TY - THES A1 - Kuhrts, Lucas T1 - The effect of Polycations on the Formation of Magnetite Nanoparticles N2 - Nanoparticles of magnetite (Fe3O4) are envisioned to find used in diverse applications, ranging from magnetic data storage, inks, ferrofluids as well as in magnetic resonance imaging, drug delivery, and hyperthermia cancer treatment. Their magnetic properties strongly depend on their size and morphology, two properties that can be synthetically controlled. Achieving appropriate control under soft chemical conditions has so far remained a challenging endeavor. One proven way of exerting this desired control has been using a biomimetic approach that emulates the proteome of magnetotactic bacteria by adding poly-L-arginine in the co- precipitation of ferrous and ferric chloride. The objective of the work presented here is to understand the impact of this polycation on the formation mechanism of magnetite and, through rational design, to enhance the control we can exert on magnetite nanoparticle size and morphology. We developed a SAXS setup to temporally and structurally resolve the formation of magnetite in the presence of poly-L-arginine in situ. Using analytical scattering models, we were able to separate the scattering contribution of a low-density 5 nm iron structure from the contribution of the growing nanoparticles. We identified that the low-density iron structure is a metastable precursor to the magnetite particles and that it is electrostatically stabilized by poly-L-arginine. In a process analogous to biomineralization, the presence of the charged macromolecule thus shifts the reaction mechanism from a thermodynamically controlled one to a kinetically controlled one. We identify this shift in reactions mechanism as the cornerstone of the proposed mechanism and as the crucial step in the paradigm of this extraordinary nanoparticle morphology and size control. Based on SAXS data, theoretical considerations suggest that an observed morphological transition between spherical, solid, and sub-structured mesocrystalline magnetite nanoparticles is induced through a pH-driven change in the wettability of the nanoparticle surface. With these results, we further demonstrate that SAXS can be an invaluable tool for investigating nanoparticle formation. We were able to change particle morphology from spherically solid particles to sub-structured mesocrystals merely by changing the precipitation pH. Improving the synthesis sustainability by substituting poly-L-arginine with renewable, polysaccharide-based polycations produced at the metric ton scale, we demonstrated that the ability to alter the reaction mechanism of magnetite can be generically attributed to the presence of polycations. Through meticulous analysis and the understanding of the formation mechanism, we were able to exert precise control over particle size and morphology, by adapting crucial synthesis parameters. We were thus able to grow mesocrystals up to 200 nm and solid nanocrystals of 100 nm by adding virtually any strong polycation. We further found a way to produce stable single domain magnetite at only slightly increased alkalinity, as magnetotactic bacteria do it. Thus through the understanding of the biological system, the consecutive biomimetic synthesis of magnetite and the following understanding of the mechanism involved in the in vitro synthesis, we managed to improve the synthetic control over the co-precipitation of magnetite, coming close biomineralization of magnetite in magnetotactic bacteria. Polyanions, in both natural as well as in synthetic systems, have been in the spotlight of recent research, yet our work shows the pivotal influence polycations have on the nucleation of magnetite. This work will contribute significantly to our ability to tailor magnetite nanoparticle size and morphology; in addition, we presume it will provide us with a model