TY - THES A1 - Hildebrand, Viet T1 - Twofold switchable block copolymers based on new polyzwitterions T1 - Neue Polyzwitterionbasierte Blockcopolymere mit „Schizophrenem Verhalten“ N2 - In complement to the well-established zwitterionic monomers 3-((2-(methacryloyloxy)ethyl)dimethylammonio)propane-1-sulfonate (“SPE”) and 3-((3-methacrylamidopropyl)dimethylammonio)propane-1-sulfonate (“SPP”), the closely related sulfobetaine monomers were synthesized and polymerized by reversible addition-fragmentation chain transfer (RAFT) polymerization, using a fluorophore labeled RAFT agent. The polyzwitterions of systematically varied molar mass were characterized with respect to their solubility in water, deuterated water, and aqueous salt solutions. These poly(sulfobetaine)s show thermoresponsive behavior in water, exhibiting upper critical solution temperatures (UCST). Phase transition temperatures depend notably on the molar mass and polymer concentration, and are much higher in D2O than in H2O. Also, the phase transition temperatures are effectively modulated by the addition of salts. The individual effects can be in parts correlated to the Hofmeister series for the anions studied. Still, they depend in a complex way on the concentration and the nature of the added electrolytes, on the one hand, and on the detailed structure of the zwitterionic side chain, on the other hand. For the polymers with the same zwitterionic side chain, it is found that methacrylamide-based poly(sulfobetaine)s exhibit higher UCST-type transition temperatures than their methacrylate analogs. The extension of the distance between polymerizable unit and zwitterionic groups from 2 to 3 methylene units decreases the UCST-type transition temperatures. Poly(sulfobetaine)s derived from aliphatic esters show higher UCST-type transition temperatures than their analogs featuring cyclic ammonium cations. The UCST-type transition temperatures increase markedly with spacer length separating the cationic and anionic moieties from 3 to 4 methylene units. Thus, apparently small variations of their chemical structure strongly affect the phase behavior of the polyzwitterions in specific aqueous environments. Water-soluble block copolymers were prepared from the zwitterionic monomers and the non-ionic monomer N-isopropylmethacrylamide (“NIPMAM”) by the RAFT polymerization. Such block copolymers with two hydrophilic blocks exhibit twofold thermoresponsive behavior in water. The poly(sulfobetaine) block shows an UCST, whereas the poly(NIPMAM) block exhibits a lower critical solution temperature (LCST). This constellation induces a structure inversion of the solvophobic aggregate, called “schizophrenic micelle”. Depending on the relative positions of the two different phase transitions, the block copolymer passes through a molecularly dissolved or an insoluble intermediate regime, which can be modulated by the polymer concentration or by the addition of salt. Whereas, at low temperature, the poly(sulfobetaine) block forms polar aggregates that are kept in solution by the poly(NIPMAM) block, at high temperature, the poly(NIPMAM) block forms hydrophobic aggregates that are kept in solution by the poly(sulfobetaine) block. Thus, aggregates can be prepared in water, which switch reversibly their “inside” to the “outside”, and vice versa. N2 - Diese Arbeit befasst sich mit der Synthese und Charakterisierung von doppelt thermisch-responsiven Blockcopolymeren mit einem polaren nicht-ionischen Block (der einen LCST-Übergang in wässriger Lösung induziert) und einem zwitterionischen Block (der einen UCST-Übergang aufweisen soll), der durch Salzzusatz über einen weiten Temperaturbereich modulierbar ist. Dafür wurden