@phdthesis{Suetterlin2013,
  author    = {S{\"u}tterlin, Martin},
  title     = {New inverse hydogel opals as protein responsive sensors},
  url       = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus-70179},
  school      = {Universit{\"a}t Potsdam},
  year      = {2013},
  abstract  = {In this work, the development of temperature- and protein-responsive sensor materials based on biocompatible, inverse hydrogel opals (IHOs) is presented. With these materials, large biomolecules can be specifically recognised and the binding event visualised. The preparation of the IHOs was performed with a template process, for which monodisperse silica particles were vertically deposited onto glass slides as the first step. The obtained colloidal crystals with a thickness of 5 μm displayed opalescent reflections because of the uniform alignment of the colloids. As a second step, the template was embedded in a matrix consisting of biocompatible, thermoresponsive hydrogels. The comonomers were selected from the family of oligo(ethylene glycol)methacrylates. The monomer solution was injected into a polymerisation mould, which contained the colloidal crystals as a template. The space in-between the template particles was filled with the monomer solution and the hydrogel was cured via UV-polymerisation. The particles were chemically etched, which resulted in a porous inner structure. The uniform alignment of the pores and therefore the opalescent reflection were maintained, so these system were denoted as inverse hydrogel opals. A pore diameter of several hundred nanometres as well as interconnections between the pores should facilitate a diffusion of bigger (bio)molecules, which was always a challenge in the presented systems until now. The copolymer composition was chosen to result in a hydrogel collapse over 35 °C. All hydrogels showed pronounced swelling in water below the critical temperature. The incorporation of a reactive monomer with hydroxyl groups ensured a potential coupling group for the introduction of recognition units for analytes, e.g. proteins. As a test system, biotin as a recognition unit for avidin was coupled to the IHO via polymer-analogous Steglich esterification. The amount of accessible biotin was quantified with a colorimetric binding assay. When avidin was added to the biotinylated IHO, the wavelength of the opalescent reflection was significantly shifted and therefore the binding event was visualised. This effect is based on the change in swelling behaviour of the hydrogel after binding of the hydrophilic avidin, which is amplified by the thermoresponsive nature of the hydrogel. A swelling or shrinking of the pores induces a change in distance of the crystal planes, which are responsible for the colour of the reflection. With these findings, the possibility of creating sensor materials or additional biomolecules in the size range of avidin is given.},
  language  = {en}
}
@misc{JeličićFriedrichJeremićetal.2009,
  author    = {Jeličić, Aleksandra and Friedrich, Alwin and Jeremić, Katarina and Siekmeyer, Gerd and Taubert, Andreas},
  title     = {Polymer hydrogel/polybutadiene/iron oxide nanoparticle hybrid actuators for the characterization of NiTi implants},
  url       = {http://nbn-resolving.de/urn:nbn:de:kobv:517-opus-48589},
  year      = {2009},
  abstract  = {One of the main issues with the use of nickel titanium alloy (NiTi) implants in cardiovascular implants (stents) is that these devices must be of very high quality in order to avoid subsequent operations due to failing stents. For small stents with diameters below ca. 2 mm, however, stent characterization is not straightforward. One of the main problems is that there are virtually no methods to characterize the interior of the NiTi tubes used for fabrication of these tiny stents. The current paper reports on a robust hybrid actuator for the characterization of NiTi tubes prior to stent fabrication. The method is based on a polymer/hydrogel/magnetic nanoparticle hybrid material and allows for the determination of the inner diameter at virtually all places in the raw NiTi tubes. Knowledge of the inner structure of the raw NiTi tubes is crucial to avoid regions that are not hollow or regions that are likely to fail due to defects inside the raw tube. The actuator enables close contact of a magnetic polymer film with the inner NiTi tube surface. The magnetic signal can be detected from outside and be used for a direct mapping of the tube interior. As a result, it is possible to detect critical regions prior to expensive and slow stent fabrication processes.},
  language  = {en}
}