@phdthesis{Wohlgemuth2012,
  author    = {Wohlgemuth, Stephanie-Angelika},
  title     = {Functional nanostructured hydrothermal carbons for sustainable technologies : heteroatom doping and superheated vapor},
  url       = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus-60120},
  school      = {Universit{\"a}t Potsdam},
  year      = {2012},
  abstract  = {The underlying motivation for the work carried out for this thesis was the growing need for more sustainable technologies. The aim was to synthesize a "palette" of functional nanomaterials using the established technique of hydrothermal carbonization (HTC). The incredible diversity of HTC was demonstrated together with small but steady advances in how HTC can be manipulated to tailor material properties for specific applications. Two main strategies were used to modify the materials obtained by HTC of glucose, a model precursor representing biomass. The first approach was the introduction of heteroatoms, or "doping" of the carbon framework. Sulfur was for the first time introduced as a dopant in hydrothermal carbon. The synthesis of sulfur and sulfur/nitrogen doped microspheres was presented whereby it was shown that the binding state of sulfur could be influenced by varying the type of sulfur source. Pyrolysis may additionally be used to tune the heteroatom binding states which move to more stable motifs with increasing pyrolysis temperature. Importantly, the presence of aromatic binding states in the as synthesized hydrothermal carbon allows for higher heteroatom retention levels after pyrolysis and hence more efficient use of dopant sources. In this regard, HTC may be considered as an "intermediate" step in the formation of conductive heteroatom doped carbon. To assess the novel hydrothermal carbons in terms of their potential for electrochemical applications, materials with defined nano-architectures and high surface areas were synthesized via templated, as well as template-free routes. Sulfur and/or nitrogen doped carbon hollow spheres (CHS) were synthesized using a polystyrene hard templating approach and doped carbon aerogels (CA) were synthesized using either the albumin directed or borax-mediated hydrothermal carbonization of glucose. Electrochemical testing showed that S/N dual doped CHS and aerogels derived via the albumin approach exhibited superior catalytic performance compared to solely nitrogen or sulfur doped counterparts in the oxygen reduction reaction (ORR) relevant to fuel cells. Using the borax mediated aerogel formation, nitrogen content and surface area could be tuned and a carbon aerogel was engineered to maximize electrochemical performance. The obtained sample exhibited drastically improved current densities compared to a platinum catalyst (but lower onset potential), as well as excellent long term stability. In the second approach HTC was carried out at elevated temperatures (550 °C) and pressure (50 bar), corresponding to the superheated vapor regime (htHTC). It was demonstrated that the carbon materials obtained via htHTC are distinct from those obtained via ltHTC and subsequent pyrolysis at 550 °C. No difference in htHTC-derived material properties could be observed between pentoses and hexoses. The material obtained from a polysaccharide exhibited a slightly lower degree of carbonization but was otherwise similar to the monosaccharide derived samples. It was shown that in addition to thermally induced carbonization at 550 °C, the SHV environment exhibits a catalytic effect on the carbonization process. The resulting materials are chemically inert (i.e. they contain a negligible amount of reactive functional groups) and possess low surface area and electronic conductivity which distinguishes them from carbon obtained from pyrolysis. Compared to the materials presented in the previous chapters on chemical modifications of hydrothermal carbon, this makes them ill-suited candidates for electronic applications like lithium ion batteries or electrocatalysts. However, htHTC derived materials could be interesting for applications that require chemical inertness but do not require specific electronic properties. The final section of this thesis therefore revisited the latex hard templating approach to synthesize carbon hollow spheres using htHTC. However, by using htHTC it was possible to carry out template removal in situ because the second heating step at 550 °C was above the polystyrene latex decomposition temperature. Preliminary tests showed that the CHS could be dispersed in an aqueous polystyrene latex without monomer penetrating into the hollow sphere voids. This leaves the stagnant air inside the CHS intact which in turn is promising for their application in heat and sound insulating coatings. Overall the work carried out in this thesis represents a noteworthy development in demonstrating the great potential of sustainable carbon materials.},
  language  = {en}
}