geeignete zwitterionische Polymer¬blöcke identifiziert und hergestellt, die ein derartiges Löslichkeitsprofil aufweisen. Da bislang nur relativ wenige Poly-sulfobetaine beschrieben sind und entsprechend das wässrige Phasenverhalten nur für einzelne ausgewählte Polymere bekannt ist, wurde ein Grundverständnis von chemischer Struktur und Phasen¬übergangs¬verhalten durch eine systematische Variation des Substitutionsmusters angestrebt. Die als geeignet erkannten Sulfobetain-Monomere wurden mit dem nicht-ionischen Monomer N-Isopropyl-methacrylamid („NIPMAM“) zu Blockcopolymeren von unterschiedlicher Größe und Blocklängen zusammengefügt. Die neuen Blockcopolymere wurden anschließend bezüglich der Lage der Phasenübergänge mit Trübheitsmessungen untersucht. Es wurden 2 Serien neuer zwitterionischer Monomere synthetisiert, deren Struktur den sehr gut untersuchten 3-((2-(methacryloyloxy)ethyl)dimethylammonio)propane-1-sulfonate („SPE“) und 3-((3-methacrylamidopropyl)dimethylammonio)propane-1-sulfonate („SPP“) ähnlich ist. Aus den Monomeren wurden fluoreszenz-markierte Homopolymere mit unterschiedlichen Molmassen mittels der Reversiblen Additions-Fragmentierungs Kettenübertragungs (RAFT) – Polymerisation unter Verwendung eines geeigneten RAFT Reagenzes synthetisiert. Die Poly¬sulfobetaine wurden bezüglich ihrer Löslichkeit in Wasser, in deuteriertem Wasser und in Salzlösungen untersucht. Ihr wässriges Phasenverhalten mit einem UCST-Übergang ist stark abhängig von ihrer Molmasse und von der Polymerkonzentration der untersuchten Lösung. Auffällig ist, dass die Phasenübergangstemperatur in D2O deutlich höher liegt als in H2O. Des Weiteren konnten die Löslichkeit und Phasen-übergangstemperatur durch Salzzusatz effektiv moduliert werden. Prinzipiell stellte sich bei den untersuchten Anionen heraus, dass das Einsalzen bzw. das Aussalzen der empirischen Hofmeister Serie folgt. Dabei hängen die individuellen Effekte sehr stark von der Konzentration und von der Art des Salzes, aber auch in nicht-trivialer Weise von der detaillierten zwitterionischen Struktur stark ab. Durch die systematische Variation der Monomerstruktur wurden interessante Tendenzen offenbar. Die Methacrylamid-basierte Polysulfobetaine besitzen eine höhere Phasenübergangstemperatur als ihre Methacrylat-basierten Analoga. Die Vergrößerung der Distanz zwischen Polymerrückrat und der zwitterionischen Gruppe von 2 auf 3 Methylengruppen führt zu einer Erniedrigung der Phasenübergangstemperatur. Polysulfobetaine mit aliphatischen Resten (Methyl-gruppen) am Ammonium-Ion haben eine höhere Phasenübergangstemperatur als ihre Analoga, in denen der Ammonium-Stickstoff Teil eines Heterozyklus ist. Als letzte Strukturvariable wurde die Distanz zwischen Kation und Anion von 3 auf 4 Methylengruppen vergrößert; diese Änderung führt zu einer massiven Erhöhung der Phasenübergangstemperatur. Die Polysulfobetaine wurden verwendet, um mit dem nicht-ionischen Monomer NIPMAM wasserlösliche Blockcopolymere mittels der RAFT Polymerisation herzustellen. Diese Blockcopolymere besitzen doppelt thermisch-responsives Verhalten (mit einem UCST- und einem LCST-Übergang). Die Besonderheit einer solchen Konstellation ist, dass eine Strukturinversion der solvophoben Aggregate induziert werden kann. Daher werden solche Blockcopolymer-Assoziate auch als „schizophrene Mizellen“ bezeichnet. Je nach der relativen Lage der beiden Phasenübergänge, die sich durch Polymerkonzentration oder durch Salzzusatz einstellen lässt, läuft die Strukturinversion über ein molekular gelöstes oder über ein unlösliches Zwischenstadium ab. Der Polysulfobetain-Block bildet bei niedriger Temperatur Aggregate, die durch den gelösten poly(NIPMAM)-Block in Lösung gehalten