system for studying biomineralization of magnetite in vitro, putting the spotlight on the important influence of polycations, which have not had the scientific attention they deserve. T2 - Der Effekt von Polykationen auf die Bildung von Magnetitnanopartikeln KW - Mechanism KW - Nanoparticle KW - SAXS KW - Biomimetic KW - Magnetite Y1 - CY - Potsdam ER - TY - JOUR A1 - Teixeira, C. V. A1 - Blanzat, Muriel A1 - Koetz, Joachim A1 - Rico-Lattes, I. A1 - Brezesinski, Gerald T1 - In-plane miscibility and mixed bilayer microstructure in mixtures of catanionic glycolipids and zwitterionic phospholipids JF - Biochimica et biophysica acta : Biomembranes N2 - SAXS/WAXS studies were performed in combination with freeze fracture electron microscopy using mixtures of a new Gemini catanionic surfactant (Gem 16-12, formed by two sugar groups bound by a hydrocarbon spacer with 12 carbons and two 16-carbon chains) and the zwitterionic phospholipid 1,2-dipalmitoyl-sn-glycero-3-phosphocholine(DPPC) to establish the phase diagram. Gem 16-12 in water forms bilayers with the same amount of hydration water as DPPC. A frozen interdigitated phase with a low hydration number is observed below room temperature. The kinetics of the formation of this crystalline phase is very slow. Above the chain melting temperature, multilayered vesicles are formed. Mixing with DPPC produces mixed bilayers above the corresponding chain melting temperature. At room temperature, partially lamellar aggregates with local nematic order are observed. Splitting of infinite lamellae into discs is linked to immiscibility in frozen state. The ordering process is always accompanied by dehydration of the system. As a consequence, an unusual order-disorder phase transition upon cooling is observed. KW - SAXS KW - bilayer KW - gemini surfactant KW - ordering process KW - Anti-HIV KW - miscibility Y1 - 2006 U6 - https://doi.org/10.1016/j.bbamem.2006.05.025 SN - 0005-2736 VL - 1758 SP - 1797 EP - 1808 PB - Elsevier CY - Amsterdam ER - TY - THES A1 - Latza, Victoria Maria T1 - Interactions involving lipid-based surfaces T1 - Wechselwirkungen lipid-basierter Oberflächen BT - from protein adsorption to membrane adhesion BT - Protein-Adsorption und Membran-Adhäsion N2 - Interactions involving biological interfaces such as lipid-based membranes are of paramount importance for all life processes. The same also applies to artificial interfaces to which biological matter is exposed, for example the surfaces of drug delivery systems or implants. This thesis deals with the two main types of interface interactions, namely (i) interactions between a single interface and the molecular components of the surrounding aqueous medium and (ii) interactions between two interfaces. Each type is investigated with regard to an important scientific problem in the fields of biotechnology and biology: 1.) The adsorption of proteins to surfaces functionalized with hydrophilic polymer brushes; a process of great biomedical relevance in context with harmful foreign-body-response to implants and drug delivery systems. 2.) The influence of glycolipids on the interaction between lipid membranes; a hitherto largely unexplored phenomenon with potentially great biological relevance. Both problems are addressed with the help of (quasi-)planar, lipid-based model surfaces in combination with x-ray and neutron scattering techniques which yield detailed structural insights into the interaction processes. Regarding the adsorption of proteins to brush-functionalized surfaces, the first scenario considered is the exposure of the surfaces to human blood serum containing a multitude of protein species. Significant blood protein adsorption was observed despite the functionalization, which is commonly believed to act as a protein repellent. The adsorption consists of two distinct modes, namely strong adsorption to the brush grafting