@phdthesis{Kossmann2021, author = {Kossmann, Janina}, title = {Controlled condensation to functional materials - synergetic effect of nitrogen content and pore structure}, doi = {10.25932/publishup-53693}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-536935}, school = {Universit{\"a}t Potsdam}, pages = {vi, 148}, year = {2021}, abstract = {The development and optimization of carbonaceous materials is of great interest for several applications including gas sorption, electrochemical storage and conversion, or heterogeneous catalysis. In this thesis, the exploration and optimization of nitrogen containing carbonaceous materials by direct condensation of smart chosen, molecular precursors will be presented. As suggested with the concept of noble carbons, the choice of a stable, nitrogen-containing precursor will lead to an even more stable, nitrogen doped carbonaceous material with a controlled structure and electronic properties. Molecules fulfilling this requirement are for example nucleobases. The direct condensation of nucleobases leads to highly nitrogen containing carbonaceous materials without any further post or pretreatment. By using salt melt templating, pore structure adjustment is possible without the use of hazardous or toxic reagents and the template can be reused. Using these simple tools, the synergetic effect of the pore structure and nitrogen content of the materials can be explored. Within this thesis, the influence of the condensation parameters will be correlated to the structure and performance of the materials. First, the influence of the condensation temperature to the porosity and nitrogen content of guanine will be discussed and the exploration of highly CO2 selective structural pores in C1N1 materials will be shown. Further tuning the pore structure of the materials by salt melt templating will be then explored, the potential of the prepared materials as heterogeneous catalysts and their basic catalytic strength will be correlated to their nitrogen content and pore morphology. A similar approach is used to explore the water sorption behavior of uric acid derived carbonaceous materials as potential sorbents for heat transformation applications. Changes in maximum water uptake and hydrophilicity of the prepared materials will be correlated to the nitrogen content and pore architecture. Due to the high thermal stability, porosity, and nitrogen content of ionic liquid derived nitrogen doped carbonaceous materials, a simple impregnation and calcination route can be conducted to obtain copper nano cluster decorated nitrogen-doped carbonaceous materials. The activity as catalyst for the oxygen reduction reaction of the obtained materials will be shown and structure performance relations are discussed. In conclusion, the versatility of nitrogen doped carbonaceous materials with a nitrogen to carbon ratio of up to one will be shown. The possibility to tune the pore structure as well as the nitrogen content by using a simple procedure including salt melt templating as well as the use of molecular precursors and their effect on the performance will be discussed.}, language = {en} } @phdthesis{Brandi2022, author = {Brandi, Francesco}, title = {Integrated biorefinery in continuous flow systems using sustainable heterogeneous catalysts}, doi = {10.25932/publishup-53766}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-537660}, school = {Universit{\"a}t Potsdam}, pages = {xii, 201}, year = {2022}, abstract = {The negative impact of crude oil on the environment has led to a necessary transition toward alternative, renewable, and sustainable resources. In this regard, lignocellulosic biomass (LCB) is a promising renewable and sustainable alternative to crude oil for the production of fine chemicals and fuels in a so-called biorefinery process. LCB is composed of polysaccharides (cellulose and hemicellulose), as well as aromatics (lignin). The development of a sustainable and economically advantageous biorefinery depends on the complete and efficient valorization of all components. Therefore, in the new generation of biorefinery, the so-called biorefinery of type III, the LCB feedstocks are selectively deconstructed and catalytically transformed into platform chemicals. For this purpose, the development of highly stable and efficient catalysts is crucial for progress toward viability in biorefinery. Furthermore, a modern and integrated biorefinery relies on process and reactor design, toward more efficient and cost-effective methodologies that minimize waste. In this context, the usage of continuous flow systems has the potential to provide safe, sustainable, and innovative transformations with simple process integration and scalability for biorefinery schemes. This thesis addresses three main challenges for future biorefinery: catalyst synthesis, waste feedstock valorization, and usage of continuous flow technology. Firstly, a cheap, scalable, and sustainable approach is presented for the synthesis of an efficient and stable 35 wt.-\% Ni catalyst on highly porous nitrogen-doped carbon support (35Ni/NDC) in pellet shape. Initially, the performance of this catalyst was evaluated for the aqueous phase hydrogenation of LCB-derived compounds such as glucose, xylose, and vanillin in continuous flow systems. The 35Ni/NDC catalyst exhibited high catalytic performances in three tested hydrogenation reactions, i.e., sorbitol, xylitol, and 2-methoxy-4-methylphenol with yields of 82 mol\%, 62 mol\%, and 100 mol\% respectively. In addition, the 35Ni/NDC catalyst exhibited remarkable stability over a long time on stream in continuous flow (40 h). Furthermore, the 35Ni/NDC catalyst was combined with commercially available Beta zeolite in a dual-column integrated process for isosorbide production from glucose (yield 83 mol\%). Finally, 35Ni/NDC was applied for the valorization of industrial waste products, namely sodium lignosulfonate (LS) and beech wood sawdust (BWS) in continuous flow systems. The LS depolymerization was conducted combining solvothermal fragmentation of water/alcohol mixtures (i.e.,methanol/water and ethanol/water) with catalytic hydrogenolysis/hydrogenation (SHF). The depolymerization was found to occur thermally in absence of catalyst with a tunable molecular weight according to temperature. Furthermore, the SHF generated an optimized cumulative yield of lignin-derived phenolic monomers of 42 mg gLS-1. Similarly, a solvothermal and reductive catalytic fragmentation (SF-RCF) of BWS was conducted using MeOH and MeTHF as a solvent. In this case, the optimized total lignin-derived phenolic monomers yield was found of 247 mg gKL-1.}, language = {en} } @phdthesis{Haubitz2021, author = {Haubitz, Toni}, title = {Transient absorption spectroscopy}, doi = {10.25932/publishup-53509}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-535092}, school = {Universit{\"a}t Potsdam}, pages = {xiii, 176}, year = {2021}, abstract = {The optical properties of chromophores, especially organic dyes and optically active inorganic molecules, are determined by their chemical structures, surrounding media, and excited state behaviors. The classical optical go-to techniques for spectroscopic investigations are absorption and luminescence spectroscopy. While both techniques are powerful and easy to apply spectroscopic methods, the limited time resolution of luminescence spectroscopy and its reliance on luminescent properties can make its application, in certain cases, complex, or even impossible. This can be the case when the investigated molecules do not luminesce anymore due to quenching effects, or when they were never luminescent in the first place. In those cases, transient absorption spectroscopy is an excellent and much more sophisticated technique to investigate such systems. This pump-probe laser-spectroscopic method is excellent for mechanistic investigations of luminescence quenching phenomena and photoreactions. This is due to its extremely high time resolution in the femto- and picosecond ranges, where many intermediate or transient species of a reaction can be identified and their kinetic evolution can be observed. Furthermore, it does not rely on the samples being luminescent, due to the active sample probing after excitation. In this work it is shown, that with transient absorption spectroscopy it was possible to identify the luminescence quenching mechanisms and thus luminescence quantum yield losses of the organic dye classes O4-DBD, S4-DBD, and pyridylanthracenes. Hence, the population of their triplet states could be identified as the competitive mechanism to their luminescence. While the good luminophores O4-DBD showed minor losses, the S4-DBD dye luminescence was almost entirely quenched by this process. However, for pyridylanthracenes, this phenomenon is present in both the protonated and unprotonated forms and moderately effects the luminescence quantum yield. Also, the majority of the quenching losses in the protonated forms are caused by additional non-radiative processes introduced by the protonation of the pyridyl rings. Furthermore, transient absorption spectroscopy can be applied to investigate the quenching mechanisms of uranyl(VI) luminescence by chloride and bromide. The reduction of the halides by excited uranyl(VI) leads to the formation of dihalide radicals X^(·-2). This excited state redox process is thus identified as the quenching mechanism for both halides, and this process, being diffusion-limited, can be suppressed by cryogenically freezing the samples or by observing these interactions in media with a lower dielectric constant, such as ACN and acetone.}, language = {en} } @phdthesis{ChandrakanthShetty2021, author = {Chandrakanth Shetty, Sunidhi}, title = {Directed chemical communication in artificial eukaryotic cells}, doi = {10.25932/publishup-53364}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-533642}, school = {Universit{\"a}t Potsdam}, year = {2021}, abstract = {Eukaryotic cells can be regarded as complex microreactors capable of performing various biochemical reactions in parallel which are necessary to sustain life. An essential prerequisite for these complex metabolic reactions to occur is the evolution of lipid membrane-bound organelles enabling compartmental- ization of reactions and biomolecules. This allows for a spatiotemporal control over the metabolic reactions within the cellular system. Intracellular organi- zation arising due to compartmentalization is a key feature of all living cells and has inspired synthetic biologists to engineer such systems with bottom-up approaches. Artificial cells provide an ideal platform to isolate and study specific re- actions without the interference from the complex network of biomolecules present in biological cells. To mimic the hierarchical architecture of eukaryotic cells, multi-compartment assemblies with nested liposomal structures also re- ferred to as multi-vesicular vesicles (MVVs) have been widely adopted. Most of the previously reported multi-compartment systems adopt bulk method- ologies which suffer from low yield and poor control over size. Microfluidic strategies help circumvent these issues and facilitate a high-throughput and robust technique to assemble MVVs of uniform size distribution. In this thesis, firstly, the bulk methodologies are explored to build MVVs and implement a synthetic signalling cascade. Next, a polydimethylsiloxane (PDMS)-based microfluidic platform is introduced to build MVVs and the significance of PEGylated lipids for the successful encapsulation of inner com- partments to generate stable multi-compartment systems is highlighted. Next, a novel two-inlet channel PDMS-based microfluidic device to create MVVs encompassing a three-step enzymatic reaction cascade is presented. A directed reaction pathway comprising of the enzymes α-glucosidase (α-Glc), glucose oxidase (GOx), and horseradish peroxidase (HRP) spanning across three compartments via reconstitution of size-selective membrane proteins is described. Furthermore, owing to the monodispersity of our MVVs due to microfluidic strategies, this platform is employed to study the effect of com- partmentalization on reaction kinetics. Further integration of cell-free expression module into the MVVs would allow for gene-mediated signal transduction within artificial eukaryotic cells. Therefore, the chemically inducible cell-free expression of a membrane protein alpha-hemolysin and its further reconstitution into liposomes is carried out. In conclusion, the present thesis aims to build artificial eukaryotic cells to achieve size-selective chemical communication that also show potential for applications as micro reactors and as vehicles for drug delivery.}, language = {en} } @phdthesis{Altabal2021, author = {Altabal, Osamah}, title = {Design and fabrication of geometry-assisted on-demand dosing systems}, doi = {10.25932/publishup-53244}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-532441}, school = {Universit{\"a}t Potsdam}, pages = {xxiv, 122}, year = {2021}, abstract = {The controlled dosage of substances from a device to its environment, such as a tissue or an organ in medical applications or a reactor, room, machinery or ecosystem in technical, should ideally match the requirements of the applications, e.g. in terms of the time point at which the cargo is released. On-demand dosage systems may enable such a desired release pattern, if the device contain suitable features that can translate external signals into a release function. This study is motivated by the opportunities arising from microsystems capable of an on-demand release and the contributions that geometrical design may have in realizing such features. The goals of this work included the design, fabrication, characterization and experimental proof-of-concept of geometry-assisted triggerable dosing effect (a) with a sequential dosing release and (b) in a self-sufficient dosage system. Structure-function relationships were addressed on the molecular, morphological and, with a particular attention, the device design level, which is on the micrometer scale. Models and/or computational tools were used to screen the parameter space and provide guidance for experiments.}, language = {en} } @phdthesis{Kirchhofer2021, author = {Kirchhofer, Tabea}, title = {The development of multi - compartmentalised systems for the directed organisation of artificial cells}, doi = {10.25932/publishup-52842}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-528428}, school = {Universit{\"a}t Potsdam}, pages = {II, 126}, year = {2021}, abstract = {Membrane contact sites are of particular interest in the field of synthetic biology and biophysics. They are involved in a great variety of cellular functions. They form in between two cellular organelles or an organelle and the plasma membrane in order to establish a communication path for molecule transport or signal transmission. The development of an artificial membrane system which can mimic membrane contact sites using bottom up synthetic biology was the goal of this research study. For this, a multi - compartmentalised giant unilamellar vesicle (GUV) system was created with the membrane of the outer vesicle mimicking the plasma membrane and the inner GUVs posing as cellular organelles. In the following steps, three different strategies were used to achieve an internal membrane - membrane adhesion.}, language = {en} } @phdthesis{Bhaskar2020, author = {Bhaskar, Thanga Bhuvanesh Vijaya}, title = {Biomimetic layers of extracellular matrix glycoproteins as designed biointerfaces}, school = {Universit{\"a}t Potsdam}, year = {2020}, abstract = {The goal of regenerative medicine is to guide biological systems towards natural healing outcomes using a combination of niche-specific cells, bioactive molecules and biomaterials. In this regard, mimicking the extracellular matrix (ECM) surrounding cells and tissues in vivo is an effective strategy to modulate cell behaviors. Cellular function and phenotype is directed by the biochemical and biophysical signals present in the complex 3D network of ECMs composed mainly of glycoproteins and hydrophilic proteoglycans. While cellular modulation in response to biophysical cues emulating ECM features has been investigated widely, the influence of biochemical display of ECM glycoproteins mimicking their presentation in vivo is not well characterized. It remains a significant challenge to build artificial biointerfaces using ECM glycoproteins that precisely match their presentation in nature in terms of morphology, orientation and conformation. This challenge becomes clear, when one understands how ECM glycoproteins self-assemble in the body. Glycoproteins produced inside the cell are secreted in the extra-cellular space, where they are bound to the cell membrane or other glycoproteins by specific interactions. This leads to elevated local concentration and 2Dspatial confinement, resulting in self-assembly by the reciprocal interactions arising from the molecular complementarity encoded in the glycoprotein domains. In this thesis, air-water (A-W) interface is presented as a suitable platform, where self-assembly parameters of ECM glycoproteins such as pH, temperature and ionic strength can be controlled to simulate in vivo conditions (Langmuir technique), resulting in the formation of glycoprotein layers with defined characteristics. The layer can be further compressed with surface barriers to enhance glycoprotein-glycoprotein contacts and defined layers of glycoproteins can be immobilized on substrates by horizontal lift and touch method, called Langmuir-Sch{\"a}fer (LS) method. Here, the benefit of Langmuir and LS methods in achieving ECM glycoprotein biointerfaces with controlled network morphology and ligand density on substrates is highlighted and contrasted with the commonly used (glyco)protein solution deposition (SO) method on substrates. In general, the (glyco)protein layer formation by SO is rather uncontrolled, influenced strongly by (glyco)protein-substrate interactions and it results in multilayers and aggregations on substrates, while the LS method results in (glyco)proteins layers with a more homogenous presentation. To achieve the goal of realizing defined ECM layers on substrates, ECM glycoproteins having the ability to self-assemble were selected: Collagen-IV (Col-IV) and fibronectin (FN). Highly packed FN layer with uniform presentation of ligands was deposited on polydimethysiloxane VIII (PDMS) by LS method, while a heterogeneous layer was formed on PDMS by SO with prominent aggregations visible. Mesenchymal stem cells (MSC) on PDMS equipped with FN by LS exhibited more homogeneous and elevated vinculin expression and weaker stress fiber formation than on PDMS equipped with FN by SO and these divergent responses could be attributed to the differences in glycoprotein presentation at the interface. Col-IV are scaffolding components of specialized ECM called basement membranes (BM), and have the propensity to form 2D networks by self-polymerization associated with cells. Col- IV behaves as a thin-disordered network at the A-W interface. As the Col-IV layer was compressed at the A-W interface using trough barriers, there was negligible change in thickness (layer thickness ~ 50 nm) or orientation of molecules. The pre-formed organization of Col-IV was transferred by LS method in a controlled fashion onto substrates meeting the wettability criterion (CA ≤ 80°). MSC adhesion (24h) on PET substrates deposited with Col-IV LS films at 10, 15 and 20 mN·m-1 surface pressures was (12269.0 ± 5856.4) cells for LS10, (16744.2 ± 1280.1) cells for LS15 and (19688.3 ± 1934.0) cells for LS20 respectively. Remarkably, by selecting the surface areal density of Col-IV on the Langmuir trough on PET, there is a linear increase between the number of adherent MSCs and the Col-IV ligand density. Further, FN has the ability to self-stabilize and form 2D networks (even without compression) while preserving native β-sheet structure at the A-W interface on a defined subphase (pH = 2). This provides the possibility to form such layers on any vessel (even on standard six-well culture plates) and the cohesive FN layers can be deposited by LS transfer, without the need for expensive LB instrumentation. Multilayers of FN can be immobilized on substrates by this approach, as easily as Layer-by-Layer method, even without the need for secondary adlayer or activated bare substrate. Thus, this facile glycoprotein coating strategy approach is accessible to many researchers to realize defined FN films on substrates for cell culture. In conclusion, Langmuir and LS methods can create biomimetic glycoprotein biointerfaces on substrates controlling aspects of presentation such as network morphology and ligand density. These methods will be utilized to produce artificial BM mimics and interstitial ECM mimics composed of more than one ECM glycoprotein layer on substrates, serving as artificial niches instructing stem cells for cell-replacement therapies in the future.