate this biomimetic function on the bilayer structure, where self-assembly on/off patterns would be realized on the surface of this construct. In summary, developing layered constructs having different properties/functions in the individual layer or exhibiting a new function as the consequence of layered structure can give novel insight for designing layered constructs in various disciplines such as packaging and transport industry, aerospace industry and health technology. N2 - Schichtstrukturen sind in der Natur und in Industrieprodukten allgegenwärtig, wobei die einzelnen Schichten unterschiedliche mechanische/thermische Eigenschaften und Funktionen haben können, die unabhängig voneinander zur Leistungsfähigkeit der gesamten Schichtstruktur für die jeweilige Anwendung beitragen. Die individuelle Abstimmung jeder einzelnen Schicht wirkt sich auf die Leistungsfähigkeit des gesamten Schichtsystems aus. Poren werden in verschiedenen Bereichen eingesetzt, in denen eine geringe Dichte, aber eine große Oberfläche erforderlich ist. Außerdem können offene und miteinander verbundene Poren als Übertragungskanal für chemische Gast-Moleküle dienen. Die Form der Poren beeinflusst das Kompressionsverhalten des Materials. In diesem Zusammenhang zielte diese Arbeit darauf ab, neue Funktionen in zweischichtigen Systemen durch die Kombination von Schichten mit unterschiedlichen Modulen und/oder Porosität zu erzeugen und geeignete Verarbeitungstechniken zu entwickeln, um diese Strukturen zu erreichen. Bei der Herstellung von Schichtstrukturen werden häufig organische Lösungsmittel verwendet, die meist eine Umweltbelastung darstellen. Daher wurden die hier untersuchten Doppelschichtstrukturen mit Verfahren hergestellt, die frei von organischen Lösungsmitteln sind. In dieser Arbeit wurden drei Doppelschichtsysteme untersucht, um die einzelnen Fragen zu beantworten. Erstens: Während verschiedene Methoden zur Einführung von Poren in der Schmelzphase für einschichtige Konstruktionen mit einfacher Geometrie bekannt sind, stellt sich die Frage, ob solche Methoden sich auf eine zweischichtige Struktur anwenden lassen und somit zwei unterschiedlich poröse Schichten ergibt? Dies wurde mit dem Zweischichtsystem 1 untersucht. Zwei poröse Schichten wurden durch das Mischen in der Schmelze von zwei verschiedenen Polyurethanen (PU) und Polyvinylalkohol (PVA) in einer co-kontinuierlichen Phase erhalten. Es folgte sequentielles Spritzgießen und das Entfernen der PVA-Phase durch „Leaching“ in entionisiertem Wasser. Es wurde eine Porosität von 50 ± 5 % mit einer hohen Interkonnektivität erzielt, wobei die Porengrößen in beiden Schichten zwischen 1 µm und 100 µm lagen, mit einem Durchschnittswert von 22 µm in beiden Schichten. Diese Herstellungsmethode ist auch auf komplexe Geometrien anwendbar, es muss lediglich eine entsprechende Form für das Spritzgießen entworfen werden. Zweitens: die Verwendung des scCO2-Schäumungsverfahrens bei erhöhter Temperatur und erhöhtem Druck wird als umweltfreundlicher Herstellungsprozess betrachtet. Durch den Einsatz dieser Methode als Nachbehandlung kann die Historie der Ausrichtung der Polymerketten, die durch frühere Herstellungsmethoden entstanden ist, verändert werden. Kann eine zweischichtige Struktur durch eine Kombination aus sequentiellem Spritzgießen und scCO2-Schäumverfahren hergestellt werden, bei der eine poröse Schicht von einer kompakten Schicht getragen wird? Ein solches Konstrukt (Bilayer System 2) wurde durch sequentielles Spritzgießen einer PCL-Schicht (Tm ≈ 58 °C) und einer PLLA-Schicht (Tg ≈ 58 °C) erzeugt. Das Einweichen dieser Struktur in scCO2 im Autoklaven bei T = 45 °C und P = 100 bar führte zum selektiven Aufschäumen von PCL mit einer Porosität von 80%, während die PLA-Schicht unverschäumt blieb. Die Behandlung im scCO2-Autoklav führte zur Bildung einer porösen Kern- und Hautschicht des PCL, während der Kristallinitätsgrad der PLLA-Schicht bei der definierten Temperatur und dem definierten Druck von 0 auf 50 % anstieg. Die mikrozelluläre Struktur von PCL sowie der Kristallinitätsgrad von PLLA wurden durch die Erhöhung der Einweichzeit gesteuert. Drittens verändern Falten auf Oberflächen im Mikro-/Nanomaßstab die Eigenschaften, die mit der Oberfläche zusammenhängen. Falten bilden sich auf der Oberfläche einer zweischichtigen Struktur mit einem nachgiebigen Substrat und einem steifen dünnen Film. Die Falten waren jedoch nicht reversibel. Darüber hinaus gibt es in der Natur zahlreiche Beispiele für dynamische Falten im Nano- und Mikromaßstab, wie z. B. Gecko-Fußhaare, die eine reversible Adhäsion ermöglichen, und die Fähigkeit von Lotusblättern, sich selbst zu reinigen, indem sie die Hydrophobizität der Oberfläche verändern. Diese biomimetische Funktion sollte auf der Doppelschichtstruktur nachgeahmt werden, wobei auf der Oberfläche dieses Konstrukts selbstorganisierende On/Off-Muster realisiert werden sollten. Zusammenfassend kann gesagt werden, dass die Entwicklung geschichteter Konstrukte mit unterschiedlichen Eigenschaften/Funktionen in den einzelnen Schichten oder mit einer neuen Funktion als Folge der geschichteten Struktur neue Erkenntnisse für den Entwurf geschichteter Konstrukte in verschiedenen Disziplinen wie der Verpackungs- und Transportindustrie, der Luft- und Raumfahrtindustrie und der Gesundheitstechnologie liefern kann. T2 - Studie zur Herstellung multifunktionaler Doppelschichtsysteme KW - bilayer system KW - biomaterials KW - wrinkles KW - polymer KW - injection molding KW - Doppelschichtstruktur KW - Biomaterialien KW - poröse Struktur KW - Falten KW - Spritzgießen Y1 - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-601968 ER - TY - JOUR A1 - Abbasi, Ali A1 - Xu, Yaolin A1 - Khezri, Ramin A1 - Etesami, Mohammad A1 - Lin, C. A1 - Kheawhom, Soorathep A1 - Lu, Yan T1 - Advances in characteristics improvement of polymeric membranes/separators for zinc-air batteries JF - Materials Today Sustainability N2 - Zinc-air batteries (ZABs) are gaining popularity for a wide range of applications due to their high energy density, excellent safety, and environmental friendliness. A membrane/separator is a critical component of ZABs, with substantial implications for battery performance and stability, particularly in the case of a battery in solid state format, which has captured increased attention in recent years. In this review, recent advances as well as insight into the architecture of polymeric membrane/separators for ZABs including