surface and weak adsorption to the brush itself. The second aspect investigated was the fate of the brush-functionalized surfaces when exposed to aqueous media containing immune proteins (antibodies) against the brush polymer, an emerging problem in current biomedical applications. To this end, it was found that antibody binding cannot be prevented by variation of the brush grafting density or the polymer length. This result motivates the search for alternative, strictly non-antigenic brush chemistries. With respect to the influence of glycolipids on the interaction between lipid membranes, this thesis focused on the glycolipids’ ability to crosslink and thereby to tightly attract adjacent membranes. This adherence is due to preferential saccharide-saccharide interactions occurring among the glycolipid headgroups. This phenomenon had previously been described for lipids with special oligo-saccharide motifs. Here, it was investigated how common this phenomenon is among glycolipids with a variety of more abundant saccharide-headgroups. It was found that glycolipid-induced membrane crosslinking is equally observed for some of these abundant glycolipid types, strongly suggesting that this under-explored phenomenon is potentially of great biological relevance. N2 - Wechselwirkungen, die von biologischen Grenzflächen wie Lipidmembranen eingegangen werden, haben tiefgreifende Auswirkungen auf alle Lebensprozesse. Dasselbe trifft auf alle künstlichen Grenzflächen zu, die in Kontakt mit biologischer Materie treten. Die Oberflächen von Wirkstoffverabreichungssystemen oder Implantaten sind hierfür prominente Beispiele. Diese Dissertationsschrift behandelt zwei Hauptkategorien von Grenzflächen-Wechselwirkungen: Zum einen die Wechselwirkung zwischen einzelnen Grenzflächen und den molekularen Komponenten des wässrigen Umfelds; zum anderen die Wechselwirkung zwischen zwei Grenzflächen. Jede dieser beiden Wechselwirkungskategorien wurde unter Bezugnahme auf eine wichtige wissenschaftliche Fragestellung aus den Bereichen der Biologie und Biotechnologie untersucht: 1.) Die Adsorption von Proteinen an Oberflächen die mit hydrophilen Polymerbürsten funktionalisiert sind; diese Anlagerung von biologischem Material stellt einen Prozess von äußerster biomedizinischer Relevanz dar, der beispielsweise beim Auftreten der schädlichen Fremdkörperabstoßung von Implantaten oder Wirkstoffverabreichungssystemen eine entscheidende Rolle spielt. 2.) Der Einfluss von Glykolipiden auf Wechselwirkungen zwischen Lipidmembranen, einem bislang größtenteils unerforschten Phänomen von potentiell herausragender biologischer Bedeutung. Die Bearbeitung beider Fragestellungen erfolgte unter Verwendung (quasi-)planarer, lipid-basierter Modellsysteme in Kombination mit Röntgen- oder Neutronenstreuung, welche detaillierte strukturelle Einblicke von Wechselwirkungsprozessen liefern. In Bezug auf die Adsorption von Proteinen an polymer-funktionalisierte Oberflächen wurde zunächst ein Szenario behandelt, bei dem die Oberflächen menschlichem Blutserum ausgesetzt sind, welches eine Vielzahl verschiedener Proteinspezies enthält. Die verwendete Funktionalisierung gilt gemeinhin als proteinabstoßend. Anders als erwartet zeigte sich dennoch signifikante Adsorption von Blutproteinen auf der Oberfläche. Die gemessene Adsorption weist zwei unterschiedliche Arten auf: Starke Adsorption an die Oberfläche, an die die Polymere kovalent gebunden sind, und schwache Adsorption an die Polymerbürste selbst. Der zweite Aspekt, der beleuchtet wurde, sind die Folgen von Antikörpern gegen die Bürstenpolymere. Deren zunehmendes Vorkommen stellt ein Problem für biomedizinische Anwendungen dar. Die Ergebnisse der Arbeit zeigen, dass die starke Adsorption von Antikörpern nicht durch die Veränderung von Bürstenparametern, wie Anbindungsdichte oder Polymerisationsgrad, aufgehalten werden kann. Diese Erkenntnis