werden. Dahingegen bildet der poly(NIPMAM)-Block bei hoher Temperatur Aggregate, welche ihrerseits durch den gelösten Polysulfobetain-Block in Lösung gehalten werden. Somit werden „schizophrene“ Aggregate in Wasser erzeugt, die fähig sind, reversibel ihr „Inneres“ nach „Außen“ und umgekehrt zu schalten durch Nutzen eines einfachen thermischen Impulses. KW - switchable block copolymer KW - polyzwitterion KW - polysulfobetaine KW - thermoresponsive polymers KW - schizophrenic behavior KW - LCST and UCST KW - electrolyte sensitivity KW - zweifach schaltbare Blockcopolymere KW - Polyzwitterion KW - Polysulfobetaine KW - thermoresponsive Polymere KW - schizophrenes Verhalten KW - LCST und UCST KW - Elektrolytempfindlichkeit Y1 - 2016 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-101372 ER - TY - JOUR A1 - Schönemann, Eric A1 - Laschewsky, Andre A1 - Rosenhahn, Axel T1 - Exploring the long-term hydrolytic behavior of zwitterionic polymethacrylates and polymethacrylamides JF - Polymers N2 - The hydrolytic stability of polymers to be used for coatings in aqueous environments, for example, to confer anti-fouling properties, is crucial. However, long-term exposure studies on such polymers are virtually missing. In this context, we synthesized a set of nine polymers that are typically used for low-fouling coatings, comprising the well-established poly(oligoethylene glycol methylether methacrylate), poly(3-(N-2-methacryloylethyl-N,N-dimethyl) ammoniopropanesulfonate) (sulfobetaine methacrylate), and poly(3-(N-3-methacryamidopropyl-N,N-dimethyl)ammoniopropanesulfonate) (sulfobetaine methacrylamide) as well as a series of hitherto rarely studied polysulfabetaines, which had been suggested to be particularly hydrolysis-stable. Hydrolysis resistance upon extended storage in aqueous solution is followed by H-1 NMR at ambient temperature in various pH regimes. Whereas the monomers suffered slow (in PBS) to very fast hydrolysis (in 1 M NaOH), the polymers, including the polymethacrylates, proved to be highly stable. No degradation of the carboxyl ester or amide was observed after one year in PBS, 1 M HCl, or in sodium carbonate buffer of pH 10. This demonstrates their basic suitability for anti-fouling applications. Poly(sulfobetaine methacrylamide) proved even to be stable for one year in 1 M NaOH without any signs of degradation. The stability is ascribed to a steric shielding effect. The hemisulfate group in the polysulfabetaines, however, was found to be partially labile. KW - polyzwitterions KW - stability KW - polymer degradation KW - hydrolysis KW - polysulfobetaine KW - polysulfabetaine KW - anti-fouling materials Y1 - 2018 U6 - https://doi.org/10.3390/polym10060639 SN - 2073-4360 VL - 10 IS - 6 PB - MDPI CY - Basel ER - TY - GEN A1 - Schönemann, Eric A1 - Laschewsky, André A1 - Rosenhahn, Axel T1 - Exploring the long-term hydrolytic behavior of zwitterionic polymethacrylates and polymethacrylamides T2 - Postprints der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe N2 - The hydrolytic stability of polymers to be used for coatings in aqueous environments, for example, to confer anti-fouling properties, is crucial. However, long-term exposure studies on such polymers are virtually missing. In this context, we synthesized a set of nine polymers that are typically used for low-fouling coatings, comprising the well-established poly(oligoethylene glycol methylether methacrylate), poly(3-(N-2-methacryloylethyl-N,N-dimethyl) ammoniopropanesulfonate) (“sulfobetaine methacrylate”), and poly(3-(N-3-methacryamidopropyl-N,N-dimethyl)ammoniopropanesulfonate) (“sulfobetaine methacrylamide”) as well as a series of hitherto rarely studied polysulfabetaines, which