TY - THES A1 - Zimmermann, Marc T1 - Multifunctional patchy silica particles via microcontact printing T1 - Multifunktionale Patchy Silika Partikel mithilfe des Mikrokontaktdruckverfahrens N2 - This research addressed the question, if it is possible to simplify current microcontact printing systems for the production of anisotropic building blocks or patchy particles, by using common chemicals while still maintaining reproducibility, high precision and tunability of the Janus-balance Chapter 2 introduced the microcontact printing materials as well as their defined electrostatic interactions. In particular polydimethylsiloxane stamps, silica particles and high molecular weight polyethylenimine ink were mainly used in this research. All of these components are commercially available in large quantities and affordable, which gives this approach a huge potential for further up-scaling developments. The benefits of polymeric over molecular inks was described including its flexible influence on the printing pressure. With this alteration of the µCP concept, a new method of solvent assisted particle release mechanism enabled the switch from two-dimensional surface modification to three-dimensional structure printing on colloidal silica particles, without changing printing parameters or starting materials. This effect opened the way to use the internal volume of the achieved patches for incorporation of nano additives, introducing additional physical properties into the patches without alteration of the surface chemistry. The success of this system and its achievable range was further investigated in chapter 3 by giving detailed information about patch geometry parameters including diameter, thickness and yield. For this purpose, silica particles in a size range between 1µm and 5µm were printed with different ink concentrations to change the Janus-balance of these single patched particles. A necessary intermediate step, consisting of air-plasma treatment, for the production of trivalent particles using "sandwich" printing was discovered and comparative studies concerning the patch geometry of single and double patched particles were conducted. Additionally, the usage of structured PDMS stamps during printing was described. These results demonstrate the excellent precision of this approach and opens the pathway for even greater accuracy as further parameters can be finely tuned and investigated, e.g. humidity and temperature during stamp loading. The performance of these synthesized anisotropic colloids was further investigated in chapter 4, starting with behaviour studies in alcoholic and aqueous dispersions. Here, the stability of the applied patches was studied in a broad pH range, discovering a release mechanism by disabling the electrostatic bonding between particle surface and polyelectrolyte ink. Furthermore, the absence of strong attractive forces between divalent particles in water was investigated using XPS measurements. These results lead to the conclusion that the transfer of small PDMS oligomers onto the patch surface is shielding charges, preventing colloidal agglomeration. However, based on this knowledge, further patch modifications for particle self-assembly were introduced including physical approaches using magnetic nano additives, chemical patch functionalization with avidin-biotin or the light responsive cyclodextrin-arylazopyrazoles coupling as well as particle surface modification for the synthesis of highly amphiphilic colloids. The successful coupling, its efficiency, stability and behaviour in different solvents were evaluated to find a suitable coupling system for future assembly experiments. Based on these results the possibility of more sophisticated structures by colloidal self-assembly is given. Certain findings needed further analysis to understand their underlying mechanics, including the relatively broad patch diameter distribution and the decreasing patch thickness for smaller silica particles. Mathematical assumptions for both effects are introduced in chapter 5. First, they demonstrate the connection between the naturally occurring particle size distribution and the broadening of the patch diameter, indicating an even higher precision for this µCP approach. Second, explaining the increase of contact area between particle and ink surface due to higher particle packaging, leading to a decrease in printing pressure for smaller particles. These calculations ultimately lead to the development of a new mechanical microcontact printing approach, using centrifugal forces for high pressure control and excellent parallel alignment of printing substrates. First results with this device and the comparison with previously conducted by-hand experiments conclude this research. It furthermore displays the advantages of such