porous polymer separators (PPSs), gel polymer electrolytes (GPEs), solid polymer electrolytes (SPEs) and anion exchange membranes (AEMs) are discussed. The paper puts forward strategies to enhance stability, ionic conductivity, ionic selectivity, electrolyte storage capacity and mechanical properties for each type of polymeric membrane. In addition, the remaining major obstacles as well as the most potential avenues for future research are examined in detail. KW - Ionic selectivity KW - Ionic conductivity KW - Gel polymer KW - Ion exchange KW - Porous KW - polymer Y1 - 2022 U6 - https://doi.org/10.1016/j.mtsust.2022.100126 SN - 2589-2347 VL - 18 PB - Elsevier CY - Amsterdam ER - TY - JOUR A1 - Behl, Marc A1 - Balk, Maria A1 - Mansfeld, Ulrich A1 - Lendlein, Andreas T1 - Phase morphology of multiblock copolymers differing in sequence of blocks JF - Macromolecular materials and engineering N2 - The chemical nature, the number length of integrated building blocks, as well as their sequence structure impact the phase morphology of multiblock copolymers (MBC) consisting of two non-miscible block types. It is hypothesized that a strictly alternating sequence should impact phase segregation. A library of well-defined MBC obtained by coupling oligo(epsilon-caprolactone) (OCL) of different molecular weights (2, 4, and 8 kDa) with oligotetrahydrofuran (OTHF, 2.9 kDa) via Steglich esterification results in strictly alternating (MBCalt) or random (MBCran) MBC. The three different series has a weight average molecular weight (M-w) of 65 000, 165 000, and 168 000 g mol(-1) for MBCalt and 80 500, 100 000, and 147 600 g mol(-1) for MBCran. When the chain length of OCL building blocks is increased, the tendency for phase segregation is facilitated, which is attributed to the decrease in chain mobility within the MBC. Furthermore, it is found that the phase segregation disturbs the crystallization by causing heterogeneities in the semi-crystalline alignment, which is attributed to an increase of the disorder of the OCL semi-crystalline alignment. KW - electron microscopy KW - multiblock copolymers KW - phase morphology KW - polymer KW - libraries KW - sequence structures KW - wide angle x‐ ray scattering Y1 - 2021 U6 - https://doi.org/10.1002/mame.202000672 SN - 1439-2054 VL - 306 IS - 3 PB - Wiley-VCH CY - Weinheim ER - TY - THES A1 - Saretia, Shivam T1 - Modulating ultrathin films of semi-crystalline oligomers by Langmuir technique T1 - Modulation ultradünner Filme aus semikristalliner Oligomere durch Langmuir-Technik N2 - Polymeric films and coatings derived from semi-crystalline oligomers are of relevance for medical and pharmaceutical applications. In this context, the material surface is of particular importance, as it mediates the interaction with the biological system. Two dimensional (2D) systems and ultrathin films are used to model this interface. However, conventional techniques for their preparation, such as spin coating or dip coating, have disadvantages, since the morphology and chain packing of the generated films can only be controlled to a limited extent and adsorption on the substrate used affects the behavior of the films. Detaching and transferring the films prepared by such techniques requires additional sacrificial or supporting layers, and free-standing or self supporting domains are usually of very limited lateral extension. The aim of this thesis is to study and modulate crystallization, melting, degradation and chemical reactions in ultrathin films of oligo(ε-caprolactone)s (OCL)s with different end-groups under ambient conditions. Here, oligomeric ultrathin films are assembled at the air-water interface using the Langmuir technique. The water surface allows lateral movement and aggregation of the oligomers, which, unlike solid substrates, enables dynamic physical and chemical interaction of the molecules. Parameters like surface pressure (π), temperature and mean molecular area (MMA) allow controlled assembly and manipulation of oligomer molecules when using the Langmuir technique. The π-MMA isotherms, Brewster angle microscopy (BAM), and interfacial infrared spectroscopy assist in detecting morphological and physicochemical changes in the film. Ultrathin films can be easily transferred to the solid silicon surface via Langmuir Schaefer (LS) method (horizontal substrate dipping). Here, the films transferred on silicon are investigated using atomic force microscopy (AFM) and optical microscopy and are compared to the films on the water surface. The semi-crystalline morphology (lamellar thicknesses, crystal number densities, and lateral crystal dimensions) is tuned by the chemical structure of the OCL end-groups (hydroxy or methacrylate) and by the crystallization temperature (Tc; 12 or 21 °C) or MMAs. Compression to lower MMA of ~2 Å2, results in the formation of a highly crystalline film, which consists of tightly packed single crystals. Preparation of tightly packed single crystals on a cm2 scale is not possible by conventional techniques. Upon transfer to a solid surface, these films retain their crystalline morphology whereas amorphous films undergo dewetting. The melting temperature (Tm) of OCL single crystals at the water and the solid surface is found proportional to the inverse crystal thickness and is generally lower than the Tm of bulk PCL. The impact of OCL end-groups on melting behavior is most noticeable at the air-solid interface, where the methacrylate end-capped OCL (OCDME) melted at lower temperatures than the hydroxy end-capped OCL (OCDOL). When comparing the underlying substrate, melting/recrystallization of OCL ultrathin films is possible at lower temperatures at the air water interface than at the air-solid interface, where recrystallization is not visible. Recrystallization at the air-water interface usually occurs at a higher temperature than the initial Tc. Controlled degradation is crucial for the predictable performance of degradable polymeric biomaterials. Degradation of ultrathin films is carried out under acidic (pH ~ 1) or enzymatic catalysis (lipase from Pseudomonas cepcia) on the water surface or on a silicon surface as transferred films. A high crystallinity strongly reduces the hydrolytic but not the enzymatic degradation rate. As an influence of end-groups, the methacrylate end-capped linear oligomer, OCDME (~85 ± 2 % end-group functionalization) hydrolytically degrades faster than the hydroxy end capped linear oligomer, OCDOL (~95 ± 3 % end-group functionalization) at different temperatures. Differences in the acceleration of hydrolytic degradation of semi-crystalline films were observed upon complete melting, partial melting of the crystals, or by heating to temperatures close to Tm. Therefore, films of densely packed single crystals are suitable as barrier layers with thermally switchable degradation rates. Chemical modification in ultrathin films is an intricate process applicable to connect functionalized molecules, impart stability or create stimuli-sensitive cross-links. The reaction of end-groups is explored for transferred single crystals on a solid surface or amorphous monolayer at the air-water interface. Bulky methacrylate end-groups are expelled to the crystal surface during chain-folded crystallization. The density of end-groups is inversely proportional to molecular weight and hence very pronounced for oligomers. The methacrylate end-groups at the crystal surface, which are present at high concentration, can be used for further chemical functionalization. This is demonstrated by fluorescence microscopy after reaction with fluorescein dimethacrylate. The thermoswitching behavior (melting and recrystallization) of fluorescein functionalized single crystals shows the temperature-dependent distribution of the chemically linked fluorescein moieties, which are accumulated on the surfaces of crystals, and homogeneously dispersed when the crystals are molten. In amorphous monolayers at the air-water interface, reversible cross-linking of hydroxy-terminated oligo(ε-caprolactone) monolayers using dialdehyde (glyoxal) lead to the formation of 2D networks. Pronounced contraction in the area occurred for 2D OCL films in dependence of surface pressure and time indicating the reaction progress. Cross linking inhibited crystallization and retarded enzymatic degradation of the OCL film. Altering the subphase pH to ~2 led to cleavage of the covalent acetal cross-links. Besides as model systems, these reversibly cross-linked films are applicable for drug delivery systems or cell substrates modulating adhesion at biointerfaces. N2 - Ultradünne Filme/Beschichtungen aus semikristallinen oligomeren Makromolekülen sind für medizinische und pharmazeutische Anwendungen von Bedeutung. Dabei kommt der Materialoberfläche eine besondere Bedeutung zu, da diese die Interaktion mit dem umgebenden biologischen System ermöglicht. Zur Modellierung der Oberfläche werden 2D Systeme und ultradünne Filme verwendet. Herkömmlichen Techniken zu deren Präparation wie Spin-Coating oder Dip-Coating haben jedoch Nachteile, da sich die Morphologie und Kettenpackung der erzeugten Filme nur sehr bedingt kontrollieren lässt und sich die Adsorption auf dem verwendeten Substrat auf das Verhalten der Filme auswirkt. Zum Ablösen oder Übertragen der mit Hilfe dieser Techniken hergestellten Filme sind zusätzliche Opfer- oder Transferschichten erforderlich. Zudem können mit diesen Methoden nur freistehende oder selbsttragende Filme von sehr geringer lateraler Ausdehnung hergestellt werden. Das Ziel dieser Arbeit ist es, Kristallisation, Schmelzen, Abbau und chemische Reaktionen in ultradünnen Filmen von Oligo(ε-caprolacton)en (OCL)s mit unterschiedlichen Endgruppen unter Umgebungsbedingungen zu untersuchen und zu kontrollieren. Dazu wurden ultradünne Filme an der Luft-Wasser-Grenzfläche mit der Langmuir-Technik erzeugt. Die Wasseroberfläche erlaubt eine ungestörte Bewegung und Aggregation der Oligomere, was, im Gegensatz zu festen Substraten, dynamische physikalische und chemische Interaktion der Moleküle miteinander ermöglicht. Die Langmuir-Technik erlaubt mit Hilfe von Parametern wie Temperatur, Oberflächendruck (π) und Fläche pro Wiederholheinheit eine kontrollierte Manipulation der Oligomere. Kompressionsiothermen, Brewster-Winkelmikroskopie und Grenzflächen-Infrarotspektroskopie halfen beim Nachweis morphologischer und physikalisch-chemischer Veränderungen im Film. Die ultradünnen Filme wurden über das Langmuir-Schäfer-Verfahren (Kontakt mit Substrat in paralleler Orientierung zur Grenzfläche) auf Siliziumsubstrate übertragen. Danach wurden die übertragenen Filme mittels AFM und optischer Mikroskopie untersucht und mit Filmen an der Wasseroberfläche verglichen. Die teilkristalline Morphologie (Lamellendicke, Kristallzahldichte und laterale Dimension der Kristalle) von Polymerfilmen kann durch die chemische Struktur der OCL-Endgruppen (Hydroxy oder Methacrylat) und durch die Kristallisationstemperatur (Tc; 12 oder 21 °C) oder die Fläche pro Wiederholeinheit beeinflusst werden. Die Kompression auf eine sehr kleine Fläche pro Wiederholeinheit von ~2 Å2 führt zur Bildung eines hochkristallinen Films, der aus dicht gepackten Einkristallen besteht. Eine Synthese von derartigen Filmen im cm2 Maßstab ist mit herkömmlichen Techniken nicht möglich. Nach Übertragung auf eine feste Oberfläche behielten die teilkristallinen Filme ihre Morphologie, während amorphe Filme das für Polymere charakteristische Entnetzungsverhalten aufwiesen. Die Schmelztemperaturen (Tm) von OCL-Einkristallen an der Wasser- und Festkörperoberfläche waren proportional zur inversen Kristalldicke und im Allgemeinen niedriger als die Tm von PCL im Festkörper. Der Einfluss der OCL-Endgruppen auf das Schmelzverhalten war an der Luft-Feststoff-Grenzfläche am deutlichsten, wo OCL mit Methacrylat-Endgruppen bei niedrigeren Temperaturen schmolz als OCL mit Hydroxyl-Endgruppen. Das Schmelzen/Rekristallisieren ultradünner OCL-Filme an der Luft-Wasser-Grenzfläche erfolgte bei niedrigeren Temperaturen als an der Luft-Feststoff-Grenzfläche, wo keine Rekristallisation beobachtet wurde. Die Rekristallisation geschmolzener Filme an der Luft-Wasser-Grenzfläche erfolgte normalerweise bei einer höheren Temperatur als der anfänglichen Tc. Der kontrollierte Abbau ist entscheidend für die Performance von abbaubaren Polymeren als Biomaterialien. Der Abbau ultradünner Filme erfolgte hydrolytisch entweder unter saurer (pH ~ 1) oder enzymatischer Katalyse (Lipase aus Pseudomonas cepcia) auf der Wasseroberfläche oder als übertragene Filme auf Siliziumoberflächen. Eine hohe Kristallinität reduzierte die hydrolytische Abbaurate stark, aber die enzymatische dagegen wenig. Das lineare Oligomer mit Methacrylat Endgruppen (~85 ± 2 % Endgruppenfunktionalisierung) wurde bei unterschiedlichen Temperaturen schneller hydrolytisch abgebaut als das lineare Oligomer mit Hydroxyl Endgruppen (~95 ± 