}, language = {en} } @phdthesis{Sanay2021, author = {Sanay, Berran}, title = {Monomers and polymers based on renewable resources for new photopolymer coating}, doi = {10.25932/publishup-51868}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-518684}, school = {Universit{\"a}t Potsdam}, pages = {XXXIII, 124}, year = {2021}, abstract = {The present work focuses on minimising the usage of toxic chemicals by integration of the biobased monomers, derived from fatty acid esters, to photopolymerization processes, which are known to be nature friendly. Internal double bond present in the oleic acid was converted to more reactive (meth)acrylate or epoxy group. Biobased starting materials, functionalized by different pendant groups, were used for photopolymerizing formulations to design of new polymeric structures by using ultraviolet light emitting diode (UV-LED) (395 nm) via free radical polymerization or cationic polymerization. New (meth)acrylates (2,3 and 4) consisting of two isomers, methyl 9-((meth)acryloyloxy)-10-hydroxyoctadecanoate / methyl 9-hydroxy-10-((meth)acryloyloxy)octadecanoate (2 and 3) and methyl 9-(1H-imidazol-1-yl)-10-(methacryloyloxy)octadecanoate / methyl 9-(methacryloyloxy)-10-(1H-imidazol-1-yl)octadecanoate (4), modified from oleic acid mix, and ionic liquid monomers (1a and 1b) bearing long alkyl chain were polymerized photochemically. New (meth)acrylates are based on vegetable oil, and ionic liquids (ILs) have nonvolatile behaviour. Therefore, both monomer types have green approach. Photoinitiated polymerization of new (meth)acrylates and ionic liquids was investigated in the presence of ethyl (2,4,6-trimethylbenzoyl) phenylphosphinate (Irgacure® TPO-L) or di(4-methoxybenzoyl)diethylgermane (Ivocerin®) as photoinitiator (PI). Additionally, the results were discussed in comparison with those obtained from commercial 1,6-hexanediol di(meth)acrylate (5 and 6) for deeper investigation of biobased monomer's potential to substitute petroleum derived materials with renewable resources for possible coating applications. Kinetic study shows that methyl 9-(1H-imidazol-1-yl)-10-(methacryloyloxy)octadecanoate / methyl 9-(methacryloyloxy)-10-(1H-imidazol-1-yl)octadecanoate (4) and ionic liquids (1a and 1b) have quantitative conversion after irradiation process which is important for practical applications. On the other hand, heat generation occurs in a longer time during the polymerization of biobased systems or ILs. The poly(meth)acrylates modified from (meth)acrylated fatty acid methyl ester monomers generally show a low glass transition temperature because of the presence of long aliphatic chain in the polymer structure. However, poly(meth)acrylates containing aromatic group have higher glass transition temperature. Therefore, new 4-(4-methacryloyloxyphenyl)-butan-2-one (7) was synthesized which can be a promising candidate for the green techniques, such as light induced polymerization. Photokinetic investigation of the new monomer, 4-(4-methacryloyloxyphenyl)-butan-2-one (7), was discussed using Irgacure® TPO-L or Ivocerin® as photoinitiator. The reactivity of that monomer was compared to commercial 2-phenoxyethyl methacrylate (8) and phenyl methacrylate (9) basis of the differences on monomer structures. The photopolymer of 4-(4-methacryloyloxyphenyl)-butan-2-one (7) might be an interesting candidate for the coating application with the properties of quantitative conversion and high molecular weight. It also shows higher glass transition temperature. In addition to the linear systems based on renewable materials, new crosslinked polymers were also designed in this thesis. Therefore, isomer mixture consisting of ethane-1,2-diyl bis(9-methacryloyloxy-10-hydroxy octadecanoate), ethane-1,2-diyl 9-hydroxy-10-methacryloyloxy-9'-methacryloyloxy10'-hydroxy octadecanoate and ethane-1,2-diyl bis(9-hydroxy-10-methacryloyloxy octadecanoate) (10) was synthesized by derivation of the oleic acid which has not been previously described in the literature. Crosslinked material based on this biobased monomer was produced by photoinitiated free radical polymerization using Irgacure® TPO-L or Ivocerin® as photoinitiator. Furthermore, material properties were diversified by copolymerization of 10 with 4-(4-methacryloyloxyphenyl)-butan-2-one (7) or methyl 9-(1H-imidazol-1-yl)-10-(methacryloyloxy)octadecanoate / methyl 9-(methacryloyloxy)-10-(1H-imidazol-1-yl)octadecanoate (4). In addition to this, influence of comonomer with different chemical structure on the network system was investigated by analysis of thermo-mechanical properties, crosslink density and molecular weight between two crosslink junctions. An increase in the glass transition temperature caused by copolymerization of biobased monomer 10 with the excess amount of 4-(4-methacryloyloxyphenyl)-butan-2-one (7) was confirmed by both techniques, differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA). On the other hand, crosslink density decreased as a result of copolymerization reactions due to the reduction in the mean functionality of the system. Furthermore, surface characterization has been tested by contact angle measurements using solvents with different polarity. This work also contributes to the limited data reported about cationic photopolymerization of the epoxidized vegetable oils in the literature in contrast to the widely investigation of thermal curing of the biorenewable epoxy monomers. In addition to the 9,10-epoxystearic acid methyl ester (11), a new monomer of bis-(9,10-epoxystearic acid) 1,2-ethanediyl ester (12) has been synthesized from oleic acid. These two biobased epoxies have been polymerized via cationic photoinitiated polymerization in the presence of bis(t-butyl)-iodonium-tetrakis(perfluoro-t-butoxy)aluminate ([Al(O-t-C4F9)4]-) and isopropylthioxanthone (ITX) as photinitiating system. Polymerization kinetic of 9,10-epoxystearic acid methyl ester (11) and bis-(9,10-epoxystearic acid) 1,2-ethanediyl ester (12) was investigated and compared with the kinetic of commercial monomers being 3,4-epoxycyclohexylmethyl-3',4'-epoxycyclohexane carboxylate (13), 1,4-butanediol diglycidyl ether (14), and diglycidylether of bisphenol-A (15). Both biobased epoxies (11 and 12) showed higher conversion than cycloaliphatic epoxy (13), and lower reactivity than 1,4-butanediol diglycidyl ether (14). Additional network systems were designed by copolymerization of bis-(9,10-epoxystearic acid) 1,2-ethanediyl ester (12) and diglycidylether of bisphenol-A (15) in different molar ratios (1:1; 1:5; 1:9). It addresses that, final conversion is dependent on polymerization rate as well as physical processes such as vitrification during polymerization. Moreover, low glass transition temperature of homopolymer derived from bis-(9,10-epoxystearic acid) 1,2-ethanediyl ester (12) was successfully increased by copolymerization with diglycidylether bisphenol-A (15). On the other hand, the surface produced from bis-(9,10-epoxystearic acid) 1,2-ethanediyl ester (12) shows hydrophobic character. Higher concentration of biobased diepoxy (12) in the copolymerizing mixture decreases surface free energy. Network systems were also investigated according to the rubber elasticity theory. Crosslinked polymer derived from the mixture of bis-(9,10-epoxystearic acid) 1,2-ethanediyl ester (12) and diglycidylether of bisphenol-A (15) (molar ratio=1:5) exhibits almost ideal polymer network.}, language = {en} } @phdthesis{Izraylit2021, author = {Izraylit, Victor}, title = {Reprogrammable and tunable actuation in multiblock copolymer blends}, doi = {10.25932/publishup-51843}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-518434}, school = {Universit{\"a}t Potsdam}, pages = {104}, year = {2021}, abstract = {Soft actuators have drawn significant attention due to their relevance for applications, such as artificial muscles in devices developed for medicine and robotics. Tuning their performance and expanding their functionality are frequently done by means of chemical modification. The introduction of structural elements rendering non-synthetic modification of the performance possible, as well as control over physical appearance and facilitating their recycling is a subject of a great interest in the field of smart materials. The primary aim of this thesis was to create a shape-memory polymeric actuator, where the capability for non-synthetic tuning of the actuation performance is combined with reprocessability. Physically cross-linked polymeric matrices provide a solid material platform, where the in situ processing methods can be employed for modification of the composition and morphology, resulting in the fine tuning of the related mechanical properties and shape-memory actuation capability. The morphological features, required for shape-memory polymeric actuators, namely two crystallisable domains and anchoring points for physical cross-links, were embedded into a multiblock copolymer with poly(ε-caprolactone) and poly(L-lactide) segments (PLLA-PCL). Here, the melting transition of PCL was bisected into the actuating and skeleton-forming units, while the cross-linking was introduced via PLA stereocomplexation in blends with oligomeric poly(D-lactide) (ODLA). PLLA segment number average length of 12-15 repeating units was experimentally defined to be capable of the PLA stereocomplexes formation, but not sufficient for the isotactic crystallisation. Multiblock structure and phase dilution broaden the PCL melting transition, facilitating its separation into two conditionally independent crystalline domains. Low molar mass of the PLA stereocomplex components and a multiblock structure enables processing and reprocessing of the PLLA-PCL / ODLA blends with common non-destructive techniques. The modularity of the PLLA-PCL structure and synthetic approach allows for independent tuning of the properties of its components. The designed material establishes a solid platform for non-synthetic tuning of thermomechanical and structural properties of thermoplastic elastomers. To evaluate the thermomechanical stability of the formed physical network, three criteria were appraised. As physical cross-links, PLA stereocomplexes have to be evenly distributed within the material matrix, their melting temperature shall not overlap with the thermal transitions of the PCL domains and they have to maintain the structural integrity within the strain ε ranges further applied in the shape-memory actuation experiments. Assigning PCL the function of the skeleton-forming and actuating units, and PLA stereocomplexes the role of physical netpoints, shape-memory actuation was realised in the PLLA-PCL / ODLA blends. Reversible strain of shape-memory actuation was found to be a function of PLA stereocomplex crystallinity, i.e. physical cross-linking density, with a maximum of 13.4 ± 1.5\% at PLA stereocomplex content of 3.1 ± 0.3 wt\%. In this way, shape-memory actuation can be tuned via adjusting the composition of the PLLA-PCL / ODLA blend. This makes the developed material a valuable asset in the production of cost-effective tunable soft polymeric actuators for the applications in medicine and soft robotics.}, language = {en} } @phdthesis{Nacak2021, author = {Nacak, Selma}, title = {Synthesis and Characterization of Upconversion Nanaparticles for Applications in Life Sciences}, school = {Universit{\"a}t Potsdam}, year = {2021}, language = {en} } @phdthesis{Ebel2021, author = {Ebel, Kenny}, title = {Quantification of low-energy electron induced single and double strand breaks in well-defined DNA sequences using DNA origami nanostructures}, doi = {10.25932/publishup-50449}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-504499}, school = {Universit{\"a}t Potsdam}, pages = {111}, year = {2021}, abstract = {Ionizing radiation is used in cancer radiation therapy to effectively damage the DNA of tumors leading to cell death and reduction of the tumor tissue. The main damage is due to generation of highly reactive secondary species such as low-energy electrons (LEE) with the most probable energy around 10 eV through ionization of water molecules in the cells. A simulation of the dose distribution in the patient is required to optimize the irradiation modality in cancer radiation therapy, which must be based on the fundamental physical processes of high-energy radiation with the tissue. In the present work the accurate quantification of DNA radiation damage in the form of absolute cross sections for LEE-induced DNA strand breaks (SBs) between 5 and 20 eV is done by using the DNA origami technique. This method is based on the analysis of well-defined DNA target sequences attached to DNA origami triangles with atomic force microscopy (AFM) on the single molecule level. The present work focuses on poly-adenine sequences (5'-d(A4), 5'-d(A8), 5'-d(A12), 5'-d(A16), and 5'- d(A20)) irradiated with 5.0, 7.0, 8.4, and 10 eV electrons. Independent of the DNA length, the strand break cross section shows a maximum around 7.0 eV electron energy for all investigated oligonucleotides confirming that strand breakage occurs through the initial formation of negative ion resonances. Additionally, DNA double strand breaks from a DNA hairpin 5'-d(CAC)4T(Bt-dT)T2(GTG)4 are examined for the first time and are compared with those of DNA single strands 5'-d(CAC)4 and 5'- d(GTG)4. The irradiation is made in the most likely energy range of 5 to 20 eV with an anionic resonance maximum around 10 eV independently of the DNA sequence. There is a clear difference between σSSB and σDSB of DNA single and double strands, where the strand break for ssDNA are always higher in all electron energies compared to dsDNA by the factor 3. A further part of this work deals with the characterization and analysis of new types of radiosensitizers used in chemoradiotherapy, which selectively increases the DNA damage upon radiation. Fluorinated DNA sequences with 2'-fluoro-2'-deoxycytidine (dFC) show an increased sensitivity at 7 and 10 eV compared to the unmodified DNA sequences by an enhancement factor between 2.1 and 2.5. In addition, light-induced oxidative damage of 5'-d(GTG)4 and 5'-d((CAC)4T(Bt-dT)T2(GTG)4) modified DNA origami triangles by singlet oxygen 1O2 generated from three photoexcited DNA groove binders [ANT994], [ANT1083] and [Cr(ddpd)2][BF4]3 illuminated in different experiments with UV-Vis light at 430, 435 and 530 nm wavelength is demonstrated. The singlet oxygen induced generation of DNA damage could be detected in both aqueous and dry environments for [ANT1083] and [Cr(ddpd)2][BF4]3.}, language = {en} } @phdthesis{Kar, author = {Kar, Manaswita}, title = {Energy band gap tuning of halide perovskite materials from first principles}, school = {Universit{\"a}t Potsdam}, abstract = {Solar cells based on hybrid perovskites materials have become significantly important among the third generation photovoltaics over the last few years. The first solid state solar cell was reported in 2012. Over the years, the power conversion efficiencies of these devices have increased at a tremendous pace and this has made the perovskite solar cell devices a serious competitor in the well-established market of thin-film and wafer technologies. Over time, a large number of articles on this topic has been published in peer-reviewed journals. The presence of lead in the most efficient hybrid perovskite materials have raised questions about the possible toxicity of these devices and the extent of their environmental impact. Therefore, a lot of research has been devoted to finding alternative perovskite materials with similar or even better opto-electronic properties. An alternative strategy to improve the efficiency of thin film solar cells is to build efficient tandem cells by combining two or more perovskite materials with specifically tailored band gaps. The first step towards the development of perovskite-only tandem solar cells is to identify complementary hybrid perovskite materials with specific band gaps that maximize the efficiency of tandem solar cells. The optimal set of optical gaps for a tandem structure made of two materials is 1.9 eV and 1.0 eV. Since the electronic properties of hybrid perovskites are known to be strongly dependent on the composition and distortion of the crystal lattice, strong focus has been made towards the structure optimisation as well as the calculation of the energy band gaps of the materials using density functional theory (DFT). In an attempt to study the structure-property relationship of these perovskite materials and to find novel perovskite materials for future applications, researchers have employed computational screening procedures to study a large range of these materials by systematic replacement of the cations and anions from the prototypical perovskite. Density functional theory in particular is used as a theoretical tool, because of it's precision to determine the properties of materials and also it's computational viability in dealing with complex systems. In this thesis, the main focus is to do a systematic screening of the perovskite materials, of the composition ABX3 again by replacing the A-site, B-site and the X-site elements to find novel materials with band gaps suitable for application in tandem solar cells. As a first step towards contributing to this vibrant field of research, a high-throughput computational screening has been performed by replacing the metal and the halogen in the conventional CH3NH3PbI3 perovskites with homovalent metals and halogens to find materials in the desired range of band gaps that has already been mentioned earlier. This is achieved by performing a geometry optimisation on all the simulated structures followed by calculating their energy band gaps at the semilocal and the hybrid levels of theory. However, it is well known that the rotation of the organic cation CH3NH3 hinders the stability of these devices by the formation of hydrogen bonds between the hydrogen atoms of the cation and the halogens. This causes the materials to degrade under normal temperature and pressure conditions. As an attempt to prevent these devices from being unstable, a next step has been taken where the CH3NH3 cation has been replaced by inorganic cations of similar ionic radius. This is followed by another thorough screening, similar to the previous step. The stability of the materials has been determined by using the empirical Goldschmidt tolerance factor. As a last part of the thesis, a small proportion of the inorganic cation is mixed with CH3NH3 in order to form mixed-halide perovskites. These structures are optimised and their band gaps are calculated using density functional theory in order to predict materials suitable for single junction as well as tandem solar cell devices. It is expected that the contribution made through this thesis will be helpful for the progress of perovskite solar cells in terms of efficiencies and will also allow the community to explore the different properties these materials for further progress and development.