TY - JOUR A1 - Niebuur, Bart-Jan A1 - Puchmayr, Jonas A1 - Herold, Christian A1 - Kreuzer, Lucas A1 - Hildebrand, Viet A1 - Müller-Buschbaum, Peter A1 - Laschewsky, Andre A1 - Papadakis, Christine M. T1 - Polysulfobetaines in aqueous solution and in thin film geometry JF - Materials N2 - Polysulfobetaines in aqueous solution show upper critical solution temperature (UCST) behavior. We investigate here the representative of this class of materials, poly (N,N-dimethyl-N-(3-methacrylamidopropyl) ammonio propane sulfonate) (PSPP), with respect to: (i) the dynamics in aqueous solution above the cloud point as function of NaBr concentration; and (ii) the swelling behavior of thin films in water vapor as function of the initial film thickness. For PSPP solutions with a concentration of 5 wt.%, the temperature dependence of the intensity autocorrelation functions is measured with dynamic light scattering as function of molar mass and NaBr concentration (0-8 mM). We found a scaling of behavior for the scattered intensity and dynamic correlation length. The resulting spinodal temperatures showed a maximum at a certain (small) NaBr concentration, which is similar to the behavior of the cloud points measured previously by turbidimetry. The critical exponent of susceptibility depends on NaBr concentration, with a minimum value where the spinodal temperature is maximum and a trend towards the mean-field value of unity with increasing NaBr concentration. In contrast, the critical exponent of the correlation length does not depend on NaBr concentration and is lower than the value of 0.5 predicted by mean-field theory. For PSPP thin films, the swelling behavior was found to depend on film thickness. A film thickness of about 100 nm turns out to be the optimum thickness needed to obtain fast hydration with H2O. KW - polyzwitterions KW - polysulfobetaines KW - dynamic light scattering KW - phase behavior Y1 - 2018 U6 - https://doi.org/10.3390/ma11050850 SN - 1996-1944 VL - 11 IS - 5 PB - MDPI CY - Basel ER - TY - JOUR A1 - Schönemann, Eric A1 - Laschewsky, Andre A1 - Rosenhahn, Axel T1 - Exploring the long-term hydrolytic behavior of zwitterionic polymethacrylates and polymethacrylamides JF - Polymers N2 - The hydrolytic stability of polymers to be used for coatings in aqueous environments, for example, to confer anti-fouling properties, is crucial. However, long-term exposure studies on such polymers are virtually missing. In this context, we synthesized a set of nine polymers that are typically used for low-fouling coatings, comprising the well-established poly(oligoethylene glycol methylether methacrylate), poly(3-(N-2-methacryloylethyl-N,N-dimethyl) ammoniopropanesulfonate) (sulfobetaine methacrylate), and poly(3-(N-3-methacryamidopropyl-N,N-dimethyl)ammoniopropanesulfonate) (sulfobetaine methacrylamide) as well as a series of hitherto rarely studied polysulfabetaines, which had been suggested to be particularly hydrolysis-stable. Hydrolysis resistance upon extended storage in aqueous solution is followed by H-1 NMR at ambient temperature in various pH regimes. Whereas the monomers suffered slow (in PBS) to very fast hydrolysis (in 1 M NaOH), the polymers, including the polymethacrylates, proved to be highly stable. No degradation of the carboxyl ester or amide was observed after one year in PBS, 1 M HCl, or in sodium carbonate buffer of pH 10. This demonstrates their basic suitability for anti-fouling applications. Poly(sulfobetaine methacrylamide) proved even to be stable for one year in 1 M NaOH without any signs of degradation. The stability is ascribed to a steric shielding effect. The hemisulfate group in the polysulfabetaines, however, was found to be partially labile. KW - polyzwitterions KW - stability KW - polymer degradation KW - hydrolysis KW - polysulfobetaine KW - polysulfabetaine KW - anti-fouling materials Y1 - 2018 U6 - https://doi.org/10.3390/polym10060639 SN - 2073-4360 VL - 10 IS - 6 PB - MDPI CY - Basel ER - TY - JOUR A1 - Nizardo, Noverra M. A1 - Schanzenbach, Dirk A1 - Schönemann, Eric A1 - Laschewsky, Andre T1 - Exploring poly(ethylene glycol)-polyzwitterion diblock copolymers as biocompatible smart macrosurfactants featuring UCST-phase behavior in normal saline solution JF - Polymers N2 - Nonionic-zwitterionic diblock copolymers are designed to feature a coil-to-globule collapse transition with an upper critical solution temperature (UCST) in aqueous media, including physiological saline solution. The block copolymers that combine presumably highly biocompatible blocks are synthesized by chain extension of a poly(ethylene glycol) (PEG) macroinitiator via atom transfer radical polymerization (ATRP) of sulfobetaine and sulfabetaine methacrylates. Their thermoresponsive behavior is studied by variable temperature turbidimetry and H-1 NMR