TY  - THES
A1  - Tan, Irene
T1  - Towards greener stationary phases : thermoresponsive and carbonaceous chromatographic supports
T1  - Zu grüner Separation : thermoresponsive und kohlenstoffhaltige chromatographische Trägermaterialien
N2  - Polymers which are sensitive towards external physical, chemical and electrical stimuli are termed as ‘intelligent materials’ and are widely used in medical and engineering applications. Presently, polymers which can undergo a physical change when heat is applied at a certain temperature (cloud point) in water are well-studied for this property in areas of separation chemistry, gene and drug delivery and as surface modifiers. One example of such a polymer is the poly (N-isopropylacrylamide) PNIPAAM, where it is dissolved well in water below 32 oC, while by increasing the temperature further leads to its precipitation. In this work, an alternative polymer poly (2-(2-methoxy ethoxy)ethyl methacrylate-co- oligo(ethylene glycol) methacrylate) (P(MEO2MA-co-OEGMA)) is studied due to its biocompatibility and the ability to vary its cloud points in water. When a layer of temperature responsive polymer was attached to a single continuous porous piece of silica-based material known as a monolith, the thermoresponsive characteristic was transferred to the column surfaces. The hybrid material was demonstrated to act as a simple temperature ‘switch’ in the separation of a mixture of five steroids under water. Different analytes were observed to be separated under varying column temperatures. Furthermore, more complex biochemical compounds such as proteins were also tested for separation. The importance of this work is attributed to separation processes utilizing environmentally friendly conditions, since harsh chemical environments conventionally used to resolve biocompounds could cause their biological activities to be rendered inactive.
N2  - Polymere, welche empfindlich gegenüber externen physikalischen, chemischen und elektrischen Einflüssen sind, werden „intelligente Materialien“ genannt. Diese werden weitverbreitet in medizinischen und technischen Anwendungen eingesetzt. Auf diesem Gebiet ausführlich erforschte Materialien sind Polymere, welche durch Hitze bei einer bestimmten Temperatur (Trübungspunkt) eine physikalische Veränderung eingehen können, genannt thermoresponsive Polymere. Eingesetzt werden diese z.B. in chromatographischen Trennverfahren, in Gen- und Wirkstofftransport Vorgängen und zur Oberflächenmodifikation. Ein Beispiel für so ein Polymer ist das poly(N-isopropylacrylamide) PNIPAAM, welches unter 32 °C in Wasser gelöst vorliegt und mit Erhöhung der Temperatur als Niederschlag ausfällt. In dieser Arbeit wurde ein alternatives Polymer, das poly(2-(2-methoxyethoxy)ethylmethacrylate-co-oligo(ethyleneglycol) methacrylate) (P(MEO2MA-co-OEGMA)), untersucht, in Bezug auf Biokompatibilität und der Änderung des Trübungspunktes in Wasser. Wenn eine Schicht eines temperaturempfindlichen Polymers auf einen Monolithen (einteiliger, poröser und auf Silika-basierendes Material) aufgebracht wird, werden die thermoresponsiven Eigenschaften auf die Oberfläche dieses Monolithen übertragen. Der Monolith dient hier als Säule in einer HPLC-Anlage. Es wurde gezeigt, dass das Hybrid-Material als einfacher „Temperaturschalter“ in der Trennung von fünf verschiedenen Steroiden in Wasser agieren kann. Untersucht wurde die Separation verschiedener Analyten mit dem Variieren der Säulentemperatur. Zusätzlich wurden mehr komplexe biochemische Stoffe, wie Proteine, getestet. Die Bedeutung dieser Arbeit ist zurückzuführen auf Separationsprozesse, welche umweltfreundlichen Bedingungen nutzen, da die rauen chemischen Bedingungen in konventionellen Separationsprozessen die biologische Inaktivität der Verbindungen zur Folge haben können. Der zweite Teil der Arbeit beschäftigte sich mit der Entwicklung eines alternativen Trägermaterials als Ersatz zu den Silika-basierende Trennungssäulen. Kohlenstoffmaterialien sind aufgrund ihrer ausgezeichneten mechanischen Härte und chemischen Stabilität eine vielversprechend Alternative. Die Synthese von Kohlenstoffkugeln als Trägermaterial kann als „grüner“ Prozess in meiner Arbeit angesehen werden, da milde Synthesebedingungen in purem Wasser verwendet wurden. Die Leistungsfähigkeit des Materials wurde mit einer Serie von Separationsreaktionen gezeigt.