}, language = {en} } @phdthesis{Raju2021, author = {Raju, Rajarshi Roy}, title = {'Smart' Janus emulsions}, school = {Universit{\"a}t Potsdam}, year = {2021}, abstract = {Emulsions constitute one of the most prominent and continuously evolving research areas in Colloid Chemistry, which involves the preparation of mixtures or dispersions of immiscible components in a continuous medium. Besides conventional oil-in-water or water-in-oil emulsions, other emulsions of complex droplet morphologies have recently attracted significant research interests. Especially Janus emulsions, in which each droplet is comprised of two distinct sub-regions, have shown versatile potential applications. One of their advantages is the possibility of compartmentalization, which enables to play with two different chemistries in a single droplet. Though microfluidic methods are conventionally used to prepare Janus emulsions, their industrial applications are largely hindered by low throughput and extensive instrumentations. Recently, it has been discovered that simply one-pot moderate/high energy emulsification is also capable of developing Janus morphology, although their preparation and stabilization remain rather substantially challenging. This cumulative doctoral thesis focuses on the preparation and characterization of 'smart' Janus emulsions, i.e. Janus emulsions with special stimuli-responsive features. One-step moderate/high energy emulsification of olive and silicone oil in an aqueous medium was carried out. Special consideration was devoted to the interfacial tensions among the components to maintain the criteria of forming characteristic droplet architectures, in addition to avoiding multiple emulsion destabilization phenomena like imminent phase separation or even separated droplet formation. A series of investigations were conducted related to the formation of complexes of charged macromolecules and role of them as stabilizers to achieve stable Janus emulsions for a realistic timeframe (more than 3 months). The correlation between the size of the stabilizer particles and the droplet size of emulsion was established. Furthermore, it was observed that Janus emulsion gels with interesting rheological properties can be fabricated in the presence of suitable polyelectrolyte complexes. Janus emulsions that could be influenced by pH, temperature or magnetic field were successfully produced in presence of characteristic stimuli-responsive stabilizers. Afterwards, the effect of these changes was studied by different characterization techniques. The size and morphology could be tuned easily by changing the pH. The incorporation of iron oxide magnetic nanoparticles (synthesized separately by a co-precipitation method) to one component of the Janus emulsion was carried out so that the movement and orientation of the complex droplets in aqueous media could be controlled by an external magnetic field. Additionally, temperature-triggered instantaneous reversible breakdown of Janus droplets was also accomplished. The responses of the Janus droplets by the stimuli were well-documented and explained. Another goal of the present contribution was to exploit this special morphological feature of emulsions as a template for producing porous materials. This was demonstrated by the preparation of ultralight magnetic responsive aerogels, utilizing Janus emulsion gels. The produced aerogels also showed the capacity to separate toxic dye from water. To the best of our knowledge, this is the first example of investigation towards batch scale production of Janus emulsion with such special stimuli-responsive properties by a simple bulk emulsification method.}, language = {en} } @phdthesis{Perovic2020, author = {Perovic, Milena}, title = {Functionalization of nanoporous carbon materials for chiral separation and heterogeneous oxidation catalysis}, doi = {10.25932/publishup-48659}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-486594}, school = {Universit{\"a}t Potsdam}, pages = {140}, year = {2020}, abstract = {The impact that catalysis has on global economy and environment is substantial, since 85\% of all chemical industrial processes are catalytic. Among those, 80\% of the processes are heterogeneously catalyzed, 17\% make use of homogeneous catalysts, and 3\% are biocatalytic processes. Especially in the pharmaceutical and agrochemical industry, a significant part of these processes involves chiral compounds. Obtaining enantiomerically pure compounds is necessary and it is usually accomplished by asymmetric synthesis and catalysis, as well as chiral separation. The efficiency of these processes may be vastly improved if the chiral selectors are positioned on a porous solid support, thereby increasing the available surface area for chiral recognition. Similarly, the majority of commercial catalysts are also supported, usually comprising of metal nanoparticles (NPs) dispersed on highly porous oxide or nanoporous carbon material. Materials that have exceptional thermal and chemical stability, and are electrically conductive are porous carbons. Their stability in extreme pH regions and temperatures, the possibility to tailor their pore architecture and chemical functionalization, and their electric conductivity have already established these materials in the fields of separation and catalysis. However, their heterogeneous chemical structure with abundant defects make it challenging to develop reliable models for the investigation of structure-performance relationships. Therefore, there is a necessity for expanding the fundamental understanding of these robust materials under experimental conditions to allow for their further optimization for particular applications. This thesis gives a contribution to our knowledge about carbons, through different aspects, and in different applications. On the one hand, a rather exotic novel application was investigated by attempts in synthesizing porous carbon materials with an enantioselective surface. Chapter 4.1 described an approach for obtaining mesoporous carbons with an enantioselective surface by direct carbonization of a chiral precursor. Two enantiomers of chiral ionic liquids (CIL) based on amino acid tyrosine were used as carbon precursors and ordered mesoporous silica SBA-15 served as a hard template for obtaining porosity. The chiral recognition of the prepared carbons has been tested in the solution by isothermal titration calorimetry with enantiomers of Phenylalanine as probes, as well as chiral vapor adsorption with 2-butanol enantiomers. Measurements in both solution and the gas phase revealed the differences in the affinity of carbons towards two enantiomers. The atomic efficiency of the CIL precursors was increased in Chapter 4.2, and the porosity was developed independently from the development of chiral carbons, through the formation of stable composites of pristine carbon and CIL-derived coating. After the same set of experiments for the investigation of chirality, the enantiomeric ratios of the composites reported herein were even higher than in the previous chapter. On the other hand, the structure‒activity relationship of carbons as supports for gold nanoparticles in a rather traditional catalytic model reaction, on the interface between gas, liquid, and solid, was studied. In Chapter 5.1 it was shown on the series of catalysts with different porosities that the kinetics of ᴅ-glucose oxidation reaction can be enhanced by increasing the local concentration of the reactants around the active phase of the catalyst. A large amount of uniform narrow mesopores connected to the surface of the Au catalyst supported on ordered mesoporous carbon led to the water confinement, which increased the solubility of the oxygen in the proximity of the catalyst and thereby increased the apparent catalytic activity of this catalyst. After increasing the oxygen concentration in the internal area of the catalyst, in Chapter 5.2 the concentration of oxygen was increased in the external environment of the catalyst, by the introduction of less cohesive liquids that serve as efficient solvent for oxygen, perfluorinated compounds, near the active phase of the catalyst. This was achieved by a formation of catalyst particle-stabilized emulsions of perfluorocarbon in aqueous ᴅ-glucose solution, that further promoted the catalytic activity of gold-on-carbon catalyst. The findings reported within this thesis are an important step in the understanding of the structure-related properties of carbon materials.}, language = {en} } @phdthesis{Harmanli2020, author = {Harmanli, İpek}, title = {Towards catalytic activation of nitrogen in ionic liquid/nanoporous carbon interfaces for electrochemical ammonia synthesis}, doi = {10.25932/publishup-48359}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-483591}, school = {Universit{\"a}t Potsdam}, pages = {v, 126}, year = {2020}, abstract = {Ammonia is a chemical of fundamental importance for nature`s vital nitrogen cycle. It is crucial for the growth of living organisms as well as food and energy source. Traditionally, industrial ammonia production is predominated by Haber- Bosch process (HBP) which is based on direct conversion of N2 and H2 gas under high temperature and high pressure (~500oC, 150-300 bar). However, it is not the favorite route because of its thermodynamic and kinetic limitations, and the need for the energy intense production of hydrogen gas by reforming processes. All these disfavors of HBP open a target to search for an alternative technique to perform efficient ammonia synthesis via electrochemical catalytic processes, in particular via water electrolysis, using water as the hydrogen source to save the process from gas reforming. In this study, the investigation of the interface effects between imidazolium-based ionic liquids and the surface of porous carbon materials with a special interest in the nitrogen absorption capability. As the further step, the possibility to establish this interface as the catalytically active area for the electrochemical N2 reduction to NH3 has been evaluated. This particular combination has been chosen because the porous carbon materials and ionic liquids (IL) have a significant importance in many scientific fields including catalysis and electrocatalysis due to their special structural and physicochemical properties. Primarily, the effects of the confinement of ionic liquid (EmimOAc, 1-Ethyl-3-methylimidazolium acetate) into carbon pores have been investigated. The salt-templated porous carbons, which have different porosity (microporous and mesoporous) and nitrogen species, were used as model structures for the comparison of the IL confinement at different loadings. The nitrogen uptake of EmimOAc can be increased by about 10 times by the confinement in the pores of carbon materials compared to the bulk form. In addition, the most improved nitrogen absorption was observed by IL confinement in micropores and in nitrogen-doped carbon materials as a consequence of the maximized structural changes of IL. Furthermore, the possible use of such interfaces between EmimOAc and porous carbon for the catalytic activation of dinitrogen during the kinetically challenging NRR due to the limited gas absorption in the electrolyte, was examined. An electrocatalytic NRR system based on the conversion of water and nitrogen gas to ammonia at ambient operation conditions (1 bar, 25 °C) was performed in a setup under an applied electric potential with a single chamber electrochemical cell, which consists of the combination of EmimOAc electrolyte with the porous carbon-working electrode and without a traditional electrocatalyst. Under a potential of -3 V vs. SCE for 45 minutes, a NH3 production rate of 498.37 μg h-1 cm-2 and FE of 12.14\% were achieved. The experimental observations show that an electric double-layer, which serves the catalytically active area, occurs between a microporous carbon material and ions of the EmimOAc electrolyte in the presence of sufficiently high provided electric potential. Comparing with the typical NRR systems which have been reported in the literature, the presented electrochemical ammonia synthesis approach provides a significantly higher ammonia production rate with a chance to avoid the possible kinetic limitations of NRR. In terms of operating conditions, ammonia production rate and the faradic efficiency without the need for any synthetic electrocatalyst can be resulted of electrocatalytic activation of nitrogen in the double-layer formed between carbon and IL ions.}, language = {en} } @phdthesis{Cataldo2020, author = {Cataldo, Vincenzo Alessandro}, title = {Design and synthesis of alkylating ionic liquids and their application in synthesis, materials and proteomics}, school = {Universit{\"a}t Potsdam}, pages = {153}, year = {2020}, language = {en} } @phdthesis{Ilic2020, author = {Ilic, Ivan}, title = {Design of sustainable cathodes for Li-ion batteries}, doi = {10.25932/publishup-48368}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-483689}, school = {Universit{\"a}t Potsdam}, pages = {iv, 154}, year = {2020}, abstract = {In recent years people have realised non-renewability of our modern society which relays on spending huge amounts of energy mostly produced from fosil fuels, such as oil and coal, and the shift towards more sustainable energy sources has started. However, sustainable sources of energy, such as wind-, solar- and hydro-energy, produce primarily electrical energy and can not just be poured in canister like many fosil fuels, creating necessity for rechragable batteries. However, modern Li-ion batteries are made from toxic heavy metals and sustainable alternatives are needed. Here we show that naturally abundant catecholic and guaiacyl groups can be utilised to replace heavy metals in Li-ion batteries. Foremost vanillin, a naturally occurring food additive that can be sustainably synthesised from industrial biowaste, lignin, was utilised to synthesise materials that showed extraordinary performance as cathodes in Li-ion batteries. Furthermore, behaviour of catecholic and guiacyl groups in Li-ion system was compared, confirming usability of guiacayl containing biopolymers as cathodes in Li-ion batteries. Lastly, naturally occurring polyphenol, tannic acid, was incorporated in fully bioderived hybrid material that shows performance comparable to commercial Li-ion batteries and good stability. This thesis presents an important advancement in understanding of biowaste derived cathode materials for Li-ion batteries. Further research should be conducted to better understand behaviour of guaiacyl groups during Li-ion battery cycling. Lastly, challenges of incorporation of lignin, an industrial biowaste, have to be addressed and lignin should be incorporated as a cathode material in Li-ion batteries.}, language = {en} } @phdthesis{Cao2020, author = {Cao, Qian}, title = {Graphitic carbon nitride and polymer hybrid materials}, school = {Universit{\"a}t Potsdam}, pages = {132}, year = {2020}, abstract = {Advanced hybrid materials are recognized as one of the most significant enablers for new technologies, which holds true especially on the quest for sustainable energy sources and energy production schemes (e.g., semiconductor based photocatalytic materials). Usually, a single component is far from meeting all the demands needed for these advanced applications. Hybrid materials are composed of at least two components commonly an inorganic and an organic material on the molecular level, which feature novel properties exceeding the sum of the individual parts and might be the milestones of next-generation applications. This dissertation aims to provide novel combinations of the metal-free semiconductor graphitic carbon nitride (g-C3N4) with polymers to obtain materials with advanced properties and applications. Visible light constitutes the core of the present work as it is the only energy source utilized either in synthesis or in the application process. In the area of applications by combination of g-C3N4 and polymers, two different hybrids were thoroughly elucidated, i.e.. their design and construction as well as potential application in photocatalysis. Novel soft 3D liquid objects were formed via charge-interaction driven interfacial jamming between polyelectrolytes in aqueous environment and colloidal dispersions of g-C3N4 in edible sunflower oil. As such, stable liquid objects could be molded into specific shapes and utilized for photodegradation of organic dyes in water. Furthermore, the grafting of polymers onto g-C3N4 was investigated. Allyl-end functionalized polymers were grafted onto g-C3N4 by a photoinitiated process to yield g-C3N4 with versatile and improved properties, e.g. advanced dispersibility enabling processing via spin coating. As g-C3N4 produces radicals under visible light irradiation, which is of significant interest for polymer science, g-C3N4 containing polymer latex and macrogel beads (MGB) were synthesized by emulsion photopolymerization and inverse suspension photopolymerization, respectively. A well-controlled emulsion photopolymerization process via g-C3N4 initiation was designed, which features synthesis of well-defined and cross-linked polymer particles. Furthermore, the polymerization process was investigated thoroughly, indicating an ad-layer polymerization in early stages of the process. The utilization of functionalized g-C3N4 allowed the polymerization of various monomer types. Moreover, g-C3N4 was utilized as photoinitiator in hydrogel MGB formation. The formed MGB properties could be tailored via process design, e.g. stirring rate, cross-linker content and g-C3N4 content. Finally, MGBs were introduced as photocatalyst for waste water remediation, i.e. the degradation of Rhodamine B in aqueous solution was studied. The present thesis therefore builds a bridge between g-C3N4 and polymers and provides strategies for hybrid material formation. Furthermore, several potential applications are revealed with significant implications for photocatalysis, polymerization processes and polymer materials.