TY - THES A1 - Ba, Jianhua T1 - Nonaqueous synthesis of metal oxide nanoparticles and their assembly into mesoporous materials T1 - Nichtwässrige Synthese von Metalloxid-Nanopartikeln und deren Anordnung zu mesoporösen Materialien N2 - This thesis mainly consist of two parts, the synthesis of several kinds of technologically interesting crystalline metal oxide nanoparticles via nonaqueous sol-gel process and the formation of mesoporous metal oxides using some of these nanoparticles as building blocks via evaporation induced self-assembly (EISA) technique. In the first part, the experimental procedures and characterization results of successful syntheses of crystalline tin oxide and tin doped indium oxide (ITO) nanoparticles are reported. SnO2 nanoparticles exhibit monodisperse particle size (3.5 nm in average), high crystallinity and particularly high dispersibility in THF, which enable them to become the ideal particulate precursor for the formation of mesoporous SnO2. ITO nanoparticles possess uniform particle morphology, narrow particle size distribution (5-10 nm), high crystallinity as well as high electrical conductivity. The synthesis approaches and characterization of various mesoporous metal oxides, including TiO2, SnO2, mixture of CeO2 and TiO2, mixture of BaTiO3 and SnO2, are reported in the second part of this thesis. Mesoporous TiO2 and SnO2 are presented as highlights of this part. Mesoporous TiO2 was produced in the forms of both films and bulk material. In the case of mesoporous SnO2, the study was focused on the high order of the porous structure. All these mesoporous metal oxides show high crystallinity, high surface area and rather monodisperse pore sizes, which demonstrate the validity of EISA process and the usage of preformed crystalline nanoparticles as nanobuilding blocks (NBBs) to produce mesoporous metal oxides. N2 - Diese Arbeit besteht hauptsächlich aus zwei Teilen. Der erste Teil befasst sich mit der Synthese von mehreren technologisch wichtigen, kristallinen Metalloxid-Nanopartikeln mittels nichtwässriger Sol-Gel Chemie. Der zweite Teil beinhaltet die Herstellung von mesoporösen Metalloxiden. Dabei wurden ausgewählte Nanopartikel als Bausteine verwendet und durch langsames Verdampfen des Lösungsmittels in die entsprechenden porösen Strukturen überführt. Das experimentelle Vorgehen wie auch die Charakterisierung der erfolgreich hergestellten Zinnoxid- und Indiumzinnoxid-Nanopartikel sind im ersten Teil beschrieben. Die Zinnoxid-Nanpartikel zeichnen sich durch einheitliche Partikelgrösse (im Durchschnitt ca. 3.5 nm), hoher Kristallinität, und guter Dispergierbarkeit in Tetrahydrofuran aus. Diese Eigenschaften machen aus den Zinnoxid-Nanopartikeln die perfekten Bausteine für den Aufbau von mesoporösem Zinnoxid. Die Indiumzinnoxid-Nanopartikel haben eine einheitliche Partikelform, eine schmale Grösseverteilung (5-10 nm), hohe Kristallinität wie auch gute elektrische Leitfähigkeit. Die Synthese und Charakterisierung von verschiedenen mesoporösen Metalloxiden wie TiO2, SnO2, Mischungen von CeO2 und TiO2, wie auch Mischungen von BaTiO3 und SnO2 werden im zweiten Teil der Arbeit diskutiert. Mesoporöses TiO2 und SnO2 werden als besonders gelungene Beispiele herausgehoben. Mesoporöses TiO2 wurde in Form von Dünnfilmen wie auch als Bulkmaterial hergestellt. Im Falle von SnO2 galt das Augenmerk vor allem der hohen Ordnung der Mesoporen. Alle diese mesoporösen Materialien zeigen eine hohe Kristallinität, grosse Oberfläche und relativ einheitliche Porengrössen. Diese Eigenschaften unterstreichen, wie wertvoll der Ansatz ist, vorgeformte Nanopartikel als Bausteine für die Synthese von porösen Materialien zu verwenden. KW - Nanopartikel KW - transparent-leitendes Oxid KW - Selbstorganisation KW - nanoparticles KW - oxides KW - assembly KW - mesostructure Y1 - 2006 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-10173 ER - TY - THES A1 - Bomm, Jana T1 - Von Gold Plasmonen und Exzitonen : Synthese, Charakterisierung und Applikationen von Gold Nanopartikeln T1 - Of gold plasmons and excitons : synthesis, characterization and applications of gold nanoparticles N2 - In dieser Arbeit wurden sphärische Gold Nanopartikel (NP) mit einem Durchmesser größer ~ 2 nm, Gold Quantenpunkte (QDs) mit einem Durchmesser kleiner ~ 2 nm sowie Gold Nanostäbchen (NRs) unterschiedlicher Länge hergestellt und optisch charakterisiert. Zudem wurden zwei neue Synthesevarianten für die Herstellung thermosensitiver Gold QDs entwickelt werden. Sphärische Gold NP zeigen eine Plasmonenbande bei ~ 520 nm, die auf die kollektive Oszillation von Elektronen zurückzuführen ist. Gold NRs weisen aufgrund ihrer anisotropen Form zwei Plasmonenbanden auf, eine transversale Plasmonenbande bei ~ 520 nm und eine longitudinale Plasmonenbande, die vom Länge-zu-Durchmesser-Verhältnis der Gold NRs abhängig ist. Gold QDs besitzen keine Plasmonenbande, da ihre Elektronen Quantenbeschränkungen unterliegen. Gold QDs zeigen jedoch aufgrund diskreter Energieniveaus und einer Bandlücke Photolumineszenz (PL). Die synthetisierten Gold QDs besitzen eine Breitbandlumineszenz im Bereich von ~ 500-800 nm, wobei die Lumineszenz-eigenschaften (Emissionspeak, Quantenausbeute, Lebenszeiten) stark von den Herstellungs-bedingungen und den Oberflächenliganden abhängen. Die PL in Gold QDs ist ein sehr komplexes Phänomen und rührt vermutlich von Singulett- und Triplett-Zuständen her. Gold NRs und Gold QDs konnten in verschiedene Polymere wie bspw. Cellulosetriacetat eingearbeitet werden. Polymernanokomposite mit Gold NRs wurden erstmals unter definierten Bedingungen mechanisch gezogen, um Filme mit optisch anisotropen (richtungsabhängigen) Eigenschaften zu erhalten. Zudem wurde das Temperaturverhalten von Gold NRs und Gold QDs untersucht. Es konnte gezeigt werden, dass eine lokale Variation der Größe und Form von Gold NRs in Polymernanokompositen durch Temperaturerhöhung auf 225-250 °C erzielt werden kann. Es zeigte sich, dass die PL der Gold QDs stark temperaturabhängig ist, wodurch die PL QY der Proben beim Abkühlen (-7 °C) auf knapp 30 % verdoppelt und beim Erhitzen auf 70 °C nahezu vollständig gelöscht werden konnte. Es konnte demonstriert werden, dass die Länge der Alkylkette des Oberflächenliganden einen Einfluss auf die Temperaturstabilität der Gold QDs hat. Zudem wurden verschiedene neuartige und optisch anisotrope Sicherheitslabels mit Gold NRs sowie thermosensitive Sicherheitslabel mit Gold QDs entwickelt. Ebenso scheinen Gold NRs und QDs für die und die Optoelektronik (bspw. Datenspeicherung) und die Medizin (bspw. Krebsdiagnostik bzw. -therapie) von großem Interesse zu sein. N2 - In this thesis, the synthesis and optical characterization of spherical gold nanoparticles (NP) with diameters larger than ~ 2 nm, gold quantum dots (QDs) with diameters smaller than ~ 2 nm and gold nanorods (NRs) with different lengths are presented. In addition, a novel one-pot synthesis for the preparation of thermosensitive gold QDs is introduced. Gold NP solutions appear red colored due to their strong absorption in the visible range at ~ 520 nm. This absorption band is a result of surface plasmon resonance, which is caused by the coherent oscillation of conduction band electrons induced by an electromagnetic field. In contrast to spherical gold NPs, gold NRs show two surface plasmon bands due to their anisotropic shape, a transverse plasmon band at ~ 520 nm and a longitudinal plasmon band depending on the aspect ratio (length-to-width-ratio) of the gold NRs. If the size of the gold NPs decreases to values below ~ 2 nm, quantum-size confinement occurs and the surface plasmon band disappears. Additionally, the overlap between conduction band and valence band disappears, discrete electronic levels arise and a band gap is created. As a consequence of quantum confinement, the gold QDs show photoluminescence (PL) upon UV-irradiation. The gold QDs synthesized via the one-pot synthesis exhibit a broadband luminescence between 500 nm and 800 nm. The luminescence properties (emission peak, quantum yield, lifetime) strongly depend on the synthetic parameters like reaction temperature, stoichiometry