3 % Endgruppenfunktionalisierung). Unterschiede in der Beschleunigung des hydrolytischen Abbaus von teilkristallinen Filmen wurden beim vollständigen Schmelzen, teilweisen Schmelzen der Kristalle, oder durch erwärmen in die Nähe von Tm beobachtet. Daher eignen sich Filme aus dicht gepackten Einkristallen als Barriereschichten mit thermisch schaltbarer Degradationsrate. Chemische Reaktionen in ultradünnen Filmen können angewandt werden, um funktionalisierte Moleküle zu verbinden und ihnen Stabilität zu verleihen oder Stimuli-sensitive Vernetzungen zu erzeugen. Hier wurden die Reaktionen der Endgruppen transferierter Einkristalle auf festen Oberflächen und amorphen Monoschichten an der Luft-Wasser-Grenzfläche untersucht. Da die Kettenenden defekte in den Einkristallen darstellen würden, werden sie bei der Kristallisation an der Kristalloberfläche angeordnet. Die Dichte der Endgruppen ist umgekehrt proportional zum Molekulargewicht und daher bei Oligomeren besonders hoch. Hier wurden mit Methacrylatendgruppen versehene OCL Moleküle verwendet. Diese Gruppen können chemisch weiter umgesetzt und für eine Funktionalisierung der Kirstalle verwendet werden. Dies wurde fluoreszenz-mikroskopisch nach der Reaktion mit Fluoresceindimethacrylat nachgewiesen. Das thermische Schalten (Schmelzen und Umkristallisieren) von Fluorescein-funktionalisierten Einkristallen erzeugt eine temperaturabhängige Verteilung der chemisch verknüpften Fluorescein-Einheiten, die sich auf den Oberflächen der Kristalle ansammeln und beim Schmelzen der Kristalle homogen dispergiert werden. In amorphen Monoschichten an der Luft-Wasser-Grenzfläche führt die reversible Vernetzung von Hydroxy-terminierten Oligo(ε-caprolacton) Monoschichten unter Verwendung eines Dialdehyds (Glyoxal) zur Bildung von zweidimensionalen (2D) Netzwerken. Bei 2D-OCL-Filmen trat eine ausgeprägte Kontraktion der Fläche in Abhängigkeit von Oberflächendruck und Zeit auf, was den Fortschritt der Reaktion anzeigte. Die Vernetzung hemmte die Kristallisation und verzögerte den enzymatischen Abbau des OCL-Films. Eine Änderung des pH-Wertes der Subphase auf ~2 führte zur Spaltung der kovalenten Acetalvernetzungen. Außer als Modellsysteme wäre der Einsatz dieser reversibel vernetzten Filme für den Einsatz als Drug-Delivery-Systeme oder als Oberflächen zur Steuerung der Adhäsion von Zellen möglich. KW - polymer KW - poly(ε-caprolactone) KW - 2D material KW - ultrathin film KW - single crystals KW - crystallization KW - melting KW - degradation KW - hydrolysis KW - reactions KW - substrate KW - end-groups KW - hydroxy KW - methacrylate KW - Polymer KW - Poly(ε-caprolacton) KW - 2D-Material KW - Beschichtungen KW - Ultradünne Filme KW - Einkristalle KW - Kristallisation KW - Schmelz KW - Abbau KW - Hydrolyse KW - Reaktion KW - Substrat KW - Hydroxyl KW - Methacrylat Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-542108 ER - TY - JOUR A1 - Lützow, Karola A1 - Weigel, Thomas A1 - Lendlein, Andreas T1 - Solvent-based fabrication method for magnetic, shape-memory nanocomposite foams JF - MRS advances N2 - This paper presents shape-memory foams that can be temporarily fixed in their compressed state and be expanded on demand. Highly porous, nanocomposite foams were prepared from a solution of polyetherurethane with suspended nanoparticles (mean aggregate size 90 nm) which have an iron(III) oxide core with a silica shell. The polymer solution with suspended nanoparticles was cooled down to -20 degrees C in a two-stage process, which was followed by freeze-drying. The average pore size increases with decreasing concentration of nanoparticles from 158 mu m to 230 mu m while the foam porosity remained constant. After fixation of a temporary form of the nanocomposite foams, shape recovery can be triggered either by heat or by exposure to an alternating magnetic field. Compressed foams showed a recovery rate of up to 76 +/- 4% in a thermochamber at 80 degrees C, and a slightly lower recovery rate of up to 65 +/- 4% in a magnetic field. KW - composite KW - foam KW - polymer KW - magnetic KW - shape memory Y1 - 2020 U6 - https://doi.org/10.1557/adv.2019.422 SN - 2059-8521 VL - 5 IS - 14-15 SP - 785 EP - 795 PB - Cambridge Univ. Press CY - Cambridge ER - TY - JOUR A1 - Behl, Marc A1 - Zhao, Qian A1 - Lendlein, Andreas T1 - Glucose-responsive shape-memory cryogels JF - Journal of materials research : JMR N2 - Boronic ester bonds can be reversibly formed between phenylboronic acid (PBA) and triol moieties. Here, we aim at a glucose-induced shape-memory effect by implementing such bonds as temporary netpoints, which are cleavable by glucose and by minimizing the volume change upon stimulation by a porous cryogel structure. The polymer system consisted of a semi-interpenetrating network (semi-IPN) architecture, in which the triol moieties were part of the permanent network and the PBA moieties were located in the linear polymer diffused into the semi-IPN. In an alkaline medium (pH = 10), the swelling ratio was approximately 35, independent of C-glu varied between 0 and 300 mg/dL. In bending experiments, shape fixity R-f approximate to 80% and shape recovery R-r approximate to 100% from five programming/recovery cycles could be determined. R-r was a function of C-glu in the range from 0 to 300 mg/dL, which accords with the fluctuation range of C-glu in human blood. In this way, the shape-memory hydrogels could play a role in future diabetes treatment options. KW - shape memory KW - polymer KW - porosity Y1 - 2020 U6 - https://doi.org/10.1557/jmr.2020.204 SN - 0884-2914 SN - 2044-5326 VL - 35 IS - 18 SP - 2396 EP - 2404 PB - Springer CY - Berlin ER - TY - JOUR A1 - Balk, Maria A1 - Behl, Marc A1 - Lendlein, Andreas T1 - Actuators based on oligo[(epsilon-caprolactone)-co-glycolide] with accelerated hydrolytic degradation JF - MRS advances : a journal of the Materials Research Society (MRS) N2 - Polyester-based shape-memory polymer actuators are multifunctional materials providing reversible macroscopic shape shifts as well as hydrolytic degradability. Here, the function-function interdependencies (between shape shifts and degradation behaviour) will determine actuation performance and its life time. In this work, glycolide units were incorporated in poly(epsilon-caprolactone) based actuator materials in order to achieve an accelerated hydrolytic degradation and to explore the function-function relationship. Three different oligo[(epsilon-caprolactone)-co-glycolide] copolymers (OCGs) with similar molecular weights (10.5 +/- 0.5 kg center dot mol(-1)) including a glycolide content of 8, 16, and 26 mol% (ratio 1:1:1 wt%) terminated with methacrylated moieties were crosslinked. The obtained actuators provided a broad melting transition in the range from 27 to 44 degrees C. The hydrolytic degradation of programmed OCG actuators (200% of elongation) resulted in a reduction of sample mass to 51 wt% within 21 days at pH = 7.4 and 40 degrees C. Degradation results in a decrease of T-m associated to the actuating units and increasing T-m associated to the skeleton forming units. The actuation capability decreased almost linear as function of time. After 11 days of hydrolytic degradation the shape-memory functionality was lost. Accordingly, a fast degradation behaviour as required, e.g., for actuator materials intended as implant material can be realized. KW - actuation KW - shape memory KW - polymer KW - crystalline Y1 - 2020 U6 - https://doi.org/10.1557/adv.2019.447 SN - 2059-8521 VL - 5 IS - 12-13 SP - 655 EP - 666 PB - Cambridge University Press CY - New York, NY ER - TY - JOUR A1 - Izraylit, Victor A1 - Gould, Oliver E. C. A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Investigating the phase-morphology of PLLA-PCL multiblock copolymer/PDLA blends cross-linked using stereocomplexation JF - MRS advances N2 - The macroscale function of multicomponent polymeric materials is dependent on their phase-morphology. Here, we investigate the morphological structure of a multiblock copolymer consisting of poly(L-lactide) and poly(epsilon-caprolactone) segments (PLLA-PCL), physically cross-linked by stereocomplexation with a low molecular weight poly(D-lactide) oligomer (PDLA). The effects of blend composition and PLLA-PCL molecular structure on the morphology are elucidated by AFM, TEM and SAXS. We identify the formation of a lattice pattern, composed of PLA domains within a PCL matrix, with an average domain spacing d0 = 12 - 19 nm. The size of the PLA domains were found to be proportional to the block length of the PCL segment of the copolymer and inversely proportional to the PDLA content of the blend. Changing the PLLA-PCL / PDLA ratio caused a shift in the melt transition Tm attributed to the PLA stereocomplex crystallites, indicating partial amorphous phase dilution of the PLA and PCL components within the semicrystalline material. By elucidating the phase structure and thermal character of multifunctional PLLA-PCL / PDLA blends, we illustrate how composition affects the internal structure and thermal properties of multicomponent polymeric materials. This study should facilitate the more effective incorporation of a variety of polymeric structural units capable of stimuli responsive phase transitions, where an understanding the phase-morphology of each component will enable the production of multifunctional soft-actuators with enhanced performance. KW - polymer KW - blend KW - nanostructure KW - morphology Y1 - 2020 U6 - https://doi.org/10.1557/adv.2019.465 SN - 2059-8521 VL - 5 IS - 14-15 SP - 699 EP - 707 PB - Cambridge Univ. Press CY - New York ER - TY - THES A1 - Noack, Sebastian T1 - Poly(lactide)-based amphiphilic block copolymers T1 - Polylactid-basierte amphiphile Blockcopolymere BT - self-assembly and stereocomplexation in aqueous media BT - Selbstorganisation und Stereokomplexierung in wässrigem Medium N2 - Due to its bioavailability and (bio)degradability, poly(lactide) (PLA) is an interesting polymer that is already being used as packaging material, surgical seam, and drug delivery system. Dependent on various parameters such as polymer composition, amphiphilicity, sample preparation, and the enantiomeric purity of lactide, PLA in an amphiphilic block copolymer can affect the self-assembly behavior dramatically. However, sizes and shapes of aggregates have a critical effect on the interactions between biological and drug delivery systems, where the general understanding of these polymers and their ability to influence self-assembly is of significant interest in science. The first part of this thesis describes the synthesis and study of a series of linear poly(L-lactide) (PLLA) and poly(D-lactide) (PDLA)-based amphiphilic block copolymers with varying PLA (hydrophobic), and poly(ethylene glycol) (PEG) (hydrophilic) chain lengths and different block copolymer sequences (PEG-PLA and PLA-PEG). The PEG-PLA block copolymers were synthesized by ring-opening polymerization of lactide initiated by a PEG-OH macroinitiator. In contrast, the PLA-PEG block copolymers were produced by a Steglich-esterification of modified PLA with PEG-OH. The aqueous self-assembly at room temperature of the enantiomerically pure PLLA-based block copolymers and their stereocomplexed mixtures was investigated by dynamic light scattering (DLS), transmission electron microscopy (TEM), wide-angle X-ray diffraction (WAXD), and differential scanning calorimetry (DSC). Spherical micelles and worm-like structures were produced, whereby the obtained self-assembled morphologies were affected by the lactide weight fraction in the block copolymer and self-assembly time. The formation of worm-like structures increases with decreasing PLA-chain length and arises from spherical micelles, which become colloidally unstable and undergo an epitaxial fusion with other micelles. As shown by DSC experiments, the crystallinity of the corresponding PLA blocks increases within the self-assembly time. However, the stereocomplexed self-assembled structures behave differently from the parent polymers and result in irregular-shaped clusters of spherical micelles. Additionally, time-dependent self-assembly experiments showed a transformation, from already self-assembled morphologies of different shapes to more compact micelles upon stereocomplexation. In the second part of this thesis, with the objective to influence the self-assembly of PLA-based block copolymers and its stereocomplexes, poly(methyl phosphonate) (PMeP) and poly(isopropyl phosphonate) (PiPrP) were produced by ring-opening polymerization to implement an alternative to the hydrophilic block PEG. Although, the 1,8 diazabicyclo[5.4.0]unde 7 ene (DBU) or 1,5,7 triazabicyclo[4.4.0]dec-5-ene (TBD) mediated synthesis of the corresponding poly(alkyl phosphonate)s was successful, however, not so the polymerization of copolymers with PLA-based precursors (PLA-homo polymers, and PEG-PLA block copolymers). Transesterification, obtained