}, language = {en} } @phdthesis{Markushyna2020, author = {Markushyna, Yevheniia}, title = {Modern photoredox transformations applied to the needs of organic synthesis}, doi = {10.25932/publishup-47766}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-477661}, school = {Universit{\"a}t Potsdam}, pages = {275}, year = {2020}, abstract = {Abstract. Catalysis is one of the most effective tools for the highly efficient assembly of complex molecular structures. Nevertheless, it is mainly represented by transition metal-based catalysts and typically is an energy consuming process. Therefore, photocatalysis utilizing solar energy is one of the appealing approaches to overcome these problems. A great alternative to classic transition metal-based photocatalysts, carbon nitrides, a group of organic polymeric semiconductors, have already shown their efficiency in water splitting, CO2 reduction, and organic pollutants degradation. However, these materials have also a great potential for the use in functionalization of complex organic molecules for synthetic needs as it was shown in recent years. This work addresses the challenge to develop efficient system for heterogeneous organic photocatalysis, employing cheap and environmentally benign photocatalysts - carbon nitrides. Herein, fundamental properties of semiconductors are studied from the organic chemistry standpoint; the inherent properties of carbon nitrides, such as ability to accumulate electrons, are deeply investigated and their effect on the reaction outcome is established. Thus, understanding of the electron charging processes allowed for the synthesis of otherwise hardly-achieved diazetidines-1,3 by tetramerization of benzylamines. Furthermore, the high electron capacity of Potassium Poly(heptazine imide)s (K-PHI) made possible a multi-electron reduction of aromatic nitro compounds to bare or formylated anilines. Additionally, two deep eutectic solvents (DES) were designed as a sustainable reaction media and reducing reagent for this reaction. Eventually, the high oxidation ability of carbon nitride K-PHI is employed in a challenging reaction of halide anion oxidation (Cl―, Br―) to accomplish electrophilic substitution in aromatic ring. The possibility to utilize NaCl solution (seawater mimetic) for the chlorination of electron rich arenes was shown. Eventually, light itself is used as a tool in a chromoselective photocatalytic oxidation of aromatic thiols and thioacetatas to three different compounds, using UV, blue, and red LEDs. All in all, the work enhances understanding the mechanism of heterogeneous photocatalysis in synthetic organic reactions and therefore, is a step forward to the sustainable methods of synthesis in organic chemistry.}, language = {en} } @phdthesis{Phung2020, author = {Phung, Thi Thuy Nga}, title = {Defect chemistry in halide perovskites}, doi = {10.25932/publishup-47652}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-476529}, school = {Universit{\"a}t Potsdam}, pages = {vi, 231}, year = {2020}, abstract = {Metallhalogenid-Perowskite haben sich aufgrund ihrer hervorragenden optoelektronischen Eigenschaften zu einer attraktiven Materialklasse f{\"u}r die Photovoltaikindustrie entwickelt. Die Langzeitstabilit{\"a}t ist jedoch noch immer ein Hindernis f{\"u}r die industrielle Realisierung dieser Materialklasse. Zunehmend zeigen sich Hinweise daf{\"u}r, dass intrinsische Defekte im Perowskit die Material-Degradation f{\"o}rdern. Das Verst{\"a}ndnis der Defekte im Perowskit ist wichtig, um seine Stabilit{\"a}t und optoelektronische Qualit{\"a}t weiter zu verbessern. Diese Dissertation konzentriert sich daher auf das Thema Defektchemie im Perowskit. Der erste Teil der Dissertation gibt einen kurzen {\"U}berblick {\"u}ber die Defekteigenschaften von Halogenid-Perowskiten. Anschließend zeigt der zweite Teil, dass das Dotieren von Methylammoniumbleiiodid mit einer kleinen Menge von Erdalkalimetallen (Sr und Mg) ein h{\"o}herwertiges, weniger fehlerhaftes Material erzeugt, was zu hohen Leerlaufspannungen sowohl in der n-i-p als auch in der p-i-n Architektur von Solarzellen f{\"u}hrt. Es wurde beobachtet, dass die Dotierung in zwei Dom{\"a}nen stattfindet: eine niedrige Dotierungskonzentration f{\"u}hrt zum Einschluss der entsprechenden Elemente in das Kristallgitter erm{\"o}glicht, w{\"a}hrend eine hohe Dotierungskonzentration zu einer Phasentrennung f{\"u}hrt. Das Material kann im Niedrigdotierungsbereich mehr n-dotiert sein, w{\"a}hrend es im Hochdotierungsbereich weniger n-dotiert ist. Die Schwelle dieser beiden Regime h{\"a}ngt von der Atomgr{\"o}ße der Dotierelemente ab. Der n{\"a}chste Teil der Dissertation untersucht die photoinduzierte Degradation von Methylammonium-Bleiiodid. Dieser Abbaumechanismus h{\"a}ngt eng mit der Bildung und Migration von defekten zusammen. Nach der Bildung k{\"o}nnen sich diese in Abh{\"a}ngigkeit von der Defektdichte und ihrer Verteilung bewegen. Demnach kann eine hohe Defektdichte wie an den Korngrenzen eines Perowskitfilms die Beweglichkeit von ionischen Punktdefekten hemmen. Diese Erkenntnis ließe sich auf das zuk{\"u}nftige Materialdesign in der Photovoltaikindustrie anwenden, da die Perowskit-Solarzellen normalerweise einen polykristallinen D{\"u}nnfilm mit hoher Korngrenzendichte verwenden. Die abschließende Studie, die in dieser Dissertation vorgestellt wird, konzentriert sich auf die Stabilit{\"a}t der neuesten „dreifach-kationen" Perowskit-basierten Solarzellen unter dem Einfluss einer permanent angelegten elektrischen Spannung. Eine l{\"a}ngere Betriebsdauer (mehr als drei Stunden permanente Spannung) f{\"o}rdert die Amorphisierung im Halogenid-Perowskiten. Es wird hierbei vermutet, dass sich eine amorphe Phase an den Grenzfl{\"a}chen bildet, insbesondere zwischen der lochselektiven Schicht und dem Perowskit. Diese amorphe Phase hemmt den Ladungstransport und beeintr{\"a}chtigt die Leistung der Perowskit-Solarzelle erheblich. Sobald jedoch keine Spannung mehr anliegt k{\"o}nnen sich die Perowskitschichten im Dunkeln bereits nach einer kurzen Pause regenerieren. Die Amorphisierung wird auf die Migration von ionischen Fehlordnungen zur{\"u}ckgef{\"u}hrt, h{\"o}chstwahrscheinlich auf die Migration von Halogeniden. Dieser Ansatz zeigt ein neues Verst{\"a}ndnis des Abbau-Mechanismus in Perowskit-Solarzellen unter Betriebsbedingungen.}, language = {en} } @phdthesis{LopezdeGuerenu2020, author = {L{\´o}pez de Guere{\~n}u, Anna}, title = {Tm3+-doped NaYF4 nanoparticles}, doi = {10.25932/publishup-47559}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-475593}, school = {Universit{\"a}t Potsdam}, pages = {119}, year = {2020}, abstract = {Lately, the integration of upconverting nanoparticles (UCNP) in industrial, biomedical and scientific applications has been increasingly accelerating, owing to the exceptional photophysical properties that UCNP offer. Some of the most promising applications lie in the field of medicine and bioimaging due to such advantages as, among others, deeper tissue penetration, reduced optical background, possibility for multicolor imaging, and lower toxicity, compared to many known luminophores. However, some questions regarding not only the fundamental photophysical processes, but also the interaction of the UCNP with other luminescent reporters frequently used for bioimaging and the interaction with biological media remain unanswered. These issues were the primary motivation for the presented work. This PhD thesis investigated several aspects of various properties and possibilities for bioapplications of Yb3+,Tm3+-doped NaYF4 upconverting nanoparticles. First, the effect of Gd3+ doping on the structure and upconverting behaviour of the nanocrystals was assessed. The ageing process of the UCNP in cyclohexane was studied over 24 months on the samples with different Gd3+ doping concentrations. Structural information was gathered by means of X-ray diffraction (XRD), transmission electron microscopy (TEM), dynamic light scattering (DLS), and discussed in relation to spectroscopic results, obtained through multiparameter upconversion luminescence studies at various temperatures (from 4 K to 295 K). Time-resolved and steady-state emission spectra recorded over this ample temperature range allowed for a deeper understanding of photophysical processes and their dependence on structural changes of UCNP. A new protocol using a commercially available high boiling solvent allowed for faster and more controlled production of very small and homogeneous UCNP with better photophysical properties, and the advantages of a passivating NaYF4 shell were shown. F{\"o}rster resonance energy transfer (FRET) between four different species of NaYF4: Yb3+, Tm3+ UCNP (synthesized using the improved protocol) and a small organic dye was studied. The influence of UCNP composition and the proximity of Tm3+ ions (donors in the process of FRET) to acceptor dye molecules have been assessed. The brightest upconversion luminescence was observed in the UCNP with a protective inert shell. UCNP with Tm3+ ions only in the shell were the least bright, but showed the most efficient energy transfer. In the final part, two surface modification strategies were applied to make UCNP soluble in water, which simultaneously allowed for linking them via a non-toxic copper-free click reaction to the liposomes, which served as models for further cell experiments. The results were assessed on a confocal microscope system, which was made possible by lesser known downshifting properties of Yb3+, Tm3+-doped UCNP. Preliminary antibody-staining tests using two primary and one dye-labelled secondary antibodies were performed on MDCK-II cells.}, language = {en} } @phdthesis{Kaergell2020, author = {K{\"a}rgell, Martin}, title = {Layer formation from perovskite nanoparticles with tunable optical and electronic properties}, doi = {10.25932/publishup-47566}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-475667}, school = {Universit{\"a}t Potsdam}, pages = {ix, 233}, year = {2020}, abstract = {Hybrid organic-inorganic perovskites have attracted attention in recent years, caused by the incomparable increase in efficiency in energy convergence, which implies the application as an absorber material for solar cells. A disadvantage of these materials is, among others, the instability to moisture and UV-radiation. One possible solution for these problems is the reduction of the size towards the nano world. With that nanosized perovskites are showing superior stability in comparison to e.g. perovskite layers. Additionally to this the nanosize even enables stable perovskite structures, which could not be achieved otherwise at room temperature. This thesis is separated into two major parts. The separation is done by the composition and the band gap of the material and at the same time the shape and size of the nanoparticles. Here the division is made by the methylammonium lead tribromide nanoplatelets and the caesium lead triiodide nanocubes. The first part is focusing on the hybrid organic-inorganic perovskite (methylammonium lead tribromide) nanoplatelets with a band gap of 2.35 eV and their thermal behaviour. Due to the challenging character of this material, several analysis methods are used to investigate the sub nano and nanostructures under the influence of temperature. As a result, a shift of phase-transition temperatures towards higher temperatures is observed. This unusual behaviour can be explained by the ligand, which is incorporated in the perovskite outer structure and adds phase-stability into the system. The second part of this thesis is focusing on the inorganic caesium lead triiodide nanocubes with a band gap of 1.83 eV. These nanocrystals are first investigated and compared by TEM, XRD and other optical methods. Within these methods, a cuboid and orthorhombic structure are revealed instead of the in literature described cubic shape and structure. Furthermore, these cuboids are investigated towards their self-assembly on a substrate. Here a high degree in self-assembly is shown. As a next step, the ligands of the nanocuboids are exchanged against other ligands to increase the charge carrier mobility. This is further investigated by the above-mentioned methods. The last section is dealing with the enhancement of the CsPbI3 structure, by incorporating potassium in the crystal structure. The results are suggesting here an increase in stability.}, language = {en} } @phdthesis{Knauf2020, author = {Knauf, Jan}, title = {Synthesis of highly fluorinated precursors and their deposition conditions for self-assembled monolayers with defined small-scale surface structures as templates for the manipulation of wetting behavior}, doi = {10.25932/publishup-47380}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-473804}, school = {Universit{\"a}t Potsdam}, pages = {X, 204}, year = {2020}, abstract = {"How Wenzel and Cassie were wrong" - this was the eye-catching title of an article published by Lichao Gao and Thomas McCarthy in 2007, in which fundamental interpretations of wetting behavior were put into question. The authors initiated a discussion on a subject, which had been generally accepted a long time ago and they showed that wetting phenomena were not as fully understood as imagined. Similarly, this thesis tries to put a focus on certain aspects of liquid wetting, which so far have been widely neglected in terms of interpretation and experimental proof. While the effect of surface roughness on the macroscopically observed wetting behavior is commonly and reliably interpreted according to the well-known models of Wenzel and Cassie/Baxter, the size-scale of the structures responsible for the surface's rough texture has not been of further interest. Analogously, the limits of these models have not been described and exploited. Thus, the question arises, what will happen when the size of surface structures is reduced to the size of the contacting liquid molecules itself? Are common methods still valid or can deviations from macroscopic behavior be observed? This thesis wants to create a starting point regarding these questions. In order to investigate the effect of smallest-scale surface structures on liquid wetting, a suitable model system is developed by means of self-assembled monolayer (SAM) formation from (fluoro)organic thiols of differing lengths of the alkyl chain. Surface topographies are created which rely on size differences of several {\AA}ngstr{\"o}ms and exhibit surprising wetting behavior depending on the choice of the individual precursor system. Thus, contact angles are experimentally detected, which deviate considerably from theoretical calculations based on Wenzel and Cassie/Baxter models and confirm that sub-nm surface topographies affect wetting. Moreover, experimentally determined wetting properties are found to correlate well to an assumed scale-dependent surface tension of the contacting liquid. This behavior has already been described for scattering experiments taking into account capillary waves on the liquid surface induced by temperature and had been predicted earlier by theoretical calculations. However, the investigation of model surfaces requires the provision of suitable precursor molecules, which are not commercially available and opens up a door to the exotic chemistry of fluoro-organic materials. During the course of this work, the synthesis of long-chain precursors is examined with a particular focus put on oligomerically pure semi-fluorinated n-alkyl thiols and n-alkyl trichlorosilanes. For this, general protocols for the syntheses of the desired compounds are developed and product mixtures are assayed to be separated into fractions of individual chain lengths by fluorous-phase high-performance liquid chromatography (F-HPLC). The transition from model systems to technically more relevant surfaces and applications is initiated through the deposition of SAMs from long-chain fluorinated n-alkyl trichlorosilanes. Depositions are accomplished by a vapor-phase deposition process conducted on a pilot-scale set-up, which enables the exact control of relevant process parameters. Thus, the influence of varying deposition conditions on the properties of the final coating is examined and analyzed for the most important parameters. The strongest effect is observed for the partial pressure of reactive water vapor, which directly controls the extent of precursor hydrolysis during the deposition process. Experimental results propose that the formation of ordered monolayers rely on the amount of hydrolyzed silanol species present in the deposition system irrespective of the exact grade of hydrolysis. However, at increased amounts of species which are able to form cross-linked molecules due to condensation reactions, films deteriorate in quality. This effect is assumed to be caused by the introduction of defects within the film and the adsorption of cross linked agglomerates. Deposition conditions are also investigated for chain extended precursor species and reveal distinct differences caused by chain elongation.}, language = {en} } @phdthesis{CerdaDonate2020, author = {Cerd{\´a} Do{\~n}ate, Elisa}, title = {Microfluidics for the study of magnetotactic bacteria towards single-cell analysis}, school = {Universit{\"a}t Potsdam}, pages = {X, 92}, year = {2020}, abstract = {Magnetotactic bacteria comprise a heterogeneous group of Gram negative bacteria which share the ability to synthesise intracellular magnetic nanoparticles surrounded by a lipid bilayer, known as magnetosomes, which are arranged in linear chains. The bacteria exert a unique level of control onto the biomineralization of these nanoparticles, which is seen in the controlled size and shape they have. These characteristics have attracted great attention on understanding the process by which the bacteria synthesise the magnetosomes. Moreover, the magnetosome chain impart the bacteria with a net magnetic dipole which makes them susceptible to interact with magnetic fields and thus orient with the Earth's magnetic field. This feature has attracted as well much interest to understand how the swimming motility of these microorganisms is affected by the presence of magnetic fields. Most of the studies performed in these bacteria so far have been conducted in the traditional manner using large populations of cells. Such studies have the disadvantage of averaging many different individuals with heterogeneous behaviours and fail to consider individual variations. In addition, in large populations each bacterium will be subjected to a different microenvironment that will influence the bacterial behaviour, but which cannot be defined using these traditional methods. In this thesis, different microfluidic platforms are proposed to overcome these limitations and to offer the possibility to study magnetotactic bacteria in defined environments and down to a single-cell resolution. First, a sediment-like microfluidic platform is presented with the purpose of mimicking the porous environment they bacteria naturally dwell in. The platform allows to observe via transmitted light microscopy that bacterial navigation in crowded environments is enhanced by the Earth's magnetic field strengths (B = 50 μT) rather than by null (B = 0 μT) or higher magnetic fields (B = 500 μT). Second, a microfluidic system to confine single-bacterial cells in physically defined environments is presented. The system allows to study via transmitted light microscopy the interplay between wall curvature, magnetic fields and bacterial speed affect the motion of a confined bacterium, and shows how bacterial trajectories depend on those three parameters. Third, a microfluidic platform to conduct semi in vivo magnetosome nucleation with a single-cell resolution via X-ray fluorescence is fabricated. It is shown that signal arising from magnetosome full chains can be observed individually in each bacterium. Finally, the iron uptake kinetics of a single bacterium are studied via a fluorescent reporter through confocal microscopy. Two different approaches are used for this: one of the previously mentioned platforms, as well as giant lipid vesicles. It is observed how iron uptake rates vary between cells, as well as how these rates are consistent with magnetosome formation taking place within some hours. The present thesis shows therefore how microfluidic technologies can be implemented for the study of magnetotactic bacteria at different degrees, and the level of resolution that can be attained by going into the single- cell scale.
