@phdthesis{Meiling2017,
  author    = {Meiling, Till Thomas},
  title     = {Development of a reliable and environmentally friendly synthesis for fluorescence carbon nanodots},
  url       = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus4-410160},
  school      = {Universit{\"a}t Potsdam},
  pages     = {198},
  year      = {2017},
  abstract  = {Carbon nanodots (CNDs) have generated considerable attention due to their promising properties, e.g. high water solubility, chemical inertness, resistance to photobleaching, high biocompatibility and ease of functionalization. These properties render them ideal for a wide range of functions, e.g. electrochemical applications, waste water treatment, (photo)catalysis, bio-imaging and bio-technology, as well as chemical sensing, and optoelectronic devices like LEDs. In particular, the ability to prepare CNDs from a wide range of accessible organic materials makes them a potential alternative for conventional organic dyes and semiconductor quantum dots (QDs) in various applications. However, current synthesis methods are typically expensive and depend on complex and time-consuming processes or severe synthesis conditions and toxic chemicals. One way to reduce overall preparation costs is the use of biological waste as starting material. Hence, natural carbon sources such as pomelo peal, egg white and egg yolk, orange juice, and even eggshells, to name a few; have been used for the preparation of CNDs. While the use of waste is desirable, especially to avoid competition with essential food production, most starting-materials lack the essential purity and structural homogeneity to obtain homogeneous carbon dots. Furthermore, most synthesis approaches reported to date require extensive purification steps and have resulted in carbon dots with heterogeneous photoluminescent properties and indefinite composition. For this reason, among others, the relationship between CND structure (e.g. size, edge shape, functional groups and overall composition) and photophysical properties is yet not fully understood. This is particularly true for carbon dots displaying selective luminescence (one of their most intriguing properties), i.e. their PL emission wavelength can be tuned by varying the excitation wavelength. In this work, a new reliable, economic, and environmentally-friendly one-step synthesis is established to obtain CNDs with well-defined and reproducible photoluminescence (PL) properties via the microwave-assisted hydrothermal treatment of starch, carboxylic acids and Tris-EDTA (TE) buffer as carbon- and nitrogen source, respectively. The presented microwave-assisted hydrothermal precursor carbonization (MW-hPC) is characterized by its cost-efficiency, simplicity, short reaction times, low environmental footprint, and high yields of approx. 80\% (w/w). Furthermore, only a single synthesis step is necessary to obtain homogeneous water-soluble CNDs with no need for further purification. Depending on starting materials and reaction conditions different types of CNDs have been prepared. The as-prepared CNDs exhibit reproducible, highly homogeneous and favourable PL properties with narrow emission bands (approx. 70nm FWHM), are non-blinking, and are ready to use without need for further purification, modification or surface passivation agents. Furthermore, the CNDs are comparatively small (approx. 2.0nm to 2.4nm) with narrow size distributions; are stable over a long period of time (at least one year), either in solution or as a dried solid; and maintain their PL properties when re-dispersed in solution. Depending on CND type, the PL quantum yield (PLQY) can be adjusted from as low as 1\% to as high as 90\%; one of the highest reported PLQY values (for CNDs) so far. An essential part of this work was the utilization of a microwave synthesis reactor, allowing various batch sizes and precise control over reaction temperature and -time, pressure, and heating- and cooling rate, while also being safe to operate at elevated reaction conditions (e.g. 230 ±C and 30 bar). The hereby-achieved high sample throughput allowed, for the first time, the thorough investigation of a wide range of synthesis parameters, providing valuable insight into the CND formation. The influence of carbon- and nitrogen source, precursor concentration and -combination, reaction time and -temperature, batch size, and post-synthesis purification steps were carefully investigated regarding their influence on the optical properties of as-synthesized CNDs. In addition, the change in photophysical properties resulting from the conversion of CND solution into solid and back into the solution was investigated. Remarkably, upon freeze-drying the initial brown CND-solution turns into a non-fluorescent white/slightly yellow to brown solid which recovers PL in aqueous solution. Selected CND samples were also subject to EDX, FTIR, NMR, PL lifetime (TCSPC), particle size (TEM), TGA and XRD analysis. Besides structural characterization, the pH- and excitation dependent PL characteristics (i.e. selective luminescence) were examined; giving inside into the origin of photophysical properties and excitation dependent behaviour of CNDs. The obtained results support the notion that for CNDs the nature of the surface states determines the PL properties and that excitation dependent behaviour is caused by the "Giant Red-Edge Excitation Shift" (GREES).},
  language  = {en}
}