by 1H-NMR spectroscopy, between the poly(phosphonate)- and PLA block caused a high-field shifted peak split of the methine proton in the PLA polymer chain, with split intensities depending on the used catalyst (DBU for PMeP, and TBD for PiPrP polymerization). An additional prepared block copolymer PiPrP-PLLA that wasn’t affected in its polymer sequence was finally used for self-assembly experiments with PLA-PEG and PEG-PLA mixing. This work provides a comprehensive study of the self-assembly behavior of PLA-based block copolymers influenced by various parameters such as polymer block lengths, self-assembly time, and stereocomplexation of block copolymer mixtures. N2 - Aufgrund seiner Bioverfügbarkeit und (biologischen) Abbaubarkeit stellt Polylactid (PLA) ein interessantes Polymer dar, welches bereits in Verpackungsmaterialien, chirurgische Fäden und in selbst organisierten Wirkstofftransportsystemen eingesetzt wird. Als ein Teil von amphiphilen Blockcopolymeren kann PLA die molekulare Selbstorganisation in wässrigen Lösungen wesentlich beeinflussen. Die gebildeten Strukturen sind dabei essenziell von Faktoren wie der Blockcopolymer Zusammensetzung, Amphiphilie, Proben Vorbereitung und der Enantiomerenreinheit des Monomers abhängig. Die Kenntnis über die beschriebenen Faktoren und das allgemeine Verständnis für die dazugehörigen Polymere sowie die Möglichkeit ihre Selbstorganisation zu beeinflussen, ist von entscheidender Bedeutung in biomedizinischen Anwendungen. Unterschiedliche Größen oder Formen der selbst organisierten Wirkstoffträgern haben einen erheblichen Effekt auf die Wechselwirkung mit dem entsprechenden biologischen System und somit einen essenziellen Einfluss auf den Ausgang der medikamentösen Therapie. Der erste Teil dieser Doktorarbeit beschreibt die Synthese und Untersuchung einer Serie von Poly(L-Lactid) (PLLA) und Poly(D-Lactid) (PDLA)-basierten amphiphilen Blockcopolymeren mit variierenden PLA (hydrophob) und Polyethylenglycol (PEG) (hydrophil) Kettenlägen, sowie unterschiedlichen Polymersequenzen (PEG-PLA und PLA-PEG). Die genannten PEG-PLA Blockcopolymere wurden mittels organokatalysierter ringöffnender Polymerisation (ROP) hergestellt, wobei das entsprechende PEG-OH als Makroinitiator diente. Im Gegensatz dazu mussten die entsprechenden PLA-PEG Blockcopolymere mittels Steglich Veresterung von modifizierten PLA mit PEG-OH hergestellt werden. Die Selbstorganisation der PLLA-basierten Blockcopolymeren und deren stereokomplexierten Mischungen in wässriger Lösung erfolgte unter Raumtemperatur und wurde mittels Dynamischer Lichtstreuung (DLS), Transmissionselektronenmikroskopie (TEM), Röntgenstrukturanalyse und Dynamische Differenzkalorimetrie (DSC) untersucht. Dabei wurden kugel- und wurmförmige Strukturen beobachtet, wobei die gebildeten Strukturen vom Lactid Gewichtsanteil im Polymer, sowie der Selbstorganisationszeit abhängig waren. Mit andauernder Selbstorganisation und zunehmender Kristallinität wurden die zuerst gebildeten kugelförmigen Strukturen kolloidal unstabil und es erfolgte ein epitaktisches Wachstum zu wurmförmigen Strukturen in Abhängigkeit der Lactid Kettenlänge. Die stereokomplexierten Blockcopolymer Mischungen hingegen bildeten, unabhängig von der Copolymersequenz der entsprechenden Polymer Partner, hauptsächlich unregelmäßige Ansammlungen kugelförmiger Strukturen welche den Eindruck einer Perlenkette erweckten. Mit dem Einsetzen der Stereokomplexierung zeigten zeitlich aufgelöste Selbstorganisationsexperimente eine Transformation von bereits gebildeten Strukturen verschiedenster Formen und Größen (Polymer abhängig) zu kompakten Mizellen. Im zweiten Teil dieser Doktorarbeit wurden, mit dem Ziel die Selbstorganisation von PLA-basierten Blockcopolymeren und deren Stereokomplexmischung vermehrt zu beeinflussen, zwei alternative Polymere zu PEG untersucht. Ähnlich wie PLA, konnten mittels organokatalysierter ROP Polymethylphosphonat (PMeP) und Polyisopropylphosphonat (PiPrP) erfolgreich hergestellt werden. Die Blockcopolymer Synthese mit PLA-basierten Polymervorgängern erwies sich jedoch als schwierig. Aufgrund einer Protonenpeakspaltung der Methingruppe in der PLA-Wiederholeinheit konnten mittels 1H-NMR Spektroskopie Umersterungsprozesse zwischen dem Polyalkylphosphonat- und PLA block nachgewiesen werden, welche in Abhängigkeit des verwendeten Katalysators (DBU oder TBD) unterschiedlich stark ausfielen. Das ebenfalls hergestellte PiPrP-PLLA Blockcopolymer wies keine Unregelmäßigkeiten in der Polymersequenz auf und wurde anschließend für Selbstorganisationsexperimente mit PLA-PEG und PEG-PLA genutzt. Diese Arbeit liefert eine umfangreiche Studie zur Selbstorganisation PLA-basierter Blockcopolymere und untersucht verschiedenste Einflussparameter wie Blocklängen, Selbstorganisationszeit und Stereokomplexierung in Polymermischungen. KW - polylactide KW - polymer KW - self-assembly KW - stereocomplexation KW - block copolymer KW - Polylactid KW - Polymer KW - Selbstorganisation KW - Stereokomplexierung KW - Block Copolymer Y1 - 2019 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-436168 ER - TY - THES A1 - Tan, Li T1 - Synthesis, assembly and thermo-responsivity of polymer-functionalized magnetic cobalt nanoparticles T1 - Synthese, Assemblierung und Temperatur-Responsivität von Polymer-funktionalisierten magnetischen Cobalt Nanopartikeln N2 - This thesis mainly covers the synthesis, surface modification, magnetic-field-induced assembly and thermo-responsive functionalization of superparamagnetic Co NPs initially stabilized by hydrophobic small molecules oleic acid (OA) and trioctylphosphine oxide (TOPO), as well as the synthesis of both superparamagnetic and ferromagnetic Co NPs by using end-functionalized-polystyrene as stabilizer. Co NPs, due to their excellent magnetic and catalytic properties, have great potential application in various fields, such as ferrofluids, catalysis, and magnetic resonance imaging (MRI). Superparamagnetic Co NPs are especially interesting, since they exhibit zero coercivity. They get magnetized in an external magnetic field and reach their saturation magnetization rapidly, but no magnetic moment remains after removal of the applied magnetic field. Therefore, they do not agglomerate in the body when they are used in biomedical applications. Normally, decomposition of metallic precursors at high temperature is one of the most important methods in preparation of monodisperse magnetic