had been suggested to be particularly hydrolysis-stable. Hydrolysis resistance upon extended storage in aqueous solution is followed by ¹H NMR at ambient temperature in various pH regimes. Whereas the monomers suffered slow (in PBS) to very fast hydrolysis (in 1 M NaOH), the polymers, including the polymethacrylates, proved to be highly stable. No degradation of the carboxyl ester or amide was observed after one year in PBS, 1 M HCl, or in sodium carbonate buffer of pH 10. This demonstrates their basic suitability for anti-fouling applications. Poly(sulfobetaine methacrylamide) proved even to be stable for one year in 1 M NaOH without any signs of degradation. The stability is ascribed to a steric shielding effect. The hemisulfate group in the polysulfabetaines, however, was found to be partially labile. T3 - Zweitveröffentlichungen der Universität Potsdam : Mathematisch-Naturwissenschaftliche Reihe - 1091 KW - polyzwitterions KW - stability KW - polymer degradation KW - hydrolysis KW - polysulfobetaine KW - polysulfabetaine KW - anti-fouling materials Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-473052 SN - 1866-8372 IS - 1091 ER - TY - THES A1 - Stephan, Niels T1 - Phänomenologische Untersuchungen zur Feuchteempfindlichkeit der elektrischen Eigenschaften von dünnen Polymerfilmen und deren Verwendung für neuartige Feuchtesensoren T1 - Phenomenological research into the humidity sensitivity of the electrical properties of thin polymer films and its use for novel humidity sensors N2 - Ziel dieser Arbeit ist die phänomenologische Untersuchung der Feuchteempfindlichkeit der elektrischen Eigenschaften dünner Polymerschichten. Diese Untersuchungen stellen gleichzeitig Vorarbeiten zur Entwicklung von Prototypen von zwei polymeren Dünnschicht-Feuchtesensoren dar, die sich durch die spezielle Auswahl der feuchtesensitiven Materialien jeweils durch eine besondere Eigenschaft gegenüber kommerziellen Massenprodukten auszeichnen. Ziel der Entwicklungsarbeiten für den ersten Prototypen war die Konstruktion eines schnellen Feuchtesensors, der plötzliche und sprunghafte Feuchteänderungen in der umgebenden Atmosphäre möglichst rasch detektieren kann. Dafür wurden dünne Schichten von Poly-DADMAC auf Interdigitalstrukturen aufgebracht, die einen möglichst direkten Kontakt zwischen feuchtesensitiver Schicht und umgebender, feuchter Atmosphäre gewährleisten. Als Messgrößen dienten die Wechselstromgrößen Widerstand und Kapazität der Schichten. Die Feuchtekennlinien der Schichten zeigen gute Konstanz und hohe Reproduzierbarkeit. Der Widerstand der Schichten ändert sich durch den Einfluss von Feuchte je nach Schichtdicke um 3 bis 5 Größenordnungen und eignet sich als Messgröße für die Feuchtigkeit im gesamten Feuchtebereich. Die Hysterese der Filme konnte auf kleiner als 2,5% r.F. bestimmt werden, die Reproduzierbarkeit auf besser als 1% r.F. Die Ansprechzeit der Schichten lässt sich schichtdickenabhängig zu 1 bis 10 Sekunden bestimmen. Hierbei zeigen besonders die dünnen Schichten kurze Ansprechzeiten. Zielstellung für den zweiten Feuchtesensor war die Entwicklung eines Prototypen, dessen sensitive Schicht sich biostatisch und biozid verhält, so dass er in biotischen Umgebungen eingesetzt werden kann. Es wurden fünf Polysulfobetaine synthetisiert, deren Biozidität und Biostatik mit dem Kontakttest nach Rönnpagel, dem ISO846-Test und Abbautests bestimmt wurde. Zwei Polymere – Poly-DMMAAPS (BT2) und Poly-[MSA-Styren-Sulfobetain] (BT5) – erwiesen sich als ausreichend biozid und biostatisch. Schichten dieser Polymere wurden auf Interdigitalstrukturen aufgezogen, anschließend wurden die Kennlinien dieser Proben aufgenommen. Die Messwerte zeigen für beide Polymere gute