a device for future applications using a mechanical printing approach, especially for accessing even smaller nano particles with great precision and excellent yield. In conclusion, this work demonstrates the successful adjustment of the µCP approach using commercially available and affordable silica particles and polyelectrolytes for high flexibility, reduced costs and higher scale-up value. Furthermore, its was possible to increase the modification potential by introducing three-dimensional patches for additional functionalization volume. While keeping a high colloidal stability, different coupling systems showed the self-assembly capabilities of this toolbox for anisotropic particles. N2 - Diese Forschungsarbeit befasste sich mit der Frage, ob es möglich ist, bekannte Mikrokontaktdruckverfahren, zur Herstellung von anisotropen Bausteinen (Patchy Partikel), weiter zu vereinfachen. Dabei sollten gängige Chemikalien verwendet werden ohne einen Verlust in Reproduzierbarkeit, hoher Präzision und Feineinstellung der Janus-Balance zu erleiden. In Kapitel 2 wurden die verwendeten Mikrokontaktdruckmaterialien sowie deren elektrostatische Wechselwirkungen vorgestellt. Insbesondere handelte es sich dabei um Polydimethylsiloxan Stempel, Silikapartikel und hoch molekulare Polyethylenimin Tinte. All diese Produkte sind kommerziel in großen und bezahlbaren Mengen erhältlich. Nicht nur die Vorteile von polymeren Tinten im Gegensatz zu molekularen Tinten wurde beschrieben, sondern auch die hohe Flexibilität dieses Verfahrens bezüglich der verwendeten Druckkraft. Mit dieser Anpassung des Mikrokontaktdrucks, wurde eine neue Methode der Lösungsmittel unterstützten Partikelablösung ermöglicht, mit deren Hilfe ein einfaches Schalten zwischen zwei dimensionaler Oberflächenfunktionalisierung und drei dimensionalem Strukturdrucks möglich war, ohne Druckparameter oder Startchemikalien zu verändern. Dadurch konnte neu erschaffenes internes Volumen verwendet werden um Nanoadditive einzuführen und so zusätzliche physikalische Eigenschaften zu integrieren, ohne die Oberflächenchemie der Patches verändert wurde. Der Erfolg dieses Systems und seine erreichbaren Grenzen wurde gründlichst in Kapitel 3 erforscht, indem detaillierte Geometrieparameter der Patches einschließlich Durchmesser, Dicke und Ausbeute, erworben wurden. Hierfür wurden Silikapartikel in einem Größenbereich von 1µm bis 5µm mit unterschiedlichen Tintenkonzentrationen bedruckt, um Veränderungen erforschen zu können. Ein notwendiger Luftplasma Ätzschritt für die Produktion von trivalenten Partikeln, mit Hilfe des sogenannten ,,Sandwich‘‘-Drucks, wurde erläutert und vergleichende Untersuchen von einfach und zweifach modifizierten Bausteinen wurden durchgeführt. Zusätzlich dazu, wurde die Verwendung von strukturierten Stempel beschrieben. Die Ergebnisse verdeutlichen die exzellente Genauigkeit dieser Methode und öffnet den Weg um eine hoch höhere Präzision zu erreichen da weitere Parametere genau eingestellt und untersucht werden können, z.B. Luftfeuchtigkeit und Temperature während der Stempelbeladung. Die Performance der herstellten anisotropen Partikel wurde in Kapitel 4 mit Verhaltensstudien in alkoholischen und wässrigen Dispersionen getestet. Dabei wurde die Stabilität der Oberflächenfunktionalisierungen in einem breiten pH Bereich untersucht. Dadurch wurde ein Ablösungsmechanismus bei sehr hohen bzw. niedrigen pH-Werten entdeckt, der zur Deaktivierung elektrostatischer Wechselwirkungen zwischen Partikeloberfläche und Polyelektrolyte Tinte führte. Desweitern wurden die Abwesenheit starker Wechselwirkung der divalenten Partikel in Wasser mit Hilfe von XPS untersucht. Das Resultat zeigte, dass der Transfer kleinster PDMS Oligomere auf die Patchoberfläche zu einer Ladungsabschirmung führte. Dadurch konnte Agglomeration verhindert werden. Aufgrund dieser Ergebnisse wurden weitere Modifikationen für Partikelassemblierung durchgeführt. Hierfür wurde die Einführung von magnetischen Nanoadditiven, die Funktionalisierung mit Avidin-Biotin sowie dem Lichtschaltbaren Cyclodextrin-Arylazopyrazol Komplexen und die Partikeloberflächenfunktionalisierung zur Herstellung amphiphiler Teilchen untersucht. Die Effizienz der Kopplung, deren Stabilität sowie das Verhalten in unterschiedlichen Lösungsmittel wurde beschrieben. Basierend auf diesen Ergebnissen können noch anspruchsvollere Strukturen durch kolloidale Selbstassemblierung erzeugt werden. Einige Ergebnisse dieser Arbeit benötigten zusätzlicher Analyse um die zugrundeliegenden Mechaniken verstehen zu können. Dazu gehörte die relative hohe Streuung des Durchmessers für unterschiedliche Partikelsysteme, sowie das Ausdünnen des Patches mit kleineren Silikapartikeln. Mathematische Modelle in Kapitel 5 beschreiben beide Effekte. Dadurch war es möglich einen