NPs, providing tunability in size and shape. Hydrophobic ligands like OA, TOPO and oleylamine are often used to both control the growth of NPs and protect them from agglomeration. The as-prepared magnetic NPs can be used in biological applications as long as they are transferred into water. Moreover, their supercrystal assemblies have the potential for high density data storage and electronic devices. In addition to small molecules, polymers can also be used as surfactants for the synthesis of ferromagnetic and superparamagnetic NPs by changing the reaction conditions. Therefore, chapter 2 gives an overview on the basic concept of synthesis, surface modification and self-assembly of magnetic nanoparticles. Various examples were used to illustrate the recent work. The hydrophobic Co NPs synthesized with small molecules as surfactants limit their biological applications, which require a hydrophilic or aqueous environment. Surface modification (e.g., ligand exchange) is a general idea for either phase transition or surface-functionalization. Therefore, in chapter 3, a ligand exchange process was conducted to functionalize the surface of Co NPs. PNIPAM is one of the most popular smart polymers and its lower critical solution temperature (LCST) is around 32 °C, with a reversible change in the conformation structure between hydrophobic and hydrophilic. The novel nanocomposites of superparamagnetic Co NPs and thermo-responsive PNIPAM are of great interest. Thus, well-defined superparamagnetic Co NPs were firstly synthesized through the thermolysis of cobalt carbonyl by using OA and TOPO as surfactants. A functional ATRP initiator, containing an amine (as anchoring group) and a 2-bromopropionate group (SI-ATRP initiator), was used to replace the original ligands. This process is rapid and facial for efficient surface functionalization and afterwards the Co NPs can be dispersed into polar solvent DMF without aggregation. FT-IR spectroscopy showed that the TOPO was completely replaced, but a small amount of OA remained on the surface. A TGA measurement allowed the calculation of the grafting density of the initiator as around 3.2 initiator/nm2. Then, the surface-initiated ATRP was conducted for the polymerization of NIPAM on the surface of Co NPs and rendered the nanocomposites water-dispersible. A temperature-dependent dynamic light scattering study showed the aggregation behavior of PNIPAM-coated Co NPs upon heating and this process was proven to be reversible. The combination of superparamagnetic and thermo-responsive properties in these hybrid nanoparticles is promising for future applications e.g. in biomedicine. In chapter 4, the magnetic-field-induced assembly of superparamagnetic cobalt nanoparticles both on solid substrates and at liquid-air interface was investigated. OA- and TOPO-coated Co NPs were synthesized via the thermolysis of cobalt carbonyl and dispersed into either hexane or toluene. The Co NP dispersion was dropped onto substrates (e.g., TEM grid, silicon wafer) and at liquid-air (water-air or ethylene glycol-air) interface. Due to the attractive dipolar interaction, 1-D chains formed in the presence of an external magnetic field. It is known that the concentration and the strength of the magnetic field can affect the assembly behavior of superparamagnetic Co NPs. Therefore, the influence of these two parameters on the morphology of the assemblies was studied. The formed 1-D chains were shorter and flexible at either lower concentration of the Co NP dispersion or lower strength of the external magnetic field due to thermal fluctuation. However, by increasing either the concentration of the NP dispersion or the strength of the applied magnetic field, these chains became longer, thicker and straighter. The reason could be that a high concentration led to a high fraction of short dipolar chains, and their interaction resulted in longer and thicker chains under applied magnetic field. On the other hand, when the magnetic field increased, the induced moments of the magnetic nanoparticles became larger, which dominated over the thermal fluctuation. Thus, the formed short chains connected to each other and grew in length. Thicker chains were also observed through chain-chain interaction. Furthermore, the induced moments of the NPs tended to direct into one direction with increased magnetic field, thus the chains were straighter. In comparison between the assembly on substrates, at water-air interface and at ethylene glycol-air interface, the assembly of Co NPs in hexane dispersion at ethylene glycol-air interface showed the most regular and homogeneous chain structures due to the better spreading of the dispersion on ethylene glycol subphase than on water subphase and substrates. The magnetic-field-induced assembly of superparamagnetic nanoparticles could provide a powerful approach for applications in data storage and electronic devices. Chapter 5 presented the synthesis of superparamagnetic and ferromagnetic cobalt nanoparticles through a dual-stage thermolysis of cobalt carbonyl (Co2(CO)8) by using polystyrene as surfactant. The amine end-functionalized polystyrene surfactants with different molecular weight were prepared via atom transfer radical polymerization technique. The molecular weight determination of polystyrene was conducted by gel permeation chromatography (GPC) and matrix-assisted laser desorption/ionization time-of-flight (MALDI-ToF) mass spectrometry techniques. The results showed that, when the molecular weight distribution is low (Mw/Mn < 1.2), the measurement by GPC and MALDI-ToF MS provided nearly similar results. For example, the molecular weight of 10600 Da was obtained by MALDI-ToF MS, while GPC gave 10500 g/mol (Mw/Mn = 1.17). However, if the polymer is poly distributed, MALDI-ToF MS cannot provide an accurate value. This was exemplified for a polymer with a molecular weight of 3130 Da measured by MALDI-TOF MS, while GPC showed 2300 g/mol (Mw/Mn = 1.38). The size, size distribution and magnetic properties of the hybrid particles were different by changing either the molecular weight or concentration of the polymer surfactants. The analysis from TEM characterization showed that the size of cobalt nanoparticles stabilized with polystyrene of lower molecular weight (Mn = 2300 g/mol) varied from 12–22 nm, while the size with middle (Mn = 4500 g/mol) and higher molecular weight (Mn = 10500 g/mol) of polystyrene-coated cobalt nanoparticles