@phdthesis{Zaupa2010,
  author    = {Zaupa, Alessandro},
  title     = {Physical crosslinking of gelatin : a supramolecular approach to biomaterials},
  url       = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus-52888},
  school      = {Universit{\"a}t Potsdam},
  year      = {2010},
  abstract  = {This work describes the realization of physically crosslinked networks based on gelatin by the introduction of functional groups enabling specific supramolecular interactions. Molecular models were developed in order to predict the material properties and permit to establish a knowledge-based approach to material design. The effect of additional supramolecular interactions with hydroxyapaptite was then studied in composite materials. The calculated properties are compared to experimental results to validate the models. The models are then further used for the study of physically crosslinked networks. Gelatin was functionalized with desaminotyrosine (DAT) and desaminotyrosyl-tyrosine (DATT) side groups, derived from the natural amino acid tyrosine. These group can potentially undergo to π-π and hydrogen bonding interactions also under physiological conditions. Molecular dynamics (MD) simulations were performed on models with 0.8 wt.-\% or 25 wt.-\% water content, using the second generation forcefield CFF91. The validation of the models was obtained by the comparison with specific experimental data such as, density, peptide conformational angles and X-ray scattering spectra. The models were then used to predict the supramolecular organization of the polymer chain, analyze the formation of physical netpoints and calculate the mechanical properties. An important finding of simulation was that with the increase of aromatic groups also the number of observed physical netpoints increased. The number of relatively stable physical netpoints, on average zero 0 for natural gelatin, increased to 1 and 6 for DAT and DATT functionalized gelatins respectively. A comparison with the Flory-Rehner model suggested reduced equilibrium swelling by factor 6 of the DATT-functionalized materials in water. The functionalized gelatins could be synthesized by chemoselective coupling of the free carboxylic acid groups of DAT and DATT to the free amino groups of gelatin. At 25 wt.-\% water content, the simulated and experimentally determined elastic mechanical properties (e.g. Young Modulus) were both in the order of GPa and were not influenced by the degree of aromatic modification. The experimental equilibrium degree of swelling in water decreased with increasing the number of inserted aromatic functions (from 2800 vol.-\% for pure gelatin to 300 vol.-\% for the DATT modified gelatin), at the same time, Young's modulus, elongation at break, and maximum tensile strength increased. It could be show that the functionalization with DAT and DATT influences the chain organization of gelatin based materials together with a controlled drying condition. Functionalization with DAT and DATT lead to a drastic reduction of helical renaturation, that could be more finely controlled by the applied drying conditions. The properties of the materials could then be influenced by application of two independent methods. Composite materials of DAT and DATT functionalized gelatins with hydroxyapatite (HAp) show a drastic reduction of swelling degree. In tensile tests and rheological measurements, the composites equilibrated in water had increased Young's moduli (from 200 kPa up to 2 MPa) and tensile strength (from 57 kPa up to 1.1 MPa) compared to the natural polymer matrix without affecting the elongation at break. Furthermore, an increased thermal stability from 40 °C to 85 °C of the networks could be demonstrated. The differences of the behaviour of the functionalized gelatins to pure gelatin as matrix suggested an additional stabilizing bond between the incorporated aromatic groups to the hydroxyapatite.},
  language  = {en}
}
@phdthesis{Tronci2010,
  author    = {Tronci, Giuseppe},
  title     = {Synthesis, characterization, and biological evaluation of gelatin-based scaffolds},
  url       = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus-49727},
  school      = {Universit{\"a}t Potsdam},
  year      = {2010},
  abstract  = {This work presents the development of entropy-elastic gelatin based networks in the form of films or scaffolds. The materials have good prospects for biomedical applications, especially in the context of bone regeneration. Entropy-elastic gelatin based hydrogel films with varying crosslinking densities were prepared with tailored mechanical properties. Gelatin was covalently crosslinked above its sol gel transition, which suppressed the gelatin chain helicity. Hexamethylene diisocyanate (HDI) or ethyl ester lysine diisocyanate (LDI) were applied as chemical crosslinkers, and the reaction was conducted either in dimethyl sulfoxide (DMSO) or water. Amorphous films were prepared as measured by Wide Angle X-ray Scattering (WAXS), with tailorable degrees of swelling (Q: 300-800 vol. \%) and wet state Young's modulus (E: 70 740 kPa). Model reactions showed that the crosslinking reaction resulted in a combination of direct crosslinks (3-13 mol.-\%), grafting (5-40 mol.-\%), and blending of oligoureas (16-67 mol.-\%). The knowledge gained with this bulk material was transferred to the integrated process of foaming and crosslinking to obtain porous 3-D gelatin-based scaffolds. For this purpose, a gelatin solution was foamed in the presence of a surfactant, Saponin, and the resulting foam was fixed by chemical crosslinking with a diisocyanate. The amorphous crosslinked scaffolds were synthesized with varied gelatin and HDI concentrations, and analyzed in the dry state by micro computed tomography (µCT, porosity: 65±11-73±14 vol.-\%), and scanning electron microscopy (SEM, pore size: 117±28-166±32 µm). Subsequently, the work focused on the characterization of the gelatin scaffolds in conditions relevant to biomedical applications. Scaffolds showed high water uptake (H: 630-1680 wt.