Zusammenhang zwischen der natürlichen Partikelgrößenverteilung sowie der Verbreitung des Patchdurchmessers festzustellen. Des Weiteren konnte eine Verkleinerung der Druckkraft durch eine Erhöhung der Packungsdichte für kleine Partikel beschrieben werden, wodurch eine Erklärung der Ausdünnung möglich war. All diese Berechnung führten schlussendlich zur Entwicklung eines neuen mechanischen Mikrokontaktdruckverfahrens, welches mit Hilfe von Zentrifugalkräften eine hohe Druckkontrolle und eine exzellente parallele Ausrichtung zwischen den Substraten ermöglicht. Erste Ergebnisse, sowie deren Vergleich mit bisher erhaltenen Resultaten schließen diese Forschung ab. Des Weiteren zeigt es die Vorteile einer solchen Vorrichtung für kommende Applikationen, besonders um noch kleinere Nanopartikel mit einer hohen Präzision modifizieren zu können. Zusammenfassend ist zu sagen, dass diese Forschung die erfolgreiche Anpassung des Mikrokontaktdruckverfahrens mit kommerziell erhältlichen und bezahlbaren Silikapartikeln und Polyelektrolyten demonstriert, um hohe Flexibilität, reduzierte Kosten und ein erweitertes Skalierungspotential zu bieten. Zusätzlich ist es gelungen, die Funktionalisierungsdichte zu erhöhen, indem drei dimensionaler Strukturdruck bisher ungenutztes Volumen schaffen konnte. Während eine hohe kolloidale Stabilität erhalten blieb, ist es gelungen unterschiedliche Kopplungssysteme zu nutzen, um das Selbstorganisationspotential dieser Toolbox für anisotrope Partikel aufzuzeigen. KW - patchy particles KW - microcontact printing KW - silica particles KW - anisotropic colloids KW - polyelectrolytes KW - Patchy Partikel KW - Mikrokontaktdruck KW - Silika Partikel KW - Anisotrope Kolloide KW - Polyelektrolyte Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-427731 ER - TY - THES A1 - Kiel, Mareike T1 - Static and ultrafast optical properties of nanolayered composites : gold nanoparticles embedded in polyelectrolytes T1 - Statische und ultraschnelle optische Eigenschaften von nanogeschichteten Kompositmaterialien. Gold-Nanopartikel in Polyelektrolytschichten. N2 - In the course of this thesis gold nanoparticle/polyelectrolyte multilayer structures were prepared, characterized, and investigated according to their static and ultrafast optical properties. Using the dip-coating or spin-coating layer-by-layer deposition method, gold-nanoparticle layers were embedded in a polyelectrolyte environment with high structural perfection. Typical structures exhibit four repetition units, each consisting of one gold-particle layer and ten double layers of polyelectrolyte (cationic+anionic polyelectrolyte). The structures were characterized by X-ray reflectivity measurements, which reveal Bragg peaks up to the seventh order, evidencing the high stratication of the particle layers. In the same measurements pronounced Kiessig fringes were observed, which indicate a low global roughness of the samples. Atomic force microscopy (AFM) images veried this low roughness, which results from the high smoothing capabilities of polyelectrolyte layers. This smoothing effect facilitates the fabrication of stratified nanoparticle/polyelectrolyte multilayer structures, which were nicely illustrated in a transmission electron microscopy image. The samples' optical properties were investigated by static spectroscopic measurements in the visible and UV range. The measurements revealed a frequency shift of the reflectance and of the plasmon absorption band, depending on the thickness of the polyelectrolyte layers that cover a nanoparticle layer. When the covering layer becomes thicker than the particle interaction range, the absorption spectrum becomes independent of the polymer thickness. However, the reflectance spectrum continues shifting to lower frequencies (even for large thicknesses). The range of plasmon interaction was determined to be in the order of the particle diameter for 10 nm, 20 nm, and 150 nm particles. The transient broadband complex dielectric function of a multilayer structure was determined experimentally by ultrafast pump-probe spectroscopy. This was achieved by simultaneous measurements of the changes in the reflectance and transmittance of the excited sample over a broad spectral range. The changes in the real and imaginary parts of the dielectric function were directly deduced from the measured data by using a recursive formalism based on the Fresnel equations. This method can be applied to a broad range of nanoparticle systems where experimental data on the transient dielectric response are rare. This complete experimental approach serves as a test ground for modeling the dielectric function of a nanoparticle compound structure upon laser excitation. N2 - Im Rahmen dieser Arbeit wurden Gold-Nanopartikel/Polyelektrolyt Multischichtstrukturen hergestellt, strukturell