}, language = {en} } @phdthesis{Kuhrts, author = {Kuhrts, Lucas}, title = {The effect of Polycations on the Formation of Magnetite Nanoparticles}, address = {Potsdam}, school = {Universit{\"a}t Potsdam}, pages = {VIII, 99}, abstract = {Nanoparticles of magnetite (Fe3O4) are envisioned to find used in diverse applications, ranging from magnetic data storage, inks, ferrofluids as well as in magnetic resonance imaging, drug delivery, and hyperthermia cancer treatment. Their magnetic properties strongly depend on their size and morphology, two properties that can be synthetically controlled. Achieving appropriate control under soft chemical conditions has so far remained a challenging endeavor. One proven way of exerting this desired control has been using a biomimetic approach that emulates the proteome of magnetotactic bacteria by adding poly-L-arginine in the co- precipitation of ferrous and ferric chloride. The objective of the work presented here is to understand the impact of this polycation on the formation mechanism of magnetite and, through rational design, to enhance the control we can exert on magnetite nanoparticle size and morphology. We developed a SAXS setup to temporally and structurally resolve the formation of magnetite in the presence of poly-L-arginine in situ. Using analytical scattering models, we were able to separate the scattering contribution of a low-density 5 nm iron structure from the contribution of the growing nanoparticles. We identified that the low-density iron structure is a metastable precursor to the magnetite particles and that it is electrostatically stabilized by poly-L-arginine. In a process analogous to biomineralization, the presence of the charged macromolecule thus shifts the reaction mechanism from a thermodynamically controlled one to a kinetically controlled one. We identify this shift in reactions mechanism as the cornerstone of the proposed mechanism and as the crucial step in the paradigm of this extraordinary nanoparticle morphology and size control. Based on SAXS data, theoretical considerations suggest that an observed morphological transition between spherical, solid, and sub-structured mesocrystalline magnetite nanoparticles is induced through a pH-driven change in the wettability of the nanoparticle surface. With these results, we further demonstrate that SAXS can be an invaluable tool for investigating nanoparticle formation. We were able to change particle morphology from spherically solid particles to sub-structured mesocrystals merely by changing the precipitation pH. Improving the synthesis sustainability by substituting poly-L-arginine with renewable, polysaccharide-based polycations produced at the metric ton scale, we demonstrated that the ability to alter the reaction mechanism of magnetite can be generically attributed to the presence of polycations. Through meticulous analysis and the understanding of the formation mechanism, we were able to exert precise control over particle size and morphology, by adapting crucial synthesis parameters. We were thus able to grow mesocrystals up to 200 nm and solid nanocrystals of 100 nm by adding virtually any strong polycation. We further found a way to produce stable single domain magnetite at only slightly increased alkalinity, as magnetotactic bacteria do it. Thus through the understanding of the biological system, the consecutive biomimetic synthesis of magnetite and the following understanding of the mechanism involved in the in vitro synthesis, we managed to improve the synthetic control over the co-precipitation of magnetite, coming close biomineralization of magnetite in magnetotactic bacteria. Polyanions, in both natural as well as in synthetic systems, have been in the spotlight of recent research, yet our work shows the pivotal influence polycations have on the nucleation of magnetite. This work will contribute significantly to our ability to tailor magnetite nanoparticle size and morphology; in addition, we presume it will provide us with a model system for studying biomineralization of magnetite in vitro, putting the spotlight on the important influence of polycations, which have not had the scientific attention they deserve.}, language = {en} } @phdthesis{Melani2019, author = {Melani, Giacomo}, title = {From structural fluctuations to vibrational spectroscopy of adsorbates on surfaces}, doi = {10.25932/publishup-44182}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-441826}, school = {Universit{\"a}t Potsdam}, pages = {119}, year = {2019}, abstract = {Aluminum oxide is an Earth-abundant geological material, and its interaction with water is of crucial importance for geochemical and environmental processes. Some aluminum oxide surfaces are also known to be useful in heterogeneous catalysis, while the surface chemistry of aqueous oxide interfaces determines the corrosion, growth and dissolution of such materials. In this doctoral work, we looked mainly at the (0001) surface of α-Al 2 O 3 and its reactivity towards water. In particular, a great focus of this work is dedicated to simulate and address the vibrational spectra of water adsorbed on the α-alumina(0001) surface in various conditions and at different coverages. In fact, the main source of comparison and inspiration for this work comes from the collaboration with the "Interfacial Molecular Spectroscopy" group led by Dr. R. Kramer Campen at the Fritz-Haber Institute of the MPG in Berlin. The expertise of our project partners in surface-sensitive Vibrational Sum Frequency (VSF) generation spectroscopy was crucial to develop and adapt specific simulation schemes used in this work. Methodologically, the main approach employed in this thesis is Ab Initio Molecular Dynamics (AIMD) based on periodic Density Functional Theory (DFT) using the PBE functional with D2 dispersion correction. The analysis of vibrational frequencies from both a static and a dynamic, finite-temperature perspective offers the ability to investigate the water / aluminum oxide interface in close connection to experiment. The first project presented in this work considers the characterization of dissociatively adsorbed deuterated water on the Al-terminated (0001) surface. This particular structure is known from both experiment and theory to be the thermodynamically most stable surface termination of α-alumina in Ultra-High Vacuum (UHV) conditions. Based on experiments performed by our colleagues at FHI, different adsorption sites and products have been proposed and identified for D 2 O. While previous theoretical investigations only looked at vibrational frequencies of dissociated OD groups by staticNormal Modes Analysis (NMA), we rather employed a more sophisticated approach to directly assess vibrational spectra (like IR and VSF) at finite temperature from AIMD. In this work, we have employed a recent implementation which makes use of velocity-velocity autocorrelation functions to simulate such spectral responses of O-H(D) bonds. This approach allows for an efficient and qualitatively accurate estimation of Vibrational Densities of States (VDOS) as well as IR and VSF spectra, which are then tested against experimental spectra from our collaborators. In order to extend previous work on unimolecularly dissociated water on α-Al 2 O 3 , we then considered a different system, namely, a fully hydroxylated (0001) surface, which results from the reconstruction of the UHV-stable Al-terminated surface at high water contents. This model is then further extended by considering a hydroxylated surface with additional water molecules, forming a two-dimensional layer which serves as a potential template to simulate an aqueous interface in environmental conditions. Again, employing finite-temperature AIMD trajectories at the PBE+D2 level, we investigated the behaviour of both hydroxylated surface (HS) and the water-covered structure derived from it (known as HS+2ML). A full range of spectra, from VDOS to IR and VSF, is then calculated using the same methodology, as described above. This is the main focus of the second project, reported in Chapter 5. In this case, comparison between theoretical spectra and experimental data is definitely good. In particular, we underline the nature of high-frequency resonances observed above 3700 cm -1 in VSF experiments to be associated with surface OH-groups, known as "aluminols" which are a key fingerprint of the fully hydroxylated surface. In the third and last project, which is presented in Chapter 6, the extension of VSF spectroscopy experiments to the time-resolved regime offered us the opportunity to investigate vibrational energy relaxation at the α-alumina / water interface. Specifically, using again DFT-based AIMD simulations, we simulated vibrational lifetimes for surface aluminols as experimentally detected via pump-probe VSF. We considered the water-covered HS model as a potential candidate to address this problem. The vibrational (IR) excitation and subsequent relaxation is performed by means of a non-equilibrium molecular dynamics scheme. In such a scheme, we specifically looked at the O-H stretching mode of surface aluminols. Afterwards, the analysis of non-equilibrium trajectories allows for an estimation of relaxation times in the order of 2-4 ps which are in overall agreement with measured ones. The aim of this work has been to provide, within a consistent theoretical framework, a better understanding of vibrational spectroscopy and dynamics for water on the α-alumina(0001) surface,ranging from very low water coverage (similar to the UHV case) up to medium-high coverages, resembling the hydroxylated oxide in environmental moist conditions.}, language = {en} } @phdthesis{Lehmann2020, author = {Lehmann, Frederike Felizia}, title = {Solubility limits and phase stabilizing effects of mixed hybrid perovskites}, school = {Universit{\"a}t Potsdam}, year = {2020}, abstract = {In recent years the development of renewable energy sources attracted much attention due to the increasing environmental pollution induced by burning fossil fuels. The growing public interest in reducing greenhouse gases and the use of pollution-free energies (bio-mass-, geothermal-, solar-, water- or wind energy) paved the way for scientific research in renewable energies. [1] Solar energy provides unlimited access and offers high applicational flexibility, which is needed for energy consumption in a modern society. The scientific interest in photovoltaics (PV) nowadays focuses on discovering new materials and improving materials properties, aiming for the production of highly efficient solar cells. Lately, a new type of absorber material based on the perovskite type structure reached power conversion efficiencies of more than 24\%. [2] By varying the chemical composition the electronic properties as e.g. the band gap energy can be tuned to increase the absorption range of this absorber material. This makes them in particular attractive for use in tandem solar cells, where silicon and perovskite absorber layers are combined to absorb a large range of the vible light (28.0\% efficiency). [2] However, perovskite based solar cells not only suffer from fast degradation when exposed to humidity, but also from the use of toxic elements (e.g. lead), which can result in long-term environmental damage. Therefore, the aim of this study was to determine the fundamental structural and optoelectronical properties of highly interesting hybrid perovskite materials, the MAPbX3 solid solution (MA=CH3NH3; X=I,Br,Cl) and the triple cation (FA1-xMAx)1-yCsyPbI3 solid solution (FA=HC(NH2)2). The study was performed on powder samples by using X-ray diffraction, revealing the crystal structure and solubility behavior of all solid solutions. Moreover the temperature-dependent behavior was studied using in-situ high resolution synchrotron X-ray diffraction and combinatorial thermal analysis methods. The influence of compositional changes on the band gap energy variation were observed using spectroscopic methods as photoluminescence and diffuse reflectance spectroscopy. The obtained results have shown that for the MAPb(I1-xBrx)3 solid solution a large miscibility gap in the range of 0.29 ( ± 0.02) ≤ x ≤ 0.92 ( ± 0.02) is present. This miscibility gap limits the suitable compositional range for use in thin film solar cells of mixed halide compounds. From the temperature-dependent in-situ synchrotron X-ray diffraction studies the complete T-X-phase diagram was established. Studies on the MAPb(Cl1-xBrx)3 solid solution revealed that MAPb(Cl1-xBrx)3 forms a complete solid solution series. For the triple cation (FA1-xMAx)1-yCsyPbI3 solid solution the aim was to study the formation of the d-modification in FAPbI3, which is undesired for solar cell application. This can be overcome by stabilizing the favored high temperature cubic a-modification at ambient conditions. By partial substituting the formamidinium molecule by methylammonium and cesium the stabilization of the cubic modification was successful. The solubility limit of FA1-xCsxPbI3 solid solution was determined to be x=0.1, while a full miscibility was observed for the FA1-xMAxPbI3 solid solution. For the triple cation (FA1-xMAx)1-yCsyPbI3 solid solution a solubility limit of cesium was observed to be y=0.1. The optoelectronic properties were investigated, revealing a linear change of band gap energy with chemical composition. It is demonstrated that the stabilized triple cation compound with cubic perovskite-type crystal structure shows enhanced stability of approximately six months. Furthermore, a short insight into lead-free perovskite-type materials is given, using germanium as non-toxic alternative to lead. For germanium based perovskites a fast decomposition in air was observed, due to the preferred formation of GeI4 in oxygen atmosphere. In-situ low temperature synchrotron X-ray diffraction measurements revealed a yet unknown low temperature modification of MAGeI3. [1] WESSELAK, Viktor; SCHABBACH, Thomas; LINK, Thomas; FISCHER, Joachim: Handbuch Regenerative Energietechnik. Springer, 2017 [2] NREL: Best Research-Cell Efficiencies. https://www.nrel.gov/pv/assets/pdfs/best-research-cell-efficiencies-190416.pdf. - 25.04.2019}, language = {en} } @phdthesis{CruzLemus2020, author = {Cruz Lemus, Saul Daniel}, title = {Enhancing Efficiency of Inverted Perovskite Solar Cells}, school = {Universit{\"a}t Potsdam}, pages = {117}, year = {2020}, abstract = {Carbon nitride and poly(ionic liquid)s (PILs) have been successfully applied in various fields of materials science owing to their outstanding properties. This thesis aims at the successful application of these polymers as innovative materials in the interfaces of hybrid organic-inorganic perovskite solar cells. A critical problem in harnessing the full thermodynamic potential of halide perovskites in solar cells is the design and modification of interfaces to reduce carrier recombination. Therefore, the interface must be properly studied and improved. This work investigated the effect of applying carbon nitride and PILs on a perovskite surface on the device performance. The facile synthetic method for modifying carbon nitride with vinyl thiazole and barbituric acid (CMB-vTA) yields 2.3 nm layers when solution processing is performed using isopropanol. The nanosheets were applied as a metal-free electron transport layer in inverted perovskite solar cells. The application of carbon nitride layers (CMB-vTA) resulted in negligible current-voltage hysteresis with a high open circuit voltage (Voc) of 1.1 V and a short-circuit current (Jsc) of 20.28 mA cm-2, which afforded efficiencies of up to 17\%. Thus, the successful implementation of a carbon nitride-based structure enabled good charge extraction with minimized interface recombination between the perovskite and PCBM. Similarly, PILs represent a new strategy of interfacial modification using an ionic polymer in an n-i-p perovskite architecture.. The application of PILs as an interfacial modifier resulted in solar cell devices with an extraordinarily high efficiency of 21.8\% and a Voc of 1.17 V. The implementation reduced non-radiative recombination at the perovskite surface through defect passivation. Finally, our work proposes a novel method to efficiently suppress non-radiative charge recombination using the unexplored properties of carbon nitride and PILs in the solar cell field. Additionally, the method for interfacial modification has general applicability because of the simplicity of the post-treatment approach, and therefore has potential applicability in other solar cells. Thus, this work opens the door to a new class of materials to be implemented.}, language = {en} } @phdthesis{Vranic2019, author = {Vranic, Marija}, title = {3D Structure of the biomarker hepcidin-25 in its native state}, doi = {10.25932/publishup-45929}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-459295}, school = {Universit{\"a}t Potsdam}, pages = {xii, 135}, year = {2019}, abstract = {Hepcidin-25 (Hep-25) plays a crucial role in the control of iron homeostasis. Since the dysfunction of the hepcidin pathway leads to multiple diseases as a result of iron imbalance, hepcidin represents a potential target for the diagnosis and treatment of disorders of iron metabolism. Despite intense research in the last decade targeted at developing a selective immunoassay for iron disorder diagnosis and treatment and better understanding the ferroportin-hepcidin interaction, questions remain. The key to resolving these underlying questions is acquiring exact knowledge of the 3D structure of native Hep-25. Since it was determined that the N-terminus, which is responsible for the bioactivity of Hep-25, contains a small Cu(II)-binding site known as the ATCUN motif, it was assumed that the Hep-25-Cu(II) complex is the native, bioactive form of the hepcidin. This structure has thus far not been elucidated in detail. Owing to the lack of structural information on metal-bound Hep-25, little is known about its possible biological role in iron metabolism. Therefore, this work is focused on structurally characterizing the metal-bound Hep-25 by NMR spectroscopy and molecular dynamics simulations. For the present work, a protocol was developed to prepare and purify properly folded Hep-25 in high quantities. In order to overcome the low solubility of Hep-25 at neutral pH, we introduced the C-terminal DEDEDE solubility tag. The metal binding was investigated through a series of NMR spectroscopic experiments to identify the most affected amino acids that mediate metal coordination. Based on the obtained NMR data, a structural calculation was performed in order to generate a model structure of the Hep-25-Ni(II) complex. The DEDEDE tag was excluded from the structural calculation due to a lack of NMR restraints. The dynamic nature and fast exchange of some of the amide protons with solvent reduced the overall number of NMR restraints needed for a high-quality structure. The NMR data revealed that the 20 Cterminal Hep-25 amino acids experienced no significant conformational changes, compared to published results, as a result of a pH change from pH 3 to pH 7 and metal binding. A 3D model of the Hep-25-Ni(II) complex was constructed from NMR data recorded for the hexapeptideNi(II) complex and Hep-25-DEDEDE-Ni(II) complex in combination with the fixed conformation of 19 C-terminal amino acids. The NMR data of the Hep-25-DEDEDE-Ni(II) complex indicates that the ATCUN motif moves independently from the rest of the structure. The 3D model structure of the metal-bound Hep-25 allows for future works to elucidate hepcidin's interaction with its receptor ferroportin and should serve as a starting point for the development of antibodies with improved selectivity.