-\%) with minimal changes in outer dimension. Since a decreased scaffold pore size (115±47-130±49 µm) was revealed using confocal laser scanning microscopy (CLSM) upon wetting, the form stability could be explained. Shape recoverability was observed after removal of stress when compressing wet scaffolds, while dry scaffolds maintained the compressed shape. This was explained by a reduction of the glass transition temperature upon equilibration with water (dynamic mechanical analysis at varied temperature (DMTA)). The composition dependent compression moduli (Ec: 10 50 kPa) were comparable to the bulk micromechanical Young's moduli, which were measured by atomic force microscopy (AFM). The hydrolytic degradation profile could be adjusted, and a controlled decrease of mechanical properties was observed. Partially-degraded scaffolds displayed an increase of pore size. This was likely due to the pore wall disintegration during degradation, which caused the pores to merge. The scaffold cytotoxicity and immunologic responses were analyzed. The porous scaffolds enabled proliferation of human dermal fibroblasts within the implants (up to 90 µm depth). Furthermore, indirect eluate tests were carried out with L929 cells to quantify the material cytotoxic response. Here, the effect of the sterilization method (Ethylene oxide sterilization), crosslinker, and surfactant were analyzed. Fully cytocompatible scaffolds were obtained by using LDI as crosslinker and PEO40 PPO20-PEO40 as surfactant. These investigations were accompanied by a study of the endotoxin material contamination. The formation of medical-grade materials was successfully obtained (<0.5 EU/mL) by using low-endotoxin gelatin and performing all synthetic steps in a laminar flow hood.},
  language  = {en}
}
@phdthesis{Piluso2012,
  author    = {Piluso, Susanna},
  title     = {Design of biopolymer-based networks with defined molecular architecture},
  url       = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus-59865},
  school      = {Universit{\"a}t Potsdam},
  year      = {2012},
  abstract  = {In this work, the synthesis of biopolymer-based hydrogel networks with defined architecture is presented. In order to obtain materials with defined properties, the chemoselective copper-catalyzed azide-alkyne cycloaddition (or Click Chemistry) was used for the synthesis of gelatin-based hydrogels. Alkyne-functionalized gelatin was reacted with four different diazide crosslinkers above its sol-gel transition to suppress the formation of triple helices. By variation of the crosslinking density and the crosslinker flexibility, the swelling (Q: 150-470 vol.-\%;) and the Young's and shear moduli (E: 50 kPa - 635 kPa, G': 0.1 kPa - 16 kPa) could be tuned in the kPa range. In order to understand the network structure, a method based on the labelling of free functional groups within the hydrogel was developed. Gelatin-based hydrogels were incubated with alkyne-functionalized fluorescein to detect the free azide groups, resulting from the formation of dangling chains. Gelatin hydrogels were also incubated with azido-functionalized fluorescein to check the presence of alkyne groups available for the attachment of bioactive molecules. By using confocal laser scanning microscopy and fluorescence spectroscopy, the amount of crosslinking, grafting and free alkyne groups could be determined. Dangling chains were observed in samples prepared by using an excess of crosslinker and also when using equimolar amounts of alkyne:azide. In the latter case the amount of dangling chains was affected by the crosslinker structure. Specifically, 0.1\% of dangling chains were found using 4,4'-diazido-2,2'-stilbene-disulfonic acid as cosslinker, 0.06\% with 1,8-diazidooctane, 0.05\% with 1,12-diazidododecane and 0.022 \% with PEG-diazide. This observation could be explained considering the structure of the crosslinkers. During network formation, the movements of the gelatin chains are restricted due to the formation of covalent netpoints. A further crosslinking will be possible only in the case of crosslinker that are flexible and long enough to reach another chain. The method used to obtain defined gelatin-based hydrogels enabled also the synthesis of hyaluronic acid-based hydrogels with tailorable properties. Alkyne-functionalized hyaluronic acid was crosslinked with three different linkers having two terminal azide functionalities. By variation of the crosslinking density and crosslinker type, hydrogels with elastic moduli in the range of 0.5-3 kPa have been prepared. The variation of the crosslinking density and crosslinker type had furthermore an influence also on the hydrolytic and enzymatic degradation of gelatin-based hydrogels. Hydrogels with a low crosslinker amount experienced a faster decrease in mass loss and elastic modulus compared to hydrogels with higher crosslinker content. Moreover, the structure of the crosslinker had a strong influence on the enzymatic degradation. Hydrogels containing a crosslinker with a rigid structure were much more resistant to enzymatic degradation than hydrogels containing a flexible crosslinker. During hydrolytic degradation, the hydrogel became softer while maintaining the same outer dimensions. These observations are in agreement with a bulk degradation mechanism, while the decrease in size of the hydrogels during enzymatic degradation suggested a surface erosion mechanism. Because of the use of small amount of crosslinker (0.002 mol.\% 0.02 mol.\%) the networks synthesized can still be defined as biopolymer-based hydrogels. However, they contain a small percentage of synthetic residues. Alternatively, a possible method to obtain biopolymer-based telechelics, which could be used as crosslinkers, was investigated. Gelatin-based fragments with defined molecular weight were obtained by controlled degradation of gelatin with hydroxylamine, due to its specific action on asparaginyl-glycine bonds. The reaction of gelatin with hydroxylamine resulted in fragments with molecular weights of 15, 25, 37, and 50 kDa (determined by SDS-PAGE) independently of the reaction time and conditions. Each of these fragments could be potentially used for the synthesis of hydrogels in which all components are biopolymer-based materials.},
  language  = {en}
}