spectroscopy. While the polymers with polysulfobetaine blocks exhibit phase transitions in the physiologically interesting window of 30-50 degrees C only in pure aqueous solution, the polymers bearing polysulfabetaine blocks enabled phase transitions only in physiological saline solution. By copolymerizing a pair of structurally closely related sulfo-and sulfabetaine monomers, thermoresponsive behavior can be implemented in aqueous solutions of both low and high salinity. Surprisingly, the presence of the PEG blocks can affect the UCST-transitions of the polyzwitterions notably. In specific cases, this results in "schizophrenic" thermoresponsive behavior displaying simultaneously an UCST and an LCST (lower critical solution temperature) transition. Exploratory experiments on the UCST-transition triggered the encapsulation and release of various solvatochromic fluorescent dyes as model "cargos" failed, apparently due to the poor affinity even of charged organic compounds to the collapsed state of the polyzwitterions. KW - block copolymer KW - amphiphile KW - macrosurfactant KW - thermoresponsive self-assembly KW - polyzwitterion KW - upper critical solution temperature (UCST) KW - salting-in Y1 - 2018 U6 - https://doi.org/10.3390/polym10030325 SN - 2073-4360 VL - 10 IS - 3 PB - MDPI CY - Basel ER - TY - JOUR A1 - Zhong, Qi A1 - Mi, Lei A1 - Metwalli, Ezzeldin A1 - Biessmann, Lorenz A1 - Philipp, Martine A1 - Miasnikova, Anna A1 - Laschewsky, Andre A1 - Papadakis, Christine M. A1 - Cubitt, Robert A1 - Schwartzkopf, Matthias A1 - Roth, Stephan V. A1 - Wang, Jiping A1 - Müller-Buschbaum, Peter T1 - Effect of chain architecture on the swelling and thermal response of star-shaped thermo-responsive (poly(methoxy diethylene glycol acrylate)-block-polystyrene)(3) block copolymer films JF - Soft matter N2 - The effect of chain architecture on the swelling and thermal response of thin films obtained from an amphiphilic three-arm star-shaped thermo-responsive block copolymer poly(methoxy diethylene glycol acrylate)-block-polystyrene ((PMDEGA-b-PS)(3)) is investigated by in situ neutron reflectivity (NR) measurements. The PMDEGA and PS blocks are micro-phase separated with randomly distributed PS nanodomains. The (PMDEGA-b-PS)(3) films show a transition temperature (TT) at 33 degrees C in white light interferometry. The swelling capability of the (PMDEGA-b-PS)(3) films in a D2O vapor atmosphere is better than that of films from linear PS-b-PMDEGA-b-PS triblock copolymers, which can be attributed to the hydrophilic end groups and limited size of the PS blocks in (PMDEGA-b-PS)(3). However, the swelling kinetics of the as-prepared (PMDEGA-b-PS)(3) films and the response of the swollen film to a temperature change above the TT are significantly slower than that in the PS-b-PMDEGA-b-PS films, which may be related to the conformation restriction by the star-shape. Unlike in the PS-b-PMDEGA-b-PS films, the amount of residual D2O in the collapsed (PMDEGA-b-PS)(3) films depends on the final temperature. It decreases from (9.7 +/- 0.3)% to (7.0 +/- 0.3)% or (6.0 +/- 0.3)% when the final temperatures are set to 35 degrees C, 45 degrees C and 50 degrees C, respectively. This temperature-dependent reduction of embedded D2O originates from the hindrance of chain conformation from the star-shaped chain architecture. Y1 - 2018 U6 - https://doi.org/10.1039/c8sm00965a SN - 1744-683X SN - 1744-6848 VL - 14 IS - 31 SP - 6582 EP - 6594 PB - Royal Society of Chemistry CY - Cambridge ER - TY - JOUR A1 - Vishnevetskaya, Natalya S. A1 - Hildebrand, Viet A1 - Dyakonova, Margarita A. A1 - Niebuur, Bart-Jan A1 - Kyriakos, Konstantinos A1 - Raftopoulos, Konstantinos N. A1 - Di, Zhenyu A1 - Müller-Buschbaum, Peter A1 - Laschewsky, Andre A1 - Papadakis, Christine M. T1 - Dual orthogonal switching of the "Schizophrenic" self-assembly of diblock copolymers JF - Macromolecules : a publication of the American Chemical Society N2 - Based on diblock copolymers, a pair of "schizophrenic" micellar systems is designed by combining a nonionic and thermoresponsive block with a zwitterionic block, which is thermoresponsive and salt-sensitive. The nonionic block is poly(N-isopropylacrylamide) (PNIPAM) or poly(N-isopropylmethacrylamide) (PNIPMAM) and exhibits a lower critical solution temperature (LCST) behavior in aqueous solution. The zwitterionic block is a polysulfobetaine, i.e., poly(4((3-methacrylamidopropyl)dimethylammonio)butane-1-sulfonate) (PSBP), and has an upper critical solution temperature (UCST) behavior with the clearing point decreasing with increasing salt concentration. The PSBP-b-PNIPAM and PSBP-b-PNIPMAM diblock copolymers are prepared by successive reversible addition-fragmentation chain transfer (RAFT) polymerizations. The PSBP block is chosen such that the clearing point of the homopolymer is