charakterisiert und bezüglich ihrer optischen Eigenschaften sowohl statisch als auch zeitaufgelöst analysiert. Die Strukturen wurden mithilfe der Dip-coating oder der Spin-coating Methode hergestellt. Beide Methoden ermöglichen das Einbetten einzelner Partikellagen in eine Polyelektrolytumgebung. Typische Strukturen in dieser Arbeit bestehen aus vier Wiederholeinheiten, wobei jede aus einer Nanopartikelschicht und zehn Polyelektrolyt-Doppellagen (kationisches und anionisches Polyelektrolyt) zusammengesetzt ist. Die Stratizierung der Gold-Nanopartikellagen wurde mittels Röntgenreflektometrie-Messungen im Kleinwinkelbereich nachgewiesen, welche Bragg Reflexionen bis zur siebten Ordnung aufzeigen. Das ausgeprägte Kiessig Interferenzmuster dieser Messungen weist zudem auf eine geringe globale Rauheit hin, die durch Oberflächenanalysen mit einem Rasterkraftmikroskop bestätigt werden konnte. Diese geringe Rauheit resultiert aus den glättenden Eigenschaften der Polyelektrolyte, die die Herstellung von Multilagensystemen mit mehreren Partikellagen erst ermöglichen. Die Aufnahme eines Transmissionselektronenmikroskops veranschaulicht eindrucksvoll die Anordnung der Partikel in einzelne Schichten. Durch photospektroskopische Messungen wurden die optischen Eigenschaften der Strukturen im UV- und sichtbaren Bereich untersucht. Beispielsweise wird eine Verschiebung und Verstärkung der Plasmonenresonanz beobachtet, wenn eine Goldnanopartikellage mit transparenten Polyelektrolyten beschichtet wird. Erst wenn die bedeckende Schicht dicker als die Reichweite der Plasmonen wird, bleibt die Absorption konstant. Die spektrale Reflektivität jedoch ändert sich auch mit jeder weiteren adsorbierten Polyelektrolytschicht. Die Reichweite der Plasmonenresonanz konnte auf diese Art für Partikel der Größe 10 nm, 20 nm und 150 nm bestimmt werden. Die Ergebnisse wurden im Kontext einer Effektiven Mediums Theorie diskutiert. Die komplexe dielektrische Funktion einer Multilagenstruktur wurde zeitabhängig nach Laserpulsanregung für einen breiten spektralen Bereich bestimmt. Dazu wurden zuerst die Änderungen der Reflektivität und Transmittivität simultan mittels der Pump-Probe (Anrege-Abtast) Spektroskopie gemessen. Anschließend wurden aus diesen Daten, mithilfe eines Formalismus, der auf den Fresnelschen Formeln basiert, die Änderungen im Real- und Imaginärteil der dielektrischen Funktion ermittelt. Diese Methode eignet sich zur Bestimmung der transienten dielektrischen Funktion einer Vielzahl von Nanopartikelsystemen. Der rein experimentelle Ansatz ermöglicht es, effektive Medien Theorien und Simulationen der dielektrischen Funktion nach Laserpulsanregung zu überprüfen. KW - Nanopartikel KW - Polyelektrolyte KW - Dielektrische Funktion KW - Anrege-Abtast Spektroskopie KW - nanoparticles KW - polyelectrolytes KW - dielectric function KW - pump-probe spectroscopy Y1 - 2012 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-61823 ER - TY - THES A1 - Haase, Martin F. T1 - Modification of nanoparticle surfaces for emulsion stabilization and encapsulation of active molecules for anti-corrosive coatings T1 - Nanopartikel Oberflächenmodifikationen zur Emulsionsstabilisierung und Verkapselung von Wirkstoffen für Antikorrosionsbeschichtungen N2 - Within this work, three physicochemical methods for the hydrophobization of initially hydrophilic solid particles are investigated. The modified particles are then used for the stabilization of oil-in-water (o/w) emulsions. For all introduced methods electrostatic interactions between strongly or weakly charged groups in the system are es-sential. (i) Short chain alkylammonium bromides (C4 – C12) adsorb on oppositely charged solid particles. Macroscopic contact angle measurements of water droplets under air and hexane on flat silica surfaces in dependency of the surface charge density and alkylchain-length allow the calculation of the surface energy and give insights into the emulsification properties of solid particles modified with alkyltrimethylammonium bromides. The measure-ments show an increase of the contact angle with increasing surface charge density, due to the enhanced adsorp-tion of the oppositely charged alkylammonium bromides. Contact angles are higher for longer alkylchain lengths. The surface energy calculations show that in particular the surface-hexane or surface-air interfacial en-ergy is being lowered upon alkylammonium adsorption, while a significant increase of the surface-water interfa-cial energy occurs only at long alkyl chain lengths and high surface charge densities. (ii) The thickness and the charge density of an adsorbed weak polyelectrolyte layer (e.g. PMAA, PAH) influence the wettability of nanoparticles (e.g. alumina, silica, see Scheme 1(b)). Furthermore, the isoelectric point and the pH