motiviert die Suche nach alternativen, nicht-antigenen Bürstenmaterialien. In der zweiten Wechselwirkungskategorie, dem Einfluss von Glykolipiden auf Wechselwirkungen zwischen Lipidmembranen, wurde die Fähigkeit der Glykolipide zur Membran-Adhäsion und der damit einhergehenden starken Anziehung von aneinander liegenden Membranen beleuchtet. Die Kohäsion erfolgt dabei über anziehende Saccharid-Saccharid-Wechselwirkungen der Kopfgruppen. Dieses Verhalten wurde schon für Lipide mit speziellen Oligosaccharid-Motiven beschrieben. Daher wurde bei der Untersuchung der Adhäsionsfähigkeit besonders die Verbreitung des Phänomens unter Glykolipiden mit häufig vorkommenden Saccharid-Kopfgruppen fokussiert. Es zeigte sich, dass die von Glykolipiden hervorgerufene Adhäsion auch für einige dieser häufig vorkommenden Glykolipidtypen beobachtet werden kann. Dies deutet darauf hin, dass dieses Phänomen von weitreichender Bedeutung für die Biologie ist und daher weiterhin intensiv erforscht werden sollte. KW - surfaces and interfaces KW - biocompatibility KW - PEG brushes KW - lipids KW - neutron reflectometry KW - biological membranes KW - glycolipids KW - SAXS KW - WAXS KW - neutron diffraction KW - off-specular scattering KW - Oberfächen KW - Grenzflächen KW - Biokompatibilität KW - PEG-Funktionalisierung KW - Lipide KW - Neutronen Reflektometrie KW - biologische Membranen KW - Glykolipide KW - SAXS KW - WAXS KW - Neutronen Diffraktion Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-445593 ER - TY - JOUR A1 - Yan, Wan A1 - Fang, Liang A1 - Nöchel, Ulrich A1 - Kratz, Karl A1 - Lendlein, Andreas T1 - Influence of programming strain rates on the shape-memory performance of semicrystalline multiblock copolymers JF - Journal of polymer science : B, Polymer physics N2 - Multiblock copolymers named PCL-PIBMD consisting of crystallizable poly(epsilon-caprolactone) segments and crystallizable poly[oligo(3S-iso-butylmorpholine-2,5-dione)] segments coupled by trimethyl hexamethylene diisocyanate provide a versatile molecular architecture for achieving shape-memory effects (SMEs) in polymers. The mechanical properties as well as the SME performance of PCL-PIBMD can be tailored by the variation of physical parameters during programming such as deformation strain or applied temperature protocols. In this study, we explored the influence of applying different strain rates during programming on the resulting nanostructure of PCL-PIBMD. Programming was conducted at 50 degrees C by elongation to epsilon(m)=50% with strain rates of 1 or 10 or 50 mmmin(-1). The nanostructural changes were visualized by atomic force microscopy (AFM) measurements and investigated by in situ wide and small angle X-ray scattering experiments. With increasing the strain rate, a higher degree of orientation was observed in the amorphous domains. Simultaneously the strain-induced formation of new PIBMD crystals as well as the fragmentation of existing large PIBMD crystals occurred. The observed differences in shape fixity ratio and recovery stress of samples deformed with various strain rates can be attributed to their different nanostructures. The achieved findings can be relevant parameters for programming the shape-memory polymers with designed recovery forces. (c) 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2016, 54, 1935-1943 KW - atomic force microscopy (AFM) KW - crystal structures KW - crystallization KW - multiblock copolymer KW - stimuli-sensitive polymers KW - SAXS KW - shape-memory effect KW - WAXS KW - X-ray scattering Y1 - 2016 U6 - https://doi.org/10.1002/polb.24097 SN - 0887-6266 SN - 1099-0488 VL - 54 SP - 1935 EP - 1943 PB - Wiley-Blackwell CY - Hoboken ER - TY - JOUR A1 - Wessig, Pablo A1 - Budach, Dennis B. A1 - Thünemann, Andreas F. T1 - Dendrimers with Oligospiroketal (OSK) Building Blocks: Synthesis and Properties JF - Chemistry - a European journal N2 - The