significantly higher in pure water than the cloud point of PNIPAM or PNIPMAM. Using turbidimetry, H-1 NMR, and small-angle neutron scattering, we investigate the overall phase behavior as well as the structure and interaction between the micelles and the intermediate phase, both in salt-free D2O and in 0.004 M NaBr in D2O in a wide temperature range. We find that PSBP-b-PNIPAM at 50 g L-1 in salt-free D2O is turbid in the entire temperature range. It forms spherical micelles below the cloud point of PNIPAM and cylindrical micelles above. Similar behavior is observed for PSBP-b-PNIPMAM at 50 g L-1 in salt-free D2O with a slight and smooth increase of the light transmission below the cloud point of PNIPMAM and an abrupt decrease above. Upon addition of 0.004 M NaBr, the UCST-type cloud point of the PSBP-block is notably decreased, and an intermediate regime is encountered below the cloud point of PNIPMAM, where the light transmission is slightly enhanced. In this regime, the polymer solution exhibits behavior typical for polyelectrolyte solutions. Thus, double thermosensitive and salt-sensitive behavior with "schizophrenic" micelle formation is found, and the width of the intermediate regime, where both blocks are hydrophilic, can be tuned by the addition of electrolyte. Y1 - 2018 U6 - https://doi.org/10.1021/acs.macromol.8b00096 SN - 0024-9297 SN - 1520-5835 VL - 51 IS - 7 SP - 2604 EP - 2614 PB - American Chemical Society CY - Washington ER - TY - JOUR A1 - Aravopoulou, Dionysia A1 - Kyriakos, Konstantinos A1 - Miasnikova, Anna A1 - Laschewsky, Andre A1 - Papadakis, Christine M. A1 - Kyritsis, Apostolos T1 - Comparative Investigation of the Thermoresponsive Behavior of Two Diblock Copolymers Comprising PNIPAM and PMDEGA Blocks JF - The journal of physical chemistry : B, Condensed matter, materials, surfaces, interfaces & biophysical chemistry N2 - The thermoresponsive behavior of two diblock copolymers PS-b-PNIPAM and PS-b-PMDEGA, which both comprise a hydrophobic polystyrene (PS) block but different thermoresponsive blocks, also differing in length, poly(N-isopropylacrylamide) (PNIPAM) and poly(methoxy diethylene glycol acrylate) (PMDEGA), respectively, was comparatively investigated in a wide temperature range. Concentrated aqueous solutions containing 25 wt % polymer were studied by small-angle X-ray scattering (SAXS), differential scanning calorimetry (DSC), and broadband dielectric spectroscopy (BDS). DSC measurements show that, during the demixing phase transition, the hydration number per oligo(ethylene glycol) side chain in the PS-b-PMDEGA solution decreases rather gradually, even up to 20 °C above the onset of the transition, i.e., the cloud point (CP). In contrast, the PS-b-PNIPAM solution exhibits an abrupt, stepwise dehydration behavior at its CP, indicated by the sharp, narrow endothermic peak. BDS measurements suggest that the organization of the expelled water during the phase transition and the subsequent evolution of the micellar aggregates are different for the two copolymers. In the PS-b-PMDEGA solution, the long-range charge transport process changes significantly at its CP and strong interfacial polarization processes appear, probably due to charge accumulation at the interfaces between the micellar aggregates and the aqueous medium. On the contrary, in the PS-b-PNIPAM solution, the phase transition has only a marginal effect on the long-range conduction process and is accompanied by a reduction in the high-frequency (1 MHz) dielectric permittivity, ε′. The latter effect is attributed to the reduced polarization strength of local chain modes due to an enhancement of intra- and interchain hydrogen bonds (HBs) in the polymer-rich phase during the water detaching process. Surprisingly, our BDS measurements indicate that prior to both the demixing and remixing processes the local chain mobility increases temporally. Our dielectric studies suggest that for PS-b-PNIPAM the water detaching process initiates a few degrees below CP and that the local chain mobility and intra- and/or interchain HBs of the PNIPAM blocks may control its thermoresponsive behavior. Dielectric “jump” experiments show that the kinetics of micellar aggregation in the PS-b-PMDEGA solution is slower than that in the PS-b-PNIPAM solution and is independent of the target temperature within the two-phase region. From the experimental point of view, it is shown that the dielectric susceptibility, especially, the dielectric permittivity, ε′, is a well-suited probe for monitoring both the reversible changes in the molecular dipolar bond polarizability and the long-range interfacial polarization at the phase transition. Y1 - 2018 U6 - https://doi.org/10.1021/acs.jpcb.7b09647 SN - 1520-6106 VL - 122 IS - 9 SP - 2655 EP - 2668 PB - American Chemical Society CY - Washington ER -