and the surface ligand. Gold NRs and gold QDs were incoroporated into different polymers (e.g. cellulose triacetate). Polymer nanocomposite films showing optical anisotropy are obtainded by stretching polymer films containing gold NRs uniaxial in a tensile test machine. In addition to the optical characterization of gold NRs and QDs, their thermal behavior in solution as well as in different nanocomposites is studied. A shortening of the gold NRs or a transformation into spherical gold NP is observed, if the polymer nanocomposites containing gold NRs are heated above a temperature of 200 °C. The PL of the synthesized gold QDs strongly depends on the ambient temperature. An increase of PL quantum yield (QY) and PL lifetime occur, if the solutions are cooled. The best PL QY of 16.6 % was observed for octadecyl mercaptan capped gold QDs at room temperature, which could be improved to 28.6 % when cooling the solutions to -7 °C. Furthermore, optically anisotropic security labels containing gold NRs and thermosensitive security devices containing gold QDs are developed. Due to their unique optical properties, gold NRs and QDs are interesting candidates for optoelectronical as well as data storage devices and medical applications like biomedical imaging or cancer therapy. KW - Gold KW - Nanopartikel KW - Quantenpunkte KW - Nanostäbchen KW - Oberflächenplasmonenlasmonen KW - gold KW - nanoparticles KW - quantum dots KW - nanorods KW - surface plasmons Y1 - 2012 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-66402 ER - TY - THES A1 - Buha, Jelena T1 - Nonaqueous syntheses of metal oxide and metal nitride nanoparticles T1 - Nichtwässrige Synthesen von Metalloxid- und Metallnitrid-Nanopartikeln N2 - Nanostructured materials are materials consisting of nanoparticulate building blocks on the scale of nanometers (i.e. 10-9 m). Composition, crystallinity and morphology can enhance or even induce new properties of the materials, which are desirable for todays and future technological applications. In this work, we have shown new strategies to synthesise metal oxide and metal nitride nanomaterials. The first part of the work deals with the study of nonaqueous synthesis of metal oxide nanoparticles. We succeeded in the synthesis of In2O3 nanopartcles where we could clearly influence the morphology by varying the type of the precursors and the solvents; of ZnO mesocrystals by using acetonitrile as a solvent; of transition metal oxides (Nb2O5, Ta2O5 and HfO2) that are particularly hard to obtain on the nanoscale and other technologically important materials. Solvothermal synthesis however is not restricted to formation of oxide materials only. In the second part we show examples of nonaqueous, solvothermal reactions of metal nitrides, but the main focus lies on the investigation of the influence of different morphologies of metal oxide precursors on the formation of the metal nitride nanoparticles. In spite of various reports, the number and variety of nanocrystalline metal nitrides is marginally small by comparison to metal oxides; hence preformed metal oxides as precursors for the preparation of metal nitrides are a logical choice. By reacting oxide nanoparticles with cyanamide, urea or melamine, at temperatures of 800 to 900 °C under nitrogen flow metal nitrides could be obtained. We studied in detail the influence of the starting material and realized that size, crystallinity, type of nitrogen source and temperature play the most important role. We have managed to propose and verify a dissolution-recrystallisation model as the formation mechanism. Furthermore we could show that the initial morphology of the oxides could be retained when ammonia flow was used instead. N2 - Nanostrukturierte Materialien sind Materialien, die aus nanopartikulären Baueinheiten in der Größenordnung von Nanonmetern (d.h. 10-9 m) bestehen. Zusammensetzung, Kristallinität und Morphologie können die natürlichen Eigenschaften dieser Materialien verbessern oder zusätzliche Eigenschaften erzeugen, die für heutige und zukünftige Anwendungen und