range of colloidal stability of particle-polyelectrolyte composites depend on the thickness of the weak polye-lectrolyte layer. Silica nanoparticles with adsorbed PAH and alumina nanoparticles with adsorbed PMAA be-come interfacially active and thus able to stabilize o/w emulsions when the degree of dissociation of the polye-lectrolyte layer is below 80 %. The average droplet size after emulsification of dodecane in water depends on the thickness and the degree of dissociation of the adsorbed PE-layer. The visualization of the particle-stabilized o/w emulsions by cryogenic SEM shows that for colloidally stable alumina-PMAA composites the oil-water interface is covered with a closely packed monolayer of particles, while for the colloidally unstable case closely packed aggregated particles deposit on the interface. (iii) By emulsifying a mixture of the corrosion inhibitor 8-hydroxyquinoline (8-HQ) and styrene with silica nanoparticles a highly stable o/w emulsion can be obtained in a narrow pH window. The amphoteric character of 8-HQ enables a pH dependent electrostatic interaction with silica nanoparticles, which can render them interfa-cially active. Depending on the concentration and the degree of dissociation of 8-HQ the adsorption onto silica results from electrostatic or aromatic interactions between 8-HQ and the particle-surface. At intermediate amounts of adsorbed 8-HQ the oil wettability of the particles becomes sufficient for stabilizing o/w emulsions. Cryogenic SEM visualization shows that the particles arrange then in a closely packed shell consisting of partly of aggregated domains on the droplet interface. For further increasing amounts of adsorbed 8-HQ the oil wet-tability is reduced again and the particles ability to stabilize emulsions decreases. By the addition of hexadecane to the oil phase the size of the droplets can be reduced down to 200 nm by in-creasing the silica mass fraction. Subsequent polymerization produces corrosion inhibitor filled (20 wt-%) poly-styrene-silica composite particles. The measurement of the release of 8-hydroxyquinoline shows a rapid increase of 8-hydroxyquinoline in a stirred aqueous solution indicating the release of the total content in less than 5 min-utes. The method is extended for the encapsulation of other organic corrosion inhibitors. The silica-polymer-inhibitor composite particles are then dispersed in a water based alkyd emulsion, and the dispersion is used to coat flat aluminium substrates. After drying and cross-linking the polmer-film Confocal Laser Scanning Micros-copy is employed revealing a homogeneous distribution of the particles in the film. Electrochemical Impedance Spectroscopy in aqueous electrolyte solutions shows that films with aggregated particle domains degrade with time and don’t provide long-term corrosion protection of the substrate. However, films with highly dispersed particles have high barrier properties for corrosive species. The comparison of films containing silica-polystyrene composite particles with and without 8-hydroxyquinoline shows higher electrochemical impedances when the inhibitor is present in the film. By applying the Scanning Vibrating Electrode Technique the localized corrosion rate in the fractured area of scratched polymer films containing the silica-polymer-inhibitor composite particles is studied. Electrochemical corrosion cannot be suppressed but the rate is lowered when inhibitor filled composite particles are present in the film. By depositing six polyelectrolyte layers on particle stabilized emulsion droplets their surface morphology changes significantly as shown by SEM visualization. When the oil wettability of the outer polyelectrolyte layer increases, the polyelectrolyte coated droplets can act as emulsion stabilizers themselves by attaching onto bigger oil droplets in a closely packed arrangement. In the presence of 3 mM LaCl3 8-HQ hydrophobized silica particles aggregate strongly on the oil-water inter-face. The application of an ultrasonic field can remove two dimensional shell-compartments from the droplet surface, which are then found in the aqueous bulk phase. Their size ranges up to 1/4th of the spherical particle shell. N2 - Im Rahmen dieser Arbeit wurden drei Oberflächenmodifikationen zur Hydrophobierung von ursprünglich hydrophilen Feststoffpartikeln entwickelt. Die so modifizierten Partikel werden dann zur Stabilisierung von Öl-in-Wasser Emulsionen verwendet. Für sämtliche entwickelte Methoden sind elektrostatische Wechselwirkungen zwischen stark oder schwach dissoziierten chemischen Gruppen essentiell. (i) Kurzkettige Alkyltrimethylammonium Bromide (C4-C12) adsorbieren auf entgegengesetzt geladenen Partikeln. Makroskopische Kontaktwinkelmessungen von Wasser Tropfen in Luft und Hexan auf flachen Siliziumoxid Oberflächen