}, language = {en} } @phdthesis{Latza2020, author = {Latza, Victoria Maria}, title = {Interactions involving lipid-based surfaces}, doi = {10.25932/publishup-44559}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-445593}, school = {Universit{\"a}t Potsdam}, pages = {217}, year = {2020}, abstract = {Interactions involving biological interfaces such as lipid-based membranes are of paramount importance for all life processes. The same also applies to artificial interfaces to which biological matter is exposed, for example the surfaces of drug delivery systems or implants. This thesis deals with the two main types of interface interactions, namely (i) interactions between a single interface and the molecular components of the surrounding aqueous medium and (ii) interactions between two interfaces. Each type is investigated with regard to an important scientific problem in the fields of biotechnology and biology: 1.) The adsorption of proteins to surfaces functionalized with hydrophilic polymer brushes; a process of great biomedical relevance in context with harmful foreign-body-response to implants and drug delivery systems. 2.) The influence of glycolipids on the interaction between lipid membranes; a hitherto largely unexplored phenomenon with potentially great biological relevance. Both problems are addressed with the help of (quasi-)planar, lipid-based model surfaces in combination with x-ray and neutron scattering techniques which yield detailed structural insights into the interaction processes. Regarding the adsorption of proteins to brush-functionalized surfaces, the first scenario considered is the exposure of the surfaces to human blood serum containing a multitude of protein species. Significant blood protein adsorption was observed despite the functionalization, which is commonly believed to act as a protein repellent. The adsorption consists of two distinct modes, namely strong adsorption to the brush grafting surface and weak adsorption to the brush itself. The second aspect investigated was the fate of the brush-functionalized surfaces when exposed to aqueous media containing immune proteins (antibodies) against the brush polymer, an emerging problem in current biomedical applications. To this end, it was found that antibody binding cannot be prevented by variation of the brush grafting density or the polymer length. This result motivates the search for alternative, strictly non-antigenic brush chemistries. With respect to the influence of glycolipids on the interaction between lipid membranes, this thesis focused on the glycolipids' ability to crosslink and thereby to tightly attract adjacent membranes. This adherence is due to preferential saccharide-saccharide interactions occurring among the glycolipid headgroups. This phenomenon had previously been described for lipids with special oligo-saccharide motifs. Here, it was investigated how common this phenomenon is among glycolipids with a variety of more abundant saccharide-headgroups. It was found that glycolipid-induced membrane crosslinking is equally observed for some of these abundant glycolipid types, strongly suggesting that this under-explored phenomenon is potentially of great biological relevance.}, language = {en} } @phdthesis{Giusto2020, author = {Giusto, Paolo}, title = {Chemical vapor deposition of carbon-based thin films}, school = {Universit{\"a}t Potsdam}, pages = {165}, year = {2020}, language = {en} } @phdthesis{Qin2019, author = {Qin, Qing}, title = {Chemical functionalization of porous carbon-based materials to enable novel modes for efficient electrochemical N2 fixation}, doi = {10.25932/publishup-44339}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-443397}, school = {Universit{\"a}t Potsdam}, pages = {146}, year = {2019}, abstract = {The central motivation of the thesis was to provide possible solutions and concepts to improve the performance (e.g. activity and selectivity) of electrochemical N2 reduction reaction (NRR). Given that porous carbon-based materials usually exhibit a broad range of structural properties, they could be promising NRR catalysts. Therefore, the advanced design of novel porous carbon-based materials and the investigation of their application in electrocatalytic NRR including the particular reaction mechanisms are the most crucial points to be addressed. In this regard, three main topics were investigated. All of them are related to the functionalization of porous carbon for electrochemical NRR or other electrocatalytic reactions. In chapter 3, a novel C-TixOy/C nanocomposite has been described that has been obtained via simple pyrolysis of MIL-125(Ti). A novel mode for N2 activation is achieved by doping carbon atoms from nearby porous carbon into the anion lattice of TixOy. By comparing the NRR performance of M-Ts and by carrying out DFT calculations, it is found that the existence of (O-)Ti-C bonds in C-doped TixOy can largely improve the ability to activate and reduce N2 as compared to unoccupied OVs in TiO2. The strategy of rationally doping heteroatoms into the anion lattice of transition metal oxides to create active centers may open many new opportunities beyond the use of noble metal-based catalysts also for other reactions that require the activation of small molecules as well. In chapter 4, a novel catalyst construction composed of Au single atoms decorated on the surface of NDPCs was reported. The introduction of Au single atoms leads to active reaction sites, which are stabilized by the N species present in NDPCs. Thus, the interaction within as-prepared AuSAs-NDPCs catalysts enabled promising performance for electrochemical NRR. For the reaction mechanism, Au single sites and N or C species can act as Frustrated Lewis pairs (FLPs) to enhance the electron donation and back-donation process to activate N2 molecules. This work provides new opportunities for catalyst design in order to achieve efficient N2 fixation at ambient conditions by utilizing recycled electric energy. The last topic described in chapter 5 mainly focused on the synthesis of dual heteroatom-doped porous carbon from simple precursors. The introduction of N and B heteroatoms leads to the construction of N-B motives and Frustrated Lewis pairs in a microporous architecture which is also rich in point defects. This can improve the strength of adsorption of different reactants (N2 and HMF) and thus their activation. As a result, BNC-2 exhibits a desirable electrochemical NRR and HMF oxidation performance. Gas adsorption experiments have been used as a simple tool to elucidate the relationship between the structure and catalytic activity. This work provides novel and deep insights into the rational design and the origin of activity in metal-free electrocatalysts and enables a physically viable discussion of the active motives, as well as the search for their further applications. Throughout this thesis, the ubiquitous problems of low selectivity and activity of electrochemical NRR are tackled by designing porous carbon-based catalysts with high efficiency and exploring their catalytic mechanisms. The structure-performance relationships and mechanisms of activation of the relatively inert N2 molecules are revealed by either experimental results or DFT calculations. These fundamental understandings pave way for a future optimal design and targeted promotion of NRR catalysts with porous carbon-based structure, as well as study of new N2 activation modes.}, language = {en} } @phdthesis{Wang2019, author = {Wang, Xuepu}, title = {Polydimethylsiloxane wrinkles for surface patterns and assembly of metallic nanoparticles}, school = {Universit{\"a}t Potsdam}, pages = {131}, year = {2019}, language = {en} } @phdthesis{Debsharma2019, author = {Debsharma, Tapas}, title = {Cellulose derived polymers}, doi = {10.25932/publishup-44131}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-441312}, school = {Universit{\"a}t Potsdam}, pages = {x, 103}, year = {2019}, abstract = {Plastics, such as polyethylene, polypropylene, and polyethylene terephthalate are part of our everyday lives in the form of packaging, household goods, electrical insulation, etc. These polymers are non-degradable and create many environmental problems and public health concerns. Additionally, these polymers are produced from finite fossils resources. With the continuous utilization of these limited resources, it is important to look towards renewable sources along with biodegradation of the produced polymers, ideally. Although many bio-based polymers are known, such as polylactic acid, polybutylene succinate adipate or polybutylene succinate, none have yet shown the promise of replacing conventional polymers like polyethylene, polypropylene and polyethylene terephthalate. Cellulose is one of the most abundant renewable resources produced in nature. It can be transformed into various small molecules, such as sugars, furans, and levoglucosenone. The aim of this research is to use the cellulose derived molecules for the synthesis of polymers. Acid-treated cellulose was subjected to thermal pyrolysis to obtain levoglucosenone, which was reduced to levoglucosenol. Levoglucosenol was polymerized, for the first time, by ring-opening metathesis polymerization (ROMP) yielding high molar mass polymers of up to ~150 kg/mol. The poly(levoglucosenol) is thermally stable up to ~220 ℃, amorphous, and is exhibiting a relatively high glass transition temperature of ~100 ℃. The poly(levoglucosenol) can be converted to a transparent film, resembling common plastic, and was found to degrade in a moist acidic environment. This means that poly(levoglucosenol) may find its use as an alternative to conventional plastic, for instance, polystyrene. Levoglucosenol was also converted into levoglucosenyl methyl ether, which was polymerized by cationic ring-opening metathesis polymerization (CROP). Polymers were obtained with molar masses up to ~36 kg/mol. These polymers are thermally stable up to ~220 ℃ and are semi-crystalline thermoplastics, having a glass transition temperature of ~35 ℃ and melting transition of 70-100 ℃. Additionally, the polymers underwent cross-linking, hydrogenation and thiol-ene click chemistry.}, language = {en} } @phdthesis{Zhang2019, author = {Zhang, Shuhao}, title = {Synthesis and self-assembly of protein-polymer conjugates for the preparation of biocatalytically active membranes}, school = {Universit{\"a}t Potsdam}, pages = {VIII, 161}, year = {2019}, abstract = {This thesis covers the synthesis of conjugates of 2-Deoxy-D-ribose-5-phosphate aldolase (DERA) with suitable polymers and the subsequent immobilization of these conjugates in thin films via two different approaches. 2-Deoxy-D-ribose-5-phosphate aldolase (DERA) is a biocatalyst that is capable of converting acetaldehyde and a second aldehyde as acceptor into enantiomerically pure mono- and diyhydroxyaldehydes, which are important structural motifs in a number of pharmaceutically active compounds. Conjugation and immobilization renders the enzyme applicable for utilization in a continuously run biocatalytic process which avoids the common problem of product inhibition. Within this thesis, conjugates of DERA and poly(N-isopropylacrylamide) (PNIPAm) for immobilization via a self-assembly approach were synthesized and isolated, as well as conjugates with poly(N,N-dimethylacrylamide) (PDMAA) for a simplified and scalable spray-coating approach. For the DERA/PNIPAm-conjugates different synthesis routes were tested, including grafting-from and grafting-to, both being common methods for the conjugation. Furthermore, both lysines and cysteines were addressed for the conjugation in order to find optimum conjugation conditions. It turned out that conjugation via lysine causes severe activity loss as one lysine plays a key role in the catalyzing mechanism. The conjugation via the cysteines by a grafting-to approach using pyridyl disulfide (PDS) end-group functionalized polymers led to high conjugation efficiencies in the presence of polymer solubilizing NaSCN. The resulting conjugates maintained enzymatic activity and also gained high acetaldehyde tolerance which is necessary for their use later on in an industrial relevant process after their immobilization. The resulting DERA/PNIPAm conjugates exhibited enhanced interfacial activity at the air/water interface compared to the single components, which is an important pre-requisite for the immobilization via the self-assembly approach. Conjugates with longer polymer chains formed homogeneous films on silicon wafers and glass slides while the ones with short chains could only form isolated aggregates. On top of that, long chain conjugates showed better activity maintenance upon the immobilization. The crosslinking of conjugates, as well as their fixation on the support materials, are important for the mechanical stability of the films obtained from the self-assembly process. Therefore, in a second step, we introduced the UV-crosslinkable monomer DMMIBA to the PNIPAm polymers to be used for conjugation. The introduction of DMMIBA reduced the lower critical solution temperature (LCST) of the polymer and thus the water solubility at ambient conditions, resulting in lower conjugation efficiencies and in turn slightly poorer acetaldehyde tolerance of the resulting conjugates. Unlike the DERA/PNIPAm, the conjugates from the copolymer P(NIPAM-co-DMMIBA) formed continuous, homogenous films only after the crosslinking step via UV-treatment. For a firm binding of the crosslinked films, a functionalization protocol for the model support material cyclic olefin copolymer (COC) and the final target support, PAN based membranes, was developed that introduces analogue UV-reactive groups to the support surface. The conjugates immobilized on the modified COC films maintained enzymatic activity and showed good mechanical stability after several cycles of activity assessment. Conjugates with longer polymer chains, however, showed a higher degree of crosslinking after the UV-treatment leading to a pronounced loss of activity. A porous PAN membrane onto which the conjugates were immobilized as well, was finally transferred to a dead end filtration membrane module to catalyze the aldol reaction of the industrially relevant mixture of acetaldehyde and hexanal in a continuous mode. Mono aldol product was detectable, but yields were comparably low and the operational stability needs to be further improved Another approach towards immobilization of DERA conjugates that was followed, was to generate the conjugates in situ by simply mixing enzyme and polymer and spray coat the mixture onto the membrane support. Compared to the previous approach, the focus was more put on simplicity and a possible scalability of the immobilization. Conjugates were thus only generated in-situ and not further isolated and characterized. For the conjugation, PDMAA equipped with N-2-thiolactone acrylamide (TlaAm) side chains was used, an amine-reactive comonomer that can react with the lysine residues of DERA, as well as with amino groups introduced to a desired support surface. Furthermore disulfide formation after hydrolysis of the Tla groups causes a crosslinking effect. The synthesized copolymer poly(N,N-Dimethylacrylamide-co-N-2-thiolactone acrylamide) (P(DMAA-co-TlaAm)) thus serves a multiple purpose including protein binding, crosslinking and binding to support materials. The mixture of DERA and polymer could be immobilized on the PAN support by spray-coating under partial maintenance of enzymatic activity. To improve the acetaldehyde tolerance, the polymer in used was further equipped with cysteine reactive PDS end-groups that had been used for the conjugation as described in the first part of the thesis. The generated conjugates indeed showed good acetaldehyde tolerance and were thus used to be coated onto PAN membrane supports. Post treatment with a basic aqueous solution of H2O2 was supposed to further crosslink the spray-coated film hydrolysis and oxidation of the thiolactone groups. However, a washing off of the material was observed. Optimization is thus still necessary.