Verfahren wünschenswert sind. In dieser Arbeit präsentieren wir neue Strategien zur Synthese von Nanopartikeln der Metaloxide und Metalnitride. Im einführenden Teil wird die nichtwässrige Synthese von Metaloxidnanopartikeln beschrieben. Uns gelang die Darstellung von In2O3 Nanopartikeln, deren Größe und Form wir durch die Wahl des Prekursors und des Lösemittels deutlich beeinflussen konnten; von ZnO Mesokristallen durch den Einsatz von Acetonitril als Lösemittel; von Übergangsmetalloxiden (Nb2O5, Ta2O5 and HfO2), die besonders schwer im Nanomaßstab zu erhalten sind und von anderen, technisch relevanten Materialien. Die Möglichkeiten der solvothermalen Synthese sind nicht mit der Darstellung von Oxidmaterialen erschöpft. Im zweiten Teil zeigen wir einige Beispiele nichtwässriger, solvothermaler Synthese von Metalnitriden auf; das Hauptaugenmerk liegt aber auf einer Betrachtung der Einflüsse der Morphologie von Metaloxidnanopartikelprekursoren auf die Bildung der Metalnitridnanopartikel. Die Anzahl und Vielfalt bekannter nanokristalliner Metalnitride ist verschwindend klein im Vergleich zu den Metaloxiden, die in der Fachliteratur etabliert sind und demzufolge einen reichen Baukasten an Prekursoren zur Darstellung von Metalnitriden liefern. Durch die Reaktion von Metaloxidnanopartikeln mit Cyanamid, Urea oder Melamine bei Temperaturen von 800 bis 900 °C unter Stickstofffluss konnten Metalnitride erhalten werden. Eine detaillierte Studie der Reaktionsbedingungen und des Reaktionsablaufs zeigte auf, dass Größe und Kristallinität der Metaloxide, die Art der Stickstoffquelle und die Temperatur die entscheidenden Faktoren sind und legte eine Auflösungs-Rekristallisation als Modelmechanismus dieser Art Reaktion nahe. Darüber hinaus konnte gezeigt worden, dass die anfängliche Morphologie des Oxids unter einem Ammoniafluss beibehalten werden konnte. KW - Nichtwässrige Synthese KW - Nanopartikel KW - Metalloxide KW - Metallnitride KW - nonaqueous synthesis KW - nanoparticles KW - metal oxides KW - metal nitrides Y1 - 2008 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-18368 ER - TY - JOUR A1 - Caetano, Daniel L. Z. A1 - Carvalho, Sidney Jurado de A1 - Metzler, Ralf A1 - Cherstvy, Andrey G. T1 - Critical adsorption of multiple polyelectrolytes onto a nanosphere BT - splitting the adsorption-desorption transition boundary JF - Interface : journal of the Royal Society N2 - Employing extensive Monte Carlo computer simulations, we investigate in detail the properties of multichain adsorption of charged flexible polyelectrolytes (PEs) onto oppositely charged spherical nanoparticles (SNPs). We quantify the conditions of critical adsorption-the phase-separation curve between the adsorbed and desorbed states of the PEs-as a function of the SNP surface-charge density and the concentration of added salt. We study the degree of fluctuations of the PE-SNP electrostatic binding energy, which we use to quantify the emergence of the phase subtransitions, including a series of partially adsorbed PE configurations. We demonstrate how the phase-separation adsorption-desorption boundary shifts and splits into multiple subtransitions at low-salt conditions, thereby generalizing and extending the results for critical adsorption of a single PE onto the SNP. The current findings are relevant for finite concentrations of PEs around the attracting SNP, such as the conditions for PE adsorption onto globular proteins carrying opposite electric charges. KW - nanoparticles KW - polyelectrolytes KW - electrostatics KW - critical adsorption KW - phase-transition boundary Y1 - 2020 U6 - https://doi.org/10.1098/rsif.2020.0199 SN - 1742-5689 SN - 1742-5662 VL - 17 IS - 167 PB - Royal Society CY - London ER - TY - JOUR A1 - Cui, Qianling A1 - Shen, Guizhi A1 - Yan, Xuehai A1 - Li, Lidong A1 - Moehwald, Helmuth A1 - Bargheer, Matias T1 - Fabrication of Au@Pt multibranched nanoparticles and their application to in situ SERS monitoring JF - ACS applied materials & interfaces N2 - Here, we present an Au@Pt core-shell multibranched nanoparticle as a new substrate