mit variabler Oberflächenladungsdichte und Alkylkettenlänge ermöglichen die Berechnung der Oberflächenenergie und geben Einblicke in die Emulgationseigenschaften von so modifizierten Feststoffpartikeln. Die Messungen zeigen einen Anstieg des Kontakwinkels mit steigender Oberflächenladungsdichte, bedingt durch die verstärkte Adsorption von entgegengesetzt geladenen Alkyltrimethylammonium Bromiden. Die Kontaktwinkel sind zudem größer für längerkettige Alkyltrimethylammonium Bromide. Die Berechnungen der Oberflächenenergie zeigen, dass besonders die Feststoff-Hexan oder Feststoff-Luft Grenzflächenenergie durch die Adsorption verringert wird, wohingegen die Feststoff-Wasser Oberflächenenergie nur bei längeren Alkylkettenlängen und hohen Oberflächenladungsdichten signifikant ansteigt. (ii) Die Schichtdicke und Ladungsdichte von adsorbierten schwachen Polyelektrolyten (z.B. PMAA, PAH) beeinflusst die Benetzbarkeit von Nanopartikeln (z.B. Aluminiumoxid, Siliziumoxid). Der isoelektrische Punkt und der pH Bereich für kolloidale Stabilität solcher Polyelektrolyt modifizierter Partikel hängt von der Dicke der Polyelektrolytschicht ab. Siliziumoxid und Aluminiumoxid Nanopartikel mit adsorbierten PAH bzw. PMAA werden Grenzflächenaktiv und dadurch befähigt Öl-in-Wasser Emulsionen zu stabilisieren, wenn der Dissoziationsgrad der Polyelektrolytschicht geringer als 80 % ist. Die durchschnittliche Tropfengröße von Dodecan-in-Wasser Emulsionen ist abhängig von der Polyelektrolytschichtdicke und dem Dissoziationsgrad. Die Visualisierung von Partikel stabilisierten Öl-in-Wasser Emulsionen durch kryogene REM zeigt, dass im Falle von kolloidal stabilen Aluminiumoxid-PMAA Partikeln die Öl-Tröpfchen mit einer dichtgepackten Partikelhülle belegt sind, während für kolloidal destabilisierte Partikel eine Hülle aus aggregierten Partikeln gefunden wird. (iii) Durch das Emulgieren einer Lösung des Korrosionsinhibitors 8-Hydroxychinolins (8HQ) in Styrol mit Siliziumoxid Nanopartikeln können stabile Öl-in-Wasser Emulsionen in einem pH Fenster von 4 - 6 hergestellt werden. Der amphoterische Charakter von 8HQ ermöglicht eine pH abhängige elektrostatische Wechselwirkung mit den Siliziumdioxid Nanopartikeln, welche diese Grenzflächenaktiv werden lässt. In Abhängigkeit der Konzentration und des Dissoziationsgrads von 8HQ folgt die Adsorption auf Siliziumdioxid aus elektrostatischen oder aromatischen Wechselwirkungen zwischen 8HQ und der Partikeloberfläche. Bei mittleren adsorbierten Mengen wird die Öl Benetzbarkeit der Partikel ausreichend erhöht um Öl-in-Wasser Emulsionen zu stabilisieren. Kryogene REM zeigt, dass die Partikel dann in dicht gepackte Hüllen, mit teilweise aggregierten Domänen auf der Öltröpfchenoberfläche vorliegen. Durch weiter ansteigende adsorbierte 8HQ Mengen wird die Öl-Benetzbarkeit wieder zurückgesetzt und die Emulgationsfähigkeit der Partikel aufgehoben. Durch die Zugabe von Hexadecan zur Öl Phase kann die Tropfengröße durch Erhöhung des Siliziumdioxid Anteils auf 200 nm herabgesetzt werden. Anschließende Polymerisation des Styrols generiert Korrosionsinhibitor gefüllte (20 Gew-%) Polystyrol-Silizumoxid Komposite. Die Messung der Freisetzungsrate von 8HQ zeigt einen schnellen Anstieg der 8HQ Konzentration in einer gerührten wässrigen Lösung innerhalb von 5 Minuten. Die Verkapselungsmethode wird auch für andere organische Korrosionsinhibitoren erweitert. Die Komposite werden dann in einer wasserbasierten Alkydpräpolymeremulsion dispergiert und diese Mischung wird zur Beschichtung von flachen Aluminiumplatten genutzt. Nach Trocknung und Quervernetzung des Films wird Konfokale Laser Mikroskopie dazu verwendet um die räumliche Verteilung der Composite im Film zu visualisieren. Elektrochemische Impedanzspektroskopie zeigt, dass die Barriereeigenschaften des Films durch die Anwesenheit der Komposite verbessert sind. Raster Vibrationselektroden Messungen zeigen, dass die Korrosionsrate in einem Kratzer des Films durch die Anwesenheit der Inhibitor efüllten Komposite reduziert ist. Durch die Ablagerung von 6 Polyelektroytschichten auf Feststoffstabilisierten Emulsionströpfchen verändert sich deren Oberflächenmorphologie deutlich (gezeigt durch REM). Wenn die Ölbenetzbarkeit der äußeren Polyelektrolytschicht ansteigt, dann können solche Polyelektolytbeschichteten Feststoffstabilisierte Emulsionströpfchen selber als Emulsionsstabilisatoren verwendet werden. Diese lagern sich dann in einer dicht gepackten Schicht auf der Oberfläche von größeren Emulsionstropfen ab. In der Gegenwart von 3 mM LaCl3 aggregieren 8HQ modifizierte Siliziumoxid Partikel stark auf der Öl-Wasser Grenzfläche. Der Einsatz von Ultraschall kann aggregierte Schalenbestandteile von der Tropfenoberfläche wegreißen. Diese Wracks können bis zu einem Viertel der Kugelhülle ausmachen und liegen