Konstanz und eine hohe Reproduzierbarkeit. BT2-Proben sind zwischen 20% und 80% r.F. besonders empfindlich und zeigen über einen Monat keine Langzeitdrift. Vernetzte Proben zeigen bis 50°C keinen temperaturbedingten Abfall der Feuchteempfindlichkeit. Der Einsatz vernetzter BT5-Schichten als kapazitiver Feuchtesensor ist bis etwa 70°C möglich, die Schichten sind selbst nach Lagerung im Hochvakuum und mehrfacher Betauung stabil. Damit liegen zwei funktionsfähige Prototypen von Feuchtesensoren vor, für die die meisten Kennwerte denen von vergleichbaren kommerziellen Feuchtesensoren entsprechen. Gleichzeitig zeichnen sie sich aber durch eine sehr niedrige Ansprechzeit bzw. eine ausreichende Lebensdauer unter biotischen Bedingungen aus. N2 - The topic of this work is the phenomenological investigation of the humidity sensitivity of the electrical properties of thin polymer films. These investigations also act as preparatory work for the development of prototypes of two polymer thin film humidity sensors, which by the choice of the humidity sensitive materials stand out by one special property each compared with commercial mass products. The aim of the development work for the first prototype was the construction of a fast humidity sensor, which can rapidly detect sudden and erratic humidity changes in the surrounding atmosphere. Thin films of poly-DADMAC were prepared on interdigitated structures that allow for undisturbed contact between the sensitive layer and the surrounding humid atmosphere. Measured variables were the ac resistance and capacity of the films. The humidity characteristics of the films show good stability and high reproducibility. Under the influence of humidity the resistance of the films changes by 3 to 5 orders of magnitude, depending on the film thickness, and is suitable to measure the humidity in the entire humidity range. The hysteresis of the films is lower than 2.5% r.h., the reproducibility better than 1% r.h. The response time of the layers can be determined to 1 to 10 seconds, depending on their thickness. The thin films, specifically, show very short response times. The aim for the second humidity sensor was the development of a prototype, where the sensitive film is biostatic and biocide, so that it can be used to measure the humidity in biotic environments. Five polysulfobetaines were synthesized and their biocidity and biostatics were tested with the contact test according to Rönnpagel, the ISO846 test and degradation tests. Two of the polymers - poly-DMMAAPS (BT2) and poly-[MSA-styrene-sulfobetaine] (BT5) - showed sufficient biocidity and biostatics. Films of these polymers were prepared on interdigitated structures, then their humidity characteristics were recorded. The measured values show good stability and high reproducibility for both polymers. Samples of BT2 are highly sensitive between 20% and 80% r.h. and show no long-term drift after one month. Cross-linked samples show no decrease of the humidity sensitivity in temperatures up to 50 degrees Celsius. Cross-linked films of BT5 can be used as a capacitive humidity sensor up to 70 degrees Celsius, and the samples are stable even after storage in high vacuum and multiple dew cycles. These two functional prototypes of humidity sensors show characteristic data comparable to those of commercial sensors. However, they stand out, respectively, with a very short response time and a sufficient life time in biotic environments. KW - Polymere KW - Feuchtesensor KW - dünne Schichten KW - Poly-DADMAC KW - Polysulfobetain KW - polymers KW - humidity sensor KW - thin films KW - poly-DADMAC KW - polysulfobetaine Y1 - 2007 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-13853 ER -