capable of in situ surface-enhanced Raman scattering (SERS), thereby enabling monitoring of the catalytic reaction on the active surface. By careful control of the amount of Pt deposited bimetallic Au@Pt, nanoparticles with moderate performance both for SERS and catalytic activity were obtained. The Pt-catalyzed reduction of 4-nitrothiophenol by borohydride was chosen as the model reaction. The intermediate during the reaction was captured and clearly identified via SERS spectroscopy. We established in situ SERS spectroscopy as a promising and powerful technique to investigate in situ reactions taking place in heterogeneous catalysis. KW - nanoparticles KW - gold KW - core-shell nanostructure KW - surface-enhanced Raman scattering KW - heterogeneous catalysis KW - bimetallic nanoparticles Y1 - 2014 U6 - https://doi.org/10.1021/am504709a SN - 1944-8244 VL - 6 IS - 19 SP - 17075 EP - 17081 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Cui, Qianling A1 - Yashchenok, Alexey A1 - Zhang, Lu A1 - Li, Lidong A1 - Masic, Admir A1 - Wienskol, Gabriele A1 - Moehwald, Helmuth A1 - Bargheer, Matias T1 - Fabrication of Bifunctional Gold/Gelatin Hybrid Nanocomposites and Their Application JF - ACS applied materials & interfaces N2 - Herein, a facile method is presented to integrate large gold nanoflowers (similar to 80 nm) and small gold nanoparticles (2-4 nm) into a single entity, exhibiting both surface-enhanced Raman scattering (SERS) and catalytic activity. The as-prepared gold nanoflowers were coated by a gelatin layer, in which the gold precursor was adsorbed and in situ reduced into small gold nanoparticles. The thickness of the gelatin shell is controlled to less than 10 nm, ensuring that the small gold nanoparticles are still in a SERS-active range of the inner Au core. Therefore, the reaction catalyzed by these nanocomposites can be monitored in situ using label-free SERS spectroscopy. In addition, these bifunctional nanocomposites are also attractive candidates for application in SERS monitoring of bioreactions because of their excellent biocompatibility. KW - core-shell nanostructure KW - gold KW - hybrid material KW - gelatin KW - nanoparticles KW - surface-enhanced Raman scattering Y1 - 2014 U6 - https://doi.org/10.1021/am5000068 SN - 1944-8244 VL - 6 IS - 3 SP - 1999 EP - 2002 PB - American Chemical Society CY - Washington ER - TY - THES A1 - Dai, Xiaolin T1 - Synthesis of artificial building blocks for sortase-mediated ligation and their enzymatic linkage T1 - Synthese von artifiziellen Bausteinen für Sortase-vermittelte Ligationen und deren enzymatische Verknüpfung N2 - Das Enzym Sortase A katalysiert die Bildung einer Peptidbindung zwischen der Erkennungssequenz LPXTG und einem Oligoglycin. Während vielfältige Ligationen zwischen Proteinen und verschiedenen Biomolekülen, Proteinen und kleinen synthetischen Molekülen, sowie Proteinen und Oberflächen durchgeführt wurden, besteht das Ziel dieser Arbeit darin, die Sortase-katalysierte Verlinkung von synthetischen Bausteinen zu untersuchen. Dies könnte den Weg bereiten für die Anwendung von Sortase A für chemische Aufgabenstellungen und eventuell sogar in den Materialwissenschaften. Für diese grundsätzliche Untersuchung wurden die verwendeten Bausteine zunächst so einfach wie möglich gehalten und leicht zugängliche SiO2 Nanopartikel und kommerziell erhältliche Polymerblöcke ausgewählt. Die Bausteine wurden als erstes mit den Peptidsequenzen für Sortase-vermittelte Ligationen funktionalisiert. SiO2 Nanopartikel wurden mit Durchmessern von 60 und 200 nm hergestellt und mit C=C Doppelbindungen oberflächenmodifiziert. Dann wurden Peptide mit einem terminalen Cystein kovalent durch eine Thiol-en Reaktion angebunden. An die 60 nm NP wurden Peptide mit einem Pentaglycin und an die 200 nm Partikel Peptide mit LPETG Sequenz gebunden. Auf die gleiche Art und Weise wurden Peptide mit terminalem Cystein an die Polymere Polyethylenglykol (PEG) und Poly(N Isopropylacrylamid) (PNIPAM), die beide über C=C Endgruppen verfügen, gebunden und G5-PEG und PNIPAM-LPETG Konjugate