KW  - thermoresponsive
KW  - poly(N-isopropylacrylamide)
KW  - oligo(ethyleneglycol)
KW  - Monolith
KW  - Chromatographie
KW  - thermoresponsive
KW  - poly(N-isopropyl acrylamide)
KW  - oligo(ethylene glycol)
KW  - monolith
KW  - chromatography
Y1  - 2011
U6  - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-53130
ER  - 
TY  - THES
A1  - Weiß, Jan
T1  - Synthesis and self-assembly of multiple thermoresponsive amphiphilic block copolymers
T1  - Synthese und Selbstorganisation von mehrfach thermisch schaltbaren amphiphilen Blockcopolymeren
N2  - In the present thesis, the self-assembly of multi thermoresponsive block copolymers in dilute aqueous solution was investigated by a combination of turbidimetry, dynamic light scattering, TEM measurements, NMR as well as fluorescence spectroscopy. The successive conversion of such block copolymers from a hydrophilic into a hydrophobic state includes intermediate amphiphilic states with a variable hydrophilic-to-lipophilic balance. As a result, the self-organization is not following an all-or-none principle but a multistep aggregation in dilute solution was observed. The synthesis of double thermoresponsive diblock copolymers as well as triple thermoresponsive triblock copolymers was realized using twofold-TMS labeled RAFT agents which provide direct information about the average molar mass as well as residual end group functionality from a routine proton NMR spectrum. First a set of double thermosensitive diblock copolymers poly(N-n-propylacrylamide)-b-poly(N-ethylacrylamide) was synthesized which differed only in the relative size of the two blocks. Depending on the relative block lengths, different aggregation pathways were found. Furthermore, the complementary TMS-labeled end groups served as NMR-probes for the self-assembly of these diblock copolymers in dilute solution. Reversible, temperature sensitive peak splitting of the TMS-signals in NMR spectroscopy was indicative for the formation of mixed star-/flower-like micelles in some cases. Moreover, triple thermoresponsive triblock copolymers from poly(N-n-propylacrylamide) (A), poly(methoxydiethylene glycol acrylate) (B) and poly(N-ethylacrylamide) (C) were obtained from sequential RAFT polymerization in all possible block sequences (ABC, BAC, ACB). Their self-organization behavior in dilute aqueous solution was found to be rather complex and dependent on the positioning of the different blocks within the terpolymers. Especially the localization of the low-LCST block (A) had a large influence on the aggregation behavior. Above the first cloud point, aggregates were only observed when the A block was located at one terminus. Once placed in the middle, unimolecular micelles were observed which showed aggregation only above the second phase transition temperature of the B block. Carrier abilities of such triple thermosensitive triblock copolymers tested in fluorescence spectroscopy, using the solvatochromic dye Nile Red, suggested that the hydrophobic probe is less efficiently incorporated by the polymer with the BAC sequence as compared to ABC or ACB polymers above the first phase transition temperature. In addition, due to the problem of increasing loss of end group functionality during the subsequent polymerization steps, a novel concept for the one-step synthesis of multi thermoresponsive block copolymers was developed. This allowed to synthesize double thermoresponsive di- and triblock copolymers in a single polymerization step. The copolymerization of different N-substituted maleimides with a thermosensitive styrene derivative (4-vinylbenzyl methoxytetrakis(oxyethylene) ether) led to alternating copolymers with variable LCST. Consequently, an excess of this styrene-based monomer allowed the synthesis of double thermoresponsive tapered block copolymers in a single polymerization step.