dann als kolloidale Schalen im Wasser vor. KW - Nanopartikel KW - Emulsionen KW - Polyelektrolyte KW - Korrosion KW - Adsorption KW - nanoparticles KW - emulsions KW - polyelectrolytes KW - corrosion KW - adsorption Y1 - 2011 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus-55413 ER - TY - THES A1 - Erbe, Andreas T1 - Ellipsometrische Lichtstreuung als neue Methode zur Charakterisierung der Grenzfläche von Kolloiden N2 - Die ellipsometrische Lichtstreuung wird als eine neue, leistungsfähige Methode zur Charakterisierung von Schichten um kolloidale Partikel vorgestellt. Theoretische Grundlage der Methode ist die Mie-Theorie der Lichtstreuung. Experimentell wurde die Polarisationsoptik eines Null-Ellipsometers in den Strahlengang eines Lichtstreuaufbaus eingebaut. Wie in der Reflexionsellipsometrie um den Brewsterwinkel herum erhält man in der ellipsometrischen Streuung einen Winkelbereich, in dem die Methode empfindlich auf Schichten an der Oberfläche der Partikel ist. An verschiedenen Systemen wurde die Tauglichkeit der ellipsometrischen Streuung zur Charakterisierung von Schichten auf Partikeln demonstriert. So wurden Dicke und Brechungsindex einer thermosensitiven Schicht von Poly(N-isopropylacrylamid) auf einem Poly(methylmethacrylat)-Kern bestimmt. Damit ist es möglich, experimentell den Schichtbrechungsindex und damit den Quellungsgrad zu bestimmen. Des Weiteren wurde der Einfluss der NaCl-Konzentration auf die Polyelektrolythülle von Poly(methylmethacrylat)-Poly(styrolsulfonat)-Blockcopolymer-Partikeln untersucht. Die Polyelektrolytketten liegen im hier untersuchten Beispiel nicht gestreckt vor. Als drittes wurde die Verteilung von niedermolekularen Ionen um elektrostatisch stabilisierte Poly(styrol)-Latexpartikel in Wasser untersucht. Hier wurde gezeigt, dass die beobachteten Schichtdicken und Schichtbrechungsindizes viel größer sind, als nach der klassischen Poisson-Boltzmann-Theorie zu erwarten ist. Des Weiteren wurde die Doppelbrechung von unilamellaren Lipidvesikeln bestimmt. Außerdem wurden Messungen der dynamische Lichtstreuung im Intensitätsminimum der Ellipsometrie durchgeführt. Dabei wird ein Prozess mit einer Korrelationszeit, die unabhängig vom Streuvektor, aber abhängig von der verwendeten Wellenlänge ist, sichtbar. Die Natur dieses Prozesses konnte hier nicht vollständig geklärt werden. N2 - Ellipsometric light scattering is introduced as a new and powerful technique to characterize layers on colloidal particles. For the experiments, the polarization optics used reflection ellipsometry was installed in the beam of a light scattering setup. Using the priciples of null ellipsometry, a small range of scattering angles is obtained, were the method is sensitive to layers on the surface of colloidal particles. This is an analogy to the layer sensitivity of reflection ellipsometry at planer interfaces close to the Brewster angle. The theoretical basis for ellipsometric scattering is the Mie theory with its modern supplements. The feasibility of characterizing layers on colloidal particles was demonstrated with several systems. First, layer thickness and layer refractive index of poly(N-isopropylacrylamide) layers on a poly(methylmethacrylate) core were determined. This was the first time that the refractive index and with that the degree of swelling of a layer was directly determined in an scattering experiment. Second, polyelectrolyte layers on Poly(methylmethacrylate)-Poly(styrenesulfonate)-blockcopolymer particles were characterized. The influence of the salt concentration on the parameters of the layer was determined. The results show that the polyelectrolyte chains in the system investigated are not streched. Third, layers of ions around electrostatically-stabilized poly(styrene) particles were characterized. The layer thickness and layer refractive index in these examples are shown to be much larger than predicted by the classical Poisson-Boltzmann-theory. In addition, the birefringence of lipid vesicles was determined. Another interesting application of the ellipsometric scattering is the dynamic light scattering with ellipsometric optics. Its results show a characteristic process with a correlation time independent of the scattering vector, but wavelength dependent. The origin of this mode is not yet completely clarified. T2 - Ellipsometrische Lichtstreuung als neue Methode zur Charakterisierung der Grenzfläche von Kolloiden KW - Ellipsometrie KW - Lichtstreuung KW - Grenzfläche KW - Kolloide KW - Ionenverteilung KW - Lipide KW - Polyelektrolyte KW - ellipsometry KW - light scattering KW - interface KW - colloids KW - ion distribution KW - lipids KW - polyelectrolytes Y1 - 2004 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-0001565 ER - TY - THES A1 - Uyaver, Sahin T1 - Simulation of annealed