erhalten. Mit den vier Bausteinen wurden nun durch Sortase-vermittelte Ligation NP–Polymer Hybride, NP–NP und Polymer–Polymer Strukturen hergestellt und die Produkte u. a. durch Transmissionselektronen-mikroskopie, MALDI-ToF Massenspektrometrie sowie Dynamische Lichtstreuung charakterisiert. Die Verlinkung dieser synthetischen Bausteine konnte eindeutig gezeigt werden. Das Verwenden von kommerziell erhältlichen Polymeren hat jedoch zu einem Gemisch der Polymer-Peptid Konjugate mit unmodifiziertem Polymer geführt, welches nicht gereinigt werden konnte. Deswegen wurden anschließend Synthesestrategien für reine Peptid-Polymer und Polymer-Peptid Konjugate als Bausteine für Sortase-vermittelte Ligationen entwickelt. Diese basieren auf der RAFT Polymerisation mit CTAs, die entweder an N- oder C-Terminus eines Peptids gebunden sind. GG-PNIPAM wurde durch das Anbinden eines geeigneten RAFT CTAs an Fmoc-GG in einer Veresterungsreaktion, Polymerisation von NIPAM und Abspalten der Fmoc Schutzgruppe synthetisiert. Weiterhin wurden mehrere Peptide durch Festphasen-Peptidsynthese erhalten. Die Anbindung eines RAFT CTAs (oder eines Polymerisationsinitiators) an den N-Terminus eines Peptids kann automatisiert als letzter Schritt in einem Peptid-Synthetisierer erfolgen. Die Synthese eines solchen Konjugats konnte in dem Zeithorizont dieser Arbeit noch nicht erreicht werden. Jedoch existieren mehrere vielversprechende Strategien, um diesen Ansatz mit verschiedenen Kopplungsreagenzien zur Anbindung des CTAs fortzusetzen. Solche Polymer Bausteine können in Zukunft für die Synthese von Protein-Polymer Konjugaten durch Sortase-Katalyse verwendet werden. Außerdem kann der Ansatz auch für die Synthese von Block-Copolymeren aus Polymerblöcken mit Peptidmotiven an beiden Enden ausgebaut werden. Auch wenn bei der grundsätzlichen Untersuchung im Rahmen dieser Arbeit Hybridstrukturen hergestellt wurden, die auch durch traditionelle chemische Synthesen erhalten werden könnten, wird ein Bausatz solcher Bausteine in Zukunft die Synthese neuer Materialien ermöglichen und kann auch den Weg für die Anwendung von Enzymen in den Materialwissenschaften ebnen. In Ergänzung zu Nanopartikeln und Block-Copolymeren können dann auch Hybridmaterialien unter Einbezug von Protein-basierten Bausteinen hergestellt werden. Daher könnten Sortase Enzyme zu einem Werkzeug werden, welches etablierte chemische Verlinkungstechniken ergänzt und mit den hoch spezifischen Peptidmotiven über funktionale Einheiten verfügt, die orthogonal zu allen chemischen Gruppen sind. N2 - The enzyme Sortase A catalyzes the formation of a peptide bond between the recognition sequence LPXTG and an oligoglycine. While manifold ligations between proteins and various biomolecules, proteins and small synthetic molecules as well as proteins and surfaces have been reported, the aim of this thesis was to investigate the sortase-catalyzed linkage between artificial building blocks. Hence, this could pave the way for the use of sortase A for tasks from a chemical point of view and maybe even materials science. For the proof of concept, the studied systems were kept as simple as possible at first by choosing easily accessible silica NPs and commercially available polymers. These building blocks were functionalized with peptide motifs for sortase-mediated ligation. Silica nanoparticles were synthesized with diameters of 60 and 200 nm and surface modified with C=C functionalities. Then, peptides bearing a terminal cysteine were covalently linked by means of a thiol-ene reaction. 