development of novel dendrimers containing oligospiroketal (OSK) rods as building blocks is described. The linkage between the core unit (CU), branching units (BU), and OSK rods relies on the CuAAC reaction between terminal alkynes and azides. Two different strategies of dendrimer synthesis were investigated and it was found that the convergent approach is clearly superior to the divergent one. SAXS measurements and MD simulations indicate that the obtained dendrimer features a globular structure with very low density. Obviously, the OSK rods stabilize a rather loose mass-fractal structure. KW - click chemistry KW - dendrimers KW - molecular rods KW - oxygen heterocycles KW - SAXS Y1 - 2015 U6 - https://doi.org/10.1002/chem.201501386 SN - 0947-6539 SN - 1521-3765 VL - 21 IS - 29 SP - 10466 EP - 10471 PB - Wiley-VCH CY - Weinheim ER - TY - JOUR A1 - Zhong, Qi A1 - Adelsberger, Joseph A1 - Niedermeier, M. A. A1 - Golosova, Anastasi A1 - Bivigou Koumba, Achille Mayelle A1 - Laschewsky, André A1 - Funari, S. S. A1 - Papadakis, Christine M. A1 - Müller-Buschbaum, Peter T1 - The influence of selective solvents on the transition behavior of poly(styrene-b-monomethoxydiethylenglycol-acrylate-b-styrene) thick films JF - Colloid and polymer science : official journal of the Kolloid-Gesellschaft N2 - Thick poly(styrene-b-monomethoxydiethylenglycol-acrylate-b-styrene) [P(S-b-MDEGA-b-S)] films (thickness 5 mu m) are prepared from different solvents on flexible substrates by solution casting and investigated with small-angle X-ray scattering. As the solvents are either PS- or PMDEGA-selective, micelles with different core-shell micellar structures are formed. In PMDEGA-selective solvents, the PS block is the core and PMDEGA is the shell, whereas in PS-selective solvents, the order is reversed. After exposing the films to liquid D2O, the micellar structure inside the films prepared from PMDEGA-selective solvents remains unchanged and only the PMDEGA (shell part) swells. On the contrary, in the films prepared from PS-selective solvents, the micelles revert the core and the shell. This reversal causes more entanglements of the PMDEGA chains between the micelles. Moreover, the thermal collapse transition of the PMDEGA block in liquid D2O is significantly broadened. Irrespective of the solvent used for film preparation, the swollen PMDEGA shell does not show a prominent shrinkage when passing the phase transition, and the transition process occurs via compaction. The collapsed micelles have a tendency to densely pack above the transition temperature. KW - Hydrogel KW - Thin film KW - Thermo-responsive KW - LCST behavior KW - SAXS Y1 - 2013 U6 - https://doi.org/10.1007/s00396-012-2879-4 SN - 0303-402X VL - 291 IS - 6 SP - 1439 EP - 1451 PB - Springer CY - New York ER - TY - THES A1 - Sapei, Lanny T1 - Characterisation of silica in Equisetum hyemale and its transformation into biomorphous ceramics T1 - Charakterisierung von Siliciumdioxid in Winterschachtelhalmen und dessen Umwandlung in biomorphe Keramiken N2 - Equisetum spp. (horsetail / “Schachtelhalm”) is the only surviving genus of the primitive Sphenopsids vascular plants which reached their zenith during the Carboniferous era. It is an herbaceous plant and is distinguished by jointed stems with fused whorl of nodal leaves. The plant has been used for scouring kitchen utensils and polishing wood during the past time due to its high silica encrustations in the epidermis. Equisetum hyemale (scouring rush) can accumulate silica up to 16% dry weight in its tissue, which makes this plant an interesting candidate as a renewable resource of silica for the synthesis of biomorphous ceramics. The thesis comprises a comprehensive experimental study of silica accumulations in E.hyemale using different characterisation techniques at all hierarchical levels. The obtained results shed light on the local