N2  - Die Selbstorganisation von mehrfach thermisch schaltbaren Blockcopolymeren in verdünnter wässriger Lösung wurde mittels Trübungsphotometer, dynamischer Lichtstreuung, TEM Messungen, NMR sowie Fluoreszenzspektroskopie untersucht. Die schrittweise Überführung eines hydrophilen in ein hydrophobes Blockcopolymer beinhaltet ein oder mehr amphiphile Zwischenstufen mit einstellbarem hydrophilen zu lipophilen Anteil (HLB). Dies führt dazu, dass die Selbstorganisation solcher Polymere in Lösung nicht nur einem Alles-oder-nichts-Prinzip folgt sondern ein mehrstufiges Aggregationsverhalten beobachtet wird. Die Synthese von doppelt thermisch schaltbaren Diblockcopolymeren und dreifach thermisch schaltbaren Triblockcopolymeren wurde durch sequenzielle RAFT Polymerisation realisiert. Dazu wurden zweifach TMS-markierte RAFT Agentien verwendet, welche die Bestimmung der molaren Masse sowie der verbliebenen Endgruppenfunktionalität direkt aus einem Protonen NMR Spektrum erlauben. Mit diesen RAFT Agentien wurde zunächst eine Serie von doppelt thermisch schaltbaren Diblockcopolymeren aus Poly(N-n-propylacrylamid)-b-Poly(N-ethylacrylamid), welche sich lediglich durch die relativen Blocklängen unterscheiden, hergestellt. In Abhängigkeit von der relativen Blocklänge wurde ein unterschiedliches Aggregationsverhalten der Diblockcopolymere in verdünnter wässriger Lösung beobachtet. Des Weiteren wirken die komplementär TMS-markierten Endgruppen als NMR-Sonden während der schrittweisen Aggregation dieser Polymere. Reversible, temperaturabhängige Peakaufspaltung der TMS-Signale in der NMR Spektroskopie spricht für eine Aggregation in gemischte stern-/blumenartige Mizellen, in denen ein Teil der hydrophoben Endgruppen in den hyrophoben Kern zurückfaltet. Obendrein wurden dreifach thermisch schaltbare Triblockcopolymere aus Poly(N-n-propylacrylamid) (A), Poly(methoxydiethylen glycol acrylat) (B) und Poly(N-ethylacrylamid) (C) in allen möglichen Blocksequenzen (ABC, BAC, ACB) durch schrittweisen Aufbau mittels RAFT Polymerisation erhalten. Das Aggregationsverhalten dieser Polymere in verdünnter wässriger Lösung war relativ komplex und hing stark von der Position der einzelnen Blöcke in den Triblockcopolymeren ab. Besonders die Position des Blocks mit der niedrigsten LCST (A) war ausschlaggebend für die resultierenden Aggregate. So wurde oberhalb der ersten Phasenübergangstemperatur nur Aggregation der Triblockcopolymere beobachtet, wenn der A Block an einem der beiden Enden der Polymere lokalisiert war. Wurde der A Block hingegen in der Mitte der Polymere positioniert, entstanden unimere Mizellen zwischen der ersten und zweiten Phasenübergangstemperatur, welche erst aggregierten, nachdem der zweite Block (B) seinen Phasenübergang durchlief. Die Transportereigenschaften dieser Triblockcopolymere wurden mittels Fluoreszenzspektroskopie getestet. Dazu wurde die Einlagerung eines hydrophoben, solvatochromen Fluoreszenzfarbstoffes, Nilrot, in Abhängigkeit der Temperatur untersucht. Im Gegensatz zu den Polymeren mit der Blocksequenz ABC oder ACB, zeigten die Polymere mit der Sequenz BAC eine verminderte Aufnahmefähigkeit des hydrophoben Farbstoffes oberhalb des ersten Phasenübergangs, was auf die fehlende Aggregation und die damit verbundenen relativ kleinen hydrophoben Domänen der unimolekularen Mizellen zwischen der ersten und zweiten Phasenübergangstemperatur zurückzuführen ist. Aufgrund des zunehmenden Verlustes von funktionellen Endgruppen während der RAFT Synthese von Triblockcopolymeren wurde ein neuartiges Konzept zur Einschrittsynthese von mehrfach schaltbaren Blockcopolymeren entwickelt. Dieses erlaubt die Synthese von mehrfach schaltbaren Diblock- und Triblockcopoylmeren in einem einzelnen Reaktionsschritt. Die Copolymeriation von verschiedenen N-substituierten Maleimiden mit einem thermisch schaltbaren Styrolderivat (4-Vinylbenzylmethoxytetrakis(oxyethylene) ether) ergab alternierende Copolymere mit variabler LCST. Die Verwendung eines Überschusses dieses styrolbasierten Monomers erlaubt ferner die Synthese von Gradientenblockcopolymeren in einem einzelnen Polymerisationsschritt.
KW  - Selbstorganisation
KW  - Blockcopolymer
KW  - RAFT
KW  - temperaturschaltbar
KW  - Mizelle
KW  - self-assembly
KW  - block copolymer
KW  - RAFT
KW  - thermoresponsive
KW  - micelle
Y1  - 2011
U6  - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-53360
ER  -