60 nm SiO2 NPs were functionalized with pentaglycines, while peptides with LPETG motif were linked to 200 nm silica particles. Polyethyleneglycol (PEG) and poly(N isopropylacrylamide) (PNIPAM) were likewise functionalized with peptides by thiol-ene reaction between cysteine residues and C=C units in the polymer end groups. Hence, G5-PEG and PNIPAM-LPETG conjugates were obtained. With this set of building blocks, NP–polymer hybrids, NP–NP, and polymer–polymer structures were generated by sortase-mediated ligation and the product formation shown by transmission electron microscopy, MALDI-ToF mass spectrometry and dynamic light scatting, among others. Thus, the linkage of these artificial building blocks by the enzyme sortase A could be demonstrated. However, when using commercially available polymers, the purification of the polymer–peptide conjugates was impossible and resulted in a mixture containing unmodified polymer. Therefore, strategies were developed for the own synthesis of pure peptide-polymer and polymer-peptide conjugates as building blocks for sortase-mediated ligation. The designed routes are based on preparing polymer blocks via RAFT polymerization from CTAs that are attached to N- or C-terminus, respectively, of a peptide. GG-PNIPAM was synthesized through attachment of a suitable RAFT CTA to Fmoc-GG in an esterification reaction, followed by polymerization of NIPAM and cleavage of the Fmoc protection group. Furthermore, several peptides were synthesized by solid-phase peptide synthesis. The linkage of a RAFT CTA (or polymerization initiator) to the N-terminus of a peptide can be conducted in an automated fashion as last step in a peptide synthesizer. The synthesis of such a conjugate couldn’t be realized in the time frame of this thesis, but many promising strategies exist to continue this strategy using different coupling reagents. Such polymer building blocks can be used to synthesize protein-polymer conjugates catalyzed by sortase A and the approach can be carried on to the synthesis of block copolymers by using polymer blocks with peptide motifs on both ends. Although the proof of concept demonstrated in this thesis only shows examples that can be also synthesized by exclusively chemical techniques, a toolbox of such building blocks will enable the future formation of new materials and pave the way for the application of enzymes in materials science. In addition to nanoparticle systems and block copolymers, this also includes combination with protein-based building blocks to form hybrid materials. Hence, sortase could become an enzymatic tool that complements established chemical linking technologies and provides specific peptide motifs that are orthogonal to all existing chemical functional groups. KW - sortase-mediated ligation KW - enzyme KW - block copolymers KW - nanoparticles KW - Ligation KW - Enzym KW - Block-Copolymere KW - Nanopartikel Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-420060 ER - TY - JOUR A1 - Dai, Xiaolin A1 - Mate, Diana M. A1 - Glebe, Ulrich A1 - Garakani, Tayebeh Mirzaei A1 - Körner, Andrea A1 - Schwaneberg, Ulrich A1 - Böker, Alexander T1 - Sortase-mediated ligation of purely artificial building blocks JF - Polymers N2 - Sortase A (SrtA) from Staphylococcus aureus has been often used for ligating a protein with other natural or synthetic compounds in recent years. Here we show that SrtA-mediated ligation (SML) is universally applicable for the linkage of two purely artificial building blocks. Silica nanoparticles (NPs), poly(ethylene glycol) and poly(N-isopropyl acrylamide) are chosen as synthetic building blocks. As a proof of concept, NP-polymer, NP-NP, and polymer-polymer structures are formed by SrtA catalysis. Therefore, the building blocks are equipped with the recognition sequence needed for SrtA reaction-the conserved peptide LPETG-and a pentaglycine motif. The successful formation of the reaction products is shown by means of transmission electron microscopy (TEM), matrix assisted laser desorption ionization-time of flight mass spectrometry (MALDI-ToF MS), and dynamic light scattering (DLS). The sortase catalyzed linkage of artificial building blocks sets the stage for the development of a new approach to link synthetic structures in cases where their synthesis by established chemical methods is complicated. KW - sortase-mediated ligation KW - enzymes KW - block copolymers KW - nanoparticles Y1 - 2018 U6 - https://doi.org/10.3390/polym10020151 SN - 2073-4360 VL - 10 IS - 2 PB - MDPI CY - Basel ER - TY - JOUR A1 - Dey, Pradip A1 - Bergmann, Tobias A1 - Cuellar-Camacho, Jose