distribution, chemical form, crystallinity, and nanostructure of biogenic silica in E.hyemale which were quite unclear until now. Furthermore, isolation of biogenic silica from E.hyemale to obtain high grade mesoporous silica with high purity is investigated. Finally, syntheses of silicon carbide (b-SiC) by a direct thermoconversion process of E.hyemale is attempted, which is a promising material for high performance ceramics. It is found that silica is deposited continuously on the entire epidermal layer with the highest concentration on the knobs. The highest silicon content is at the knob tips (≈ 33%), followed by epidermal flank (≈ 17%), and inner lower knob (≈ 6%), whereas there is almost no silicon found in the interior parts. Raman spectroscopy reveals the presence of at least two silica modifications in E.hyemale. The first type is pure hydrated amorphous silica restricted to the knob tips. The second type is accumulated on the entire continuous outer layer adjacent to the epidermis cell walls. It is lacking silanol groups and is intimately associated with polysaccharides (cellulose, hemicellulose, pectin) and inorganic compounds. Silica deposited in E.hyemale is found to be mostly amorphous with almost negligible amounts of crystalline silica in the form of a-quartz (< 7%). The silica primary particles have a plate-like shape with a thickness of about 2 nm. Pure mesoporous amorphous silica with an open surface area up to 400 m2/g can be obtained from E.hyemale after leaching the plant with HCl to remove the inorganic impurities followed by a calcination treatment. The optimum calcination temperature appears to be around 500°C. Calcination of untreated E.hyemale causes a collapse of the biogenic silica structure which is mainly attributed to the detrimental action of alkali ions present in the native plant. Finally, pure b-SiC with a surface area of about 12 m2/g is obtained upon direct pyrolysis of HCl-treated E.hyemale samples in argon atmosphere. The original structure of native E.hyemale is substantially retained in the biomorphous b-SiC. The results of this thesis lead to a better understanding of the silicification process and allow to draw conclusions about the role of silica in E.hyemale. In particular, a templating role of the plant biopolymers for the synthesis of the nanostructured silica within the plant body can be deduced. Moreover, the high grade ultrafine amorphous silica isolated from E.hyemale promises applications as adsorbent and catalyst support and as silica source for the fabrication of silica-based composites. The synthesis of biomorphous b-SiC from sustainable and low-cost E.hyemale is still in its initial stage. The present thesis demonstrates the principal possibility of carbothermal synthesis of SiC from E.hyemale with the prospect of potential applications, for instance as refractory materials, catalyst supports, or high performance advanced ceramics. N2 - Equisetum spp. (Schachtelhalm) ist die einzige überlebende Gattung der Schachtelhalmgewächse, die ihren Zenit während der Karbon Ära erreichten. Der Schachtelhalm ist eine krautartige Pflanze und wird durch verbundene Stämme mit fixiertem Wirtel der Knotenblätter unterschieden. Aufgrund seiner hohen Siliciumdioxid Bedeckung in der Epidermis sind Winterschachtelhalmen lange Zeit zur Reinigung von Küchegeräten und zum Polieren von Holz verwendet worden. Der Winterschachtelhalm (auch Scheuerkraut genannt) kann Siliciumdioxid bis zu 16% Trockengewicht in seinem Gewebe ansammeln. Dies macht aus dieser Pflanze einen interessanten Kandidaten als erneubare Ressource von Siliciumdioxid für die Synthese von biomorphen Keramiken. Die vorliegende Doktorarbeit beinhaltet eine ausführliche experimentelle Studie der Siliciumdioxidansammlungen in Winterschachtelhalmen mittels unterschiedlicher Charakterisierungstechniken auf allen hierarchischen Ebenen. Die Ergebnisse