}, language = {en} } @phdthesis{Schuerings2019, author = {Sch{\"u}rings, Marco Philipp Hermann}, title = {Synthesis of 1D microgel strands and their motion analysis in solution}, doi = {10.25932/publishup-43953}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-439532}, school = {Universit{\"a}t Potsdam}, pages = {167}, year = {2019}, abstract = {The fabrication of 1D nanostrands composed of stimuli responsive microgels has been shown in this work. Microgels are well known materials able to respond to various stimuli from outer environment. Since these microgels respond via a volume change to an external stimulus, a targeted mechanical response can be achieved. Through carefully choosing the right composition of the polymer matrix, microgels can be designed to react precisely to the targeted stimuli (e.g. drug delivery via pH and temperature changes, or selective contractions through changes in electrical current125). In this work, it was aimed to create flexible nano-filaments which are capable of fast anisotropic contractions similar to muscle filaments. For the fabrication of such filaments or strands, nanostructured templates (PDMS wrinkles) were chosen due to a facile and low-cost fabrication and versatile tunability of their dimensions. Additionally, wrinkling is a well-known lithography-free method which enables the fabrication of nanostructures in a reproducible manner and with a high long-range periodicity. In Chapter 2.1, it was shown for the first time that microgels as soft matter particles can be aligned to densely packed microgel arrays of various lateral dimensions. The alignment of microgels with different compositions (e.g. VCL/AAEM, NIPAAm, NIPAAm/VCL and charged microgels) was shown by using different assembly techniques (e.g. spin-coating, template confined molding). It was chosen to set one experimental parameter constant which was the SiOx surface composition of the templates and substrates (e.g. oxidized PDMS wrinkles, Si-wafers and glass slides). It was shown that the fabrication of nanoarrays was feasible with all tested microgel types. Although the microgels exhibited different deformability when aligned on a flat surface, they retained their thermo-responsivity and swelling behavior. Towards the fabrication of 1D microgel strands interparticle connectivity was aspired. This was achieved via different cross-linking methods (i.e. cross-linking via UV-irradiation and host-guest complexation) discussed in Chapter 2.2. The microgel arrays created by different assembly methods and microgel types were tested for their cross-linking suitability. It was observed that NIPAAm based microgels cannot be cross-linked with UV light. Furthermore, it was found that these microgels exhibit a strong surface-particle-interaction and therefore could not be detached from the given substrates. In contrast to the latter, with VCL/AAEM based microgels it was possible to both UV cross-link them based on the keto-enol tautomerism of the AAEM copolymer, and to detach them from the substrate due to the lower adhesion energy towards SiOx surfaces. With VCL/AAEM microgels long, one-dimensional microgel strands could be re-dispersed in water for further analysis. It has also been shown that at least one lateral dimension of the free dispersed 1D microgel strands is easily controllable by adjusting the wavelength of the wrinkled template. For further work, only VCL/AAEM based microgels were used to focus on the main aim of this work, i.e. the fabrication of 1D microgel nanostrands. As an alternative to the unspecific and harsh UV cross-linking, the host-guest complexation via diazobenzene cross-linkers and cyclodextrin hosts was explored. The idea behind this approach was to give means to a future construction kit-like approach by incorporation of cyclodextrin comonomers in a broad variety of particle systems (e.g. microgels, nanoparticles). For this purpose, VCL/AAEM microgels were copolymerized with different amounts of mono-acrylate functionalized β-cyclodextrin (CD). After successfully testing the cross-linking capability in solution, the cross-linking of aligned VCL/AAEM/CD microgels was tried. Although the cross-linking worked well, once the single arrays came into contact to each other, they agglomerated. As a reason for this behavior residual amounts of mono-complexed diazobenzene linkers were suspected. Thus, end-capping strategies were tried out (e.g. excess amounts of β-cyclodextrin and coverage with azobenzene functionalized AuNPs) but were unsuccessful. With deeper thought, entropy effects were taken into consideration which favor the release of complexed diazobenzene linker leading to agglomerations. To circumvent this entropy driven effect, a multifunctional polymer with 50\% azobenzene groups (Harada polymer) was used. First experiments with this polymer showed promising results regarding a less pronounced agglomeration (Figure 77). Thus, this approach could be pursued in the future. In this chapter it was found out that in contrast to pearl necklace and ribbon like formations, particle alignment in zigzag formation provided the best compromise in terms of stability in dispersion (see Figure 44a and Figure 51) while maintaining sufficient flexibility. For this reason, microgel strands in zigzag formation were used for the motion analysis described in Chapter 2.3. The aim was to observe the properties of unrestrained microgel strands in solution (e.g. diffusion behavior, rotational properties and ideally, anisotropic contraction after temperature increase). Initially, 1D microgel strands were manipulated via AFM in a liquid cell setup. It could be observed that the strands required a higher load force compared to single microgels to be detached from the surface. However, with the AFM it was not possible to detach the strands in a controllable manner but resulted in a complete removal of single microgel particles and a tearing off the strands from the surface, respectively. For this reason, to observe the motion behavior of unrestrained microgel strands in solution, confocal microscopy was used. Furthermore, to hinder an adsorption of the strands, it was found out that coating the surface of the substrates with a repulsive polymer film was beneficial. Confocal and wide-field microscopy videos showed that the microgel strands exhibit translational and rotational diffusive motion in solution without perceptible bending. Unfortunately, with these methods the detection of the anisotropic stimuli responsive contraction of the free moving microgel strands was not possible. To summarize, the flexibility of microgel strands is more comparable to the mechanical behavior of a semi flexible cable than to a yarn. The strands studied here consist of dozens or even hundreds of discrete submicron units strung together by cross-linking, having few parallels in nanotechnology. With the insights gained in this work on microgel-surface interactions, in the future, a targeted functionalization of the template and substrate surfaces can be conducted to actively prevent unwanted microgel adsorption for a given microgel system (e.g. PVCL and polystyrene coating235). This measure would make the discussed alignment methods more diverse. As shown herein, the assembly methods enable a versatile microgel alignment (e.g. microgel meshes, double and triple strands). To go further, one could use more complex templates (e.g. ceramic rhombs and star shaped wrinkles (Figure 14) to expand the possibilities of microgel alignment and to precisely control their aspect ratios (e.g. microgel rods with homogeneous size distributions).}, language = {en} } @phdthesis{NaderiMehr2019, author = {Naderi Mehr, Fatemeh}, title = {Preparation and self-assembly behavior of anisotropic polymer patchy particles}, pages = {74, XX}, year = {2019}, language = {en} } @phdthesis{Matic, author = {Matic, Aleksandar}, title = {Myrcene to materials}, school = {Universit{\"a}t Potsdam}, pages = {117}, language = {en} } @phdthesis{Noack2019, author = {Noack, Sebastian}, title = {Poly(lactide)-based amphiphilic block copolymers}, doi = {10.25932/publishup-43616}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-436168}, school = {Universit{\"a}t Potsdam}, pages = {xvii, 148}, year = {2019}, abstract = {Due to its bioavailability and (bio)degradability, poly(lactide) (PLA) is an interesting polymer that is already being used as packaging material, surgical seam, and drug delivery system. Dependent on various parameters such as polymer composition, amphiphilicity, sample preparation, and the enantiomeric purity of lactide, PLA in an amphiphilic block copolymer can affect the self-assembly behavior dramatically. However, sizes and shapes of aggregates have a critical effect on the interactions between biological and drug delivery systems, where the general understanding of these polymers and their ability to influence self-assembly is of significant interest in science. The first part of this thesis describes the synthesis and study of a series of linear poly(L-lactide) (PLLA) and poly(D-lactide) (PDLA)-based amphiphilic block copolymers with varying PLA (hydrophobic), and poly(ethylene glycol) (PEG) (hydrophilic) chain lengths and different block copolymer sequences (PEG-PLA and PLA-PEG). The PEG-PLA block copolymers were synthesized by ring-opening polymerization of lactide initiated by a PEG-OH macroinitiator. In contrast, the PLA-PEG block copolymers were produced by a Steglich-esterification of modified PLA with PEG-OH. The aqueous self-assembly at room temperature of the enantiomerically pure PLLA-based block copolymers and their stereocomplexed mixtures was investigated by dynamic light scattering (DLS), transmission electron microscopy (TEM), wide-angle X-ray diffraction (WAXD), and differential scanning calorimetry (DSC). Spherical micelles and worm-like structures were produced, whereby the obtained self-assembled morphologies were affected by the lactide weight fraction in the block copolymer and self-assembly time. The formation of worm-like structures increases with decreasing PLA-chain length and arises from spherical micelles, which become colloidally unstable and undergo an epitaxial fusion with other micelles. As shown by DSC experiments, the crystallinity of the corresponding PLA blocks increases within the self-assembly time. However, the stereocomplexed self-assembled structures behave differently from the parent polymers and result in irregular-shaped clusters of spherical micelles. Additionally, time-dependent self-assembly experiments showed a transformation, from already self-assembled morphologies of different shapes to more compact micelles upon stereocomplexation. In the second part of this thesis, with the objective to influence the self-assembly of PLA-based block copolymers and its stereocomplexes, poly(methyl phosphonate) (PMeP) and poly(isopropyl phosphonate) (PiPrP) were produced by ring-opening polymerization to implement an alternative to the hydrophilic block PEG. Although, the 1,8 diazabicyclo[5.4.0]unde 7 ene (DBU) or 1,5,7 triazabicyclo[4.4.0]dec-5-ene (TBD) mediated synthesis of the corresponding poly(alkyl phosphonate)s was successful, however, not so the polymerization of copolymers with PLA-based precursors (PLA-homo polymers, and PEG-PLA block copolymers). Transesterification, obtained by 1H-NMR spectroscopy, between the poly(phosphonate)- and PLA block caused a high-field shifted peak split of the methine proton in the PLA polymer chain, with split intensities depending on the used catalyst (DBU for PMeP, and TBD for PiPrP polymerization). An additional prepared block copolymer PiPrP-PLLA that wasn't affected in its polymer sequence was finally used for self-assembly experiments with PLA-PEG and PEG-PLA mixing. This work provides a comprehensive study of the self-assembly behavior of PLA-based block copolymers influenced by various parameters such as polymer block lengths, self-assembly time, and stereocomplexation of block copolymer mixtures.}, language = {en} } @phdthesis{Walczak2019, author = {Walczak, Ralf}, title = {Molecular design of nitrogen-doped nanoporous noble carbon materials for gas adsorption}, doi = {10.25932/publishup-43524}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-435241}, school = {Universit{\"a}t Potsdam}, pages = {II, 155}, year = {2019}, abstract = {In den modernen Gesellschaften f{\"u}hrt ein stetig steigender Energiebedarf zu dem zunehmenden Verbrauch fossiler Brennstoffe wie Kohle, {\"O}l, und Gas. Die Verbrennung dieser kohlenstoffbasierten Brennstoffe f{\"u}hrt unweigerlich zur Freisetzung von Treibhausgasen, vor allem von CO2. Die CO2 Aufnahme unmittelbar bei den Verbrennungsanlagen oder direkt aus der Luft, zusammen mit Regulierung von CO2 produzierenden Energiesektoren (z.B. K{\"u}hlanlagen), k{\"o}nnen den CO2 Ausstoß reduzieren. Allerdings f{\"u}hren insbesondere bei der CO2 Aufnahme die geringen CO2 Konzentrationen und die Aufnahme konkurrierender Gase zu niedrigen CO2 Kapazit{\"a}ten und Selektivit{\"a}ten. Das Zusammenspiel der Gastmolek{\"u}le mit por{\"o}sen Materialien ist dabei essentiell. Por{\"o}se Kohlenstoffmaterialien besitzen attraktive Eigenschaften, unter anderem elektrische Leitf{\"a}higkeit, einstellbare Porosit{\"a}t, als auch chemische und thermische Stabilit{\"a}t. Allerdings f{\"u}hrt die zu geringe Polarisierbarkeit dieser Materialien zu einer geringen Affinit{\"a}t zu polaren Molek{\"u}len (z.B. CO2, H2O, oder NH3). Diese Affinit{\"a}t kann durch den Einbau von Stickstoff erh{\"o}ht werden. Solche Materialien sind oft „edler" als reine Kohlenstoffe, dies bedeutet, dass sie eher oxidierend wirken, als selbst oxidiert zu werden. Die Problematik besteht darin, einen hohen und gleichm{\"a}ßig verteilten Stickstoffgehalt in das Kohlenstoffger{\"u}st einzubauen. Die Zielsetzung dieser Dissertation ist die Erforschung neuer Synthesewege f{\"u}r stickstoffdotierte edle Kohlenstoffmaterialien und die Entwicklung eines grundlegenden Verst{\"a}ndnisses f{\"u}r deren Anwendung in Gasadsorption und elektrochemischer Energiespeicherung. Es wurde eine templatfreie Synthese f{\"u}r stickstoffreiche, edle, und mikropor{\"o}se Kohlenstoffmaterialien durch direkte Kondensation eines stickstoffreichen organischen Molek{\"u}ls als Vorl{\"a}ufer erarbeitet. Dadurch konnten Materialien mit hohen Adsorptionskapazit{\"a}ten f{\"u}r H2O und CO2 bei niedrigen Konzentrationen und moderate CO2/N2 Selektivit{\"a}ten erzielt werden. Um die CO2/N2 Selektivit{\"a}ten zu verbessern, wurden mittels der Einstellung des Kondensationsgrades die molekulare Struktur und Porosit{\"a}t der Kohlenstoffmaterialien kontrolliert. Diese Materialien besitzen die Eigenschaften eines molekularen Siebs f{\"u}r CO2 {\"u}ber N2, das zu herausragenden CO2/N2 Selektivit{\"a}ten f{\"u}hrt. Der ultrahydrophile Charakter der Porenoberfl{\"a}chen und die kleinen Mikroporen dieser Kohlenstoffmaterialien erm{\"o}glichen grundlegende Untersuchungen f{\"u}r die Wechselwirkungen mit Molek{\"u}len die polarer sind als CO2, n{\"a}mlich H2O und NH3. Eine weitere Reihe stickstoffdotierter Kohlenstoffmaterialien wurde durch Kondensation eines konjugierten mikropor{\"o}sen Polymers synthetisiert und deren strukturelle Besonderheiten als Anodenmaterial f{\"u}r die Natriumionen Batterie untersucht. Diese Dissertation leistet einen Beitrag zur Erforschung stickstoffdotierter Kohlenstoffmaterialien und deren Wechselwirkungen mit verschiedenen Gastmolek{\"u}len.}, language = {en} } @phdthesis{Tian2019, author = {Tian, Zhihong}, title = {Oxygen-, Sulfur-doped Novel Porous Carbon-Nitrogen Frameworks by Salt Melt Method}, school = {Universit{\"a}t Potsdam}, pages = {101}, year = {2019}, language = {en} } @phdthesis{Lai2019, author = {Lai, Feili}, title = {Functionalized ordered mesoporous carbon materials for enhancing the energy density of supercapacitors}, school = {Universit{\"a}t Potsdam}, pages = {115}, year = {2019}, language = {en} } @phdthesis{Sarhan2019, author = {Sarhan, Radwan Mohamed}, title = {Plasmon-driven photocatalytic reactions monitored by surface-enhanced Raman spectroscopy}, doi = {10.25932/publishup-43330}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-433304}, school = {Universit{\"a}t Potsdam}, year = {2019}, abstract = {Plasmonic metal nanostructures can be tuned to efficiently interact with light, converting the photons into energetic charge carriers and heat. Therefore, the plasmonic nanoparticles such as gold and silver nanoparticles act as nano-reactors, where the molecules attached to their surfaces benefit from the enhanced electromagnetic field along with the generated energetic charge carriers and heat for possible chemical transformations. Hence, plasmonic chemistry presents metal nanoparticles as a unique playground for chemical reactions on the nanoscale remotely controlled by light. However, defining the elementary concepts behind these reactions represents the main challenge for understanding their mechanism in the context of the plasmonically assisted chemistry. Surface-enhanced Raman scattering (SERS) is a powerful technique employing the plasmon-enhanced electromagnetic field, which can be used for probing the vibrational modes of molecules adsorbed on plasmonic nanoparticles. In this cumulative dissertation, I use SERS to probe the dimerization reaction of 4-nitrothiophenol (4-NTP) as a model example of plasmonic chemistry. I first demonstrate that plasmonic nanostructures such as gold nanotriangles and nanoflowers have a high SERS efficiency, as evidenced by probing the vibrations of the rhodamine dye R6G and the 4-nitrothiophenol 4-NTP. The high signal enhancement enabled the measurements of SERS spectra with a short acquisition time, which allows monitoring the kinetics of chemical reactions in real time. To get insight into the reaction mechanism, several time-dependent SERS measurements of the 4-NTP have been performed under different laser and temperature conditions. Analysis of the results within a mechanistic framework has shown that the plasmonic heating significantly enhances the reaction rate, while the reaction is probably initiated by the energetic electrons. The reaction was shown to be intensity-dependent, where a certain light intensity is required to drive the reaction. Finally, first attempts to scale up the plasmonic catalysis have been performed showing the necessity to achieve the reaction threshold intensity. Meanwhile, the induced heat needs to quickly dissipate from the reaction substrate, since otherwise the reactants and the reaction platform melt. This study might open the way for further work seeking the possibilities to quickly dissipate the plasmonic heat generated during the reaction and therefore, scaling up the plasmonic catalysis.