Luis A1 - Ehrmann, Svenja A1 - Chowdhury, Mohammad Suman A1 - Zhang, Minze A1 - Dahmani, Ismail A1 - Haag, Rainer A1 - Azad, Walid T1 - Multivalent flexible nanogels exhibit broad-spectrum antiviral activity by blocking virus entry JF - ACS nano N2 - The entry process of viruses into host cells is complex and involves stable but transient multivalent interactions with different cell surface receptors. The initial contact of several viruses begins with attachment to heparan sulfate (HS) proteoglycans on the cell surface, which results in a cascade of events that end up with virus entry. The development of antiviral agents based on multivalent interactions to shield virus particles and block initial interactions with cellular receptors has attracted attention in antiviral research. Here, we designed nanogels with different degrees of flexibility based on dendritic polyglycerol sulfate to mimic cellular HS. The designed nanogels are nontoxic and broad-spectrum, can multivalently interact with viral glycoproteins, shield virus surfaces, and efficiently block infection. We also visualized virus-nanogel interactions as well as the uptake of nanogels by the cells through clathrin-mediated endocytosis using confocal microscopy. As many human viruses attach to the cells through HS moieties, we introduce our flexible nanogels as robust inhibitors for these viruses. KW - multivalent KW - herpes simplex virus KW - heparan sulfate KW - nanoparticles KW - click chemistry KW - polyglycerol Y1 - 2018 U6 - https://doi.org/10.1021/acsnano.8b01616 SN - 1936-0851 SN - 1936-086X VL - 12 IS - 7 SP - 6429 EP - 6442 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Draude, F. A1 - Galla, S. A1 - Pelster, Axel A1 - Tentschert, J. A1 - Jungnickel, H. A1 - Haase, Alfred A1 - Mantion, Alexandre A1 - Thuenemann, Andreas F. A1 - Taubert, Andreas A1 - Luch, A. A1 - Arlinghaus, H. F. T1 - ToF-SIMS and Laser-SNMS analysis of macrophages after exposure to silver nanoparticles JF - Surface and interface analysis : an international journal devoted to the development and application of techniques for the analysis surfaces, interfaces and thin films N2 - Silver nanoparticles (SNPs) are among the most commercialized nanoparticles because of their antibacterial effects. Besides being employed, e. g. as a coatingmaterial for sterile surfaces in household articles and appliances, the particles are also used in a broad range of medical applications. Their antibacterial properties make SNPs especially useful for wound disinfection or as a coating material for prostheses and surgical instruments. Because of their optical characteristics, the particles are of increasing interest in biodetection as well. Despite the widespread use of SNPs, there is little knowledge of their toxicity. Time-of-flight secondary ion mass spectrometry (ToF-SIMS) and laser post-ionization secondary neutral mass spectrometry (Laser-SNMS) were used to investigate the effects of SNPs on human macrophages derived from THP-1 cells in vitro. For this purpose, macrophages were exposed to SNPs. The SNP concentration ranges were chosen with regard to functional impairments of the macrophages. To optimize the analysis of the macrophages, a special silicon wafer sandwich preparation technique was employed; ToF-SIMS was employed to characterize fragments originating from macrophage cell membranes. With the use of this optimized sample preparation method, the SNP-exposed macrophages were analyzed with ToF-SIMS and with Laser-SNMS. With Laser-SNMS, the three-dimensional distribution of SNPs in cells could be readily detected with very high efficiency, sensitivity, and submicron lateral resolution. We found an accumulation of SNPs directly beneath the cell membrane in a nanoparticular state as well as agglomerations of SNPs inside the cells. KW - Laser-SNMS KW - ToF-SIMS KW - life sciences KW - imaging KW - nanoparticles KW - three-dimensional depth profiling Y1 - 2013 U6 - https://doi.org/10.1002/sia.4902 SN - 0142-2421 VL - 45 IS - 1 SP - 286 EP - 289 PB - Wiley-Blackwell CY - Hoboken ER -