polyelectrolytes in poor solvents N2 - Polymere sind lange kettenartige Moleküle. Sie bestehen aus vielen elementaren chemischen Einheiten, den Monomeren, die durch kovalente Bindungen aneinander gekettet sind. Polyelektrolyte sind Polymere, die ionisierbare Monomeren enthalten. Aufgrund ihrer speziellen Eigenschaften sind Polyelektrolyte sowohl in der Molekular- und Zellbiologie von großen Bedeutung als auch in der Chemie großtechnisch relevant. Verglichen mit ungeladenen Polymeren sind Polyelektrolyte theoretisch noch wenig verstanden. Insbesondere gilt dies für Polyelektrolyte in sogenanntem schlechten Lösungsmittel. Ein schlechtes Lösungsmittel bewirkt eine effektive Anziehung zwischen den Monomeren. Für Polyelektrolyte in schlechtem Lösungsmittel kommt es daher zu einer Konkurrenz zwischen dieser Anziehung und der elektrostatischen Abstoßung. Geladene Polymere werden im Rahmen der chemischen Klassifikation in starke und schwache Polyelektrolyte unterschieden. Erstere zeigen vollständige Dissoziation unabhängig vom pH-Wert der Lösung. Die Position der Ladungen auf der Kette wird ausschließlich während der Polymersynthese festgelegt. In der Physik spricht man deshalb von Polyelektrolyten mit eingefrorener Ladungsverteilung (quenched polyelectrolytes). Im Falle von schwachen Polyelektrolyten ist die Ladungsdichte auf der Kette nicht konstant, sondern wird durch der pH-Wert der Lösung kontrolliert. Durch Rekombinations- und Dissoziationsprozesse sind die Ladungen auf der Kette beweglich. Im allgemeinen stellt sich eine inhomogene Gleichgewichtsverteilung ein, die mit der Struktur der Kette gekoppelt ist. Diese Polymere werden deshalb auch Polyelektrolyte mit Gleichgewichtsladungsverteilung (annealed polyelectrolytes) genannt. Wegen des zusätzlichen Freiheitsgrades in der Ladungsverteilung werden eine Reihe ungewöhnlicher Eigenschaften theoretisch vorhergesagt. Mit Hilfe von Simulationen ist es zum ersten Mal gelungen, zu zeigen daß 'annealed' Polyelektrolyte in relativ schlechtem Lösungsmittel einen diskontinuierlichen Phasenübergang durchlaufen, wenn ein kritischer pH-Werts der Lösung überschritten wird. Bei diesem Phasenübergang, gehen die Polyelektolyte von einer schwach geladenen kompakten globulären Struktur zu einer stark geladenen gestreckten Konfiguration über. Aufgrund theoretischer Vorhersagen wird erwartet, daß die globuläre Struktur in weniger schlechtem Lösungsmittel instabil wird und sich eine Perlenkettenkonfiguration ausbildet. Diese Vorhersage konnte für 'annealed' Polyelektrolyte mit den durchgeführten Simulationen zum ersten Mal bestätigt werden - inzwischen auch durch erste experimentelle Ergebnisse. Schließlich zeigen die Simulationen auch, daß annealed Polyelektrolyte bei einer kritischen Salzkonzentration in der Lösung einen scharfen Übergang zwischen einem stark geladenen gestreckten Zustand und einem schwach geladenen globulären Zustand aufweisen, wiederum in Übereinstimmung mit theoretischen Erwartungen. N2 - A polymer is a large molecule made up of many elementary chemical units, joined together by covalent bonds (for example, polyethylene). Polyelectrolytes (PELs) are polymer chains containing a certain amount of ionizable monomers. With their specific properties PELs acquire big importance in molecular and cell biology as well as in technology. Compared to neutral polymers the theory of PELs is less understood. In particular, this is valid for PELs in poor solvents. A poor solvent environment causes an effective attraction between monomers. Hence, for PELs in a poor solvent, there occurs a competition between attraction and repulsion. Strong or quenched PELs are completely dissociated at any accessible pH. The position of charges along the chain is fixed by chemical synthesis. On the other hand, in weak or annealed PELs dissociation of charges depends on solution pH. For the first time the simulation results have given direct evidence that at rather poor solvents an annealed PEL indeed undergoes a first-order phase transition when the chemical potential (solution pH) reaches at a certain value. The discontinuous transition occurs between a weakly charged compact globular structure and a strongly charged stretched configuration. At not too poor solvents theory predicts that globule would become unstable with respect to the formation of pearl-necklaces. The results show that pearl-necklaces exist in annealed PELs indeed. Furthermore, as predicted by theory, the simulation results have shown that annealed PELs display a sharp transition from a highly charged stretched state to a weakly charged globule at a critical salt concentration. KW - Polymer-Plastik KW - Polyelektrolyte KW - Simulation KW - polymer KW - polyelectrolytes KW - simulation Y1 - 2004 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-0001488 ER -