}, language = {en} } @phdthesis{RuizRodriguez2019, author = {Ruiz Rodriguez, Janete Lorena}, title = {Osmotic pressure effects on collagen mimetic peptides}, school = {Universit{\"a}t Potsdam}, pages = {139}, year = {2019}, abstract = {Collagen is the most abundant protein in mammals. In many tissues, collagen molecules assemble to form a hierarchical structure. In the smallest supramolecular unit, named fibril, each molecule is displaced in the axial direction with respect to its neighbors. This staggering creates a periodic gap and overlap regions, where the gap regions exhibit 20\% less density. These fibril-forming collagens play an essential role in the strength of connective tissues. Despite much effort, directed at understanding collagen function and regulation, the influence of the chemical environment on the local structural and mechanical properties remains poorly understood. Recent studies, aimed at elucidating the effect of osmotic pressure, showed that collagen contracts upon water removal. This observation highlights the importance of water for the stabilization and mechanics of the collagen molecule. Using collagen mimetic peptides (CMPs), which fold into triple helical structures reminiscent of natural collagen, the primary goal of this work was to investigate the effect of the osmotic pressure on specific collagen-mimetic sequences. CMPs were used as the model system as they provide sequence control, which is essential for discriminating local from global structural changes and for relating the observed effects to existing knowledge about the full-length collagen molecule. Of specific interest was the structure of individual collagen triple helices as well as their organization into self-assembled higher order structures. These key structural features were monitored with infrared spectroscopy (IR) and synchrotron X-ray scattering, while varying the osmotic pressure. For controlling the osmotic pressure, CMP powder samples were incubated in air of defined relative humidity, ranging from dry conditions to highly "humid". In addition, to obtain more biologically relevant conditions, the CMPs were measured in ultrapure water and in solutions containing small molecule osmolytes. Using the sequences (Pro-Pro-Gly)10, (Pro-Hyp-Gly)10 and (Hyp-Hyp-Gly)10, it was shown that CMPs with different degrees of proline hydroxylation (Hyp = hydroxyproline) exhibit a sequence-specific response to osmotic pressure. IR spectroscopy revealed that osmotic pressure changes affect the strength of the triple helix stabilizing, interchain hydrogen bond and that the extent of this change depends on the degree of hydroxylation. X-ray scattering experiments further showed that changes in osmotic pressure affect both the molecular length as well as the higher order organization of CMPs. Starting from a pseudo-hexagonal packing in the dry state, all three CMPs showed isotropic swelling when increasing the water content to approximately 1.2 water molecules per amino acid, again to different extents depending on the degree of hydroxylation. When increasing the water content further, this pseudo-hexagonal arrangement breaks down. In the fully hydrated state, each CMP is characterized by its own specific and more complex packing geometry. While these changes in the lateral packing arrangement suggest swelling upon hydration, an overall decrease of the molecular length (i.e. contraction) was observed in the axial direction. Also for this structural feature, a strong dependency on the specific amino acid sequence was found. Interestingly, the observed contraction is the opposite of what has been reported for natural collagen. As (Pro-Pro-Gly)n, (Pro-Hyp-Gly)n and (Hyp-Hyp-Gly)n repeat units are found in collagen with a relatively high abundance, this suggests that other collagen sequence fragments need to respond to hydration in the opposite way to obtain a net elongation of the full-length collagen molecule. To test this hypothesis, sequences predicted to be sensitive to osmotic pressure were considered. One such sequence, consisting of two repeat units (Ala-Arg-Gly-Ser-Asp-Gly), was inserted as a guest into a (Pro-Pro-Gly) host. When compared to the canonical CMP sequences investigated earlier, the lateral helix packing follows a similar trend with increasing hydration; however, the host-guest CMP axially elongates with increasing water content. This behavior is more similar to what has been found for natural collagen and suggests that different sequences do determine the molecular length of collagen sequences differently. Interestingly, the canonical sequences are more abundant in the overlap region while the guest sequence is found in the gap region. This allows to speculate that sequences in the gap and overlap regions possess a specifically fine-tuned local response to osmotic pressure changes. Clearly, more experiments with additional sequences are needed to confirm this. In conclusion, the results obtained in this work indicate a highly sequence specific interaction between collagen and water. Osmotic pressure-induced conformational changes mostly originate from local geometries and bonding patterns and affect both the structure of individual triple helices as well as higher order assemblies. One key remaining question is how these conformational changes affect the local mechanical properties of the collagen molecule. As a first step, the stiffness (persistence length) of full-length collagen was determined using atomic force microscopy. In the future, experimental strategies need to be developed that allow for investigating the mechanical properties of specific collagen sequences, e.g. performing single-molecule force spectroscopy of CMPs.}, language = {en} } @phdthesis{Yan2019, author = {Yan, Runyu}, title = {Nitrogen-doped and porous carbons towards new energy storage mechanisms for supercapacitors with high energy density}, doi = {10.25932/publishup-43141}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-431413}, school = {Universit{\"a}t Potsdam}, pages = {152}, year = {2019}, abstract = {Supercapacitors are electrochemical energy storage devices with rapid charge/discharge rate and long cycle life. Their biggest challenge is the inferior energy density compared to other electrochemical energy storage devices such as batteries. Being the most widely spread type of supercapacitors, electrochemical double-layer capacitors (EDLCs) store energy by electrosorption of electrolyte ions on the surface of charged electrodes. As a more recent development, Na-ion capacitors (NICs) are expected to be a more promising tactic to tackle the inferior energy density due to their higher-capacity electrodes and larger operating voltage. The charges are simultaneously stored by ion adsorption on the capacitive-type cathode surface and via faradic process in the battery-type anode, respectively. Porous carbon electrodes are of great importance in these devices, but the paramount problems are the facile synthetic routes for high-performance carbons and the lack of fundamental understanding of the energy storage mechanisms. Therefore, the aim of the present dissertation is to develop novel synthetic methods for (nitrogen-doped) porous carbon materials with superior performance, and to reveal a deeper understanding energy storage mechanisms of EDLCs and NICs. The first part introduces a novel synthetic method towards hierarchical ordered meso-microporous carbon electrode materials for EDLCs. The large amount of micropores and highly ordered mesopores endow abundant sites for charge storage and efficient electrolyte transport, respectively, giving rise to superior EDLC performance in different electrolytes. More importantly, the controversial energy storage mechanism of EDLCs employing ionic liquid (IL) electrolytes is investigated by employing a series of porous model carbons as electrodes. The results not only allow to conclude on the relations between the porosity and ion transport dynamics, but also deliver deeper insights into the energy storage mechanism of IL-based EDLCs which is different from the one usually dominating in solvent-based electrolytes leading to compression double-layers. The other part focuses on anodes of NICs, where novel synthesis of nitrogen-rich porous carbon electrodes and their sodium storage mechanism are investigated. Free-standing fibrous nitrogen-doped carbon materials are synthesized by electrospinning using the nitrogen-rich monomer (hexaazatriphenylene-hexacarbonitrile, C18N12) as the precursor followed by condensation at high temperature. These fibers provide superior capacity and desirable charge/discharge rate for sodium storage. This work also allows insights into the sodium storage mechanism in nitrogen-doped carbons. Based on this mechanism, further optimization is done by designing a composite material composed of nitrogen-rich carbon nanoparticles embedded in conductive carbon matrix for a better charge/discharge rate. The energy density of the assembled NICs significantly prevails that of common EDLCs while maintaining the high power density and long cycle life.}, language = {en} } @phdthesis{Jiang2019, author = {Jiang, Yi}, title = {Tailoring surface functions of micro/nanostructured polymeric substrates by thermo-mechanical treatments}, school = {Universit{\"a}t Potsdam}, pages = {93}, year = {2019}, language = {en} } @phdthesis{Zimmermann2018, author = {Zimmermann, Marc}, title = {Multifunctional patchy silica particles via microcontact printing}, doi = {10.25932/publishup-42773}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-427731}, school = {Universit{\"a}t Potsdam}, pages = {IX, 121, xiii}, year = {2018}, abstract = {This research addressed the question, if it is possible to simplify current microcontact printing systems for the production of anisotropic building blocks or patchy particles, by using common chemicals while still maintaining reproducibility, high precision and tunability of the Janus-balance Chapter 2 introduced the microcontact printing materials as well as their defined electrostatic interactions. In particular polydimethylsiloxane stamps, silica particles and high molecular weight polyethylenimine ink were mainly used in this research. All of these components are commercially available in large quantities and affordable, which gives this approach a huge potential for further up-scaling developments. The benefits of polymeric over molecular inks was described including its flexible influence on the printing pressure. With this alteration of the µCP concept, a new method of solvent assisted particle release mechanism enabled the switch from two-dimensional surface modification to three-dimensional structure printing on colloidal silica particles, without changing printing parameters or starting materials. This effect opened the way to use the internal volume of the achieved patches for incorporation of nano additives, introducing additional physical properties into the patches without alteration of the surface chemistry. The success of this system and its achievable range was further investigated in chapter 3 by giving detailed information about patch geometry parameters including diameter, thickness and yield. For this purpose, silica particles in a size range between 1µm and 5µm were printed with different ink concentrations to change the Janus-balance of these single patched particles. A necessary intermediate step, consisting of air-plasma treatment, for the production of trivalent particles using "sandwich" printing was discovered and comparative studies concerning the patch geometry of single and double patched particles were conducted. Additionally, the usage of structured PDMS stamps during printing was described. These results demonstrate the excellent precision of this approach and opens the pathway for even greater accuracy as further parameters can be finely tuned and investigated, e.g. humidity and temperature during stamp loading. The performance of these synthesized anisotropic colloids was further investigated in chapter 4, starting with behaviour studies in alcoholic and aqueous dispersions. Here, the stability of the applied patches was studied in a broad pH range, discovering a release mechanism by disabling the electrostatic bonding between particle surface and polyelectrolyte ink. Furthermore, the absence of strong attractive forces between divalent particles in water was investigated using XPS measurements. These results lead to the conclusion that the transfer of small PDMS oligomers onto the patch surface is shielding charges, preventing colloidal agglomeration. However, based on this knowledge, further patch modifications for particle self-assembly were introduced including physical approaches using magnetic nano additives, chemical patch functionalization with avidin-biotin or the light responsive cyclodextrin-arylazopyrazoles coupling as well as particle surface modification for the synthesis of highly amphiphilic colloids. The successful coupling, its efficiency, stability and behaviour in different solvents were evaluated to find a suitable coupling system for future assembly experiments. Based on these results the possibility of more sophisticated structures by colloidal self-assembly is given. Certain findings needed further analysis to understand their underlying mechanics, including the relatively broad patch diameter distribution and the decreasing patch thickness for smaller silica particles. Mathematical assumptions for both effects are introduced in chapter 5. First, they demonstrate the connection between the naturally occurring particle size distribution and the broadening of the patch diameter, indicating an even higher precision for this µCP approach. Second, explaining the increase of contact area between particle and ink surface due to higher particle packaging, leading to a decrease in printing pressure for smaller particles. These calculations ultimately lead to the development of a new mechanical microcontact printing approach, using centrifugal forces for high pressure control and excellent parallel alignment of printing substrates. First results with this device and the comparison with previously conducted by-hand experiments conclude this research. It furthermore displays the advantages of such a device for future applications using a mechanical printing approach, especially for accessing even smaller nano particles with great precision and excellent yield. In conclusion, this work demonstrates the successful adjustment of the µCP approach using commercially available and affordable silica particles and polyelectrolytes for high flexibility, reduced costs and higher scale-up value. Furthermore, its was possible to increase the modification potential by introducing three-dimensional patches for additional functionalization volume. While keeping a high colloidal stability, different coupling systems showed the self-assembly capabilities of this toolbox for anisotropic particles.}, language = {en} } @phdthesis{Guenther, author = {G{\"u}nther, Erika}, title = {Intracellular processes in magnetotactic bacteria studied by optical tools}, school = {Universit{\"a}t Potsdam}, pages = {113}, language = {en} } @phdthesis{Kumru2018, author = {Kumru, Baris}, title = {Utilization of graphitic carbon nitride in dispersed media}, doi = {10.25932/publishup-42733}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-427339}, school = {Universit{\"a}t Potsdam}, pages = {III, 190}, year = {2018}, abstract = {Utilization of sunlight for energy harvesting has been foreseen as sustainable replacement for fossil fuels, which would also eliminate side effects arising from fossil fuel consumption such as drastic increase of CO2 in Earth atmosphere. Semiconductor materials can be implemented for energy harvesting, and design of ideal energy harvesting devices relies on effective semiconductor with low recombination rate, ease of processing, stability over long period, non-toxicity and synthesis from abundant sources. Aforementioned criteria have attracted broad interest for graphitic carbon nitride (g-CN) materials, metal-free semiconductor which can be synthesized from low cost and abundant precursors. Furthermore, physical properties such as band gap, surface area and absorption can be tuned. g-CN was investigated as heterogeneous catalyst, with diversified applications from water splitting to CO2 reduction and organic coupling reactions. However, low dispersibility of g-CN in water and organic solvents was an obstacle for future improvements. Tissue engineering aims to mimic natural tissues mechanically and biologically, so that synthetic materials can replace natural ones in future. Hydrogels are crosslinked networks with high water content, therefore are prime candidates for tissue engineering. However, the first requirement is synthesis of hydrogels with mechanical properties that are matching to natural tissues. Among different approaches for reinforcement, nanocomposite reinforcement is highly promising. This thesis aims to investigate aqueous and organic dispersions of g-CN materials. Aqueous g-CN dispersions were utilized for visible light induced hydrogel synthesis, where g-CN acts as reinforcer and photoinitiator. Varieties of methodologies were presented for enhancing g-CN dispersibility, from co-solvent method to prepolymer formation, and it was shown that hydrogels with diversified mechanical properties (from skin-like to cartilage-like) are accessible via g-CN utilization. One pot photografting method was introduced for functionalization of g-CN surface which provides functional groups towards enhanced dispersibility in aqueous and organic media. Grafting vinyl thiazole groups yields stable additive-free organodispersions of g-CN which are electrostatically stabilized with increased photophysical properties. Colloidal stability of organic systems provides transparent g-CN coatings and printing g-CN from commercial inkjet printers. Overall, application of g-CN in dispersed media is highly promising, and variety of materials can be accessible via utilization of g-CN and visible light with simple chemicals and synthetic conditions. g-CN in dispersed media will bridge emerging research areas from tissue engineering to energy harvesting in near future.}, language = {en} } @phdthesis{Heiden2018, author = {Heiden, Sophia L.}, title = {Water at α-alumina surfaces}, doi = {10.25932/publishup-42636}, url = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-426366}, school = {Universit{\"a}t Potsdam}, pages = {124}, year = {2018}, abstract = {The (0001) surface of α-Al₂O₃ is the most stable surface cut under UHV conditions and was studied by many groups both theoretically and experimentally. Reaction barriers computed with GGA functionals are known to be underestimated. Based on an example reaction at the (0001) surface, this work seeks to improve this rate by applying a hybrid functional method and perturbation theory (LMP2) with an atomic orbital basis, rather than a plane wave basis. In addition to activation barriers, we calculate the stability and vibrational frequencies of water on the surface. Adsorption energies were compared to PW calculations and confirmed PBE+D2/PW stability results. Especially the vibrational frequencies with the B3LYP hybrid functional that have been calculated for the (0001) surface are in good agreement with experimental findings. Concerning the barriers and the reaction rate constant, the expectations are fully met. It could be shown that recalculation of the transition state leads to an increased barrier, and a decreased rate constant when hybrid functionals or LMP2 are applied. Furthermore, the molecular beam scattering of water on (0001) surface was studied. In a previous work by Hass the dissociation was studied by AIMD of molecularly adsorbed water, referring to an equilibrium situation. The experimental method to obtaining this is pinhole dosing. In contrast to this earlier work, the dissociation process of heavy water that is brought onto the surface from a molecular beam source was modeled in this work by periodic ab initio molecular dynamics simulations. This experimental method results in a non-equilibrium situation. The calculations with different surface and beam models allow us to understand the results of the non-equilibrium situation better. In contrast to a more equilibrium situation with pinhole dosing, this gives an increase in the dissociation probability, which could be explained and also understood mechanistically by those calculations. In this work good progress was made in understanding the (1120) surface of α-Al₂O₃ in contact with water in the low-coverage regime. This surface cut is the third most stable one under UHV conditions and has not been studied to a great extent yet. After optimization of the clean, defect free surface, the stability of different adsorbed species could be classified. One molecular minimum and several dissociated species could be detected. Starting from these, reaction rates for various surface reactions were evaluated. A dissociation reaction was shown to be very fast because the molecular minimum is relatively unstable, whereas diffusion reactions cover a wider range from fast to slow. In general, the (112‾0) surface appears to be much more reactive against water than the (0001) surface. In addition to reactivity, harmonic vibrational frequencies were determined for comparison with the findings of the experimental "Interfacial Molecular Spectroscopy" group from Fritz-Haber institute in Berlin. Especially the vibrational frequencies of OD species could be assigned to vibrations from experimental SFG spectra with very good agreement. Also, lattice vibrations were studied in close collaboration with the experimental partners. They perform SFG spectra at very low frequencies to get deep into the lattice vibration region. Correspondingly, a bigger slab model with greater expansion perpendicular to the surface was applied, considering more layers in the bulk. Also with the lattice vibrations we could obtain reasonably good agreement in terms of energy differences between the peaks.}, language = {en} }