der Arbeit werfen neues Licht auf die lokale Verteilung, die chemischen Form, die Kristallinität und die Nanostruktur des biogenen Siliciumdioxids, die bisher ziemlich unklar waren. Außerdem werden Möglichkeiten zur Isolierung des biogenen Siliciumdioxids aus Winterschachtelhalmen untersucht, um hochgradig reines Siliciumdioxid zu erhalten. Auch wird die direkte carbothermale Synthese von Siliciumkarbid (b-SiC) aus Schachtelhalmen untersucht, mit dem Ziel einer kostengünstigen Herstellung von Hochleistungskeramiken aus nachwachsenden Rohstoffen Es wird gezeigt, dass das Siliciumdioxid in einer kontinuierlichen Schicht in der Epidermis vorliegt, mit der höchsten Siliciumkonzentration in den auffälligen knopfartigen Ausbuchtungen. Den höchsten Siliciumgehalt zeigen die Knopfspitzen (≈ 33%), gefolgt von der epidermalen Flanke (≈ 17%) und inneren unteren Teile der Knöpfe (≈ 6%), während es in den inneren Teilen der Pflanze praktisch kein Silicium gibt. Ramanspektroskopie beweist eindeutig, dass mindestens zwei Siliciumdioxid Modifikationen vorhanden sind. Der erste Typ ist reines hydratisiertes amorphes Siliciumdioxid, das auf den Bereich der Knopfspitzen beschränkt ist. Der zweite Typ wird in der gesamten kontinuierlichen äußeren Schicht angesammelt, weist keine Ramanbanden von Silanolgruppen auf, und ist örtlich eng verknüpft mit Banden von Polysacchariden (Zellulose, Hemizellulose, Pektin) sowie anorganischen Verbindungen. Der Großteil des Siliciumdioxids in Winterschachtelhalmen ist amorph mit unwesentlichen Mengen an kristallinem a-Quarz (< 7%). Die primären Siliciumdioxidpartikel haben eine plattenähnliche Form mit einer Dicke von ungefähr 2 nm. Hochreines mesoporöses amorphes Siliciumdioxid mit offener Porosität und innerer Oberfläche bis zu 400 m2/g kann aus Winterschachtelhalmen isoliert werden. Dies wird erreicht indem man die Pflanze mit Salzsäure behandelt um die anorganischen Verunreinigungen zu entfernen, gefolgt von einer Kalzinierung, wobei die optimale Temperatur bei etwa 500°C liegt. Im Gegensatz zu den chemisch vorbehandelten Schachtelhalmen, verursacht die Kalzinierung von unbehandelten Winterschachtelhalmen einen Kollaps der biogenen Siliciumdioxidstruktur, und es werden nur sehr kleine innere Oberflächen erzielt. Dies wird hauptsächlich dem Einfluss der Alkaliionen zugeschrieben die in der unbehandelten Pflanze vorhanden sind. Es wird schließlich gezeigt, dass durch direkte Pyrolyse der HCl-behandelten Winterschachtelhalme in Argonatmosphäre reines b-SiC mit einer Oberfläche von ungefähr 12 m2/g erzeugt werden kann. Die ursprüngliche Struktur von natürlichen Winterschachtelhalmen bleibt dabei im Wesentlichen im biomorphen b-SiC erhalten. Die Ergebnisse dieser Arbeit führen zu einem besseren Verständnis des Silicifizierungsprozesses und erlauben es auch, Aussagen über die mögliche Rolle von Siliciumdioxid in E.hyemale zu treffen. Insbesondere kann den Pflanzenpolymeren die Rolle eines Templates bei der Synthese des biogenen Siliciumdioxids im Pflanzengewebe zugeschrieben werden. Das aus den Pflanzen isolierte ultrafeine amorphe Siliciumdioxid mit hoher Reinheit verspricht potentielle Anwendungen, z.B. als Adsorbent oder Katalysatorsupport, und auch als Füllmaterial für die Herstellung von Komopositmaterialien. Die Synthese von biomorphem b-SiC aus erneubaren und preiswerten Winterschachtelhalmen steht zwar erst am Anfang, jedoch konnte die vorliegende Arbeit die prinzipielle Machbarkeit aufzeigen. Dieses Material scheint sehr vielversprechend für eine Reihe technischer Anwendung, zum Beispiel als Refraktärmaterial, Katalysatorsupport oder neuartige Hochleistungskeramik. KW - Siliciumdioxid KW - Winterschachtelhalm KW - Raman KW - Röntgenbeugung KW - Mikrotomographie KW - silica KW - Equisetum hyemale KW - Raman KW - SAXS KW - microtomography Y1 - 2007 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-15883 ER -