showed little change. Magnetic measurements exhibited that the small cobalt particles (12 nm) were superparamagnetic, while larger particles (21 nm) were ferromagnetic and assembled into 1-D chains. The grafting density calculated from thermogravimetric analysis showed that a higher grafting density of polystyrene was obtained with lower molecular weight (Mn = 2300 g/mol) than those with higher molecular weight (Mn = 10500 g/mol). Due to the larger steric hindrance, polystyrene with higher molecular weight cannot form a dense shell on the surface of the nanoparticles, which resulted in a lower grafting density. Wide angle X-ray scattering measurements revealed the epsilon cobalt crystalline phases of both superparamagnetic Co NPs coated with polystyrene (Mn = 2300 g/mol) and ferromagnetic Co NPs coated with polystyrene (Mn = 10500 g/mol). Furthermore, a stability study showed that PS-Co NPs prepared with higher polymer concentration and polymer molecular weight exhibited a better stability. N2 - Im Rahmen dieser Arbeit wurden superparamagnetische Cobalt Nanopartikel (NP) synthetisiert, die Selbstassemblierung im Magnetfeld untersucht und die ursprünglichen Liganden Ölsäure (Englisch oleic acid, OA) und Trioctylphosphanoxid (TOPO) ersetzt, um eine Funktionalisierung der Nanopartikel mit einem Temperatur-responsiven Polymer zu erreichen. Außerdem wurden superparamagnetische und ferromagnetische Co NP mit Polystyrol als Stabilisator synthetisiert. Co NP haben aufgrund ihrer herausragenden magnetischen und katalytischen Eigenschaften viele potentielle Anwendungen beispielsweise als Ferrofluide, in der Katalyse und der Magnetresonanztomografie (Englisch magnetic resonance imaging, MRI). Besonders interessant sind dabei superparamagnetische Co NP, die in einem äußeren Magnetfeld magnetisiert werden, aber nach Entfernen des angelegten Magnetfelds keine Magnetisierung mehr aufweisen. Bei biomedizinischen Anwendungen aggregieren sie daher nicht im Körper. Hydrophobe Co NP, die von kleinen Molekülen stabilisiert werden, eignen sich nicht für biologische Anwendungen, für die ein hydrophiles oder wässriges Medium vonnöten ist. Kapitel 3 beschreibt einen Ligandenaustausch zur Funktionalisierung von Co Nanopartikeln und das Herstellen neuer Nanokomposite aus superparamagnetischen Co NP und Temperatur-responsivem PNIPAM. Zunächst wurden wohldefinierte superparamagnetische Co NP mit OA und TOPO als Stabilisatoren durch die Thermolyse von Cobalt Carbonyl synthetisiert. Die ursprünglichen Liganden wurden dann durch einen funktionalen Liganden mit einer Amingruppe (zum Binden an die Oberfläche) und einer 2 Brompropionat-Gruppe (Polymerisationsinitiator) ersetzt. Nach diesem schnellen und einfachen Prozess der Oberflächenfunktionalisierung können die Nanopartikel ohne Aggregation in dem polaren Lösungsmittel DMF dispergiert werden. Nach thermogravimetrischen Messungen konnte die Dichte der Initiatoren mit ungefähr 3,2 Initiatoren / nm2 berechnet werden. Anschließend wurde Oberflächen-initiierte ATRP zur Polymerisation von NIPAM durchgeführt. Temperatur-abhängige Messungen der dynamischen Lichtstreuung der nun in Wasser dispergierbaren Nanokomposite zeigte das reversible Aggregationsverhalten nach Erhitzen über 32 °C. Kapitel 4 behandelt die Untersuchung der Assemblierung von superparamagnetischen OA- und TOPO-stabilisierten Co NP im äußeren Magnetfeld sowohl auf festen Oberflächen als auch der Flüssigkeit-Luft Grenzfläche. Durch die anziehende dipolare Wechselwirkung bildeten sich im äußeren Magnetfeld 1-D Ketten. Der Einfluss der Konzentration der Dispersion und der Stärke des Magnetfelds auf die Morphologie der assemblierten Strukturen wurde untersucht. Bei niedrigerer Konzentration der Dispersion und geringerer Magnetfeldstärke bildeten sich kurze und flexible Ketten. Bei höherer Konzentration oder höherer Magnetfeldstärke wurden die Ketten länger, breiter und gerader. Andererseits sind die induzierten magnetischen Momente bei erhöhter Magnetfeldstärke größer und dominieren über die thermische Fluktuation. Daher verbinden sich die kurzen Ketten zu längeren, und dickere Ketten entstehen durch Interaktion benachbarter Ketten. Außerdem zeigen die induzierten Momente der NP verstärkt in die gleiche Richtung je größer das äußere Magnetfeld ist, weshalb die Ketten gerader werden. Im Vergleich der Assemblierung auf Substraten (TEM-Grids, Siliciumwafer), an der Wasser-Luft und Ethylenglycol-Luft Grenzfläche, zeigte die Assemblierung von Co NP aus Hexan-Dispersion an der Ethylenglycol-Luft Grenzfläche die geordnetsten und homogensten Strukturen. Kapitel 5 präsentierte die Synthese von superparamagnetischen und ferromagnetischen Cobalt Nanopartikeln durch die zwei-stufige Thermolyse von Cobalt Carbonyl (Co2(CO)8) mit Polystyrol als Stabilisator. Polystyrol Polymere mit Amin-Endgruppen wurden durch ATRP-Technik mit unterschiedlichen Molekulargewichten hergestellt. Die Größe, Größenverteilung und magnetischen Eigenschaften der hybriden Partikel haben sich mit dem Molekulargewicht und der Konzentration der Polymer-Stabilisatoren unterschieden. Eine Analyse mit Transmissionselektronenmikroskopie zeigte, dass die Größe der Co NP zwischen 12–22 nm variierte, wenn sie durch Polystyrol geringen Molekulargewichts (Mn = 2300 g/mol) stabilisiert wurden, während sich die Größe der Partikel mit Polystyrol mittleren (Mn = 4500 g/mol) und höheren (Mn = 10500 g/mol) Molekulargewichts kaum unterschied. Messungen der magnetischen Eigenschaften zeigten, dass die kleinen Cobalt Partikel (12 nm) superparamagnetisch waren, während größere Partikel (21 nm) ferromagnetisch waren und zu 1-D Ketten assemblierten. Die Dichte der Polymere auf der Oberfläche wurde nach einer thermogravimetrischen Analyse berechnet. Mit kleinem Molekulargewicht (Mn = 2300 g/mol) wurde eine höhere Dichte erreicht als mit hohem Molekulargewicht (Mn = 10500 g/mol). Durch eine stärker ausgeprägte sterische Hinderung kann ein Polymer hohen Molekulargewichts keine dichte Hülle um die Nanopartikel bilden. Das Vorliegen einer epsilon kristallinen Phase wurde durch Weitwinkel-Röntgenstreuung sowohl für superparamagnetische Co NP (mit PS Mn = 2300 g/mol) als auch ferromagnetische Co NP (mit PS Mn = 10500 g/mol) bestimmt. KW - magnetic nanoparticles KW - assembly KW - polymer KW - cobalt nanoparticles KW - magnetische Nanopartikel KW - Assemblierung KW - Polymer KW - Cobalt Nanopartikeln Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-418153 ER -